Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Active catalyst construction for CO2 recycling via catalytic synthesis of N-doped carbon on supported Cu


Bridging homogeneous and heterogeneous catalysis is a long-term pursuit in the field of catalysis. Herein, we report our results in integration of nano- and molecular catalysis via catalytic synthesis of nitrogen doped carbon layers on AlOx supported nano-Cu which can finely tune the catalytic performance of the supported copper catalyst. This synthetic catalytic material, which can be generated in situ by the reaction of CuAlOx and 1,10-Phen in the presence of hydrogen, could be used for controllable synthesis of N,N-dimethylformamide (DMF) from dimethylamine and CO2/H2 via blocking reaction pathways of further catalytic hydrogenation of DMF to N(CH3)3. Detailed characterizations and DFT calculations reveal that the presence of N-doped layered carbon on the surface of the nano-Cu particles results in higher activation energy barriers during the conversion of DMF to N(CH3)3. Our primary results could promote merging of homogeneous catalysis and heterogeneous catalysis and CO2 recycling.


Utilization and transformation of CO2 into value-added chemicals have the potential to alleviate climate change and mitigate the dependence on fossil fuels1,2,3. Among various CO2 transformation routes, the reductive functionalization of CO2 to DMF is one of the most promising approaches for its chemical utilization, since DMF is a versatile multipurpose reagent in numerous synthetic processes and important solvent having widespread applications in industry4,5. Currently, DMF is primarily produced by sodium methoxide catalyzed carbonylation of dimethylamine with carbon monoxide in methanol at 2–10 MPa and 353–373 K6. To substitute the toxic carbon monoxide, the reductive coupling of dimethylamine with CO2 and H2 would offer a fascinating route for sustainable production of DMF. Since the initial report by Haynes et al. on (Ph3P)2(CO)IrCl catalyzed preparation of DMF from dimethylamine with CO2 and H2 in 19707, a series of homogeneous and heterogeneous transition-metal catalysts, such as ruthenium8,9,10,11, palladium12,13,14, platinum15, iridium16, iron17,18, copper19,20,21,22, and others23,24,25, are developed for the reduction of CO2 to synthesize DMF. Although it has been extensively studied, the highly controlled synthesis of DMF remains a tremendous challenge because DMF is prone to further reduction into N(CH3)326. Therefore, the development of efficient methods for controllable synthesis of DMF from dimethylamine and CO2/H2 via suppression of further reduction of DMF to N(CH3)3 is highly desirable, especially by heterogeneous catalysts, because it is easy to be applied in practical process. However, the regulation of the catalytic performance of heterogeneous catalysts on molecular level is difficult. Noteworthy, the development of homogeneous catalysis gives us nice inspirations, in which the catalytic performance can be precisely modulated by organic ligand27,28,29. For example, N-formylation and N-methylation of amines with CO2 and phenylsilane can be precisely controlled by organic ligand, i.e., DPPB (1,4-bis(diphenylphosphino)butane) promoted N-methylation whereas Ph2CyP (diphenylcyclohexylphosphine) favored for N-formylation29. Also, it has been revealed that the addition of molecular organic ligands can tune the catalytic performance of heterogeneous catalysts, too30,31,32,33,34,35,36,37,38,39,40,41,42. So, a heterogeneous catalyst with the catalytic performance of homogeneous catalyst might be obtained if the traditional organic ligand can be controllably deposited on the surface of heterogeneous catalyst.

It is well known that transition-metal catalysts such as Cu possess the ability of converting the organic molecules into carbon materials, such as CNT (carbon nanotube), graphite/graphene (oxide), amorphous carbon, and ordered mesoporous carbon43,44. In addition, Cu was found to be an active catalyst for catalytic hydrogenation of CO2 to methanol45 and nitrogen-containing ligand was usually used to tuning the catalytic performance of active metals30,33. Inspired by the discussions above, a N-doped carbon layer on the surface of nanoparticles might be formed in situ by using the nitrogen-containing ligand as the carbon layer precursor (Fig. 1). In this way, a facile methodology to integrate heterogeneous and homogeneous catalysts can be built, and the preparation of heterogeneous catalyst with homogeneous characteristics for controllable synthesis of DMF with CO2/H2 may be realized.

Fig. 1

Illustration of carbon coated copper catalyst generation. The nitrogen doped carbon layers can be generated in situ by the reaction of CuAlOx and 1,10-Phen in the presence of hydrogen

Herein, we report a facile methodology for integration of nano- and molecular catalysis via catalytic synthesis of nitrogen doped carbon layers on AlOx supported nano-Cu. This synthetic catalytic material, which can be generated in situ by the reaction of CuAlOx and 1,10-Phen in the presence of hydrogen, could be used for controllable synthesis of DMF from dimethylamine and CO2/H2 via blocking reaction pathways of further catalytic hydrogenation of DMF to N(CH3)3.


Optimization of the reaction conditions

To validate our hypothesis, we commenced our studies by investigating the reactions of N,N-dimethylammonium N′,N′-dimethylcarbamate (DIMCARB) in the presence of CuAlOx and different organic nitrogen-containing ligands under 3 MPa of CO2 and 7 MPa of H2 in DME at 160 °C for 24 h (Table 1). The CuAlOx catalyst used here was prepared by a co-precipitation method by adding an aqueous solution of Na2CO3 to a Cu(NO3)2 and Al(NO3)3 solution. It was found that the reaction proceeded smoothly in the absence of ligand leading to DMF and N(CH3)3 in 93.7% total yield with low selectivity of 41.8% toward DMF (Entry 1). Among the common monodentate nitrogen-containing ligands in this study, the selectivity to DMF slightly decreased when Et3N and PhNMe2 were used while Py slightly promoted to deliver DMF with 44.0% selectivity (Entries 2–4). Then, various bidentate ligands were also evaluated. Bipy had a negligible impact on the observed selectivity (Entry 5). Clearly, the selectivity toward DMF can be improved slightly if TMEDA was added during the reactions (Entry 6). Compared with TMEDA, the selectivity to DMF sharply increased to 77.9% if DMEDA was employed (Entry 7). In addition, it was discovered that 1,10-Phen exhibited the highest DMF selectivity, i.e., 86.7% (Entry 8). Reducing the amount of 1,10-Phen to 5 mol% resulted in a lower selectivity toward DMF but the same reactivity was kept (Entry 9). Further increasing the amount of 1,10-Phen led to a higher selectivity to DMF (Entries 10–11). Importantly, this catalyst was easily recovered by simple filtration, and it can be reused directly without further treatment. To our delight, 89.6% yield with 97.3% selectivity to DMF was maintained when it was used at the third run, thus, this catalyst exhibits nice reusability (Entry 12).

Table 1 Results for DMF synthesis from DIMCARB and CO2/H2a

Kinetic and product distribution

To obtain kinetic and product distribution data, the reactions of DIMCARB with CO2 and H2 in the presence of CuAlOx, CuAlOx/1,10-Phen, and CuAlOx/TMEDA were traced with varied reaction times. Their performance versus time is shown in Fig. 2. The CuAlOx catalyst or CuAlOx with TMEDA exhibited significant decline in the DMF selectivity with prolonging the reaction time, whereas the high DMF selectivity was still maintained after 24 h if CuAlOx and 1,10-Phen were applied. These results indicated that further reduction of DMF to N(CH3)3 was suppressed when 1,10-Phen was used as ligand but the activity for DMF generation was not influenced remarkably.

Fig. 2

Products distribution during the reactions of DIMCARB with CO2 and H2. Reaction conditions: DIMCARB (0.5 mmol), CuAlOx (100 mg), ligand (10 mol%), 1,2-Dimethoxyethane (4 mL), 3 MPa CO2, 7 MPa H2, 160 °C. Except DMF, N(CH3)3 is the main product

Catalyst characterization

In order to explore whether N-doped carbon layer was formed on the surface of the supported nano-copper and which condition could form a N-doped carbon layer on the surface of nanoparticles, the fresh CuAlOx catalyst and the samples being treated by different conditions were characterized by TEM, XPS, XRD, EXAFS, TGA, and N2 adsorption−desorption instruments. At first, the morphology of the CuAlOx samples was examined by TEM and HRTEM as shown in Fig. 3 and Supplementary Fig. 1. The HRTEM image of the fresh CuAlOx provided a lattice fringe with the d-spacing of 0.21 nm, according with the (111) plane of Cu. Compared with fresh catalyst, the HRTEM images of fresh catalyst after being treated with DIMCARB + Phen + CO2 + H2, Phen + CO2 + H2, Phen + H2 conditions show that the copper nanoparticles are coated with a carbon layer on their surface (shown by an arrow.) The spacing between these layers is around 0.28 nm, which is consistent with that of layered carbon. This result well agrees our hypothesis, i.e., N-doped carbon layer can be in situ synthesized on the heterogenous catalyst sample during the reaction. To trace the formation process of layered carbon, a fresh CuAlOx treated with 1,10-Phen in the presence of H2 for 8, 16, and 24 h were also characterized by HRTEM (Fig. 3d–f). Clearly, after being treated for 8 h (Fig. 3d), layered carbon was formed on the edge of catalyst (shown by an arrow). Clearly, the carbon layers grew from edge to surface of CuAlOx after being treated for 16 and 24 h (Fig. 3e, f). The HRTEM images of the fresh CuAlOx catalyst after being treated with Et3N, PhNMe2, Py, Bipy, TMEDA, and DMEDA revealed that carbon layer was not formed on the surface of CuAlOx catalyst under the same treating conditions.

Fig. 3

TEM and HRTEM images of the catalysts. HRTEM images of CuAlOx (a); CuAlOx + DIMCARB + Phen + CO2 + H2 (c); CuAlOx + Phen + H2 (8 h) (d); CuAlOx + Phen + H2 (16 h) (e); CuAlOx + Phen + H2 (24 h) (f); and TEM image of CuAlOx + DIMCARB + Phen + CO2 + H2 (b). c is a magnified picture of a region from b. The scale bar of a, c, d, e, f is 5 nm; b is 10 nm

Furthermore, XPS was performed to explore the chemical state and composition of surface elements in the fresh and treated catalysts (Supplementary Fig. 2). The XPS spectra of all catalysts display two main peaks at 933.5 and 953.5 eV, which are in agreement with Cu 2p3/2 and Cu 2p1/2 the binding energies of Cu2+, respectively. Considering that metallic copper was observed in TEM characterizations, the appearance of Cu2+ on catalyst surface should be attributed to the oxidation of Cu(0) when the catalyst samples were exposed to air19,46,47. The C 1 s and N 1 s spectra of the catalysts were also analyzed by XPS (Supplementary Fig. 3). However, the C1s spectra were overlapped by the organic carbon from environment, and the N1s spectra were too weak due to the low concentration. So the structure of the carbon layers can not be determined by XPS analysis.

According to the nitrogen adsorption–desorption isotherms, the formation of mesoporous structure for the fresh CuAlOx catalyst was observed (Supplementary Fig. 4). Clearly, it was composed of pores with diameters of 5.1 and 12.2 nm. It should be noted that the porous structure partly disappeared after the treatment of fresh catalyst under different conditions, which should be attributed to that formation of layered carbon, resulting in clogged mesoporous of the fresh CuAlOx catalyst. The N2 adsorption−desorption tests showed that the BET surface areas of the fresh and treated catalysts (Supplementary Table 1) were 250.3−330.3 m2 g−1.

Then, fresh CuAlOx catalyst and the samples being treated by different conditions were characterized by XRD measurement, too (Fig. 4a and Supplementary Fig. 5). The fresh CuAlOx samples show diffraction peaks at 25.3, 37.9, 48.2, 54.1, and 55.3, which can be assigned as (101), (004), (200), (105), and (211) reflection lines of γ-Al2O3. The treated catalysts showed XRD reflections at 43.3°, 50.4°, 74.1°, 89.9°, and 95.0°, which are ascribed to the metallic copper phase. As the copper particle size can not be precisely determined by TEM, in which the copper particles were overlapped with AlOx, the crystallite sizes of different catalysts were calculated from Cu (111) diffraction peak in XRD by using Scherrer equation. As shown in Supplementary Table 1, these samples have a copper crystallite size in the range from 5.1 to 19.9 nm. Besides, the fresh CuAlOx catalyst treated with DIMCARB + Phen + CO2 + H2, Phen + CO2 + H2, Phen + H2 conditions exhibited a new diffraction peak located at 18.0°. This peak is the typical diffraction peak of N-dope carbon (PDF#51–2183), which clearly proves our hypothesis. In addition, no diffraction peak was observable at 18.1° in fresh catalyst after being treated with Et3N, PhNMe2, Py, Bipy, TMEDA, and DMEDA. These results revealed that layered carbon was not formed on the surface of CuAlOx catalyst under the above conditions, which is in line with the TEM results. Therefore, we could draw conclusion that other ligands are not able to modulate the selectivity because of lack formation of the carbon shell on the catalysts.

Fig. 4

XRD patterns of the samples. a XRD patterns of CuAlOx catalysts treated in different conditions: CuAlOx (curve a); CuAlOx + DIMCARB + CO2 + H2 (curve b); CuAlOx + Phen + CO2 (curve c); CuAlOx + Phen + Ar (curve d); CuAlOx + DIMCARB + Phen + CO2 + H2 (curve e); CuAlOx + Phen + CO2 + H2 (curve f); and CuAlOx + Phen + H2 (curve g). b Time-resolved XRD patterns of CuAlOx catalysts treated with 1,10-Phen and H2 at different times: 0, 4, 8, 12, 16, 20, and 24 h

Following, time-resolved XRD patterns of CuAlOx catalysts treated with 1,10-Phen and H2 were collected in order to trace the formation progress of carbon layer (Fig. 4b). Clearly, a new peak at 18.0° appears and slowly enhancing, representing the layered carbon. This unambiguously confirmed that layered N-doped carbon coated on the surface of nanoparticle can be synthesized by reaction of CuAlOx and 1,10-Phen in the presence of H2. TG analysis (Supplementary Fig. 6) was used to gain the quantity of carbon layers or adsorbed organic molecules on CuAlOx after being treated under different conditions, which were 2.5–12.0 wt% (Supplementary Table 2). The corresponding copper loadings were 3.67–5.58 wt%.

Next, the Fourier transformed Cu K-edge EXAFS spectra were analyzed to reveal the coordination environment of Cu in CuAlOx catalyst samples (Fig. 5). The fitting results including coordination number, bond distance were listed in Supplementary Table 3. The Cu K-edge for fresh CuAlOx catalyst shows some resemblance to the CuOx reference, which may be due to the oxidation of Cu(0) when exposed to air and average particle size remains small. The results from fitting the Cu K edge EXAFS spectra show that the bond distance of Cu−Cu remains constant and a slight increase in the Cu−Cu coordination number (0.5–6.9) after CuAlOx catalyst being treated, indicating Cu particle size slightly increases after treatment. This result confirms the observations from XRD patterns.

Fig. 5

Fourier transform (FT) of Cu K-edge EXAFS. CuAlOx (curve a); CuAlOx + DIMCARB + CO2 + H2 (curve b); CuAlOx + Phen + CO2 (curve c); CuAlOx + Phen + Ar (curve d); CuAlOx + DIMCARB + Phen + CO2 + H2 (curve e); CuAlOx + Phen + CO2 + H2 (curve f); CuAlOx + Phen + H2 (curve g); and Cu foil

To verify whether this structure have the ability as we hypothesized, control experiments were conducted under the same conditions. In the reaction of DIMCARB with CO2 and H2, fresh CuAlOx catalyst produced DMF and N(CH3)3 in 93.7% combined yield with low DMF selectivity of 41.8%. If applying N-doped layer carbon coated nano-copper (CuAlOx catalyst treated with 1,10-Phen and H2) as the catalyst, 95.8% combined yield with much higher DMF selectivity of 80.2% was obtained. In addition, for the catalytic hydrogenation of DMF, fresh CuAlOx catalyst afforded 100% conversion while CuAlOx treated with 1,10-Phen and H2 only gave 25% conversion (Fig. 6). The results obviously demonstrated that the precisely synthesized catalyst indeed possesses ability for controllable synthesis of DMF from CO2/H2. The copper contents in the solution after each cycle were tested by ICP-AES (Supplementary Table 4). 2.970, 1.928, and 0.900 ppm copper were observed in the solutions with CuAlOx itself as catalyst at the first, second, and third runs, while it was only 0.513, 0.028, and 0.013 ppm if Phen was added. Therefore, except the improving of the catalytic performance for DMF synthesis, the formation of carbon layer also can stabilize the CuAlOx catalyst.

Fig. 6

Catalytic hydrogenation of DMF with different catalysts. Hundred percent conversion of DMF to N(CH3)3 was observed with CuAlOx as catalyst while it was only 25% conversion if CuAlOx treated by 1,10-Phen and H2 was applied as catalyst

DFT calculations

In order to explore the role of N-doped nano-carbon layer in controlling the selective synthesis of DMF, DFT calculations were performed to simulate the detailed reaction mechanism of DMF hydrogenation to N(CH3)3 on clean and Phen-covered Cu(111) surfaces, where five reaction pathways are considered as shown in Supplementary Figs. 8 and 9. More specifically, the adsorbed (CH3)2NCHO could produce (CH3)2NCH + O species via C–O bond breaking, and further hydrogenation of (CH3)2NCH would produce undesired N(CH3)3 species, which finally results in the lose in (CH3)2NCHO selectivity. (CH3)2NCHO could also generate (CH3)2NCH2O and (CH3)2NCHOH species via hydrogenation. Then, (CH3)2NCH2O could produce either (CH3)2NCH2 + O species via C–O bond breaking or (CH3)2NCH2OH species via deep hydrogenation. Similarly, (CH3)2NCHOH could produce either (CH3)2NCH + OH species via C–O bond breaking or (CH3)2NCH2OH species via hydrogenation. Furthermore, (CH3)2NCH2OH could produce (CH3)2NCH2 + OH species via C–O bond breaking. Finally, the (CH3)2NCH and (CH3)2NCH2 species will be hydrogenated to N(CH3)3 species. All the detailed energetics as well as structures of all the species and transition states could be found in Supplementary Figs. 10 to 13. On the basis of the systematic reaction mechanism computations, we are able to have direct comparison the difference between clean and Phen-covered Cu catalyst. Figure 7 depicts the potential energy diagrams for the most favorable reaction pathways of DMF hydrogenation to N(CH3)3 on clean and Phen-covered Cu(111) surfaces. Clearly, the presence of Phen on Cu(111) surface increases the energy barriers of C–H bond formation and C-O bond breaking in DMF hydrogenation, which indicates its lower DMF hydrogenation activity compared with clean Cu(111) surface. Therefore, the computational results can reasonably explain our experimental findings.

Fig. 7

Potential energy diagram for the most favorable reaction pathway. black line: DMF hydrogenation to N(CH3)3 on clean Cu(111) surfaces; blue line: DMF hydrogenation to N(CH3)3 on Phen-covered Cu(111) surfaces

In conclusion, we have successfully developed a facile methodology to integrate heterogeneous and homogeneous catalysts via construction of N-doped carbon layer on the surface of supported nano-catalyst. The synthetic catalytic material with defined structure exhibited a remarkable catalytic performance in contrallable synthesis of DMF. Also, the applying of this concept in other catalytic hydrogenation reactions were ongoing. This work offers an effective methodology for the precise and controlled synthesis of heterogeneous catalysts with defined active sites, and it may provide an important insight in merging homogeneous catalysis with heterogeneous catalysis as well as controlled catalytic conversion of CO2.


Preparation of CuAlOx

0.145 g (0.6 mmol) of Cu(NO3)2·3H2O and 4.275 g (11.4 mmol) of Al(NO3)3·9H2O were added into 125 mL deionized water at room temperature in a 250 mL flask. Then, 38 mL of Na2CO3 solution (0.93 mol/L) was added dropwise into the solution under vigorous stirring and the mixture was stirred for a further 5 h at room temperature. The reaction mixture was centrifuged and washed with water to remove the base until the pH value of the aqueous solution was ≈7. Subsequently, the solid was dried at 100 °C overnight, calcined at 350 °C for 12 h, and then reduced under hydrogen flow at 350 °C for 3 h. Finally, a black powder was obtained and denoted as CuAlOx.

N-formylation of dimethylamine with CO2/H2

A mixture of DIMCARB (67 mg), CuAlOx (100 mg), 1,10-Phen (0–0.15 mmol), and 1,2-dimethoxyethane (4 mL) were added in a 100 mL autoclave. The autoclave was sealed and exchanged with CO2 three times and reacted at 160 °C (oven temperature 180 °C) under 3 MPa CO2 and 7 MPa H2 for 24 h. After cooling to room temperature, the autoclave was placed in a cold trap (−20 °C) for 20 min and the gas was pumped slowly into 120 mL 2 mol/L HCl methanol solution to absorb the gaseous N(CH3)3. Then, the methanol solution was concentrated under vacuum and the yield of gaseous N(CH3)3 was obtained. Subsequently, 0.5 mL triethylamine and 15 mL 1,2-dimethoxyethane were added into the reaction mixture quickly. The GC yield of liquid N(CH3)3 and DMF were determined by GC-FID (Agilent 7890 A) using 1,4-dioxane as the internal standard. The overall yield of N(CH3)3 was calculated by adding gaseous and liquid yields together.

Procedure for recycling test

The used catalyst was separated from the reaction mixtures by centrifuging, washed three times alternately with DME and acetone. After being dried in air at room temperature, it was recovered and directly recharged into the reaction tube for the next run.

The procedures for CuAlOx catalyst treated

For CuAlOx + DIMCARB + Phen + CO2 + H2, the processing condions are the same as that of N-formylation of dimethylamine. After cooling to room temperature, the catalyst was washed alternately with methanol and acetone for three times and then dried in the air. For CuAlOx + DIMCARB + CO2 + H2 and CuAlOx + Phen + CO2 + H2, the processing conditions are the same with the reaction conditions without adding Phen or DIMCARB. For CuAlOx + Phen + CO2, CuAlOx + Phen + H2 and CuAlOx + Phen + Ar, the processing conditions are consistent with the reaction conditions with only 3 MPa of gaseous atmosphere (CO2/H2/Ar).

DFT calculations

All calculations were performed by using the plane-wave based DFT method as implemented in the Vienna ab initio simulation package (VASP)48,49. Periodic slab models were used to model the Cu catalyst. The electron ion interaction was described with the projector augmented wave (PAW) method50,51. The electron exchange and correlation energy was treated within the generalized gradient approximation in the Perdew-Burke-Ernzerhof formalism (GGA-PBE)52. The density-dependent dDsC method was used for the dispersion correction53. More computational details could be found in Supplementary Material.

Data availability

All data are available from the corresponding authors upon reasonable request.


  1. 1.

    He, M., Sun, Y. & Han, B. Green carbon science: scientific basis for integrating carbon resource processing, utilization, and recycling. Angew. Chem. Int. Ed. 52, 9620–9633 (2013).

    CAS  Article  Google Scholar 

  2. 2.

    Liu, Q., Wu, L., Jackstell, R. & Beller, M. Using carbon dioxide as a building block in organic synthesis. Nat. Commun. 6, 5933 (2015).

    Article  ADS  PubMed  Google Scholar 

  3. 3.

    Artz, J., Müller, T. E. & Thenert, K. Sustainable conversion of carbon dioxide: an integrated review of catalysis and life cycle assessment. Chem. Rev. 118, 434–504 (2018).

    CAS  Article  Google Scholar 

  4. 4.

    Ding, S. & Jiao, N. N,N-Dimethylformamide: a multipurpose building block. Angew. Chem. Int. Ed. 51, 9226–9237 (2012).

    CAS  Article  Google Scholar 

  5. 5.

    Muzart, J. N,N-Dimethylformamide: much more than a solvent. Tetrahedron 65, 8313–8323 (2009).

    CAS  Article  Google Scholar 

  6. 6.

    Weissermel, K. & Arpe, H.-J. Industrial organic chemistry. 3rd edn (Wiley-VCH, Weinheim, 1997).

  7. 7.

    Haynes, P., Slaugh, L. H. & Kohnle, J. F. Formamides from carbon dioxide, amines and hydrogen in the presence of metal complexes. Tetrahedron Lett. 11, 365–368 (1970).

    Article  Google Scholar 

  8. 8.

    Jessop, P. G., Hsiao, Y., Ikariya, T. & Noyori, R. Catalytic production of dimethylformamide from supercritical carbon dioxide. J. Am. Chem. Soc. 116, 8851–8852 (1994).

    CAS  Article  Google Scholar 

  9. 9.

    Kobayashi, K., Kikuchi, T., Kitagawa, S. & Tanaka, K. Selective generation of formamides through photocatalytic CO2 reduction catalyzed by ruthenium carbonyl compounds. Angew. Chem. Int. Ed. 53, 11813–11817 (2014).

    CAS  Article  Google Scholar 

  10. 10.

    Kröcher, O., Köppel, R. A. & Baiker, A. Highly active ruthenium complexes with bidentate phosphine ligands for the solvent-free catalytic synthesis of N, N-dimethylformamide and methyl formate. Chem. Commun. 0, 453–454 (1997).

  11. 11.

    Zhang, L., Han, Z., Zhao, X., Wang, Z. & Ding, K. Highly efficient ruthenium-catalyzed N-formylation of amines with H2 and CO2. Angew. Chem. Int. Ed. 54, 6186–6189 (2015).

    CAS  Article  Google Scholar 

  12. 12.

    Cui, X., Zhang, Y., Deng, Y. & Shi, F. Amine formylation via carbon dioxide recycling catalyzed by a simple and efficient heterogeneous palladium catalyst. Chem. Commun. 50, 189–191 (2014).

    CAS  Article  Google Scholar 

  13. 13.

    Kudo, K., Phala, H., Sugita, N. & Takezaki, Y. Synthesis of dimethyl formamide from carbon dioxide, hydrogen and dimethyl amine catalyzed by palladium (II) chloride. Chem. Lett. 6, 1495–1496 (1977).

    Article  Google Scholar 

  14. 14.

    Zhang, Y., Wang, H., Yuan, H. & Shi, F. Hydroxyl group-regulated active nano-Pd/C catalyst generation via in situ reduction of Pd(NH3)xCly/C for N-formylation of amines with CO2/H2. ACS Sustain. Chem. Eng. 5, 5758–5765 (2017).

    CAS  Article  Google Scholar 

  15. 15.

    Schreiner, S., Yu, J. Y. & Vaska, L. Reversible homogeneous catalysis of carbon dioxide hydrogenation/reduction at room temperature and low pressures. J. Chem. Soc., Chem. Commun. 0, 602–603 (1988).

  16. 16.

    Bi, Q.-Y. et al. Partially reduced iridium oxide clusters dispersed on titania as efficient catalysts for facile synthesis of dimethylformamide from CO2, H2 and dimethylamine. Chem. Commun. 50, 9138–9140 (2014).

    CAS  Article  Google Scholar 

  17. 17.

    Federsel, C. et al. A well-defined iron catalyst for the reduction of bicarbonates and carbon dioxide to formates, alkyl formates, and formamides. Angew. Chem. Int. Ed. 49, 9777–9780 (2010).

    CAS  Article  Google Scholar 

  18. 18.

    Ziebart, C. et al. Well-defined iron catalyst for improved hydrogenation of carbon dioxide and bicarbonate. J. Am. Chem. Soc. 134, 20701–20704 (2012).

    CAS  Article  Google Scholar 

  19. 19.

    Liu, J. et al. Synthesis of dimethylformamide from CO2, H2 and dimethylamine over Cu/ZnO. Chem. Commun. 46, 5770–5772 (2010).

    CAS  Article  ADS  Google Scholar 

  20. 20.

    Kumar, S. & Jain, S. L. An efficient copper catalyzed formylation of amines utilizing CO2 and hydrogen. RSC Adv. 4, 64277–64279 (2014).

    CAS  Article  Google Scholar 

  21. 21.

    Motokura, K. et al. Copper-diphosphine complex catalysts for N-formylation of amines under 1 atm of carbon dioxide with polymethylhydrosiloxane. Catal. Sci. Tech. 3, 2392–2396 (2013).

    CAS  Article  Google Scholar 

  22. 22.

    Zhiani, R., Saadati, S. M., Zahedifar, M. & Sadeghzadeh, S. M. Synthesis of new class of copper(II) complex-based FeNi3/KCC1 for the N-formylation of amines using dihydrogen and carbon dioxide. Catal. Lett. 148, 2487–2500 (2018).

    CAS  Article  Google Scholar 

  23. 23.

    Minato, M. et al. Reactions of quadruply chelated silyl–and germyl–molybdenum hydrido complexes with carboxylic acids and carbon dioxide: a first example of carbon dioxide fixation utilizing the trans effect of a silyl ligand. Chem. Commun. 0, 2654–2655 (2001).

  24. 24.

    Itagaki, S., Yamaguchi, K. & Mizuno, N. Catalytic synthesis of silyl formates with 1 atm of CO2 and their utilization for synthesis of formyl compounds and formic acid. J. Mol. Catal. A 366, 347–352 (2013).

    CAS  Article  Google Scholar 

  25. 25.

    Jacquet, O., Gomes, C. D. N., Ephritikhine, M. & Cantat, T. Recycling of carbon and silicon wastes: room temperature formylation of N-H bonds using carbon dioxide and polymethylhydrosiloxane. J. Am. Chem. Soc. 134, 2934–2937 (2012).

    CAS  Article  Google Scholar 

  26. 26.

    Cui, X., Dai, X., Zhang, Y., Deng, Y. & Shi, F. Methylation of amines, nitrobenzenes and aromatic nitriles with carbon dioxide and molecular hydrogen. Chem. Sci. 5, 649–655 (2014).

    CAS  Article  Google Scholar 

  27. 27.

    Beller, M. & Bolm, C. Transition metals for organic synthesis. (Wiley-VCH, Weinheim, 2004).

  28. 28.

    Zhang, S. et al. Copper-catalyzed N-formylation of amines with CO2 under ambient conditions. RSC Adv. 6, 32370–32373 (2016).

    CAS  Article  Google Scholar 

  29. 29.

    Li, X.-D. et al. Copper catalysis: ligand-controlled selective N-methylation or N-formylation of amines with CO2 and phenylsilane. Green. Chem. 20, 4853–4858 (2018).

    CAS  Article  Google Scholar 

  30. 30.

    Ernst, J. B. et al. Molecular adsorbates switch on heterogeneous catalysis: induction of reactivity by N-heterocyclic carbenes. J. Am. Chem. Soc. 139, 9144–9147 (2017).

    CAS  Article  PubMed  Google Scholar 

  31. 31.

    Fedorov, A., Liu, H.-J., Lo, H.-K. & Copéret, C. Silica-supported Cu nanoparticle catalysts for alkyne semihydrogenation: effect of ligands on rates and selectivity. J. Am. Chem. Soc. 138, 16502–16507 (2016).

    CAS  Article  PubMed  Google Scholar 

  32. 32.

    Almora-Barrios, N., Cano, I., Leeuwen, P. W. N. Mv & López, N. Concerted chemoselective hydrogenation of acrolein on secondary phosphine oxide decorated gold nanoparticles. ACS Catal. 7, 3949–3954 (2017).

    CAS  Article  Google Scholar 

  33. 33.

    Cao, Z. et al. A molecular surface functionalization approach to tuning nanoparticle electrocatalysts for carbon dioxide reduction. J. Am. Chem. Soc. 138, 8120–8125 (2016).

    CAS  Article  PubMed  Google Scholar 

  34. 34.

    Chen, G. et al. Interfacial electronic effects control the reaction selectivity of platinum catalysts. Nat. Mater. 15, 564–569 (2016).

    CAS  Article  ADS  PubMed  Google Scholar 

  35. 35.

    Choi, K. M., Na, K., Somorjai, G. A. & Yaghi, O. M. Chemical environment control and enhanced catalytic performance of platinum nanoparticles embedded in nanocrystalline metal-organic frameworks. J. Am. Chem. Soc. 137, 7810–7816 (2015).

    CAS  Article  PubMed  Google Scholar 

  36. 36.

    Hughes, M. D. et al. Tunable gold catalysts for selective hydrocarbon oxidation under mild conditions. Nature 437, 1132–1135 (2005).

    CAS  Article  ADS  PubMed  Google Scholar 

  37. 37.

    Jia, X. et al. Carboxylic acid-modified metal oxide catalyst for selectivity-tunable aerobic ammoxidation. Nat. Commun. 9, 933 (2018).

    Article  ADS  PubMed  Google Scholar 

  38. 38.

    Kahsar, K. R., Schwartz, D. K. & Medlin, J. W. Control of metal catalyst selectivity through specific noncovalent molecular interactions. J. Am. Chem. Soc. 136, 520–526 (2014).

    CAS  Article  PubMed  Google Scholar 

  39. 39.

    Pang, S. H., Schoenbaum, C. A., Schwartz, D. K. & Medlin, J. W. Directing reaction pathways by catalyst active-site selection using self-assembled monolayers. Nat. Commun. 4, 2448 (2013).

    Article  ADS  Google Scholar 

  40. 40.

    Vang, R. T. et al. Controlling the catalytic bond-breaking selectivity of Ni surfaces by step blocking. Nat. Mater. 4, 160–162 (2005).

    CAS  Article  ADS  Google Scholar 

  41. 41.

    Wu, B., Huang, H., Yang, J., Zheng, N. & Fu, G. Selective hydrogenation of α,β-unsaturated aldehydes catalyzed by amine-capped platinum-cobalt nanocrystals. Angew. Chem. Int. Ed. 124, 3496–3499 (2012).

    Article  Google Scholar 

  42. 42.

    Zhao, X. et al. Thiol treatment creates selective palladium catalysts for semihydrogenation of internal alkynes. Chem 4, 1–12 (2018).

    Article  Google Scholar 

  43. 43.

    Moisala, A., Nasibulin, A. G. & Kauppinen, E. I. The role of metal nanoparticles in the catalytic production of single-walled carbon nanotubes-a review. J. Phys. Condens. Matter 15, S3011–S3035 (2003).

    CAS  Article  ADS  Google Scholar 

  44. 44.

    Yan, Y. et al. Carbon nanotube catalysts: recent advances in synthesis, characterization and applications. Chem. Soc. Rev. 44, 3295–3346 (2015).

    CAS  Article  Google Scholar 

  45. 45.

    Goeppert, A., Czaun, M., Jones, J.-P., Surya Prakash, G. K. & Olah, G. A. Recycling of carbon dioxide to methanol and derived products—closing the loop. Chem. Soc. Rev. 43, 7995–8048 (2014).

    CAS  Article  Google Scholar 

  46. 46.

    Yurderi, M., Bulut, A., Ertas, İ. E., Zahmakiran, M. & Kaya, M. Supported copper–copper oxide nanoparticles as active, stable and low-cost catalyst in the methanolysis of ammonia–borane for chemical hydrogen storage. Appl. Catal. B 165, 169–175 (2015).

    CAS  Article  Google Scholar 

  47. 47.

    Blandez, J. F., Primo, A., Asiri, A. M., Alvaro, M. & Garcia, H. Copper nanoparticles supported on doped graphenes as catalyst for the dehydrogenative coupling of silanes and alcohols. Angew. Chem. Int. Ed. 53, 12581–12586 (2014).

    CAS  Google Scholar 

  48. 48.

    Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  49. 49.

    Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    CAS  Article  ADS  Google Scholar 

  50. 50.

    Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).

    Article  ADS  Google Scholar 

  51. 51.

    Kresse, G. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).

    CAS  Article  ADS  Google Scholar 

  52. 52.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    CAS  Article  ADS  Google Scholar 

  53. 53.

    Steinmann, S. N. & Corminboeuf, C. Comprehensive benchmarking of a density-dependent dispersion correction. J. Chem. Theory Comput. 7, 3567–3577 (2011).

    CAS  Article  PubMed  Google Scholar 

Download references


Financial supports from the NSFC (91745106, 21633013, 21802147), National Key Research and Development Program of China (2017YFA0403103), the Youth Innovation Promotion Association of CAS (2019409), Key Research Program of Frontier Sciences of CAS (QYZDJ-SSW-SLH051), and Fujian Institute of Innovation of CAS are gratefully acknowledged.

Author information




F.S. designed and supervised the project. Y.W., H.W., X.W. and X.D. performed most of the experiments. T.W. performed the DFT computations. H.W., Y.W. and F.S. authored the manuscript.

Corresponding author

Correspondence to Feng Shi.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wu, Y., Wang, T., Wang, H. et al. Active catalyst construction for CO2 recycling via catalytic synthesis of N-doped carbon on supported Cu. Nat Commun 10, 2599 (2019).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing