Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Metal-free atom transfer radical polymerization with ppm catalyst loading under sunlight


Organocatalytic atom transfer radical polymerization (O-ATRP) is recently emerging as an appealing method for the synthesis of metal-free polymer materials with well-defined microstructures and architectures. However, the development of highly effective catalysts that can be employed at a practical low loading are still a challenging task. Herein, we introduce a catalyst design logic based on heteroatom-doping of polycyclic arenes, which leads to the discovery of oxygen-doped anthanthrene (ODA) as highly effective organic photoredox catalysts for O-ATRP. In comparison with known organocatalysts, ODAs feature strong visible-light absorption together with high molar extinction coefficient (ε455nm up to 23,950 M–1 cm–1), which allow for the establishment of a controlled polymerization under sunlight at low ppm levels of catalyst loading.


Since the discovery in the 1990s, atom transfer radical polymerization (ATRP) has evolved into one of the most versatile and utilized polymerization methods for the synthesis of polymer materials with well-defined structures and architectures, and widely employed in a variety of industrial applications including coatings, adhesives, cosmetics, inkjet printings, etc.1,2,3 However, conventional ATRPs rely on transition metal catalysts [i.e., Cu(I), Ru(II)],3 which will result in transition metal contaminations in the final products, and thus raise concerns when applied to fields sensitive to metal contaminants.4,5,6 Therefore, considerable efforts have been dedicated to lowering catalyst loadings or removing residual metals since the initial discovery of ATRP.5,6,7,8 Whereas, the recent emerging organocatalytic atom transfer radical polymerization (O-ATRP) using organic photoredox catalysts, undoubtedly, represents an ideal solution to this challenging issue.9,10,11,12,13,14,15

Since the conceptual work first demonstrated O-ATRP in 2014 by using organic molecules such as N-phenyl phenothiazine or perylene as a catalyst,16,17,18 it has immediately attracted wide research interests in the past 5 years.19,20,21,22 Until now, several frameworks/core structures22 including phenothiazine (1),16,23,24 dihydrophenazine (2),25,26,27,28 phenoxazine (3),29,30 etc.31,32,33,34,35,36,37 have been successfully identified as efficient photocatalysts (PC) for O-ATRP (Fig. 1a). However, a 1000-ppm level of catalyst loading was typically required to reach a satisfactory control over the polymerization. Controlled polymerization at a practical low catalyst loading (<10 ppm) could not only eliminate the need of further product purification or residual catalyst removal, but could also decrease the cost of commercial production.14,28 Therefore, the development of highly effective photocatalysts for O-ATRP has thus become a focus of extensive studies in recent years.20,21,22,24,28 Whereas, many mechanistic aspects in O-ATRP remain unclear so far, and there is still a lack of general guidelines for the catalyst design.22,38

Fig. 1: The development of catalysts for O-ATRP.

a Catalyst development via core structure modification. b O-ATRP photocatalyst design based on a heteroatom-doping logic (this work). c Catalytic cycle for a light-mediated O-ATRP. d Polymerization under sunlight and the product color (PMMA). SET single electron transfer, OPC organic photocatalyst, PMMA polymethyl methacrylate.

Phenothiazine,16 dihydrophenazine,25 and phenoxazine29 are among the most efficient and widely used catalyst frameworks that could achieve a well-controlled O-ATRP polymerization with low dispersity.22 To further increase the catalyst efficiency, much effort has been dedicated to the modifications of the catalyst structures such as introducing aryl groups, which could enhance the visible-light absorption, but the red shift of absorption maximum (λmax) was often quite limited.21,22 Interestingly, an analysis on the UV-visible-light absorption of these photocatalysts unveiled a uniformly decreased light absorption profile from its absorption maximum (<400 nm) to visible light.16,22,25,29 Therefore, we questioned whether there is a possibility to find a suitable and tunable O-ATRP catalyst framework with its absorption maximum located in the visible-light region, and a stronger light absorption could probably lower the catalyst loading. The three photocatalysts (1–3) can be recognized as derivatives obtained by modifying the corresponding core chromophoric structures: phenothiazine, dihydrophenazine, and phenoxazine, respectively (Fig. 1a). Recently, we were thinking that heteroatom-doping39,40 of small polycyclic arenes might be a feasible catalyst design logic for the O-ATRP photocatalyst development (Fig. 1b).

According to the oxidative quenching mechanism (Fig. 1c), organic photoredox catalysts possessing a highly reducing excited state are required to reduce the alkyl bromides via a single electron transfer (SET) to initiate the polymerization.41 Besides, redox potential, photophysical property, stability, etc. of the related catalytic species are also critical to establish a fast and effective switching between propagating and dormant states of the macro-initiators, thus achieving a controlled polymerization with narrow dispersities.38,41,42,43 The integration of heteroatoms such as N, O, S, etc. into aromatic hydrocarbons could regulate the photophysical and photoredox properties of these polycyclic arene catalysts39,41, and thus probably lead to an improvement in their catalytic performance on polymerization and suppress undesired catalyst decomposition or catalyst-initiation.17,31,32 With this idea in mind, we thus decided to practice this heteroatom-doping strategy on graphene, and narrowed down the parental aromatic (extended π) system to anthanthrene (Fig. 1b, left), which possesses the desired strong absorption in the visible-light region.44 Oxygen-doping was chosen for the current research, as: (i) the known high-performance photocatalysts for O-ATRP were developed based on the charge-transfer (CT) principle,24,25,26,27,28,29,30 and typically contain a triaryl amine part, which is required to impose a twisted donor–acceptor structure to favor the CT process.24,25,26,27,28,45 Therefore, the development of a completely new photocatalyst framework lacking this moiety and that could also achieve the same level or even better performance can be of fundamental significance, which, to the best of our knowledge, remains unknown so far; (ii) O-doping can regulate the photophysical and redox properties of anthanthrene, probably leading to a more oxidizing OPC•+ in comparison with the typical amine-containing catalysts 1–3, which may thus afford a better deactivation control.25,26,27,28,41 Here, we report our efforts toward this goal, and the discovery of oxygen-doped anthanthrene (ODA) as an effective organocatalyst framework for O-ATRP, which exhibits strong absorption at the visible-light region (ε450nm > 20,000 M–1 cm–1), and allows for a ppm/sub-ppm level of catalyst loading only to deliver a metal-free, controlled polymerization under visible light or even sunlight (Fig. 1d).


Catalyst synthesis and characterization

The ODA can be readily constructed via dual oxidative cyclization46 from the commercially available 1,1′-bisnaphthol (BINOL) (Fig. 2a). Further, by virtue of its high modifiability,47 ODAs with different substituents can be readily synthesized via a 3,3′-modification of BINOL/oxidative cyclization sequence (see Supplementary Methods). To improve the catalyst solubility, we synthesized the n-butyl substituted catalyst 5b, while 5c and 5d were prepared to examine the influence of aryl substituents (for synthetic procedures and spectra, see Supplementary Information). As anticipated, 5a did show a strong absorption in the visible-light region (Fig. 2b), with a red shift of the absorption maximum from 437 to 443 nm (comparing with the parental anthanthrene44). This absorption profile is in sharp contrast to that of the known photocatalysts such as 1–3, which possess a smaller conjugation in the core structure and absorption maximums appearing in the ultra-violet region (<400 nm). Both the absorption maximums (λmax = 454 and 455 nm) of 5c and 5d have shown a further red shift (ca. 12 nm) as well as enhanced light absorption (εmax = 22,580 and 23,950 vs 17,450 M–1 cm–1). In addition, a notable feature of the ODA catalysts substantially different from the known high-performance O-ATRP photocatalysts24,28 is the lack of a charge-separation in their excited states (Fig. 2c). Based on the fluorescence emission and the cyclic voltammetry (CV) data, we could assess the reducing capability of the excited singlet states (E0*(PC•+/1PC*)) of these catalysts, ranging from −1.76 to −1.84 V vs SCE (saturated calomel electrode) (Fig. 2d). Density functional theory (DFT) was used to estimate the reduction ability of the triplet excited-states (E0 (PC•+/3PC*), which are in the range of −1.58 to −1.71 V vs SCE (Fig 2c, for details, see Supplementary Information and Computational details). Although the excited states of ODA 5a–5d are less reductive than that of N-phenyl phenothiazine (1, Ar = Ph, R = H, E0* = −2.1 V vs SCE),16 all are more negative than −0.7 V that is required to reduce ethyl α-bromophenylacetate (EBP, a common initiator, E0(EBP/EBP•–) = –0.74 V SCE).25 Notably, the radical cations (PC•+) of ODA catalysts are much more oxidizing (up to +0.82 V vs SCE), in comparison with the most efficient dihydrophenazine-based photocatalyst (+0.38 V vs SCE).28

Fig. 2: Synthesis and characterization of photocatalysts.

a Synthesis of oxygen-dopants of anthanthrene 5a–d. b UV-Vis absorption profiles. c SOMO orbitals and triplet reducing power of 5a and 5d. d Characterization data of photocatalyst 5a–5d by UV-Vis, fluorescence emission, CV, and calculated redox potentials. SCE saturated calomel electrode, SOMO singly occupied molecular orbital, CV cyclic voltammetry.

Table 1 Catalyst evaluation in the atom-transfer radical polymerization of MMA.

Initial evaluation of the photocatalysts

We conducted the initial evaluation of these oxygen-doped catalysts in the polymerization of methyl methacrylate (MMA) by using EBP as initiator, dimethylacetamide (DMA) as solvent under the irradiation of purple light-emitting diodes (LEDs, λmax 400 nm). To our delight, 5a could afford a controlled polymerization with a moderate dispersity (Table 1, entry 1). The polymerization can also be conducted with control in other solvents, such as dimethylformamide (DMF, entry 2), dichloromethane (DCM), toluene, tetrahydrofuran, etc. (Supplementary Table 2). DCM gave the lowest dispersity (Đ = 1.25) together with a good agreement between the experimental and theoretical Mn (entry 3). Remarkably, ODA 5a is also effective with other initiators such as ethyl-bromopropanoate (EBrP), ethyl-2-bromoisobutanoate (EBiB), diethyl 2-bromomalonate (DBM), and diethyl 2-bromo-2-methylmalonate (DBMM) (Đ 1.19–1.27,  entries 4–7). 5b–5d with different substituents were then compared under the standard conditions by using EBP as the initiator. Pleasingly, all the three new catalysts are effective for the polymerization (entries 8–10), and ODA 5b could achieve a dispersity (Đ) lower than 1.20 (entry 8). Catalysts 5b and 5d were further examined with DBMM (entries 12 & 13), and a remarkable narrow dispersity (Đ = 1.12, entry 12) was obtained with 5d. Irradiation with lower energy blue LEDs was also effective (entries 13 & 14).

Light regulation, kinetics, and block polymer synthesis

A prominent feature of the O-ATRP is that the polymerization can be regulated by light.48,49 To examine the temporal control ability of the current system, a light on–off experiment was performed with light on–off cycle repeating for several times until over 90% conversion was achieved. As depicted in Fig. 3a, the polymerization only preceded in the presence of light irradiation, while no polymerization was observed in dark. Further, light on–off experiments have shown no conversion even over a long dark period up to 12 h. This strict control by light over the whole process suggests an effective activation and deactivation mechanism of the polymerization. The polymerization was then followed by 1H NMR to gain some insights about the polymerization kinetics, which unveiled a first-order kinetics through the course of the reaction (Fig. 3b). The Mn,GPC values were plotted against the monomer conversion, as shown in Fig. 3c, and a linear increase of molecular mass throughout the polymerization process was observed. Notably, the y-intercept of the Mn vs conversion plot was 870 Da, indicating that the control of the polymerization was achieved after the initial addition of ~6 MMA (Fig. 3c).25 This strict control may benefit from a more efficient deactivation process26,37,45 due to the radical cations of ODA photocatalysts possessing a better oxidizing ability, when compared with the dihydrophenazine-derived photocatalysts.25,28

Fig. 3: Temporal control and kinetic study on ODA 5d-catalyzed ATRP of MMA.

a Light on–off experiments and the plot of monomer conversion vs time. b Kinetic plot for the metal-free ATRP. c Plot of Mn and Đ vs monomer conversion for the polymerization of MMA under continuous irradiation. d GPC traces of each polymer depicted in (c) (color coded). All polymerizations were performed at a ratio of [MMA]0:[DBMM]0:[5d]0 = 200:1:0.05 under purple LED irradiation (400 nm, 25 mW cm–2) .

Regarding the chain-end fidelity, a polymethyl methacrylate (PMMA) sample obtained via 5d-mediated metal-free ATRP was subjected to MALDI-TOF (matrix-assisted laser desorption/ionization time-of-flight mass-spectrometer) analysis (Supplementary Fig. 10), which shows a consistence observed molecular weight with the expected values with each peak separated by the mass of one MMA (100 Da), and individual PMMA polymers having the initiating unit at one chain end and a bromine atom at the propagating chain end. An advantage of high chain-end fidelity is it enables the synthesis of block polymers. As shown in Fig. 4, chain extension (PMMA-b-PMMA) and block copolymerization products (PMMA-b-PBnMA and PMMA-b-PBA) can all be prepared with this catalytic system. Notably, the gel permeation chromatography (GPC) traces, all clearly show an obvious shift to higher molecular weight species with little tailing in the homo-polymer regime, giving further support to the high alkyl bromide chain-end fidelity in the PMMA macro-initiators (purified via re-precipitation from methanol) and also a high re-initiation efficiency. Of note, this result is also in consistence with the high initiator efficiency observed in the polymerizations with freshly distilled DBMM (Supplementary Table 8). Moreover, triblock copolymer synthesis is also viable with this system as demonstrated with the preparation of PMMA-b-PBnMA-b-PBA (see Supplementary Fig. 13).

Fig. 4: Block polymer preparation.

a Chain-extension from a PMMA macro-initiator (black) to produce block copolymers after a further polymerization with MMA (green), BnMA (red), and BA (blue). b GPC traces of the corresponding polymers depicted in left by using the same color coded. BnMA benzyl methacrylate, BA butyl acrylate.

Polymerization at low ppm catalyst loadings

The high molar-extinction coefficiency (εmax upto 23,950 M–1 cm–1) of ODA catalysts at the visible-light region encouraged us to examine their performance at low catalyst loadings. As shown in Tables 1 and 2, decreasing the catalyst loading from 500 to 10 ppm, both photocatalysts 5a and 5d could maintain their catalytic efficiency, giving a controlled polymerization with low dispersity (Table 2, entries 1–3). To our delight, in the present system, very narrow dispersity can be achieved with 10 ppm 5d only (entry 3). Remarkably, the catalyst loading of 5d can be further decreased from 10 to 0.1 ppm (entries 3–6), and even to 50 ppb by more than two orders of magnitude (entry 7), which is among the lowest catalyst loadings so far in O-ATRP.28 It is worth mentioning that a catalyst loading less than 10 ppm could be very meaningful, which may eliminate the need of the catalyst removal process. Importantly, white polymer products can be obtained at the catalyst loading less than 50 ppm, even though the photocatalysts are normally colored compounds (Fig. 1d). The high catalytic performance may benefit from their strong visible-light absorption (5d, ε455nm = 23,950 M–1 cm–1). In fact, the strength of visible-light absorption is approximately one order of magnitude stronger than that of fac-Ir(ppy)3458nm = 2450 M–1 cm–1), which is a commonly used organometallic photoredox catalyst.50 Remarkably, sunlight is also suitable to drive the polymerization with 10 ppm catalyst only (entries 8 & 9). To the best of our knowledge, 10 ppm represents the lowest catalyst loading achieved so far in controlled O-ATRP under sunlight. Furthermore, other methacrylate monomers such as 2,2,2-trifluoroethyl methacrylate (TFEMA) and benzyl methacrylate (BnMA) can also be polymerized with low dispersity at 10 or 50 ppm catalyst loading (entries 10–12). Surprisingly, ODA catalysts could also deliver a controlled polymerization with low dispersity in the polymerization of n-butyl acrylate (entries 13 & 14, also see Supplementary Table 6). It is worth mentioning that acrylate monomers proved to be very challenging to achieve a controlled polymerization with low dispersity by O-ATRP methods due to their high polymerization rate.25,28,45 To our delight, this control on low dispersity is even better than that with dihydroacridine photocatalysts, which was developed especially for this type of monomers very recently.45 Notably, ODA 5d also represents a rare example of organic photocatalysts that could promote the polymerization of both MMA and BA with good controls.28,45

Table 2 Polymerization with low catalyst loadings.


In this work, a catalyst design logic based on heteroatom-doping of polycyclic arenes has been successfully introduced into the development of photocatalysts for O-ATRP. ODA has been identified as a catalyst framework with high efficiency, featuring its strong visible-light absorption and excellent performance at very low catalyst loadings (50 ppb to 10 ppm) in organocatalytic ATRP. This framework also represents a rare example of non-N-heterocyclic organocatalysts lacking a CT character that could mediate the ATRP with good control and low dispersity (Ɖ < 1.20) at a ppm level of catalyst loading. We anticipate that this class of photoredox catalysts will find further applications in polymer synthesis and other photocatalysis-related fields.


Typical procedure for O-ATRP of MMA under light

Typical metal-free organocatalytic ATRP procedures with the molar ratio of [MMA]0:[initiator]0:[catalyst]0 = 100:1:0.05 were shown as follows. The polymerization was conducted with MMA (1.0 mL, 9.35 mmol, 100 eq.) as the model monomer, DBMM (18 μL, 93.5 μmol, 1.0 eq.) as the ATRP initiator, organic photocatalyst (4.70 μmol, 0.5 eq.), and DCM (1.0 mL) as the solvent in a Schlenk tube with a PTFE stirring bar. The mixture was deoxygenized by freeze–pump–thaw cycle three times, backfilled argon, and sealed up subsequently. And then the polymerization occurred under purple LED or blue LED or sunlight irradiation at room temperature. After the desired time, the tube was opened under argon and 20.0 μL of mixture was syringed out and quenched into CDCl3 containing 250 ppm BHT to determine the monomer conversion by 1H NMR. The reaction mixture was then diluted with 0.5 mL dichloromethane and dissolved completely, then dripped into 75 mL methanol and stirred for 2 h. The precipitate was then collected by suction filtration with a Buchner funnel and dried in vacuum oven until a constant weight was achieved, at 30 °C to give the purified polymers. For details, additional data, and experiments, please see the Supplementary Information (Supplementary Methods, Supplementary Figs. 118, Supplementary Tables 18, etc.).

Data availability

The authors declare that all data supporting the findings of this study are available within the article and Supplementary Information files, and are also available from the corresponding author upon reasonable request.


  1. 1.

    Matyjaszewski, K. Advanced materials by atom transfer radical polymerization. Adv. Mater. 30, 1706441 (2018).

    Article  CAS  Google Scholar 

  2. 2.

    Matyjaszewski, K. & Tsarevsky, N. V. Macromolecular engineering by atom transfer radical polymerization. J. Am. Chem. Soc. 136, 6513–6533 (2014).

    CAS  PubMed  Article  Google Scholar 

  3. 3.

    Braunecker, W. A. & Matyjaszewski, K. Controlled/living radical polymerization: features, developments, and perspectives. Prog. Polym. Sci. 32, 93–146 (2007).

    CAS  Article  Google Scholar 

  4. 4.

    Tsarevsky, N. V. & Matyjaszewski, K. “Green” atom transfer radical polymerization: from process design to preparation of well-defined environmentally friendly polymeric materials. Chem. Rev. 107, 2270–2299 (2007).

    CAS  PubMed  Article  Google Scholar 

  5. 5.

    Matyjaszewski, K. et al. Diminishing catalyst concentration in atom transfer radical polymerization with reducing agents. Proc. Natl Acad. Sci. USA 103, 15309–15314 (2006).

    ADS  CAS  PubMed  Article  Google Scholar 

  6. 6.

    Pintauer, T. & Matyjaszewski, K. Atom transfer radical addition and polymerization reactions catalyzed by ppm amounts of copper complexes. Chem. Soc. Rev. 37, 1087–1097 (2008).

    CAS  PubMed  Article  Google Scholar 

  7. 7.

    Ding, M., Jiang, X., Zhang, L., Cheng, Z. & Zhu, X. Recent progress on transition metal catalyst separation and recycling in ATRP. Macromol. Rapid Commun. 36, 1702–1721 (2015).

    CAS  PubMed  Article  Google Scholar 

  8. 8.

    Boyer, C. et al. Copper-mediated living radical polymerization (atom transfer radical polymerization and copper(0) mediated polymerization): from fundamentals to bioapplications. Chem. Rev. 116, 1803–1949 (2016).

    CAS  PubMed  Article  Google Scholar 

  9. 9.

    Corrigan, N., Shamugam, S., Xu, J. & Boyer, C. Photocatalysis in organic polymer synthesis. Chem. Soc. Rev. 45, 6165–6212 (2016).

    CAS  PubMed  Article  Google Scholar 

  10. 10.

    Zivic, N. et al. Photocatalysts in polymerization reactions. ChemCatChem 8, 1617–1631 (2016).

    CAS  Article  Google Scholar 

  11. 11.

    Ottou, W. N., Sardon, H., Mecerreyes, D., Vignolle, J. & Taton, D. Update and challenges in organo-mediated polymerization reactions. Prog. Polym. Sci. 56, 64–115 (2016).

    CAS  Article  Google Scholar 

  12. 12.

    Pan, X. et al. Photomediated controlled radical polymerization. Prog. Polym. Sci. 62, 73–125 (2016).

    CAS  Article  Google Scholar 

  13. 13.

    Dadashi-Silab, S., Doran, S. & Yagci, Y. Photoinduced electron transfer reactions for macromolecular syntheses. Chem. Rev. 116, 10212–10275 (2016).

    CAS  PubMed  Article  Google Scholar 

  14. 14.

    Shanmugam, S. & Boyer, C. Organic photocatalysts for cleaner polymer synthesis. Science 352, 1053–1054 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  15. 15.

    Hu, S., Zhao, J., Zhang, G. & Schlaad, H. Macromolecular architectures through organocatalysis. Prog. Polym. Sci. 74, 34–77 (2017).

    CAS  Article  Google Scholar 

  16. 16.

    Treat, N. J. et al. Metal-free atom transfer radical polymerization. J. Am. Chem. Soc. 136, 16096–16101 (2014).

    CAS  PubMed  Article  PubMed Central  Google Scholar 

  17. 17.

    Miyake, G. M. & Theriot, J. C. Perylene as an organic photocatalyst for the radical polymerization of functionalized vinyl monomers through oxidative quenching with alkyl bromides and visible light. Macromolecules 47, 8255–8261 (2014).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Pan, X., Lamson, M., Yan, J. & Matyjaszewski, K. Photoinduced metal-free atom transfer radical polymerization of acrylonitrile. ACS Macro Lett. 4, 192–196 (2015).

    CAS  Article  Google Scholar 

  19. 19.

    Shanmugam, S., Xu, J. & Boyer, C. Photocontrolled living polymerization systems with reversible deactivations through electron and energy transfer. Macromol. Rapid Commun. 38, 1700143 (2017).

    Article  CAS  Google Scholar 

  20. 20.

    Kreutzer, J. & Yagci, Y. Metal free reversible-deactivation radical polymerizations: advances, challenges, and opportunities. Polymers 10, 35 (2018).

    Article  CAS  Google Scholar 

  21. 21.

    Yilmaz, G. & Yagci, Y. Photoinduced metal-free atom transfer radical polymerizations: state-of-the-art, mechanistic aspects and applications. Polym. Chem. 9, 1757–1762 (2018).

    CAS  Article  Google Scholar 

  22. 22.

    Discekici, E. H., Anastasaki, A., Read de Alaniz, J. & Hawker, C. J. Evolution and future directions of metal-free atom transfer radical polymerization. Macromolecules 51, 7421–7434 (2018).

    ADS  CAS  Article  Google Scholar 

  23. 23.

    Dadashi-Silab, S., Pan, X. & Matyjaszewski, K. Phenyl benzo[b]phenothiazine as a visible light photoredox catalyst for metal-free atom transfer radical polymerization. Chem. Eur. J. 23, 5972–5977 (2017).

    CAS  PubMed  Article  Google Scholar 

  24. 24.

    Singh, V. K. et al. Highly efficient organic photocatalysts discovered via a computer-aided-design strategy for visible-light-driven atom transfer radical polymerization. Nat. Catal. 1, 794–804 (2018).

    CAS  Article  Google Scholar 

  25. 25.

    Teriot, J. C. et al. Organocatalyzed atom transfer radical polymerization driven by visible light. Science 352, 1082–1086 (2016).

    ADS  Article  CAS  Google Scholar 

  26. 26.

    Lim, C.-H. et al. Intramolecular charge transfer and ion pairing in N,N-diaryl dihydrophenazine photoredox catalysts for efficient organocatalyzed atom transfer radical polymerization. J. Am. Chem. Soc. 139, 348–355 (2017).

    CAS  PubMed  Article  Google Scholar 

  27. 27.

    Theriot, J. C., Miyake, G. M. & Boyer, C. A. N,N‑Diaryl dihydrophenazines as photoredox catalysts for PET-RAFT and sequential PET-RAFT/O-ATRP. ACS Macro Lett. 7, 662–666 (2018).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  28. 28.

    Cole, J. P., Federico, C. R., Lim, C.-H. & Miyake, G. M. Photoinduced organocatalyzed atom transfer radical polymerization using low ppm catalyst loading. Macromolecules 52, 747–754 (2019).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  29. 29.

    Pearson, R. M., Lim, C.-H., McCarthy, B. G., Musgrave, C. B. & Miyake, G. M. Organocatalyzed atom transfer radical polymerization using N-aryl phenoxazines as photoredox catalysts. J. Am. Chem. Soc. 138, 11399–11407 (2016).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  30. 30.

    McCarthy, B. G. et al. Structure–property relationships for tailoring phenoxazines as reducing photoredox catalysts. J. Am. Chem. Soc. 140, 5088–5101 (2018).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  31. 31.

    Allushi, A., Jockusch, S., Yilmaz, G. & Yagci, Y. Photoinitiated metal-free controlled/living radical polymerization using polynuclear aromatic hydrocarbons. Macromolecules 49, 7785–7792 (2016).

    ADS  CAS  Article  Google Scholar 

  32. 32.

    Aydogan, C., Yilmaz, G. & Yagci, Y. Synthesis of hyperbranched polymers by photoinduced metal-free ATRP. Macromolecules 50, 9115–9120 (2017).

    ADS  CAS  Article  Google Scholar 

  33. 33.

    Huang, Z. et al. Metal-free atom transfer radical polymerization of methyl methacrylate with ppm level of organic photocatalyst. Macromol. Rapid Commun. 38, 1600461 (2017).

    Article  CAS  Google Scholar 

  34. 34.

    Kutahya, C. et al. Photoinduced metal-free atom transfer radical polymerization using highly conjugated thienothiophene derivatives. Macromolecules 50, 6903–6910 (2017).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Trotta, J. T. & Fors, B. P. Organic catalysts for photocontrolled polymerizations. Synlett 27, 702–713 (2016).

    CAS  Article  Google Scholar 

  36. 36.

    Corbin, D. A., Lim, C.-H. & Miyake, G. M. Phenothiazines, dihydrophenazines, and phenoxazines: sustainable alternatives to precious-metal-based photoredox catalysts. Aldrichim. Acta 52, 7–21 (2019).

    CAS  Google Scholar 

  37. 37.

    Dell’Amico, L., Vega-Penaloza, A., Mateos, J., Companyo, X. & Escudero-Casao, M. A Rational approach to organo-photocatalysis. Novel designs and structure-property-relationships. Angew. Chem. Int. Ed. (2020).

  38. 38.

    Teriot, J. C., McCarthy, B. G., Lim, C.-H. & Miyake, G. M. Organocatalyzed atom transfer radical polymerization: perspectives on catalyst design and performance. Macromol. Rapid Commun. 38, 1700040 (2017).

    Article  CAS  Google Scholar 

  39. 39.

    Duan, J., Chen, S., Jaroniec, M. & Qiao, S. Z. Heteroatom-doped graphene-based materials for energy-relevant electrocatalytic processes. ACS Catal. 5, 5207–5234 (2015).

    CAS  Article  Google Scholar 

  40. 40.

    Liu, J. & Feng, X. Bottom-up synthesis of nitrogen-doped polycyclic aromatic hydrocarbons. Synlett 31, 211–222 (2020).

    CAS  Article  Google Scholar 

  41. 41.

    Pan, X. et al. Mechanism of photoinduced metal-free atom transfer radical polymerization: experimental and computational studies. J. Am. Chem. Soc. 138, 2411–2425 (2016).

    CAS  PubMed  Article  Google Scholar 

  42. 42.

    Chen, M., Zhong, M. & Johnson, J. A. Light-controlled radical polymerization: mechanisms, methods, and applications. Chem. Rev. 116, 10167–10211 (2016).

    CAS  PubMed  Article  Google Scholar 

  43. 43.

    Koyama, D., Dale, HarveyJ. A. & Orr-Ewing, A. J. Ultrafast observation of a photoredox reaction mechanism: photoinitiation in organocatalyzed atom-transfer radical polymerization. J. Am. Chem. Soc. 140, 1285–1293 (2018).

    CAS  PubMed  Article  Google Scholar 

  44. 44.

    Shah, B. K., Neckers, D. C., Shi, J., Forsythe, E. W. & Morton, D. Photophysical properties of anthanthrene-based tunable blue emitters. J. Phys. Chem. A 109, 7677–7681 (2005).

    CAS  PubMed  Article  Google Scholar 

  45. 45.

    Buss, B. L., Lim, C.-H. & Miyake, G. M. Dimethyl dihydroacridines as photocatalysts in organocatalyzed atom transfer radical polymerization of acrylate monomers. Angew. Chem. Int. Ed. 132, 3235–3243 (2020).

    Article  Google Scholar 

  46. 46.

    Kamei, T., Uryu, M. & Shimada, T. Cu-catalyzed aerobic oxidative C–H/C–O cyclization of 2,2′-binaphthols: practical synthesis of PXX derivatives. Org. Lett. 19, 2714–2717 (2017).

    CAS  PubMed  Article  Google Scholar 

  47. 47.

    Akiyama, T. Stronger Brønsted acids. Chem. Rev. 107, 5744–5758 (2007).

    CAS  PubMed  Article  Google Scholar 

  48. 48.

    Pan, X., Fantin, M., Yuana, F. & Matyjaszewski, K. Externally controlled atom transfer radical polymerization. Chem. Soc. Rev. 47, 5457–5490 (2018).

    CAS  PubMed  Article  Google Scholar 

  49. 49.

    Corrigan, N., Yeow, J., Judzewitsch, P., Xu, J. & Boyer, C. Seeing the light: advancing materials chemistry through photopolymerization. Angew. Chem. Int. Ed. 58, 5170–5189 (2019).

    CAS  Article  Google Scholar 

  50. 50.

    Fors, B. P. & Hawker, C. J. Control of a living radical polymerization of methacrylates by light. Angew. Chem. Int. Ed. 51, 8850–8853 (2012).

    CAS  Article  Google Scholar 

Download references


We thank Prof. Krzysztof Matyjaszewski (Carnegie Mellon University) and Prof. Junfang Li (Shanghai Institute of Organic Chemistry, CAS) for helpful discussions and suggestions. Dr. Zechun Jiang is highly appreciated for his support with GPC (Wyatt MALS) measurements. Many thanks to Dr. Zhiwei Lin (Xiamen University) for her help in the MALDI-TOF test, and to Prof. Jianjun Sun and Ms. Xingyuan Du (Fuzhou University) for their help in electrochemical measurements. We thank the Recruitment Program of Global Experts, National Natural Science Foundation of China (21602028), Beijing National Laboratory for Molecular Sciences (BNLMS201913), the Hundred-Talent Project of Fujian, and Fuzhou University for the financial support. In memory of my beloved son, David Liao, who remains a lifelong inspiration for my scientific work (S.L.).

Author information




Q.M. conducted the research on the catalyst synthesis, polymerization evaluation, kinetic study, characterization, etc.; J.S. performed the computational study; X.Z., Y. J., and L.J. participated in the catalyst synthesis and polymerization development; S.L. conceived this concept and prepared this manuscript with feedback from Q.M. and J.S.

Corresponding author

Correspondence to Saihu Liao.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Cyrille Boyer, Douglas Henrique Pereira, and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ma, Q., Song, J., Zhang, X. et al. Metal-free atom transfer radical polymerization with ppm catalyst loading under sunlight. Nat Commun 12, 429 (2021).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing