Potassium-ion batteries are a compelling technology for large scale energy storage due to their low-cost and good rate performance. However, the development of potassium-ion batteries remains in its infancy, mainly hindered by the lack of suitable cathode materials. Here we show that a previously known frustrated magnet, KFeC2O4F, could serve as a stable cathode for potassium ion storage, delivering a discharge capacity of ~112 mAh g−1 at 0.2 A g−1 and 94% capacity retention after 2000 cycles. The unprecedented cycling stability is attributed to the rigid framework and the presence of three channels that allow for minimized volume fluctuation when Fe2+/Fe3+ redox reaction occurs. Further, pairing this KFeC2O4F cathode with a soft carbon anode yields a potassium-ion full cell with an energy density of ~235 Wh kg−1, impressive rate performance and negligible capacity decay within 200 cycles. This work sheds light on the development of low-cost and high-performance K-based energy storage devices.
Lithium-ion batteries (LIBs) are the state-of-the-art power technologies for portable electronic devices, electric vehicles, etc., owing to their high-energy density and long-term cycling life1,2,3,4,5,6. However, the limited resource of lithium has restricted some applications of LIBs, especially in the field of large-scale energy storage for intermittent renewable energies, such as solar, wind, and tidal energy1,5. Recently, rechargeable energy storage devices based on other alkali elements, such as sodium-ion batteries (SIBs)7,8,9,10,11,12 and potassium-ion batteries (KIBs)13,14,15,16, have attracted extensive attention because of their obvious advantage in abundant resources. Between them, KIBs have higher working voltages because of the lower redox potential of K/K+ (−2.93 V for K/K+, and −2.71 V for Na/Na+ vs SHE)17. In addition, K ion electrolyte exhibits a relatively higher conductivity due to the weaker Lewis acidity of K and the resultant smaller radii of solvated K ions, and the corresponding system displays a lower interfacial resistance caused by the smaller desolvation energy18,19,20. Although KIBs can utilize graphite-related materials as the anode to achieve a capacity of 280 mAh g−1 via the formation of KC821,22,23,24, the development of high-performance KIBs is so far limited by the lack of appropriate cathode materials.
As the size of K+ (1.38 Å) is much larger than Na+ (1.02 Å) and Li+ (0.76 Å)25, large migration channels and stable crystal structures are essential for K ion migration, which raises a great challenge to develop suitable cathodes. Among the cathode materials reported for KIBs26,27,28,29,30,31,32,33,34,35,36,37,38,39,40,41,42,43,44,45,46,47, Prussian blue analogs (PBAs) have received most intensive studies with good capacity and favorable cycling stability because of their 3D open framework structures14,31,32,33,34,35,48,49,50. For instance, Goodenough et al. reported a cyanoperovskite KxMnFe(CN)6 (0 ≤ x ≤ 2) cathode for KIBs, delivering a stable discharge capacity of ~ 100 mAh g−1 and a capacity retention of 91% over 100 cycles33. More recently, Zhang et al. demonstrated RGO@PB@SSM cathode with a discharge capacity of 61.4 mAh g−1 and a lifespan of 305 cycles in KIBs31. Nevertheless, the preparation and handling of these materials are relatively difficult in controlling defects and water. The vacancies in the [TM(CN)6] (TM = Fe, Mn, etc.) framework and residual water from the synthesis process reduce the available electron reservoir, and lead to slow kinetics, low Coulombic efficiency (CE), and poor cycle life24,28. Further optimization of PBAs or searching for new cathode materials with a similar 3D framework is promising strategies to break through the limitation of cathode and pave the way to practical use of KIBs.
Upon close inspection of a magnetic material, KFeC2O4F, we notice that its 3D open structure is similar to PBAs51,52, which is very promising for K ion storage. Therefore, we carry out systematical electrochemical investigation of KFeC2O4F as a cathode material in KIBs using combined experimental and theoretical approaches. After optimization, a stable capacity of 112 mAh g−1 has been obtained and high-capacity retention of 94% is remained after 2000 cycles, with 0.003% capacity fading per cycle, which is the best long-term stability among the reported KIBs cathode materials. Moreover, a K-based full cell has been constructed by coupling this KFeC2O4F cathode with a soft carbon anode, which exhibits a reversible capacity of ~ 85 mAh g−1 (based on the mass of the cathode) and negligible capacity decay within 200 cycles, as well as impressive rate performance, paving the way for developing highly stable and low-cost K-based energy storage devices.
KFeC2O4F crystallites were synthesized via an optimized hydrothermal process (see Methods). An optical image is shown in Fig. 1a, and the inset shows a single crystallite, which exhibits a typical tetra-prismatic morphology in the size of ~ 1.0 × 0.6 × 0.5 mm. The phase of the prepared sample was checked by Rietveld refinement on powder X-ray diffraction (XRD) as illustrated in Fig. 1b. All diffraction peaks could be well indexed in the space group of Cmc21 with the lattice parameters a = 7.7611(5) Å, b = 11.8591(1) Å, c = 10.4037(7) Å, in accordance with the previously reported data52. The Rietveld refinement also revealed that there is no detectable impurity in the sample. A sheet of KFeC2O4F (Supplementary Fig. 1) with the size of ~ 6 μm × 4 μm × 80 nm was prepared by focused ion beam and then examined by a transmission electron microscope (TEM) and energy dispersion spectroscopy (EDS), as shown in Fig. 1c. The results confirm the evenly distribution of K, Fe, C, O, and F in the obtained crystallites. The Fourier transform infrared and Raman spectra shown in Supplementary Fig. 2 confirm the existence of typical vibration peaks of the oxalate group (Supplementary Table 1)53. Meanwhile, our attempts in taking high-resolution TEM or selected area electron diffraction proved unsatisfactory owing to the sample’s sensitivity to intense electron beams, similar to some other oxalate, fluorosulphates and metal-organic frameworks.54,55,56,57
The thermal behavior of KFeC2O4F was analyzed by simultaneous thermogravimetric–differential scanning calorimetry and variable-temperature XRD. As shown in Fig. 1d, negligible weight loss was detected from the TG curve until 310 °C, confirming the good stability of KFeC2O4F below this temperature. A distinct weight loss step of ca. 32% from 310 °C to 450 °C was exhibited in the TG curve, accompanied by a broad endothermic peak in the DSC curve, which is mainly attributed to the decomposition of oxalate groups. Thereafter, XRD patterns at different temperatures were measured between room temperature and 310 °C (Fig. 1e), demonstrating the excellent phase stability in the chosen temperature range.
Electrochemical performance as KIB cathode in half cells
To apply KFeC2O4F as a cathode material in KIBs, pristine KFeC2O4F was downsized and mixed with a carbon conductor by ball milling to improve its electric conductivity. The purity and morphology of samples after each treatment were checked by XRD, scanning electron microscope (SEM) and EDS element mapping of K, Fe, C, O, F (details in Supplementary Figs. 3, 4). After these treatments, the diffraction peaks of XRD patterns are consistent with those of the pristine sample, which indicates no phase change during ball milling. From SEM images, KFeC2O4F particles with an average size of ϕ ~ 250 nm were homogeneously mixed with the conductive carbon after ball milling, significantly smaller than hand-ground KFeC2O4F particles (Supplementary Fig. 5). This composite cathode was installed in coin-type cells to characterize the electrochemical performance of KFeC2O4F.
K half-cells were firstly fabricated in Ar-filled glove box, with K metal as anode and 1 m KPF6 in PC + EC (1:1 v/v) as the electrolyte. Typical cyclic voltammogram (CV) curves of the KFeC2O4F electrode in 10th, 20th, and 30th cycles in the range of 1.5–4.6 V were recorded at a scan rate of 0.1 mV s−1 (Fig. 2a). The overlapping of these curves indicated the good cyclic stability of the cathode. Meanwhile, a pair of peaks at 3.80/3.35 V is observed in the electrochemical processes during the de-intercalation/intercalation of K ions, corresponding to Fe2+/Fe3+ redox reactions. The rate performance of the cathode is plotted in Fig. 2b, c. Similar profiles of charge-discharge curves are observed, with moderate increase of discharge plateau from 0.5 to 0.1 A g−1 (Fig. 2b). In addition, the discharge capacity of KFeC2O4F cathode is 126, 102, 93, 89, and 87 mAh g−1 for 0.1, 0.2, 0.3, 0.4, and 0.5 A g−1, respectively, with the corresponding CEs over 95% (Fig. 2c). The discharge capacity is recovered to 126 mAh g−1 when the current density is changed back to 0.1 A g−1, demonstrating both good rate capability and good capacity retention of KFeC2O4F. Moreover, a half cell was measured by the galvanostatic intermittent titration technique (details in Supplementary Fig. 6), to reveal K ion diffusion kinetics indicated by chemical diffusion coefficients (D). The results show a variation of D values with depths of charge/discharge as shown in Supplementary Fig. 7. On the whole, the D values of 10−10–10−12 cm2 s−1 were at the similar level to that of Li+ in popular cathode materials (D of Li+ in LiFePO4 (10−14–10−15 cm2 s−1) and in LiMn2O4 (10−11–10−9 cm2 s−1))58. Thus, the good rate performance of KFeC2O4F was likely attributed to the fast K ion diffusion in the [FeC2O4F] framework.
The cycling performance of the KFeC2O4F cathode was illustrated in Fig. 2d. The battery with a KFeC2O4F cathode delivered a stable discharge capacity of ~ 112 mAh g−1 at 0.2 A g−1 after electrochemical activation in initial several cycles and kept a high capacity retention of 94% after 2000 cycles, with only 0.003% capacity fading per cycle. Noted that the voltage profiles of the first few cycles differ from the stabilized ones, possibly attributing to the reaction of conductive carbon wrapped on active material. To figure out the main underneath mechanism, we checked the voltage profile of the conductive carbon, and found out that the first charge–discharge profile of KFeC2O4F composite cathode (Supplementary Fig. 8a) resembles that of the conductive carbon (Supplementary Fig. 8c). As the active KFeC2O4F cathode had been mixed thoroughly with conductive carbon by ball milling, our KFeC2O4F particles had been wrapped entirely by the conductive carbon, so that the first charge–discharge process was mainly originated from the reaction of conductive carbon. As the process went on, KFeC2O4F particles became more and more exposed to the electrolyte, and the intrinsic electrochemical feature of KFeC2O4F became more and more dominating in following charge–discharge profiles. Although the cell based on the conductive carbon initially delivered a relatively high capacity, but its capacity faded gradually to ~30 mAh g−1 after 1000 cycles (Supplementary Fig. 8d). Considering the content of the carbon black in KFeC2O4F cathode material is 25%, its contribution to the whole capacity shall be ~ 7 mAh g−1, thus the obtained capacity on composite cathode material mainly comes from the KFeC2O4F compound. Stable discharge capacities of ~ 126 mAh g−1 and 80 mAh g−1 were obtained at 0.1 A g−1 and 0.5 A g−1, respectively, (Supplementary Fig. 9), with CE constantly above 96.5%. The galvanostatic charging–discharging (GCD) curves at the 1000th and 2000th cycles at 0.2 A g−1 match well with that of the 100th cycle (Fig. 2e). A stable medium discharging voltage (Vm) of ~2.85 V of the cell is observed for 2000 cycles (Fig. 2f). These results demonstrate the outstanding cyclic stability of the cell throughout the testing period (around 2000 h). Further, to reveal the distinctive nature of the long-term reaction kinetics of KFeC2O4F cathode, electrochemical impedance spectroscopy (EIS) tests in different cycles were performed, with the Nyquist plots shown in Supplementary Fig. 10. Each plot comprises a depressed semicircle in the high-medium frequency region originated from the charge transfer resistance (Rct), and a sloping line in the low frequency region attributed to Warburg impedance. It is obviously seen that the Rct value rises first and descends later in the first five cycles, probably owing to the generation of cathode electrolyte interphase films. The Rct kept almost constant after the first 10 cycles, again revealing the good stability of the cell. Dozens of compounds have been thoroughly investigated so far as cathode materials for KIBs. Figure 2g shows the comparison of cycling stability between KFeC2O4F and the reported cathode materials for KIBs (detailed data refer to Supplementary Table 2), demonstrating that the cycling stability of this cathode is significantly better than that of reported KIB cathodes.
Investigation of the reaction mechanism
To investigate the redox chemistry of KFeC2O4F as a cathode in KIBs, synchrotron-based in situ X-ray absorption spectra (in situ XAS) have been measured on a half cell during charging–discharging process, which is known as an advanced method to study the oxidation states and coordination environments of transition metals. The Fe absorption edge from 7000 to 7400 eV was recorded in a gas ionization chamber to track the incident and transmitted X-ray intensities in the transmission mode, whereas the GCD curve of the cell was recorded simultaneously in a battery testing system (see Methods). As a comparison, FeO and Fe2O3 were used for references. Figure 3a shows a typical GCD curve of the in situ cell during XAS measurement, and the color highlighted dots represent the states where in situ XAS were recorded. Figure 3b, c display the Fe K-edge X-ray absorption near-edge spectra (XANES) during charging and discharging, respectively, and Fig. 3d, e illustrate the corresponding extended synchrotron X-ray absorption fine-structure (EXAFS) spectra after k2-weighted Fourier transform. The Fe K-edge XANES spectra shown in Fig. 3b shifted to higher energy region during charging, which is ascribed to the transformation of Fe2+ to Fe3+ during K ion extraction. An opposite shift was observed during discharging (Fig. 3c), attributing to the reduction of Fe3+ to Fe2+ during K ion insertion. The change of XANES in a full cycle indicates a reversible change of Fe valence upon K ion extraction/insertion. In addition, the outline of spectra was mostly identical throughout a full cycle, indicating the high stability of the octahedral [FeO4F2] motif. In the analysis of EXAFS, oscillations within k = 2.6–10 Å−1 were chosen to minimize noise. As illustrated in Fig. 3d, e, broad peaks were identified at ~ 1.5 Å, corresponding to fourfold Fe-O and twofold Fe-F bonds in the octahedral [FeO4F2] motif. The peak shifted to lower distance upon charging, and vice versa upon discharging, suggesting Fe-O/F bonds contraction/expansion. The overlaps of XANES and EXAFS curves of the cathode at the beginning of the charging and the end of discharging (Supplementary Figs. 11, 12) also indicate the good reversibility of the process.
Apart from in situ synchrotron XAS, ex situ XRD patterns were also collected to explore the structural stability and the change of the lattice during K ion extraction/insertion. Figure 3f shows the XRD spectra of KFeC2O4F under different charging/discharging states. A broad peak centered at 20.5° was originated from the conductive carbon black (Supplementary Fig. 13a). It can be seen that the profiles of XRD patterns were almost unchanged within the cycle, indicating the good structural stability of the framework upon K ion extraction and insertion. The characteristic peaks of ex situ XRD in 22.5–23.3° and 28.3–29.2° are highlighted in Fig. 3g, h, corresponding to (200) and (221) plane, respectively. Both characteristic peaks display the same tendency of changes, that is, shifting to higher angle during charging and vice versa during discharging, corresponding to the lattice contraction and expansion, respectively. It should be noted that the shift is very small and reversible, indicating the finite volumetric change and high reversibility during the extraction/insertion of K ions. Moreover, a XRD pattern of KFeC2O4F cathode after long cycling was collected, indicating the well-maintained crystal structure after long cycling (Supplementary Fig. 13b).
To illustrate the fundamental mechanism of the stable while reversible potassium storage in the framework of KFeC2O4F, in-depth structural analysis was performed, along with density functional theory (DFT) calculations based on the DFT + U method, in which the Hubbard U term stands for the strong onsite Coulomb repulsion of localized Fe 3d electrons. As illustrated in Fig. 4a, KFeC2O4F has a 2D [Fe(C2O4)]∞ network with F ions linking adjacent layers common, building a three dimensional [Fe(C2O4)F]∞ skeleton. Three tunnels along the , , and  directions can be delimited with the cross-section dimensions of (4.3 × 4.2 Å), (6.3 × 3.7 Å), and (6.3 × 3.3 Å), respectively. Such large tunnels are feasible for K ion migration. The DFT calculations results that the lattice parameters of KFeC2O4F transform from a = 7.793 Å, b = 11.911 Å, c = 10.463 Å, to a = 7.721 Å, b = 11.539 Å, c = 10.098 Å, after full extraction of K from KFeC2O4F to form FeC2O4F (Fig. 4b). This lattice change only results in 7.6% volume shrinkage, comparable to that of LiFePO4 (~ 7.8%)59. Moreover, the smooth evolution of lattice constants and volume change at varied charging stages (Fig. 4c) could reduce the possibility of mechanical failure (e.g., crack formation) during cycling.
Figure 5a presents the detailed structural evolution of KFeC2O4F at different charging stages based on DFT calculation, which reveals that the 3D framework undergoes a slight change with the marginal shrinking of octahedral [FeO4F2] building blocks during charge. More specifically, the Fe-O bonds on the bc plane shorten by ~ 0.16 Å upon full depotassiation, whereas the Fe-F bonds along the a axis undergo much less shrinkage by 0.06 Å, showing that the interlayer bridging F ions play a pivotal role in stabilizing the 3D framework. Along with the structural changes, Fig. 5b displays the corresponding density of states of the Fe 3d orbitals. In the pristine KFeC2O4F, Fe2+ exhibits a high-spin electron configuration t2g4eg2 (S = 2). It is inferred that the spin-down states (t2g) shall be redox active since they locate right below the Fermi level (EF). As potassium ions being extracted, these t2g states of Fe2+ shift gradually above the EF while emigrating electrons to surrounding anions. In contrast, its majority spin-up states shift further below the EF. In the full-charging [FeC2O4F], Fe3+ exhibits a half-filled electron configuration t2g3eg2 in the highest spin state (S = 5/2), obeying the Hund’s rule. This calculated Fe2+ to Fe3+ transformation agrees with the in situ XANES measurements during charging in Fig. 3b. Moreover, the high structural stability of KFeC2O4F upon charging/discharging under long cycles intimately associates with the above atomic and electronic properties. Figure 5c shows that the energy of C2O42− decomposition in the bulk K1–xFeC2O4F continually decreases with the extraction of potassium ions over x < 0.875, caused by the depletion of Fe 3d electrons and the accumulation of C 2p electrons near the EF that are responsible for the redox reaction upon charging (Fig. 5d). At x ≥ 0.875, it reveals a turning point to prevent the decomposition energy becoming too negative upon full K extraction, owing to the stable 3d electron configuration with half-filled t2g and eg orbitals in FeC2O4F according to the Hund’s rule. Although the reaction energy indicates thermodynamically possible decomposition of C2O42− in the K1-xFeC2O4F during deep charge, its kinetic barrier of ~1.4 eV shown in Fig. 5e effectively inhibits the structure decomposition under ambient condition, resulting in a stable 3D framework for potassium battery chemistry.
Electrochemical performance of a full cell
In practical applications, owing to the high combustibility of metallic K, a metallic K battery would not be safe. Following this consideration, a prototype K ion full cell was configured by combining KFeC2O4F cathode with a soft carbon (SC) anode. The working mechanism of the full cell is sketched in Fig. 6a, where K ions are removed from KFeC2O4F and migrate into the SC anode during charging, and a reverse transformation occurs during discharging. Figure 6b demonstrates that one prepared K ion full cell could power a LED screen. The rate performance of the full cell is shown in Fig. 6c, reaching a reversible capacity of 83.7, 71.0, 65.7 64.7, 62.6 mAh g−1 at a current rate from 0.1 to 0.5 A g−1. The discharge capacity returned back to 76.1 mAh g−1 when the current density recovered to 0.1 A g−1, demonstrating its good rate capability. Moreover, the full cell delivered a reversible capacity of ~ 85 mAh g−1 (based on the mass of the cathode) and remained stable with negligible capacity decay within 200 cycles at a current density of 0.1 A g−1 (Fig. 6d). The energy density of the full cell was estimated ~ 235 Wh kg−1. The GCD curves at 200th, 100th, 50th, and 10th cycles almost overlap with each other (Fig. 6e), manifesting the considerable cycling stability of our full battery.
In conclusion, we have identified KFeC2O4F as a promising cathode candidate for KIBs. Owing to its intrinsic Fe2+/Fe3+ redox mechanism, rigid 3D [FeC2O4F] framework and three open channels, the KFeC2O4F cathode yielded a reversible discharge capacity of ~ 112 mAh g−1 at 0.2 A g−1 and kept high capacity retention of 94% over 2000 cycles, with 0.003% capacity fading per cycle. Moreover, a full K ion cell was successfully constructed by combining this KFeC2O4F cathode with soft carbon anode, which delivered negligible capacity decay for 200 cycles with energy density of ~ 235 Wh kg−1 and impressive rate performance. Although the performance of this K ion full cell may be further enhanced by optimizing the electrolyte systems and utilizing suitable anode materials, etc., this study clearly indicates the feasibility of KFeC2O4F as a promising KIB cathode for sustainable large-scale energy storage applications.
Iron (II) oxalate dihydrate (FeC2O4∙2H2O, 99.5%), oxalic acid dihydrate (H2C2O4∙2H2O, 99.8%), potassium fluoroborate (KBF4, 99.99%), potassium carbonate (K2CO3, 99%), perylene-3,4,9,10-tetracarboxylic dianhydride (PTCDA), and potassium block (K, 99%) were purchased from Aladdin Reagent. Polyvinylidene fluoride (PVDF) binder, and N-methyl-2-pyrrolidone (NMP) were provided by Shenzhen KejingStar Technology. Ketjenblack EC600JD was purchased from Lion Corporation in Japan. Potassium hexafluorophosphate (KPF6, 99.99%), propylene carbonate (PC, 99.95%), ethylene carbonate (EC, 99.95%), and potassium molecular sieve were provided by Dodochem. The glass fiber separator (Whatman, 47 mm) was bought from Shanghai Huanao Technology Ltd. All of the above were used directly as received without further self-processing.
Single crystals of KFeC2O4F were grown via a hydrothermal reaction in mild conditions. A mixture of FeC2O4∙2H2O, H2C2O4∙2H2O, KBF4, and K2CO3 in the molar ratio of 1:3:2:4 (one for 1 mmol) was put in a Teflon-lined autoclave with 1 mL distilled water. After sealing, the autoclave was moved to a 180 °C oven for 48 h, then cooled to room temperature by turning off the oven. The resulting product was filtered with distilled water for several times until all by-products being removed, and then dried at a vacuum environment overnight. The soft carbon was fabricated facilely by thermal polymerizing PTCDA at a heating rate of 10 °C min−1 until 900 °C and kept for 4 h.
The optical images of as-synthesized crystallites were taken by a Leica DVM6M video microscope with ultra-depth-of-field. For the transmission electron microscope (TEM) characterization, a single crystallite was directly moved to the focused ion beam (FIB) chamber. A sheet section from the crystallite was prepared by a FEI Scios FIB/FE-SEM at an accelerating voltage of 30 kV under a selective etching process. The final sheet of the sample was positioned and secured on a Cu grid and transferred to the TEM chamber. The EDS of TEM were conducted by a JEOL JEM-3200FS field emission TEM equipped with an Oxford Instruments EDS analyzer. SEM measurements and EDS element mapping of the sample were carried out on ZEISS SUPRA 55 equipped with an EDS analyzer.
Powder XRD patterns were collected by a Rigaku diffractometer (MiniFlex600) with Cu Kα radiation (λ = 0.154056 nm). Scans were taken with a 2θ step of 0.02° over the range of 10–80°. Rietveld method was used to refine the data sets using the GSAS package incorporated with the EXPGUI interface60. Parameters, such as scale factor, background, lattice parameters, and zero point were refined until convergence. Analyses of recollected cathodes at different states, after being washed with PC to remove electrolyte and dried overnight, were conducted on the same XRD detector at a 2θ step of 2 ° min−1 over the range of 10–60°. Variable-temperature XRD patterns were recorded on a Smartlab 9KW diffractometer equipped with a SmartLab SOH-150F furnace with Cu Kα radiation. The scans were performed in the 2θ step of 2 ° min−1 in the range of 10–60° when heating samples from room temperature to 310 °C at various intervals.
The thermal behavior of KFeC2O4F was detected by simultaneous thermogravimetric and differential scanning calorimetry using a STA449F3 thermal analyzer (Netzsch, Germany). Hand-ground crystallites of ~ 10 mg were placed in an alumina crucible and heated from room temperature to 800 °C under a flow of air at a rate of 10 °C min−1. Fourier transform infrared (FTIR) spectrum was collected by a Perkin Elmer Frontier FTIR spectrometer in the range 400–4000 cm−1 with a resolution of 1 cm−1. The Raman spectrum was carried out using HORIBA, XploRA PLUS detector in the backscattering mode at the frequency range of 400–2000 cm−1. The wavelength resolution and probe aperture are 1 cm−1 and near 10 μm, respectively.
The electrochemical performance of KFeC2O4F was studied in CR2032 coin-type half-cells assembled in an glove box (MIKROUNA) filled with high pure Argon gas, with water and oxygen levels < 0.1 ppm. KFeC2O4F crystallites were first hand-milled for several minutes and then ball milled for 4 h using a high-energy planetary ball mill. To improve the conductivity of KFeC2O4F, the above-mentioned sample was ball milled again with Kejten black carbon (3:1 w/w) for 8 h. Samples at each states were checked under powder XRD, ensuring the sample was not contaminated or destroyed during milling (Supplementary Figs. 3, 4). The subsequent powder was mixed with PVDF (85%:15% w/w), and NMP was added drop-by-drop until forming a homogeneous slurry. The slurry was then hand coated onto a carbon-coated Al foil, and dried at 80 °C in vacuum for 12 h and punched into circular sheets with diameters of 10 mm and loading mass of ~1.0 mg cm−2. Potassium metal foils, 1 m KPF6 in EC: PC = 1:1 (v/v) and glass fiber sheets (16 mm in diameter) were used as counter electrode, electrolyte and separators, respectively. Galvanostatic charge–discharge and galvanostatic intermittent titration technique (GITT) tests were performed on a battery test system (NEWARE CT-4008). Before GITT measurements, cells were initially activated for several cycles at 0.1 A g−1, and subsequently charged or discharged for 10 min at a pulse current of 50 mA g−1, followed by a duration of 10 min relaxation to achieve potassium equilibrium potential. Cyclic voltammetry and electrochemical impedance spectroscopy were performed on an Autolab (PGSTAT302N, Switzerland) electrochemical workstation. The full battery was assembled in similar conditions as half-cells, except that the anode was replaced by SC.
Synchrotron-based X-ray tests were performed on CR2016 coin-type half-cells with two sides kapton windows at SUT-NANOTEC-SLRI XAS beamline (BL5.2), Synchrotron Light Research Institute (SLRI, public organization), Thailand.61 A beam energy of 1.2 GeV generates the synchrotron radiation source at the storage ring and the beamline photon source covers an energy range of 40–1040 eV at the resolving power of 10,000. The typical loading of KFeC2O4F cathode is 5–8 mg cm−2.
All calculations presented were performed by the Vienna ab initio simulation package based on spin-polarized DFT62,63, with projector-augmented-wave method64,65 and a plan-wave cutoff energy of 450 eV. The Perdew–Burke–Ernzerhof functional66 with the Hubbard U correction67 was adopted for the exchange correlation energy. A value of 4.0 eV was applied to U to correct the onsite Coulomb repulsion of Fe 3d electrons68. The Brillouin zone was sampled with a 6 × 4 × 4 Γ-centered k mesh to keep the reciprocal spacing of all calculations with supercells of K8–xFe8(C2O4)8F8 (8 ≥ x ≥ 0) < 0.03 Å−1. The criteria for energy convergence was set to be 10−5 eV. The optimized orthorhombic lattice of K8Fe8(C2O4)8F8 is 7.81 × 11.92 × 10.48 Å, consistent well with the lattice determined by XRD as 7.76 × 11.86 × 10.40 Å. The oxalate dissociation barriers in the bulk were simulated using climbing image nudged elastic band method69 with force convergence criteria on each atom of 0.05 eV Å−1.
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.
Tarascon, J.-M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001).
Li, M., Lu, J., Chen, Z. & Amine, K. 30 years of lithium-ion batteries. Adv. Mater. 30, 1800561 (2018).
Goodenough, J. B. & Park, K. S. The Li-ion rechargeable battery: a perspective. J. Am. Chem. Soc. 135, 1167–1176 (2013).
Dunn, B., Kamath, H. & Tarascon, J. M. Electrical energy storage for the grid: a battery of choices. Science 334, 928–935 (2011).
Goodenough, J. B. & Kim, Y. Challenges for rechargeable Li batteries. Chem. Mater. 22, 587–603 (2010).
Lu, J., Wu, T. & Amine, K. State-of-the-art characterization techniques for advanced lithium-ion batteries. Nat. Energy 2, 1–13 (2017).
Larcher, D. & Tarascon, J. M. Towards greener and more sustainable batteries for electrical energy storage. Nat. Chem. 7, 19–29 (2015).
Han, M. H., Gonzalo, E., Singh, G. & Rojo, T. A comprehensive review of sodium layered oxides: powerful cathodes for Na-ion batteries. Energy Environ. Sci. 8, 81–102 (2015).
Jiang, C. et al. A multi-ion strategy towards rechargeable sodium-ion full batterieswith high working voltage and rate capability. Angew. Chem. Int. Ed. 57, 16370–16374 (2018).
Kim, S.-W., Seo, D.-H., Ma, X., Ceder, G. & Kang, K. Electrode materials for rechargeable sodium-ion batteries: potential alternatives to current lithium-ion batteries. Adv. Energy Mater. 2, 710–721 (2012).
Xie, D., Zhang, M., Wu, Y., Xiang, L. & Tang, Y. A flexible dual-ion battery based on sodium-ion quasi-solid-state electrolyte with long cycling life. Adv. Funct. Mater. 30, 1906770 (2020).
Kundu, D., Talaie, E., Duffort, V. & Nazar, L. F. The emerging chemistry of sodium ion batteries for electrochemical energy storage. Angew. Chem. Int. Ed. 54, 3431–3448 (2015).
Zhang, W., Liu, Y. & Guo, Z. Approaching high-performance potassium-ion batteries via advanced design strategies and engineering. Sci. Adv. 5, eaav7412 (2019).
Xu, Y. et al. Enhancing potassium-ion battery performance by defect and interlayer engineering. Nanoscale Horiz. 4, 202–207 (2019).
Hwang, J.-Y., Myung, S.-T. & Sun, Y.-K. Recent progress in rechargeable potassium. Batteries. Adv. Func. Mater. 28, 1802938 (2018).
Ji, B., Zhang, F., Wu, N. & Tang, Y. A dual-carbon battery based on potassium-ion electrolyte. Adv. Energy Mater. 7, 1700920 (2017).
Marcus, Y. International union of pure and applied chemistry. Pure Appl. Chem. 57, 1129–1132 (1985).
Okoshi, M., Yamada, Y., Komaba, S., Yamada, A. & Nakai., H. Theoretical analysis of interactions between potassium ions and organic electrolyte solvents: a comparison with lithium, sodium, and magnesium ions. J. Electrochem. Soc. 164, A54–A60 (2017).
Lei, K. et al. High K-storage performance based on the synergy of dipotassium terephthalate and ether-based electrolytes. Energy Environ. Sci. 10, 552–557 (2017).
Chang, X. et al. Ultrahigh nitrogen doping of carbon nanosheets for high capacity and long cycling potassium ion storage. Adv. Energy Mater. 9, 1902672 (2019).
Nobuhara, K., Nakayama, H., Nose, M., Nakanishi, S. & Iba, H. First-principles study of alkali metal-graphite intercalation compounds. J. Power Sources 243, 585–587 (2013).
Komaba, S., Hasegawa, T., Dahbi, M. & Kubota, K. Potassium intercalation into graphite to realize high-voltage/high-power potassium-ion batteries and potassium-ion capacitors. Electrochem. Commun. 60, 172–175 (2015).
Jian, Z., Luo, W. & Ji, X. Carbon electrodes for K-ion batteries. J. Am. Chem. Soc. 137, 11566–11569 (2015).
Xu, Y. et al. Highly nitrogen doped carbon nanofibers with superior rate capability and cyclability for potassium ion batteries. Nat. Commun. 9, 1720 (2018).
Shannon, R. D. Revised effective ionic radii and systematic studies of interatomie distances in halides and chaleogenides. Acta Cryst. A32, 751–767 (1976).
Kim, H. et al. K-Ion Batteries Based on a P2-Type K0.6CoO2 Cathode. Adv. Energy Mater. 7, 1700098 (2017).
Hwang, J.-Y., Kim, J., Yu, T.-Y., Myung, S.-T. & Sun, Y.-K. Development of P3-K0.69CrO2 as an ultra-high-performance cathode material for K-ion batteries. Energy Environ. Sci. 11, 2821–2827 (2018).
Masese, T. et al. Rechargeable potassium-ion batteries with honeycomb-layered tellurates as high voltage cathodes and fast potassium-ion conductors. Nat. Commun. 9, 3823 (2018).
Kim, H. et al. Investigation of potassium storage in layered P3-Type K0.5MnO2 cathode. Adv. Mater. 29, 1702480 (2017).
Gao, A. et al. K-brnessite electrode obtained by ion exchange for potassium-ion batteries: insight into the concerted ionic diffusion and K storage mechanism. Adv. Energy Mater. 9, 1802739 (2019).
Zhu, Y. H. et al. Transformation of rusty stainless-steel meshes into stable, low-cost, and binder-free cathodes for high-performance potassium-ion batteries. Angew. Chem. Int. Ed. 56, 7881–7885 (2017).
Zhang, C. et al. Potassium prussian blue nanoparticles: a low-cost cathode material for potassium-ion batteries. Adv. Funct. Mater. 27, 1604307 (2017).
Xue, L. et al. Low-cost high-energy potassium cathode. J. Am. Chem. Soc. 139, 2164–2167 (2017).
Wang, J. et al. A bi-functional device for self-powered electrochromic window and self-rechargeable transparent battery applications. Nat. Commun. 5, 4921 (2014).
Pei, Y., Mu, C., Li, H., Li, F. & Chen, J. Low-cost K4Fe(CN)6 as a high-voltage cathode for potassium-ion batteries. Chem. Sus. Chem. 11, 1285–1289 (2018).
Chen, Y. et al. Organic electrode for non-aqueous potassium-ion batteries. Nano Energy 18, 205–211 (2015).
Fan, L., Ma, R., Wang, J., Yang, H. & Lu, B. An ultrafast and highly stable potassium-organic battery. Adv. Mater. 30, 1805486 (2018).
Han, J. et al. Nanocubic KTi2(PO4)3 electrodes for potassium-ion batteries. Chem. Commun. 52, 11661–11664 (2016).
Gao, H., Xue, L., Xin, S. & Goodenough, J. B. A high-energy-density potassium battery with a polymer-gel electrolyte and a polyaniline cathode. Angew. Chem. Int. Ed. 57, 5449–5453 (2018).
Ding, Y. et al. A liquid-metal-enabled versatile organic alkali-ion battery. Adv. Mater. 31, 1806956 (2019).
Park, W. B. et al. KVP2O7 as a robust high-energy cathode for potassium-ion batteries: pinpointed by a full screening of the inorganic registry under specific search conditions. Adv. Energy Mater. 8, 1703099 (2018).
Kim, H. et al. A new strategy for high-voltage cathodes for K-ion batteries: stoichiometric KVPO4F. Adv. Energy Mater. 8, 1801591 (2018).
Lin, B. et al. Birnessite nanosheet arrays with high K content as a high-capacity and ultrastable cathode for K-ion batteries. Adv. Mater. 31, 1900060 (2019).
Lin, X., Huang, J., Tan, H., Huang, J. & Zhang, B. K3V2(PO4)2F3 as a robust cathode for potassium-ion batteries. Energy Storage Mater. 16, 97–101 (2019).
Lu, K. et al. Rechargeable potassium-ion batteries enabled by potassium-iodine conversion chemistry. Energy Storage Mater. 16, 1–5 (2019).
Zhang, L. et al. Constructing the best symmetric full K-ion battery with the NASICON-type K3V2(PO4)3. Nano Energy 60, 432–439 (2019).
Choi, J. U. et al. K0.54[Co0.5Mn0.5]O2: new cathode with high power capability for potassium-ion batteries. Nano Energy 61, 284–294 (2019).
Hosaka, T., Shimamura, T., Kubota, K. & Komaba, S. Polyanionic compounds for potassium-ion batteries. Chem. Rec. 18, 1–12 (2018).
Xu, Y.-S. et al. Recent developments in electrode materials for potassium-ion batteries. J. Mater. Chem. A 7, 4334–4352 (2019).
He, G. & Nazar, L. F. Crystallite size control of prussian white analogues for nonaqueous potassium-ion batteries. ACS Energy Lett. 2, 1122–1127 (2017).
Tustain, K. et al. Materialization of a geometrically frustrated magnet in a hybrid coordination framework: a study of the iron(II) oxalate fluoride framework, KFe(C2O4)F. Inorg. Chem. 58, 11971–11977 (2019).
Yao, W. et al. Diverse family of layered frustrated magnets with tailorable interlayer interactions. Chem. Mater. 29, 6616–6620 (2017).
Frost, R. L., Locke, A. & Martens, W. N. Synthesis and Raman spectroscopic characterisation of the oxalate mineral wheatleyite Na2Cu2+(C2O4)2·2H2O. J. Raman Spectrosc. 39, 901–908 (2008).
Recham, N. et al. A 3.6 V lithium-based fluorosulphate insertion positive electrode for lithium-ion batteries. Nat. Mater. 9, 68–74 (2010).
Turner, S. O. et al. Direct imaging of loaded metal–organic framework materials (Metal@MOF-5). Chem. Mater. 20, 5622–5627 (2008).
Houk, R. J. et al. Silver cluster formation, dynamics, and chemistry in metal–organic frameworks. Nano Lett. 6, 3413–3418 (2009).
Song, T. et al. A low-cost and environmentally friendly mixed polyanionic cathode for sodium-ion storage. Angew. Chem. Int. Ed. 59, 740–745 (2020).
Park, M., Zhang, X., Chung, M., Less, G. B. & Sastry, A. M. A review of conduction phenomena in Li-ion batteries. J. Power Sources 195, 7904–7929 (2010).
Ouyang, C. Y., Shi, S. Q., Fang, Q. & Lei, M. S. Li1+xFePO4 (0≤x≤3) as anode material for lithium ion batteries: from ab initio studies. J. Power Sources 175, 891–896 (2008).
Toby, B. H. EXPGUI, a graphical user interface for GSAS. J. Appl. Cryst. 34, 210–213 (2001).
Yao, W. et al. An oxalate cathode for lithium ion batteries with combined cationic and polyanionic redox. Nat. Commun. 10, 3483 (2019).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal–amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
John, P. P., Kieron., B. & Matthias, E. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Dudarev, S. L., Botton, G. A., Savrasov, S. Y., Humphreys, C. J. & Sutton, A. P. Electron-energy-loss spectra and the structural stability of nickel oxide: an LSDA+U study. Phys. Rev. B 57, 1505–1509 (1998).
Wang, L., Maxisch, T. & Ceder, G. Oxidation energies of transition metal oxides within the GGA+U framework. Phys. Rev. B 73, 195107 (2006).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
We acknowledge the financial support from the National Natural Science Foundation of China (51822210, 51902339, 51972329), SIAT Innovation Program for Excellent Young Researchers (201811, 201825), the Science and Technology Planning Project of Guangdong Province (2018A050506066, 2019B090914003), Shenzhen Science and Technology Planning Project (JCYJ20170818153427106, JCYJ20180507182512042), and the Program for Guangdong Innovative and Entrepreneurial Teams (no. 2017ZT07C341).
The authors declare no competing interests.
Peer review information Nature Communications thanks Yong Lei and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Ji, B., Yao, W., Zheng, Y. et al. A fluoroxalate cathode material for potassium-ion batteries with ultra-long cyclability. Nat Commun 11, 1225 (2020). https://doi.org/10.1038/s41467-020-15044-y
This article is cited by
Journal of Materials Science: Materials in Electronics (2022)
Journal of Molecular Modeling (2022)
Journal of Molecular Modeling (2022)
Transactions of Tianjin University (2021)
Structural engineering of sulfur-doped carbon encapsulated bismuth sulfide core-shell structure for enhanced potassium storage performance
Nano Research (2021)