Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

High-speed domain wall racetracks in a magnetic insulator

Abstract

Recent reports of current-induced switching of ferrimagnetic oxides coupled to heavy metals have opened prospects for implementing magnetic insulators into electrically addressable devices. However, the configuration and dynamics of magnetic domain walls driven by electrical currents in insulating oxides remain unexplored. Here we investigate the internal structure of the domain walls in Tm3Fe5O12 (TmIG) and TmIG/Pt bilayers, and demonstrate their efficient manipulation by spin–orbit torques with velocities of up to 400 ms−1 and minimal current threshold for domain wall flow of 5 × 106 A cm−2. Domain wall racetracks are defined by Pt current lines on continuous TmIG films, which allows for patterning the magnetic landscape of TmIG in a fast and reversible way. Scanning nitrogen-vacancy magnetometry reveals that the domain walls of TmIG thin films grown on Gd3Sc2Ga3O12 exhibit left-handed Néel chirality, changing to an intermediate Néel–Bloch configuration upon Pt deposition. These results indicate the presence of interfacial Dzyaloshinskii–Moriya interaction in magnetic garnets, opening the possibility to stabilize chiral spin textures in centrosymmetric magnetic insulators.

Introduction

Spintronics relies on the use of current-induced torques for manipulating the magnetization of thin films and nanodevices1. Owing to spin–orbit coupling, charge currents flowing in heavy metals, such as Pt, Ta, or W, generate spin currents that exert a torque onto an adjacent ferromagnetic layer2,3. These so-called spin–orbit torques (SOTs) are capable of reversing the magnetization of ferromagnets in a highly efficient and ultra-fast manner4,5,6,7,8, as well as driving domain walls (DWs) at very high velocities9,10,11. Most studies in this area, however, have been performed on ultrathin metallic ferromagnets, for which extensive characterizations of the DW structure and velocity have been reported12,13,14,15,16,17,18,19,20.

Magnetic insulators offer exciting perspectives for spintronic and magnonic applications beyond conventional metallic systems21. In particular, ferrimagnetic rare-earth garnets coupled to heavy metal layers have attracted attention due to the possibility of electrically exciting and detecting propagating magnons22,23,24,25, as well as for their low-power and high-frequency magnetization dynamics26. Despite increasing interest in such systems, however, the electrical manipulation of the equilibrium magnetization has not been investigated in detail. Current-induced switching of magnetic insulators has been only recently demonstrated in Tm3Fe5O12 (TmIG) and BaFe12O19 in combination with either Pt or W layers27,28,29,30. These studies relied on magnetoresistance measurements to detect the orientation of the magnetization, from which the dynamics of the switching process cannot be inferred.

In this work, we present a combined scanning nitrogen-vacancy (NV) magnetometry and spatially resolved magneto-optic Kerr effect (MOKE) study of the DW structure and dynamics driven by SOTs in racetrack structures embedded in a TmIG layer. We demonstrate highly efficient current-induced DW motion in TmIG/Pt, with mobility comparable or larger than metallic ferromagnets, a remarkable low threshold for DW flow, and very small depinning fields. We further provide a direct characterization of the DW width and internal structure in thin-film TmIG and TmIG/Pt bilayers. Previous studies in garnets were only able to provide estimates of the DW width based on indirect or diffraction-limited optical measurements, with reported values ranging from tens of nanometers to micrometers31,32,33,34. Scanning NV magnetometry reveals that the DWs in TmIG films are only ~20 nm wide and have a well-defined chiral structure, which changes from the left Néel in TmIG to intermediate left Néel–Bloch in TmIG/Pt. Given that the crystal structure of TmIG is centrosymmetric, these findings evidence the presence of strong interfacial Dzyaloshinskii–Moriya interaction (DMI) in TmIG grown on substituted gadolinium gallium garnet Gd3Sc2Ga3O12 (SGGG), which is attenuated by the deposition of Pt. The DMI is the key ingredient required to stabilize chiral Néel DWs in ferromagnets and ferrimagnets with perpendicular magnetization, which can then be driven by SOTs at very high velocities10,11,12,13,14,15. In contrast with metallic ferromagnets, TmIG thin films support the formation of Néel DWs without introducing heavy metal layers. Our results show that ferrimagnetic garnets are ideal materials for fabricating efficient and high-speed DW racetracks.

Results

Local switching in continuous TmIG films

TmIG(8 nm)/Pt(5 nm) bilayers were grown on SGGG (111)-oriented substrates by a combination of pulsed laser deposition for epitaxial growth of the garnet and in-situ dc sputtering for Pt. The numbers between parentheses indicate the thickness of each layer. Pt current lines were patterned in the shape of Hall bars by optical lithography and etching of the metal, leaving a continuous TmIG film (see Methods). Figure 1a shows an optical image of a TmIG/Pt device. The structural, topographic, magnetic, and electric characterization of the TmIG film and the TmIG/Pt bilayer are reported in the Supplementary Notes 13.

Fig. 1
figure1

Device schematics and local switching of TmIG. a Optical image of a Pt Hall bar patterned on TmIG with superposed electric wiring, coordinate system, and magnetization vector m. b Hall resistance Rxy as a function of Hz. The anomalous Hall-like signal arises from the interaction of the spin current generated in the Pt layer with the out-of-plane magnetization component mz of TmIG27,54, leading to a high (low) Rxy for −m (+m). The data are shown after subtraction of a constant sample-dependent offset. c Electrical measurement of current-induced switching of TmIG (tp = 1 ms, Hx = + 20, black dots, and −20 Oe, red dots). Note that, starting from a film saturated in the –m state, higher current densities are required to induce forward switching relative to backward switching. The same behavior is observed for ±Hx, thus ruling out a misalignment of the sample as a possible explanation for this effect. d Wide-field differential MOKE image of a TmIG/Pt device after injection of a current pulse (Jx = 0.94 × 108 A cm−2, tp = 150 ns, Hx = 100 Oe). The film was initially saturated in the –m state by applying a magnetic field Hz = −100 Oe. The bright contrast shows that only the TmIG region underneath the Pt current line has switched to +m. Scale bar, 40 μm

The magnetic state of the TmIG film underneath the Pt current line, +m (up) or −m (down), can be read electrically by measuring the transverse Hall resistance Rxy, as shown in Fig. 1b during a sweep of the out-of-plane magnetic field Hz. The measurement confirms that the films exhibit robust perpendicular magnetic anisotropy with a coercive field of about 40 Oe. In agreement with a previous report27, the magnetization of TmIG can be deterministically switched upon the application of a current pulse of sufficient current density Jx in the presence of a constant in-plane field Hx (Fig. 1c). The switching polarity is determined by the damping-like component of the SOT2,3,4, which stabilizes +m for Jx parallel to Hx and –m for Jx antiparallel to Hx in TmIG/Pt. Notably, we found that full switching can be achieved with pulses of 1 ms at current densities below 107 A cm−2 for an in-plane field as small as |Hx| = 20 Oe, which confirms the high quality of our devices (see also Supplementary Note 3).

A distinctive feature of our experiments is that TmIG covers the entire substrate, but switching occurs only in the region defined by the Pt current line. This is clearly seen in Fig. 1d, which shows a differential MOKE image of a TmIG/Pt device after the application of a current pulse. The bright contrast coinciding with the Pt current line shows the region where the magnetization has switched from −m to +m, demonstrating that it is possible to control the magnetization of a continuous TmIG film in a local way without altering the magnetic moments of the surroundings. Only in the presence of an out-of-plane field, or for a significant Oersted field and Joule heating produced by an intense current pulse, the switched magnetic domain may extend beyond the Pt line (see Supplementary Note 4). Such local control of the magnetization is unique to magnetic insulators due to the confinement of the current in the metal overlayer. As discussed further below, we also find that the surrounding magnetic medium influences the switching dynamics underneath the Pt current line. This is seen by the fact that a larger current is required for inducing down-to-up switching relative to up-to-down switching when starting from a homogenously magnetized TmIG film pointing down (Fig. 1c).

Chiral DWs in TmIG revealed by scanning NV magnetometry

As SOT-induced switching is strongly dependent on the DW structure12,13,14,15, we use scanning NV magnetometry to reveal the DW magnetization profile in both TmIG and TmIG/Pt layers. The technique is based on a single NV defect located at the apex of a diamond tip, which senses the magnetic stray field BNV(X,Y) emanating from a magnetic surface with high spatial resolution (Fig. 2a)17,35,36. Figure 2b shows BNV(X,Y) of the TmIG film measured in a region where a DW intersects an area partially covered by Pt. From this measurement, we reconstruct the out-of-plane component of the surface magnetization MZ(X,Y)t (see Methods), as shown in Fig. 2c. Although the DW runs continuously across the Pt edge, the line scans of BNV(X,Y) shown in Fig. 2d, e reveal that the DW structure changes going from TmIG/Pt to TmIG. In order to extract the magnetization profile of the DW from these measurements, we fit BNV(X,Y) by assuming that the magnetization components in the rotated coordinate system XYZ (Fig. 2a) vary as17,33

$$\begin{array}{*{20}{l}} {M_X\left( X \right)} \hfill & = \hfill & {M_{\mathrm{s}}\frac{{{\mathrm{cos}}\psi }}{{{\mathrm{cosh}}\left( {\frac{X}{{{\mathrm{\Delta }}_{{\mathrm{DW}}}}}} \right)}},} \hfill \\ {M_Y\left( X \right)} \hfill & = \hfill & {0,} \hfill \\ {M_Z\left( X \right)} \hfill & = \hfill & { - M_{\mathrm{s}}{\mathrm{tanh}}\left( {\frac{X}{{{\mathrm{\Delta }}_{{\mathrm{DW}}}}}} \right),} \hfill \end{array}$$
(1)

where ψ defines the angle of the in-plane magnetization direction with respect to the X-axis, ΔDW is the DW width, and Ms the saturation magnetization. Figure 2d, e compares representative BNV(X,Y) line profiles for TmIG/Pt and TmIG together with the stray field profile of a pure Bloch wall (ψ = 90°), a left Néel wall (ψ = 180°), and a right Néel wall (ψ = 0°). The best fits of the BNV(X,Y) line profiles give ψ = (116 ± 33)° and ψ = (173 ± 17)°, corresponding to an intermediate left-handed Néel–Bloch wall for TmIG/Pt and a left-handed Néel wall for TmIG, respectively. The DW widths are ΔDW = (17 ± 17) nm and ΔDW = (27 ± 6) nm for TmIG/Pt and TmIG, respectively (see Methods). Despite the large uncertainty in ΔDW, which is due to the weak dependence of BNV on ΔDW, and which prevents us to determine the relative change of DW width between TmIG/Pt and TmIG, the fits show that the DWs in 8 nm-thick TmIG are very narrow. Measurements performed in a reference unetched TmIG layer of the same thickness showed that ψ = 180° and ΔDW = (20 ± 4) nm (see Supplementary Note 7), which confirms the left-handed Néel chirality and the narrow width of the DWs in thin TmIG films grown on SGGG.

Fig. 2
figure2

Domain wall structure and chirality in TmIG and TmIG/Pt measured by scanning NV magnetometry. a Schematic of the NV probe and sample. The color code represents the out-of-plane component of the surface magnetization of the film, with red (blue) corresponding to areas of opposite magnetization. A DW crosses the TmIG/Pt and TmIG regions. The inset shows a NV center within the diamond lattice and the corresponding spin quantization axis. b Stray field BNV(X,Y) measured by scanning the diamond tip over the sample surface shown in a. c Reconstructed out-of-plane magnetic surface map MZ(X,Y)t from the data shown in b, where t is the thickness of the TmIG layer (see Methods) and μB the Bohr magneton. The difference in the measured surface magnetization MZt = (66.8 ± 1.5) μB nm−2 in TmIG/Pt and MZt = (39.5 ± 2.2) μB nm−2 in TmIG is attributed to both the etching process and to proximity-induced polarization of the Pt layer (see Supplementary Notes 2 and 7). d, e Line scans of BNV along the dashed lines indicated in b (square dots). The solid lines are calculated BNV profiles using Eqs. (13) assuming pure Bloch (ψ = 90°, cyan), left-handed Néel (ψ = 180°, violet), and right-handed Néel (ψ = 0°, green) DW structures for comparison with the measured stray field profiles. Mst and ΔDW are set from the fits of the BNV(X,Y) map. The fits give ψ = (116 ± 33)° and \({\mathrm{\Delta }}_{{\mathrm{DW}}} = (17 \pm 17)\) nm for TmIG/Pt, and ψ = (173 ± 17)° and \({\mathrm{\Delta }}_{DW} = (27 \pm 6)\) nm for TmIG

The change of the DW chirality from left-handed Néel to an intermediate left-handed Néel–Bloch configuration in going from TmIG to TmIG/Pt is a compelling indication of the presence of negative DMI in the bare TmIG layer, most likely due to symmetry breaking at the SGGG/TmIG interface. The deposition of Pt reduces the DMI, which we ascribe to the presence of positive DMI at the TmIG/Pt interface, consistently with the sign of the DMI found in metallic ferromagnetic/Pt bilayers14,15,17. These findings have important consequences for the operation of DW racetracks in magnetic insulators, because the reduced ΔDW favors the localization of DWs, whereas the finite DMI allows for their efficient manipulation by SOTs.

Spatially resolved switching dynamics

In order to prove this last point, we investigate the switching dynamics and current-induced DW motion below the Pt line. We refer to the switching of the magnetization starting from a homogeneously magnetized TmIG layer as forward switching (domain nucleation and expansion), and to the return to a homogenous magnetic state starting from a reversed domain as backward switching (domain contraction). Figure 3a shows the relative change in the magnetization induced by a single forward switching current pulse as a function of Hx and Jx. Within the experimental error, we find that the switching diagram is symmetric upon inversion of Hx or Jx, indicating that the SOT efficiency is the same for up-to-down and down-to-up switching and independent on the current direction. Distinct to electrical reading27,28,29, which is only sensitive to the magnetic moments in the vicinity of the Hall cross (Fig. 1b, c and Supplementary Note 5), MOKE measurements reveal that for a wide range of Hx and Jx only partial switching is achieved. We thus study the distribution and evolution of reversed magnetic domains induced by a sequence of current pulses. As we expect an influence of the surrounding TmIG on the magnetization dynamics underneath the Pt current line (Fig. 1c) and because the switching process is symmetric upon inverting both m and H4,8, we investigate the forward and backward switching processes for one fixed initial state of the film (−m).

Fig. 3
figure3

Current-induced DW dynamics in embedded TmIG racetracks. a Magnetization switching diagram showing the percent change of the magnetization underneath the Pt current line as a function of Jx and Hx. For each switching event, the initial m was always set fully up or down by applying an out-of-plane field Hz = + 100 or −100 Oe, respectively (+m for ±Hx, \(\mp J_x\) and –m for ±Hz, ±Jz according to the symmetry of SOT switching). Forward switching is triggered by a single current pulse with tp = 500 ns. b Sequence of differential MOKE images showing current-induced domain nucleation and expansion and c domain contraction for the different combinations of Hx and Jx that allow each scenario to take place. Δtp = Ntp is the accumulated pulse time after applying N current pulses of length tp. The pulse length is tp = 350 and 50 ns, and the current density |Jx| = 0.65 × 108 and 0.75 × 108 A cm−2 for b and c, respectively. |Hx| = 250 Oe in all cases. Bright and dark MOKE contrasts correspond to +m and –m states, respectively. It is noteworthy that the TmIG film not covered by Pt remains fully down magnetized. Scale bars, 20 μm b, c. d Switching diagram showing the minimum pulse length tp required to nucleate a domain starting from a fully saturated film (green triangles), to expand a domain (red circles), and to contract a domain (black squares) as a function of |Hx|. The current density of the pulses is fixed to |Jx| = 0.75 × 108 A cm−2. The results show that it is easier to move a DW than to nucleate a domain, and that the onset of DW motion is lower for contraction relative to expansion

Figure 3b, c shows two representative sequences of differential MOKE images taken during forward switching and backward switching, respectively. For each case, we compare the combinations of field and current that allow for domain nucleation and expansion (±Hx, ±Jx) and domain contraction (±Hx, \(\mp J_x\)). These images reveal that forward switching occurs via nucleation of a reversed domain at a defect site (as confirmed by a series of repetitions) and subsequent domain expansion along the Pt current line, with comparable speeds for both DWs on the left- and right-hand sides of the domain. Backward switching takes place by pushing the outer DWs towards the center of the domain. Similar dynamics—for either nucleation and expansion or contraction—is observed upon inverting Hx and Jx. The different timescales of the switching processes (see Fig. 3b, c) indicate that domain contraction is significantly faster than domain expansion. We attribute this asymmetry to the tendency of the reversed domain to shrink in order to reduce the DW surface tension37,38. The latter is proportional to the DW length and can thus significantly offset the balance of SOT, pinning potential, and demagnetizing field. Accordingly, we find that the minimum pulse length required to induce DW motion upon contraction is much smaller than for expansion (Fig. 3d).

DW velocity and DMI

Measurements of the DW velocity vDW are reported in Fig. 4 for an up–down DW as a function of Jx and Hx during both domain expansion and domain contraction. vDW is evaluated by considering the total DW displacement after a sequence of current pulses of length tp as the DW moves along the Pt current line. As the same tp does not allow for sampling a large Hx, Jx parameter space, we used longer (shorter) pulses for smaller (larger) Hx, Jx values. It is noteworthy that, up to |Jx|  1 × 108 A cm−2, the DW velocity remains almost constant when changing tp, indicating that it is not influenced by inertia, and that Joule heating plays a minor role on the DW velocity in this regime (see Methods and Supplementary Fig. 11). Our measurements reveal robust DW velocities of up to ~200 m s−1 for domain expansion (Fig. 4a) and ~400 m s−1 for domain contraction (Fig. 4b), which are comparable to the ones found in all-metallic structures under similar conditions9,14,15. Most remarkably, however, the DW mobility \(\mu _{{\mathrm{DW}}} = \frac{{v_{{\mathrm{DW}}}}}{{J_x}}\) reaches values in excess of 3 × 10−10 m3 A−1 s−1 for Jx = 5 × 107 A cm−2, which is comparable to that observed in compensated metallic ferrimagnets11,39. In contrast, most metallic ferromagnets feature μDW = 0 in this current range9,10,14,15.

Fig. 4
figure4

DW velocity upon expansion and contraction of domains in TmIG/Pt surrounded by uniformly magnetized TmIG. a vDW of an up–down DW (corresponding to a +m domain in a –m medium) as a function of Jx upon expansion and b contraction. The magnetic field is set to |Hx| = 300 Oe. The inset in a shows an enlarged view of vDW in the flow regime at low current density. c vDW of an up–down DW as a function of Hx upon expansion and d contraction. The current density is fixed at |Jx| = 0.75 × 108 A cm−2 in either case. DWs move faster when Jx is opposite to vDW (red symbols), indicating the presence of a weak DMI favoring left-handed Néel chiral DWs. Dashed lines in either c or d are linear fits to the experimental data assuming the same slope of vDW(Hx) for both polarities of Jx and opposite magnetic field at which vDW crosses zero, which allows evaluating the effective DMI field |HDMI| ~ 12 ± 3 Oe (see ref. 15). The error bars account for the uncertainty in estimating vDW from each measurement

The linear increase of vDW with Jx for expanding and contracting walls (Fig. 4a, b) further reveals a very low onset of the DW flow regime (5 × 106 A cm−2) compared with conventional ferromagnetic layers9,10,14,15. This behaviour is attributed to the reduced depinning field of TmIG, ~1–2 Oe (see Supplementary Fig. 6), which is one to two orders of magnitude smaller than in metallic and semiconducting thin-film ferromagnets with perpendicular magnetic anisotropy40. Upon increasing the current, vDW reaches a plateau between ~0.5 × 108 A cm−2 and ~0.9 × 108 A cm−2, followed by a further upturn. The plateau indicates the saturation of the DW velocity at \(v_{{\mathrm{DW}}}^{{\mathrm{sat}}} \approx \gamma \Delta _{{\mathrm{DW}}}\frac{\pi }{2}(H_x + H_{{\mathrm{DMI}}})\), which occurs at a current density \(J_x > > \frac{{2e\alpha \mu _0M_{\mathrm{s}}t}}{{\hbar \theta _{{\mathrm{SH}}}}}(H_x + H_{{\mathrm{DMI}}})\), where γ is the gyromagnetic ratio, α the damping constant, e the electron charge, ħ the reduced Planck constant, μ0 the vacuum permeability, θSH the effective spin Hall angle of Pt, and HDMI the effective DMI field12,16. Taking γ ~ 1.43 × 107 Oe−1 s−1 (ref. 41) and ΔDW ~ 20 nm (Fig. 2), and by approximating Hx + HDMI ≈ Hx = 300 Oe, we find that \(v_{{\mathrm{DW}}}^{{\mathrm{sat}}}\sim 135\,{\mathrm{m}}\,{\mathrm{s}}^{ - 1}\), which agrees well with the experimental data (Fig. 4a, b). It is noteworthy that the influence of the surrounding film on vDW is not considered in this estimate. In fact, the DW surface tension results in a variation of the DW mobility between contracting and expanding domains by approximately a factor of 1.75, a difference that remains constant as a function of field and current for DWs moving in the flow and saturation regimes up to |Jx|  0.9 × 108 A cm−2 (see Supplementary Fig. 12). The further increase of vDW beyond saturation, which is typical also of metallic ferromagnets10,15, is attributed to the influence of Joule heating and Oersted field (see Supplementary Note 4 and Supplementary Figs. 11 and 12). In this high current regime (|Jx|  0.9 × 108 A cm−2), the steeper slope of vDW(Jx) for domain expansion relative to domain contraction is consistent with the longer (shorter) pulses employed for expanding (contracting) domains (see Fig. 3d), resulting in a larger (smaller) Joule heating.

In agreement with the presence of DMI inferred from the DW magnetization profile, we observe a slightly larger vDW when the DW moves against the direction of the current (red symbols in Fig. 4). The same behaviour is also confirmed for down–up DWs (see Supplementary Fig. 13). This asymmetry, which is characteristic of chiral Néel DWs14,15, is consistent with the partially left-handed Néel chirality derived from scanning NV magnetometry and the sign of the torques in TmIG/Pt (see Supplementary Fig. 14 for more details). Provided that the dynamics of the DWs is restricted to the flow regime, we can estimate the effective internal DMI field of the DWs by fitting vDW(Hx) to a linear function and extrapolating it to vDW = 0 (see ref. 15). The fit yields |HDMI| ~ 12 ± 3 Oe (Fig. 4c, d), which allows us to calculate the effective DMI constant as9,14 \(D = \mu _0H_{{\mathrm{DMI}}}M_{\mathrm{s}}{\mathrm{\Delta }}_{{\mathrm{DW}}}\sim - 2 \pm 2\) μJ m−2, where we have taken Ms = (6.0 ± 1.0) × 104 A m−1 and ΔDW ~ 20 nm. Alternatively, the DMI constant can be estimated from the DW chirality using the equation cos ψ = D/Dc, where \(D_{\mathrm{c}} = 2\mu _0M_{\mathrm{s}}^2t\ln 2/\pi ^2\) (see refs. 42,43). This estimate gives D ~ −2.3 ± 2.6 μJ m−2, in good agreement with the value obtained from the analysis of the DW velocity. From the NV measurements of the bare TmIG, we estimate that the DMI of SGGG/TmIG is D ~ −5.3 ± 1.8 μJ m−2.

The DMI in TmIG is thus two to three orders of magnitude smaller compared with ultrathin metallic ferromagnet/Pt bilayers14,15,18 and one to two orders of magnitude smaller than that of ferrimagnetic metal/Pt bilayers11. As the DW mobility in the flow regime is proportional to ΔDW/αMs, the large mobility and high DW velocities in TmIG/Pt appear as the direct consequence of the small Ms and low-damping α typical of garnet layers31,44. By tuning the interfacial DMI, we anticipate that even larger vDW may be reached at a relatively low current density.

Discussion

Our results demonstrate fast current-driven DW motion in a magnetic insulator and reveal the internal DW structure of thin garnet layers. The chiral Néel structure of the DWs in TmIG indicates that oxide interfaces support a finite DMI even in the absence of heavy metal layers, which makes it possible, in principle, to stabilize nontrivial topological configurations in centrosymmetric insulating magnetic thin films, such as spin spirals and skyrmions. The low current threshold for DW flow and the large DW mobility, combined with the possibility of defining DW racetracks embedded in a continuous magnetic medium, make TmIG extremely attractive for spintronic applications. Local control of the magnetization is unique to magnetic insulators, which opens the possibility of printing arbitrary circuit paths enabling, for instance, the implementation and in-situ reconfiguration of synthetic magnetic structures with tailored magnonic bands21,45 and nanomagnonic waveguides46,47. Finally, we note that recent reports also demonstrate fast current-induced DW motion in TmIG/Pt at zero field48 as well as the emergence of a finite topological Hall effect above room temperature49. These works further prove the potential of hybrid magnetic insulator/metal heterostructures for stabilizing and manipulating chiral magnetic textures by proximity charge currents.

Methods

Films growth and devices fabrication

The TmIG thin films were grown by pulsed laser deposition on (111)-oriented Gd3Sc2Ga3O12 substrates (lattice constant a = 12.56 Å) to achieve high tensile strain (~2%), which promotes perpendicular magnetic anisotropy50. The substrate temperature was 650 °C, the oxygen pressure was 0.2 mbar, whereas the laser fluence and repetition rate were set to 1.35 J cm−2 and 8 Hz, respectively. After deposition, the samples were cooled in 200 mbar oxygen at a rate of −10 K/min. To ensure a high quality of the TmIG/Pt interface, the TmIG films were directly transferred to the sputter chamber without breaking vacuum, where the Pt layer was deposited at room temperature for 3 min at a power of 10 W in 0.05 mbar Ar. The thickness of the layers was calibrated by X-ray reflectometry. For the sample presented in the main text, the thicknesses of TmIG and Pt were 8.3 and 5.0 nm, respectively. Atomic force microscopy measurements of the surface topography showed a root-mean-square roughness of about 0.15 nm over a ~5 × 5 µm2 area (see Supplementary Fig. 2). The films were magnetically characterized in a superconducting quantum interference vibration sample magnetometer system. The Pt layer was patterned into Hall bars (consisting of three Hall crosses separated by L = 50 µm with a total channel length of 140 µm and width W = 10 µm) by photolithography and subsequent Argon plasma etching. According to the topographic and magnetic characterization of the patterned TmIG/Pt and reference TmIG samples, we estimate that etching of Pt results also in partial etching and passivation of TmIG, leading to a reduction of the effective thickness of TmIG in the etched region by ~1 nm (see Supplementary Notes 2 and 3).

Electric transport measurements

The longitudinal and transverse Hall resistances Rxx = Vx/Ix and Rxy = Vy/Ix, respectively, were measured by applying an alternating current of amplitude Ix = 0.3 mA and frequency f = 11 Hz, and by recording the first harmonic longitudinal (Vx) and transverse (Vy) voltages, as shown schematically in Fig. 1a.

MOKE measurements

We used a home-built wide-field polar MOKE microscope with Koehler illumination to measure the out-of-plane component of TmIG. As a light source, we employed a collimated light-emitting diode from Prizmatix, Ltd, model MIC-LED-455L, whose spectral emission is characterized by a maximum peak emission at 454 nm, centroid at 455 nm, and a full width at half maximum of 28 nm. Magnetic contrast was enhanced by taking differential MOKE images, i.e., each image was subtracted by a reference image captured in a fully magnetized state. The setup was equipped with two sets of orthogonal coils for the generation of out-of-plane and in-plane magnetic fields. For the switching and DW velocity studies, current pulses were injected using an AGILENT 8114A (100V/2A) pulse generator with a 50 Ω output impedance. The impedance matching with the Pt current line was achieved by connecting a 50 Ω resistance in parallel to the current line.

The relative change in the magnetization shown in Fig. 3a was evaluated by integrating the differential MOKE signal along the Pt current line (corresponding to the bright area in Fig. 1d) after the application of a single current pulse starting from a fully magnetized state.

For the domain expansion measurements (Fig. 4a, c), an initial domain was nucleated by a single current pulse at a defect site near the center of the Hall bar. For the domain contraction experiments (Fig. 4b, d), the initial domain was generated by switching the area underneath the Pt current line with a single current pulse of tp = 150 ns, |Jx| = 0.94 × 108 A cm−2 and |Hx| = 125 Oe, leading to a domain as the one shown in Fig. 1d.

In order to compare the DW velocities obtained for domain expansion and domain contraction, we studied the same DW moving back and forth over the same area. The case presented in Fig. 4 corresponds to an up–down DW moving between the center and the right end of the Hall bar. The DW velocity vDW was evaluated by measuring the total DW displacement Δx (as identified by direct MOKE imaging) obtained after the application of a series of Np current pulses of width tp, yielding \(v_{{\mathrm{DW}}} = {\mathrm{\Delta }}x/(N_{\mathrm{p}}\,t_{\mathrm{p}})\). The pulses were applied at a frequency of 1 Hz, to minimize the heat load during the experiment. vDW was found to be nearly independent of tp—only showing a slight increase of 10% or less when doubling the pulse length, which we attribute to Joule heating—indicating that the DW motion coincides with the pulse duration (see Supplementary Fig. 11 for more details).

Scanning NV magnetometry

Spatially resolved scans of the magnetic stray field produced by a DW in TmIG (see Fig. 2a) were acquired on a home-built nanoscale scanning diamond magnetometer (NSDM) microscope. Experiments were carried out in ambient environment and at zero magnetic bias field. The NSDM employed a monolithic diamond probe tip with a single NV center implanted at the apex (QZabre LLC, www.qzabre.com). The NV center spin resonance was monitored by optically detected magnetic resonance (ODMR) spectroscopy36,51 using a nearby microwave antenna (~2.9 GHz) for spin excitation and fluorescence microscopy (532 nm excitation, 630–800 nm detection) for spin state readout. The laser power employed in our measurements was 145 μW and 10 μW for the sample of the main text and the TmIG (8.5 nm) reference sample, respectively. No influence of the illumination power on the DW structure or position was noticed over time.

To convert the spin resonance frequencies to units of magnetic field, we fitted the ODMR spectrum to a double Lorentzian and extracted the frequency difference Δf between the resonance peaks. The detected field BNV is then given by \(|B_{{\mathrm{NV}}}| = \frac{{{\mathrm{\pi }}\,{\mathrm{\Delta }}f}}{\gamma }\), where γ = 2π · 28.0 GHz/T is the electron gyromagnetic ratio. To re-establish the relative sign of BNV, we inverted (BNV → −BNV) the image on one side of the DW (Fig. 2b). It is noteworthy that scanning NV magnetometry provides a vector projection of the magnetic field,

$$B_{{\mathrm{NV}}} = {\mathbf{B}} \cdot {\mathbf{e}}_{{\mathrm{NV}}} = {\mathrm{sin}}\theta _{{\mathrm{NV}}}{\mathrm{cos}}\phi _{{\mathrm{NV}}}B_x + {\mathrm{sin}}\theta _{{\mathrm{NV}}}{\mathrm{sin}}\phi _{{\mathrm{NV}}}{\mathrm{B}}_y + {\mathrm{cos}}\theta _{{\mathrm{NV}}}B_z,$$

because the NV center is sensitive only to fields that are parallel to its symmetry axis eNV. Here, B = (Bx, By, Bz) is the vector field at the position of the NV center, and θNV and ϕNV are the polar and azimuth angles of eNV in the laboratory frame (see Supplementary Fig. 15). The direction eNV is determined by the crystallographic orientation of the diamond tip and the probe arrangement in the setup (see Fig. 2a). θNV and ϕNV were calibrated by a series of ODMR measurements and confirmed by line scans. For the experiments presented in Fig. 2, θNV = (55 ± 2)° and ϕNV = (83 ± 3)°.

We investigated the magnetization, spin structure, and width of the DW by analyzing the local field image BNV(X,Y) shown in Fig. 2b. In a first step, we fitted line cuts across the TmIG to TmIG/Pt step edge to extract the NV center stand-off distance, d = (104 ± 5) nm (see Supplementary Note 7). To characterize the chirality and width of the DW, we took line cuts of BNV perpendicular to the DW as shown in Fig. 2b and compared them with the analytical model given through Eq. (1). The associated magnetic stray field was obtained by forward propagation of Eq. (1) in k-space according to52,53,

$$\begin{array}{l}\hat B_X = \hat g\left( { - k\widehat{M}_X + ik_X\widehat{M}_Z} \right)\\ \hat B_Y = \hat g\left( { - k\widehat{M}_Y + ik_Y\widehat{M}_Z} \right)\\ \hskip 32pt\hat B_Z = \hat g\left( {ik_X\widehat{M}_X + ik_Y\widehat{M}_Y + k\widehat{M}_Z} \right)\end{array}$$
(3)

where hat symbols indicate Fourier transforms, kX, kY, and k = (kX2 + kY2)1/2 are the in-plane k-space vectors, \(\hat g = \frac{{\mu _0t}}{2}\left( {\frac{{1 - e^{ - kt}}}{{kt}}} \right)e^{ - kd}\) is the Fourier transform of the Green’s function53, and t is the TmIG film thickness, which is taken to be 8.3 and 7.3 nm for the TmIG/Pt and TmIG regions, respectively (see Supplementary Notes 2 and 3). It is worth noting that Eq. (3) shows that only changes in MZ lead to a stray field, which is otherwise zero for a uniformly magnetized magnetic surface. The stray field is therefore strongest near the DW and decays to zero as one moves away from the DW. When taking line cuts along X across a DW extending along Y, the Y and \(\hat M_Y\) terms become zero and Eq. (3) simplifies to \(\hat B_X = \hat g\left( { - k\hat M_X + ik_X\hat M_Z} \right)\), \(\hat B_Y = 0\), and \(\hat B_Z = \hat g\left( {ik_X\hat M_X + k\hat M_Z} \right)\).

To extract values for Ms, ψ, and ΔDW, we fitted the experimentally measured BNV to the analytical prediction by Eqs. (13), with the DW position x = x0 as an additional fit parameter. By repeating the fitting procedure for a series of line scans, we obtained distributions for all parameters together with their means and standard deviations. A detailed description of the fitting procedure and error analysis is given in the Supplementary Note 7. It is noteworthy that we can infer ΔDW values that are below the NV-to-sample distance due to the large signal-to-noise ratio in our experiments and because the stray field extends far beyond the nominal DW width (see Eq. (1)).

By assuming that the magnetization is predominantly out-of-plane, we further reconstructed the surface magnetization from the magnetic field map BNV(X,Y) by using

$$\hat M_Z = \frac{{ - \hat B_{{\mathrm{NV}}}\zeta}}{{g(ik_Xe_X + ik_Ye_Y - ke_Z)}},$$
(4)

where ζ is a low-pass filter (cutoff λ = d) that suppressed high spatial frequencies in the image53. Independently of the thickness of the film, Eq. (4) yields the surface magnetization of the film in units of magnetic moment/area, i.e., it provides the value of MZt. The resultant \(M_Z(X,Y) t\) surface map is plotted in Fig. 2c. It is noteworthy that although the magnetic domains of TmIG and TmIG/Pt are well reproduced, the reconstruction slightly overestimates MZ near the DW due to the left Néel character of the DW.

Data availability

The data that support the findings of this study are available from the corresponding authors on reasonable request.

References

  1. 1.

    Brataas, A., D. Kent, A. & Ohno, H. Current-induced torques in magnetic materials. Nat. Mater. 11, 372–381 (2012).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  2. 2.

    Garello, K. et al. Symmetry and magnitude of spin-orbit torques in ferromagnetic heterostructures. Nat. Nanotechnol. 8, 587–593 (2013).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  3. 3.

    Manchon, A. et al. Current-induced spin-orbit torques in ferromagnetic and antiferromagnetic systems. Rev. Mod. Phys. 91, 035004 (2019).

    Article  ADS  Google Scholar 

  4. 4.

    Miron, I. M. et al. Perpendicular switching of a single ferromagnetic layer induced by in-plane current injection. Nature 476, 189–193 (2011).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  5. 5.

    Liu, L. et al. Spin-torque switching with the giant spin Hall effect of tantalum. Science 336, 555–558 (2012).

    Article  ADS  CAS  Google Scholar 

  6. 6.

    Garello, K. et al. Ultrafast magnetization switching by spin-orbit torques. Appl. Phys. Lett. 105, 212402 (2014).

    Article  ADS  CAS  Google Scholar 

  7. 7.

    Fukami, S., Anekawa, T., Zhang, C. & Ohno, H. A spin-orbit torque switching scheme with collinear magnetic easy axis and current configuration. Nat. Nanotechnol. 11, 621–625 (2016).

    Article  ADS  CAS  Google Scholar 

  8. 8.

    Baumgartner, M. et al. Spatially and time-resolved magnetization dynamics driven by spin–orbit torques. Nat. Nanotechnol. 12, 980–986 (2017).

    Article  ADS  CAS  Google Scholar 

  9. 9.

    Miron, I. M. et al. Fast current-induced domain-wall motion controlled by the Rashba effect. Nat. Mater. 10, 419–423 (2011).

    Article  ADS  CAS  Google Scholar 

  10. 10.

    Yang, S.-H., Ryu, K.-S. & Parkin, S. Domain-wall velocities of up to 750 m s−1 driven by exchange-coupling torque in synthetic antiferromagnets. Nat. Nanotechnol. 10, 221–226 (2015).

    Article  ADS  CAS  Google Scholar 

  11. 11.

    Caretta, L. et al. Fast current-driven domain walls and small skyrmions in a compensated ferrimagnet. Nat. Nanotechnol. 13, 1154–1160 (2018).

    Article  ADS  CAS  Google Scholar 

  12. 12.

    Thiaville, A., Rohart, S., Jué, É., Cros, V. & Fert, A. Dynamics of Dzyaloshinskii domain walls in ultrathin magnetic films. Europhys. Lett. 100, 57002 (2012).

    Article  ADS  CAS  Google Scholar 

  13. 13.

    Khvalkovskiy, A. V. et al. Matching domain-wall configuration and spin-orbit torques for efficient domain-wall motion. Phys. Rev. B 87, 020402 (2013).

    Article  ADS  CAS  Google Scholar 

  14. 14.

    Emori, S., Bauer, U., Ahn, S.-M., Martinez, E. & Beach, G. S. D. Current-driven dynamics of chiral ferromagnetic domain walls. Nat. Mater. 12, 611–616 (2013).

    Article  ADS  CAS  Google Scholar 

  15. 15.

    Ryu, K.-S., Thomas, L., Yang, S.-H. & Parkin, S. Chiral spin torque at magnetic domain walls. Nat. Nanotechnol. 8, 527–533 (2013).

    Article  ADS  CAS  Google Scholar 

  16. 16.

    Martinez, E., Emori, S., Perez, N., Torres, L. & Beach, G. S. D. Current-driven dynamics of Dzyaloshinskii domain walls in the presence of in-plane fields: full micromagnetic and one-dimensional analysis. J. Appl. Phys. 115, 213909 (2014).

    Article  ADS  CAS  Google Scholar 

  17. 17.

    Tetienne, J.-P. et al. The nature of domain walls in ultrathin ferromagnets revealed by scanning nanomagnetometry. Nat. Commun. 6, 6733 (2015).

    Article  ADS  CAS  Google Scholar 

  18. 18.

    Ha Pham, T. et al. Very large domain wall velocities in Pt/Co/GdOx and Pt/Co/Gd trilayers with Dzyaloshinskii-Moriya interaction. Europhys. Lett. 113, 67001 (2016).

    Article  ADS  CAS  Google Scholar 

  19. 19.

    Torrejon, J., Martinez, E. & Hayashi, M. Tunable inertia of chiral magnetic domain walls. Nat. Commun. 7, 13533 (2016).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  20. 20.

    Safeer, C. K. et al. Spin-orbit torque magnetization switching controlled by geometry. Nat. Nanotechnol. 11, 143–146 (2016).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  21. 21.

    Chumak, A. V., Vasyuchka, V. I., Serga, A. A. & Hillebrands, B. Magnon spintronics. Nat. Phys. 11, 453–461 (2015).

    Article  CAS  Google Scholar 

  22. 22.

    Kajiwara, Y. et al. Transmission of electrical signals by spin-wave interconversion in a magnetic insulator. Nature 464, 262–266 (2010).

    Article  ADS  CAS  Google Scholar 

  23. 23.

    Cornelissen, L. J., Liu, J., Duine, R. A., Youssef, J. Ben & Wees, B. Jvan Long-distance transport of magnon spin information in a magnetic insulator at room temperature. Nat. Phys. 11, 1022–1026 (2015).

    Article  CAS  Google Scholar 

  24. 24.

    Goennenwein, S. T. B. et al. Non-local magnetoresistance in YIG/Pt nanostructures. Appl. Phys. Lett. 107, 172405 (2015).

    Article  ADS  CAS  Google Scholar 

  25. 25.

    Evelt, M. et al. Emission of coherent propagating magnons by insulator-based spin-orbit-torque oscillators. Phys. Rev. Appl. 10, 041002 (2018).

    Article  ADS  CAS  Google Scholar 

  26. 26.

    Collet, M. et al. Generation of coherent spin-wave modes in yttrium iron garnet microdiscs by spin-orbit torque. Nat. Commun. 7, 10377 (2016).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  27. 27.

    Avci, C. O. et al. Current-induced switching in a magnetic insulator. Nat. Mater. 16, 309–314 (2017).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  28. 28.

    Avci, C. O. et al. Fast switching and signature of efficient domain wall motion driven by spin-orbit torques in a perpendicular anisotropy magnetic insulator/Pt bilayer. Appl. Phys. Lett. 111, 072406 (2017).

    Article  ADS  CAS  Google Scholar 

  29. 29.

    Shao, Q. et al. Role of dimensional crossover on spin-orbit torque efficiency in magnetic insulator thin films. Nat. Commun. 9, 3612 (2018).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  30. 30.

    Li, P. et al. Spin-orbit torque-assisted switching in magnetic insulator thin films with perpendicular magnetic anisotropy. Nat. Commun. 7, 12688 (2016).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  31. 31.

    Paoletti, A. Physics of Magnetic Garnets (North-Holland Company, 1978).

  32. 32.

    Malozemoff, A. P. & Slonczewski, J. C. Magnetic Domain Walls in Bubble Materials (Academic Press, 1979).

  33. 33.

    Hubert, A. & Schäfer, R. Magnetic Domains: The Analysis of Magnetic Microstructures (Springer, 1998).

  34. 34.

    Bokov, V. A., Volkov, V. V., Petrichenko, N. L. & Maryshko, M. Relation between relaxation losses in domain-wall motion and ferromagnetic resonance in garnet films. Phys. Solid State 40, 1377–1382 (1998).

    Article  ADS  Google Scholar 

  35. 35.

    Degen, C. L. Scanning magnetic field microscope with a diamond single-spin sensor. Appl. Phys. Lett. 92, 243111 (2008).

    Article  ADS  CAS  Google Scholar 

  36. 36.

    Schirhagl, R., Chang, K., Loretz, M. & Degen, C. L. Nitrogen-vacancy centers in diamond: nanoscale sensors for physics and biology. Annu. Rev. Phys. Chem. 65, 83–105 (2014).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  37. 37.

    Bates, L. F. & Davis, P. F. Direct measurement of domain wall energy. Proc. Phys. Soc. 74, 170–176 (1959).

    Article  ADS  Google Scholar 

  38. 38.

    Zhang, X. et al. Direct observation of domain-wall surface tension by deflating or inflating a magnetic bubble. Phys. Rev. Appl. 9, 024032 (2018).

    Article  ADS  CAS  Google Scholar 

  39. 39.

    Siddiqui, S. A., Han, J., Finley, J. T., Ross, C. A. & Liu, L. Current-induced domain wall motion in a compensated ferrimagnet. Phys. Rev. Lett. 121, 057701 (2018).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  40. 40.

    Jeudy, V., Díaz Pardo, R., Savero Torres, W., Bustingorry, S. & Kolton, A. B. Pinning of domain walls in thin ferromagnetic films. Phys. Rev. B 98, 054406 (2018).

    Article  ADS  CAS  Google Scholar 

  41. 41.

    Randoshkin, V. V. et al. Ferromagnetic resonance in (Bi,Tm)3(Fe,Ga)5O12(210) epitaxial films. Tech. Phys. 52, 495–497 (2007).

    Article  CAS  Google Scholar 

  42. 42.

    Je, S.-G. et al. Asymmetric magnetic domain-wall motion by the Dzyaloshinskii-Moriya interaction. Phys. Rev. B 88, 214401 (2013).

    Article  ADS  CAS  Google Scholar 

  43. 43.

    Gross, I. et al. Direct measurement of interfacial Dzyaloshinskii-Moriya interaction in X|CoFeB|MgO heterostructures with a scanning NV magnetometer (X = Ta,TaN, and W). Phys. Rev. B 94, 064413 (2016).

    Article  ADS  CAS  Google Scholar 

  44. 44.

    Wu, C. N. et al. High-quality thulium iron garnet films with tunable perpendicular magnetic anisotropy by off-axis sputtering – correlation between magnetic properties and film strain. Sci. Rep. 8, 11087 (2018).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  45. 45.

    Yu, H. et al. Approaching soft X-ray wavelengths in nanomagnet-based microwave technology. Nat. Commun. 7, 11255 (2016).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  46. 46.

    Wagner, K. et al. Magnetic domain walls as reconfigurable spin-wave nanochannels. Nat. Nanotechnol. 11, 432–436 (2016).

    Article  ADS  CAS  Google Scholar 

  47. 47.

    Haldar, A., Kumar, D. & Adeyeye, A. O. A reconfigurable waveguide for energy-efficient transmission and local manipulation of information in a nanomagnetic device. Nat. Nanotechnol. 11, 437–443 (2016).

    Article  ADS  CAS  Google Scholar 

  48. 48.

    Avci, C. O. et al. Interface-driven chiral magnetism and current-driven domain walls in insulating magnetic garnets. Nat. Nanotechnol. 14, 561–566 (2019).

    Article  ADS  CAS  Google Scholar 

  49. 49.

    Shao, Q. et al. Topological Hall effect at above room temperature in heterostructures composed of a magnetic insulator and a heavy metal. Nat. Electron. 2, 182–186 (2019).

    Article  CAS  Google Scholar 

  50. 50.

    Kubota, M. et al. Systematic control of stress-induced anisotropy in pseudomorphic iron garnet thin films. J. Magn. Magn. Mater. 339, 63–70 (2013).

    Article  ADS  CAS  Google Scholar 

  51. 51.

    Gruber, A. et al. Scanning confocal optical microscopy and magnetic resonance on single defect centers. Science 276, 2012–2014 (1997).

    Article  CAS  Google Scholar 

  52. 52.

    Beardsley, I. A. Reconstruction of the magnetization in a thin film by a combination of Lorentz microscopy and external field measurements. IEEE Trans. Magn. 25, 671–677 (1989).

    Article  ADS  Google Scholar 

  53. 53.

    Roth, B. J., Sepulveda, N. G. & Wikswo, J. P. Using a magnetometer to image a two-dimensional current distribution. J. Appl. Phys. 65, 361–372 (1989).

    Article  ADS  Google Scholar 

  54. 54.

    Chen, Y.-T. et al. Theory of spin Hall magnetoresistance. Phys. Rev. B 87, 144411 (2013).

    Article  ADS  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by ETH Zurich, the Swiss Competence Centre for Materials Science and Technology (CCMX), by the Swiss National Science Foundation under Grant Number 200020-172775 and by the European Research Council through the Advanced Grant Number 694955—INSEETO. We thank Rudolf Schäfer and Eva Grimaldi for discussions, and Kevin Chang and Jan Rhensius for help in construction of the scanning NV magnetometer, as well as for providing diamond tips. M.F. thanks ETH Zurich and CEMS at RIKEN for support of his research sabbatical. C.L.D. acknowledges funding by the Swiss National Science Foundation under Grant Numbers 200020-175600 and the NCCR QSIT, and by the European Commission through Grant Number 820394 “ASTERIQS”.

Author information

Affiliations

Authors

Contributions

S.V., J.S., M.T. and P.G. conceived the study. J.S., E.G. and M.T. grew the TmIG and TmIG/Pt films and characterized the magnetic and structural properties. S.V. fabricated the TmIG/Pt devices and performed and analyzed the electrical measurements. S.V., J.S. and M.M. performed the MOKE measurements and S.V. and J.S. analyzed the data. M.M., C.G. and C.N. built the wide-field MOKE setup. M.S.W., P.W. and C.L.D. built the scanning NV magnetometer and performed and analyzed the scanning NV measurements. M.T., M.F., C.L.D. and P.G. supervised the work. S.V. and P.G. wrote the manuscript. All authors contributed to the scientific discussion and manuscript revision.

Corresponding authors

Correspondence to Saül Vélez or Christian L. Degen or Morgan Trassin or Manfred Fiebig or Pietro Gambardella.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Chunhui Du and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Vélez, S., Schaab, J., Wörnle, M.S. et al. High-speed domain wall racetracks in a magnetic insulator. Nat Commun 10, 4750 (2019). https://doi.org/10.1038/s41467-019-12676-7

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing