Selective NMR observation of the SEI–metal interface by dynamic nuclear polarisation from lithium metal


While lithium metal represents the ultimate high-energy-density battery anode material, its use is limited by dendrite formation and associated safety risks, motivating studies of the solid–electrolyte interphase layer that forms on the lithium, which is key in controlling lithium metal deposition. Dynamic nuclear polarisation enhanced NMR can provide important structural information; however, typical exogenous dynamic nuclear polarisation experiments, in which organic radicals are added to the sample, require cryogenic sample cooling and are not selective for the interface between the metal and the solid–electrolyte interphase. Here we instead exploit the conduction electrons of lithium metal to achieve an order of magnitude hyperpolarisation at room temperature. We enhance the 7Li, 1H and 19F NMR spectra of solid–electrolyte interphase species selectively, revealing their chemical nature and spatial distribution. These experiments pave the way for more ambitious room temperature in situ dynamic nuclear polarisation studies of batteries and the selective enhancement of metal–solid interfaces in a wider range of systems.


The development of longer lasting, higher energy density and cheaper rechargeable batteries represents a major technological challenge1 in both the shift from gasoline-powered to electric vehicles and the increased use of typically intermittent renewable energy sources2. One strategy to increase energy density is to use lithium metal in place of the commercial anode graphite, in a “lithium metal battery” (LMB)3,4. All-solid-state batteries (ASSBs), which replace the flammable organic liquid electrolyte of traditional lithium ion batteries (LIBs) with a safer solid alternative, also require a lithium metal anode if they are to compete with the energy density of LIBs5. Similarly, lithium air and sulphur batteries generally use a lithium metal anode6. A commercially viable, room temperature, rechargeable battery with a lithium metal anode (LMB or ASSB) has yet to be developed, however, due to difficulties related to plating and stripping lithium and the low Coulombic efficiency caused by reaction of lithium metal with the electrolyte upon cycling1,3,7. Mossy and dendritic lithium structures form during plating, which can cause short circuits and severe safety concerns. Lithium deposits can also form on the graphite anode of traditional LIBs upon fast charging, particularly at low temperatures8.

While lithium deposition at high rates is largely dictated by the mobility of ions in the electrolyte, Li microstructures are still formed at low rates, in processes that are controlled by the nature of the passivating layer that grows on the lithium metal4,9,10. This layer, the solid electrolyte interphase (SEI), is formed by degradation of the electrolyte on contact with lithium metal, resulting in a highly heterogeneous mixed organic/inorganic film11. Non-uniform Li+ transport across the SEI creates instabilities and nucleation points that determine the extent and nature of the lithium microstructure formation12,13.

The SEI has been studied by a range of techniques, including X-ray photoelectron spectroscopy (XPS)14,15 and time-of-flight secondary-ion mass spectrometry (TOF-SIMS)16; however, the nature and distribution of chemical components in the SEI, the Li+ mobility within them, and their relationship to dendrite formation, are still relatively unclear. Significant strides have also been made to study the SEI with NMR spectroscopy17,18, however NMR can suffer from issues of sensitivity and selectivity.

Dynamic nuclear polarisation (DNP) is a promising approach that exploits the ~103 times greater gyromagnetic ratio of paramagnetic electrons to hyperpolarise nuclear spins and hence increase the signal in NMR experiments, by irradiating the electron spin resonance (ESR) transitions with microwaves19,20,21. The SEI on reduced graphene oxide and silicon anodes has been studied by exogenous DNP22,23,24, whereby a solution of organic radicals is added to the system before cooling to 100 K or below, slowing the electron relaxation times (T1e) of the radicals so that the ESR transition can be more easily saturated20,25. This approach has several limitations: (i) addition of an organic radical solution may alter the nature of SEI and/or introduce impurities to the system; (ii) the organic radicals are not stable over the large voltage window that most batteries operate in; (iii) the organic radicals are external to the SEI so cannot be readily used to probe the buried SEI–metal interface; (iv) exogenous DNP is not selective to the SEI and can also enhance the signals from any impurities in the system; and (v) low temperature experiments cannot readily be coupled with in situ electrochemical cycling or used to study Li+ dynamics. Endogenous DNP has also been used to investigate bulk battery anodes doped with paramagnetic metal ions26, but this is not immediately applicable to the study of interfacial structures.

Intriguingly, the first DNP experiments were performed on lithium metal more than 60 years ago at room temperature27 and yet this approach is no longer used. Although the T1e of lithium metal is short (~10 ns, depending on the purity28, c.f. >10 μs for commonly used organic radicals at 100 K20), the relaxation is largely temperature independent28, removing the requirement of cryogenic temperatures. Here, instead of localised radicals, the Pauli paramagnetism of the metallic electrons is the source of polarisation. In the absence of an applied magnetic field, the partially filled up and down electron spin-bands of a metal are degenerate (Fig. 1a); in an applied magnetic field the energies of these bands are shifted in opposite direction, but they maintain a common Fermi level—a net unpaired spin density results which augments the applied field (Fig. 1b). This Pauli paramagnetism can be exploited to enhance nuclear magnetisation via the Overhauser effect29: on irradiation of the conduction ESR (CESR) transition, the populations of the spin-bands are (partially) equalised (Fig. 1c); the electrons can then cross relax with 7Li nuclei in the metal, thereby inducing nuclear hyperpolarisation (see Supplementary Fig. 1). We therefore asked the questions: Could room temperature Li-metal DNP be achieved at high magnetic fields with the much higher power microwave sources now available? And could saturation of the electron spins be used to polarize nearby diamagnetic nuclei? LMBs are well-suited for this study due to the high Li metal surface areas formed on lithium plating.

Fig. 1: The mechanism of Li metal DNP.

ac The conduction electron spin-bands of a metal, plotted against energy (E): a in the absence of a magnetic field; b in an applied magnetic field (B0), resulting in a Pauli paramagnetic moment (M); and c after microwave (μw) irradiation at the CESR frequency. Note that the arrows for each spin-band represent the electron magnetic moment, not the electron spin which is opposite in sign. d Schematic of hyperpolarisation of lithium metal on application of microwaves (DNP, black dashed arrows) and subsequent spin diffusion in the heterogenous mixed organic/inorganic SEI (grey dashed arrows).

This paper reports the significant hyperpolarisation of the room temperature 7Li NMR signal of cycled lithium metal anodes under magic angle spinning (MAS) by Overhauser DNP. The hyperpolarisation is then harnessed to investigate the interface between Li metal and the SEI (Fig. 1d). Selective enhancement of the SEI is observed in the diamagnetic 7Li, 1H and 19F NMR spectra, and the relative DNP enhancements allow the proximity of different species to the metal surface to be inferred. Double resonance experiments—7Li → 1H cross polarisation (CP), 7Li → 19F CP, and 7Li{19F} rotational echo double resonance (REDOR30)—identify further components of the SEI such as polymeric organic species and LiF. The chemical composition and structure of the SEI is highly dependent on the electrolyte system used, so a comparison is made between samples prepared using electrolytes with and without the common additive fluoroethylene carbonate (FEC), which has been shown to yield a more uniform lithium deposition and improved electrochemical performance31,32,33,34,35,36. Finally, experiments on static samples are used to evaluate the feasibility of in situ experiments on working batteries.


Lithium metal DNP

Figure 2a shows the room temperature (14.1 T) 7Li MAS NMR spectrum of microstructural lithium (sample A), with and without 15.6 W of microwave irradiation. The large shift of the Li metal signal (>200 ppm) is due to the Fermi contact interaction with the Pauli paramagnetic moment of the conduction electrons (M, Fig. 1b), a so-called Knight shift37. Two clear observations can be made: first, a noticeable enhancement of the lithium metal signal of 7.9 is seen based on the peak area (εarea); second, microwave irradiation results in a spreading of the NMR signal to lower frequencies, so that the enhancement, based on the peak height is lower (εpeak = 4.9). The latter is ascribed to partial saturation of the CESR transition which reduces the moment (Fig. 1c) and hence the Knight shift; the greater the microwave power, the greater the saturation and the lower the observed shift (Supplementary Fig. 2). Early experiments also demonstrated this effect at 0.34 T, where the Knight shift was reduced by ~75% due to the much greater saturation of the CESR transition at the lower field38. The distribution of frequencies for the resonance is tentatively ascribed to differences in the degree of CESR saturation in the sample resulting from inhomogeneities of both the sample and the microwave field.

Fig. 2: DNP enhancement of Li metal.

a 7Li NMR spectrum of microstructural lithium metal (sample A), with and without 15.6 W of microwave irradiation at 395.29 GHz (μw ON/OFF), recorded at 14.1045 T, 12.5 kHz MAS and a sample temperature of ~300 K, using a Hahn echo pulse sequence, a recycle delay of 0.25 s and 80 scans. Spinning sidebands are marked with an asterisk. b The enhancement of the integrated intensity and peak intensity as a function of the B0 field (sample B), measured at 100 K.

To determine the effect of temperature on the DNP enhancement, the experiment was repeated at 100 K, yielding an enhancement of εarea = 7.3 (Supplementary Fig. 3), i.e., of comparable magnitude. A field sweep performed on a second sample (B) confirms the DNP mechanism (Fig. 2b); a single, sharply peaked positive enhancement is observed at the Li CESR frequency, indicating an Overhauser mechanism for which zero-quantum cross-relaxation dominates, given that the gyromagnetic ratio of 7Li is positive20. The electron g-factor corresponding to the peak enhancement is 2.0024 ± 0.0002, compared to 2.0026 from the peak absorbance in the X band ESR spectrum (Supplementary Fig. 4). A narrow sweep at room temperature for a further sample (G) reveals the same sharp feature (Supplementary Fig. 5) at the same field, as expected, since the position of the CESR resonance is temperature independent (Supplementary Fig. 4). Both the field at which the optimal enhancement is achieved (Supplementary Figs. 6 and 7) and the peak absorbance of the ESR spectrum (Supplementary Fig. 8) depend slightly on the applied microwave power, which may be due to partial saturation effects39. There is no evidence of a solid effect, which would occur at magnetic fields of ±8.3 mT from the CESR resonance.

Further experiments performed at a lower field strength of 9.4 T with 44 W of gyrotron irradiation on a third sample (C), yielded higher enhancements of εarea = 18 at room temperature and εarea = 27 at 100 K (Supplementary Fig. 10), the higher enhancements being ascribed to a combination of the higher microwave power achievable, the lower field, and variations between samples. Moreover, even with a lower power klystron source (~2.7 W), enhancements could be achieved at this field on this sample of εarea = 7.6 at room temperature and εarea = 11 at 100 K (Supplementary Fig. 11), potentially further reducing the technological requirements and cost of running these experiments.

The temperature dependence of the enhancement appears to depend on a number of factors including the magnetic field (see Supplementary Fig. 9), and will also be affected by the temperature dependence of the T1n and T1e relaxation constants, and hence by the presence of paramagnetic impurities in the sample. For example, the greater enhancement sometimes seen at lower temperatures is at least in part due to differences in the 7Li spin lattice relaxation times (T1) of the metal, which was measured as 0.36 s at 100 K compared to 0.14 s at room temperature (for sample G, Supplementary Table 1). These phenomena are currently under further investigation, but qualitatively similar enhancements are nevertheless achieved between 100 K and room temperature.

The metal–SEI interface

Having demonstrated Overhauser DNP enhancement of the lithium metal signal at high magnetic fields, experiments were then performed to determine if this hyperpolarisation can be exploited to probe the interface between the SEI and lithium metal. Two representative samples were chosen, one prepared with a standard electrolyte LP30, and the second with a 1:10 volume ratio of the additive FEC in LP30 (samples D and E, Fig. 3). Two further samples prepared with the same electrolytes corroborate the results (samples F and G, Supplementary Fig. 13, Supplementary Tables 3 and 4). The metallic 7Li signal is again enhanced for all samples (Supplementary Fig. 12), although there is a spread of enhancements (εarea = 6–13) that does not correlate with the electrolyte used and is ascribed to factors such as variations in the T1e and the surface-to-volume ratio. Importantly, there is still sufficient hyperpolarisation in all cases to investigate the SEI.

Fig. 3: Selective enhancement of the SEI by Li metal DNP.

Diamagnetic 7Li (ad), 1H (eh), and 19F (il) NMR spectra of lithium microstructures produced by cycling with the LP30 (top half, sample D) and LP30 + FEC (bottom half, sample E) electrolytes, recorded with and without 15.6 W of microwave irradiation (μw ON/OFF). (b) and (d) are deconvolutions of the μw ON spectra in (a) and (c), respectively; see Supplementary Figs. 15, 16 and Supplementary Table 2. All spectra were recorded at 12.5 kHz MAS, 14.1 T and room temperature, unless otherwise stated. Spinning sidebands are marked with asterisks. The direct spectra were recorded with a Hahn echo pulse sequence and the CP spectra were recorded with the 7Li carrier at 0 ppm and contact times of 1 and 0.1 ms for 7Li → 1H and 7Li → 19F respectively. For the direct 1H and 19F experiments, the difference between the spectra recorded with and without microwave irradiation is also shown. Recycle delays and experimental times are given in Supplementary Table 5.

Firstly, microwave irradiation of the Li CESR resonance produces clear enhancements in the 7Li diamagnetic signals from the SEI that surprisingly are of the same order as that seen for the metal itself (Fig. 3a–d); these must correspond to lithium species within the SEI, such as Li2CO3 and LiOH40,41,42. The sharp component in the LP30 7Li spectrum at −0.8 ppm is not enhanced and is therefore ascribed to Li+ in the residual electrolyte, as the electrodes were not rinsed after disassembly.

The sample formed with the LP30 + FEC electrolyte also exhibits a signal at −0.9 ppm, but it is broader than for the LP30 sample and is enhanced by microwave irradiation (Fig. 3c, d). This suggests that there is residual electrolyte closer to the metal surface, perhaps due to a thinner SEI, or that there is more effective spin diffusion through the SEI due to a greater density of 7Li spins. A minor signal is seen at −0.8 ppm with a large enhancement of 10.3, indicating that the corresponding species is close to the lithium metal surface; on the basis of the shift it is tentatively assigned to LiF arising from reduction of FEC35,36 and decomposition of the LiPF6 salt43,44. Similar results are observed at 105 K, but with significantly broader resonances (Supplementary Fig. 14).

Irradiation of the CESR transition is also found to enhance the signal of other nearby nuclei, via mechanisms that will be discussed below. This allows the organic compounds that form a key part of the SEI to be identified without rinsing the electrodes to remove the excess electrolyte and salts that can obscure conventional NMR spectra, a process which may lead to the partial dissolution of the SEI and changes in structure and composition45. 1H NMR spectra (Fig. 3e, g) were recorded with and without microwave irradiation at 240 K, because microwave irradiation at room temperature can cause melting of ethylene carbonate (see Supplementary Note 2). Although the enhancements are not large, the intensity clearly increases on application of microwaves; furthermore, the spectra are not enhanced uniformly, so the signals arising from the SEI can be distinguished from the significant background intensity.

The 1H spectra of the LP30 sample (Fig. 3e, deconvolution in Supplementary Fig. 17 and Supplementary Table 6), show the greatest enhancement for the 3.8 ppm signal, which can only be seen with microwave irradiation, and is assigned to poly-ethylene oxide (PEO)-like species formed through the decomposition of EC molecules; these have been shown to be the major species present in the SEI formed on silicon anodes with an LP30 electrolyte23,45. The sharp resonance at 4.7 ppm, which exhibits a comparably large enhancement of ~2, is ascribed to more mobile EC molecules trapped within pores in the SEI16, and/or small organic lithium carbonates such as lithium ethylene dicarbonate (LEDC) that are sufficiently close to the metal surface to be enhanced. The same sharp signals are not observed for the LP30 + FEC sample, which suggests that the SEI is less porous to the electrolyte and/or that these organics are further from the Li metal in this case. The broad unenhanced resonance centred at ~4.6 ppm is assigned to solid residual EC electrolyte, broadened by significant homonuclear dipolar coupling. The unenhanced signals at 0.1–0.2 and 7.2–7.3 ppm are impurities (most likely grease and an ammonium salt, respectively).

For the 1H spectra of the LP30 + FEC sample (Fig. 3e, deconvolution in Supplementary Fig. 18 and Supplementary Table 6), a noticeably broader signal at ~4.7 ppm is observed with an enhancement of 1.8, from more rigid organic polymers in the SEI such as poly-vinylene carbonate (poly-VC), produced by cross-linking of FEC degradation species; notably, no PEO signal is seen. This is consistent with previous studies on chemically reduced FEC35 and again with the SEI seen on silicon anodes23,24. The other signals at around 1–2 ppm, seen in both samples with minor enhancements, are ascribed to aliphatic groups, such as in lithium butylene dicarbonate (LBDC)-like species, which form from the reaction of more than one EC/FEC molecule at low potentials45.

To improve the sensitivity of the 1H spectra, 7Li → 1H CP experiments were performed which exploit the greater enhancement of the 7Li. The room temperature 7Li → 1H CP spectra (Fig. 3f, h) contain broad asymmetric signals for both samples, which are ascribed to polymeric species and organic carbonates coordinated to or nearby lithium ions23,45; these broad signals are obscured in the direct 1H spectra. The signal for the LP30 sample has a centre of mass of 2.5 ppm, whereas for the LP30 + FEC sample the centre of mass is at a higher shift of 3.0 ppm; this is consistent with the greater proportion of poly-VC species in the latter due to FEC decomposition. Both samples exhibit noticeable enhancements of around ε = 5, which is similar to the enhancements of the diamagnetic 7Li, and the species could also be reproducibly identified in the second set of samples (Supplementary Fig. 13f, h). The CP predominantly occurs from the diamagnetic lithium rather than the lithium metal nuclei, as demonstrated by performing experiments with 7Li carrier frequencies corresponding to either the metal or diamagnetic 7Li signals (Supplementary Fig. 19).

19F NMR spectra were acquired to improve the assignments of the species found at the metal–lithium interface. Only the signal from the PF6 anion (−72 ppm) can be observed in the direct 19F spectra for both samples (Fig. 3i, k); furthermore, this resonance is not enhanced upon microwave irradiation, indicating that the species is not close to the lithium metal, which supports the current understanding that the SEI is impermeable to PF611. For the FEC sample, the two signals at around −72 ppm (enlarged in Supplementary Fig. 20) are ascribed to PF6 species in different coordination environments; no signal from residual FEC is seen, presumably due to it having evaporated. While no LiF signal (−203 ppm) could be observed in the direct 19F NMR spectra for either sample, a clear signal was observed in the 7Li → 19F CP spectrum for the LP30 + FEC sample (Fig. 3l) with a large enhancement of ε ≈ 12. This is more than double the enhancement of the broad diamagnetic 7Li signal, which implies that LiF is closer to the metal–SEI interface than other lithium species on average. Again, the CP occurs predominantly from the diamagnetic lithium, rather than from the metal surface, as shown by varying the 7Li carrier frequency (Supplementary Fig. 21); however, the enhancement still demonstrates proximity to the metal, since only diamagnetic lithium near the metal surface can be hyperpolarised. The presence of LiF for the LP30 + FEC sample is also supported by 7Li{19F} REDOR experiments, which exhibit dephasing on 19F recoupling (Supplementary Fig. 22), although only for a minor component of the signal. There is a significant enhancement of the difference spectrum, εarea = 8 (Supplementary Fig. 23) providing further evidence that LiF in the SEI is close to the metal surface. No LiF is seen for the LP30 sample (D) in the 7Li → 19F CP or 7Li{19F} REDOR experiments (Fig. 3j and Supplementary Fig. 24), which is consistent with its formation from FEC reduction. LiF can also form without FEC32, and a weak LiF signal was observed for the second LP30 sample (F) in the 7Li → 19F CP spectrum (Supplementary Fig. 13j), but again significantly more LiF is present near the metal surface for the second LP30 + FEC sample (G, Supplementary Fig. 13l).

Mechanisms of metal and SEI hyperpolarisation

To explore the selectivity of lithium metal DNP to the metal–SEI interface, first the spatial dependence of the lithium metal enhancement should be considered, which depends on a number of factors. As lithium metal is a conductor, electromagnetic radiation is limited to the skin depth46; for microwave irradiation at 395 GHz, the skin depth is ~0.2 μm (see Supplementary Note 1). This would suggest that electrons are only saturated at the surface, in theory limiting the extent of enhancement. However, the paramagnetic electrons near the Fermi level also diffuse rapidly with kinetic energies corresponding to the Fermi energy. An electron retains its saturation on average for a time T2e, during which it diffuses a distance known as the spin depth, given by \(\sqrt {2DT_{2{\mathrm{e}}}}\)47; for lithium metal at room temperature, using the T1e extracted from the power saturation of ~30 ns (assuming T1e = T2e, Supplementary Fig. 25) and the electron diffusivity D = 21 cm2 s−1 48, this yields a spin depth of ~11 μm. Comparing this to the average diameter of the lithium dendrites, ~0.5 μm (see Supplementary Figs. 26 and 27), the electron saturation and hence lithium hyperpolarisation are expected to be uniform within the dendrites. The radiofrequency pulses used to record the 7Li NMR spectrum at 233 MHz have a skin depth of ~8 μm, so the microstructural lithium metal is uniformly observed.

Although the hyperpolarisation of the lithium metal is not surface selective on the length-scale of microstructural lithium, the enhancement of the metal–SEI interface is still selective since only the SEI, which is in contact with the metal, will be enhanced (Fig. 1d). Hyperpolarisation of diamagnetic 7Li in the SEI can occur either directly via the Overhauser DNP mechanism, if the nuclei are sufficiently close to interact with the conduction electrons, or via spin diffusion from the hyperpolarised 7Li metal; evidence of the latter can be seen from a two dimensional exchange (EXSY) spectrum (Supplementary Fig. 29), where cross peaks between the Li metal and diamagnetic Li signals are observed with a mixing time of 100 ms, indicating spin diffusion on this timescale. For both mechanisms, polarisation then propagates away from the metal surface through the diamagnetic 7Li nuclei in the SEI by spin diffusion and the selectivity to the SEI–metal interface is therefore determined by the spin diffusion rate and the DNP build-up time used. Propagation of polarisation by physical diffusion of Li in the SEI is another possibility; however, since similar enhancements of the diamagnetic signals are observed at room temperature and cryogenic temperatures (Supplementary Fig. 14 and Supplementary Table 2), this mechanism is unlikely to dominate.

For the direct 1H experiments, there are also two possible mechanisms via which the hyperpolarisation could occur. If there are 1H nuclei close to the metal surface, they could be hyperpolarised directly via the Overhauser DNP effect, and this hyperpolarisation could propagate through spin diffusion if there is a sufficient density of 1H spins. Alternatively, hyperpolarisation could, in principle, be induced by cross-relaxation with hyperpolarised diamagnetic 7Li via a nuclear Overhauser effect; experiments to test this proposal are underway. In either case, species closer to the metal surface (i.e., in the SEI) will experience a greater enhancement. The comparatively low direct 1H enhancements could be due to a low density of 1H nuclei in the immediate proximity of the metal surface, as this region is expected to be more inorganic-rich, and/or due to a relatively inefficient hyperpolarisation mechanism.

Static lithium metal DNP

Finally, although MAS experiments offer the best chemical resolution, it is extremely challenging to perform in situ electrochemical experiments under spinning conditions, and such experiments are necessary to study dynamic processes such as SEI formation and degradation in battery systems, as well as to detect transient species49. A MAS cell has recently been demonstrated50, but cycling was not performed in the NMR magnet and metal electrodes were not used. To test whether the methodologies presented here could be applicable to in situ studies, 7Li NMR spectra were recorded under static conditions at 9.4 T, with and without microwave irradiation (Fig. 4). The resonances are broader, but an appreciable enhancement of the metallic signal is still observed (εarea = 13, c.f. εarea = 18 under MAS, Supplementary Fig. 10a), as well as minor enhancement of the diamagnetic signal, particularly of the sharper component. Experiments to harness this enhanced polarisation to investigate other nuclei are in progress.

Fig. 4: Static DNP-enhanced NMR of microstructural lithium.

7Li NMR spectra of sample C, recorded with and without microwave irradiation at 263.7 GHz and 44 W, at 9.4 T and room temperature, using a Hahn echo pulse sequence, a 0.25 s recycle delay and 128 scans. Shown too are the enhancements by area of the different signals.


High-field room temperature Overhauser DNP of lithium metal has been demonstrated for samples of electrodeposited microstructural lithium metal, with enhancements of around an order of magnitude. The polarisation source is intrinsic to the system, the addition of potentially reactive radicals is not required, and hyperpolarisation is selectively achieved for the species of interest. The enhancement can also be increased at lower fields and with higher microwave powers. Notably, by removing the need for cryogenic temperatures, the technological requirement for performing such DNP experiments is significantly reduced.

The hyperpolarisation of the lithium metal has further been harnessed to selectively investigate the metal–SEI interface via the 7Li, 1H and 19F NMR spectra, specifically in this case to determine the effect of the FEC electrolyte additive. Selective enhancement of the 1H NMR spectra distinguishes the organic SEI components, showing that the addition of FEC to the electrolyte reduces the amount of trapped EC in the SEI and promotes the formation of poly-VC species at the expense of PEO-like species. The greater enhancement of the diamagnetic 7Li nuclei can be harnessed to increase the polarisation of 1H and 19F nuclei via CP, which reveals polymeric species and LiF in the SEI, respectively. The latter has a significantly higher concentration with the addition of FEC. Furthermore, the greater enhancement of the LiF 7Li → 19F CP signal relative to that of the overall diamagnetic 7Li signal provides compelling evidence that this inorganic species is closer on average to the lithium metal surface than other Li-containing species in the SEI. While there are many factors that affect the composition of the SEI, selective observation of the SEI via Overhauser DNP as demonstrated here will help to identify the critical factors for the formation of a stable, uniform, SEI which can minimise lithium dendrite growth in LMBs and other battery systems.

Furthermore, although resolution is reduced, preliminary experiments show that appreciable 7Li enhancements can still be achieved by Overhauser DNP under static conditions, which suggests that in situ experiments will be possible whereby DNP can be used to observe the species of interest selectively (e.g. dendritic lithium and/or the SEI), in a working (battery) system where the presence of other components such as the electrolyte would typically drown out such signals. This could allow for the study of SEI formation and growth, one of the fundamental open questions regarding the SEI11.

The enhancement afforded by Overhauser DNP of lithium metal could also be applied to investigate very small masses of lithium metal, such as the dendrites or deposits that can also form in commercial lithium-ion batteries due to heterogenous local current densities under fast-charging conditions8, as well as in lithium-metal solid-state batteries5: such dendrites are challenging to study due to their low concentrations, but understanding how and when they form is of great importance in preventing short-circuits. More generally, this technique allows buried/internal metal–diamagnetic solid–solid interfaces to be directly probed to reveal structural and physical information, even though NMR is typically a bulk technique. In principle, the Overhauser mechanism can operate for any metallic material, and the study of metal anodes for next-generation Na, K and Mg batteries could also be readily envisaged, and even graphitic and LiCoO2 electrodes, which are metallic for certain degrees of lithiation. Other applications in solid state chemistry and physics to examine buried metallic–diamagnetic interfaces can be readily imagined.


As described in more detail in the Supplementary Information (with a full list of samples A–G given in Supplementary Table 7), lithium metal was deposited onto either lithium disks (samples A, D–G) or copper disks (samples B, C) in coin cells with 75 μL of either 1 M LiPF6 in ethylene carbonate/dimethyl carbonate 1:1 vol (EC:DMC; Sigma Aldrich, battery grade), referred to as LP30 (samples B, C, D, F), or the same electrolyte with a 1:10 volume ratio of FEC (Sigma Aldrich, anhydrous), referred to as LP30 + FEC (samples A, E, G). After galvanostatic electrodeposition with current densities ranging from 0.033 to 1.25 mA cm−2, the coin cells were disassembled in an Ar atmosphere glovebox and the microstructures scraped off gently with a razorblade without rinsing. The sample was then diluted by ~5× by mass with KBr (previously dried at 200 °C for 24 h) to improve microwave penetration and allow the metallic samples to be more easily spun; this does not have a significant effect on the microstructural morphology (see SEM images, Supplementary Fig. 28). Finally, the sample was packed into a 3.2 mm outer (2.2 mm inner) diameter sapphire rotor.

The majority of the DNP NMR experiments were performed at the UK DNP MAS NMR Facility at the University of Nottingham, UK on a 14.1 T AVANCE III HD spectrometer with a 395 GHz gyrotron microwave source. Additional experiments were performed at Bruker Billerica, USA on a 9.4 T AVANCE III HD spectrometer with a 263.7 GHz gyrotron or a klystron operating at 264.6 GHz. In both cases, a 3.2 mm wide-bore probe was used. Details of the NMR experiments are given in the figure captions and the Supplementary Information. Enhancements, ε, are defined as the signal intensity or area with microwave irradiation, divided by that without.

Data availability

The raw and processed NMR data analysed in the current study are available in the Apollo University of Cambridge repository at


  1. 1.

    Goodenough, J. B., Abruna, H. D. & Buchanan, M. V. Basic Research Needs for Electrical Energy Storage. Report of the Basic Energy Sciences Workshop on Electrical Energy Storage, April 2–4 (2007).

  2. 2.

    Chu, S., Cui, Y. & Liu, N. The path towards sustainable energy. Nat. Mater. 16, 16–22 (2017).

    ADS  Google Scholar 

  3. 3.

    Wood, K. N., Noked, M. & Dasgupta, N. P. Lithium metal anodes: toward an improved understanding of coupled morphological, electrochemical, and mechanical behavior. ACS Energy Lett. 2, 664–672 (2017).

    CAS  Google Scholar 

  4. 4.

    Liu, B., Zhang, J.-G. & Xu, W. Advancing lithium metal batteries. Joule 2, 833–845 (2018).

    CAS  Google Scholar 

  5. 5.

    Manthiram, A., Yu, X. & Wang, S. Lithium battery chemistries enabled by solid-state electrolytes. Nat. Rev. Mater. 2, 16103 (2017).

    ADS  CAS  Google Scholar 

  6. 6.

    Bruce, P. G., Hardwick, L. J. & Abraham, K. M. Lithium-air and lithium-sulfur batteries. MRS Bull. 36, 506–512 (2011).

    CAS  Google Scholar 

  7. 7.

    Fang, C., Wang, X. & Meng, Y. S. Key issues hindering a practical lithium-metal anode. Trends Chem. 1, 152–158 (2019).

    Google Scholar 

  8. 8.

    Waldmann, T., Hogg, B.-I. & Wohlfahrt-Mehrens, M. Li plating as unwanted side reaction in commercial Li-ion cells – A review. J. Power Sources 384, 107–124 (2018).

    ADS  CAS  Google Scholar 

  9. 9.

    Chang, H. J. et al. Correlating microstructural lithium metal growth with electrolyte salt depletion in lithium batteries using 7Li MRI. J. Am. Chem. Soc. 137, 15209–15216 (2015).

    PubMed  CAS  Google Scholar 

  10. 10.

    Brissot, C., Rosso, M., Chazalviel, J.-N. & Lascaud, S. Dendritic growth mechanisms in lithium/polymer cells. J. Power Sources 81–82, 925–929 (1999).

    Google Scholar 

  11. 11.

    Peled, E. & Menkin, S. Review—SEI: Past, Present and Future. J. Electrochem. Soc. 164, A1703–A1719 (2017).

    CAS  Google Scholar 

  12. 12.

    Aurbach, D. Review of selected electrode–solution interactions which determine the performance of Li and Li ion batteries. J. Power Sources 89, 206–218 (2000).

    ADS  CAS  Google Scholar 

  13. 13.

    Yoon, G., Moon, S., Ceder, G. & Kang, K. Deposition and stripping behavior of lithium metal in electrochemical system: continuum mechanics study. Chem. Mater. 30, 6769–6776 (2018).

    CAS  Google Scholar 

  14. 14.

    Aurbach, D., Weissman, I., Schechter, A. & Cohen, H. X-ray photoelectron spectroscopy studies of lithium surfaces prepared in several important electrolyte solutions. A comparison with previous studies by Fourier transform infrared spectroscopy. Langmuir 12, 3991–4007 (1996).

    CAS  Google Scholar 

  15. 15.

    Xu, C. et al. Improved performance of the silicon anode for Li-ion batteries: understanding the surface modification mechanism of fluoroethylene carbonate as an effective electrolyte additive. Chem. Mater. 27, 2591–2599 (2015).

    CAS  Google Scholar 

  16. 16.

    Lu, P. & Harris, S. J. Lithium transport within the solid electrolyte interphase. Electrochem. Commun. 13, 1035–1037 (2011).

    CAS  Google Scholar 

  17. 17.

    Haber, S. & Leskes, M. What can we learn from solid state NMR on the electrode–electrolyte interface? Adv. Mater. 30, e1706496 (2018).

  18. 18.

    Pecher, O., Carretero-González, J., Griffith, K. J. & Grey, C. P. Materials’ methods: NMR in battery research. Chem. Mater. 29, 213–242 (2017).

    CAS  Google Scholar 

  19. 19.

    Becerra, L. R. et al. A spectrometer for dynamic nuclear polarization and electron paramagnetic resonance at high frequencies. J. Magn. Reson. Ser. A 117, 28–40 (1995).

    ADS  CAS  Google Scholar 

  20. 20.

    Thankamony, A. S. L., Wittmann, J. J., Kaushik, M. & Corzilius, B. Dynamic nuclear polarization for sensitivity enhancement in modern solid-state NMR. Prog. Nucl. Magn. Reson. Spectrosc. 102–103, 120–195 (2017).

    Google Scholar 

  21. 21.

    Kemp, T. F. et al. Dynamic nuclear polarization enhanced NMR at 187 GHz/284 MHz using an extended interaction Klystron amplifier. J. Magn. Reson. 265, 77–82 (2016).

    ADS  PubMed  CAS  Google Scholar 

  22. 22.

    Leskes, M. et al. Surface-sensitive NMR detection of the solid electrolyte interphase layer on reduced graphene oxide. J. Phys. Chem. Lett. 8, 1078–1085 (2017).

    PubMed  CAS  Google Scholar 

  23. 23.

    Jin, Y. et al. Identifying the structural basis for the increased stability of the solid electrolyte interphase formed on silicon with the additive fluoroethylene carbonate. J. Am. Chem. Soc. 139, 14992–15004 (2017).

    PubMed  CAS  Google Scholar 

  24. 24.

    Jin, Y. et al. Understanding fluoroethylene carbonate and vinylene carbonate based electrolytes for Si anodes in lithium ion batteries with NMR spectroscopy. J. Am. Chem. Soc. 140, 9854–9867 (2018).

    PubMed  CAS  Google Scholar 

  25. 25.

    Berruyer, P., Emsley, L. & Lesage, A. DNP in materials science: touching the surface. eMagRes 7, 93–104 (2018).

    CAS  Google Scholar 

  26. 26.

    Wolf, T. et al. Endogenous dynamic nuclear polarization for natural abundance 17O and lithium NMR in the bulk of inorganic solids. J. Am. Chem. Soc. 141, 451–462 (2018).

    PubMed  Google Scholar 

  27. 27.

    Carver, T. R. & Slichter, C. P. Polarization of nuclear spins in metals. Phys. Rev. 92, 212–213 (1953).

    ADS  CAS  Google Scholar 

  28. 28.

    Feher, G. & Kip, A. F. Electron spin resonance absorption in metals. I. Experimental. Phys. Rev. 98, 337–348 (1955).

    ADS  CAS  Google Scholar 

  29. 29.

    Overhauser, A. W. Polarization of nuclei in metals. Phys. Rev. 92, 411–415 (1953).

    ADS  MATH  CAS  Google Scholar 

  30. 30.

    Gullion, T. & Schaefer, J. Rotational-echo double-resonance NMR. J. Magn. Reson. 81, 196–200 (1989).

    ADS  CAS  Google Scholar 

  31. 31.

    Markevich, E., Salitra, G., Chesneau, F., Schmidt, M. & Aurbach, D. Very stable lithium metal stripping–plating at a high rate and high areal capacity in fluoroethylene carbonate-based organic electrolyte solution. ACS Energy Lett. 2, 1321–1326 (2017).

    CAS  Google Scholar 

  32. 32.

    Brown, Z. L., Jurng, S., Nguyen, C. C. & Lucht, B. L. Effect of fluoroethylene carbonate electrolytes on the nanostructure of the solid electrolyte interphase and performance of lithium metal anodes. ACS Appl. Energy Mater. 1, 3057–3062 (2018).

    CAS  Google Scholar 

  33. 33.

    Fang, C. et al. Quantifying inactive lithium in lithium metal batteries. Nature 572, 511–515 (2019).

    ADS  PubMed  CAS  Google Scholar 

  34. 34.

    Heine, J. et al. Fluoroethylene carbonate as electrolyte additive in tetraethylene glycol dimethyl ether based electrolytes for application in lithium ion and lithium metal batteries. J. Electrochem. Soc. 162, A1094–A1101 (2015).

    CAS  Google Scholar 

  35. 35.

    Michan, A. L. et al. Fluoroethylene carbonate and vinylene carbonate reduction: Understanding lithium-ion battery electrolyte additives and solid electrolyte interphase formation. Chem. Mater. 28, 8149–8159 (2016).

    CAS  Google Scholar 

  36. 36.

    Shkrob, I. A., Wishart, J. F. & Abraham, D. P. What makes fluoroethylene carbonate different? J. Phys. Chem. C. 119, 14954–14964 (2015).

    CAS  Google Scholar 

  37. 37.

    Bennett, L. H., Watson, R. E. & Carter, G. C. Relevance of knight shift measurements to the electronic density of states. J. Res. Natl Bur. Stand. Sect. A Phys. Chem. 74A, 569–610 (1970).

    Google Scholar 

  38. 38.

    Pressley, R. J. & Berk, H. L. g Factor of conduction electrons in metallic lithium. Phys. Rev. 140, A1207–A1210 (1965).

    ADS  Google Scholar 

  39. 39.

    Lesseux, G. G. et al. Unusual diffusive effects on the ESR of Nd3+ ions in the tunable topologically nontrivial semimetal YBiPt. J. Phys. Condens. Matter 28, 125601 (2016).

    PubMed  CAS  Google Scholar 

  40. 40.

    Leskes, M., Moore, A. J., Goward, G. R. & Grey, C. P. Monitoring the electrochemical processes in the lithium-air battery by solid state NMR spectroscopy. J. Phys. Chem. C. 117, 26929–26939 (2013).

    CAS  Google Scholar 

  41. 41.

    Meyer, B. M., Leifer, N., Sakamoto, S., Greenbaum, S. G. & Grey, C. P. High Field multinuclear NMR investigation of the SEI layer in lithium rechargeable batteries. Electrochem. Solid-State Lett. 8, A145 (2005).

    CAS  Google Scholar 

  42. 42.

    Hu, Y.-Y. et al. Origin of additional capacities in metal oxide lithium-ion battery electrodes. Nat. Mater. 12, 1130–1136 (2013).

    ADS  PubMed  CAS  Google Scholar 

  43. 43.

    Aurbach, D. A comparative study of synthetic graphite and Li electrodes in electrolyte solutions based on ethylene carbonate-dimethyl carbonate mixtures. J. Electrochem. Soc. 143, 3809–3820 (1996).

    CAS  Google Scholar 

  44. 44.

    Sloop, S. E., Pugh, J. K., Wang, S., Kerr, J. B. & Kinoshita, K. Chemical reactivity of PF5 and LiPF6 in ethylene carbonate/dimethyl carbonate solutions. Electrochem. Solid-State Lett. 4, A42–A44 (2001).

    CAS  Google Scholar 

  45. 45.

    Michan, A. L., Leskes, M. & Grey, C. P. Voltage dependent solid electrolyte interphase formation in silicon electrodes: monitoring the formation of organic decomposition products. Chem. Mater. 28, 385–398 (2016).

    CAS  Google Scholar 

  46. 46.

    Kittel, C. Introduction to Solid State Physics. (John Wiley & Sons, 2004).

  47. 47.

    Pifer, J. H. & Magno, R. Conduction-electron spin resonance in a lithium film. Phys. Rev. B 3, 663–673 (1971).

    ADS  Google Scholar 

  48. 48.

    Palenskis, V. Drift mobility, diffusion coefficient of randomly moving charge carriers in metals and other materials with degenerated electron gas. World J. Condens. Matter Phys. 03, 73–81 (2013).

    ADS  CAS  Google Scholar 

  49. 49.

    Pecher, O., Vyalikh, A. & Grey, C. P. Challenges and new opportunities of in situ NMR characterization of electrochemical processes. AIP Conf. Proc. 1765, 020011 (2016).

  50. 50.

    Freytag, A. I., Pauric, A. D., Krachkovskiy, S. A. & Goward, G. R. In situ magic-angle spinning 7Li NMR analysis of a full electrochemical lithium-ion battery using a jelly roll cell design. J. Am. Chem. Soc. 141, 13758–13761 (2019).

    PubMed  CAS  Google Scholar 

Download references


This work was supported by the Faraday Institution [grant number FIRG001]. M.A.H. and A.B.G. acknowledge support from the Royal Society (RP/R1/180147). M.A.H. is also grateful to the Oppenheimer foundation and A.B.G. acknowledges EPSRC-EP/M009521/1. B.L.D.R. was supported by NECCES, an Energy Frontier Research Centre funded by the U.S. Department of Energy, under Award No. DE-SC0012583. C.P.G. thanks the EU ERC for an Advanced Fellowship DLV-835073. S.M. thanks the Blavatnik Cambridge Fellowships. The Nottingham DNP MAS NMR Facility is funded by the University of Nottingham and EPSRC (EP/L022524/1, EP/R042853/1). We would like to thank Remington Carey and Prof. H. Sirringhaus (University of Cambridge) for the acquisition of X-band EPR spectra of lithium metal, Prof. Lauren Marbella (Columbia University) for providing additional samples for experiments in the U.S., and Dr. Melanie Rosay and Dr. Ralph Weber (Bruker Billerica, U.S.) for helpful discussions, assistance setting up the experiments at 9.4 T, and measuring the Li T1e.

Author information




C.P.G. and M.A.H. conceived the experiments; M.A.H., B.L.D.R. and S.P. performed the DNP experiments at 14.1 T; K.M., C.P.G. and I.S. performed the DNP experiments at 9.4 T; A.B.G., S.M. and K.M. made the microstructural lithium samples and A.B.G. recorded the SEM images. M.A.H. and C.P.G. wrote the manuscript, with input and approval from all authors.

Corresponding author

Correspondence to Clare P. Grey.

Ethics declarations

Competing interests

I.V.S. is an employee of Bruker Biospin Corporation. Bruker Biospin manufactures and sells DNP instrumentation.

Additional information

Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hope, M.A., Rinkel, B.L.D., Gunnarsdóttir, A.B. et al. Selective NMR observation of the SEI–metal interface by dynamic nuclear polarisation from lithium metal. Nat Commun 11, 2224 (2020).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing