Abstract
Fermi liquids (FLs) display a quadratic temperature (T) dependent resistivity. This can be caused by electronelectron (ee) scattering in presence of interband or Umklapp scattering. However, dilute metallic SrTiO_{3} was found to display T^{2} resistivity in absence of either of the two mechanisms. The presence of soft phonons as possible scattering centers raised the suspicion that T^{2} resistivity is not due to ee scattering. Here, we present the case of Bi_{2}O_{2}Se, a layered semiconductor with hard phonons, which becomes a dilute metal with a small singlecomponent Fermi surface upon doping. It displays T^{2} resistivity well below the degeneracy temperature in absence of Umklapp and interband scattering. We observe a universal scaling between the T^{2} resistivity prefactor (A) and the Fermi energy (E_{F}), an extension of the KadowakiWoods plot to dilute metals. Our results imply the absence of a satisfactory understanding of the ubiquity of ee T^{2} resistivity in FLs.
Introduction
Collision between electrons of a metal leads to a Tsquare resistivity. Postulated in 1930s by Landau and Pomeranchuk^{1} and independently by Baber^{2}, this feature has been widely documented in elemental^{3} and strongly correlated^{4} metals. At sufficiently low temperature, their resistivity (ρ) follows this simple expression:
The residual resistivity, ρ_{0}, depends on defects but, A is an intrinsic property of the metal, found to scale with the electronicspecific heat^{3,4} in dense metals (i.e., those having roughly one carrier per formula unit). The quadratic temperature dependence of the phase space is a consequence of the fact that both participating electrons reside within a thermal window of the Fermi level.
In absence of a lattice, an electron–electron collision conserves momentum and cannot degrade the charge current. To generate finite resistivity, such collisions should transfer momentum to the lattice. There are two known mechanisms: either it is because there are multiple electron reservoirs unequally coupled to the lattice^{2,3}, or because the collision is an Umklapp event^{5,6}. In the first case, the two colliding electrons have distinct electron masses^{2}. Momentum transfer between these two distinct reservoirs sets the temperature dependence of resistivity, and the mass mismatch causes momentum leak to the lattice thermal bath. In the second case, one of the two colliding electrons is scattered to the second Brillouin zone and returns to the first one by transferring a unit vector of the reciprocal lattice (G) of momentum to the lattice^{5,6}.
The observation of a T^{2} resistivity in dilute metallic SrTiO_{3} indicated, however, that our understanding of the microscopic foundations of this ubiquitous phenomenon is unsatisfactory^{7}. SrTiO_{3} is a cubic perovskite at room temperature. It is a quantum paraelectric and becomes a dilute metal upon introduction of a tiny concentration of mobile electrons^{8}. Three concentric conducting bands centered at Γ point of the Brillouin zone are successively filled^{9}. The quadratic temperature dependence of its electrical resistivity^{10,11} persists^{7} even when its Fermi surface shrinks to a single pocket^{12} and none of the two mechanisms operate. However, it was more recently suggested that this enigmatic Tsquare resistivity may be caused by exotic mechanisms such as scattering by magnetic impurities^{13} or by two soft transverse optical phonons (See Supplementary Discussion)^{14,15}. Such soft phonons are known to play a decisive role in transport properties of the system, at least at high temperatures^{16,17,18,19}.
Here, we report on another dilute metal, doped Bi_{2}O_{2}Se. We show that it displays T^{2} resistivity whilst the Hall carrier density (n) changes by two orders of magnitude and in absence of interband and Umklapp scattering. Moreover, there are no soft phonons and the Tsquare resistivity is restricted to temperatures well below the degeneracy temperature. The e–e origin of this Tsquare resistivity is unambiguous. Comparing the evolution of A with n and E_{F} in Bi_{2}O_{2}Se and SrTiO_{3}, we uncover a universal scaling between A and E_{F} in dense and dilute Fermi liquids. Our results imply that a proper microscopic theory of the link between electron–electron scattering and Tsquare resistivity is still missing.
Results
Firstprinciple calculations of Bi_{2}O_{2}Se single crystal
Stoichiometric Bi_{2}O_{2}Se is a layered semiconductor with tetragonal crystal structure (antiThCr_{2}Si_{2} phase) at room temperature^{20}, shown in Fig. 1a. Available Bi_{2}O_{2}Se singlecrystals are metallic with extremely mobile carriers^{21,22,23}. The insulator is doped by unavoidable defects, such as Se or O vacancies and Se–Bi antisite defects^{24,25}. According to density functional theory (DFT) calculations^{24}, the conduction band is centered at the Γ point of the Brillouin zone, following a parabolic dispersion (Fig. 1b and Supplementary Fig. 1). This has been revealed by angleresolved photoemission spectroscopy (ARPES) measurements^{21,26}. The Fermi surface is an elongated ellipsoid (Fig. 1a) seen by quantum oscillations^{26}. The comparison of crystal and band structure between Bi_{2}O_{2}Se and SrTiO_{3} is summarized in Supplementary Table 1.
Our DFT calculations of phonon spectrum for the tetragonal phase of Bi_{2}O_{2}Se are in agreement with what was reported previously^{27,28}. Figure 1c presents the phonon dispersion at ambient pressure. The absence of imaginary frequencies implies that the tetragonal phase is dynamically stable. Figure 1d–f shows the evolution of the calculated local potential and phonon frequencies with hydrostatic pressure. Clearly, the singlewell local potential at ambient pressure is different from a quantum paraelectric, where the local potential is a shallow doublewell and the ferroelectric phase is aborted due to quantum tunneling between two local minima of the well. In a quantum paraelectric, the soft mode is very sensitive to hydrostatic pressure. For example, in PbTe a wellknown quantum paraelectric, the soft mode frequency almost triples by reducing the lattice constant (a) by 1%^{29}. In contrast, all three optical modes change moderately by reducing a, in Fig. 1f. The lowest mode (TO_{1}) hardens only by 20% by a similar reduction of a. We also note that a large negative pressure (≈−5 GPa) is required to make the system ferroelectric. These observations rule out the proximity to a ferroelectric instability, excluding the presence of soft phonons.
Quadratic temperature dependence of resistivity
Figure 2a shows the temperature dependence of resistivity ρ(T) in our Bi_{2}O_{2}Se samples with various n (See Supplementary Fig. 2, Supplementary Fig. 3 and Supplementary Table 2 for more information). We note that our data (obtained for n < 1 × 10^{19} cm^{−3}) smoothly joins what was recently reported for n = 1.1 × 10^{19} cm^{−3}^{22}. Upon cooling from room temperature to 1.8 K, resistivity decreases by two orders of magnitude, comparable to what is seen in doped quantum paraelectrics such as SrTiO_{3}, KTaO_{3}, and PbTe^{16}.
Panels b–e of Fig. 2 document the lowtemperature quadratic temperature dependence of resistivity. It persists down to the lowest temperatures in all the samples. Equation (1) holds below a characteristic temperature (dubbed T_{quad}). As seen in Fig. 2f, T_{quad} is an order of magnitude lower than T_{F}, the degeneracy temperature of the fermionic system (extracted from our study of quantum oscillations described below). The relevance of T_{quad} ≪ T_{F} inequality in Bi_{2}O_{2}Se contrasts with what was seen in SrTiO_{3}^{7}. Only well below the degeneracy temperature, one expects the phase space of the fermionfermion scattering to be quadratic temperature. Therefore, one reason to question the attribution of Tsquare resistivity to e–e scattering, which was raised in the case of SrTiO_{3}, is absent.
Figure 2g presents the evolution of the T^{2} prefactor (A) with n for Bi_{2}O_{2}Se. For comparison, the relevant data for doped SrTiO_{3} and KTaO_{3} are also shown. In both cases, A decreases with increasing n. While A(n) is more fluctuating in Bi_{2}O_{2}Se than in SrTiO_{3}, the two slopes (\(\frac{n}{A}\frac{{\rm{d}}A}{{\rm{d}}n}\)) are close to each other. At similar n, the magnitude of A differs by more than one order of magnitude lower. We will see below that this arises because of the difference in the magnitude of the effective electron mass, which sets the Fermi energy at a given carrier density.
Thus, Bi_{2}O_{2}Se is the second metallic system in which Tsquare resistivity is observed in presence of a singlecomponent and small Fermi surface. The absence of multiple pockets leaves no place for interband scattering. The smallness of the Fermi surface excludes Umkalpp events (See below for quantitative discussion).
Two features make the theoretical challenge thrown down by Bi_{2}O_{2}Se more solid than the one presented by SrTiO_{3}. First of all, since T_{quad} ≪ T_{F}, one objection to associating Tsquare resistivity and e–e scattering vanishes. Moreover, the absence of any exotic soft phonons, rules out their possible role as scattering centers^{14,15}.
Having shown that Tsquare resistivity is present in Bi_{2}O_{2}Se like in SrTiO_{3} without objections ascribing it to e–e collisions, let us consider the relevance of the expression previously used^{7} for the Tsquare prefactor:
Here, ℏ is Planck’s constant divided by 2π, e is the electron charge, k_{B} is the Boltzmann constant and l_{quad} is a materialdependent characteristic length, which arises uniquely due to a dimensional analysis. Such an examination requires to know E_{F} at a given n. For this, we performed a detailed study of quantum oscillations.
Resistive quantum oscillations
Figure 3a, b shows that in presence of magnetic field, resistivity shows quantum oscillations with a single frequency for both inplane and outofplane orientations of the magnetic field. When n ≈ 4.3 × 10^{18} cm^{−3}, the oscillation frequency is F_{H∥c} ≈ 51 T and F_{H∥ab} ≈ 93 T. This implies that the Fermi surface is an ellipsoid at the center of the Brillouin zone. The Fermi surface anisotropy \(\alpha =\frac{{F}_{{\rm{H}}\parallel {\rm{ab}}}}{{F}_{{\rm{H}}\parallel {\rm{c}}}}=1.8\). This is in excellent agreement with our theoretical calculations (Fig. 1b), which finds that the dispersion along ΓX and ΓZ with the value of anisotropy (α) differ by 1.75. Similar data for other samples are presented in the Supplementary Fig. 4 and summarized in Supplementary Table 3.
The volume of the ellipsoidal Fermi pocket implies a carrier concentration n_{SdH} = 3.8 × 10^{18} cm^{−3}, close to the Hall carrier concentration. The numbers remain close to each other when n > 10^{18} cm^{−3} (see Supplementary Table 3). At very low densities, n_{SdH} starts to fall below n, which may indicate that the single Fermi sea begins to fall apart to isolated lakes due to insufficient homogeneity in doping.
The small size of the Fermi surface excludes the possible occurrence of Umklapp event, which requires a Fermi wave vector larger than onefourth of the smallest reciprocal lattice vector, G. For Bi_{2}O_{2}Se, the smallest G is along caxis, \({{\bf{G}}}_{{\rm{c}}}=\frac{2\pi }{c}\approx 5.17\) nm^{−1}, given the lattice constant c = 12.16 Å of the tetragonal unit cell. Then the threshold carrier density for Umklapp scattering (n_{U}) can be estimated to be \({n}_{{\rm{U}}}=\frac{1}{3{\pi }^{2}}{k}_{{\rm{Fa}}}^{2}{k}_{{\rm{Fc}}}=3\times 1{0}^{19}\) cm^{−3} with \({k}_{{\rm{Fc}}}=\frac{{{\bf{G}}}_{{\rm{c}}}}{4}\) and \(\alpha =\frac{{k}_{{\rm{Fc}}}}{{k}_{{\rm{Fa}}}}\approx 1.8\) (k_{Fc} and k_{Fa} are Fermi wave vector along caxis and aaxis). For n < n_{U}, no Umklapp scattering is expected, which includes our range of study and beyond.
Figure 3c shows how quantum oscillations are damped with increasing temperature. This allows us to extract the effective mass m^{*} using the Lifshitz–Kosevich (L–K) formula:
where \(\eta =\frac{2{\pi }^{2}{k}_{{\rm{B}}}}{{\rm{e}}\hslash }\). We find an inplane effective electron mass \({m}_{{\rm{H}}\parallel {\rm{c}}}^{* }\approx 0.17{m}_{{\rm{e}}}\), in agreement with previous reports^{21,22,26}, and an outofplane mass \({m}_{{\rm{H}}\parallel {\rm{ab}}}^{* }\approx 0.25{m}_{{\rm{e}}}\) (m_{e} is the free electron mass). As expected, the ratio of these cyclotron masses is close to the ratio of the two ellipsoid axes.
Figure 3d shows \({E}_{{\rm{F}}}={\scriptstyle{\frac{{\left(\hslash {k}_{{\rm{Fab}}}\right)}^{2}}{2{m}_{{\rm{H}}\parallel {\rm{c}}}^{* }}}}\) as a function of k_{Fab} (the inplane wave vector). Each data point represents a different sample. As seen in Fig. 3e, the magnitude of the effective mass and Fermi surface anisotropy remain unchanged with doping. The data imply that the conducting band dispersion is parabolic. We also note that the effective mass resolved here (m^{*} = 0.17 ± 0.1m_{e}, see Table S1) is only 1.3 ± 0.1 larger than the DFT calculated bare mass of m_{b} = 0.125m_{e}. In contrast, in SrTiO_{3}, band dispersion of the lower band is nonparabolic and there is a significant mass enhancement due to coupling to phonons^{7,11}. This comparison highlights the simplicity of the case of Bi_{2}O_{2}Se where any polaronic effect seems to be absent.
Scaling between A and E _{F}
With the help of Fig. 3d, we can map n to E_{F} and translate the data of Fig. 2g in a new figure (Fig. 4a), which compares the evolution of A with E_{F} in Bi_{2}O_{2}Se and in SrTiO_{3−δ}. Remarkably, the two sets of data join each other. Because of the lightness of its electrons, Bi_{2}O_{2}Se has a Fermi energy ten times higher than SrTiO_{3−δ} at the same carrier density.
In Fig. 4b, we include the new Bi_{2}O_{2}Se data in a universal plot of A v.s. E_{F}. The data for other materials are taken from references^{7,8,30} and are summarized in Supplementary Table 4–6. Note that for all anisotropic conductors including Bi_{2}O_{2}Se, the plot shows the prefactor in the plane with the higher conductivity.
This plot is an extension of the original Kadowaki–Woods plot^{4} to dilute Fermi liquids. In a dense metal, the electronicspecific heat (in molar units) is an accurate measure of the Fermi energy. In a dilute metal, on the other hand, the molar units for atoms and electrons differ by orders of magnitude and therefore, one cannot use the electronicspecific heat as a measure of the Fermi energy.
Kadowaki and Woods observed originally that correlation between A and γ^{2} in heavyelectron metals, such A/γ^{2} ≈ 10 μΩ.cm.K^{2}.mol^{2}.J^{−2}^{4} and contrasted it with a similar ratio noticed by Rice in elemental metals (A/γ^{2} ≈ 0.4 μΩ.cm.K^{2}.mol^{2}.J^{−2})^{3}, where γ is the electronicspecific heat coefficient. Subsequent studies^{31} brought new data indicating that these ratios define two rough and lower boundaries (and recently even ^{3}He has been shown to be on the Kadowaki–Woods plot^{32}).
According to Fig. 4b, this 25fold difference in the A/γ^{2} magnitude is equivalent to a statement on the boundaries of l_{quad}, which lies between 1.6 and 40 nm across systems whose carrier concentration and Fermi energy differ by many orders of magnitude. This is in agreement with a recent observation by Kurita et al.^{30}. They put under scrutiny the correlation between A and the lowtemperature slope of the Seebeck efficient (which remains a measure of the Fermi energy even in dilute systems^{33}) and found that in a variety of systems l_{quad} ≈ 4 nm^{30}.
l_{quad} is a phenomenological quantity coming out of dimensional analysis. Nevertheless, it is welldefined and equal to the product of the Fermi wave vector and the crosssection of electron–electron collision^{7,34}. This implies that its boundaries are meaningful and beg for an explanation.
Discussion
Most previous theoretical attempts focus on isolated cases and did not seek a global scenario. Let us consider briefly their relevance to our data. One scenario for T^{2} resistivity, proposed decades ago, invokes inelastic electronimpurity scattering and its interplay with electron–phonon interaction^{35,36,37}. Such an effect has been reported in several impure metals. It appears too weak to account for the T^{2} term in Bi_{2}O_{2}Se where \(\frac{A}{{\rho }_{0}} \sim 1{0}^{3}\) K^{−2}. Pal and coauthors proposed that nonGalilean invariant FLs can display T^{2} resistivity even in the absence of Umklapp events^{38}. However, this scenario for T^{2} resistivity does not expect it in a systems with parabolic dispersion such as Bi_{2}O_{2}Se. Quantum interference near a ferromagnetic quantum critical point (QCP) can induce a resistivity proportional to \({T}^{2}{\rm{ln}}T\)^{39}. This is inapplicable to Bi_{2}O_{2}Se, which is not close to any QCP. Lucas pointed to hydrodynamic flow of electrons in random magnetic fields as a possible source of T^{2} resistivity^{13} in SrTiO_{3}, speculating that oxygen vacancies can be magnetic there. Its relevance to a nonmagnetic systems such as Bi_{2}O_{2}Se is quite unlikely.
In summary, we find that the fermiology of dilute metallic Bi_{2}O_{2}Se is such that interband or Umklapp scattering cannot happen. Nevertheless, there is a T^{2} resistivity unambiguously caused by electron–electron scattering. We find a universal link between Fermi energy and the prefactor of Tsquare resistivity, which persists across various Fermi liquids. We conclude that a proper understanding of the microscopic origin of Tsquare resistivity in Fermi liquids is missing.
Methods
Sample growth
Bi_{2}O_{2}Se polycrystals were synthesized through solid state reaction with stoichiometric Bi (5N), Se (5N), and Bi_{2}O_{3} (5N) powders of high purity. The mixed materials are sealed in an evacuated quartz tube and heated in an oven at 823K for 24 h. The singlecrystalline phase was obtained through the chemical vapor transport (CVT) method by using polycrystals as precursors. The sealed quartz tubes were placed in a horizontal furnace at a temperature gradient from 1123 to 1023 K over one week. The resulting singlecrystals are shiny and airstable. Note that, we didn’t use transport agents such as I_{2}, in order to avoid unintentional doping. Samples with n below and above 10^{18} cm^{−3} are cleaved from two individual batches, respectively. Hence, we may expect a moderate inhomogeneous distribution of carrier concentrations in each sample.
Experiments
Xray diffraction patterns were performed using a Bruker D8 Advanced Xray diffractometer with Cu Kα radiation at room temperature. The composition of samples was determined by an energydispersive Xray (EDX) spectrometer affiliated to a Zeiss field emission scanning electron microscope (SEM). The transport measurements were done by a standard fourterminal method in Quantum Design PPMSDynacool equipped with 14T magnet. Ohmic contacts were obtained by evaporating gold pad to samples before attaching wires with silver paste.
DFT calculations
All firstprinciples calculations were carried out using density functional theory (DFT) as implemented in Quantum Espresso^{40}. The generalized gradient approximation (GGA) of Perdew–Burke–Ernzerhof revised for solids (PBEsol) type^{41} was used to describe the exchangecorrelation energy. We used ultrasoft pseudopotentials from the Garrity, Bennett, Rabe, Vanderbilt (GBRV) highthroughput pseudopotential set^{42} and a planewave energy cutoff of 50 Ry and charge density cutoff of 250 Ry. The full phonon spectrum was calculated using the supercell approach as implemented in phonopy^{43} with the nonanalytical term correction at the Γ point included. As Bi is known for its strong spinorbit coupling (SOC), the electronic band structure with SOC was calculated using the fully relativistic pseudopotentials taken from pslibrary (version 1.0.0)^{44}. Both electronic band structure and phonon spectrum were calculated along the highsymmetry lines of the Brillouin zone of a bodycentered tetragonal unit cell.
Data availability
The data that support the findings of this study are included in this article and its supplementary information file and are available from the corresponding author upon reasonable request.
References
Landau, L. & Pomerantschuk, I. Über Eigneschaften der metalle bei sehr niedrigen Temperaturen. Phys. Z. Sowjet 10, 649–653 (1936).
Baber, W. G. The contribution to the electrical resistance of metals from collisions between electrons. Proc. R. Soc. Lond. Ser. A 158, 383–396 (1937).
Rice, M. J. Electronelectron scattering in transition metals. Phys. Rev. Lett. 20, 1439–1441 (1968).
Kadowaki, K. & Woods, S. B. Universal relationship of the resistivity and specific heat in heavyFermion compounds. Solid State Commun. 58, 507–509 (1986).
Yamada, K. & Yosida, K. Fermi liquid theory on the basis of the periodic Anderson Hamiltonian. Prog. Theor. Phys. 76, 621–638 (1986).
Maebashi, H. & Fukuyama, H. Electrical conductivity of interacting fermions. II Effects of normal scattering processes in the presence of Umklapp scattering processes. J. Phys. Soc. Jpn. 67, 242–251 (1998).
Lin, X., Fauqué, B. & Behnia, K. Scalable T ^{2} resistivity in a small singlecomponent Fermi surface. Science 349, 945 (2015).
Collignon, C., Lin, X., Rischau, C. W., Fauqué, B. & Behnia, K. Metallicity and superconductivity in doped strontium titanate. Ann. Rev. Cond. Mat. Phys. 10, 25–44 (2019).
Lin, X. et al. Critical doping for the onset of a twoband superconducting ground state in SrTiO_{3−δ}. Phys. Rev. Lett. 112, 207002 (2014).
Okuda, T., Nakanishi, K., Miyasaka, S. & Tokura, T. Large thermoelectric response of metallic perovskites: Sr_{1−x} La_{x} TiO_{3} (0 ≤ x ≤ 1). Phys. Rev. B 63, 113104 (2001).
Van Der Marel, D., van Mechelen, J. L. M. & Mazin, I. I. Common Fermiliquid origin of T ^{2} resistivity and superconductivity in ntype SrTiO_{3}. Phys. Rev. B 84, 205111 (2011).
Lin, X., Zhu, Z., Fauqué, B. & Behnia, K. Fermi surface of the most dilute superconductor. Phys. Rev. X 3, 021002 (2013).
Lucas, A. Kinetic theory of electronic transport in random magnetic fields. Phys. Rev. Lett. 120, 116603 (2018).
Maslov, D. L. & Chubukov, A. V. Optical response of correlated electron systems. Rep. Prog. Phys. 80, 026503 (2017).
Epifanov, Y. N., Levanyuk, A. P. & Levanyuk, G. M. Interaction of carriers with TOphonons and electrical conductivity of ferroelectrics. Ferroelectrics 35, 199–202 (1981).
Lin, X. et al. Metallicity without quasiparticles in roomtemperature strontium titanate. npj Quant. Mat. 2, 41 (2017).
Zhou, J. J., Hellman, O. & Bernardi, M. Electronphonon scattering in the presence of soft modes and electron mobility in SrTiO_{3} perovskite from first principles. Phys. Rev. Lett. 121, 226603 (2018).
Zhou, J. J. & Bernardi, M. Predicting charge transport in the presence of polarons: the beyondquasiparticle regime in SrTiO_{3}. Phys. Rev. Res. 1, 033138 (2019).
Collignon, C., Bourges, P., Fauqué, B. & Behnia, K., Heavy nondegenerate electrons in doped strontium titanate. Preprint at https://arxiv.org/abs/2001.04668 (2020).
Boller, H. The crystal structure of Bi_{2} O_{2} Se. Monatsh. Chem. Chem. Mon. 104, 916–919 (1973).
Wu, J. X. et al. High electron mobility and quantum oscillations in nonencapsulated ultrathin semiconducting Bi_{2} O_{2} Se. Nat. Nanotech. 12, 530–C534 (2017).
Lv, Y. Y. et al. Electronelectron scattering dominated electrical and magnetotransport properties in the quasitwodimensional Fermi liquid singlecrystal Bi_{2} O_{2} Se. Phys. Rev. B 99, 195143 (2019).
Wu, J. X. et al. Low residual carrier concentration and high mobility in 2D semiconducting Bi_{2} O_{2} Se. Nano Lett. 19, 197–202 (2019).
Fu, H. X., Wu, J. X., Peng, H. L. & Yan, B. H. Selfmodulation doping effect in the highmobility layered semiconductor Bi_{2} O_{2} Se. Phys. Rev. B 97, 241203 (2018).
Li, H. L. et al. Native point defects of semiconducting layered Bi_{2} O_{2} Se. Sci. Rep. 8, 10920 (2018).
Chen, C. et al. Electronic structures and unusually robust bandgap in an ultrahighmobility layered oxide semiconductor, Bi_{2} O_{2} Se. Sci. Adv. 4, eaat8355 (2018).
Wang, C., Ding, G. Q., Wu, X. M., Wei, S. S. & Gao, G. Y. Electron and phonon transport properties of layered Bi_{2} O_{2} Se and Bi_{2} O_{2} Te from firstprinciples calculations. N. J. Phys. 20, 123014 (2018).
Pereira, A. L. J. et al. Experimental and theoretical study of Bi_{2} O_{2} Se under compression. J. Phys. Chem. C. 122, 8853–8867 (2018).
An, J., Subedi, A. & Singh, D. J. Ab initio phonon dispersions for PbTe. Sol. Stat. Comm. 148, 417–419 (2008).
Kurita, K., Sakabayashi, H. & Okazaki, R. Correlation in transport coefficients of holedoped CuRhO_{2} single crystals. Phys. Rev. B 99, 115103 (2019).
Tsujii, N., Yoshimura, K. & Kosuge, K. Deviation from the Kadowaki–Woods relation in Ybbased intermediatevalence systems. Matter 15, 1993–2003 (2003).
Jaoui, A. et al. Departure from the WiedemannFranz law in WP_{2} driven by mismatch in T square resistivity prefactors. npj Quant. Mat. 3, 64 (2018).
Behni, K., Jaccard, D. & Flouquet, J. On the thermoelectricity of correlated electrons in the zerotemperature limit. J. Phys. Cond. Mat. 16, 5187–5198 (2004).
Mott, N.F. MetalInsulator Transitions 2nd edn. (Taylor and Francis, London, 1990) pp. 72–73.
Koshino, S. Scattering of electrons by the thermal motion of impurity ions. II. Prog. Theor. Phys. 24, 1049–1054 (1960).
Taylor, P. L. Changes in electrical resistance caused by incoherent electronphonon scattering. Phys. Rev. 135, A1333–A1335 (1964).
Reizer, M. Y. & Sergeev, A. V. The effect of the electronphonon interaction of the conductivity of impure metals. Sov. Phys. JETP 65, 1291–1298 (1987).
Pal, H. K., Yudson, V. I. & Maslov, D. L. Resistivity of nonGalileaninvariant Fermi and nonFermi liquids. Lith. J. Phys. 52, 142–164 (2012).
Paul, I. Interaction correction of conductivity near a ferromagnetic quantum critical point. Phys. Rev. B 77, 224418 (2008).
Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and opensource software project for quantum simulations of materials. J. Phys. Condens. Matter 21, 395502 (2009).
Csonka, G. I. et al. Assessing the performance of recent density functionals for bulk solids. Phys. Rev. B 79, 155107 (2009).
Garrity, K. F., Bennett, J. W., Rabe, K. M. & Vanderbilt, D. Pseudopotentials for highthroughput DFT calculations. Comput. Mater. Sci. 81, 446–452 (2014).
Togo, A. & Tanaka, I. First principles phonon calculations in materials science. Scr. Materialia 108, 1–5 (2015).
Corso, A. D. Pseudopotentials periodic table: from H to Pu. Comput. Mater. Sci. 95, 337–350 (2014).
Sakai, A., Kanno, T., Yotsuhashi, S., Adachi, H. & Tokura, Y. Thermoelectric properties of electrondoped KTaO_{3}. Jpn. J. Appl. Phys. 48, 097002 (2009).
Martino, E. et al. Twodimensional conical dispersion in ZrTe_{5} evidenced by optical spectroscopy. Phys. Rev. Lett. 122, 217402 (2019).
Maruhashi, K. et al. Anisotropic quantum transport through a single spin channel in the magnetic semiconductor EuTiO_{3}. Adv. Mater. 32, 1908315 (2020).
Acknowledgements
This research was supported by National Natural Science Foundation of China via Project 11904294, Zhejiang Provincial Natural Science Foundation of China under Grant No. LQ19A040005 and the foundation of Westlake University. We thank the support provided by Dr. Chao Zhang from Instrumentation and Service Center for Physical Sciences (ISCPS) and computational resource provided by Supercomputer Center in Westlake University. This work is part of a DFGANR project funded by Agence Nationale de la Recherche (ANR18CE92002001) and by the DFG through projects LO 818/61 and HE 3219/61.
Author information
Authors and Affiliations
Contributions
J.L.W. prepared the samples and did the experiments. He was assisted in the measurements by Z.K.X., J.F.W., W.H.H., and Z.R. J.W. and S.L. did DFT calculations. J.L.W., T.W., and X.L. prepared the figures. K.B. and X.L. wrote the manuscript. X.L. led the project. All authors contributed to the discussion.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Filip Ronning and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, J., Wu, J., Wang, T. et al. Tsquare resistivity without Umklapp scattering in dilute metallic Bi_{2}O_{2}Se. Nat Commun 11, 3846 (2020). https://doi.org/10.1038/s41467020176926
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467020176926
Further reading

Thermal resistivity and hydrodynamics of the degenerate electron fluid in antimony
Nature Communications (2021)

Huge permittivity and premature metallicity in Bi2O2Se single crystals
Science China Physics, Mechanics & Astronomy (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.