Abstract
The absence of mirror symmetry, or chirality, is behind striking natural phenomena found in systems as diverse as DNA and crystalline solids. A remarkable example occurs when chiral semimetals with topologically protected band degeneracies are illuminated with circularly polarized light. Under the right conditions, the part of the generated photocurrent that switches sign upon reversal of the light’s polarization, known as the circular photogalvanic effect, is predicted to depend only on fundamental constants. The conditions to observe quantization are nonuniversal, and depend on material parameters and the incident frequency. In this work, we perform terahertz emission spectroscopy with tunable photon energy from 0.2 –1.1 eV in the chiral topological semimetal CoSi. We identify a large longitudinal photocurrent peaked at 0.4 eV reaching ~550 μ A/V^{2}, which is much larger than the photocurrent in any chiral crystal reported in the literature. Using firstprinciples calculations we establish that the peak originates only from topological band crossings, reaching 3.3 ± 0.3 in units of the quantization constant. Our calculations indicate that the quantized circular photogalvanic effect is within reach in CoSi upon doping and increase of the hotcarrier lifetime. The large photoconductivity suggests that topological semimetals could potentially be used as novel midinfrared detectors.
Introduction
Circular photogalvanic effect (CPGE) exists only in gyrotropic crystals^{1,2}. Its transverse component, where the current flows perpendicular to light propagation direction, is by far the most commonly observed. It has been recently measured in transition metal dichalcogenides^{3}, topological insulators^{4,5,6} and Weyl semimetals^{7,8,9}. In contrast, the longitudinal CPGE, where current flows parallel to light propagation direction, remains more elusive since its discovery in tellurium in 1979^{10}.
In chiral topological semimetals, the longitudinal CPGE is particularly remarkable because it was recently predicted to be quantized^{11,12,13,14}. These materials feature protected nodal crossings near the Fermi level, and because all mirror symmetries are broken, nodes with opposite chirality generically appear at different energies^{15} (see Fig. 1a, b), in contrast to mirrorsymmetric Weyl metals, like TaAs with nodes at the same energy^{16,17}. The existence of these nodes is protected by an integer topological charge C, which quantizes the longitudinal CPGE trace to Cβ_{0} where β_{0} = πe^{3}/h^{2}^{11}. Chiral Weyl metals, where C = ±1 (Fig. 1a)^{15}, are elusive. Nevertheless, separated topological nodes with degeneracies larger than two, known as multifold fermions, are demonstrated to exist in chiral crystals such as CoSi, RhSi and AlPt (with C = ±4)^{12,18,19,20,21,22,23} (Fig. 1b). Furthermore, the presence of cubic symmetry in these materials makes transverse CPGE vanishing and longitudinal CPGE isotropic with only one nonzero independent term, β_{xx}, so that averaging over the three directions is not needed to measure the tensor trace β (β = 3β_{xx}).
Several challenges remain to observe the quantized CPGE in chiral semimetals. In this family of materials, the presence of spinorbit coupling leads to a splitting of the nodes, which can still display quantization but in a reduced frequency range determined by the strength of the spinorbit coupling, for example as happens in RhSi^{12,13,14,24,25}. Interband excitations between the spinorbit split bands contribute to the nonquantized CPGE, a nonnegligible effect in RhSi^{14}. Therefore a small spinorbit splitting is advantageous to observe the quantized CPGE in multifold materials^{11,13}. In this work, we measure the CPGE in CoSi as its spinorbit coupling is much smaller than in RhSi^{12,19}.
We measure the CPGE by detecting radiated terahertz (THz) pulses emitted from the illuminated regions, a method with several advantages compared to DC current measurements ^{8,9,24,25,26,27}. Firstly, detecting CPGE in a contactless way avoids contact misalignment as we measure second harmonic generation to align the crystal axis. Secondly, the emitted THz pulse originates from a local illuminated region, and therefore thermal current and the nonlocal diffusion of photoexcited carriers to the contacts, typical of a DC current measurement, are not concerns^{28}. Thirdly, in the process of THz emission, photocarriers move at the band velocity and then recombine, which creates a timedependent photocurrent within the penetration depth. This timedependent current radiates a THz pulse into free space, which in the far field is related to the first timederivative of the surface current and is directly related with the quantized CPGE as the quantized quantity is the rate of the inject current, dj/dt = iCβ_{0}, instead of the current j itself^{29}. Note that optical rectification is generally at least two orders of magnitude smaller than the photocurrent in the resonant regime^{27,30}. Therefore, we neglect the optical rectification effect in CoSi.
In this work, we have developed the capability to measure THz emission in the midinfrared regime (0.20–0.48 eV) for the first time. We use it to measure CPGE in CoSi across a broad range of 0.2–1.1 eV. We identify a large longitudinal CPGE peaked at 0.4 eV reaching ~ 550 μ A/V^{2}. Comparing our measurements to firstprinciples calculations, we establish that the peak originates from topological band crossings, reaching 3.3 ± 0.3 in units of the quantization constant under the assumption of a constant hotcarrier lifetime. We develop a k ⋅ p model, including quadratic corrections to the dispersion of the nodal bands, and show that the location of the chemical potential can conspire to create a more complex frequency profile than it has been anticipated even in the spinless model. Our calculations also lay out the conditions to observe the quantized CPGE in CoSi in future experiments.
Results
Sample and second harmonic generation
The chiral crystal structure of CoSi seen from the (111) direction is depicted in Fig. 1c. As a first step, we pick up large homogeneous (111) natural facets by scanning secondharmonic generation (SHG) measurement^{31}. To stimulate SHG, we focused light pulses centered at 800 nm under nearnormal incidence to a 10μm diameter spot on the sample and the second harmonic signal centered at 400 nm is measured. As shown in Fig. 1d, polar patterns of SHG are found as a function of the direction of the linear polarization of the incident light in the corotating parallelpolarizer (orange) and crossedpolarizer (blue) configurations. These patterns agree well with a fit with only one nonzero parameter based on the point group symmetry (see “Methods” section).
Longitudinal CPGE in CoSi
Figure 2a shows schematically the measurement of the longitudinal CPGE. When circularly polarized light is incident on the sample, a current flows along the light propagation direction inside of the material. Under normal incidence, the current flows perpendicular to the surface, which prevents THz emission into free space from CPGE in the bulk^{24,29}. THz emission does originate from the surface current density under oblique incidence^{29}. See Supplementary Note 1 for more details. Therefore, in order to emit THz radiation into free space, we utilize offnormal incidence at 45 degrees as shown in Fig. 2a. An achromatic quarterwave plate is used to control the polarization of the incident light. Terahertz wave components in xz and y direction are detected by using a THz polarizer before the ZnTe detector. Figure 2b, e shows the reversal of the polarity of the time trace of emitted THz electric field under left and right circularlypolarized light at the incident photon energy of 0.50 eV, which indicates the change of the direction of the photocurrent under opposite helicity of circularly polarized incident light (i.e., the CPGE).
To confirm that the CPGE we observe is a longitudinal photocurrent, we studied the polarization dependence of the CPGE by rotating both the achromatic quarterwaveplate and the samples. The experimental geometry is shown in Fig. 2a, and we detect the emitted THz components in the incident plane, E_{xz}(t), and perpendicular to the plane, E_{y}(t). In Fig. 2b (orange) we show the peak value of the emitted THz field E_{y}(t) at the incident photon energy of 0.50 eV as a function of the angle of the quarterwave plate. The THz field under left and right circularly polarized light has the same direction and magnitude, which indicates no CPGE. The almost identical time traces of E_{y}(t) with opposite circular polarizations are shown in Fig. 2c. The CPGE component (E_{↺}(t) − E_{↻}(t))/2 is zero within the detection sensitivity, as shown in Fig. 2d. (E_{↺}(t) + E_{↻}(t))/2 is the linear photogalvanic effect (LPGE) component under circularlypolarized light (see Supplementary Note 1B for details).
In contrast, the inplane THz field E_{xz}(t) shows completely different polarization dependence as shown in Fig. 2b (blue). When the helicity of the circularly polarized light is reversed, the direction of the peak THz field in E_{xz}(t) changes, and the waveform is shown in Fig. 2e. They are not simply the same curve with opposite signs because of a sizable LPGE contribution. Nevertheless, (E_{↺} − E_{↻})/2 is not zero in E_{xz}(t) and relatively large compared to (E_{↺} + E_{↻})/2, as shown in Fig. 2f. The observation of a nonzero CPGE only in the incident xz plane is consistent with the longitudinal CPGE, where the current flows along the wave vector direction inside CoSi. This longitudinal CPGE is unchanged as we rotate the sample due to the cubic symmetry constraints, as shown for 0.50 eV incident photon energy in Fig. 2g. We also observed similar angle dependence at other photon energies. See Supplementary Note 2 for more details.
To quantify the longitudinal CPGE, we performed a symmetry analysis by fitting the angle dependence of the quarterwave plate on E_{xz} and E_{y}. The solid lines in Fig. 2b are the best fit to the functions determined by the crystal symmetry, \({E}_{y}(\theta )={B}_{1}\sin (4\theta )+{C}_{1}\cos (4\theta )+{D}_{1}\) and \({E}_{xz}(\theta )=A\sin (2\theta )+{B}_{2}\sin (4\theta )+{C}_{2}\cos (4\theta )+{D}_{2}\), where the coefficients A, B_{1}, B_{2}, C_{1}, C_{2}, D_{1}, D_{2} are determined by the CPGE and LPGE conductivity (see Supplementary Note 1B for details). Both curves are fitted simultaneously with the same fit weights. The \(\sin (2\theta )\) term describes the CPGE while \(\sin (4\theta )\), \(\cos (4\theta )\) and the constant terms describe the LPGE. The symmetry analysis shows that the outofplane component E_{y} does not contribute to the CPGE, while the inplane component E_{xz} dominates the CPGE.
CPGE spectrum in CoSi
After confirming the longitudinal direction of the CPGE, we now study the amplitude of the CPGE current inside the sample at different incident photon energies. We use circularlypolarized laser pulses with a duration 50–100 fs and a tunable incident photon energy from 0.2 eV to 1.1 eV to generate a CPGE inside of the sample. For the first time, we detected THz emission with incident photon energy below 0.5 eV, comparing with previous measurements^{8,9,24,26,27}. In order to convert the detected THz electric field into the CPGE current inside the sample, we measured a benchmarking ZnTe sample at the same position at each wavelength immediately after measuring CoSi. ZnTe is useful as a benchmark due to its relatively flat frequency dependence on the electricoptical sampling coefficient for photon energy below the gap^{32}. See Supplementary Note 1F and Supplementary Fig. 3 for the raw data. We first convert the collected THz electric fields on CoSi and ZnTe from the time domain to the frequency domain by a Fourier transformation. By taking the ratio of the two Fourier transforms of the electric fields and considering the Fresnel coefficient, refractive indices and penetration depth, we obtain the ratio between the CPGE response of CoSi and the optical rectification of ZnTe. The use of ZnTe circumvents assumptions regarding the incident pulse length, the wavelength dependent focus spot size on the sample, and the calculation of collection efficiency of the offaxis parabolic mirrors (see Supplementary Note 1C for details).
The CPGE follows \(j(\Omega )=\frac{{\beta }_{xx}}{i\Omega +1/\tau }{E}_{0}^{2}(\Omega )\), where Ω is the THz frequency and τ is the hotcarrier lifetime. When the hotcarrier lifetime satisfies τ ≪ 1/Ω, \(j\approx {\beta }_{xx}\tau {E}_{0}^{2}\). This is the case for the current experiment as j(Ω) depends weakly on Ω. (See Supplementary Fig. 6.) The secondorder photoconductivity plotted in Fig. 3a was an average value of the CPGE over the frequency range of 0.5–2.0 THz in Supplementary Fig. 6, which should also be the DC limit. When τ is much longer than the pulse width, which is in the quantization regime, \({\rm{d}}j/{\rm{d}}t={\beta }_{xx}{E}_{0}^{2}\). When 1/τ is comparable to Ω, the CPGE conductivity, \(\frac{{\beta }_{xx}}{i\Omega +1/\tau }\), will have strong frequency dependence in the THz regime, which will enable the extraction of β_{xx} and τ separately. Anticipating our theory analysis, we note that the CPGE spectrum is determined by the only symmetryindependent nonzero CPGE response tensor β_{xx}, which is a photocurrent rate multiplied by the hotcarrier lifetime τ. The measured CPGE photocurrent per incident field squared as a function of frequency, which we will denote as the CPGE spectrum, is shown in Fig. 3a for room temperature, showing a peak value of ~550 μ A/V^{2} at 0.4 eV. The CPGE spectrum peak value is much larger than the photogalvanic effect in any chiral crystals reported in the literature^{33}, BaTiO_{3}^{34}, singlelayer monochalcogenides^{34,35}, the colossal bulkphotovoltaic response in TaAs^{36} and RhSi in the same space group^{24,25}.
Firstprinciple calculation
Next, we address the relationship between the large photoconductivity peak and the multifold fermions near the Fermi level shown in Fig. 3b. In Fig. 3a, we show our abinitio calculations of the CPGE for CoSi with and without spinorbit coupling (SOC) at room temperature and at a chemical potential E_{f} crossing the flat hole band, as indicated by the dashed line in Fig. 3b (see “Methods” section and Supplementary Note 4). They quantitatively reproduce the experimental data across a wide frequency range. The SOC splitting, ≈20 meV at the Γ point node, determines the finer structure in the optical response^{37}.
To match the firstprinciples calculations with the CPGE spectrum, we considered β_{xx}, which is related to the CPGE trace by β = 3β_{xx} due to cubic symmetry^{11,12}. Note that β_{xx} is directly calculated from the band structure at certain chemical potential. It is plotted in Fig. 3a times τ, the only free parameter, which was determined by matching the calculated peak width and magnitude to the CPGE data. This selfconsistent constraint is satisfied with a broadening ℏ/τ ≈ 38 meV at 300 K. As shown from the right y axis of Fig. 3a, the CPGE trace β reaches 3.3 (±0.3) in units of the quantization constant β_{0}.
For frequencies below 0.6 eV, all the interband excitations on CoSi occur in the vicinity of its multifold bands at the nodes Γ and R^{37}. We conclude this from the optical conductivity on CoSi at 300 K that is shown in Fig. 3c. With the subtraction of the Drude response and the four phonon peaks, the interband contribution has a kink at ~0.2 eV that separates two quasilinear regimes. The details of the theoretical and experimental studies could be found in ref. ^{37}. Below 0.2 eV, the interband excitations involve the threefold fermion at the Γ point, while the excitations near the double Weyl fermion at R become active only above 0.2 eV^{37}. The main contribution to the peak around 0.6 eV comes from the saddle point M^{37}. In addition to the optical conductivity, our momentum resolved calculation (Fig. 3d) for the CPGE peak at 0.4 eV reveals that it originates from these multifold fermions only, which contribute with opposite signs to the CPGE current. Therefore, this giant CPGE peak has a purely topological origin, although it is not quantized due to the sum of contributions of two kinds of multifold fermions and the quadratic contributions to the energy bands.
The position of the chemical potential is crucial to relate the CPGE to quantization. Our abinitio calculations, supported by our lowenergy analysis below, reveal that the CPGE shows a dippeak structure as the one of Fig. 4a, b) when E_{f} is below the Γ node (E_{f} < 0) in our sample. Such Fermi energy is consistent with recent quasiparticle interference^{38} and linear optical conductivity experiments^{37}. Note that this dippeak structure was clearly observed recently in RhSi as the energy splitting between the nodes at the Γ and R in RhSi is around twice larger than CoSi so that the sign change in CPGE is pushed to around 0.4 eV in RhSi^{25}. The dippeak structure for E_{f} < 0 is also produced by using a fourband tight binding model for CoSi^{13} (see Supplementary Note 5). As shown in Fig. 4a, the dip reaches the quantized value of 4β_{0} at low temperatures in the clean limit, and remains quantized for hot carrier lifetime broadening up to 5 meV at 100 meV photon energy (see Supplementary Note 4 and Supplementary Fig. 7 for details.). The quantization of the dip is determined by the threefold fermion at the Γ point as the vertical excitations at the R point are Pauli blocked below 0.2 eV^{37}. Therefore, the CPGE will not be quantized in the current sample at low temperature in the photon energy range of 0.2–1.1 eV as the peak around 0.4 eV after the dip appears nonuniversal in general due to contributions from both nodes at Γ and R (see see E_{f} = −37 meV curve in Fig. 4a). However, if E_{f} is decreased further to lie close to the R point, this peak can reach 4β_{0} at room temperature even with a broadening of 38 meV (see E_{f }= −67 meV curve in Fig. 4b). As discussed below, this peak originates from the double Weyl fermion at the R point, and it is enabled by an accidental window of vanishing CPGE contribution from the Γ point. Finally, we note that electronelectron interactions can also correct the quantized value, as occurs for chiral Weyl semimetals^{39}. While it is currently unknown how relevant these corrections are for multifold fermions, the large hole and electron pockets at Γ and R in CoSi suggest that screening should be strong and therefore interactions should have a small effect. The good agreement of our model calculations with the data, shown in Fig. 3a, is also consistent with this point of view. Experimentally, from the optical conductivity measurements we estimate a relative dielectric constant ϵ_{1} of the order of −2500 at 300 K and −10,000 at 10 K, further supporting a normal metallic behavior with very large screening of interactions. Also, specific heat measurements on CoSi also showed that it is a weakly correlated semimetal, as evidenced by a normal metallic Sommerfeld constant^{40}. Because of these reasons interactions are neglected in this work.
k ⋅ p model
To understand the origin of the dippeak structure, it is necessary to describe the curvature of the middle band. To this end we derived a lowenergy k ⋅ p type model keeping symmetryallowed terms up to quadratic order in momentum k. The resulting Hamiltonian reads
where S is the vector of spin1 matrices, and k = ∣k∣. We fixed its coefficients v, b, c, and \({c}_{1}=\frac{1}{3}(3a+2c)\) with a fit to the band structure shown in Fig. 3b around the Γ point. The second term includes three out of the four symmetryallowed quadratic terms because the fourth has a negligible effect on the CPGE (see Supplementary Note 6 for details). The energies expanded to second order in momentum for the three bands are plotted as colored lines in Fig. 3b. The coefficients b and c determine the curvature in the Γ−X and Γ−R directions, respectively. For the R point bands, we use a spindegenerate double Weyl model that has a step increase in the CPGE current by 4β_{0} when excitations at R are allowed in Fig. 4d^{12}.
The possible optical transitions in the band structure near the Γ point are illustrated in Fig. 3b. We label the bands with increasing energies as 1, 2, 3. For E_{f} above the threefold node, the only possible transition is from bands 2 to 3. As the frequency increases, this transition becomes active and yields a monotonically increasing joint density of states (JDOS)^{13}. As shown in Fig. 4c, for E_{f} below the node, however, two types of transitions contribute: 1 to 2 and 2 to 3. The first transition from band 1 to band 2 (open purple circles) is active for a small range of energies, and then decays to zero. The second transition from band 2 to band 3 (open gold squares) only starts picking up at larger frequencies, leaving a dip in the JDOS and, therefore, a dip in the CPGE (solid blue line). The different frequencies where the transitions become active or inactive are labeled in Figs. 3b, 4c, d. Figure. 4d show that when we add the contributions from the threefold fermions at Γ and double Weyl fermion at R, the existence of the dip from the threefold fermions leads to the dippeak structure observed in the abinitio calculations, only when E_{f} is below the threefold node. In the k ⋅ p model, we also show that while the dip is universally quantized, the peak is not because of the incomplete transitions from Γ. Note that the quantization of the peak not only depends on the Γ contribution but it also may be altered by the quadratic dispersion of the double Weyl fermion when it fully contributes to CPGE. However, as shown in Fig. 4b, decreasing E_{f} further could be used to diminish the contribution from the threefold fermions at around 0.4 eV and reveal the quantization due to the R point (see Supplementary Note 4 for details).
Discussion
By studying the CPGE in the chiral topological semimetal CoSi we found a large longitudinal photoconductivity in the midinfrared regime, which has a purely topological origin linked to the existence of multifold fermions in this material. CoSi could potentially be used as a new midinfrared detector based on a topological mechanism if the hotcarrier lifetime could be increased to around 1 ps, as observed in other semimetals^{41}. Moreover, our theory suggests that a quantized CPGE is within reach in CoSi by several means. With the chemical potential below the threefold node, the very narrow quantized plateau around 100 meV corresponding to the Γ node could be accessible at low temperatures if the hotcarrier lifetime increases by one order of magnitude. Also, electron doping the E_{f} above the threefold node will result in a wider quantized plateau over 100–350 meV from the Γ node corresponding to the dip we calculate at low temperatures also if the hotcarrier lifetime increases by one order of magnitude. A quantized plateau around 0.4 eV corresponding to the R node can be revealed at T = 300 K by holedoping, even with a similar short hot carrier lifetime as that of our current sample. We expect that these possibilities, opened by our work, motivate further effort on crystal growth with longer hot carrier lifetime and different doping, as well as timeresolved measurements in the midinfrared regime to probe the hot carrier dynamics. The methods developed in our work could also be applied to other chiral topological semimetals^{18,42} to realize the quantized CPGE.
Methods
Crystal growth
High quality CoSi single crystals were prepared by a high temperature flux method with tellurium as flux. Cobalt pieces (Alfa Aesar 99.98%), silicon pieces (Alfa Aesar 99.999%), and tellurium lumps (Alfa Aesar 99.99%) with the molar ratio of 1:1:15–20 were set in an alumina crucible and then sealed in a fused silica ampule in around 0.8 atm argon environment. The ampule was heated to 1100 ^{∘}C with a speed of about 150 ^{∘}C/h. After soaking at 1100 ^{∘}C for 10 h, the ampule was cooled down to 700 ^{∘}C at the rate of 2 ^{∘}C/h, and the excess flux was centrifuged out at that temperature to get several single crystals with large (111) facet^{43}. Crystals larger than 2 × 2 mm were picked for THz emission experiments. We also performed a spatial SHG scanning of the sample and found an homogeneous signal.
Second harmonic generation fit
For CoSi (111), the fits are:
\({\chi }_{xyz}^{(2)}\) is the only nonzero SHG tensor element in CoSi. θ is the angle between the incident polarization and the [1, 1, −2] axis.
Terehertz emission spectroscopy
A laser beam from a Ti:sapphire amplifier (center photon energy 1.55 eV, repetition rate 1 kHz, duration ~35 fs) was split by a beam splitter into pump and probe beams. On the pump side, an optical parametric amplifier is used to convert the photon energy to 0.47–1.1 eV (pulse duration 40–70 fs), and a different frequency generation is used to further convert photon energy to 0.20–0.48 eV (pulse duration 70–110 fs). The laser beams were then focused by a 40cm BaF_{2} lens or a 40cm germanium lens onto the sample with a diameter of 1 mm under 45 degree angle of incidence. A typical pump power of 15 μJ per pulse was used, which falls into the linear response range. The emitted THz wave was collected by an offaxis parabolic mirror (OAP) and focused by another OAP onto an electrooptic (EO) crystal, ZnTe (110). The probe beam was copropagating with the THz wave into the EO crystal to detect the THz electric field using EOsampling method^{29}. All of the measurement were performed in a dryair environment with relative humidity less than 3% to avoid water absorption. To control the polarization of pump pulses, a quartzMgF_{2} achromatic quarterwave plate (600–2700 nm, retardance error ≤ λ/500) and a MgF_{2} achromatic quarterwave plate (2500–7000 nm, retardance error ≤ λ/100) were used. A THz wiregrid polarizer was used to extract outofplane (E_{y}) and inplane (E_{xz}) components of THz electric field. A benchmarking crystal ZnTe (110) was used as a standard candle to extract the photogalvanic response from CoSi. Both crystals were mounted on a computercontrolled motor to reliably change the position. For each incident photon energy, measurement of CoSi was immediately followed by ZnTe to avoid longterm fluctuation of laser power. By comparing the THz electric field of CoSi and ZnTe in frequency domain, the photogalvanic response of the CoSi crystal could be obtained (see Supplementary Note 1 for details).
First principle calculation
To calculate the CPGE current, we obtain the densityfunctional theory (DFT) Bloch wave functions from the FullPotential LocalOrbital program (FPLO)^{44} within the generalized gradient approximation (GGA)^{45}. By projecting the Bloch wave functions onto Wannier functions, we obtain a tightbinding Hamiltonian with 104 bands from 3d, 4s, 4p orbitals of Co and 3s, 3p, orbitals of Si, which we use for efficient evaluation of the CPGE photocurrent.
To implement the CPGE integrals in Eq. (4), the Brillouin zone was sampled by kgrids from 200 × 200 × 200 to 960 × 960 × 960^{46}. Satisfactory convergence (less than 2% change) was achieved for a kgrid of size 400 × 400 × 400. The temperature dependence is implemented by the FermiDirac distribution function and we also include a hotcarrier lifetime broadening factor (see Supplementary Note 4 for details). CoSi is in space group P2_{1}3 (#198), with point group 23 (T). Owing to the twofold glide rotation symmetry s_{2x}, s_{2y}, s_{2z}, only diagonal tensor elements are nonzero, and the C_{3} rotation symmetry further leads to a single independent component β_{xx} = β_{yy} = β_{zz}. We carefully checked the symmetry of numerically calculated tensor elements with the tensor shape given by lattice symmetry and found the errors to be within 10^{−6}. The full circular photogalvanic effect tensor is given by
where E_{mn} ≡ E_{m} − E_{n}, f_{mn} ≡ f_{m} − f_{n} are the difference of band dispersion and Fermi–Dirac distribution, respectively, \({\Delta }_{mn}^{a}\equiv {\partial }_{{k}_{a}}{E}_{mn}/\hslash\), \({r}_{mn}^{a}\equiv i\langle m {\partial }_{{k}_{a}}n\rangle\) is the interband transition matrix element or offdiagonal Berry connection. The finite relaxation time τ is considered via the Lorentzian function \({{\mathcal{L}}}_{\tau }({E}_{nm}\omega )\).
Data availability
All data needed to evaluate the conclusions in the paper are present in the paper and the Supplementary Information. Additional data related to this paper could be requested from the authors.
References
Sturman, B. I. & Fridkin, V. M. Photovoltaic and PhotoRefractive Effects in Noncentrosymmetric Materials, Vol. 8 (CRC Press, 1992).
Ganichev, S. D. & Prettl, W. Spin photocurrents in quantum wells. J. Phys. Condens. Matter 15, R935 (2003).
Yuan, H. et al. Generation and electric control of spin–valleycoupled circular photogalvanic current in WSe_{2}. Nat. Nanotechnol. 9, 851 (2014).
McIver, J., Hsieh, D., Steinberg, H., JarilloHerrero, P. & Gedik, N. Control over topological insulator photocurrents with light polarization. Nat. Nanotechnol. 7, 96 (2012).
Olbrich, P. et al. Roomtemperature highfrequency transport of Dirac fermions in epitaxially grown Sb_{2}Te_{3} and Bi_{2}Te_{3}based topological insulators. Phys. Rev. Lett. 113, 096601 (2014).
Okada, K. N. et al. Enhanced photogalvanic current in topological insulators via Fermi energy tuning. Phys. Rev. B 93, 081403 (2016).
Ma, Q. et al. Direct optical detection of Weyl fermion chirality in a topological semimetal. Nat. Phys. 13, 842 (2017).
Sirica, N. et al. Tracking ultrafast photocurrents in the Weyl semimetal TaAs using THz emission spectroscopy. Phys. Rev. Lett. 122, 197401 (2019).
Gao, Y. et al. Chiral terahertz wave emission from the Weyl semimetal TaAs. Nat. Commun. 11, 1–10 (2020).
Asnin, V. et al. “Circular” photogalvanic effect in optically active crystals. Solid State Commun. 30, 565–570 (1979).
de Juan, F., Grushin, A. G., Morimoto, T. & Moore, J. E. Quantized circular photogalvanic effect in Weyl semimetals. Nat. Commun. 8, 15995 (2017).
Chang, G. et al. Unconventional chiral fermions and large topological Fermi arcs in RhSi. Phys. Rev. Lett. 119, 206401 (2017).
Flicker, F. et al. Chiral optical response of multifold fermions. Phys. Rev. B 98, 155145 (2018).
de Juan, F. et al. Difference frequency generation in topological semimetals. Phys. Rev. Res. 2, 012017 (2020).
Huang, S.M. et al. New type of Weyl semimetal with quadratic double Weyl fermions. Proc. Natl Acad. Sci. USA 113, 1180–1185 (2016).
Weng, H., Fang, C., Fang, Z., Bernevig, B. A. & Dai, X. Weyl semimetal phase in noncentrosymmetric transitionmetal monophosphides. Phys. Rev. X 5, 011029 (2015).
Huang, S.M. et al. A Weyl Fermion semimetal with surface Fermi arcs in the transition metal monopnictide TaAs class. Nat. Commun. 6, 1–6 (2015).
Bradlyn, B. et al. Beyond Dirac and Weyl fermions: unconventional quasiparticles in conventional crystals. Science 353, aaf5037 (2016).
Tang, P., Zhou, Q. & Zhang, S.C. Multiple types of topological fermions in transition metal silicides. Phys. Rev. Lett. 119, 206402 (2017).
Rao, Z. et al. Observation of unconventional chiral fermions with long Fermi arcs in CoSi. Nature 567, 496 (2019).
Sanchez, D. S. et al. Topological chiral crystals with helicoidarc quantum states. Nature 567, 500 (2019).
Takane, D. et al. Observation of chiral fermions with a large topological charge and associated Fermiarc surface states in CoSi. Phys. Rev. Lett. 122, 076402 (2019).
Schröter, N. B. et al. Chiral topological semimetal with multifold band crossings and long Fermi arcs. Nat. Phys. 15, 759–765 (2019).
Rees, D. et al. Helicitydependent photocurrents in the chiral Weyl semimetal RhSi. Sci. Adv. 6, eaba0509 (2020).
Ni, Z. et al. Linear and nonlinear optical responses in the chiral multifold semimetal RhSi. npj Quantum Mater. https://doi.org/10.1038/s4153502000298y (2020). In press.
Braun, L. et al. Ultrafast photocurrents at the surface of the threedimensional topological insulator Bi_{2}Se_{3}. Nat. Commun. 7, 13259 (2016).
Sotome, M. et al. Spectral dynamics of shift current in ferroelectric semiconductor sbsi. Proc. Natl Acad. Sci. USA 116, 1929–1933 (2019).
Song, J. C. & Levitov, L. S. ShockleyRamo theorem and longrange photocurrent response in gapless materials. Phys. Rev. B 90, 075415 (2014).
Shan, J. & Heinz, T. F. Terahertz radiation from semiconductors. In Ultrafast Dynamical Processes in Semiconductors. 1–56 (Springer, 2004).
Nastos, F. & Sipe, J. Optical rectification and shift currents in GaAs and GaP response: Below and above the band gap. Phys. Rev. B 74, 035201 (2006).
Wu, L. et al. Giant anisotropic nonlinear optical response in transition metal monopnictide Weyl semimetals. Nat. Phys. 13, 350 (2017).
HernándezCabrera, A., Tejedor, C. & Meseguer, F. Linear electrooptic effects in zinc blende semiconductors. J. Appl. Phys. 58, 4666–4669 (1985).
Zhang, Y., de Juan, F., Grushin, A. G., Felser, C. & Sun, Y. Strong bulk photovoltaic effect in chiral crystals in the visible spectrum. Phys. Rev. B 100, 245206 (2019).
Fei, R., Tan, L. Z. & Rappe, A. M. Shiftcurrent bulk photovoltaic effect influenced by quasiparticle and exciton. Phys. Rev. B 101, 045104 (2020).
Rangel, T. et al. Large bulk photovoltaic effect and spontaneous polarization of singlelayer monochalcogenides. Phys. Rev. Lett. 119, 067402 (2017).
Osterhoudt, G. B. et al. Colossal midinfrared bulk photovoltaic effect in a typeI Weyl semimetal. Nat. Mater. 18, 471 (2019).
Xu, B. et al. Optical signatures of multifold fermions in the chiral topological semimetal CoSi. Proc. Natl Acad. Sci. USA 117, 27104–27110 (2020).
Yuan, Q.Q. et al. Quasiparticle interference evidence of the topological Fermi arc states in chiral fermionic semimetal CoSi. Sci. Adv. 5, eaaw9485 (2019).
Avdoshkin, A., Kozii, V. & Moore, J. E. Interactions remove the quantization of the chiral photocurrent at Weyl points. Phys. Rev. Lett. 124, 196603 (2020).
Petrova, A. E. et al. Elastic, thermodynamic, and electronic properties of MnSi, FeSi, and CoSi. Phys. Rev. B 82, 155124 (2010).
Zhu, C. et al. Broadband hotcarrier dynamics in threedimensional Dirac semimetal Cd_{3}As_{2}. Appl. Phys. Lett. 111, 091101 (2017).
Chang, G. et al. Topological quantum properties of chiral crystals. Nat. Mater. 17, 978 (2018).
Xu, X. et al. Crystal growth and quantum oscillations in the topological chiral semimetal CoSi. Phys. Rev. B 100, 045104 (2019).
Koepernik, K. & Eschrig, H. Fullpotential nonorthogonal localorbital minimumbasis bandstructure scheme. Phys. Rev. B 59, 1743 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Zhang, Y. et al. photogalvanic effect in Weyl semimetals from first principles. Phys. Rev. B 97, 241118(R) (2018).
Acknowledgements
We thank C. L. Kane for helpful discussions and N. P. Armitage and J. Stensberg for proofreading the manuscript. Z.N. and L.W. are supported by the ARO YIP award under the Grant W911NF1910342. X.H. is partially supported by the ARO MURI under the Grant W911NF2020166. The acquisition of the oscillator laser for the SHG experiment is supported by NSF through the University of Pennsylvania Materials Research Science and Engineering Center (MRSEC) (DMR1720530). E.J.M’s theoretical work is supported by the DOE under grant DE FG02 84ER45118. Research at the University of Maryland was supported by the Gordon and Betty Moore Foundation’s EPiQS Initiative through Grant No. GBMF9071, and the Maryland Quantum Materials Center. Y.Z. is currently supported by the DOE Office of Basic Energy Sciences under Award desc0018945 to Liang Fu. F.J. acknowledges funding from the Spanish MCI/AEI through grant No. PGC2018101988BC21. O.P. is supported by an FPU predoctoral contract from MECD No. FPU16/05460 and the Spanish grant PGC2018099199BI00 from MCIU/AEI/FEDER. B.X. is supported by the Schweizerische Nationalfonds (SNF) by Grant No. 200020172611. A.G.G. is supported by the ANR under the grant ANR18CE30000101 (TOPODRIVE) and the European Union Horizon 2020 research and innovation programme under grant agreement No. 829044 (SCHINES). Y.Z., K.M., and C.F. acknowledge the financial support from the European Research Council (ERC) Advanced Grant No. 742068 "TOPMAT”; Deutsche Forschungsgemeinschaft (DFG) through SFB 1143, and the WürzburgDresden Cluster of Excellence on Complexity and Topology in Quantum Matterct.qmat (EXC 2147, Project No. 390858490). The DFT calculations are carried on Draco cluster of MPCDF, Max Planck society.
Author information
Authors and Affiliations
Contributions
L.W. conceived the project and coordinated the experiments and theory. Z.N., X.H., and L.W. built the THz emission setup. Z.N. performed the THz emission experiments under the supervision of L.W.. Z.N., and L.W. analyzed the data. Z.N., L.W., and E.J.M. performed the symmetry analysis. B.X. performed the optical conductivity measurement. Y.Z. performed DFT calculation. O.P. and F.J. performed the k ⋅ p calculation. A.G.G. performed the tightbinding calculation. K.W., K.M., J.P., and C.F. grew the crystals. L.W., F.J., and A.G.G. wrote the manuscript from contributions of all authors. E.J.M. edited the manuscript. L.W., Z.N., O.P., A.G.G., F.J., and Y. Z. wrote the supplementary information. Z.N., K.W., and Y.Z. contributed equally to this work.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ni, Z., Wang, K., Zhang, Y. et al. Giant topological longitudinal circular photogalvanic effect in the chiral multifold semimetal CoSi. Nat Commun 12, 154 (2021). https://doi.org/10.1038/s41467020204085
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467020204085
This article is cited by

Photocurrent as a multiphysics diagnostic of quantum materials
Nature Reviews Physics (2023)

Ultrafast helicitydependent photocurrents in Weyl Magnet Mn3Sn
Communications Physics (2023)

Causal structure of interacting Weyl fermions in condensed matter systems
Nature Communications (2023)

Ultrafast terahertz emission from emerging symmetrybroken materials
Light: Science & Applications (2023)

Magnetic bulk photovoltaic effect as a probe of magnetic structures of $\mathrm{{EuSn_{2}As_{2}}}$
Quantum Frontiers (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.