Highly active nanostructured CoS2/CoS heterojunction electrocatalysts for aqueous polysulfide/iodide redox flow batteries


Aqueous polysulfide/iodide redox flow batteries are attractive for scalable energy storage due to their high energy density and low cost. However, their energy efficiency and power density are usually limited by poor electrochemical kinetics of the redox reactions of polysulfide/iodide ions on graphite electrodes, which has become the main obstacle for their practical applications. Here, CoS2/CoS heterojunction nanoparticles with uneven charge distribution, which are synthesized in situ on graphite felt by a one-step solvothermal process, can significantly boost electrocatalytic activities of I/I3 and S2−/Sx2− redox reactions by improving absorptivity of charged ions and promoting charge transfer. The polysulfide/iodide flow battery with the graphene felt-CoS2/CoS heterojunction can deliver a high energy efficiency of 84.5% at a current density of 10 mA cm−2, a power density of 86.2 mW cm−2 and a stable energy efficiency retention of 96% after approximately 1000 h of continuous operation.


Energy storage technologies are crucial for effectively utilizing intermittent renewable resources like solar and wind1,2,3. Inorganic or organic redox flow batteries (RFBs) have been explored and advocated as a prospective technology for grid-scale energy storage in virtue of their design flexibility in decoupling power and energy, high power performance, and ease of scale-up4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23. Nowadays, all-vanadium RFBs represent the current state-of-the-art, but their system price is near 4-fold higher than the price targets outlined by the Department of Energy of U.S., $10024. Besides developing abundant redox organic charge storage materials3, it remains highly technologically and economically attractive to advance the flow battery chemistries of abundant and low cost redox active inorganic compounds such as iron salts, halides, and sulfides 2.

$${\mathrm{Cathode}}:3{\mathrm{I}}^ - - 2e^ - \leftrightarrow {\mathrm{I}}_3^ - E^\theta = 0.54\;{\mathrm{V}}\;{\mathrm{vs}}\;{\mathrm{SHE}}$$
$${\mathrm{Anode}}:{\mathrm{S}}_4^{2 - } + 2e^ - \leftrightarrow 2{\mathrm{S}}_2^{2 - }E^\theta = - 0.48\;{\mathrm{V}}\;{\mathrm{vs}}\;{\mathrm{SHE}}$$
$${\mathrm{Full}}\;{\mathrm{cell}}:3{\mathrm{I}}^ - + {\mathrm{S}}_4^{2 - } \leftrightarrow {\mathrm{I}}_3^ - + 2{\mathrm{S}}_2^{2 - }E_{\mathrm{cell}} = 1.02\;{\mathrm{V}}$$

I/I3 and S2−/Sx2− couples are promising redox-active species for high-energy-density flow batteries on account of their high solubility in water and low costs. Aqueous polysulfide/iodide redox flow batteries (SIFBs) have been studied but require further development for practical energy storage25. The working principle of the proposed SIFB with polysulfide anolyte and iodide catholyte can be depicted in Eqs. 13. For example, Lu et al. reported that an aqueous SIFB delivered an energy efficiency (EE) of ca. 68% at 10 mA cm−2 for 70 cycles25. However, the poor electrocatalytic activities for the redox reactions of I/I3 and S2−/Sx2− on carbon material electrode usually restrict the EE and power density of SIFBs. In fact, power density and charge–discharge EE of a practical flow battery are mainly limited by the polarization derived from ohmic resistance, diffusion of active materials, and charge transfer overpotential at electrodes. Furthermore, larger overpotential at electrodes can lead to the evolution of H2 and O2 in aqueous electrolyte, which results in energy loss and safety problems3,26. In general, carbon materials are used as electrodes in most RFBs owing to their high electronic conductivity, good chemical stability, and economical cost27. Thus enhancing the electrocatalytic activities of electrodes to facilitate the I/I3 and S2−/Sx2− redox reactions is an effective way to boost the performances of SIFBs 27,28.

Nowadays, regulating electronic structures of active sites via different methods, such as forming solid solution, heteroatom doping, phase controlling, and so on, can effectively improve the catalytic activity by optimized host–guest electronic interactions and the specific adsorption free energy for reactants29. From basic semiconductor physics, two opposite space charge regions and a built-in field will be formed when two semiconductors with different energy structure come into contact and reach thermodynamic equilibrium state30. The strongly charged region of in this heterojunction would have the potential to modulate the absorption process of reactant species. Furthermore, the built-in field would also contribute to the charge transfer during the catalytic process. Therefore, the design and fabrication of semiconductor junctions would be a feasible strategy to improve the activity of catalysts.

Metal sulfides (e.g., Co, Cu, Pb) with different compositions, structures, or morphologies, including CuS31,32, CoS33,34,35,36, PbS37,38, and Cu2S/reduced graphene oxide composites39, have been shown to have high electrocatalytic activities toward I3 and Sx2− redox systems. Cobalt sulfide has various chemical formulas (e.g., CoS2, Co9S8, CoS, Co3S4, and Co4S3) and can form heterojunctions with each other due to their different energy structures. The built-in field of a heterojunction (Supplementary Figs. 1 and 2 and Supplementary Table 1) can accelerate the charge carriers and has been explored in photocatalysts, photodetection, photovoltaics, and light-emitting diodes40,41,42,43,44. Thus we envisioned that the uneven charge distribution of semiconductor junctions would improve the activity of cobalt sulfide-based electrocatalysts via enhanced charge transfer activities. Herein CoS2/CoS n-n heterojunction, with uneven charge distribution, was fabricated and used as positive and negative electrodes to electrochemically catalyze the I/I3 and S2−/Sx2− redox reactions. The polysulfide/iodide flow battery with the CoS2/CoS heterojunction-modified graphite felt (GF) electrodes can deliver a high EE of 84.5% at the current density of 10 mA cm−2, a power density of 86.2 mW cm−2, and an EE retention of 96% after ca. 1000 h continuous working.


Synthesis and characterization

CoS2, CoS, and CoS2/CoS heterojunction were synthesized from CoSO4•7H2O, urea, and sulfur via tuning the ratio of dimethylformamide (DMF) and ethylene glycol (EG) in a mixed solvent (see “Methods” for details). As shown in Fig. 1a, all diffraction peaks can be indexed well to cubic CoS2 (JCPDS 89–1492) and hexagonal CoS (JCPDS 65–3418) when VEG/VDMF = 0.5 and 2, respectively. Notably, mixed phases of cubic CoS2 and hexagonal CoS were obtained when VEG/VDMF = 0.9. In Raman spectra, the characteristic peaks are at 292, 323, and 393 cm−1, which match well with the reported value of CoS2 (Fig. 1b)45. The peaks at 475, 517, and 676 cm−1 represent the Eg, F2g, and A1g modes of CoS, respectively46. Both the characteristic peaks of CoS2 (292 cm−1, 390 cm−1) and CoS (477 cm−1, 678 cm−1) can be found in the obtained the CoS2/CoS heterojunction spectrum. It is noted that the peaks corresponding of CoS2 slightly shifts from 393 cm−1 of pure CoS2 to 390 cm−1 of CoS2/CoS heterojunction. On the contrary, the peaks corresponding of CoS slightly shifts from 475 cm−1 of pure CoS to 477 cm−1 of CoS2/CoS heterojunction. The opposite shifts of CoS2 and CoS diagnostic peaks in the Raman spectra imply an opposite charge transfer due to the formation of a heterojunction.

Fig. 1

X-ray powder diffraction (XRD) and Raman characterization. a XRD patterns of the as-prepared cobalt sulfides compared with the standard patterns of CoS2 (JCPDS 89–1492) and CoS (JCPDS 65–3418). b Raman spectra of CoS2 (blue), CoS2/CoS (magenta), and CoS (olive)

Transmission electron microscopy (TEM) image (Fig. 2a) shows the CoS2/CoS particles of 100 nm in size. Clear lattice fringes and the interface between CoS2 and CoS without obvious amorphous area confirmed the formation of heterojunction of CoS2/CoS (Fig. 2b, c). As shown in the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) image and elemental mappings in Fig. 2d–g, uniform distributions of Co and S are in accordance with the morphology of the CoS2/CoS heterojunction. The line-scan energy-dispersive X-ray spectroscopy (EDX) of the CoS2/CoS heterojunction demonstrates that the atomic ratio of S and Co at the left of line-scan spectrum is 2:1 for CoS2 and suddenly changes to 1:1 for CoS at the right of line-scan spectrum (Fig. 2h).

Fig. 2

Morphology characterization of CoS2/CoS. a Transmission electron microscopic (TEM), b, c high-resolution TEM, d, h high-angle annular dark-field scanning transmission electron microscopic (HAADF-STEM), eg energy-dispersive X-ray spectroscopic (EDX) mapping images, and h line-scan EDX of the as-prepared CoS2/CoS heterojunction. i HAADF-STEM image of CoS2/CoS with an arrow indicating electron energy loss spectra (EELs) line-scan direction and j corresponding EELs line-scan spectra of the CoS2/CoS heterojunction. k EELs spectra of Co L23 edge selected from center of CoS2, heterojunction boundary, and center of CoS, respectively

To understand the formation of the CoS2/CoS heterojunction and the charge distribution at the interface more clearly, line-scan electron energy loss spectra (EELs) of Co L23 edge (Fig. 2i–k) in the CoS2/CoS heterojunction and X-ray photoelectron spectra (XPS) were further investigated. The chemical shift of Co L3 edge of 0.25 eV to lower energy at the heterojunction boundary was observed, indicating the negatively charged characteristics assigned to the side of CoS of the heterojunction. The heterojunction interfaces of other CoS2/CoS nanoparticles also have chemical shift evidenced by line-scan EELs spectra (as shown in Supplementary Figs. 3 and 4). However, EELs line scan across a single particle indicated that there is an unchanged chemical state of Co species despite particle thickness (Supplementary Fig. 5). In XPS, sharp peaks of Co 2p and S 2p are detected in all samples (Supplementary Fig. 6), and Co is mainly at a valence state of Co2+ in all samples47. From the S 2p spectra of pure CoS2 and CoS (Supplementary Fig. 7), one can see the typical peaks at 162.3 and 163.5 eV of the bridging S22− in CoS2 and the peaks at 161.5 and 162.7 eV of divalent sulfide (S2−) in CoS48,49,50. In the CoS2/CoS heterojunction, the broad S 2p spectrum can be fitted into two pairs of peaks corresponding to bridging S22− of CoS2 (162.4 and 163.5 eV) and divalent sulfide (S2−) of CoS (161.3 and 162.7 eV) with a ratio of 1/0.17, which is obtained by integrating peak areas. It is noted that the binding energy of S 2p3/2 (S2−) in CoS2/CoS heterojunction shifts slightly to a lower binding energy by ca. 0.2 eV than that in CoS due to extra negative charges in the region of CoS, while the binding energy of S 2p3/2 (S22−) is slightly higher than that in CoS251. The opposite shift of S 2p3/2 demonstrates the distribution of opposite charges in CoS2/CoS because of the formation of a heterojunction. The EELs and XPS results confirm the uneven charge distribution at the interface region of the CoS2/CoS heterojunction.

Adsorption behaviors

The CoS2, CoS2/CoS, and CoS can be uniformly assembled onto the GF to form an integrated GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes, respectively (1.0 mg cm−2 loading, Supplementary Figs. 810). The adsorption behavior of these electrodes to redox species is a critical factor of the electrocatalytic process. As shown in Fig. 3a, the NaI3 aqueous solution with GF-CoS2/CoS exhibits more obvious decoloration than ones with the GF, GF-CoS2, and GF-CoS and nearly turns to a colorless solution. In addition, the ultraviolet–visible (UV-Vis) absorption of the NaI3 solution after adsorption with GF-CoS2/CoS, the typical absorption peaks of I3 ions are nearly disappeared. The sharp contrasts indicate that CoS2/CoS heterojunction has remarkable adsorption effect on iodide species. The adsorption capacity of the materials for polysulfides has also been investigated (Fig. 3b) and shows a similar sequence to their absorptivity to iodide solutions.

Fig. 3

Adsorption characterization of the electrode materials. Ultraviolet-visible spectra of the NaI + I2 (a) and Na2S2 (b) initial solutions and the solutions after interacting with graphite felt (GF), GF-CoS2, GF-CoS2/CoS, and GF-CoS, respectively. The loading amount of electrocatalysts onto GF is 1.0 mg cm−2. Inset: Visualized adsorption of NaI + I2 and Na2S2 and aqueous solutions on GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS

To qualitatively elucidate the interactions between the (CoS2 (200), CoS (100) and the heterostructure CoS2 (200)/CoS (100) with iodide or polysulfide ions, density functional theory (DFT) was used to calculate their adsorption energy (Table 1, Supplementary Figs. 11 and 12). The DFT results revealed that the adsorption energies of the CoS2 (200)/CoS (100) heterojunction to polysulfide or iodide ions is higher than the individual pure structures of CoS2 (200) and CoS (100) surface, which is consistent with the experimental results. Constructing heterojunction improves the adsorption energy of the system and the negative value of adsorption energy indicates that these adsorption processes are thermodynamically favorable. The above results suggest the significantly promoted affinity of CoS2/CoS heterojunction with polysulfide and iodide molecules in comparison to CoS2 or CoS.

Table 1 Surface calculation data of CoS2, CoS, and CoS2/CoS

Electrocatalytic activity investigation

The effect of the CoS2/CoS heterojunction on the electrocatalytic activity of I/I3 and S2−/Sx2− redox reactions were studied by cyclic voltammogram (CV). In Fig. 4a, each curve exhibits a pair of peaks corresponding to the redox reactions of I/I3 couples using GF, CoS2, CoS, and CoS2/CoS electrodes. The peak-to-peak separation (Epp) and peak current density are vital parameter indicators to evaluate the electrocatalytic property of electrodes52. The corresponding parameters are listed in Table 2. Compared with CoS2 and CoS, the smallest Epp (0.10 V) and highest peak current density of CoS2/CoS indicate that the heterojunction is more effective to facilitate the redox reaction of I/I3. The 1.15 value of JOx/|JRed| for CoS2/CoS also implies its better reversibility to I/I3 redox reaction. Two typical pairs of redox peaks of electrodes in Supplementary Fig. 13 can be ascribed to the redox reaction of I/I3 and I3/I5. The linear relationship between peak currents and the square root of scan rate (ν1/2, Supplementary Figs. 14 and 15) indicates the diffusion-controlled process of the I/I3 redox reaction. The diffusion coefficient D of I can be estimated by the Berzins–Delahay equation (Supplementary Table 2), which follows an order of GF < CoS < CoS2 < CoS2/CoS, being consistent with the order of the electrode catalytic performances. Moreover, the 200 consecutive CVs indicates the better stability of CoS2/CoS than CoS2 and CoS for the I/I3 redox reaction (Supplementary Fig. 16). As shown in Fig. 4b, the CoS2/CoS electrode indeed greatly enhanced the electrochemical reactivity of the polysulfide couple and resulted in resolved multiple redox peaks of polysulfides, which are integrated into one pair of asymmetry broad peaks in case of other electrodes. The multiple electron transfers are present in the potential range of ~−1.2 V–0.1 V vs Ag/AgCl, which has the two oxidation peaks and three reduction peaks. This suggests that the polysulfide may undergo more complicated electrochemical reactions with likely involvement of more polysulfide species, e.g., Sx2− (x = from 2 to 8), which has been demonstrated in both aqueous and nonaqueous electrolytes53,54.

Fig. 4

Cyclic voltammetry characterization. The cyclic voltammograms (CVs) of the catalysts deposited on glassy carbon in 4 mM NaI + 0.5 M NaCl solution (a) and 0.06 M Na2S + 0.02 M S + 0.5 M NaCl solution (b) at a scan rate of 50 mV s−1

Table 2 Parameters obtained from CV curves for I/I3 on GF, CoS2, CoS2/CoS, and CoS, respectively

Flow battery studies

The schematic representation for the proposed SIFB cell configuration is shown in Fig. 5a. SIFB cells based on GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS as both positive and negative electrodes were assembled. A combination of N115 and N117 were used as the two-layer separator to promote the Na+ cation transport and limit the crossover of active species24. For battery tests, the electrolyte volume was 5 mL for both 2.0 M NaI + 0.5 M I2 catholyte and 2.0 M Na2S2 anolyte and the flow rate was fixed at 10 mL min−1. Figure 5b, c and Supplementary Fig. 17 show the galvanostatic cycling performance of the polysulfide/iodide flow battery at 20 mA cm−2 with the charge state of 50% state of charge (SOC). The corresponding charge/discharge voltage profiles of SIFBs are plotted in Supplementary Fig. 18. The GF-CoS2/CoS displayed the highest EE value than others electrodes at the same charge/discharge current density resulting from the reduced charge/discharge overpotentials. The voltage efficiency (VE) value is a derivative of the coulombic efficiency (CE) and EE (VE = EE/CE). The SIFB with GF-CoS2/CoS delivered an EE of 71.6% at 20 mA cm−2 and 84.0% capacity retention for 60 cycles, which is significantly higher than the one with bare GF electrodes (47.8% EE). The SIFBs with GF-CoS2 and GF-CoS delivered an EE of 68.9% and 69.4% at 20 mA cm−2 and 58.5% and 68.6% capacity retention for 60 cycles, respectively. Furthermore, the trend of CE, VE, and EE over current densities of SIFBs are outlined in Supplementary Figs. 19 and 20. CE stayed above ca. 91% at all current densities. The EE of GF-CoS2/CoS decreased from 72.0 % for 15 mA cm−2 to 55.9% for 50 mA cm−2. The observed trends for the VE and EE typically attribute to the increased cell overpotential at higher current densities. In addition, GF-CoS2/CoS electrode has the highest EE of 84.5% at 10 mA cm−2, and the EE retention was 96% after 500 cycles of continuous working at 10% SOC (ca. 1000 h) with multiple electrolyte refreshments (Supplementary Fig. 21). As shown in Fig. 5d, the discharge polarization curves and power density curves of SIFBs clearly reveal that the GF-CoS2/CoS electrode has the highest power density of 86.2 mW cm−2 compared to GF (8.9 mW cm−2), GF-CoS2 (44.6 mW cm−2), and GF-CoS (56.6 mW cm−2), respectively. The charge and discharge polarization curves of SIFBs shows that the open circuit voltage of the GF-CoS2/CoS cell is 1.03 V, which is in good agreement with the theoretical value of 1.02 V. And the hysteresis voltage between charge and discharge processes of the SIFB cell using GF-CoS2/CoS electrodes is smaller than other electrodes under the same current density (Fig. 5e). Electrochemical impedance spectroscopy (EIS) was used to investigate the charge transfer resistance (Rct) and evaluate the electrode activity. The EIS plots of the SIFBs with different electrodes are simulated (Fig. 5f) and the results are summarized in Table 3. In the Nyquist plot of electrodes, a semicircle is observed, which corresponds to Rct at the electrolyte/electrode interface55. It is clearly seen that the Rct1s are 3.66, 1.03, 0.46, and 0.84 Ω cm2, respectively, for GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes. The Rct2s are 36.6, 4.19, 2.40, and 2.83 Ω cm2, respectively, for GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes. These results further illustrate that the CoS2/CoS heterojunction can facilitate the charge transfer process and improve diffusion dynamics, which fits well with the CV experiments. To evaluate the stability of electrodes, the catholyte of SIFBs based on the GF-CoS2 GF-CoS2/CoS, and GF-CoS electrodes were sampled after 60 cycles and further tested by the inductively coupled plasma spectroscopy (ICP). The ICP results showed that no cobalt was detected in the catholyte of GF-CoS2/CoS and GF-CoS electrodes and 0.3 ppm cobalt was detected using GF-CoS2 electrode, which confirms the good stability of GF-CoS2/CoS electrode and no particles were fallen off. Supplementary Fig. 22 exhibits that the surface morphology of the GF-CoS2/CoS electrode after 60 cycles at a current density of 20 mA cm−2 still maintained its integrity similar to the fresh one. All of the results discussed above demonstrate remarkable power densities and promising long-term cycling stability of the GF-CoS2/CoS electrode.

Fig. 5

Configuration and performance of the polysulfide/iodide redox flow batteries (SIFBs). a Scheme of the proposed SIFB cell configuration. b The first charge and discharge curves of SIFBs based on graphite felt (GF), GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes with N115 and N117 as the separator at 20 mA cm−2 with the 50% state of charge (SOC). c The galvanostatic cycling energy efficiency of the SIFBs at 20 mA cm−2. d The discharge polarization and power density curves of the SIFBs at 50% SOC. e The polarization curves of both charge and discharge with the same flow cell at 50% SOC. f The electrochemical impedance spectroscopic (EIS) plots of SIFBs with GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes in the frequency range of 100 kHz to 100 mHz with 5 mV ac oscillation

Table 3 Summary of simulation results from EIS spectra of GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes, respectively


In summary, the CoS2/CoS n-n heterojunction with uneven charge distribution was prepared by a rationally designed solvothermal system via simply adjusting the proportion of DMF and EG in the mixed solvent and employed as highly active electrocatalysts in aqueous SIFBs. The charged surfaces derived from space charge regions of the CoS2/CoS heterojunction can enhance the electrochemical activities of I/I3 and S2−/Sx2− redox reactions by the improved absorptivity to charged ions and promoted the charge transfer process. Therefore, the flow cell with the GF-CoS2/CoS electrode gives a high EE of 84.5% at 10 mA cm−2 and the EE retention of 96% after ca. 1000 h continuous working. Moreover, the GF-CoS2/CoS electrode has a much higher power density of 86.2 mW cm−2 compared to GF electrode (8.9 mW cm−2). The design of heterojunction electrocatalysts would offer an effective strategy to enhance the performance and competitiveness of SIFBs and other RFBs.



Sodium iodide (NaI, 99%), sodium sulfide nonahydrate (Na2S∙9H2O, >98%), sodium chloride, sublimed sulfur (99.5%), sulfuric acid (H2SO4, 98%), hydrogen peroxide (H2O2, 30 wt% in H2O), CoSO4∙7H2O, urea, DMF, and EG were purchased from Sinopharm Chemical Reagent Co., Ltd. Iodine (I2, 99.8%) was purchased from Shanghai Titan Scientific Co., Ltd. Nafion membrane (N115 and N117, Dupont, DE, USA) was received from Innochem. Sodium polysulfide (Na2Sx) electrolytes were prepared by mixing stoichiometric ratios of Na2S and S at room temperature. Sodium triiodide (NaI3) electrolytes were prepared by mixing stoichiometric ratios of NaI and I2 at room temperature.

Synthesis of the electrode materials

Prior to synthesis, the as-received GF (Beijing Jinglong Carbon Technology Co., Ltd.) was first soaked overnight in 6 M H2SO4. It was rinsed with deionized (DI) water until the effluent pH is near 7 and then heat treated at 300 °C for 2 h. The CoS2/CoS heterojunction was synthesized by a facile and one-step hydrothermal method. In a typical procedure, 2 mmol CoSO4∙7H2O, 10 mmol urea, and 25 mmol sublimed sulfur were mixed in 70 mL mixed solution of EG and DMF (VEG/VDMF = 0.9). The precursor solution was magnetically stirred for 1 h and subsequently added into a 100 mL Teflon-lined autoclave. The autoclave was kept at 180 °C for 12 h in an oven. After cooling down, the product was collected by centrifugation, washed with DI water and absolute ethanol several times, and dried at 60 °C for 12 h under vacuum. Similarly, to obtain the GF-CoS2/CoS electrode, the GF (1.3 cm × 1.3 cm × 3 mm) was placed inside the precursor solution and the reaction temperature was kept at 180 °C for 12 h. After cooling down, the GF loaded with CoS2/CoS heterojunction was washed in an ultrasonic cleaner by water several times until no obvious CoS2/CoS particles were observed in the wastewater stream and finally dried at 60 °C for 12 h under vacuum. For comparison, the pure CoS2 and CoS were also synthesized using a similar process via tuning the mixed solvent of DMF and EG. When VEG/VDMF = 0.5 and 2, the products were CoS2 nanospheres and CoS, respectively. Similarly, in the GF-CoS2 and GF-CoS electrode experiments, the GFs were inserted into the corresponding precursor solution and the reaction temperature was kept at 180 °C for 12 h. Finally, the GF-CoS2 and GF-CoS electrodes were collected. Their mass loadings on GF were calculated through the weight change of the GF. The mass loadings of CoS2, CoS2/CoS, and CoS on the GF were 1.07, 0.83, and 1.12 mg cm−2, respectively.

Assembly of aqueous SIFBs

The Supplementary Fig. 23 showed the configurations of aqueous SIFB cells. The flow cell used in this study was similar to previous literature reports with interdigitated flow fields and a geometric active area of 1.69 cm2 (1.3 × 1.3 cm2)1. Carbon papers (Beijing Jinglong Carbon Technology Co., Ltd.) were used as the current collector. The GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS electrodes were used as both positive and negative electrodes. Commercially available Nafion membranes (N115 and N117) were utilized as separators. First, membranes were treated with 5% H2O2 under 80 °C for 1 h and then were transferred to 5% H2SO4 at 80 °C for 1 h. Finally, 1 M NaOH aqueous solution was used to change the H-type (i.e., proton conductive) Nafion membranes to Na-type (i.e., Na+ conductive) under 80 °C for 2 h. The membranes were rinsed in DI water for 30 min to wash away the chemicals after each step. Electrolytes were prepared at room temperature under continuously bubbling argon gas for 30 min to prevent oxidation by oxygen before the use. Two half cell bodies with the GF, GF-CoS2, GF-CoS2/CoS, or GF-CoS electrodes as both positive and negative electrodes and the Nafion membrane (N115 and N117) in between were assembled in the ambient air. A peristaltic pump (BT100LC, Baoding Chuang Rui Precision Pump Co., Ltd) was used to drive electrolytes through the flow cell and reservoirs. Silicone tube (1.6 mm inner diameter) was used to circulate the electrolyte through the system.


The as-prepared products were characterized on an XRD (Bruker-D8 advance) equipped with a Cu Kα radiation source (λ = 1.5418 Å) at a scanning rate of 6 ° min−1; X-ray tube voltage and current were set at 40 kV and 40 mA, respectively. SEM, TEM, and HAADF-STEM images were taken with an FEI Nova NanoSEM NPE218, JEM-2100, and JEM-ARM200F, respectively. The samples were prepared by dropping ethanol dispersion of samples onto carbon-coated copper TEM grids using pipettes and dried under ambient condition. EELs were recorded using an FEI Talos F200X equipped with super-EDX and energy filter (Gatan GIF Quantum ER 965) operated at 200 kV under STEM mode. By using Gatan Quantum 965 with dual EELs capability, both low- and high-loss region were collected near simultaneously, which allows accurate measurement of chemical shifts as EELs SI analysis was carried out. XPS was performed on an AXIS ULTRA DLD X-ray photoelectron spectrometer. UV-Vis absorption spectrum was obtained from Lambda 750S (Perkin Elmer, Inc., USA). Elemental content was tested by EDX and ICP-optical emission spectroscopy (iCAP7600). Raman spectra were recorded by a DXR Raman spectrophotometer (Thermo Fisher Scientific) at an excitation radiation wavelength of 532 nm.

Visualized adsorption test

The GF, GF-CoS2, GF-CoS2/CoS, and GF-CoS with the same mass were added into 10 mL of iodide (5.2 mM NaI + 1.3 mM I2) or polysulfide (12 mM Na2S2) aqueous solution separately, and the mixtures were vigorously stirred 12 h to realize through adsorption. The UV-Vis spectroscopy of the solutions was further recorded for comparison.

Electrochemical measurements

CV tests were performed in a three-electrode configuration with a Zahner Zennium CIMPS-1 electrochemical workstation. For fabrication of the working electrodes, 10 mg of catalysts (for example, CoS2/CoS) was dispersed in 500 μL of DI water, 500 μL of isopropanol, and 20 μL of 5 wt% Nafion solution to form a homogeneous ink. Ten microliters of the catalyst ink was loaded onto a glassy carbon electrode of 3 mm in diameter. Then the electrode was dried at room temperature. The electrochemical studies were recorded with a three-electrode system containing an aqueous solution of 4 mM NaI + 0.5 M NaCl or 0.06 M Na2S + 0.02 M S + 0.5 M NaCl at a scan rate of 50 mV s−1 at room temperature, in which Pt sheet and Ag/AgCl electrode worked as the counter electrode and the reference electrode, respectively. The Mott–Schottky plot was characterized in a three-electrode system containing a 0.5 mol L−1 Na2SO4 solution, in which Pt worked as the counter electrode, the samples as the working electrode, and Ag/AgCl as the reference electrode, respectively.

Flow cell tests

The galvanostatic characterizations of the SIFB cells were conducted on battery testing system (LAND, CT2001A, Wuhan LAND electronics Co., Ltd). The electrolyte volume was 5 mL for both 2.0 M NaI + 0.5 M I2 catholyte and 2.0 M Na2S2 anolyte and the electrolyte flow rate was fixed at 10 mL min−1 throughout all the experiments. The theoretical capacity was calculated by catholyte (the iodide part), which was 5 mL of 2.0 M NaI + 0.5 M I2, with a nominal capacity of 134 mAh. The charge process is limited to the capacity-limiting factor for the full cell. The flow cell was galvanostatically charged to 50% SOC (capacity cutoff) and discharge to 0.1 V voltage cutoff. The flow cell was operated at current densities from 15 to 50 mA cm−2. During the cycle test, the electrolytes are filled with N2. The extended cycling experiment was conducted at 20 mA cm−2. Using the Zahner Zennium CIMPS-1 electrochemical workstation, at the charged state, the EIS measurement was conceived in the frequency range of 100 kHz to 100 MHz with 5 mV ac oscillation.

Computational methods

In order to optimize both CoS2 and CoS structures, the exchange correlation function, Perdew, Burke, and Ernzerhof of the generalized gradient approximation with Koelling–Hamon relativistic treatment and spin polarization assumption is employed. Broyden–Fletcher–Goldfarb–Shanno geometry optimization is used for cell optimization (at fixed internal stress). The interaction between valence electrons and the ionic core is described by using On-The-Fly-Generation ultra soft pseudo potential. The kinetic cutoff energy for convergence test is 300 eV, a k-point set mesh (3 × 3 × 1) parameter is used for Brillouin zone sampling56,57. The threshold for self-consistent field iterations used is 2.0 × 10−6 eV atom−1. The convergence tolerance parameters of the optimized calculation are the tolerance for energy 2.0 × 10−5 eV atom−1, the maximum force of 0.05 eV Å−1, and maximum displacement of 2 × 10−3 Å58,59.

Data availability

The data underlying Figs. 1, 2a–g, and 6d, 6f and Supplementary Figs. 3–5 and 21 are provided as a Source Data file. The other data that support the findings of this study are available from the corresponding author on reasonable request.


  1. 1.

    Chu, S., Cui, Y. & Liu, N. The path towards sustainable energy. Nat. Mater. 16, 16–22 (2016).

    ADS  Article  Google Scholar 

  2. 2.

    Yang, Z. G. et al. Electrochemical energy storage for green grid. Chem. Rev. 111, 3577–3613 (2011).

    CAS  Article  Google Scholar 

  3. 3.

    Winsberg, J., Hagemann, T., Janoschka, T., Hager, M. D. & Schubert, U. S. Redox-flow batteries: from metals to organic redox-active materials. Angew. Chem. Int. Ed. 56, 686–711 (2017).

    CAS  Article  Google Scholar 

  4. 4.

    Janoschka, T. et al. An aqueous, polymer-based redox-flow battery using non-corrosive, safe, and low-cost materials. Nature 527, 78–81 (2015).

    CAS  ADS  Article  Google Scholar 

  5. 5.

    Lin, K. et al. Alkaline quinone flow battery. Science 349, 1529–1532 (2015).

    CAS  ADS  Article  Google Scholar 

  6. 6.

    Luo, J., Hu, B., Debruler, C. & Liu, T. L. A π-conjugation extended viologen as a two-electron storage anolyte for total organic aqueous redox flow batteries. Angew. Chem. Int. Ed. 57, 231–235 (2018).

    CAS  Article  Google Scholar 

  7. 7.

    Hu, B., DeBruler, C., Rhodes, Z. & Liu, T. L. Long-cycling aqueous organic redox flow battery (AORFB) toward sustainable and safe energy storage. J. Am. Chem. Soc. 139, 1207–1214 (2017).

    CAS  Article  Google Scholar 

  8. 8.

    DeBruler, C. et al. Designer two-electron storage viologen anolyte materials for neutral aqueous organic redox flow. Battery Chem. 3, 961–978 (2017).

    CAS  Article  Google Scholar 

  9. 9.

    DeBruler, C., Hu, B., Moss, J., Luo, J. & Liu, T. L. A sulfonate-functionalized viologen enabling neutral cation exchange, aqueous organic redox flow batteries toward renewable energy storage. ACS Energy Lett. 3, 663–668 (2018).

    CAS  Article  Google Scholar 

  10. 10.

    Montoto, E. C. et al. Redox active colloids as discrete energy storage carriers. J. Am. Chem. Soc. 138, 13230–13237 (2016).

    CAS  Article  Google Scholar 

  11. 11.

    Zhou, M. et al. Nernstian-potential-driven redox-argeting reactions of battery. Mater. Chem. 3, 1036–1049 (2017).

    CAS  Google Scholar 

  12. 12.

    Li, W., Fu, H.-C., Zhao, Y., He, J.-H. & Jin, S. 14.1% Efficient monolithically integrated solar flow battery. Chem 11, 2644–2657 (2018).

    Article  Google Scholar 

  13. 13.

    Weng, G.-M., Li, Z., Cong, G., Zhou, Y. & Lu, Y.-C. Unlocking the capacity of iodide for high-energy-density zinc/polyiodide and lithium/polyiodide redox flow batteries. Energy Environ. Sci. 10, 735–741 (2017).

    CAS  Article  Google Scholar 

  14. 14.

    Zhao, Y. & Byon, H. R. High-performance lithium-iodine flow battery. Adv. Energy Mater. 3, 1630–1635 (2013).

    CAS  Article  Google Scholar 

  15. 15.

    Ding, Y. & Yu, G. A bio-inspired, heavy-metal-free, dual-electrolyte liquid battery towards sustainable energy storage. Angew. Chem. Int. Ed. 128, 4850–4854 (2016).

    Article  Google Scholar 

  16. 16.

    Ding, Y., Zhao, Y. & Yu, G. A membrane-free ferrocene-based high-rate semiliquid battery. Nano Lett. 15, 4108–4113 (2015).

    CAS  ADS  Article  Google Scholar 

  17. 17.

    Hollas, A. et al. A biomimetic high-capacity phenazine-based anolyte for aqueous organic redox flow batteries. Nat. Energy 3, 508–514 (2018).

    CAS  ADS  Article  Google Scholar 

  18. 18.

    Wei, X. et al. Radical compatibility with nonaqueous electrolytes and its impact on an all-organic redox flow battery. Angew. Chem. Int. Ed. 54, 8684–8687 (2015).

    CAS  Article  Google Scholar 

  19. 19.

    Zhou, H., Zhang, H., Zhao, P. & Yi, B. Novel cobalt coated carbon felt as high performance negative electrode in sodium polysulfide/bromine redox flow battery. Electrochemistry 74, 296–298 (2006).

    CAS  Article  Google Scholar 

  20. 20.

    Li, Z. et al. Air-breathing aqueous sulfur flow battery for ultralow-cost long-duration electrical storage. Joule 1, 306–327 (2017).

    CAS  Article  Google Scholar 

  21. 21.

    Wei, X. et al. An aqueous redox flow battery based on neutral alkali metal ferri/ferrocyanide and polysulfide electrolytes. J. Electrochem. Soc. 163, A5150–A5153 (2016).

    CAS  Article  Google Scholar 

  22. 22.

    Fan, F. Y. et al. Polysulfide flow batteries enabled by percolating nanoscale conductor networks. Nano Lett. 14, 2210–2218 (2014).

    CAS  ADS  Article  Google Scholar 

  23. 23.

    Pan, H. L. et al. On the way toward understanding solution chemistry of lithium polysulfides for high energy Li-S redox flow batteries. Adv. Energy Mater. 5, 1500113 (2015).

    Article  Google Scholar 

  24. 24.

    ARPA-E. GRIDS Program Overview. http://arpa-e.energy.gov/sites/default/files/documents/files/GRIDS_ProgramOverview.pdf (The Department of Energy, Washington, D.C., 2011).

  25. 25.

    Li, Z., Weng, G., Zou, Q., Cong, G. & Lu, Y.-C. A high-energy and low-cost polysulfide/iodide redox flow battery. Nano Energy 30, 283–292 (2016).

    CAS  Article  Google Scholar 

  26. 26.

    Park, S. & Kim, H. Preparation of a sulfonated poly(ether ether ketone)-based composite membrane with phenyl isocyanate treated sulfonated graphene oxide for a vanadium redox flow battery. J. Electrochem. Soc. 163, A2293–A2298 (2016).

    CAS  Article  Google Scholar 

  27. 27.

    Zhao, Y. et al. A 3.5 V lithium-iodine hybrid redox battery with vertically aligned carbon nanotube current collector. Nano Lett. 14, 1085–1092 (2014).

    CAS  ADS  Article  Google Scholar 

  28. 28.

    Wang, S., Zhao, X., Cochell, T. & Manthiram, A. Nitrogen-doped carbon nanotube/graphite felts as advanced electrode materials for vanadium redox flow batteries. J. Phys. Chem. Lett. 3, 2164–2167 (2012).

    CAS  Article  Google Scholar 

  29. 29.

    Zhu, C., Gao, D., Ding, J., Chao, D. & Wang, J. TMD-based highly efficient electrocatalysts developed by combined computational and experimental approaches. Chem. Soc. Rev. 47, 4332–4356 (2018).

    CAS  Article  Google Scholar 

  30. 30.

    Lin, Y. et al. Growth of p-type hematite by atomic layer deposition and its utilization for improved solar water splitting. J. Am. Chem. Soc. 134, 5508–5511 (2012).

    CAS  Article  Google Scholar 

  31. 31.

    Ye, M. D. et al. In situ growth of CuS and Cu1.8S nanosheet arrays as efficient counter electrodes for quantum dot-sensitized solar cells. J. Mater. Chem. A 3, 9595–9600 (2015).

    CAS  Article  Google Scholar 

  32. 32.

    Jiang, Y. et al. ITO@Cu2S tunnel junction nanowire arrays as efficient counter electrode for quantum-dot-sensitized solar cells. Nano Lett. 14, 365–372 (2014).

    CAS  ADS  Article  Google Scholar 

  33. 33.

    Reddy, A. E. et al. Morphology controllable time-dependent CoS nanoparticle thin films as efficient counter electrode for quantum dot-sensitized solar cells. J. Chem. Phys. Lett. 687, 238–243 (2017).

    CAS  ADS  Article  Google Scholar 

  34. 34.

    Chen, C. et al. Preparation of hollow Co9S8 nanoneedle arrays as effective counter electrodes for quantum dot-sensitized solar cells. J. Mater. Chem. A 3, 6311–6314 (2015).

    CAS  Article  Google Scholar 

  35. 35.

    Yang, Z. S., Chen, C. Y., Liu, C. W. & Chang, H. T. Electrocatalytic sulfur electrodes for CdS/CdSe quantum dot-sensitized solar cells. Chem. Commun. 46, 5485–5487 (2010).

    CAS  Article  Google Scholar 

  36. 36.

    Que, M. L. et al. Flexible quantum dot-sensitized solar cells employing CoS nanorod arrays/graphite paper as effective counter electrodes. J. Mater. Chem. A 2, 13661–13666 (2014).

    CAS  Article  Google Scholar 

  37. 37.

    Tachan, Z. et al. PbS as a highly catalytic counter electrode for polysulfide-based quantum dot solar cells. J. Phys. Chem. C 115, 6162–6166 (2011).

    CAS  Article  Google Scholar 

  38. 38.

    Yang, Y. Y. et al. Composite counter electrode based on nanoparticulate PbS and carbon black: towards quantum dot-sensitized solar cells with both high efficiency and stability. ACS Appl. Mater. Interfaces 4, 6162–6168 (2012).

    CAS  Article  Google Scholar 

  39. 39.

    Chen, H. N., Zhu, L. Q., Liu, H. C. & Li, W. P. ITO porous film-supported metal sulfide counter electrodes for high-performance quantum-dot-sensitized solar cells. J. Phys. Chem. C 117, 3739–3746 (2013).

    CAS  Article  Google Scholar 

  40. 40.

    Tan, C., Chen, J., Wu, X.-J. & Zhang, H. Epitaxial growth of hybrid nanostructures. Nat. Rev. Mater. 3, 17089 (2018).

    CAS  ADS  Article  Google Scholar 

  41. 41.

    Pradhan, N. R. et al. An optoelectronic switch based on intrinsic dual schottky diodes in ambipolar MoSe2 field-effect transistors. Adv. Electron. Mater. 1, 1500215 (2015).

    Article  Google Scholar 

  42. 42.

    Prusty, G. et al. Modulated binary-ternary dual semiconductor heterostructures. Angew. Chem. Int. Ed. 55, 2705–2708 (2016).

    CAS  Article  Google Scholar 

  43. 43.

    Li, X. et al. Two-dimensional GaSe/MoSe2 misfit bilayer heterojunctions by van der Waals epitaxy. Sci. Adv. 2, e1501882 (2016).

    ADS  Article  Google Scholar 

  44. 44.

    Pospischil, A., Furchi, M. M. & Mueller, T. Solar-energy conversion and light emission in an atomic monolayer p-n diode. Nat. Nanotechnol. 9, 257–261 (2014).

    CAS  ADS  Article  Google Scholar 

  45. 45.

    Kinner, T. et al. Majority carrier type control of cobalt iron sulfide (CoxFe1–xS2) pyrite nanocrystals. J. Phys. Chem. C 120, 5706–5713 (2016).

    CAS  Article  Google Scholar 

  46. 46.

    Peng, S. et al. Unique cobalt sulfide/reduced graphene oxide composite as an anode for sodium-ion batteries with superior rate capability and long cycling stability. Small 12, 1359–1368 (2016).

    CAS  Article  Google Scholar 

  47. 47.

    Chen, W. et al. In situ electrochemically derived nanoporous oxides from transition metal dichalcogenides for active oxygen evolution catalysts. Nano Lett. 16, 7588–7596 (2016).

    CAS  ADS  Article  Google Scholar 

  48. 48.

    Zhu, L. et al. Investigation of CoS2-based thin films as model catalysts for the oxygen reduction reaction. J. Catal. 258, 235–242 (2008).

    CAS  Article  Google Scholar 

  49. 49.

    Chen, Y. et al. Silicon decorated with amorphous cobalt molybdenum sulfide catalyst as an efficient photocathode for solar hydrogen generation. ACS Nano 9, 3829–3836 (2015).

    CAS  Article  Google Scholar 

  50. 50.

    Wang, P. et al. Precise tuning in platinum-nickel/nickel sulfide interface nanowires for synergistic hydrogen evolution catalysis. Nat. Commun. 8, 14580 (2017).

    CAS  ADS  Article  Google Scholar 

  51. 51.

    Zhu, C. et al. In situ grown epitaxial heterojunction exhibits high-performance electrocatalytic water splitting. Adv. Mater. 30, e1705516 (2018).

    Article  Google Scholar 

  52. 52.

    Huang, S. et al. Synergistically enhanced electrochemical performance of Ni3S4-PtX (X = Fe, Ni) heteronanorods as heterogeneous catalysts in dye-sensitized solar cells. ACS Appl. Mater. Interfaces 9, 27607–27617 (2017).

    CAS  Article  Google Scholar 

  53. 53.

    Zou, Q. L. et al. Cation-directed selective polysulfide stabilization in alkali metal-sulfur batteries. J. Am. Chem. Soc. 140, 10740–10748 (2018).

    CAS  Article  Google Scholar 

  54. 54.

    Zou, Q. & Lu, Y.-C. Solvent-dictated lithium sulfur redox reactions: an operando UV-vis spectroscopic study. J. Phys. Chem. Lett. 7, 1518–1525 (2016).

    CAS  Article  Google Scholar 

  55. 55.

    Bayeh, A. W. et al. Ta2O5-nanoparticle-modified graphite felt as a high-performance electrode for a vanadium redox flow battery. ACS Sustain. Chem. Eng. 6, 3019–3028 (2018).

    CAS  Article  Google Scholar 

  56. 56.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    CAS  ADS  Article  Google Scholar 

  57. 57.

    Vanderbilt, D. Soft self-consistent pseudopotentials in a generalized eigenvalue formalism. Phys. Rev. B 41, 7892–7895 (1990).

    CAS  ADS  Article  Google Scholar 

  58. 58.

    Lejaeghere, K., Van Speybroeck, V., Van Oost, G. & Cottenier, S. Error estimates for solid-state density-functional theory predictions: an overview by means of the ground-state elemental crystals. Crit. Rev. Solid State 39, 1–24 (2014).

    CAS  Article  Google Scholar 

  59. 59.

    Clark, S. J. et al. First principles methods using CASTEP. Z. Kristallogr. 220, 567–570 (2005).

    CAS  Google Scholar 

Download references


This work was supported by National Natural Science Foundation of China (21771124, 21501120, 21331004 and 21673273), Science and Technology Commission of Shanghai Municipality (17ZR1441200), Shanghai Rising-Star Program (18QA1402400) and Scientific Innovation Talent of Henan Province (174200510017), National Science Foundation (Career Award, Grant No. 1847674), Utah State University Faculty start-up (to T.L.L.), the Utah Science Technology and Research initiative (USTAR) research award, and Utah Energy Triangle Faculty Award sponsored by the Utah State government. B.H. is grateful for China CSC Abroad Studying Fellowship and Utah Energy Triangle Student Award supported by the Utah State government.

Author information




D.M., J.Z., and T.L.L. conceived and designed the experiments. D.M., B.H., and C.S. carried out the design and material synthesis. D.M., X.L., L.C., B.H., W.W., J.Z. and T.L.L. performed the measurements and data analysis. T.T.T. built the theoretical modeling and analyzed the computational data. D.M., J.Z., B.H., W.W., T.L.L., and X.Q. participated in the preparation of the manuscript.

Corresponding authors

Correspondence to Jiantao Zai or Xuefeng Qian or T. Leo Liu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information: Nature Communications would like to thank the anonymous reviewers for their contributions to the peer review of this work.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ma, D., Hu, B., Wu, W. et al. Highly active nanostructured CoS2/CoS heterojunction electrocatalysts for aqueous polysulfide/iodide redox flow batteries. Nat Commun 10, 3367 (2019). https://doi.org/10.1038/s41467-019-11176-y

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing