Abstract
Water confined within one-dimensional (1D) hydrophobic nanochannels has attracted significant interest due to its unusual structure and dynamic properties. As a representative system, water-filled carbon nanotubes (CNTs) are generally studied, but direct observation of the crystal structure and proton transport is difficult for CNTs due to their poor crystallinity and high electron conduction. Here, we report the direct observation of a unique water-cluster structure and high proton conduction realized in a metal-organic nanotube, [Pt(dach)(bpy)Br]4(SO4)4·32H2O (dach: (1R, 2R)-(–)-1,2-diaminocyclohexane; bpy: 4,4’-bipyridine). In the crystalline state, a hydrogen-bonded ice nanotube composed of water tetramers and octamers is found within the hydrophobic nanochannel. Single-crystal impedance measurements along the channel direction reveal a high proton conduction of 10−2 Scm−1. Moreover, fast proton diffusion and continuous liquid-to-solid transition are confirmed using solid-state 1H-NMR measurements. Our study provides valuable insight into the structural and dynamical properties of confined water within 1D hydrophobic nanochannels.
Similar content being viewed by others
Introduction
Water confined within a hydrophobic nanospace has been of particular interest for researchers due to the unusual structural and dynamical properties, which differ significantly from those of bulk water1,2. In a hydrophobic nanochannel with a small aperture size (<3−4 nm), confined water shows remarkable physical properties which arise from the reduced number of neighbouring water molecules, resulting in a restricted hydrogen-bond network2,3. To study the effect of confining water in a one-dimensional (1D) nanospace, water-filled carbon nanotubes (CNTs) have been an attractive research focus, with interesting water-cluster formation4,5, fast water transport6,7, and high proton conductivity observed8,9,10. Such studies on the dynamics of water confinement in hydrophobic nanochannels are especially important as biomimetics11,12 for understanding transport mechanisms in proton pumps13 or water transport proteins14. However, the poor crystallinity and high electrical conductivity of CNTs cause difficulties for detailed investigation of the structure and proton transport properties of confined water within the 1D hydrophobic nanochannels.
In contrast to CNTs, structural fabrication of nanochannels using coordination chemistry is a promising approach due to the richness in structural degrees of freedom and the relative ease of structural characterisation through crystallographic techniques. Among coordination complexes, metal-organic frameworks (MOFs), which are infinite coordination networks of metal ions bridged through organic ligands, have attracted much interest due to their structural designability and uniform porosity15,16,17. Recently, we have developed a rational bottom-up synthesis of a metal-organic nanotube18 based on the oxidative polymerisation of a square-shaped platinum complex using elemental iodine. This nanotube is composed of four 1D halogen-bridged transition-metal chains (MX-chains) which are connected linearly bridging organic ligands to form a right square prism-shaped nanotubular structure (MX-tube)19.
Herein, we present the direct observation of the proton dynamics of water confined in the hydrophobic channel of a synthetic nanotubular material20,21 (Fig. 1a). We synthesise the metal-organic nanotube [Pt(dach)(bpy)Br]4(SO4)4·32H2O (1, dach: (1R, 2R)-(-)-1,2-diaminocyclohexane; bpy: 4,4′-bipyridine), and elucidate unique water clustering composed of water tetramers and octamers within the hydrophobic nanochannel of 1 using single-crystal X-ray analyses. Single-crystal impedance spectroscopy measurements and solid-state 1H-NMR studies, both supported by theoretical calculations, are used to show high proton conductivity of 1 that originates from the confined water within the hydrophobic nanochannel. In addition, we find a continuous liquid-to-solid transition of the confined water, which is significantly different from that of bulk water.
Results
Confined water in the nanochannel of a metal-organic nanotube
Single crystals of 1 were obtained by the oxidative polymerisation of a square-shaped complex, [Pt(dach)(bpy)]4(SO4)4, using elemental Br2 (Supplementary Figs. 1–7, see Supplementary Information for details). The crystal structure of 1 was determined by single-crystal X-ray diffraction (SCXRD) at 100 K (Fig. 1b, c, Supplementary Figs. 8–16, and Supplementary Table 1). The structure consists of symmetrically equivalent nanotubes, with square [Pt(dach)(bpy)]4 units bridged to each other along through bromide anions at the corners of the square, resulting in tubes that propagate parallel to one another along the a-axis. Overall, there is a net 8+ charge per square [Pt(dach)(bpy)Br]4 unit, which is charge-balanced by four sulfate anions that reside between the tubes. The tubes are spaced 14.1 Å (17.0 Å) apart along the b- and c-direction and are propped apart due to steric interactions between the bulky exterior dach ligands and sulfate counter anions. This spacing leaves two types of water-filled 1D channels in the crystal, a hydrophobic interior channel A and a hydrophilic exterior channel B (Fig. 1c). Within channel B, water molecules form a 1D hydrogen-bond network which includes terminal dach amino groups and sulfate anions (Supplementary Fig. 9). Within channel A on the other hand, water forms two unique clusters of alternating octamers and tetramers, having strong hydrogen-bond interactions within the cluster and weaker interactions between clusters (Fig. 2). These tetramers and octamers are similar to theoretically-predicted conformations of small water clusters22. There are three crystallographically-unique water molecules in the octamer and two in the tetramer, and medium strength hydrogen bonds hold each cluster together at 2.5–2.7 Å O–O distances. The clusters form weak hydrogen bonds between one another in the channel direction at distances of 3.0–3.4 Å. Water in the clusters are separated from the walls of the tube by >2.9 Å, indicating weak contact forces between the clusters and the inner surface of the nanochannel. This clustering arises from the hydrophobic nature of the channel, which is similar to that of CNTs or biological channels in ion transport proteins6,13,14. In 1, the alternating M-X nature of the tube gives rise to a corrugated interior which narrows near the bpy surfaces, which is in contrast to the smooth interior surface of a CNT (Supplementary Fig. 12). Variable-temperature SCXRD was used to understand the dynamics of the water clusters with increasing temperature; water-clusters were clearly observed below 200 K, but became slightly disordered above 250 K (Supplementary Fig. 13).
High proton conductivity
To investigate any unique transport properties arising from the nanoconfinement of water, impedance spectroscopy measurements on a single crystal of 1 were performed along the channel direction (a-direction; Fig. 3b inset). We first confirmed that the dc conductivity is less than the lower limit of measurement, ruling out significant electrical conductivity in the tube. On the other hand, when measured with ac impedance spectroscopy, 1 gave a semi-circular response in the Nyquist plot, suggesting that the conductivity is protonic in nature. Upon increasing the relative humidity (RH) from 40 to 95%, the conductivity increased significantly by over three orders of magnitude (Fig. 3b). This strong humidity dependence clearly suggests that the included water molecules are essential for the high level of conductivity. At 55 °C and 95% RH, the conductivity of 1 reached 1.7 × 10−2 S cm−1 (Fig. 3c). This value is quite high and in the range of superprotonic conductivity, which is comparable to the commercial proton-exchange polymer membrane Nafion23. This high level of conductivity means that 1 is among the most proton-conductive MOFs despite the fact that 1 does not have any free functional acidic groups or free acids inside the pores.24,25 The proton conductivity measured on a pelletised powder sample (Supplementary Figs. 17–20) was about a hundredth lower than that measured with a single crystal at 95% RH, suggesting that the proton conduction is highly anisotropic and that the conducting pathway is in the channel direction. The conductivity showed Arrhenius behaviour with varying temperature, with an activation energy (Ea) of 0.22 eV (Fig. 3d). This low Ea is close to those of typical proton-conductive MOFs showing Grotthuss-type proton hopping, where a protonic charge defect diffuses through the hydrogen-bond network17,26,27. Moreover, the water-cluster structures of 1 were retained above 200 K (~250 K, Supplementary Fig. 13), indicating that high proton conductivity is derived not from mobile hydronium ions (H3O+) themselves but rather from proton shuttling through the hydrogen-bond network between interacting water clusters.
Proton-conducting mechanism
For further investigation of the transport mechanism of 1, solid-state 1H-NMR measurements were performed (Supplementary Figs. 21–27). In the 1H-MAS NMR spectra, the peak of the crystallization water was observed as a single component, indicating the rapid exchange of protons of water between channel A and B (Supplementary Fig. 22). The self-diffusion coefficient of 1H in a water molecule can be estimated by the pulsed-field gradient (PFG) method28,29,30, by which the diffusion movement is detected as the attenuation of an observed echo signal. Because the self-diffusion coefficient of 1H in water has a linear relationship with the mobility of the proton carrier in proton conduction, PFG-NMR measurements provide useful insight into the mechanism of conduction. Figure 4 shows the results of PFG-NMR measurements at 25 °C and 95% RH. The peak centred at 4.54 ppm was assigned as crystallization water protons and was observed to decay with the increasing strength of the gradient pulse (g) (Fig. 4a and Supplementary Figs. 23–27). The echo attenuation follows different equations depending on the dimensionality of the diffusion path (isotropic, anisotropic, or unidirectional; see Supplementary Materials for detail)29,30,31, and in our case, the curve fitting was successful when considering the single component of an anisotropic diffusion model (Fig. 4b) expressed as,
where k = γ2δ2γ2(Δ−δ/3), and D is the self-diffusion coefficient. The subscripts of D represent the diffusion parallel (D||) and perpendicular (D⊥) to the channel alignment direction. The fitting result gave self-diffusion coefficients of D|| = 2.9 × 10−11 m2s−1 and D⊥ = 1.6 × 10−12 m2s−1. The diffusion time (Δ) dependence of D and mean-square displacement of 1H also supports the anisotropic nature of the diffusion (Supplementary Figs. 24 and 25). The self-diffusion coefficient of D|| is comparable to that reported for Nafion (0.2–20 × 10–10 m2s–1; D of Nafion largely varies with water mass fraction)32. From the temperature dependence of self-diffusion coefficients, the activation energies are estimated to be 0.18 eV for D|| and 0.14 eV for D⊥ (Supplementary Fig. 26). Compared to the impedance result, smaller activation energies were likely determined because PFG-NMR observes shorter-range diffusion. It should be noted that the observed D|| contains the contributions from both channel A and B. The very smooth proton diffusivity in the hydrophobic nanochannel A is expected because of weak interactions among the confined waters and the inner wall of the tube6,7,8,9,10, resulting in the lowering of the potential barrier heights of the rotational and translational movements of the included water molecules. Conversely, moderate diffusivity in channel B would be expected due to the low dimensionality of the diffusion path and the large number of hydrogen bonds among the water molecules, sulfate anions, and amines of the tubular framework, which restricts water reorientation and diffusion29. In addition, our recent study on related nanotubular analogues having ultrasmall diameters revealed that the observed proton conductivities are much lower than that of 133. In these analogue compounds, no water molecule exists inside the hydrophobic nanotube, whereas the hydrophilic channel outside of the nanotube contains several water molecules. These results suggest that the existence of confined waters within hydrophobic channel A with smooth proton diffusivity plays an important role in the realization of the high proton conductivity of 1.
As the conductivity (σ) can be expressed as σ = neμ (n: the number of carriers, e: charge, μ: mobility of carriers), the existence of mobile proton sources is very important for attaining high proton conduction. In our case, the amine sites of the dach ligand that are coordinated to the PtIV sites could be considered as possible proton sources. Compared to the pKa value of free amines (pKa = 25–30), the pKa of amines coordinated to metal ions are known to be much lower34. DFT calculations clearly support this assumption and indicate that the amine groups coordinated to PtIV cations in 1 have similar acidity to carbonic acid (Supplementary Figs. 28 and 29 and Supplementary Table 3).
To obtain atomistic insights on the proton diffusivity in the hydrophobic nanochannel, we performed quantum-mechanical molecular dynamics (QM-MD) simulations (Supplementary Figs. 30–35, Supplementary Tables 4–6 and Supplementary Movies 1–3; see Supplementary Materials for details). The vehicular diffusion35 coefficients (Dv) estimated from the time dependence of mean square displacement indicate that water molecules in channel A move approximately 1.5 times faster than those in channel B (Supplementary Fig. 35a). According to the decomposition into parallel and perpendicular contributions with respect to channel alignment direction, the vehicular diffusion is not completely isotropic in both channel A and B (Supplementary Table 7). The Grotthuss diffusion26,27 coefficients (DG) were calculated based on the proton transfer rate, which was quantified by counting proton shuttling at each simulation step36,37. The proton transfer rate in channel A was more than two times higher that of channel B because attractive interaction with the sulfate anion in channel B hindered the proton shuttling (Supplementary Fig. 35b). The averaged value of DG obtained from channel A and B accounts for the larger portion in overall proton diffusion coefficient (Dp) given by the summation of DG and Dv38,39,40. The comparison of Dp among three water environments showed that the proton diffusivity in the hydrophobic nanochannel is in between the liquid and solid state (Supplementary Table 8).
Liquid-to-solid phase transition of confined water
The liquid-to-solid phase transition behaviour of confined water has been of interest because the nature of the freezing of water in quasi-one-dimensional systems is not simple and has not been fully understood4,5,41,42. The experimental and theoretical investigations of CNTs have indicated that the phase transition behaviour strongly depends on the pore diameter and pressure; the transition behaviour has been predicted to be discontinuous (first-order-like) for a pore diameter of >1.2 nm and continuous for a pore diameter of <1.2 nm at ambient pressure43. We investigated the liquid-to-solid phase transition behaviour of confined water in 1 using differential scanning calorimetry (DSC), solid-state 1H-NMR and impedance measurements at low temperature (Supplementary Figs. 36–39). The DSC measurements showed no obvious phase transition (ice transition or melting) of the confined water between 163 and 293 K (Supplementary Fig. 36), suggesting that the confined water shows a continuous liquid-to-solid transition in the channels. The temperature dependence of the solid-state 1H-NMR signal line width for the crystallisation water of 1 showed a gradual and continuous broadening as the temperature decreased (Supplementary Figs. 37 and 39). These results indicate that the confined water in 1 exhibits no clear liquid-to-solid phase transition, which is markedly different from the behaviour of the bulk water or water confined in micropores5,43. This is also supported by the proton conductivity showing a gradual increase with temperature, rather than an inflection indicative of a phase transition (Supplementary Fig. 38). From the combination of solid-state 1H-NMR and proton conductivity, the correlation between the proton conductivity and the continuous liquid-to-solid phase transition is clearly visualized (Fig. 5).
Discussion
We have synthesised and characterised a metal-organic nanotube that has water-filled hydrophobic nanochannels in the crystalline state. The hydrophobic nanochannel of the nanotube has the square-shaped aperture with the size of ca. 1.0 nm (Fig. 1). The confined water in the hydrophobic nanochannel of 1 forms unique clustered structures, which was confirmed by SCXRD measurements. Single crystal impedance spectroscopy revealed that 1 exhibits very high proton conductivity along the 1D channel direction. The high conductivity of 1 is attributed to both the high proton diffusivity within the hydrophobic nanochannel combined with the acidity of the coordinated amine protons, both of which were supported by PFG-NMR and theoretical calculations. In addition, the continuous liquid-to-solid phase transition of the confined water in 1 was observed from DSC, solid-state 1H-NMR and impedance measurements, showing markedly different behaviour from bulk water. In 2001, Brewer et al.8, pointed out that the properties of confined water and proton transport through that water in a hydrophobic nanochannel are highly sensitive to the size of the channel. These properties of confined water originate from the reduced number of possible hydrogen-bond interaction in the nanochannel and negligible water–channel wall interaction2,3, which become similar to those of bulk water as the diameter of the nanochannel become larger. Recent experimental results using CNTs also validated these theoretical predictions.2,5,44 For example, Noy et al., experimentally demonstrated that 0.8-nm-diameter CNT porins show extraordinarily fast proton transport while 1.5-nm-diameter CNT porins show the proton transport rate comparable to bulk water44. Consistent with these previous works on CNTs with the aperture sizes of <1.5 nm, our nanotube experimentally demonstrated the unique clustering structures, high proton mobility, and a continuous liquid-to-solid phase transition of the confined water. The present results show strong experimental evidence of the predicted behaviour of confined water in hydrophobic nanochannels. Nanotube fabrication based on coordination chemistry can allow for systematic structural tuning of pore size, shape and surface properties. This tunability can thus enable us to systematically investigate the properties of confined water. We believe that these findings will provide valuable structural and dynamic insights about confined molecular species in nanotubular materials as well as in biological channels.
Methods
Syntheses and characterisation of compounds
Reagents and solvents were purchased from Wako Pure Chemical Industries, Ltd., TCI Co., Ltd., and Sigma-Aldrich Chemical Co. and used without further purification. Elemental analyses for all compounds were performed using Yanaco MT-5 and MT-6 CHN recorders at the Centre for Organic Elemental Microanalysis, Kyoto University.
Synthesis of [Pt(dach)(bpy)Br]4(SO4)4·32H2O (1)
To an aqueous solution containing equimolar amounts of the square-shaped unit [Pt(dach)(bpy)]48+ and its brominated square unit [Pt(dach)(bpy)Br2]48+, an excess amount of tetrabutylammonium sulfate [(C4H9)4N]2(SO4) were added, and then the mixture was stirred at rt. A red-purple precipitate of 1 was collected by filtration (60% yield from the starting material (Pt(dach)(NO3)2)). Single crystals were obtained by slow tetrahydrofuran diffusion to an aqueous solution of the powder sample. Elemental analysis (%) calcd for C64H88N16O16S4Br4Pt4·28H2O: C 25.04, H 4.73, N 7.30, S 4.18; found: C 24.73, H 4.35, N 7.26 S 4.25. (IR spectrum and TGA curve are shown in Supplementary Figs. 4 and 5, respectively. See Supplementary Discussion for the experimental detail).
Adsorption/desorption isotherms
The sorption experiments for H2O (298 K) were carried out using a BELSORP-max (MicrotracBEL). The as-synthesized sample 1 was dried under high vacuum (<10−1 Pa) at 35 °C for 2 days to remove the crystallisation water before measurements. Isotherms are shown in Fig. 2a.
Single-crystal X-ray crystallography
An X-ray crystal structure analyses were carried out using a Bruker SMART APEX II CCD detector with graphite-monochromated Mo Kα radiation (λ = 0.71073 Å) at 100 K. Single crystals were prepared by the vapour diffusion method using a water solution of 1 and THF, as described above. Suitable single-crystals were selected in the mother liquid and quickly transferred to paraton oil to avoid undesired solvent loss. The single crystals were mounted on MicroMesh (MiTeGen). The structures were solved by direct methods (SIR92), expanded using Fourier techniques (DIRDIF99) and refined by full-matrix least-squares refinement on F2 (SHELXL-97) using the CrystalStructure software package. The refinement result for 1 is summarized in Supplementary Table 1.
Impedance measurements
Impedance measurements were carried out with a Solartron SI 1260 Impedance/Gain-Phase Analyser and 1296 Dielectric Interface in the frequency range of 1–1 × 106 Hz. The relative humidity and temperature were controlled by an Espec Corp. SH-221 incubator. The measurements in the low temperature region (140–300 K) were taken using Oxford OptistatDN2 and Lakeshore 340 temperature controllers.
Solid-state 1H NMR measurements
Solid-state 1H nuclear magnetic resonance (NMR) measurements of 1 were performed on an AVANCE II+ 400 NMR spectrometer (Bruker Biospin K. K.) with an UltraShieldTM 400 WB 9.4 T superconducting magnet. 1H magic angle spinning (MAS) spectra and 13C cross-polarization (CP) MAS spectra were measured with a rotor of 4 mm diameter. Pulse field gradient (PFG)-NMR measurements were performed with a Diff 50 diffusion probe (Bruker Biospin K. K.).
Data availability
The experiment data that support the findings of this study are available from the corresponding authors upon reasonable request. Crystallographic data in CIF format have been deposited in the Cambridge Crystallographic Data Centre (CCDC) under deposition numbers CCDC-1441696, 1441697, and 1441705. These data can be obtained free of charge via www.ccdc.cam.ac.uk/data_request/cif (or from the Cambridge Crystallographic Data Centre, 12 Union Road, Cambridge CB2 1EZ, U.K.).
Code availability
The executable for running quantum-mechanical molecular dynamics simulations used in the present study can be downloaded for academic purpose via www.chem.waseda.ac.jp/dcdftbmd.
References
Li, Q., Song, J., Besenbacher, F. & Dong, M. Two-dimensional material confined water. Acc. Chem. Res. 48, 119–127 (2015).
Park, H. G. & Jung, Y. Carbon nanofluidics of rapid water transport for energy applications. Chem. Soc. Rev. 43, 565–576 (2014).
Alexiadis, A. & Kassinos, S. Molecular simulation of water in carbon nanotubes. Chem. Rev. 108, 5014–5034 (2008).
Koga, K., Gao, G. T., Tanaka, H. & Zeng, X. C. Formation of ordered ice nanotubes inside carbon nanotubes. Nature 412, 802–805 (2001).
Kyakuno, H. et al. Confined water inside single-walled carbon nanotubes: global phase diagram and effect of finite length. J. Chem. Phys. 134, 244501 (2011).
Hummer, G., Rasaiah, J. C. & Noworyta, J. P. Water conduction through the hydrophobic channel of a carbon nanotube. Nature 414, 188–190 (2001).
Holt, J. K. et al. Fast mass transport through sub-2-nanometer carbon nanotubes. Science 312, 1034–1037 (2006).
Brewer, M. L., Schmitt, U. W. & Voth, G. A. The formation and dynamics of proton wires in channel environments. Biophys. J. 80, 1691–1702 (2001).
Dellago, C., Naor, M. M. & Hummer, G. Proton transport through water-filled carbon nanotubes. Phys. Rev. Lett. 90, 105902 (2003).
Cao, Z. et al. Mechanism of fast proton transport along one-dimensional water chains confined in carbon nanotubes. J. Am. Chem. Soc. 132, 11395–11397 (2010).
Zhu, F. & Schulten, K. Water and proton conduction through carbon nanotubes as models for biological channels. Biophys. J. 85, 236–244 (2003).
Geng, J. et al. Stochastic transport through carbon nanotubes in lipid bilayers and live cell membranes. Nature 514, 612–615 (2014).
Umena, Y., Kawakami, K., Shen, J. R. & Kamiya, N. Crystal structure of oxygen-evolving photosystem II at a resolution of 1.9 Å. Nature 473, 55–60 (2011).
Sui, H. X., Han, B. G., Lee, J. K., Walian, P. & Jap, B. K. Structural basis of water-specific transport through the AQP1 water channel. Nature 414, 872–878 (2001).
Kitagawa, S., Kitaura, R. & Noro, S. Functional porous coordination polymers. Angew. Chem. Int. Ed. 43, 2334–2375 (2004).
Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, 1230444 (2013).
Ramaswamy, P., Wong, N. E. & Shimizu, G. K. H. MOFs as proton conductors-challenges and opportunities. Chem. Soc. Rev. 43, 5913–5932 (2014).
Otsubo, K. et al. Bottom-up realization of a porous metal–organic nanotubular assembly. Nat. Mater. 10, 291–295 (2011).
Yamashita, M. & Okamoto, H. (eds) English, Material Desings and New Physical Properties in MX- and MMX-Chain Compounds (Springer, Verlag Wien, 2013).
Bong, D. T., Clark, T. D., Granja, J. R. & Ghandiri, M. R. Self-assembling organic nanotubes. Angew. Chem. Int. Ed. 40, 988–1011 (2001).
Shimizu, T. et al. Self-organized nanotube materials and their application in bioengineering. Polym. J. 46, 831–858 (2014).
Ludwig, R. Water: from clusters to the bulk. Angew. Chem. Int. Ed. 40, 1808–1827 (2001).
Maruitz, K. A. & Moore, R. B. State of understanding of Nafion. Chem. Rev. 104, 4535–4586 (2004).
Sadakiyo, M., Yamada, T. & Kitagawa, H. Rational designs for highly proton-conductive metal−organic frameworks. J. Am. Chem. Soc. 131, 9906–9907 (2009).
Ramaswamy, P., Wang, N. E. & Shimizu, G. K. H. MOFs as proton conductors – challenges and opportunities. Chem. Soc. Rev. 43, 5913–5932 (2014).
Agmon, N. The Grotthuss mechanism. Chem. Phys. Lett. 244, 456–462 (1995).
Kreuer, K.-D., Paddison, S. J., Spohr, E. & Schuster, M. Transport in proton conductors for fuel-cell applications: simulations, elementary reactions, and phenomenology. Chem. Rev. 104, 4637–4678 (2004).
Stejskal, E. O. & Tanner, J. E. spin diffusion measurements: spin echoes in the presence of a time – dependent field gradient. J. Chem. Phys. 42, 288–292 (1965).
Dippel, Th. & Kreuer, K. D. Proton transport mechanism in concentrated aqueous solutions and solid hydrates of acids. Solid State Ion. 46, 3–9 (1991).
Callaghan, P. T. Translational Dynamics & Magnetic Resonance (OXFORD, New York, 2011).
Stallmach, F. et al. Evidence of anisotropic self-diffusion of guest molecules in nanoporous materials of MCM-41. J. Am. Chem. Soc. 122, 9237–9242 (2000).
Gong, X. et al. Self-diffuion of water, ethanol and decafluropentane in perfluorosulfonate ionomer by pulse field gradient NMR. Polymer 42, 6485–6492 (2001).
Otake, K.-i, Otsubo, K., Sugimoto, K., Fujiwara, A. & Kitagawa, H. Ultrafine metal-organic right square prism shaped nanowires. Angew. Chem. Int. Ed. 55, 6448–6451 (2016).
Wilkins, R. G. Kinetics and Mechanisms of Transition Metal Complexes. (Wiley-VCH, Weinheim, 2002).
Kreuer, K.-D., Rabenau, A. & Weppner, W. Vehicle mechanism, a new model for the interpretation of the conductivity of fast proton conductors. Angew. Chem. Int. Ed. 21, 208–209 (1982).
Maupin, C. M., Aradi, B. & Voth, G. A. The self-consistent charge density functional tight binding method applied to liquid water and the hydrated excess proton: Benchmark simulations. J. Phys. Chem. B. 114, 6922–6931 (2010).
Nakai, H., Sakti, A. W. & Nishimura, Y. Divide-and-conquer-type density-functional tight-binding molecular dynamics simulations of proton diffusion in a bulk water system. J. Phys. Chem. B. 120, 217–221 (2016).
Mills, R. Self-diffusion in normal and heavy water in the range 1–45.deg. J. Phys. Chem. 77, 685–688 (1973).
Meiboom, S. Nuclear magnetic resonance study of the proton transfer in water. J. Chem. Phys. 34, 375–388 (1961).
Roberts, N. K. & Northey, H. L. Proton and deuteron mobility in normal and heavy water solutions of electrolytes. J. Chem. Soc. Faraday Trans. 70, 253–262 (1974).
Takaiwa, D. et al. Phase diagram of water in carbon nanotubes. Proc. Natl Acad. Sci. USA 105, 39–43 (2008).
Mochizuki, K. & Koga, K. Solid−liquid critical behavior of water in nanopores. Proc. Natl Acad. Sci. USA 112, 8221–8226 (2015).
Liu, Z. K., Muldrew, R. G. & Elliott, J. A. W. Measurement of freezing point depression of water in glass capillaries and the associated ice front shape. Phys. Rev. E. 67, 061602 (2003).
Tunuguntla, R. H., Allen, F. I., Kim, K., Belliveau, A. & Noy, A. Ultrafast proton transport in sub-1-nm diameter carbon nanotube porins. Nat. Nanotech. 11, 639–644 (2016).
Acknowledgements
This work was supported by Core Research for Evolutional Science and Technology (CREST) “Creation of Innovative Functions of Intelligent Materials on the Basis of the Element Strategy”, ACCEL from Japan Science and Technology Agency (JST), JSPS KAKENHI Grant Numbers JP20350030, JP23245012, JP15H05479, JP17H05366, JP19K05494 and JP19H04572 (Coordination Asymmetry) and MEXT Project for Developing Innovation Systems (Regional Innovation Strategy Support Program “Kyoto Next-Generation Energy System Creation Strategy”). Theoretical calculations were supported in part by the supercomputer of ACCMS, Kyoto University. Synchrotron XRD measurements were supported by the Japan Synchrotron Radiation Research Institute (JASRI) (Proposal Nos. 2016A1343, 2016A1361, 2016B1438, 2017A1349, 2017A1366, 2017B1483, and 2018A1434).
Author information
Authors and Affiliations
Contributions
K. Otsubo, J.M.T., and H.K. conceived and designed this study. K. Otake contributed to all of the experimental works. NMR measurements were conducted and analysed by S.D., J.M.T., and R.I. Theoretical calculation was performed by T.K. QM-MD simulation were conducted by C-P.C., A.W.S., Y.N. and H.N. K.S. and A.F. contributed to the single-crystal structure analysis. K. Otake, K. Otsubo, T.K., J.M.T., R.I., C-P.C., A.W.S., Y.N., H.N., and H.K. co-wrote the manuscript. All authors commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Valeska Ting and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Otake, Ki., Otsubo, K., Komatsu, T. et al. Confined water-mediated high proton conduction in hydrophobic channel of a synthetic nanotube. Nat Commun 11, 843 (2020). https://doi.org/10.1038/s41467-020-14627-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-14627-z
This article is cited by
-
2H-NMR study of molecular reorientation of D2O confined into the slit-shaped micropores of activated carbon fiber
Adsorption (2024)
-
The ω3 scaling of the vibrational density of states in quasi-2D nanoconfined solids
Nature Communications (2022)
-
A stable quasi-solid electrolyte improves the safe operation of highly efficient lithium-metal pouch cells in harsh environments
Nature Communications (2022)
-
Short hydrogen-bond network confined on COF surfaces enables ultrahigh proton conductivity
Nature Communications (2022)
-
Two-dimensional monolayer salt nanostructures can spontaneously aggregate rather than dissolve in dilute aqueous solutions
Nature Communications (2021)