Control over carrier type and doping levels in semiconductor materials is key for optoelectronic applications. In colloidal quantum dots (CQDs), these properties can be tuned by surface chemistry modification, but this has so far been accomplished at the expense of reduced surface passivation and compromised colloidal solubility; this has precluded the realization of advanced architectures such as CQD bulk homojunction solids. Here we introduce a cascade surface modification scheme that overcomes these limitations. This strategy provides control over doping and solubility and enables n-type and p-type CQD inks that are fully miscible in the same solvent with complete surface passivation. This enables the realization of homogeneous CQD bulk homojunction films that exhibit a 1.5 times increase in carrier diffusion length compared with the previous best CQD films. As a result, we demonstrate the highest power conversion efficiency (13.3%) reported among CQD solar cells.
Colloidal quantum dots (CQDs) have attracted intense attention for optoelectronic applications, including light-emitting diodes1,2, photodetectors3,4, lasers5, and photovoltaic devices6,7,8. The broad tunability of their optical and electrical properties through size9,10 and surface chemistry modification6,11 enables bottom-up design for function and performance. The understanding and manipulation of these properties has triggered continued progress in the performance of CQD devices. In solar cells, improvements in synthesis12, surface passivation13,14, and device architecture6,15 have enabled advances in power conversion efficiency (PCE), which has now reached certified values of 12% in single-junction solar cells16.
Major strides in improving the performance of CQD solar cells have been achieved through increasing the carrier diffusion length (LD), which provides improved charge extraction efficiency14,16,17. The diffusion length is determined by the lifetime and the mobility of minority carriers. One strategy for increasing the diffusion length is to minimize the deep electronic trap states at CQD surface. Ligand exchanges enable surface passivation of CQDs, which results in improved carrier transport and longer carrier lifetime in CQD solids14,18.
In a complementary strategy, one may architect devices that favor charge transport and extraction in CQD solids by—in a bulk heterojunction—separating photoexcited electrons and holes into distinct phases and then collecting them at charge-selective contacts. This approach results in extended carrier lifetimes, reduced recombination rates, and therefore longer effective diffusion lengths19,20. CQD/semiconducting polymer blends21,22, or two different CQD materials20,23, are material combinations used previously to implement bulk heterojunctions.
A single-bandgap choice in CQD materials can also be used, forming bulk homojunctions in which the two phases are distinguished by their doping24. The density of states of ligand/CQD systems is influenced by ligand functionalization (arising from their electron-donating vs. electron-withdrawing character)6,25,26,27,28, and as a result, the use of different ligands provides another degree of freedom in control over the doping level in CQDs6,11.
However, despite their advantages in carrier extraction and transport, CQD bulk homojunction devices are yet to outperform24 planar devices due to the difficulty in making both p-type and n-type CQD inks with complete surface passivation. In particular, previously explored ligand-exchange approaches for p-type CQD inks have resulted in surface defects that find their origins in the steric hindrance of the doping ligands29, a fact that prevents comprehensive surface coverage. The two ink types also need to be fully miscible with one another. Instability in blend CQD inks leads to aggregation of CQDs and nonuniform morphology in the final films, factors detrimental to optoelectronic device performance.
Here we demonstrate homogeneous CQD bulk homojunction solids through a cascade surface modification (CSM) strategy. The CSM consists of an initial halogenation step of CQD surfaces to attain an initial sufficient passivation, and a subsequent step that reprograms CQD surfaces with functional ligands to control the doping character and solubility properties of the resulting CQD inks. The resulting p-type and n-type CQDs exhibit a distinct potential difference, which induces a built-in electric field between the constituent classes of CQDs. By controlling the colloidal solubility of the inks, we achieve homogeneous CQD bulk homojunction films, whereas we show that the use of prior ink strategies results in inhomogeneous films as a result of poor miscibility. The homogeneous CQD bulk homojunction films exhibit a 1.5-fold increase in the carrier diffusion length and outperform previously reported CQD solar cells, achieving a record PCE of 13.3%.
Materials synthesis and characterization
We synthesized n-type and p-type CQD inks via the CSM process depicted in Fig. 1a. Initially, CQDs are capped with oleic acid and dispersed in octane. We first proceed with surface halogenation of CQDs with lead halide anions to obtain n-type CQD inks, after which the dots are transferred to dimethylformamide (DMF) in which they form a stable colloid. In the second step, we reprogram the CQD surface—rich in lead halide anions—with thiol ligands, introduced to render the CQD inks p-type. X-ray photoelectron spectroscopy (XPS) was used to monitor the surface reprogramming of CQD inks. The measurements revealed a bound thiolate peak in XPS S 2p spectra and a strong decrease of the XPS I 3d peak (Supplementary Fig. 1).
To evaluate the degree of surface passivation of CQD inks, we measured the materials’ photoluminescence quantum yield (PLQY). Prior solution-phase ligand-exchange methods give a low PLQY of 6% due to a lack of surface passivation (Fig. 1b). In contrast, the CSM-programmed CQD inks using the same 1-thioglycerol (TG) ligands exhibit a threefold higher PLQY of 18%. This highlights the role of the initial halogenation step to infiltrate sites otherwise inaccessible to bulky organic ligands.
Figure 1c shows the chemical structure of various functional ligands [TG, 2-mercaptoethanol (ME), cysteamine (CTA), 4-hydroxythiophenol (HTP), 4-aminothiophenol (ATP), and malonic acid (MA)]. In contrast with previous ink strategies, which were limited to the use of TG, the CSM method enables use of a wider set of molecules on CQD surfaces, and achieves stable colloids (Fig. 1d), showcasing the versatility of the method.
The surface reprogramming with thiol ligands increases the S/Pb atomic ratio of CQD inks from 0.81 to 1.15 (Supplementary Fig. 1), and we found that this stoichiometric control induces p-type characteristics as evidenced by ultraviolet photoelectron spectroscopy (Fig. 1e and Supplementary Fig. 2). The n-type CQD inks are tuned to p-type after surface reprogramming: the energy difference between the valence band and the Fermi level decreases from 0.77 to 0.6 (TG), 0.43 (ME), and 0.45 (CTA), respectively.
We employed Kelvin probe force microscopy (KPFM) to measure the surface potential difference between n-type and p-type CQDs to assess whether net doping of each phase was retained following self-assembly to the final CQD solid (Fig. 1f). The inset shows a schematic of the film structure. The two-dimensional KPFM potential image shows an ~0.2-eV change at the interface between p-type and n-type CQDs, giving evidence of the energy offset in Fermi levels between n- and p-type CQDs within the thin films. The local variation in surface potential is due to variation in the film thickness over the area studied in KPFM, which is confirmed by atomic force microscopy topographic image (Supplementary Fig. 3).
We also investigated the effect of doping on carrier transport properties using the space charge-limited current (SCLC) method30. Hole- and electron-only devices fabricated with n-type and p-type CQDs, respectively, reveal that the p-type CQDs exhibit a higher hole mobility (μh = 1.3 × 10−3 V cm−1 s−1) and lower electron mobility (μe = 1.5 × 10−3 V cm−1 s−1) compared with the n-type CQDs (μh = 8 × 10−4 V cm−1 s−1; μe = 3 × 10−3 V cm−1 s−1) (Supplementary Fig. 4), a trend also seen in a prior report26.
Fabrication of homogeneous CQD bulk homojunction films
We sought to fabricate CQD bulk homojunction films by using these oppositely doped inks (Fig. 2a). In this step, the solution miscibility of two inks is needed to realize homogeneous CQD films. Precipitation, aggregation, and size polydispersity of CQDs occur when blend inks are not colloidally stable, as a result of heterogeneous fusion between CQDs. This leads to energetic disorder that inhibits carrier transport in the films. CQD fusion and polydispersity are observed as inhomogeneous broadening in the absorption spectra, where the intensity of the bandedge exciton peak will decrease, and its half-width at half-maximum (HWHM) will increase (Fig. 2b). Measuring the absorption spectra over time shows that the mixture of n-type and p-type CQD inks produced by conventional solution exchange methods (control inks) undergoes rapid degradation of their initial properties (Fig. 2c).
Since it was previously demonstrated that n-type CQD inks are dispersed well in butylamine (BTA) due to surface lead halides16, we sought to tailor solubility of p-type CQD inks by using CSM method to form stable colloids of blend inks in BTA. The colloidal solubility of p-type inks is determined by the other functional group in thiol ligands (–L in SH–R–L) because thiols (–SH) bind strongly to the CQD surface. We hypothesized that the strength of the hydrogen bond of the –L termination with respect to BTA would be the key determinant of colloid stability. A competing scenario where –L moieties possessed a stronger hydrogen bond with one another compared with BTA would promote CQD aggregation and colloid precipitation. Only when the strength of the hydrogen bond for L-BTA is balanced or stronger than L–L can p-type CQD inks form stable colloids in BTA.
Given the strength of hydrogen bonds between each functional group (COOH–COOH > OH–OH > NH2–NH2), we reasoned that NH2 would be the most well-suited functional group to form stable colloids in BTA because BTA contains NH2 group. We then synthesized CSM-programmed CQD inks employing various bifunctional thiol ligands containing different functional groups (COOH, OH, and NH2). The experiments revealed that the NH2 group (CTA) enables the formation of stable colloids, whereas the OH group (ME) exhibited limited stability, and the COOH groups (3-mercaptopropionic acid, MPA) were insoluble in BTA (Supplementary Fig. 5). We therefore developed stable-blend CQD inks consisting of CTA-reprogrammed p-type inks and n-type CQD inks (Fig. 2c). Henceforth, we define p-type CQD inks as CTA-reprogrammed CQD inks.
To investigate the impact of colloidal stability of inks on the final film formation and morphology, we carried out grazing-incidence small-angle X-ray scattering (GISAXS) measurements. For the CQD bulk homojunction film made from CSM inks, intensity accumulation indicates a hexagonal pattern and in-plane ordering of CQDs (Fig. 2d)31. Notably, conventional inks lose packing uniformity and do not show a clear hexagonal pattern in the final CQD solid (Fig. 2e). Azimuthal integration of the diffraction pattern shows an average inter-dot distance of 3.32 nm for CQD bulk homojunction film with CSM inks (Fig. 2f). Comparatively, inter-dot distances of 3.30 nm for the n-type CQD film and 3.35 nm for the p-type CQD film were found (Supplementary Fig. 6). This agrees with the picture that a substantially homogeneous CQD bulk homojunction film is formed.
Photophysical properties of CQD bulk homojunction films
We sought to investigate the carrier diffusion length of CQD bulk homojunction films made from CSM inks. We employed a one-dimensional donor–acceptor scheme32 in which incident light excites the top-donor CQD layer (Eg = 1.3 eV, diffusive layer) and the photoexcited carriers transport to the bottom-acceptor CQD layer (Eg = 1.0 eV, emitter) where they can recombine radiatively (see the “Methods” section for sample preparation). Given the different solubility properties between the donor CQDs and the acceptor CQDs, we opted to avoid three-dimensional donor–acceptor scheme33, because it would be difficult to gauge if the acceptor CQDs would homogeneously mix with the donor CQDs. UPS measurements show that the energy level of the acceptor CQD layer forms a type-I heterojunction with both n-type and p-type CQDs, making it suitable to be used as quencher in the 1D diffusion length studies (Supplementary Fig. 7). We monitored this recombination as a function of thickness of the donor layer (Fig. 3a). As the thickness of the donor layer is increased, the photoluminescence (PL) intensity of the acceptor layer starts to decrease after a certain thickness is reached (Fig. 3b), when fewer charge carriers reach the acceptor layer due to nonradiative recombination in the diffusive layer. Normalized acceptor PL intensity is plotted as a function of donor layer thickness (Fig. 3c). To evaluate the carrier diffusion length, we fit the data using a 1D diffusion length model32. It indicates that the CQD bulk homojunction films show longer carrier diffusion lengths (340 nm) by a factor of 1.5× compared with those of the previous best CQD control films (221 nm), which consist of only n-type halogenated CQDs. The optical constants (n and k values) of the n-type and p-type CQD solids show similar values to within experimental error (Supplementary Fig. 8). This supports the view that the results obtained from the one-dimensional donor–acceptor diffusion length measurements are not due to different optical parameters among the doped CQD solids.
The orthogonality in the surface chemistry of p-type and n-type CQD inks in blend solution (their ability to retain their surface ligands when mixed in solution and in solid state), as well as their stability, were also studied to verify the retention of their original band offset. The blend inks show stable PL intensity for an hour, indicating no appreciable evolution in chemistry in the solution phase (Supplementary Fig. 9). We then prepared blend inks consisting of wide Eg p-type inks (Eg = 870 nm) and narrow Eg n-type inks (Eg = 1090 nm). Because thiol passivation induces a red shift in the first excitonic peak34 (Supplementary Fig. 10), we used it as a proxy to monitor thiol migration from p-type to n-type species. The addition of CTA in n-type inks produces a significant red shift in the first excitonic peak. In contrast, the blend inks do not show a peak shift in the n-type CQD population (Supplementary Fig. 11). Taken together, the stable PL intensity of the blend inks, combined with the invariance in the peak position of the n-type CQD inks, indicates the retention of chemical orthogonality in, and the colloidal stability of, the blend inks.
We further investigated the dynamics of charge carrier transfer between the constituent classes of CQDs. The PL intensity of blend films consisting of n-type and p-type CQDs having the same size and bandgap (Eg = 950 nm) exhibits strong emission quenching compared with that of purely n-type and p-type CQD films, a signature of charge carrier transfer in the blend films (Supplementary Fig. 12). We then carried out ultrafast transient absorption (TA) spectroscopy to acquire additional information. First, we prepared blend CQD films consisting of a wide Eg p-type CQD (Eg = 980 nm) and a narrow Eg n-type CQD (Eg = 1090 nm) to identify the charge transfer dynamics between the two populations. We selectively populated the narrow-bandgap CQDs using a photoexcitation wavelength of 1100 nm. In this configuration, charge carrier transfer from narrow to wide Eg CQDs will be indicated by the appearance of an increasing exciton bleach signal in the TA spectra at the corresponding wavelength. Kinetic traces of signal amplitude at wavelengths corresponding to the p-type and n-type CQD bandedge exciton bleach confirm charge carrier transfer from narrow Eg to wide Eg (Fig. 4d, f and Supplementary Fig. 13), evidenced in the rapid increase in the signal at 980 nm and the simultaneous decrease of the signal at 1090 nm. This evidences a functioning type-II heterojunction between p-type and n-type CQDs (Fig. 4b), indicating that holes are undergoing charge transfer from larger to smaller CQDs33. When using instead a mixture of different sized n-type CQDs (i.e., the same surface functionalization but different Eg), this produces a type-I heterojunction (Fig. 4a), and there is no appreciable electron or hole transfer between the two spectrally distinct CQDs, evidenced by the lack of signal amplitude exchanged between the two bandedge exciton bleach peaks (Fig. 4c, e).
Solar cell structure and performance
Given these promising properties of CQD bulk homojunction films, we pursued the realization of CQD solar cells with enhanced performance. We employed CQD bulk homojunction films as the active layer in a conventional CQD solar cell structure: ITO/ZnO as the electron-accepting layer/CQD film as the active layer/thin CQD film treated with 1,2-ethanethiol (EDT) as hole-transport layer/Au (Fig. 5a). We note that p-type CQD inks cannot be employed as the HTL in CQD devices due to their similar solubility properties to those of the n-type CQD inks. We first sought to optimize the p-type to n-type CQD ratio and obtained our best PCE using a 2:1 mass ratio (Fig. 5b). We then explored the PCE as a function of thickness. Notably, the bulk homojunction devices exhibit a substantially greater optimized thickness (580 nm) compared with the devices based on n-type CQDs (390 nm) and p-type CQDs (400 nm) (Fig. 5c), which is in good agreement with our observations of longer carrier diffusion lengths in the bulk homojunction films. This was accompanied by an enhanced short-circuit current density (Jsc) without compromise to open-circuit voltage (Voc) and fill factor (FF), and as a result, it led to superior PCE. Using this architecture, we achieved an AM1.5 PCE of 13.3% through the combination of Voc of 0.65 V, Jsc of 30.2 mA/cm2, and FF of 68% (Fig. 5d). The AM1.5 PCE from an accredited laboratory (Newport) shows a value of 12.47 ± 0.33%, the highest certified PCE reported for CQD solar cells (Supplementary Fig. 14). The devices with p-type CQDs exhibit higher Voc compared with the devices with n-type CQDs. The downshifted Fermi level of p-type CQDs increases the built-in potential of devices, accounting for the higher Voc35,36,37. Statistical data of the bulk homojunction devices show the reproducibility of these efficiencies (Supplementary Fig. 15). External quantum efficiency (EQE) measurements confirm the high Jsc of the bulk homojunction device (30 mA/cm2) compared with the control device (26.8 mA/cm2) (Fig. 5e). We further tested the stability of the CQD bulk homojunction devices. They retained 87% of their initial PCE following 110 h of device operation at their maximum power point under AM1.5 G illumination in an N2 atmosphere (Supplementary Fig. 16). We made larger-area (1.1 cm2) devices using CQD bulk homojunctions (Supplementary Fig. 17) and obtained similar Voc and Jsc values. A somewhat lower PCE in large-area devices comes from a lower FF related to the series resistance of the transparent conductive oxide16.
This work introduces a way to realize the homogeneous bulk homojunction structure in CQD solids. It is achieved via development of a CSM ligand-exchange strategy that enables the synthesis of p-type and n-type CQD inks that combine excellent surface passivation with miscibility for stable mixed-dot colloids. The CQD bulk homojunction films show an increase in carrier diffusion length compared with the state-of-the-art planar CQD films owing to improved separation and transport of photoexcited carriers through distinct physical paths. This is supported by observations of ultrafast charge transfer between n- and p-type domains as probed using transient absorption spectroscopy. The resulting solar cells exhibit the highest power conversion efficiency reported in CQD photovoltaic devices (13.3%).
Oleic-acid-capped PbS CQDs at 950 nm (1.31 eV) were synthesized based on a previous report38. Lead(II) oxide (0.9 g), oleic acid (3 mL), and octadecene (20 mL) were mixed in a three-neck flask and heated to 120 °C under vacuum for 2 h and then filled with N2. A stock solution, 0.24 mL of hexamethyldisilathiane dissolved in 8 mL of octadecene, was then injected rapidly into the flask for PbS CQD synthesis. The CQD solution was then slowly cooled to room temperature. Acetone was added to precipitate the QD solution, and the precipitate was then redispersed in toluene. The CQDs were further purified twice by adding a mixture of acetone and methanol. Finally the QDs were dissolved in octane (50 mg mL−1).
CSM process and film fabrication
For both n-type and p-type CQD inks, PbS CQDs at 950 nm were used. The first exchange was carried out using a modified previous method14. Precursor solution was prepared by dissolving lead halides (lead iodide 0.1 M and lead bromide 0.02 M) and NH4Ac (0.055 M) in dimethylformamide (DMF). A 5 mL of CQD solution dissolved in octane (7 mg mL−1) was added to 5 mL of precursor solution. Then the solution was mixed vigorously for 1–2 min until CQDs were transferred to DMF phase. The octane phase was discarded and DMF solution was washed with octane three times. The DMF solution was precipitated by adding toluene and dried in vacuum. The CQD solids were redispersed in butylamine (BTA). These CQD inks were used as n-type CQDs. To produce p-type inks, the above DMF solution was further treated with the second surface modification. Thiol solution was prepared by dissolving cysteamine in DMF (0.1 M). The thiol solution was slowly dropped into the DMF solution with gentle stirring (range of 100–400 μL) and precipitated by adding toluene. The CQD solids were dried in vacuum and redispersed in butylamine (BTA). The CQD inks were deposited on a substrate by single-step spin coating to achieve CQD films. The process was carried out under ambient air conditions.
CQD solar cell fabrication
The ZnO nanoparticles were synthesized using a published method6. The ZnO nanoparticles were spin-cast on an ITO substrate at 3000 r.p.m for 30 s. Then CQD inks were spin-cast onto the ZnO/ITO substrate. The blend CQD inks (mixture of n-type and p-type CQD inks) were used to fabricate bulk homojunction devices. The CQD films were annealed at 70 °C for 5 min in N2-filled glove box. Two PbS–EDT layers were then deposited as a hole-transport layer. Oleic-acid-capped CQDs were spin-cast, and then soaked with 0.01 vol% 1,2-ethanedithiol in propionitrile solution for 30 s, followed by three repetitions of washing using propionitrile. Finally, 120 nm of Au was deposited via e-beam evaporation as the top electrode. We note that the use of propionitrile provides higher device performance compared with acetonitrile that was used in prior works14,16.
Solar cell measurements
The active area (0.049 cm2) was determined by placing an aperture between the devices and the AM1.5 solar simulator (Sciencetech class A). Current–voltage (I–V) characteristics were measured with the aid of a Keithley 2400 source measuring unit under simulated AM1.5 illumination. Devices were tested under a continuous nitrogen flow. The I–V curves were scanned from −0.70 to +0.1 V at 0.02-V interval steps without wait time between voltage steps. The spectral mismatch was calibrated using a reference solar cell (Newport). EQE spectra were taken by subjecting the solar cells to chopped (220 Hz) monochromatic illumination (400-W Xe lamp passing through a monochromator and appropriate cutoff filters). Newport 818-UV and Newport 838-IR photodetectors were used to calibrate the output power. The response of the cell was measured with a Lakeshore preamplifier feeding into a Stanford Research 830 lock-in amplifier at short-circuit conditions.
Transient absorption measurements
Femtosecond pulses at 1030 nm with a 5-kHz repetition rate were produced using a regeneratively amplified Yb:KGW laser (PHAROS, Light Conversion). A portion of the beam was used to pump an optical parametric amplifier (ORPHEUS, Light Conversion) to serve as a narrowband pump tuned between 1000 and 1200 nm. The other portion of the beam power was focused into a sapphire crystal to generate a white-light supercontinuum probe (900–1300-nm window with various optical filters). Both pulses were directed into a commercial transient absorption spectrometer (Helios, Ultrafast). A time window up to 8 ns was obtained by delaying the probe pulse relative to the pump pulse. The time resolution of these experiments was ~300 fs (pulse duration of the pump pulse). All experiments were performed with fluence less than or equal to ~600 μJ cm−2 to minimize Auger recombination33.
Grazing-incidence small-angle X-ray spectroscopy (GISAXS)
Grazing-incidence small-angle X-ray spectroscopy (GISAXS) measurements were conducted at the Hard X-ray MicroAnalysis (HXMA) beamline of the Canadian Light Source (CLS). An energy of 17.998 keV (λ = 0.6888 Å) was selected using a Si (111) monochromator. Patterns were collected on a SX165 CCD camera (Rayonix) placed at a distance of 157 mm from the sample. A lead beamstop was used to block the direct beam. Images were calibrated using LaB6 and processed via the Nika software package39 and the GIXSGUI MATLAB plug-in40.
One-dimensional carrier diffusion length measurements
For the acceptor CQD layer (Eg = 1.0 eV), 5 mL of oleic-acid-capped CQD solution dissolved in octane (7 mg mL−1) was added to 5 mL of precursor solution (lead iodide 0.1 M and lead bromide 0.02 M, and NaAc 0.055 M in DMF)41. Then the solution was mixed vigorously for 5 min until CQDs were transferred to the DMF phase. The octane phase was discarded and the DMF solution was washed with octane three times. The DMF solution was precipitated by adding toluene. The supernatant was removed, and the precipitated material was dried in vacuum. The CQD solids were redispersed in a mixture of BTA:DMF (4:1). The acceptor CQD inks were spin-coated on glass substrates with a thickness of 50–60 nm. Then, the donor CQD layer (Eg = 1.3 eV) was deposited on top of the acceptor CQD layer using n-type CQD inks, p-type CQD inks, or blend CQD inks (n-type:p-type = 1:1). We note that the deposition of the donor CQD inks does not redisperse the underlying CQD acceptor layer: the CQD acceptor layer does not redisperse in butylamine solvent (Supplementary Fig. 18).
Samples were illuminated through the donor CQD layer side using a monochromated Xe lamp at 400-nm wavelength. The normalized PL intensity as a function of donor CQD layer thickness is fit using the equation:32
where Ld is the carrier diffusion length, d is the thickness of donor CQD layer, α is the absorption coefficient, and τ is the carrier lifetime.
Photoluminescence measurements were carried out using a Horiba Fluorolog Time Correlated Single Photon Counting system equipped with UV/Vis/NIR photomultiplier tube detectors, dual-grating spectrometers, and a monochromatized xenon lamp excitation source. Optical absorption measurements were carried out in a Lambda 950 UV–Vis–IR spectrophotometer. XPS measurements were carried out using a Thermo Scientific K-Alpha system, with a 75-eV pass energy, and binding energy steps of 0.05 eV. All signals are normalized to Pb. Atomic force microscopy and scanning Kelvin probe microscopy were done using an Asylum Research Cypher AFM. Samples were electrically grounded and AC160-R2 silicon probes with a titanium–iridium coating were used. Imaging was done in tapping mode and a nap pass was done to measure the contact potential difference. Spectroscopic ellipsometry was performed using a Horiba UVISEL Plus Extended Range ellipsometer with an ~200-ms integration time, a 10-nm step size, and an ~1-mm-diameter spot size. Three incident angles (60, 65, and 70°) were used. Soda-lime glass slides were used as substrates for each individual material, with their back sides covered with opaque adhesive tape to eliminate back reflections. Fitting was performed using the Horiba DeltaPsi2 software. Dispersion functions composed of four Voigt oscillators achieved fits with χ2 < 1.
Further information on research design is available in the Nature Research Reporting Summary linked to this article.
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
Shirasaki, Y., Supran, G. J., Bawendi, M. G. & Bulovic, V. Emergence of colloidal quantum-dot light-emitting technologies. Nat. Photon. 7, 13–23 (2013).
Sun, L. F. et al. Bright infrared quantum-dot light-emitting diodes through inter-dot spacing control. Nat. Nanotechnol. 7, 369–373 (2012).
Konstantatos, G. et al. Ultrasensitive solution-cast quantum dot photodetectors. Nature 442, 180–183 (2006).
Lee, J. S., Kovalenko, M. V., Huang, J., Chung, D. S. & Talapin, D. V. Band-like transport, high electron mobility and high photoconductivity in all-inorganic nanocrystal arrays. Nat. Nanotechnol. 6, 348–352 (2011).
Lim, J., Park, Y. S. & Klimov, V. I. Optical gain in colloidal quantum dots achieved with direct-current electrical pumping. Nat. Mater. 17, 42–49 (2018).
Chuang, C. H. M., Brown, P. R., Bulovic, V. & Bawendi, M. G. Improved performance and stability in quantum dot solar cells through band alignment engineering. Nat. Mater. 13, 796–801 (2014).
Luther, J. M. et al. Schottky solar cells based on colloidal nanocrystal films. Nano Lett. 8, 3488–3492 (2008).
Brown, P. R. et al. Improved current extraction from ZnO/PbS quantum dot heterojunction photovoltaics using a MoO3 interfacial layer. Nano Lett. 11, 2955–2961 (2011).
Hines, M. A. & Scholes, G. D. Colloidal PbS nanocrystals with size-tunable near-infrared emission: Observation of post-synthesis self-narrowing of the particle size distribution. Adv. Mater. 15, 1844–1849 (2003).
Liu, Y. et al. Dependence of carrier mobility on nanocrystal size and ligand length in PbSe nanocrystal solids. Nano Lett. 10, 1960–1969 (2010).
Kroupa, D. M. et al. Tuning colloidal quantum dot band edge positions through solution-phase surface chemistry modification. Nat. Commun. 8, 15257 (2017).
Weidman, M. C., Beck, M. E., Hoffman, R. S., Prins, F. & Tisdale, W. A. Monodisperse, air-stable PbS nanocrystals via precursor stoichiometry control. ACS Nano 8, 6363–6371 (2014).
Tang, J. et al. Colloidal-quantum-dot photovoltaics using atomic-ligand passivation. Nat. Mater. 10, 765–771 (2011).
Liu, M. X. et al. Hybrid organic-inorganic inks flatten the energy landscape in colloidal quantum dot solids. Nat. Mater. 16, 258–263 (2017).
Ning, Z. J. et al. Air-stable n-type colloidal quantum dot solids. Nat. Mater. 13, 822–828 (2014).
Xu, J. X. et al. 2D matrix engineering for homogeneous quantum dot coupling in photovoltaic solids. Nat. Nanotechnol. 13, 456–462 (2018).
Zhitomirsky, D. et al. Engineering colloidal quantum dot solids within and beyond the mobility-invariant regime. Nat. Commun. 5, 3803 (2014).
Carey, G. H., Levina, L., Comin, R., Voznyy, O. & Sargent, E. H. Record charge carrier diffusion length in colloidal quantum dot solids via mutual dot-to-dot surface passivation. Adv. Mater. 27, 3325–3330 (2015).
Kramer, I. J. et al. Ordered nanopillar structured electrodes for depleted bulk heterojunction colloidal quantum dot solar cells. Adv. Mater. 24, 2315–2319 (2012).
Rath, A. K. et al. Solution-processed inorganic bulknano-heterojunctions and their application to solar cells. Nat. Photon. 6, 529–534 (2012).
Nam, M., Park, J., Kim, S. W. & Lee, K. Broadband-absorbing hybrid solar cells with efficiency greater than 3% based on a bulk heterojunction of PbS quantum dots and a low-bandgap polymer. J. Mater. Chem. A 2, 3978–3985 (2014).
Palaniappan, K. et al. Poly(3-hexylthiophene)−CdSe quantum dot bulk heterojunction solar cells: influence of the functional end-group of the polymer. Macromolecules 42, 3845–3848 (2009).
Tan, F. et al. Interpenetrated inorganic hybrids for efficiency enhancement of PbS quantum dot solar cells. Adv. Mater. 4, 1400512 (2014).
Yang, Z. Y. et al. Mixed-quantum-dot solar cells. Nat. Commun. 8, 1325 (2017).
Kim, D., Kim, D.-H., Lee, J.-H. & Grossman, J. C. Impact of stoichiometry on the electronic structure of PbS quantum dots. Phys. Rev. Lett. 110, 196802 (2013).
Balazs, D. M. et al. Stoichiometric control of the density of states in PbS colloidal quantum dot solids. Sci. Adv. 3, eaao1558 (2017).
Brown, P. R. et al. Energy level modification in lead sulfide quantum dot thin films through ligand exchange. ACS Nano 8, 5863–5872 (2014).
Santra, P. K. et al. Improving performance in colloidal quantum dot solar cells by tuning band alignment through surface dipole moments. J. Phys. Chem. C. 119, 2996–3005 (2015).
Ip, A. H. et al. Hybrid passivated colloidal quantum dot solids. Nat. Nanotechnol. 7, 577–582 (2012).
Nikolka, M. et al. High-mobility, trap-free charge transport in conjugated polymer diodes. Nat. Commun. 10, 2122 (2019).
Bian, K. et al. Shape-anisotropy driven symmetry transformations in nanocrystal superlattice polymorphs. ACS Nano 5, 2815–2823 (2011).
Zhitomirsky, D., Voznyy, O., Hoogland, S. & Sargent, E. H. Measuring charge carrier diffusion in coupled colloidal quantum dot solids. ACS Nano 7, 5282–5290 (2013).
Proppe, A. H. et al. Picosecond charge transfer and long carrier diffusion lengths in colloidal quantum dot solids. Nano Lett. 18, 7052–7059 (2018).
Giansante, C. et al. “Darker-than-Black” PbS quantum dots: enhancing optical absorption of colloidal semiconductor nanocrystals via short conjugated ligands. J. Am. Chem. Soc. 137, 1875–1886 (2015).
Choi, M. J. et al. Highly asymmetric n+–p heterojunction quantum-dot solar cells with significantly improved charge-collection efficiencies. Adv. Mater. 28, 1780–1787 (2016).
Azmi, R. et al. Low-temperature-processed 9% colloidal quantum dot photovoltaic devices through interfacial management of p–n heterojunction. Adv. Energy Mater. 6, 1502146 (2016).
Song, J. H., Choi, H., Kim, Y. H. & Jeong, S. High performance colloidal quantum dot photovoltaics by controlling protic solvents in ligand exchange. Adv. Energy Mater. 9, 1700301 (2017).
Yuan, M. J. et al. Doping control via molecularly engineered surface ligand coordination. Adv. Mater. 25, 5586–5592 (2013).
Ilavsky, J. Nika: software for two-dimensional data reduction. J. Appl. Crystallogr. 45, 324–328 (2012).
Jiang, Z. GIXSGUI: a MATLAB toolbox for grazing-incidence X-ray scattering data visualization and reduction, and indexing of buried three-dimensional periodic nanostructured films. J. Appl. Crystallogr. 48, 917–926 (2015).
Kim, Y. et al. A facet-specific quantum dot passivation strategy for colloid management and efficient infrared photovoltaics. Adv. Mater. 25, 1805580 (2019).
This work was supported by Ontario Research Fund–Research Excellence program (ORF7—Ministry of Research and Innovation, Ontario Research Fund–Research Excellence Round 7), and by the Natural Sciences and Engineering Research Council (NSERC) of Canada. This work was also supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIT) (NRF-2017R1A2B2009948). We thank D. Kopilovic, E. Palmiano, L. Levina and R. Wolowiec for the technical support. The authors acknowledge the financial support from QD Solar Inc.
The authors declare no competing interests.
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Choi, MJ., García de Arquer, F.P., Proppe, A.H. et al. Cascade surface modification of colloidal quantum dot inks enables efficient bulk homojunction photovoltaics. Nat Commun 11, 103 (2020). https://doi.org/10.1038/s41467-019-13437-2
This article is cited by
Light: Science & Applications (2023)
Science China Physics, Mechanics & Astronomy (2023)
Nano Research (2022)
Nano Research (2022)
Journal of Materials Science: Materials in Electronics (2022)