Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Long-range exciton transport and slow annihilation in two-dimensional hybrid perovskites


Two-dimensional hybrid organic-inorganic perovskites with strongly bound excitons and tunable structures are desirable for optoelectronic applications. Exciton transport and annihilation are two key processes in determining device efficiencies; however, a thorough understanding of these processes is hindered by that annihilation rates are often convoluted with exciton diffusion constants. Here we employ transient absorption microscopy to disentangle quantum-well-thickness-dependent exciton diffusion and annihilation in two-dimensional perovskites, unraveling the key role of electron-hole interactions and dielectric screening. The exciton diffusion constant is found to increase with quantum-well thickness, ranging from 0.06 ± 0.03 to 0.34 ± 0.03 cm2 s−1, which leads to long-range exciton diffusion over hundreds of nanometers. The exciton annihilation rates are more than one order of magnitude lower than those found in the monolayers of transition metal dichalcogenides. The combination of long-range exciton transport and slow annihilation highlights the unique attributes of two-dimensional perovskites as an exciting class of optoelectronic materials.


Two-dimensional (2D) Ruddlesden-Popper phase organic–inorganic metal halide perovskites have emerged as an exciting class of optoelectronic materials. Efficient light emitting diodes (LED), lasers, and solar cells with superior stability over their 3D counterparts have been demonstrated1,2,3,4,5,6,7,8,9,10,11. 2D perovskites have a general structure of (RNH3)2(A)n−1BnX3n+1, where R is an alkyl or aromatic moiety, A is an organic cation, B is a metal cation, and X is a halide12,13,14. The variable n corresponds to the number of the inorganic quantum-well layers sandwiched between the long organic chains RNH3. Because dielectric screening is low from the surrounding organic ligands, excitons with binding energy as high as 0.5 eV dominate the optical properties of these materials15,16,17,18,19,20. The exciton binding energy for the n = 1 structure is comparable with those found in monolayer transition metal dichalcogenides (TMDCs)18,21. The structure of 2D perovskites is extremely programmable; for instance, continuous tuning of the exciton emission over a wide range of energy can be achieved by either changing n or the halide in the composition11,22. In addition, both the R and A site cations can be modified to influence electron-phonon coupling, dielectric environment, and lattice disorder3,19,23. The highly tunable structure coupled with emission quantum yield as high as 79%3 represents a significant advantage of 2D perovskites over other 2D semiconductors.

To harvest excitons in a device, a thorough understanding of exciton transport and annihilation in 2D perovskites is necessary. For example, the ability to transport excitons over long distances is necessary for solar cell performance. On the other hand, many-body exciton–exciton annihilation (EEA), a form of Auger recombination, is an important loss mechanism that limits the density of excitons and ultimately determines the efficiency of lasers and LEDs. EEA occurs when an exciton recombines nonradiatively by transferring its kinetic energy to another exciton. Rapid EEA rates are usually associated with nanostructures with large exciton binding energies because of the enhanced electron-hole interactions in these systems24,25,26, representing a key challenge in realizing their optoelectronic applications.

Despite the impressive progress made in the optoelectronic devices based on 2D perovskites11, the understanding of exciton transport is extremely limited and currently there is no direct measurement on exciton diffusion. Because of the requirement of two excitons in proximity, exciton diffusion typically proceeds annihilation in 1D or 2D materials. EEA can occur either in the diffusion-limited or the reaction-limited regime27. To differentiate these two regimes, measurements of exciton population dynamics in both spatial and temporal domains are required. However, the majority of studies on exciton annihilation so far are based on time-resolved photoluminescence (PL) or transient absorption (TA) spectroscopy that offers no spatial resolution, leading to annihilation rates convoluted with exciton diffusion constants28,29,30, making it difficult to elucidate factors that control these two processes independently.

To address this challenge, here we employ transient absorption microscopy (TAM) as a direct means to image exciton population in space and in time to disentangle exciton diffusion and annihilation in 2D perovskites. We have demonstrated in a previous work the capability of TAM in imaging free carrier diffusion and extracting Auger recombination constants in bulk 3D perovskites31. Distinct from the results in 3D perovskites, the measurements on 2D perovskites elucidated the critical role of electron-hole interactions in controlling exciton dynamics and transport. These results showcase the unique ability of 2D perovskites in achieving a combination of large exciton binding energy, long-range exciton transport, and slow annihilation, suggesting their large potential in optoelectronic applications.


Structural and optical characterizations

2D perovskites with composition of (C4H9NH3)2(CH3NH3)n−1PbnI3n+1 ((BA)2(MA)n−1PbnI3n+1) were investigated in this study, as schematically illustrated in Fig. 1a, b. Pure-phase single crystals with n ranging from 1 to 5 were mechanically exfoliated on fused silica for the optical measurements as shown in Supplementary Fig. 1. The single-crystalline samples allow for the elucidation of the role of dielectric screening by systematically investigating the dependence on quantum-well thickness n. In these samples, the [PbI6]4− octahedral layers are parallel to the substrate surface, as shown in the X-ray diffraction profiles (Supplementary Fig. 2). In order to correctly determine the exciton densities for the optical measurements, we carried out microreflectance and transmittance spectroscopy as well as atomic force microscopy (AFM) measurements (Supplementary Fig. 3). By solving the Fresnel’s equations, we obtained the linear extinction coefficient α (Fig. 1c) and the refractive index (Supplementary Fig. 4) as detailed in Supplementary Note 1.

Fig. 1: The structure and optical characterizations of 2D perovskite quantum wells.

a Illustration of the crystal structures and excitons of (BA)2(MA)n-1PbnI3n+1 with n varying from 1 to 5. b Scheme of exciton diffusion and annihilation. c Linear extinction coefficient α and d PL spectra of (BA)2(MA)n-1PbnI3n+1 with n varying from 1 to 5.

Excitons dominate the optical responses in all five structures as evidenced in the absorption and PL spectra. In the absorption spectra, narrow exciton resonances to the lower-energy side of the broad continuum absorption band are observed (Fig. 1c). Sharp exciton emission peaks correlated with the exciton absorption resonances are seen in the PL spectra (Fig. 1d), indicating high quality and phase-purity of the single crystals. These 2D perovskite quantum wells are very efficient absorbers with extinction coefficient α on the order of 105 cm−1 (Fig. 1c), resulting from the strongly bound excitons with large oscillator strengths, similar to TMDCs32. Exciton binding energy Eb for n = 1 is found to be as large as 470 meV18, with a Bohr radius a0 of around 1 nm15,16. As shown in Fig. 1c, exciton oscillator strength decreases as n increases, which can be explained by that the oscillator strength is proportional to Eb 18,33. Eb has been reported to reduce to 125 meV when n increases to 518. The integral α per Pb atom converge at high energy side of the spectra (Supplementary Fig. 5). This is because the sum of the oscillation strength over the entire spectral range is determined by the number of electrons involved in the transition, which should be the same for each Pb atom in [PbI6]4−. In other words, due to the stronger bound excitons, more oscillator strength is concentrated in the exciton absorption band for the n = 1 than for the n > 1 quantum wells. The exciton resonance, as given by EspEb (Esp is the single-particle bandgap), shifts to higher energy as n decreases (Figs. 1c, d). This is due to the quantum confinement along the out-of-plane direction which gives rise to the enlarging Esp with a decreasing n value. The enlarged Esp is counteracted to some extent by the increased Eb.

TAM imaging of exciton transport

We employed TAM to image the exciton population dynamics in both spatial and temporal domains (more details in Supplementary Fig. 6 and Methods). We have recently demonstrated TAM as an effective tool for imaging exciton transport in 2D semiconductors34,35. In these measurements, the exciton population was monitored by probing resonantly at the photoinduced bleach of the exciton bands. Figure 2a shows the representative TA spectra for n= 5, and the photoinduced bleach band at 1.86 eV is consistent with the exciton absorption resonance in Fig. 1c. The probe beam was scanned relative to the pump in space using a Galvanometer scanner to image exciton transport. 2D TAM images were obtained by plotting pump induced change in probe transmission ∆T as a function of probe position. At time zero, initial exciton distribution was given by a Gaussian pump beam with a pulse duration of approximately 300 fs, \( N\left( {x,y,0} \right) = N_0{\mathrm{exp}}\Big [ - \frac{{(x - x_0)^2}}{{2\sigma _{x,0}^2}} - \frac{{(y - y_0)^2}}{{2\sigma _{y,0}^2}}\Big] \). TAM images at later delay times measured the exciton diffusion away from the initial location that results in a population distribution of \( N\left( {x,y,t} \right) = N_t{\mathrm{exp}}\Big[ - \frac{{(x - x_0)^2}}{{2\sigma _{x,t}^2}} - \frac{{(y - y_0)^2}}{{2\sigma _{y,t}^2}}\Big ] \).

Fig. 2: Transient absorption spectroscopy and microscopy for n = 5.

a TA spectra for (BA)2(MA)4Pb5I16, showing the photoinduced bleaching of the exciton resonance at 1.86 eV. b Two-dimensional TAM imaging of (BA)2(MA)4Pb5I16 with pump-probe delay time varying from 2 ps to 2 ns. Pump beam is fixed while probe beam scanning to form the images. Pump photon energy: 1.97 eV, probe photon energy: 1.86 eV. Excitation density: 2.4 × 1012 cm−2. Maximum intensities are normalized to 1 by multiplying with the factors shown in the images. Scale bar: 1 μm.

The exciton population was observed to expand as pump-probe delay time increased. The representative TAM images for n = 5 at time delays ranging from 2 ps to 2 ns are illustrated in Fig. 2b. These TAM measurements reflect the in-plane exciton transport in the quantum wells because the [PbI6]4− octahedral layers are parallel to the substrate surface. The exciton diffusion in ab plane is isotropic so that σx,t = σy,t = σt. To reduce the data redundancy, one-dimensional scanning N(x, 0, t) instead of two-dimensional imaging N(x, y, t) was performed for the following TAM measurements. 1D imaging also allowed more measurement cycles to improve the signal-to-noise ratio. Although the pump and probe beam sizes were diffraction-limited (100 s of nm in visible light range), the accuracy to determine the width of exciton population profile was determined by the signal-to-noise ratio and it was better than 50 nm31 (more details in Supplementary Note 2).

Modeling of exciton diffusion and annihilation

To extract both exciton diffusion constants and annihilation parameters, we carried out exciton-density-dependent TAM measurements. The initial exciton densities were kept below 2.4 × 1012 cm−2, well below the Mott density estimated by \(a_0^{ - 2} = 10^{14}{\mathrm{cm}}^{ - 2}\); thus, excitons remained the main excited-state species. All the measurements were performed in the linear regime so that the TA signal was proportional to exciton density (Supplementary Fig. 7), i.e., ΔT N. When exciton–exciton annihilation is negligible at low exciton densities, the time and spatial dependent exciton density is given by,

$$ \frac{{\partial N(x,{\mathrm{y}},t)}}{{\partial t}} = D\left[ {\frac{{\partial ^2N\left( {x,{\mathrm{y}},t} \right)}}{{\partial x^2}} + \frac{{\partial ^2N\left( {x,{\mathrm{y}},t} \right)}}{{\partial y^2}}} \right] - k_1N\left( {x,y,t} \right) $$

where D is the diffusion constant, k1 is the exciton recombination rate. Under this condition, the experimentally measured \( \sigma _t^2 - \sigma _0^2 \) corresponds to the mean squared distance travelled by the excitons, and the diffusion constant \( D = \frac{{\sigma _t^2 - \sigma _0^2}}{{2t}} \).

At high densities, the spatial-temporal population distribution reflects both exciton diffusion and annihilation. EEA is a bimolecular process, which is represented by an additional second-order term in the rate equation. Further, third-order Auger recombination of free charge carriers is also possible for n > 1 quantum wells, as a finite free carrier population exists due to smaller exciton binding energy20. Therefore, there are two additional terms to Eq. 1,

$$ \frac{{\partial N(x,y,t)}}{{\partial t}} = \ D\left[ {\frac{{\partial ^2N\left( {x,y,t} \right)}}{{\partial x^2}} + \frac{{\partial ^2N\left( {x,{\mathrm{y}},t} \right)}}{{\partial y^2}}} \right] \\ - k_1N\left( {x,y,t} \right) - k_2N^2\left( {x,y,t} \right) - k_3N^3\left( {x,y,t} \right) $$

where k2 describes EEA rate and k3 corresponds to the Auger recombination rate of free carriers.

To understand the spatial-temporal behavior, we modeled the exciton population as function of pump-probe delay time and probe position using Eq. 2. As an illustration, Fig. 3a shows the 3D surfaces representing the temporal and spatial distribution of excitons at both low- and high-density limits, which is simulated by numerically solving Eq. 2 to obtain \( N\left( {x,0,t} \right) = N_t{\mathrm{exp}}[\frac{{ - (x - x_0)^2}}{{2\sigma _t^2}}] \), taking into account the convolution with the probe beam (~500 nm, full width at half maximum). Exciton population decays faster at higher densities as expected from more significant annihilation. Broadening of \( \sigma _t^2 \) is observed at high densities, which can be explained by faster EEA at the center compared to the edge of the pump beam due to the higher exciton density. Instead of plotting the spatial-temporal distribution of excitons N(x, 0, t) in 3D, we depicted \( \sigma _t^2 \) from the fitting of the Gaussian profiles (Fig. 3b, c) as well as the ∆T(0, 0, t) at the center (0 pump-probe spatial separation) as a function of pump-probe delay time, which conveyed the same information. The fitting results are shown in Fig. 3b–e for n = 5. The experimental and simulated results for n ranging from 1 to 4 quantum wells are illustrated in Fig. 4. The model has satisfactorily fitted the experimental results with the initial exciton density varying over one order of magnitude using the same set of parameters for each n. The initial exciton densities were determined experimentally using absorption coefficient shown in Fig. 1c. A deviation from the modeling by around 5% can be seen in the first 100 ps for n = 1, which is likely due to defect trapping of the excitons that is not included in the modeling. Defect density was the highest in n = 1, and probably not all the defects were passivated by the pump photons under our experimental conditions30. For n ranging from 2 to 5, such deviation was not observed because defect density decreased in thicker quantum wells and the pump fluences used were sufficiently high to passivate the defects30. The extracted D, k1, k2, and k3 from the fitting are summarized in Table 1. Sensitivity analysis of the model to the parameters is shown in Supplementary Fig. 8.

Fig. 3: Exciton population dynamics for n = 5.

a 3D population surface N(x, 0, t) simulated at initial exciton densities of 1.5 × 1011 cm−2 (low-density limit, gray surface) and 2.4 × 1012 cm−2 (high-density limit, blue surface). bc Experimental exciton population spatial profiles at different delay time measured by TAM with initial excitation densities of 1.5 × 1011 cm−2 (b) and 2.4 × 1012 cm−2 (c). The solid lines are fits to a Gaussian function to obtain \(\sigma _t^2\). de Experimental (symbols) and simulated (solid lines) ∆T at 0 pump-probe separation (d) and time evolution of \( \sigma _t^2 \) (e) with excitation densities ranging from 1.5 × 1011 cm−2 to 2.4 × 1012 cm−2. Pump photon energy: 1.97 eV, probe photon energy: 1.86 eV.

Fig. 4: Exciton population dynamics for n ranging from 1 to 4.

ad Experimental (symbols) and fitted (solid lines) time evolution of \( \sigma _t^2 \). eh Experimental and fitted time evolution of ∆T at 0 pump-probe separation. n = 1 (a, e), n = 2 (b, f), n = 3 (c, g), and n = 4 (d, h). Pump photon energies are 2.61 eV, 2.32 eV, 2.14 eV, and 2.14 eV for n ranging from 1 to 4, respectively. Probe photon energies are 2.43 eV, 2.18 eV, 2.03 eV, and 1.97 eV for n ranging from 1 to 4, respectively. The error bars indicate the standard error of Gaussian fit of the exciton population spatial profiles.

Table 1 Exciton diffusion constant and recombination rate constants for (BA)2(MA)n-1PbnI3n+1.

The n dependence of exciton diffusion and annihilation

Both exciton diffusion constant D and diffusion length L0 exhibit strong dependence on n. As shown in Table 1 and Fig. 5a, D increases as n increases, from 0.06 ± 0.03 (n = 1) to 0.34 ± 0.03 cm2 s−1 (n = 5). Within the band transport picture36, the diffusion constant is determined by \(D = \frac{{\tau _{\mathrm{s}}{\mathrm{k}}T}}{m}\), where τs is the momentum relaxation time corresponding to the inverse of the sum of all scattering rates, k is the Boltzmann constant, T is temperature, and m is the reduced mass of the exciton. m was reported to be only weakly dependent on n18, and therefore the n dependence of D is more likely resulting from the difference in τs. The scattering sources include carriers, phonons, defects, and impurities. Defect density has been found to be higher for n = 1 than the thicker quantum wells30, which contributes to a more frequent defect scattering (a shorter τs) and a lower D. Dielectric screening could also play a role. As the n value increases from 1 to 5, the thickness of inorganic layer grows from 0.6 to 3 nm leading to the effective optical-frequency dielectric constant enlarging from 4 to 5.537. Because the scattering by charge carriers, polar optical phonons, and charge impurities are coulombic in nature, the reduced Coulomb interactions in the thicker quantum wells with higher dielectric constant results in a longer τs. The exciton diffusion constants measured for the 2D perovskites are consistent with the carrier diffusion constant of around 1 cm2 s−1 at the 3D limit of n = ∞38.

Fig. 5: Exciton diffusion constant, diffusion length, and annihilation rate as a function of n.

a Exciton diffusion constant D and diffusion length L0 for n ranging from 1 to 5. D and L0 increase as n increases. The error bars are estimated from the sensitivity of model to the parameters. b Total annihilation rate as a function of n for (BA)2(MA)n-1PbnI3n+1, showing enhanced annihilation at decreasing n. As a comparison, the exciton recombination rates k1 are denoted by the circles.

Long-range exciton transport over hundreds of nanometers is achieved in all five quantum-well structures. We calculate exciton diffusion length by \(L_0 = \sqrt {2D/k_1}\) and L0 as a function of n is presented in Fig. 5a. L0 increases from 160 to 670 nm as n increases from 1 to 5 (Fig. 5a), due to the combined effects of higher diffusion constant and slower recombination rate k1. The diffusion length in all five structures is on the same order or longer than the thickness of effective layer of solar cell devices10.

It is possible that photon recycling that has been proposed to enhance carrier diffusion in 3D perovskites contributes to the long-range exciton transport observed here39,40,41. To differentiate the contributions from photon recycling from pure exciton diffusion, we have carried out Monte Carlo simulations as shown in Supplementary Fig. 9. As detailed in Supplementary Note 3, both electronic transport and photonic transport from photon recycling can be microscopically described as random walks but with significantly different parameters (Supplementary Table 1). For electronic transport, each step of the random walk during τs between scattering events is on the order of nm. To achieve a final average transport distance of 100 s of nm, excitons need to walk around 105 steps randomly, resulting in a Gaussian distribution of transport distance. For photonic transport, the step size is much larger, on the order of 100 s of nm as determined by the penetration depth α−1. To achieve a final average transport distance of 100 s of nm, the number of steps for photons is small, such as 1 or 2, which results in a distribution of transport distance strongly deviates from the Gaussian type. Therefore, we can use the TAM profiles to determine if transport via photon recycling playing a role by examining the spatial distributions of the excitons. As shown in Supplementary Fig. 9, the exciton population profiles are described very well by Gaussian functions. Therefore, we conclude that photonic contributions from photon recycling in exciton transport is negligible.

EEA takes place at densities of around 1011 cm−2 or lower, corresponding to an average exciton–exciton distance d > 30 nm, much larger than the exciton size of around 1–2 nm15. Thus, exciton diffusion must proceed annihilation. Note that Auger recombination of free carriers contributes significantly less than EEA at density of around 1011 cm−2; thus, we focus our discussion on EEA rate k2. We find that k2 decreases with n; for n = 5, k2 is determined to be 1.3 × 10−3 cm2 s−1, which is an order of magnitude lower than that of 1.7 × 10−2 cm2 s−1 for n = 1. For all five structures, exciton diffusion constants are significantly larger than annihilation rates (D k2). Therefore, EEA is reaction-limited instead of diffusion-limited, i.e., only a fraction of exciton encounters result in annihilation. We use the ratio of k2/D to describe the annihilation probability per encounter as given in Table 1. Although excitons are the most mobile in n = 5 and they encounter at the highest rate, only about 0.4% of the encounters result in annihilation. Annihilation probability increases by two orders of magnitudes to 30% for n = 1. The reaction-limited EEA in 2D perovskites is in contrast to the diffusion-limited EEA in other low-dimensional nanostructures, such as single-walled carbon nanotubes27,42, which suggests that exciton diffusion and annihilation can be separately optimized.

The strong n dependence of k2 underscores the importance of electron-hole interactions and dielectric screening in exciton annihilation26. EEA is mediated by the coupling between the transition dipole for promoting exciton 1 to the higher excited state and that for exciton 2 to decay to the ground state26. As n increases, the exciton wavefunction becomes located only in the inorganic layer with higher dielectric constant (Fig. 1a), which enhances dielectric screening. Therefore, for thicker quantum wells, the dipole-dipole interaction is weakened by more effective dielectric screening, leading to slower k2. k2 shares a similar n dependence as the exciton binding energy Eb because the dielectric screening also reduces Eb24. Another factor could also play a role is the spatial overlap between the initial and final exciton wavefunctions. As Eb increase, exciton states contain components corresponding to electron and hole wavefunctions with large momenta, relaxing the requirement of momentum conservation24. For Auger recombination of free carriers, a maximum is observed for k3 when n = 3. The nonmonotonic n dependence of k3 can be explained by the combination of the following two competing effects: (1) similar to EEA, the Auger recombination probability for free carriers per encounter decreases with increasing n due to enhanced screening; and (2) the fraction of free carriers increases with as n increases.

The observation of enhanced EEA rates at larger exciton binding energies in 2D perovskites are consistent with those reported in single-walled carbon nanotubes and colloidal quantum dots24,26,42,43. We note that there are a few previous studies on EEA and Auger recombination in 2D perovskites; however, an explicit n dependence of EEA rate has not been reported. Delport et al.30 reported EEA rate was nearly independent on n using time-resolved PL spectroscopy. The discrepancy between our results and those reported in Delport et al.30 could be due to that PL measurements only monitor a subset of the exciton population, namely the emissive species. In contrast, the photoinduced bleach TA signal reflects to all exciton population. Using TA spectroscopy, Chen et al.29 reported both k2 and k3 increases as n decreases; however, they interpreted the k2 in terms of bimolecular recombination of free carriers instead of EEA. Auger recombination in mixed-phase 2D-3D perovskites has been studied by time-resolved THz measurements by Milot et al.;28 however, THz measurements are sensitive to free carriers instead of excitons.

Comparison with other 2D semiconductors

We compare exciton transport and annihilation properties of 2D perovskites to those of TMDCs. We have measured the exciton diffusion constant in exfoliated WS2 monolayers34 to be around 2 cm2 s−1, more than one order higher than the n = 1 quantum-well. A possible reason is the formation of exciton polarons44 that have larger effective mass leading to slower diffusion. Another feasible explanation is that structural disorder is much larger in hybrid perovskites than in TMDCs due to the ionic nature. Structural disorder results in fluctuations in the energy landscape, slowing down exciton transport45. We suggest that exciton transport in 2D perovskites can be further enhanced through structural tuning to increase rigidity and reduce structural disorder, for instance, by employing phenyl group motifs at the R site3.

Notably, exciton annihilation is significantly reduced in 2D perovskites in comparison to TMDCs. In a previous work, we determined the exciton–exciton annihilation rate to be 0.41 cm2 s−1 for monolayer WS246, similar to other TMDCs47, which is more than one order of magnitude higher than that of n = 1. This large difference in exciton annihilation rates given similar exciton binding energies in two materials is intriguing and could be related to the unique dielectric function of hybrid perovskites, for instance, as the result of the motion of the polar organic cations48. Further, an advantage brought by the highly tunable structure of 2D perovskites is the ability to modulate Coulomb interactions to suppress annihilation through composition tuning. Different from TMDCs that undergo direct to indirect bandgap transition at bilayer49, 2D perovskites are direct bandgap semiconductors with high PL quantum yields regardless of the value of n.

As a guide, we plot the total annihilation rates (\(k_2N + k_3N^2\)) as a function of exciton densities for n ranging from 1 to 5 in Fig. 5b, showing the reduction of annihilation loss by increasing n. k2 becomes larger than k1 at exciton density as low as 2 × 1010 cm−2 for n = 1, indicating that EEA turns into the dominant recombination pathway. This is probably one of the key reasons why high-performance solar cell and LED based on n = 1 2D perovskites have not been successfully demonstrated so far. For n = 5, the switch over occurs at higher exciton density around 1011 cm−2. The benefit of the reduction in annihilation is most significant for increasing from n = 1 to n ranging from 2 to 4, suggesting that these structures with Eb ranging from 150 to 250 meV might be optimal for light emitting devices with the combined benefits of large exciton binding energy and slow annihilation. This is consistent with a recent study50 in which van-der-Waals-coupled 2D perovskite multi-quantum-wells were shown to have better light emitting performance than 3D perovskites due to strongly bound excitons. For solar cells, quantum wells with large n are suitable because of the combined benefits of the small exciton binding energy and long-range diffusion. Further suppression of EEA should be possible through modulating R and A site organic cations to modify dielectric screening. Such promise has been demonstrated recently, for instance, a study has showed that Auger recombination rate in the hybrid perovskite nanocrystals containing polar organic cations is significantly lower than in the fully inorganic Cs-based ones51.


A major challenge in realizing optoelectronic applications for low-dimensional nanostructures is to achieve long-range transport and suppressed annihilation while maintaining large exciton binding energy. As unraveled by the spatially- and temporally resolved measurements reported here, 2D perovskites present unique opportunities in addressing this challenge. The exciton binding energies of 2D perovskites are comparable to those found in TMDCs but their annihilation rates are orders of magnitude lower. These properties make 2D perovskites excellent candidates for light emitting applications. Further, 2D perovskites are also promising as solar cell materials, with long-range exciton diffusion over hundreds of nanometers. Finally, their structures are uniquely programmable, which allows for further enhancement of exciton transport and suppression of annihilation through composition engineering.


Synthesis of 2D halide perovskite crystals

The 2D Ruddlesden-Popper phase halide perovskite crystals (BA)2(MA)n−1PbnI3n+1 (n ranging from 1 to 5) were synthesized via a solution precipitation reaction. PbO powders, hydroiodic acid (HI, 57 wt.% in H2O), hypophosphorous acid (H3PO2, 50 wt. % in H2O) were purchased from Sigma–Aldrich. Methylammonium iodide (MAI), formamidinium iodide (FAI), n-Butylammonium bromide (BABr), and n-Butylammonium iodide (BAI) were purchased from Greatcell Solar Ltd. All chemicals were used as received. Commercial Scotch tapes (3 M) were used to exfoliate 2D halide perovskite crystals. The mechanical exfoliation was performed in N2-filled glovebox. The thicknesses of the flakes were measured by AFM (Veeco Dimension 3100). More details on the synthesis and sample preparation can be found in Supplementary Note 4.

Optical absorption and photoluminescence (PL) measurements

A home-built microscope was used for the micro-absorption and PL spectroscopy measurements. For the micro-absorption measurements, a halogen tungsten lamp was used as white light source, which was focused by objective on sample to form light spot with size of around 2 µm. The reflective or transmitted light was collected by an objective (×40, NA = 0.6, Nikon), and detected by a spectrometer (Andor Shamrock 303i) and CCD (Andor Newton 920) for spectral analysis. For the PL measurements, a picosecond pulse laser with wavelength of 447 nm was used as excitation light and an objective (×40, NA = 0.6, Nikon) was employed to focus the excitation light on the sample and collect the epic scattered PL light. The same spectrometer and CCD combo as described above were used for PL spectral analysis.

Transient absorption microscopy (TAM)

The home-built TAM setup used in this study has been described in our previous publication31. Briefly, the output from two independent optical parametric amplifiers (OPAs, 400 kHz, ~300 fs, Light Conversion) served as pump and probe beam respectively, which were focused on sample with an objective (×60, NA = 0.95, Nikon). An acousto-optic modulator (Gooch and Housego, R23080-1) triggered by a lock-in amplifier (SR830, SRS, Inc.) was used to modulate the pump beam. A mechanical translation stage (Thorlabs, DDS600-E) was used to delay the probe with respect to the pump. A 2D Galvo mirror (Thorlabs GVS012) was employed to scan the probe beam relative to the pump beam in space (path 1 in Supplementary Fig. 6). Spatial filters were used to optimize the profile of the beams. The transmitted probe light was detected by an avalanche photodiode (APD) (Hamamatsu, C5331-04). The pump-induced change in the probe reflection (ΔT) was extracted by the lock-in amplifier.

Data availability

All data needed to evaluate the conclusions in the paper are present in the paper and/or the supplementary information. Correspondence and requests for materials should be addressed to L.H.

Code availability

Correspondence and requests for codes used in the paper should be addressed to L.H.


  1. 1.

    Yuan, M. et al. Perovskite energy funnels for efficient light-emitting diodes. Nat. Nanotechnol. 11, 872–877 (2016).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  2. 2.

    Wang, N. et al. Perovskite light-emitting diodes based on solution-processed self-organized multiple quantum wells. Nat. Photonics 10, 699 (2016).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Gong, X. et al. Electron–phonon interaction in efficient perovskite blue emitters. Nat. Mater. 17, 550–556 (2018).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  4. 4.

    Chen, Y. et al. 2D Ruddlesden–Popper perovskites for optoelectronics. Adv. Mater. 30, 1703487 (2018).

    Article  CAS  Google Scholar 

  5. 5.

    Quan, L. N. et al. Tailoring the energy landscape in quasi-2D halide perovskites enables efficient green-light emission. Nano Lett. 17, 3701–3709 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  6. 6.

    Su, R. et al. Room temperature long-range coherent exciton polariton condensate flow in lead halide perovskites. Sci. Adv. 4, eaau0244 (2018).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  7. 7.

    Li, M. et al. Enhanced exciton and photon confinement in Ruddlesden–Popper perovskite microplatelets for highly stable low‐threshold polarized lasing. Adv. Mater. 30, 1707235 (2018).

    Article  CAS  Google Scholar 

  8. 8.

    Tsai, H. et al. High-efficiency two-dimensional Ruddlesden–Popper perovskite solar cells. Nature 536, 312–316 (2016).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  9. 9.

    Wang, Z. et al. Efficient ambient-air-stable solar cells with 2D–3D heterostructured butylammonium-caesium-formamidinium lead halide perovskites. Nat. Energy 2, 17135 (2017).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Blancon, J. C. et al. Extremely efficient internal exciton dissociation through edge states in layered 2D perovskites. Science 355, 1288–1292 (2017).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  11. 11.

    Quan, L. N. et al. Perovskites for next-generation optical sources. Chem. Rev. 119, 7444–7477 (2019).

    CAS  Article  Google Scholar 

  12. 12.

    Mitzi, D. B. in Progress in Inorganic Chemistry (ed. Karlin K. D.) (John Wiley & Sons, Inc., 2007).

  13. 13.

    Mitzi, D. B. Synthesis, crystal structure, and optical and thermal properties of (C4H9NH3)2MI4 (M=Ge, Sn, Pb). Chem. Mater. 8, 791–800 (1996).

    CAS  Article  Google Scholar 

  14. 14.

    Dou, L. et al. Atomically thin two-dimensional organic-inorganic hybrid perovskites. Science 349, 1518–1521 (2015).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  15. 15.

    Hirasawa, M. et al. Magnetoreflection of the lowest exciton in a layered perovskite-type compound (C10H21NH3)2PbI4. Solid State Commun. 86, 479–483 (1993).

    ADS  CAS  Article  Google Scholar 

  16. 16.

    Tanaka, K. et al. Image charge effect on two-dimensional excitons in an inorganic-organic quantum-well crystal. Phys. Rev. B 71, 045312 (2005).

    ADS  Article  CAS  Google Scholar 

  17. 17.

    Yaffe, O. et al. Excitons in ultrathin organic-inorganic perovskite crystals. Phys. Rev. B 92, 045414 (2015).

    ADS  Article  CAS  Google Scholar 

  18. 18.

    Blancon, J. C. et al. Scaling law for excitons in 2D perovskite quantum wells. Nat. Commun. 9, 538 (2018).

    ADS  Article  CAS  Google Scholar 

  19. 19.

    Mauck, C. M. & Tisdale, W. A. Excitons in 2D organic–inorganic halide perovskites. Trends Chem. 1, 380–393 (2019).

    Article  Google Scholar 

  20. 20.

    Wu, X., Trinh, M. T. & Zhu, X. Y. Excitonic many-body interactions in two-dimensional lead iodide perovskite quantum wells. J. Phys. Chem. C 119, 14714–14721 (2015).

    CAS  Article  Google Scholar 

  21. 21.

    Chernikov, A. B. T. C. et al. Exciton binding energy and nonhydrogenic Rydberg series in monolayer WS2. Phys. Rev. Lett. 113, 076802 (2014).

    ADS  PubMed  Article  CAS  Google Scholar 

  22. 22.

    Saparov, B. & Mitzi, D. B. Organic–inorganic perovskites: structural versatility for functional materials design. Chem. Rev. 116, 4558–4596 (2016).

    CAS  PubMed  Article  Google Scholar 

  23. 23.

    Straus, D. B. & Kagan, C. R. Electrons, excitons, and phonons in two-dimensional hybrid perovskites: connecting structural, optical, and electronic properties. J. Phys. Chem. Lett. 9, 1434–1447 (2018).

    CAS  PubMed  Article  Google Scholar 

  24. 24.

    Wang, F., Wu, Y., Hybertsen, M. S., Heinz, T. F. Auger recombination of excitons in one-dimensional systems. Phys. Rev. B 73, 245424 (2006).

  25. 25.

    Klimov, V. V., Mikhailovsky, A. A., McBranch, D. W., Leatherdale, C. A. & Bawendi, M. G. Quantization of multiparticle auger rates in semiconductor quantum dots. Science 287, 1011–1013 (2000).

    ADS  CAS  PubMed  Article  Google Scholar 

  26. 26.

    Philbin, J. P. & Rabani, E. Electron-hole correlations govern Auger recombination in nanostructures. Nano Lett. 18, 7889–7895 (2018).

    ADS  CAS  PubMed  Article  Google Scholar 

  27. 27.

    Srivastava, A. & Kono, J. Diffusion-limited exciton-exciton annihilation in single-walled carbon nanotubes: a time-dependent analysis. Phys. Rev. B 79, 205407 (2009).

    ADS  Article  CAS  Google Scholar 

  28. 28.

    Milot, R. L. et al. Charge-carrier dynamics in 2D hybrid metal-halide perovskites. Nano Lett. 16, 7001–7007 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  29. 29.

    Chen, X. et al. Impact of layer thickness on the charge carrier and spin coherence lifetime in two-dimensional layered perovskite single crystals. ACS Energy Lett. 3, 2273–2279 (2018).

    CAS  Article  Google Scholar 

  30. 30.

    Delport, G. et al. Exciton-exciton annihilation in two-dimensional halide perovskites at room temperature. J. Phys. Chem. Lett., 10, 5153–5159 (2019).

    CAS  Article  Google Scholar 

  31. 31.

    Guo, Z., Manser, J. S., Wan, Y., Kamat, P. V., Huang, L. B. Spatial and temporal imaging of long-range charge transport in perovskite thin films by ultrafast microscopy. Nat. Commun. 6, 7471 (2015).

  32. 32.

    Li, Y. et al. Measurement of the optical dielectric function of monolayer transition-metal dichalcogenides: MoS2, MoSe2, WS2, and WSe2. Phys. Rev. B 90, 205422 (2014).

    ADS  Article  CAS  Google Scholar 

  33. 33.

    Perebeinos, V., Tersoff, J. & Avouris, P. Scaling of excitons in carbon nanotubes. Phys. Rev. Lett. 92, 257402 (2004).

    ADS  PubMed  Article  CAS  PubMed Central  Google Scholar 

  34. 34.

    Yuan, L., Wang, T., Zhu, T., Zhou, M. & Huang, L. Exciton dynamics, transport, and annihilation in atomically thin two-dimensional semiconductors. J. Phys. Chem. Lett. 8, 3371–3379 (2017).

    CAS  PubMed  Article  PubMed Central  Google Scholar 

  35. 35.

    Zhu, T. et al. Highly mobile charge-transfer excitons in two-dimensional WS2/tetracene heterostructures. Sci. Adv. 4, eaao3104 (2018).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  36. 36.

    Sze, S. M., Ng, K. K. Physics of semiconductor devices (John Wiley & Sons, 2006).

  37. 37.

    Soe, C. M. M. et al. Structural and thermodynamic limits of layer thickness in 2D halide perovskites. Proc. Natl Acad. Sci. USA 116, 58–66 (2019).

    PubMed  Article  CAS  PubMed Central  Google Scholar 

  38. 38.

    Hill, A. H., Kennedy, C. L., Massaro, E. S. & Grumstrup, E. M. Perovskite carrier transport: disentangling the impacts of effective mass and scattering time through microscopic optical detection. J. Phys. Chem. Lett. 9, 2808–2813 (2018).

    CAS  PubMed  Article  PubMed Central  Google Scholar 

  39. 39.

    Pazos-Outón, L. M. et al. Photon recycling in lead iodide perovskite solar cells. Science 351, 1430–1433 (2016).

    ADS  PubMed  Article  CAS  PubMed Central  Google Scholar 

  40. 40.

    Gan, Z. et al. The dominant energy transport pathway in halide perovskites: photon recycling or carrier diffusion? Adv. Energy Mater. 9, 1900185 (2019).

    Article  CAS  Google Scholar 

  41. 41.

    Bercegol, A. et al. Quantitative optical assessment of photonic and electronic properties in halide perovskite. Nat. Commun. 10, 1–8 (2019).

    CAS  Article  Google Scholar 

  42. 42.

    Ma, X. et al. Influences of exciton diffusion and exciton-exciton annihilation on photon emission statistics of carbon nanotubes. Phys. Rev. Lett. 115, 017401 (2015).

    ADS  PubMed  Article  CAS  Google Scholar 

  43. 43.

    Hou, X. et al. Engineering Auger recombination in colloidal quantum dots via dielectric screening. Nat. Commun. 10, 1750 (2019).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  44. 44.

    Thouin, F. et al. Phonon coherences reveal the polaronic character of excitons in two-dimensional lead halide perovskites. Nat. Mater. 69, 1 (2019).

    Google Scholar 

  45. 45.

    Raja, A. et al. Dielectric disorder in two-dimensional materials. Nat. Nanotechnol. 14, 832–837 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  46. 46.

    Yuan, L. & Huang, L. Exciton dynamics and annihilation in WS2 2D semiconductors. Nanoscale 7, 7402–7408 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  47. 47.

    Kumar, N. C. Q., Ceballos, F., He, D., Wang, Y. & Zhao, H. Exciton-exciton annihilation in MoSe2 monolayers. Phys. Rev. B 89, 125427 (2014).

    ADS  Article  CAS  Google Scholar 

  48. 48.

    Herz, L. M. How lattice dynamics moderate the electronic properties of metal-halide perovskites. J. Phys. Chem. Lett. 9, 6853–6863 (2018).

    CAS  PubMed  Article  Google Scholar 

  49. 49.

    Mak, K. F. L. C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).

    ADS  PubMed  Article  CAS  Google Scholar 

  50. 50.

    Xing, G. et al. Transcending the slow bimolecular recombination in lead-halide perovskites for electroluminescence. Nat. Commun. 8, 14558 (2017).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  51. 51.

    Eperon, G. E., Jedlicka, E. & Ginger, D. S. Biexciton Auger recombination differs in hybrid and inorganic halide perovskite quantum dots. J. Phys. Chem. Lett. 9, 104–109 (2017).

    PubMed  Article  CAS  PubMed Central  Google Scholar 

Download references


L.H. S.D., L.Y. and L.J. acknowledge the support from U.S. Department of Energy, Office of Basic Energy Sciences through award DE-SC0016356. L.D. acknowledges the support from U.S. Department of Defense, Office of Naval Research (Grant Number: N00014-19-1-2296, Program Manager: Dr. Paul Armistead and Dr. Joe Parker). E.S. acknowledges the support from Davidson School of Chemical Engineering of Purdue University.

Author information




S.D. and L.H. designed the experiments. S.D., L.Y. and L.J. carried out the optical measurements. E.S. and L.D. contributed to sample growth and characterizations. S.D., L.Y. and L.H. analyzed experimental data. S.D. and L.H. wrote the manuscript with input from all authors.

Corresponding author

Correspondence to Libai Huang.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Guichuan Xing and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Deng, S., Shi, E., Yuan, L. et al. Long-range exciton transport and slow annihilation in two-dimensional hybrid perovskites. Nat Commun 11, 664 (2020).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing