Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

# Femtosecond exciton dynamics in WSe2 optical waveguides

## Abstract

Van-der Waals (vdW) atomically layered crystals can act as optical waveguides over a broad range of the electromagnetic spectrum ranging from Terahertz to visible. Unlike common Si-based waveguides, vdW semiconductors host strong excitonic resonances that may be controlled using non-thermal stimuli including electrostatic gating and photoexcitation. Here, we utilize waveguide modes to examine photo-induced changes of excitons in the prototypical vdW semiconductor, WSe2, prompted by femtosecond light pulses. Using time-resolved scanning near-field optical microscopy we visualize the electric field profiles of waveguide modes in real space and time and extract the temporal evolution of the optical constants following femtosecond photoexcitation. By monitoring the phase velocity of the waveguide modes, we detect incoherent A-exciton bleaching along with a coherent optical Stark shift in WSe2.

## Introduction

In the steady-state, it is customary to characterize the behavior of optical waveguide modes with the in-plane component of the complex wavevector, qr = q1,r + iq2,r1,2,3,4,5; the subscript r stands for “reference”. The real component of the wavevector, q1,r, describes the phase velocity of the waveguide mode; the imaginary component of the wavevector, q2,r, characterizes attenuation. Previous works have demonstrated that the qr formalism applied to scanning near-field microscopy (SNOM) visualization of the steady state waveguide modes is well suited to evaluate the anisotropic dielectric tensor of vdW semiconductors4. This class of materials hosts uncommonly strong excitonic resonances, which are of particular interest given their substantial impact on the ab-plane optical polarizability in the near-infrared and visible range3,6,7,8. These excitonic resonances yield absorptive and refractive spectral features that are, likewise, encoded in the complex wavevector, qr, of waveguide modes3. In this work we focus on the ultrafast dynamics of the extraordinary waveguide mode in the prototypical vdW crystal, WSe2 (Fig. 1a, b) produced by photoexcitation. Photoexcitation perturbs excitons8,9,10,11,12,13 prompting changes of the complex wavevector, qp, where the subscript p indicates that qp is obtained in the “photo-excited” state. Our waveguide imaging data (Figs. 13) expose the rich photo-induced response of WSe2 rooted in both coherent and incoherent dynamics of the A-exciton. Coherent dynamics are registered in our WSe2 waveguides at the sub-picosecond (ps) timescale and are attributed to the optical Stark shift10,11,12. Incoherent dynamics persist on longer (10 ps) time scales and are indicative of bleaching of the A-exciton. Our work uncovers the utility of waveguide modes in quantifying non-equilibrium light-driven effects in vdW crystals.

## Results

### Time-resolved nano-imaging of waveguide modes

To experimentally access and control waveguide modes in vdW crystals we utilize state-of-the-art time-resolved scattering near-field optical microscopy (tr-SNOM)8,14,15,16,17,18, Fig. 1a. Here, the metalized tip of an atomic force microscope (AFM) is illuminated with p-polarized light. The evanescent field is confined at the tip apex with radius of curvature, a. The extreme confinement provides access to local near-fields scattered by the AFM tip with a = 20 nm spatial resolution, and waveguides modes with momenta up to q ~ 1/a, independent of the wavelength of probe radiation (methods, Supplementary Note 1)19,20. Monitoring the amplitude of the near-field scattering signal, Sr, (methods) along the surface of the crystal we observe a characteristic periodic pattern (Fig. 1b)3,4,5. A representative line profile in the direction normal to the crystal edge (Fig. 1c–e) highlights periodic oscillations. These imaging data are consistent with the following scenario. The AFM tip launches a waveguide mode, which travels in the bulk of the layered crystals. When the waveguide mode reaches the edge of the crystal after traveling the distance x from the AFM probe, the mode scatters to free space and reaches the detector. By measuring the near-field amplitude as a function of x, we visualize the electric field profile of the waveguide mode (see Supplementary Note 1). Non-equilibrium data are obtained by illuminating the crystal with an s-polarized pump beam, with nearly homogeneous intensity across the scanned region (see Supplementary Note 1). In the photo-excited case, the complex wavevector of the waveguided mode is altered. In this work, we focus on the response of WSe2 because its A-exciton resonance lies in the frequency region that can be readily accessed with our tr-SNOM allowing us to fully characterize dynamics of excitons under intense optical pumping of this particular vdW waveguide.

### WSe2 in the steady state

We begin with the electrodynamics of WSe2 at equilibrium. In Fig. 2a we display line profiles of the near-field amplitude collected with several probe energies, E. The experimental profiles exhibit oscillations (Fig. 2a) characterized by the steady-state wavevector, qr. To extract quantitative information from the line profiles we implemented the Fourier Transform (FT) analysis. We generalized the FT procedure to correct the observed wavevector for the angle of incidence of the probe radiation, see Supplementary Note 2. The incidence-corrected FT line profiles reveal peaks located at q1,r(E) that are dependent on the probe energy, E (Fig. 2b). The energy-momentum (E-q1,r) dispersion of the waveguide mode is plotted in Fig. 2d. A non-monotonic dependence of q1,r on the probe photon energy, E is observed. The prominent ‘back-bending’ dispersion of q1,r(E) is evident in the vicinity of 1.61 eV where the electromagnetic response is dominated by the A-exciton (Fig. 2c, d; methods). The dispersion of the waveguide mode is uniquely determined by the complex dielectric tensor ||ε|| of the material whose in-plane component, εab = ε1,ab + 2,ab, is accurately represented with a series of Lorentz oscillators (methods; see Supplementary Fig. 8)3,21. The absorption spectra obtained from first principles calculations shares good agreement with our Lorentz model only when excitonic contributions are included (Fig. 2c). The dispersion relationship calculated with the Lorentz model reproduces the experimental results supporting the excitonic interpretation of the dispersion anomaly.

### Femtosecond dynamics in the WSe2 waveguide

We now introduce a pump beam, as schematically shown in Fig. 1a, to interrogate light-induced effects of WSe2 and their transient dynamics. The photon energy of the pump is chosen to be red-detuned by 50 +/− 8 meV from the A-exciton (methods; see Supplementary Note 5). We fix the energy of the probe 5 meV red-detuned from the center frequency of the A-exciton and explore dynamics of the complex wavevector qp under pumping. It is instructive to analyze photoinduced effects with the differential wavevector δqj = qj,pqj,r where the subscript j = 1, 2 refers to the real and imaginary components of the wavevector respectively. Our analysis reveals an abrupt drop of the imaginary part, q2q2 < 0) and an equally prompt recovery all occurring within the first picosecond after the photoexcitation (Fig. 3a). In other words, red-detuned photoexcitation transiently suppresses absorption in the vicinity of the excitonic resonance, thus reducing waveguide losses. Suppressed dissipation within the duration of the pump pulse is a hallmark of coherent dynamics. In addition, incoherent photo-induced effects occurring on the picosecond timescale (Δt > 1 ps) are also evident in the evolution of q1 in Fig. 3b.

We proceed with the inquiry into the non-equilibrium waveguide dispersion by varying the probe photon energy at fixed pump-probe time delay (Fig. 3c–e). We witness anomalies in the dispersion of δq1 occurring on the femtosecond timescale when the probe energy is in the vicinity of the A-exciton (Fig. 3e). In order to disentangle various transient mechanisms, we have chosen to describe the differential wavevector data with a model described by an effective value of the in-plane component of the dielectric tensor, εab, constructed from a series of Lorentzian oscillators (methods). The validity of this approach is attested by an accurate account of the equilibrium spectra of WSe2 (Fig. 2). To extract changes of the effective value of εab, we weakly perturbed the oscillators parameters and obtained good agreement with the pump-probe data. The above analysis reveals that features in the differential dispersion near the A-exciton are caused by two concomitant effects: (i) a 7 meV blueshift of the A-exciton observed only at Δt = 0; and (ii) bleaching of the A-exciton, defined as spectral broadening and/or a decrease in the oscillator strength (see Fig. 3d). Trend (i) recovers within 1 ps, consistent with the dynamics of suppressed dissipation (Fig. 3a); we therefore conclude that the transient blueshift of the A-exciton resonance is due to a coherent light-induced process22. Trend (ii) persists on a much longer timescale and is, therefore, attributed to incoherent exciton dynamics. The dispersion results in Fig. 3 implicate the A-exciton in the observed photo-induced transformations. An overall decrease of the static dielectric function, $$\varepsilon _{{\it{stat}}}^ \ast$$, which stems from contributions of high-energy excitons outside of our frequency range and also from the response of a photo-excited electron-hole plasma (EHP) is also identified.

## Discussion

The coherent 7 meV blueshift of the A-exciton admits the interpretation within the framework of the optical Stark effect. The optical Stark shift implies that eigenstates of the system are transiently modified under red-detuned photoexcitation. The Floquet formalism is a customary tool for describing the eigenstates of out-of-equilibrium time-periodic quantum systems10,11,12,22,23. The latter formalism predicts a coherent blueshift of the excitonic resonance, in accord with spectral features we observe in Fig. 3e with zero time-delay between the pump and probe pulses (Table 1; methods). The eigenstates of the hybrid light-matter system were, therefore, found to govern the complex wavevector of the packet of probe photons.

To account for the incoherent response (ii) we consider plausible roles of optically generated carriers. A substantial photo-excited carrier density is independently implied by our observation of transient spectral weight in the mid-infrared (see Supplementary Fig. 9), which may be produced by bound excitons and/or a Drude response from itinerant carriers. Bound excitons cannot account for the observed pump induced change of the static dielectric function, $$\varepsilon _{{\it{stat}}}^ \ast$$, which is caused by optical transitions at higher energies than those investigated in our work. The net carrier density extracted from time-resolved mid-infrared spectroscopy (see Supplementary Fig. 9) is approximately ne = 1019 cm−3, which is sufficient to reach the Mott transition threshold13 provided that a significant fraction of ne is comprised of an optically generated EHP (see Supplementary Note 9). At the Mott threshold, the EHP screens the Coulomb interaction that binds excitons, which causes excitons to dissociate. As the EHP density approaches the Mott threshold, elastic scattering of excitons leads to spectral broadening of the excitonic transitions while screening of the Coulomb interaction suppresses the excitons’ oscillator strengths9,13,24,25,26. Both of these effects are manifest in trend (ii) above. The same physical mechanisms that produce trend (ii) are likely to influence high-energy excitons outside of our frequency range, which would impact $$\varepsilon _{{\it{stat}}}^ \ast$$. We comment that photoexcitation is also likely to cause both Joule and electronic heating of the WSe2 crystal, which results in spectral broadening of the A-exciton resonance27 and may also lead to a decrease of $$\varepsilon _{{\it{stat}}}^ \ast$$. Heating, therefore, may partially contribute to our observation of trend (ii), but is unrelated to trend (i) occurring on much faster time scales.

In conclusion, transient nano-imaging of waveguide modes allowed us to quantify photo-induced changes of optical properties of WSe2 with sub-ps temporal resolution. The procedures detailed here are expected to remain valid provided that the effective optical constants do not change appreciably during the course of waveguide propagation. If the latter condition is not satisfied then uncommon phenomena, including light amplification without population inversion, could be observed28. Our analysis reveals that the magnitude of the pump-induced changes of the effective in-plane component of the dielectric function, δε1,ab(E = 1.45 eV) reaches 1.3 and therefore exceeds 5% of the value of ε1,ab at equilibrium (Fig. 1). Substantial photo-induced changes of the phase velocity were also observed on WS2 indicating that the observed effects are likely generic within vdW semiconductors (see Supplementary Note 13). Our observations, furthermore, suggest the possibility to substantially tune the optical birefringence of vdW semiconductors on-demand (see Supplementary Note 10). The spectral analysis of δq1(E) presented in Fig. 3, which are recast as δε1,ab(E) in Supplementary Fig. 10, indicate that the observed changes of the dielectric function are dominated by photo-induced perturbation of the A-exciton resonance. Both coherent and incoherent light-induced processes were revealed through systematic study of the dynamics of the complex wavevector of the elliptic waveguide modes. Our work expands on pioneering efforts to monitor ultrafast exciton dynamics with tr-SNOM8 and paves the way to utilize waveguide modes as a quantitative spectroscopic tool to interrogate light-induced phases at the nanoscale. The inherent spatial resolution of this pump-probe method may be suitable for imaging edge modes and edge effects in topologically nontrivial materials29.

## Methods

### Experimental set-up

For nano-optical imaging experiments, we used a scattering-type scanning near-field optical microscope (s-SNOM, Neaspec). The atomic force microscope (AFM) operates in tapping-mode with a frequency of about 70 kHz and a tapping amplitude of approximately 50 nm. The time-resolved Pseudoheterodyne technique is used to extract the amplitude (S) and phase (ψ) of the near-field signal14. In this work we discussed the amplitude, S. The additive background contribution was strongly attenuated by considering only information modulated at the third harmonic of the tapping frequency of the AFM tip. The pump and probe channels were derived from a 20 W, 1030 nm Yb:kGW amplified laser source operating at a repetition rate of RR = 750 kHz (Pharos, Light Conversion). The intense laser pulse was converted to two separate, pump and probe channels of visible radiation by employing two optical parametric amplifiers (OPAs). To facilitate self-referencing as described below, and in detail within Supplementary Note 1 and ref. 14, the pump pulse operates at half of the repetition rate, RR/2 which is approximately 375 kHz. The broadband pulses were sent through bandpass filters (approximately 15-20 meV FWHM) before they were delivered to the Neasepc microscope (see Supplementary Note 12). For all data displayed in the main text the center energy of the pump was fixed at approximately 1.56 eV.

We collect the self-referenced and time-resolved near-field amplitude14 (see Supplementary Note 1). Specifically, we acquire the near-field amplitude in the steady-state (Sr) as well as in the photo-excited state (Sp) ‘simultaneously’ at each pixel using homebuilt software as described in Supplementary Note 1 and in ref. 14. The differential change in the near-field amplitude is calculated as ΔS = (Sp-Sr)/<Sr > where <Sr > is the mean value of the reference near-field amplitude in the interior of WSe2. The quantity ΔS is used to extract differential changes in the complex wavevector as we describe in the Supplementary Notes 1, 2, 4 and 5. The samples studied here are WSe2 planar waveguides. The high quality WSe2 crystals were synthesized by self-flux method, then mechanically exfoliated onto an SiO2/Si substrate30.

### Model for the dielectric function of WSe2

The dielectric tensor of WSe2 determines the complex wavevector of waveguide modes that propagate within these crystals as described in Supplementary Note 3 and in refs. 3,4. A Lorentz model is used to approximately describe the in-plane component of the dielectric function of WSe2:

$$\varepsilon _{{\mathrm{ab}}} \cong \varepsilon _{{\mathrm{stat}}}^ \ast - {\updelta}\varepsilon _{{\mathrm{stat}}} + \frac{{f_1(1 - {\updelta}N \cdot C)}}{{(E_1 + {\updelta}E)^2 - E^2 - {\mathrm{i}}E\gamma _1(1 + {\updelta}N \cdot (1 - C))}}$$
(1)

In this expression the parameters f1,γ1, E1 represent, respectively, the oscillator strength, spectral breadth and center frequency of the A-exciton respectively at equilibrium. The parameter $$\varepsilon _{{\it{stat}}}^ \ast$$ represents the static dielectric function, which absorbs contributions from high-energy (B, C, D, etc.) excitons as well as contributions from interband optical transitions (see Supplementary Note 8). The parameters are given by f1 = 1.2 eV2, γ1 = 106 meV, E1 = 1.612 eV, and $$\varepsilon _{{\it{stat}}}^ \ast$$ = 22.5 + 2i as described in Supplementary Note 8 and describe the in-plane component of the dielectric function in the steady state. The remaining parameters in Eq. (1) represent differential changes to the dielectric function in the photo-excited situation. The parameter is δεstat represents a change in the static dielectric function. The parameter δE represents a shift of the center frequency of the A-excitons while δN represents a change in the oscillator strength and/or spectral breadth. Finally, C determines the relative value of the change in oscillator strength vs. a change of the spectral breadth. An arbitrary choice of this parameter on the interval [0,1] provides an adequate fit to our experimental data. Values for these parameters, that are extracted from the measurements reported in Fig. 3, are given in Table 1. The out-of-plane dielectric function is dispersion-less within the experimentally investigated range of probe energies. Thickness dependence of the complex wavevector in the steady state (see Supplementary Note 11) are used to extract the out-of-plane component of the dielectric function given by a constant value of εc = 8 that is assumed to be unchanged by photoexcitation. We emphasize that the out-of-plane optical polarizability exhibits negligible dispersion in the steady state31. Thus, possible pump-induced changes of εc would have a negligible impact the extracted values of δN or δE, which give rise to the dispersive trends observed in Fig. 3e.

## Data availability

The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.

## References

1. 1.

Low, T. et al. Polaritons in layered two-dimensional materials. Nat. Mater. 16, 182–194 (2017).

2. 2.

Basov D. N., Fogler M. M., García de Abajo F. J. Polaritons in van der Waals materials. Science 354, aag1992 (2016).

3. 3.

Hu, F. et al. Imaging exciton–polariton transport in MoSe2 waveguides. Nat. Photonics 11, 356 (2017).

4. 4.

Hu, D. et al. Probing optical anisotropy of nanometer-thin van der waals microcrystals by near-field imaging. Nat. Commun. 8, 1471 (2017).

5. 5.

Hu, D. et al. Tunable modal birefringence in a low-loss van der Waals waveguide. Adv. Mater. 31, 1807788 (2019).

6. 6.

Mak, K. F. & Shan, J. Photonics and optoelectronics of 2D semiconductor transition metal dichalcogenides. Nat. Photonics 10, 216 (2016).

7. 7.

Wang, G. et al. Colloquium: excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 90, 021001 (2018).

8. 8.

Mrejen, M., Yadgarov, L., Levanon, A. & Suchowski, H. Transient exciton-polariton dynamics in WSe2 by ultrafast near-field imaging. Sci. Adv. 5, eaat9618 (2019).

9. 9.

Chernikov, A., Ruppert, C., Hill, H. M., Rigosi, A. F. & Heinz, T. F. Population inversion and giant bandgap renormalization in atomically thin WS2 layers. Nat. Photonics 9, 466 (2015).

10. 10.

Sie, E. J. et al. Valley-selective optical Stark effect in monolayer WS2. Nat. Mater. 14, 290 (2014).

11. 11.

Ye, Z., Sun, D. & Heinz, T. F. Optical manipulation of valley pseudospin. Nat. Phys. 13, 26 (2016).

12. 12.

Yong, C.-K. et al. Biexcitonic optical Stark effects in monolayer molybdenum diselenide. Nat. Phys. 14, 1092–1096 (2018).

13. 13.

Wang, J. et al. Optical generation of high carrier densities in 2D semiconductor heterobilayers. Sci. Adv. 5, eaax0145 (2019).

14. 14.

Sternbach, A. J. et al. Artifact free time resolved near-field spectroscopy. Opt. Express 25, 28589–28611 (2017).

15. 15.

Eisele, M. et al. Ultrafast multi-terahertz nano-spectroscopy with sub-cycle temporal resolution. Nat. Photonics 8, 841 (2014).

16. 16.

Charnukha, A. et al. Ultrafast nonlocal collective dynamics of Kane plasmon-polaritons in a narrow-gap semiconductor. Sci. Adv. 5, eaau9956 (2019).

17. 17.

Huber, M. A. et al. Femtosecond photo-switching of interface polaritons in black phosphorus heterostructures. Nat. Nanotechnol. 12, 207–211 (2017).

18. 18.

Dönges, S. A. et al. Ultrafast nanoimaging of the photoinduced phase transition dynamics in VO2. Nano Lett. 16, 3029–3035 (2016).

19. 19.

Atkin, J. M., Berweger, S., Jones, A. C. & Raschke, M. B. Nano-optical imaging and spectroscopy of order, phases, and domains in complex solids. Adv. Phys. 61, 745–842 (2012).

20. 20.

McLeod, A. S. et al. Model for quantitative tip-enhanced spectroscopy and the extraction of nanoscale-resolved optical constants. Phys. Rev. B 90, 085136 (2014).

21. 21.

Li, Y. et al. Measurement of the optical dielectric function of monolayer transition-metal dichalcogenides: MoS2, MoSe2, WS2, and WSe2. Phys. Rev. B 90, 205422 (2014).

22. 22.

Giovannini, U. D. & Hübener, H. Floquet analysis of excitations in materials. J. Phys.: Mater. 3, 012001 (2019).

23. 23.

Claassen, M., Jia, C., Moritz, B. & Devereaux, T. P. All-optical materials design of chiral edge modes in transition-metal dichalcogenides. Nat. Commun. 7, 13074 (2016).

24. 24.

Chernikov, A. et al. Electrical tuning of exciton binding energies in monolayer WS2. Phys. Rev. Lett. 115, 126802 (2015).

25. 25.

Steinhoff, A., Rösner, M., Jahnke, F., Wehling, T. O. & Gies, C. Influence of excited carriers on the optical and electronic properties of MoS2. Nano Lett. 14, 3743–3748 (2014).

26. 26.

Chakraborty, B. et al. Control of strong light–matter interaction in monolayer WS2 through electric field gating. Nano Lett. 18, 6455–6460 (2018).

27. 27.

Raja, A. et al. Enhancement of exciton–phonon scattering from monolayer to bilayer WS2. Nano Lett. 18, 6135–6143 (2018).

28. 28.

Sun, Z., Basov, D. N. & Fogler, M. M. Adiabatic amplification of plasmons and demons in 2D systems. Phys. Rev. Lett. 117, 076805 (2016).

29. 29.

McIver, J. W. et al. Light-induced anomalous Hall effect in graphene. Nat. Phys. 16, 38–41 (2020).

30. 30.

Edelberg, D. et al. Approaching the intrinsic limit in transition metal diselenides via point defect control. Nano Lett. 19, 4371–4379 (2019).

31. 31.

Haastrup, S. et al. The computational 2D materials database: high-throughput modeling and discovery of atomically thin crystals. 2D Mater. 5, 042002 (2018).

## Acknowledgements

This work is supported as part of Programmable Quantum Materials, an Energy Frontier Research Center funded by the U.S. Department of Energy (DOE), Office of Science, Basic Energy Sciences (BES), under award DE-SC0019443. D.N.B. is the Vannevar Bush Faculty Fellow (N00014-19-1-2630). We acknowledge support from the European Research Council (ERC-2015-AdG694097) and the Cluster of Excellence ‘Advanced Imaging of Matter’ (AIM). Support by the Flatiron Institute, a division of the Simons Foundation, is acknowledged. S. L. acknowledges support from the Alexander von Humboldt foundation.

## Author information

Authors

### Contributions

A.J.S. and S.H.C., conducted the nanoscale infrared measurements and sample characterization. A.J.S., P.K., R.D.A. and D.N.B. contributed to the development of scientific instrumentation used in this study. S.H.C., D.R., B.K. and J.H. designed and created samples and devices used in this work. S.L., H.H., U.D.G., L.X., Z.S., A.J.M., M.M.F. and A.R. provided theoretical support. A.J.S., N.S. and N.Y. performed far-field optical characterizations. Y.S., L.X., G.X.N., P.J.S., M.L. and X.Y.Z. helped to interpret the results. D.N.B. supervised the project. A.J.S., S.L., A.R. and D.N.B. co-wrote the manuscript with input from all co-authors.

### Corresponding author

Correspondence to Aaron J. Sternbach.

## Ethics declarations

### Competing interests

The authors declare no competing interests.

Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer review reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

Reprints and Permissions

Sternbach, A.J., Latini, S., Chae, S. et al. Femtosecond exciton dynamics in WSe2 optical waveguides. Nat Commun 11, 3567 (2020). https://doi.org/10.1038/s41467-020-17335-w

• Accepted:

• Published:

• ### Programmable hyperbolic polaritons in van der Waals semiconductors

• A. J. Sternbach
• , S. H. Chae
• , S. Latini
• , A. A. Rikhter
• , Y. Shao
• , B. Li
• , D. Rhodes
• , B. Kim
• , P. J. Schuck
• , X. Xu
• , X.-Y. Zhu
• , R. D. Averitt
• , J. Hone
• , M. M. Fogler
• , A. Rubio
•  & D. N. Basov

Science (2021)

• ### Nanoscale‐Confined Terahertz Polaritons in a van der Waals Crystal

• Thales V. A. G. Oliveira
• , Tobias Nörenberg
• , Gonzalo Álvarez‐Pérez
• , Lukas Wehmeier
• , Javier Taboada‐Gutiérrez
• , Maximilian Obst
• , Franz Hempel
• , Eduardo J. H. Lee
• , J. Michael Klopf
• , Ion Errea
• , Alexey Y. Nikitin
• , Susanne C. Kehr
• , Pablo Alonso‐González
•  & Lukas M. Eng

• ### Quantitative Nanoinfrared Spectroscopy of Anisotropic van der Waals Materials

• Francesco L. Ruta
• , Aaron J. Sternbach
• , Adji B. Dieng
• , Alexander S. McLeod
•  & D. N. Basov

Nano Letters (2020)