Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Probing the ionic defect landscape in halide perovskite solar cells


Point defects in metal halide perovskites play a critical role in determining their properties and optoelectronic performance; however, many open questions remain unanswered. In this work, we apply impedance spectroscopy and deep-level transient spectroscopy to characterize the ionic defect landscape in methylammonium lead triiodide (MAPbI3) perovskites in which defects were purposely introduced by fractionally changing the precursor stoichiometry. Our results highlight the profound influence of defects on the electronic landscape, exemplified by their impact on the device built-in potential, and consequently, the open-circuit voltage. Even low ion densities can have an impact on the electronic landscape when both cations and anions are considered as mobile. Moreover, we find that all measured ionic defects fulfil the Meyer–Neldel rule with a characteristic energy connected to the underlying ion hopping process. These findings support a general categorization of defects in halide perovskite compounds.


Triggered by the first demonstration of a perovskite solar cell in 20091, significant research efforts have been devoted to the field of perovskite photovoltaics leading to a record power conversion efficiency of 25.5%2. This remarkable performance is made possible by a combination of advantageous properties of perovskite materials, among which most noteworthy are their low exciton binding energies, high absorption coefficients, high charge carrier diffusion lengths and correspondingly long lifetimes of free charge carriers3,4,5,6. Additionally, significant progress has been made over the last decade in the development of novel fabrication methods and device architectures as well as optimization by interfacial engineering7,8,9,10,11.

Despite these advancements, several aspects of perovskite solar cells remain a challenge. For example, in many different fabrication approaches, mobile ions have proven to be a major limitation12,13,14,15,16. Mobile ions or ionic defects were shown to be the source of current density-voltage hysteresis and were linked to a reduced stability of devices12,14,17,18,19,20. Moreover, ionic defects that form states within the bandgap which act as recombination centers, can reduce the photovoltaic performance of the device21,22. Despite their importance, characterization of ionic defects and their properties in perovskite materials is incomplete. According to calculations and experimental reports, the most likely native point defects in methylammonium lead triiodide (MAPbI3) perovskites are charged vacancies, such as \({V}_{{\rm{I}}}^{+}\) and \({V}_{{\rm{MA}}}^{-}\) and interstitials such as \({{{I}}}_{{\mathrm{i}}}^{-}\) and \({{\rm{MA}}}_{{\rm{i}}}^{+}\)23,24,25,26. Experimentally, ionic defects and their migration have been observed by a range of methods27,28,29.

Noteworthy is the work by Futscher et al.30, who employed transient capacitance measurements on MAPbI3 solar cells to reveal both a fast (t < ms) and relatively slow (t ~ s) species, which varied by several orders of magnitude in both their concentration and diffusion coefficient. While in all their measurements the authors assigned the fast species to \({{{I}}}_{{\mathrm{i}}}^{-}\) and the slow species to \({{\rm{MA}}}_{{\mathrm{i}}}^{+}\), they also observed variations in activation energies, diffusion coefficients, and ion concentrations when measuring different samples fabricated either in their laboratory or that of others. This observation is not uncommon, especially in light of the wide range of reported defect parameters presented in literature for the same perovskite material23,30,31,32,33,34,35,36,37,38. One contributing factor to this observation is related to the method of evaluation of the transient ion-drift measurements. Recently, we developed an extended regularization algorithm for inverse Laplace transform for deep-level transient spectroscopy (DLTS) that reveals distributions of migration rates for ionic species instead of single migration rates39. This finding suggests that in part, the differences and inconsistencies reported in literature can originate from the fact that various experimental methods may probe different parts of the same ionic defect distribution.

Another significant contributing factor, is the high sensitivity of perovskite materials to their fabrication conditions. Subtle changes in the atmospheric environment40, annealing process41, or perovskite precursor stoichiometry42,43 have all been shown to affect the properties of the perovskite layers. These changes will also influence the properties of the ionic defects. For example, the model reported by Meggiolaro et al21. describes the dependence of defect formation energies on the microstructure of the perovskite layer and is in good agreement with the experimental results of Xing et al44. Taken together, these observations highlight the need to investigate more deeply the ionic defect landscape in perovskite materials, and identify fundamental processes that govern their formation and physical properties.

In this work, we purposefully tune the ionic defect landscape of MAPbI3 perovskite samples by fractionally modifying the stoichiometry of the perovskite precursor solution. This results in a gradual change in the densities of the various types of defects as suggested by both X-ray photoemission spectroscopy42 and photoluminescence microscopy measurements45. Herein, we directly probe the variations to the ionic defect landscape by impedance spectroscopy (IS) and DLTS, and reveal the interplay between this defect landscape and the electronic landscape of the device. We found, that even small ion densities can have an impact on the electronic landscape. By comparing the ionic migration rates with literature values, we discovered that the systematic variation in our study allows to categorize the results from literature, leading to a remarkably good agreement. Moreover, we show that the temperature dependent diffusion parameters of all the ionic defects fulfill the Meyer–Neldel rule, which we link to the fundamental hopping process of mobile ion transport in halide perovskite solar cells.


To controllably tune the defect landscape in MAPbI3 perovskite solar cells, we exploited the method developed by Fassl et al42. to fabricate a series of samples from precursor solutions with gradually changing stoichiometry. In short, we start by intentionally preparing an understoichiometric solution, in which a slight deficiency of methylammonium iodide (MAI) is expected to result in films rich in vacancies such as \({V}_{{\rm{I}}}^{+}\) and \({V}_{{\rm{MA}}}^{-}\). By gradually increasing the MAI content in the solution, a stoichiometric ratio is reached, followed by a transition to an overstoichimetric regime, in which access of MAI increases the densities of \({{{I}}}_{{\mathrm{i}}}^{-}\) and \({{\rm{MA}}}_{{\rm{i}}}^{+}\) interstitials. Chemical analysis for verification of the composition change with stoichiometry were performed by Fassl et al42. on a series of identical samples. To eliminate the influence of different extraction layers, all devices share a common architecture, in which poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) is used for hole extraction, while [6,6]-phenyl-C61-butyric acid methyl ester (PC61BM) is used for electron extraction. A thin layer of bathocuproine (BCP) is introduced between the PC61BM layer and the Ag contact in order to achieve efficient hole-blocking46,47. The current density–voltage (JV) characteristics of the resulting photovoltaic devices are shown in Supplementary Fig. 1. A very small hysteresis, often associated with the presence of mobile ions15,16,48,49,50, appears when sweeping in both voltage directions. The solar cell parameters averaged over both scan directions are shown in Supplementary Fig. 2 and are in agreement with the previous report by Fassl et al.42. In short, while the fill factor (FF) and short-circuit current (Jsc) are only very slightly influenced by the changes in stoichiometry, the open-circuit voltage (Voc) and consequently the power conversion efficiency (PCE) strongly increase for increasing stoichiometric ratios. For more information about detailed SEM, XRD, and film morphology analysis see ref. 42.

Capacitance–voltage (CV) profiling

CV measurements may offer first insights into the ionic defect landscape of the devices. We performed these measurements at an ac frequency of 80 kHz using a fast sweep rate of 30 V/s in the reverse scan direction. Following the methodology of Fischer et al51. the devices were pre-biased for 60 s at 1 V, in order to minimize the influence of mobile ions present at the interfaces of the active layer. The results of the CV measurements (Supplementary Fig. 3a) were evaluated using the Mott–Schottky approach52,53:

$$1/{C}^{2}\,=\,\frac{2({V}_{{\rm{bi}}}\,-\,V)}{e{\epsilon }_{0}{\epsilon }_{{\rm{R}}}{N}_{{\rm{eff}}}},$$

where V is the applied external voltage, e is the elementary charge, ϵ0 is the absolute permittivity and ϵR is the relative permittivity. The relative permittivity can be obtained at reverse bias in the CV measurements, where complete depletion can be assumed. In this case the capacitance in this region corresponds to the geometrical capacitance Cgeo, which can be used to calculate the relative permittivity as follows:

$${C}_{{\rm{geo}}}\,=\,\frac{{\epsilon }_{0}{\epsilon }_{{\rm{R}}}}{d}.$$

The obtained values are shown in Supplementary Fig. 3b. In the case of high frequencies, the temperature dependence of the capacitance is small and can be neglected. By applying Eq. (1) to the range dominated by the depletion capacitance, the built-in potential (Vbi) and effective doping density (Neff) can be extracted. In Fig. 1, these values are compared to the PCE values from Supplementary Fig. 2. The results indicate that both Vbi and Neff increase with increasing stoichiometry. The increase in Vbi is in agreement with the findings of Fassl et al.42, where a shift in the exponential diode characteristics revealed a similar trend in Vbi. According to literature54,55,56, the increase in Neff suggests an overall higher defect density for overstoichiometric samples since ions introduce additional charges and affect the net doping concentration. This is in agreement with the experimental observation of a lower photoluminescence quantum efficiency for samples with higher stoichiometry45.

Fig. 1: Capacitance–voltage parameters in comparison to PCE.
figure 1

The dependence of power conversion efficiency PCE (green), built-in potential Vbi (red) and effective doping density Neff (blue) on stoichiometry (MAI:PbAc2) of the precursor solution is shown. PCE values are taken from Supplementary Fig. 2 for comparison. Vbi can be corrected (yellow circles) by estimating the potential drop caused by mobile ions at the interfaces.

Determining the defect landscape by impedance spectroscopy (IS) and DLTS

Advanced spectroscopic techniques such as IS and DLTS offer further insights into the defect landscape of the devices. In an IS experiment, the current response to an externally applied alternating voltage at a certain frequency ω is measured and considered as a capacitance signal by taking into account the imaginary part of the impedance Z57,58:

$$C=\frac{{\rm{Im}}(1/Z)}{\omega },$$

by modeling the solar cell as a capacitor in parallel to a shunt resistance. To obtain a complete picture of the defects and to quantify their physical properties, we performed IS measurements over a wide frequency range (0.6 Hz < ω < 3.2 MHz) and at different temperatures (200–350 K in 5 K increments).

There are two responses in the representative IS spectra as shown in Figs. 2 and S4: a low frequency response (<102 Hz) at high temperatures (>315 K) and a step at higher frequencies (>102 Hz) and lower temperatures (<285 K) for each of the investigated samples. These responses can be assigned to two different defects. Particularly noteworthy is the increase of the low frequency section of the spectra with increasing stoichiometry, which indicates its impact on the properties of the corresponding ionic defect. From the capacitance spectra, we are able to extract the ion (defect) diffusion coefficient D based on the equation:

$$D\,=\,{D}_{0}\exp \left(-\frac{{E}_{{\rm{A}}}}{{k}_{{\rm{B}}}T}\right),$$

where the kB is the Boltzmann constant, T is the temperature, D0 is the diffusion coefficient at infinite temperature and EA is the activation energy for ion migration. This is done by extracting the ion migration rates (emission rates is the corresponding term from DLTS when applied to study electronic defects in semiconductors)30,33,59,60 as defined by:

$${e}_{{\rm{t}}}=\frac{{e}^{2}{N}_{{\rm{eff}}}{D}_{0}}{{k}_{{\rm{B}}}T{\epsilon }_{0}{\epsilon }_{{\rm{R}}}}\exp \left(-\frac{{E}_{{\rm{A}}}}{{k}_{{\rm{B}}}T}\right),$$

from the maxima of the derivative—ωdC/dω, shown in Supplementary Fig. 5. The presence of two maxima in these spectra reveal two distinct ionic defects, β and γ. We summarized the migration rates associated with these two defects in an Arrhenius diagram (Supplementary Fig. 6) and calculated the activation energies EA and the diffusion coefficients D300 K at 300 K based on Eq. (5).

Fig. 2: Comparison of DLTS and IS spectra.
figure 2

DLTS spectra (top) and IS spectra (bottom) for the samples with precursor stoichiometry: 2.96 (red), 3.00 (green) and 3.04 (blue) are shown. Areas are shaded differently in order to highlight where each defect (βγ, and δ) is observable. Defect γ is not completely visible for the chosen rate window t2/t1 = 10. For a more detailed overview see Supplementary Figs. 5 and 8.

Interestingly, the defects β and γ show opposing trends in terms of EA, D300 K, and Nion with varying stoichiometric ratios (Fig. 3). For β, the activation energy decreases whereas the diffusion coefficient at 300 K increases for increasing stoichiometry, whereas γ shows the inverse behavior. We conclude that by increasing the sample stoichiometry, ion migration of defect γ is suppressed, while the defect β becomes more mobile.

Fig. 3: Defect parameters for ionic species β, γ, and δ.
figure 3

Activation energy EA (red), diffusion coefficient D300 K at 300 K (green) and ionic defect concentration Nion (blue), extracted by IS (circles) and DLTS (crosses) for all perovskite solar cells with stoichiometric ratio of precursor solution (MAI:PbAc2).

The accumulation of mobile ions at the interfaces of the active layer, driven by the internal electric field of the photovoltaic devices, was reported in several studies15,50,61,62. The resultant inhomogeneity of the ionic distribution in the perovskite active layer leads to the formation of a Debye layer of cations at the hole transport layer and a Debye layer of anions at the electron transport layer63,64. As a result of the inhomogeneity, the defect density from IS measurements cannot be determined by using the approach by Walter et al65. for semiconductor defects. A more feasible approach can be found by taking into account the capacitance of the ionic Debye layer 66:

$${N}_{{\rm{ion}}}=\frac{{k}_{{\rm{B}}}T\Delta {C}^{2}}{{e}^{2}{\epsilon }_{0}{\epsilon }_{{\rm{R}}}}.$$

In this case, ΔC is proportional to the capacitance step observed in Supplementary Fig. 4. Following this approach, the ionic defect concentration of β slightly decreases with increasing stoichiometry, while Nion of γ shows a notable increase as shown in Fig. 3. We conclude that defect γ dominates the behavior of overstoichiometric samples, while the more mobile defect β dominates the understoichiometric ones.

To expand the insights gained by IS, we performed DLTS measurements on the same set of solar cells. For DLTS, a voltage filling pulse (from 0 to 1 V for a duration of 100 ms) is applied to the devices, while measuring the capacitance response at 80 kHz until the solar cell returns to equilibrium conditions58,67. During the filling pulse, mobile ions are pushed from both interfaces of the perovskite layer into the perovskite bulk until they reach a new steady state condition. After the filling pulse, the mobile ions move back to the interfaces caused by the internal field, which introduces a change of the solar cell capacitance30. The resulting transients, shown in Supplementary Fig. 7, were averaged over 35 single measurements to yield a high signal-to-noise ratio, and were measured within the same temperature range as the IS measurements. For the evaluation, we performed the commonly utilized boxcar method67 as shown in Figs. 2 and S8.

The analysis of the DLTS data reveals three different temperature-dependent peaks associated with three distinct defect states. Two of these defects exhibit high migration rates at low to medium temperature range, while the third shows low migration rates at higher temperatures. Following the good agreement in the peak position shown in Fig. 2 and that of the migration rates plotted in the Arrhenius diagram (Supplementary Fig. 6), we conclude that one of the two defect states with high migration rates corresponds to defect β previously identified by IS. The defect exhibiting low migration rates is attributed to γ in agreement with IS. Similarly to the IS data, defect γ dominates the boxcar spectrum for high stoichiometry samples. The remaining defect with comparably high migration rates was labeled δ. This defect cannot be evaluated with IS as it is only observable as a shoulder, not a peak, and only for higher stoichiometric ratios in a very narrow temperature range.

Unlike IS, DLTS data allows to distinguish between positive and negative ionic defects, i.e., anions and cations. As shown in Fig. 2 and S8, defects β and δ have a positive sign and correspond therefore to anions, whereas γ corresponds to a cation. As mentioned above, the migration rates (et = 1/τ) of these ionic defects can be extracted from the position of the peaks shown in Supplementary Fig. 8 and complement the results of IS measurements when plotted in the same Arrhenius diagram (Supplementary Fig. 6). We note that since the slow response of γ dominates for overstoichiometric devices, the transients for these devices at very high temperatures did not return to equilibrium within the recorded transient time length of 30 s (Supplementary Fig. 7). We excluded these non-equilibrium transients from the determination of defect parameters, as they lead to overestimated migration rates for a given temperature.

The overall trend of EA and D300 K for defects β and γ, shown in Fig. 3, is comparable with the results obtained by IS. We note that while defect parameters extracted using IS and DLTS exhibit the same general trend, they do show some variance in the absolute values of the extracted defect parameters. These differences, which are visible as an offset in the defect parameters, might arise from the broad distributions of ionic defects, reported in our recent work39. Different parts of the same defect distribution are probed by each of the two methods. Furthermore, the difference between IS and DLTS can be caused by the fact that the mobile ions with IS are detected when they reside near the interfaces at 0 V DC bias, whereas with DLTS, the mobile ions are probed while they move from the bulk to the interface. For defect δ, identified solely via DLTS, we observe a significant increase in EA for overstoichiometric samples, accompanied by a strong decrease in D300 K. The ionic defect concentration, Nion, can be extracted from DLTS measurements by using the ratio between the capacitance change ΔC caused by the ionic movement and the steady state capacitance C, given by:

$${N}_{{\rm{ion}}}\propto \frac{\Delta C}{{C}_{\infty }}{N}_{{\rm{eff}}}\,{\rm{if}}\,{N}_{{\rm{ion}}}\ll {N}_{{\rm{eff}}}.$$

As shown in Fig. 3, the trend of Nion for defects β and γ with changing stoichiometry is also in agreement with the results obtained with IS. For defect δ, the ionic defect concentration is found to increase with stoichiometry, similar to the behavior of defect γ. Due to the fact that the diffusion coefficient of γ is relatively small, it cannot be ensured that this ionic species reaches equilibrium within the duration of the filling pulse. As a result, the determined ion density for γ represents only a lower limit.

Since we performed reverse-DLTS measurements in our recent work to distinguish between electronic and ionic defects39, we attribute all observed defects to mobile ions. As part of our scenario in this recent work, we assign the anion β to \({V}_{{\rm{MA}}}^{-}\) and δ to \({{{I}}}_{{\mathrm{i}}}^{-}\). The cation γ is attributed to \({{\rm{MA}}}_{{\rm{i}}}^{+}\). This assignment is in good agreement with the results of Fassl et al.42, where XPS measurements showed an increase in the I/Pb and N/Pb ratios with increasing stoichiometry. We note that the assignment of cation γ to \({{\rm{MA}}}_{{\mathrm{i}}}^{+}\) may appear in contrast to the reports by Maier and coworkers that claim that methylammonium cations are only mobile in terms of reorientation, ruling out the migration of this species68,69. However, it was shown that rotational dynamics of methylammonium cations occurs with relaxation times in the ps timescale at room temperature70,71,72, which would be too fast to explain hysteresis. Other groups propose that methylammonium can slowly migrate15,31,54, since other possible cations, such as iodine vacancies, are expected to have far higher diffusion coefficients32,73,74. Nevertheless, we stress that DLTS provides information solely on the charge of the ionic defects and cannot directly determine the specific ionic species. Only electrically charged species can be observed. We therefore exclude neutral protonic species of MAI as reported in literature75 to be the origin of the observed mobile ions.

Interplay between the ionic and electronic landscapes

The mixed ionic–electronic conducting nature of perovskites dictates that the ionic and electronic landscapes of these materials cannot easily be decoupled76,77. One aspect linking the two is related to the effect of ion accumulation at the interfaces of the perovskite layer and the extraction layers that sandwich it78. Such ionically charged interfacial layers influence the internal electric field and the built-in potential of the device, suggesting that the estimation of Vbi from CV measurements as discussed above needs to be re-evaluated79. The validity of the Mott–Schottky relation (Eq. 1) is based on the assumption that the charge carrier density within the perovskite layer is homogeneously distributed, which may not be the case for perovskite solar cells. While we prebiased the devices before measuring CV in an attempt to eliminate the accumulation of ions at the interfaces, the resultant trend in Vbi is consistent with what has been observed by diode J–V characterization, for which no pre-biasing was applied42. This might indicate that ions still accumulate at the interfaces, resulting in a voltage drop that changes the Vbi. A simple model that accounts for this voltage drop can be constructed by considering these interfacial ion densities as Debye layers63,66,78. The overall charge for one ionic species can be expressed by ΔQ = eNionLD, where LD is the Debye length according to:

$${L}_{{\rm{D}}}=\sqrt{\frac{{\epsilon }_{{\rm{R}}}{\epsilon }_{0}{k}_{{\rm{B}}}T}{{e}^{2}{N}_{{\rm{ion}}}}}.$$

In order to account for the potential drop ΔV caused by the mobile ion density of cations NC and anions NA, we assumed a series connection of the capacitance caused by cations CC and anions CA,

$$\Delta V=\sqrt{{\epsilon }_{{\rm{R}}}{\epsilon }_{0}{k}_{{\rm{B}}}T}\left(\frac{1}{{C}_{{\rm{C}}}}+\frac{1}{{C}_{{\rm{A}}}}\right)(\sqrt{{N}_{{\rm{C}}}}-\sqrt{{N}_{{\rm{A}}}}).$$

With Eq. (9) the corrected Vbi,corr can be obtained by correcting the determined built-in potential by CV measurements with the voltage drop caused by mobile ions at the interfaces:

$${V}_{{\rm{bi}},{\rm{corr}}}={V}_{{\rm{bi}},{\rm{CV}}}-\Delta V.$$

The capacitance responses CA and CC by anions and cations, respectively, can be estimated by the capacitance steps in the IS spectra from Supplementary Fig. 4, as they correspond to the ion density Nion according to Eq. (6). Taking into consideration the ionic interfacial layers to suppress the trend observed in Vbi, a more consistent value of around 1.1 V can be obtained as shown in Fig. 1. This result is more in line with our expectations, since all the devices share the same extraction layers and contacts. As shown in a recent study77, a shift in Vbi can also be caused by electronic charge carrier accumulation at the hole transport layer interface. While our calculation correct the influence of ions on Vbi, we cannot rule out an additional electronic influence. However, the result of our correction suggests that, here, the consideration of ions is sufficient. We note that we use a model assuming two mobile ionic species to correct the shift of the built-in potential in contrast to several studies, where only one mobile species is assumed64,66. Accordingly, the magnitude of the defect density necessary to cause band bending reported here is lower compared to these studies (for more information, see SI).

One interesting, and seemingly contradicting, observation is related to the observed increase in Voc, which coincides with an increase in the overall ionic defect density with increasing stoichiometry. Recent studies suggest that mobile ions may act as non-radiative recombination centers21,22,80, evidenced, for example, by a decrease in the photoluminescence quantum efficiency (PLQE). Indeed, overstoichiometric samples exhibit a markedly lower PLQE than understoichiometric ones45. Based on these results, one might expect for overstoichiometric devices lower open-circuit voltages than for understoichiometric ones81, in contrast to the experimental observation shown in Supplementary Fig. 2. However, this apparent discrepancy can be reconciled when taking into account the substantial increase in Vbi with higher stoichiometric ratio. Consequently, while a high ionic defect concentration has a negative effect on Voc due to increase of non-radiative recombination, this effect is weaker than the considerable increase introduced by changes to the energetic alignment between MAPbI3 and the transport layers and the resultant change in Vbi42. Moreover, the impact of ions on the energy landscape is in agreement with a recent study by the group of Maier82, where the authors report an increase of band bending in MAPbI3 toward the electron transport layer originating from an ionically dominated space charge. The interplay of ions and the space charge potential enable device improvements by interfacial engineering.

The intricacy of the interplay between the ionic and electronic landscapes is exemplified by plotting the EA versus the Vbi,CV as shown in Fig. 4. The EA of defects β and γ are of similar magnitude and show a broadly linear dependence on the built-in potential, albeit with slopes of opposing signs. Straight dashed lines with slopes of  ±1 were added to Fig. 4 as a guide to the eye. These similar, but opposing trends in slope supports our earlier assignment of these defects to be related to the same type of MA ion. We can associate defect β with an MA vacancy with negative charge, and γ with a positively charged MA interstitial. Our interpretation of defect δ cannot be confirmed in this manner, since we do not observe the corresponding defect species with an opposing charge.

Fig. 4: Activation energy versus built-in potential.
figure 4

Activation energy EA of the ionic defects β (red), γ (green), and δ (blue) plotted in dependence of the built-in potential Vbi,CV extracted from CV measurements for all investigated perovskite solar cells. The dashed lines with slopes of  ±1 are guides for the eye.

The dependence of EA on Vbi might be a consequence of the band bending introduced by the interfacial ion accumulation. As the ion concentration increases, stronger band bending at the interfaces leads to higher fields that impedes the ionic hopping process at the interfaces lowering their overall mobility. This explanation is supported by plotting EA and D300 K versus Nion (see Supplementary Fig. 9). Although the trends are less clear, we generally observe an increase of EA and a decrease in D300 K for higher defect concentrations. The dependence is in agreement with our finding that mobile ions are pushed stronger towards the interfaces caused by the relation between the internal electric field and the density of ions. As a result, the diffusion coefficient decreases with higher ion density. This interaction between the ionic and electronic landscapes highlights the need to construct a clearer picture of the underlying defect physics in perovskite devices. We point out that the observed trends in activation energy, diffusion coefficient, and defect density cannot be explained by morphology changes, as measurements on an identically made set of samples show only a slight change of the grain size by a few percent, which we exclude to be the origin of the change in the defect parameters by several orders of magnitude42.

Unraveling the defect landscape across the literature

To evaluate our results in a broader context, we compared the migration rates measured herein, with data available from literature. We chose several studies with similar measurement methods such as DLTS and IS, but with a selection of different perovskite materials and transport layers as summarized in Table S10. Included in Fig. 5 are the results of Samiee et al.36, who observed two different defects in a mixed halide perovskite using IS, and three defects (attributed to cations) probed by Yang et al.34 using DLTS on FAPbI3. Additionally, included are the emission rates of two defects measured using current DLTS by Rosenberg et al.35 in MAPbBr3 single crystals and those probed by Xu et al.38 on FAPbI3 light-emitting diodes. Finally, the results of Futscher et al.30 using transient ion-drift measurements (which is DLTS under a different name) were added, which exhibit two ionic species assigned as \({{{I}}}_{\rm{{i}}}^{-}\) and \({{\rm{MA}}}_{{\rm{i}}}^{+}\) interstitials in MAPbI3 solar cells.

Fig. 5: Literature comparison.
figure 5

Migration rates reported in literature30,34,35,36,38 (often called emission rates in the papers) were plotted in an Arrhenius diagram for comparison to our findings (species β (crosses), γ (circles), δ (stars)). All reported emission rates can be associated with two regimes at low emission rates and high temperatures and at high emission rates at high and middle temperatures.

This comparison reveals a remarkable agreement between reports despite the use of different perovskite compositions and device structures. The reported emission rates broadly fall into two categories: those with low emission rates at high temperatures or those with high emission rates at high or medium temperatures. This assessment indicates that there are most likely two dominant underlying ionic defects, which can be universally observed in all perovskite materials investigated thus far.

Meyer–Neldel rule

To gain an understanding of the underlying mechanism for ion transport, we examine the relationship between the diffusion coefficient D0 (at infinite temperature) and the activation energy EA according to Eq. (4) and Fig 3. Figure 6a reveals a clear linear dependence between these two values for each of the ionic defects. Such a linear relation is known as the Meyer–Neldel rule, which is often used to describe thermally activated processes83. According to the Arrhenius Eq. (4), the Meyer–Neldel rule states that the prefactor D0 itself depends on the activation energy EA via:

$${D}_{0}\,=\,{D}_{{\rm{00}}}\exp \left(\frac{{E}_{{\rm{A}}}}{{E}_{{\rm{MN}}}}\right){\rm{with}}\,{E}_{{\rm{MN}}}\,=\,{k}_{{\rm{B}}}{T}_{{\rm{MN}}},$$

where D00 refers to the critical diffusion coefficient, EMN is the characteristic energy and TMN is the corresponding characteristic temperature. Equation (11) yields very similar values for EMN: 28 meV, 30 meV, and 35 meV for β, δ and γ, respectively. The critical diffusion coefficient D00 of β with 3 × 10−7 cm2/s is one order of magnitude higher than for δ (1 × 10−8 cm2/s). γ has the lowest D00 which is equal to 4 × 10−10 cm2/s. As a consequence of the Meyer–Neldel rule, the migration rates shown in Supplementary Fig. 6 and the diffusion coefficients (presented in Fig. 6b) that are associated with the same defect, intersect at 1000/TMN. At this intersection point, which is different for each defect species, the migration rates become independent of stoichiometry. In other words, the ionic defect landscape is no longer affected by stoichiometry at TMN. As guide to the eye, we added dashed lines to Fig. 6b, which were extracted from the values of the fits presented in Fig. 6a.

Fig. 6: Meyer–Neldel rule in two representations.
figure 6

a Arrhenius plot with diffusion coefficients over the temperature. Additional dashed lines, which correspond to the start and end points of the fits (solid lines) from the Meyer–Neldel plot (b), illustrate the range and common nature of diffusion coefficients for each ionic defect (βγ, and δ) and for all precursor stoichiometric ratios. b Meyer–Neldel plot: diffusion coefficients at infinite temperature D0 plotted over the corresponding activation energy EA. The characteristic energy EMN and the critical diffusion coefficient D00 can be extracted from the linear fits (solid lines).

We propose two possible origins for the Meyer–Neldel behavior. The first is based on disordered organic semiconductors, where the legitimacy of the Meyer–Neldel rule was linked to a Gaussian distribution of defect levels or hopping energies84. Despite being crystalline materials, it is well established that halide perovskites contain a significant amount of disorder due to spatial and temporal variations of octahedral tilts and molecular rotations85. A range of defect environments and transition pathways are therefore expected. Indeed, in our recent work, we demonstrated a distribution of migration rates for each of the reported defects39. This is also supported by a combined experimental–theoretical work, where modeling of ion migration induced PL quenching was only possible by applying a Gaussian distribution of ion migration rates86.

A second explanation arises if a multiexcitation entropy model is considered. A single hopping event is usually the result of a multiphonon excitation, since the activation energy for ion migration is large compared to the phonon energy (e.g., 16.5 meV for optical phonons)87,88. Consequently, a large number of activation pathways are available for each hopping event. A higher activation energy results in a larger number of distinct pathways expressed by the entropy, which is proportional to the exponential prefactor D089,90. Based on this model, the Meyer–Neldel rule originates from the absorption of NA phonons with NA Eph = EA, which transfers the ion first to an activated state, and then—accompanied by the emission of multiple phonons—to the target site of the perovskite lattice91.

To probe the atomistic nature of a typical diffusion process, we performed first-principles calculations of charged vacancy migration in the room temperature phase of MAPbI3 using the technical setup reported elsewhere31. We consider a low energy transition in the (001) plane as illustrated in Fig. 7. The associated migration barrier is 0.55 eV and it follows a curved diffusion pathway. Even in a single plane, due to the presence of MA, the initial and final states differ in energy by 60 meV, which supports the first disorder explanation. We further determine the vibrational frequency at T = 300 K around using CarrierCapture92. Effective frequencies of 0.4–0.7 THz represent the curvature of the potential energy surface along the directions of ion diffusion. These are unusually soft owing to a combination of the heavy elements and the flexible perovskite structure. A simple estimation of NA suggests that hundreds of phonon modes are involved in a single hopping process, which supports the second explanation. While we cannot yet assign the validity of the Meyer–Neldel rule to a single origin, it offers interesting insights into the physical mechanisms of ion migration in halide perovskites.

Fig. 7: First-principles analysis of the activation energy for hopping.
figure 7

a Calculated 2D energy surface on a 20 × 20 real-space grid for V\({\,}_{{\rm{I}}}^{+}\) migration in a (001) plane of tetragonal MAPbI3 from initial state A to final state B along the configurational coordinate Q. b The projected 1D pathway showing the associated activation energy.


In summary, we investigated the ionic defect landscape of MAPbI3 samples with gradually varying defect densities, introduced by fractionally varying the stoichiometry of the perovskite precursor solution (MAI:PbAc2). By combining the results of IS and DLTS measurements, we identify three ionic defect, which we attribute to \({V}_{{\rm{MA}}}^{-}\), \({{{I}}}_{{\rm{i}}}^{-}\), and \({{\rm{MA}}}_{i}^{+}\). We explore the tight link between the ionic defect and electronic landscapes in perovskite devices, and reveal that the accumulation of defects at the interfaces of the perovskite layer results in an increase of the built-in potential for increasing stoichiometry, which we show to be the dominant factor influencing the open-circuit voltage of the devices. Interestingly, the interplay between electronic landscape and mobile ions are found to be present at even small ion densities when considering both type of ions as mobile. The presence of ionic interfacial layers is also shown to affect the EA of the various defects, by impeding their transport due to the high electric fields they introduce. We compared the temperature dependent ion migration rates to the literature, and were able to categorize defect parameters of different perovskite materials and device architectures. Importantly, we find that the ionic defects we observed fulfill the Meyer–Neldel rule. We propose that the origin of the Meyer–Neldel rule lies either in the distribution of migration pathways or the multiphonon emission process that characterizes the hopping of ions. Our results offer significant insights into the defect physics of perovskite materials and progress the current understanding of the underlying processes, that govern the properties of this phenomenal class of materials.


Device fabrication

Pre-patterned indium tin oxide (ITO) coated glass substrates (PsiOTech Ltd., 15 Ω/cm2) were ultrasonically cleaned with 2% Hellmanex detergent, deionized water, acetone, and isopropanol, followed by 10 min oxygen plasma treatment. Modified poly(3,4-ethylene-dioxythiophene):poly(styrenesulfonate) (m-PEDOT:PSS) was spin cast on the clean substrates at 4000 rpm for 30 s and annealed at 150 °C for 15 min to act as hole transport layer93. To fabricate devices with varying stoichiometry, a MAPbI3 precursor solution was prepared by adding MAI (greatcell solar materials) and lead acetate dehydrate (Sigma Aldrich) in a molar ratio of 2.96 to anhydrous N,N-dimethylformamide (DMF, Sigma Aldrich) at a concentration of 42 wt%. Hypophosphorous acid (HPA, Sigma Aldrich) was added to the precursor solution (6.47 μl per 1 ml DMF). To increase the stoichiometry, a pure 2.4 M MAI solution (in DMF) was prepared, and based on the target stoichiometry (2.98 to 3.06 in 0.02 steps), different amounts of the pure MAI solution were added to the 2.96 precursor solution. For further details please see ref. 42. The perovskite solution was spin cast at 2000 rpm for 60 s in a dry air filled glovebox (relative humidity <0.5%). The prepared samples were transferred to a nitrogen filled glove box, where an electron transport layer PC61BM, 20 mg/ml dissolved in chlorobenzene, was dynamically spin cast at 2000 rpm for 30 s on the perovskite layer followed by a 10 min annealing at 100 °C. Sequentially, a bathocuproine (0.5 mg/ml dissolved in isopropanol) hole blocking layer was spin cast on top of the PC61BM. The device was completed with a thermally evaporated 80 nm thick silver layer.

Current–voltage characterization

The current density–voltage (JV) characteristics were measured by a computer controlled Keithley 2450 Source Measure Unit under simulated AM 1.5 sunlight with 100 mW/cm2 irradiation (Abet Sun 3000 Class AAA solar simulator). The light intensity was calibrated with a Si reference cell (NIST traceable, VLSI) and corrected by measuring the spectral mismatch between the solar spectrum, the spectral response of the perovskite solar cell and the reference cell. All measurements were performed at room temperature (300 K) with a scan rate of 0.25 V/s. To verify that the samples did not degrade during the experiment, JV measurements were performed both before and after the characterization by defect spectroscopy.

Defect spectroscopy measurements

All defects were measured using a setup consisting of a Zurich Instruments MFLI lock-in amplifier with MF-IA and MF-MD options, a Keysight Technologies 33600A function generator and a cryo probe station Janis ST500 with a Lakeshore 336 temperature controller. We performed the defect spectroscopy in the temperature range of 200–350 K in 5 K steps, controlled accurately within 0.01 K, using liquid nitrogen for cooling. DLTS, IS and CV measurements were done applying an AC frequency of 80 kHz with amplitude of Vac = 20 mV. For DLTS, the perovskite solar cells were biased from 0 to 1 V for 100 ms. The transients were measured over 30 s and averaged over 35 single measurements. For CV profiling, the solar cells were pre-biased at 1 V for 60 s and rapidly swept with 30 V/s in reverse direction. All measurements were performed on two different batches for proving repeatability.

Reporting summary

Further information on research design is available in the Nature Research Reporting Summary linked to this article.

Data availability

The data that support the findings of this study are available in Zenodo with the identifier


  1. Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050 (2009).

    CAS  PubMed  Article  Google Scholar 

  2. NREL Best research-cell efficiency chart. Accessed 10 November 2020 (2020).

  3. Miyata, A. et al. Direct measurement of the exciton binding energy and effective masses for charge carriers in organic–inorganic tri-halide perovskites. Nat. Phys. 11, 582 (2015).

    CAS  Article  Google Scholar 

  4. Stranks, S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341 (2013).

    ADS  CAS  PubMed  Article  Google Scholar 

  5. Chouhan, A. S., Jasti, N. P., Hadke, S., Raghavan, S. & Avasthi, S. Large grained and high charge carrier lifetime CH3NH3PbI3 thin-films: implications for perovskite solar cells. Curr. Appl. Phys. 17, 1335 (2017).

    ADS  Article  Google Scholar 

  6. Leguy, A. M. A. et al. How to make over 20% efficient perovskite solar cells in regular (n-i-p) and inverted (p-i-n) architectures. Chem. Mater. 30, 4193 (2018).

    Article  CAS  Google Scholar 

  7. Li, Y., Ji, L., Liu, R. & Zhang, C. et al. A review on morphology engineering for highly efficient and stable hybrid perovskite solar cells. J. Mater. Chem. A 6, 12842 (2018).

    CAS  Article  Google Scholar 

  8. Bing, J., Huang, S. & Ho-Baillie, A. W. Y. A review on halide perovskite film formation by sequential solution processing for solar cell applications. Energy Technol. 8, 1901114 (2019).

  9. Song, Z., Watthage, S. C., Phillips, A. B. & Heben, M. J. Pathways toward high-performance perovskite solar cells: review of recent advances in organo-metal halide perovskites for photovoltaic applications. J. Photonics Energy 6, 022001 (2016).

    ADS  Article  Google Scholar 

  10. Shi, Z. & Jayatissa, A. Perovskites-based solar cells: a review of recent progress, materials and processing methods. Materials 11, 729 (2018).

    ADS  PubMed Central  Article  CAS  Google Scholar 

  11. Tai, Q., Tang, K.-C. & Yan, F. Recent progress of inorganic perovskite solar cells. Energy Environ. Sci. 12, 2375 (2019).

    CAS  Article  Google Scholar 

  12. Jacobs, D. A. et al. Hysteresis phenomena in perovskite solar cells: the many and varied effects of ionic accumulation. Phys. Chem. Chem. Phys. 19, 3094 (2017).

    CAS  PubMed  Article  Google Scholar 

  13. Yuan, Y. & Huang, J. Ion migration in organometal trihalide perovskite and its impact on photovoltaic efficiency and stability. Acc. Chem. Res. 49, 286 (2016).

    CAS  PubMed  Article  Google Scholar 

  14. Rivkin, B. et al. Effect of ion migration-induced electrode degradation on the operational stability of perovskite solar cells. ACS Omega 3, 10042 (2018).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  15. Lee, J.-W., Kim, S.-G., Yang, J.-M., Yang, Y. & Park, N.-G. Verification and mitigation of ion migration in perovskite solar cells. APL Mater. 7, 041111 (2019).

    ADS  Article  CAS  Google Scholar 

  16. Kim, G. Y. et al. Large tunable photoeffect on ion conduction in halide perovskites and implications for photodecomposition. Nat. Mater. 17, 445 (2018).

    ADS  CAS  PubMed  Article  Google Scholar 

  17. Snaith, H. J. et al. Anomalous hysteresis in perovskite solar cells. J. Phys. Chem. Lett. 5, 1511 (2014).

    CAS  PubMed  Article  Google Scholar 

  18. Tress, W. et al. Understanding the rate-dependent j-v hysteresis, slow time component, and aging in CH3NH3PbI3 perovskite solar cells: the role of a compensated electric field. Energy Environ. Sci. 8, 995 (2015).

    CAS  Article  Google Scholar 

  19. Chen, B. et al. Impact of capacitive effect and ion migration on the hysteretic behavior of perovskite solar cells. J. Phys. Chem. Lett. 6, 4693 (2015).

    CAS  PubMed  Article  Google Scholar 

  20. Miyano, K., Yanagida, M., Tripathi, N. & Shirai, Y. Hysteresis, stability, and ion migration in lead halide perovskite photovoltaics. J. Phys. Chem. Lett. 7, 2240 (2016).

    CAS  PubMed  Article  Google Scholar 

  21. Meggiolaro, D., Mosconi, E. & Angelis, F. D. Formation of surface defects dominates ion migration in lead-halide perovskites. ACS Energy Lett. 4, 779 (2019).

    CAS  Article  Google Scholar 

  22. Du, M. H. Efficient carrier transport in halide perovskites: theoretical perspectives. J. Mater. Chem. A 2, 9091 (2014).

    CAS  Article  Google Scholar 

  23. Yin, W.-J., Shi, T. & Yan, Y. Unusual defect physics in CH3NH3PbI3 perovskite solar cell absorber. Appl. Phys. Lett. 104, 063903 (2014).

    ADS  Article  CAS  Google Scholar 

  24. Buin, A. et al. Halide-dependent electronic structure of organolead perovskite materials. Chem. Mater. 27, 4405 (2015).

    CAS  Article  Google Scholar 

  25. Senocrate, A. et al. Charge carrier chemistry in methylammonium lead iodide. Solid State Ion. 321, 69 (2018).

    CAS  Article  Google Scholar 

  26. Senocrate, A. & Maier, J. Solid-state ionics of hybrid halide perovskites. J. Am. Chem. Soc. 141, 8382 (2019).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  27. Li, C. et al. Iodine migration and its effect on hysteresis in perovskite solar cells. Adv. Mater. 28, 2446 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  28. Yuan, Y. et al. Electric-field-driven reversible conversion between methylammonium lead triiodide perovskites and lead iodide at elevated temperatures. Adv. Energy Mater. 6, 1501803 (2015).

    Article  CAS  Google Scholar 

  29. Yang, B. et al. Perovskites: enhancing ion migration in grain boundaries of hybrid organic-inorganic perovskites by chlorine. Adv. Funct. Mater. 27, 1700749 (2017a).

  30. Futscher, M. H. et al. Quantification of ion migration in CH3NH3PbI3 perovskite solar cells by transient capacitance measurements. Mater. Horiz. 6, 1497 (2019).

    CAS  Article  Google Scholar 

  31. Eames, C. et al. Ionic transport in hybrid lead iodide perovskite solar cells. Nat. Commun. 6, 7497 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  32. Azpiroz, J. M., Mosconi, E., Bisquert, J. & Angelis, F. D. Defect migration in methylammonium lead iodide and its role in perovskite solar cell operation. Energy Environ. Sci. 8, 2118 (2015).

    CAS  Article  Google Scholar 

  33. Yang, D., Ming, W., Shi, H., Zhang, L. & Du, M.-H. Fast diffusion of native defects and impurities in perovskite solar cell material CH3NH3PbI3. Chem. Mater. 28, 4349 (2016).

    CAS  Article  Google Scholar 

  34. Yang, W. S. et al. Iodide management in formamidinium-lead-halide-based perovskite layers for efficient solar cells. Science 356, 1376 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  35. Rosenberg, J. W., Legodi, M. J., Rakita, Y., Cahen, D. & Diale, M. Laplace current deep level transient spectroscopy measurements of defect states in methylammonium lead bromide single crystals. J. Appl. Phys. 122, 145701 (2017).

    ADS  Article  CAS  Google Scholar 

  36. Samiee, M. et al. Defect density and dielectric constant in perovskite solar cells. Appl. Phys. Lett. 105, 153502 (2014).

    ADS  Article  CAS  Google Scholar 

  37. Duan, H.-S. et al. The identification and characterization of defect states in hybrid organic-inorganic perovskite photovoltaics. Phys. Chem. Chem. Phys. 17, 112 (2015).

    CAS  PubMed  Article  Google Scholar 

  38. Xu, W. et al. Rational molecular passivation for high-performance perovskite light-emitting diodes. Nat. Photonics 13, 418 (2019).

    ADS  CAS  Article  Google Scholar 

  39. Reichert, S. et al. Ionic-defect distribution revealed by improved evaluation of deep-level transient spectroscopy on perovskite solar cells. Phys. Rev. Appl. 13, 034018 (2020).

  40. Sheikh, A. D. et al. Atmospheric effects on the photovoltaic performance of hybrid perovskite solar cells. Sol. Energy Mater. Sol. Cells 137, 6 (2015).

    CAS  Article  Google Scholar 

  41. Li, Y. et al. High-efficiency robust perovskite solar cells on ultrathin flexible substrates. Nat. Commun. 7, 10214 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  42. Fassl, P. et al. Fractional deviations in precursor stoichiometry dictate the properties, performance and stability of perovskite photovoltaic devices. Energy Environ. Sci. 11, 3380 (2018a).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  43. Falk, L. M. et al. Effect of precursor stoichiometry on the performance and stability of MAPbBr3 photovoltaic devices. Energy Technol. 8, 1900737 (2020).

    CAS  Article  Google Scholar 

  44. Xing, J. et al. Ultrafast ion migration in hybrid perovskite polycrystalline thin films under light and suppression in single crystals. Phys. Chem. Chem. Phys. 18, 30484 (2016).

    CAS  PubMed  Article  Google Scholar 

  45. Fassl, P. et al. Effect of density of surface defects on photoluminescence properties in MAPbI3 perovskite films. J. Mater. Chem. C 7, 5285 (2019).

    CAS  Article  Google Scholar 

  46. Wang, Q. et al. Qualifying composition dependent p and n self-doping in CH3NH3PbI3. Appl. Phys. Lett. 105, 163508 (2014).

    ADS  Article  CAS  Google Scholar 

  47. An, Q. et al. Enhancing the open-circuit voltage of perovskite solar cells by up to 120 mV using π-extended phosphoniumfluorene electrolytes as hole blocking layers. Adv. Energy Mater. 9, 1901257 (2019).

    ADS  Article  CAS  Google Scholar 

  48. Contreras, L. et al. Specific cation interactions as the cause of slow dynamics and hysteresis in dye and perovskite solar cells: a small-perturbation study. Phys. Chem. Chem. Phys. 18, 31033 (2016).

    CAS  PubMed  Article  Google Scholar 

  49. Weber, S. A. L. et al. How the formation of interfacial charge causes hysteresis in perovskite solar cells. Energy Environ. Sci. 11, 2404 (2018).

    CAS  Article  Google Scholar 

  50. Calado, P. et al. Evidence for ion migration in hybrid perovskite solar cells with minimal hysteresis. Nat. Commun. 7, 13831 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  51. Fischer, M., Tvingstedt, K., Baumann, A. & Dyakonov, V. Doping profile in planar hybrid perovskite solar cells identifying mobile ions. ACS Appl. Energy Mater. 1, 5129 (2018).

    CAS  Google Scholar 

  52. Sze, S. & Ng, K. K. Physics of Semiconductor Devices (Wiley, Hoboken, 2006).

  53. Grundmann, M. The Physics of Semiconductors (Springer, Berlin Heidelberg, 2010).

  54. Yuan, Y. et al. Photovoltaic switching mechanism in lateral structure hybrid perovskite solar cells. Adv. Energy Mater. 5, 1500615 (2015b).

    Article  CAS  Google Scholar 

  55. Kim, J., Lee, S.-H., Lee, J. H. & Hong, K.-H. The role of intrinsic defects in methylammonium lead iodide perovskite. J. Phys. Chem. Lett. 5, 1312 (2014).

    CAS  PubMed  Article  Google Scholar 

  56. Wang, Q. et al. Large fill-factor bilayer iodine perovskite solar cells fabricated by a low-temperature solution-process. Energy Environ. Sci. 7, 2359 (2014).

    CAS  Article  Google Scholar 

  57. Schroder, D. K. Semiconductor Material and Device Characterization (Wiley, Hoboken, 2005).

  58. Heath, J. & Zabierowski, P. in Advanced Characterization Techniques for Thin Film Solar Cells (ed. Abou-Ras, D. et al.) Ch. 4, 93–119 (Wiley, Hoboken, 2016).

  59. Heiser, T. & Mesli, A. Determination of the copper diffusion coefficient in silicon from transient ion-drift. Appl. Phys. A Solids Surf. 57, 325 (1993).

    ADS  Article  Google Scholar 

  60. Zamouche, A., Heiser, T. & Mesli, A. Investigation of fast diffusing impurities in silicon by a transient ion drift method. Appl. Phys. Lett. 66, 631 (1995).

    ADS  CAS  Article  Google Scholar 

  61. Ebadi, F., Aryanpour, M., Mohammadpour, R. & Taghavinia, N. Coupled ionic-electronic equivalent circuit to describe asymmetric rise and decay of photovoltage profile in perovskite solar cells. Sci. Rep. 9, 1–9 (2019).

  62. Zhu, T.-Y. & Shu, D.-J. Role of ionic charge accumulation in perovskite solar cell: Carrier transfer in bulk and extraction at interface. J. Phys. Chem. C 123, 5312 (2019).

    CAS  Article  Google Scholar 

  63. Richardson, G. et al. Can slow-moving ions explain hysteresis in the current-voltage curves of perovskite solar cells? Energy Environ. Sci. 9, 1476 (2016).

    MathSciNet  CAS  Article  Google Scholar 

  64. Bertoluzzi, L. et al. Mobile ion concentration measurement and open-access band diagram simulation platform for halide perovskite solar cells. Joule 4, 109–127 (2020).

  65. Walter, T., Herberholz, R., Müller, C. & Schock, H. W. Determination of defect distributions from admittance measurements and application to Cu(In, Ga)Se2-based heterojunctions. J. Appl. Phys. 80, 4411 (1996).

    ADS  CAS  Article  Google Scholar 

  66. Almora, O. et al. Capacitive dark currents, hysteresis, and electrode polarization in lead halide perovskite solar cells. J. Phys. Chem. Lett. 6, 1645 (2015).

    CAS  PubMed  Article  Google Scholar 

  67. Lang, D. V. Deep-level transient spectroscopy: a new method to characterize traps in semiconductors. J. Appl. Phys. 45, 3023 (1974).

    ADS  CAS  Article  Google Scholar 

  68. Senocrate, A. et al. Slow CH3NH3+ diffusion in CH3NH3PbI3 under light measured by solid-state NMR and tracer diffusion. J. Phys. Chem. C 122, 21803 (2018b).

    CAS  Article  Google Scholar 

  69. Senocrate, A., Moudrakovski, I. & Maier, J. Short-range ion dynamics in methylammonium lead iodide by multinuclear solid state NMR and127i NQR. Phys. Chem. Chem. Phys. 20, 20043 (2018c).

    CAS  PubMed  Article  Google Scholar 

  70. Mosconi, E., Quarti, C., Ivanovska, T., Ruani, G. & Angelis, F. D. Structural and electronic properties of organo-halide lead perovskites: a combined IR-spectroscopy and ab initio molecular dynamics investigation. Phys. Chem. Chem. Phys. 16, 16137 (2014).

    CAS  PubMed  Article  Google Scholar 

  71. Chen, T. et al. Rotational dynamics of organic cations in the CH3NH3PbI3 perovskite. Phys. Chem. Chem. Phys. 17, 31278 (2015b).

    CAS  PubMed  Article  Google Scholar 

  72. Kanno, S., Imamura, Y., Saeki, A. & Hada, M. Rotational energy barriers and relaxation times of the organic cation in cubic methylammonium lead/tin halide perovskites from first principles. J. Phys. Chem. C 121, 14051 (2017).

    CAS  Article  Google Scholar 

  73. Barboni, D. & Souza, R. A. D. The thermodynamics and kinetics of iodine vacancies in the hybrid perovskite methylammonium lead iodide. Energy Environ. Sci. 11, 3266 (2018).

    CAS  Article  Google Scholar 

  74. Senocrate, A. et al. The nature of ion conduction in methylammonium lead iodide: a multimethod approach. Angew. Chem. Int. Ed. 56, 7755 (2017).

    CAS  Article  Google Scholar 

  75. Cardenas-Daw, C., Simon, T., Stolarczyk, J. K. & Feldmann, J. Migration of constituent protons in hybrid organic–inorganic perovskite triggers intrinsic doping. J. Am. Chem. Soc. 139, 16462 (2017).

    CAS  PubMed  Article  Google Scholar 

  76. Kerner, R. A. & Rand, B. P. Ionic-electronic ambipolar transport in metal halide perovskites: Can electronic conductivity limit ionic diffusion? J. Phys. Chem. Lett. 9, 132 (2017).

    PubMed  Article  CAS  Google Scholar 

  77. Tessler, N. & Vaynzof, Y. Insights from device modeling of perovskite solar cells. ACS Energy Lett. 5, 1260–1270 (2020).

  78. Courtier, N. E., Cave, J. M., Foster, J. M., Walker, A. B. & Richardson, G. How transport layer properties affect perovskite solar cell performance: insights from a coupled charge transport/ion migration model. Energy Environ. Sci. 12, 396 (2019).

    CAS  Article  Google Scholar 

  79. Almora, O., Aranda, C., Mas-Marzá, E. & Garcia-Belmonte, G. On mott-schottky analysis interpretation of capacitance measurements in organometal perovskite solar cells. Appl. Phys. Lett. 109, 173903 (2016).

    ADS  Article  CAS  Google Scholar 

  80. Yang, C. et al. MAPbI3 single crystals free from hole-trapping centers for enhanced photodetectivity. ACS Energy Lett. 30, 2579–2584 (2019).

  81. Goetz, K. P., Taylor, A. D., Paulus, F. & Vaynzof, Y. Shining light on the photoluminescence properties of metal halide perovskites. Adv. Funct. Mater. 1910004 (2020).

  82. Kim, G. Y., Senocrate, A., Moia, D. & Maier, J. Ionically generated built in equilibrium space charge zones—a paradigm change for lead halide perovskite interfaces. Adv. Funct. Mater. 30, 2002426 (2019).

  83. Meyer, W. & Neldel, H. Relation between the energy constant and the quantity constant in the conductivity–temperature formula of oxide semiconductors. Z. Tech. Phys. 18, 588 (1937).

    CAS  Google Scholar 

  84. Metselaar, R. & Oversluizen, G. The Meyer–Neldel rule in semiconductors. J. Solid State Chem. 55, 320 (1984).

    ADS  CAS  Article  Google Scholar 

  85. Beecher, A. N. et al. Direct observation of dynamic symmetry breaking above room temperature in methylammonium lead iodide perovskite. ACS Energy Lett. 1, 880 (2016).

    CAS  Article  Google Scholar 

  86. Fassl, P. et al. Effect of crystal grain orientation on the rate of ionic transport in perovskite polycrystalline thin films. ACS Appl. Mater. Interfaces 11, 2490 (2018).

    Article  CAS  Google Scholar 

  87. Sendner, M. et al. Optical phonons in methylammonium lead halide perovskites and implications for charge transport. Mater. Horiz. 3, 613 (2016).

    CAS  Article  Google Scholar 

  88. Kirchartz, T., Markvart, T., Rau, U. & Egger, D. A. Impact of small phonon energies on the charge-carrier lifetimes in metal-halide perovskites. J. Phys. Chem. Lett. 9, 939 (2018).

    CAS  PubMed  Article  Google Scholar 

  89. Fishchuk, I. I. et al. Origin of Meyer–Neldel type compensation behavior in organic semiconductors at large carrier concentrations: disorder versus thermodynamic description. Phys. Rev. B 90, 245201 (2014).

  90. Przybytek, J., Markovich, V. & Jung, G. Meyer–Neldel rule in the conductivity of manganite single crystals. Phys. Rev. B 98, 115159 (2018).

  91. Shimakawa, K. & Aniya, M. Dynamics of atomic diffusion in condensed matter: origin of the Meyer–Neldel compensation law. Chem. Monthly 144, 67 (2012).

    Article  CAS  Google Scholar 

  92. Kim, S., Hood, S., van Gerwen, P., Whalley, L. & Walsh, A. Carriercapture.jl: Anharmonic carrier capture. J. Open Source Softw. 5, 2102 (2020).

    ADS  Article  Google Scholar 

  93. Zuo, C. & Ding, L. Modified PEDOT layer makes a 1.52 VVocfor perovskite/PCBM solar cells. Adv. Energy Mater. 7, 1601193 (2016).

    Article  CAS  Google Scholar 

Download references


C.D. and S.R. acknowledge financial support by the Bundesministerium für Bildung und Forschung (BMBF Hyper project, contract no. 03SF0514C) and thank their project partners from the University of Würzburg and ZAE Bayern for interesting discussions. Y.W.W. thanks Sunghyun Kim for assistance. Via our membership of the UK’s HEC Materials Chemistry Consortium, which is funded by EPSRC (EP/L000202), this work used the ARCHER UK National Supercomputing Service ( This work was also supported by a National Research Foundation of Korea (NRF) grant funded by the Korean government (MSIT) (no. 2018R1C1B6008728). Y.V. and C.D. thank the DFG for generous support within the framework of SPP 2196 project (PERFECT PVs). This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation programme (ERC Grant Agreement no. 714067, ENERGYMAPS).


Open Access funding enabled and organized by Projekt DEAL.

Author information

Authors and Affiliations



Y.V. and C.D. conceptualised the study. Q.A. fabricated the photovoltaic devices and characterised their photovoltaic performance under the supervision of Y.V. S.R., and C.D. planned, and S.R. performed, the defect spectroscopy measurements. Y.W.W. and A.W. performed the first-principles modelling and analysis. S.R. wrote the manuscript with input and revisions by C.D. and Y.V. All authors contributed by discussion to the manuscript.

Corresponding author

Correspondence to Carsten Deibel.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Moritz H. Futscher, Byung-wook Park and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Reichert, S., An, Q., Woo, YW. et al. Probing the ionic defect landscape in halide perovskite solar cells. Nat Commun 11, 6098 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing