Identification of active sites is one of the main obstacles to rational design of catalysts for diverse applications. Fundamental insight into the identification of the structure of active sites and structural contributions for catalytic performance are still lacking. Recently, X-ray absorption spectroscopy (XAS) and density functional theory (DFT) provide important tools to disclose the electronic, geometric and catalytic natures of active sites. Herein, we demonstrate the structural identification of Zn-N2 active sites with both experimental/theoretical X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectra. Further DFT calculations reveal that the oxygen species activation on Zn-N2 active sites is significantly enhanced, which can accelerate the reduction of oxygen with high selectivity, according well with the experimental results. This work highlights the identification and investigation of Zn-N2 active sites, providing a regular principle to obtain deep insight into the nature of catalysts for various catalytic applications.
Active sites are at the heart of catalysts, while the nature of active sites plays a key role in the performance of catalysts1,2,3,4,5,6. During the past decade, the active sites of transition metal–nitrogen–carbon (TMNC) catalysts have not been well identified and are simply defined as TM-Nx based on information from X-ray photoelectron spectroscopy (XPS)7,8,9,10,11. Such rough recognition of active sites leads to ambiguous understanding of the reaction mechanisms occurring on the surface of the catalysts, as well as stagnation of the development of rational catalyst design strategies. Recently, synchrotron radiation-based extended X-ray absorption fine structure (EXAFS) spectrum analysis, along with experimental characterization and theoretical simulation, has gradually been introduced to identify the geometric structures of active sites12,13,14,15. Despite this progress, however, the more structurally sensitive X-ray absorption near edge structure (XANES) spectrum analysis has been neglected. To obtain fundamental understanding of active sites and catalytic mechanisms, identifying the electronic and geometric structures of active sites with both XANES and EXAFS spectra is still highly desired.
Among various TMNC catalysts, zinc (Zn)-based materials, due to the low sublimation temperature, have been difficult to achieve and little progress has been made. After the removal of metallic Zn by sublimation, Zn-containing materials are frequently used as precursors to produce porous nitrogenated carbon for various electrochemical applications or Zn-free single atom catalysts12,15,16,17,18,19. However, none of these can maintain the presence of elemental Zn, not to mention the relevant active sites. Recently, single Zn atoms have been stabilized on carbon black (ZnNx/C), with Zn-N4 as the structure of the active sites20,21. However, the active sites have been investigated simply by EXAFS, without XANES spectrum analysis, making identification of active site structures and ensuing reaction mechanisms ambiguous and unreliable. It is still a great challenge to construct and identify Zn-based active sites, as well as to discern structural activation for catalytic applications.
Herein we demonstrate the synthesis and structural identification of Zn-based active sites, as well as the related structural activation for oxygen species. Combined EXAFS and XANES spectra analysis confirmed Zn-N2 as the structure of the active sites. First-principles density-functional theory (DFT) calculations reveal that the O-O bond stretching of adsorbed O2 (*O2) and OOH (*OOH) on Zn-N2 active sites are significantly enhanced. The high degree of O-O bond stretching can accelerate the highly selective four-electron reduction of adsorbed oxygen on the surface of Zn-N2 active sites, which agrees well with the experimental results.
Synthesis and structural characterization
Figure 1 shows typical structures of active sites of TMNC catalysts. With different coordination environments, the electronic and geometric structures of the active sites are largely different. Importantly, differences of the electronic and geometric structures can lead to diverse adsorption behaviours, which play key roles in the performance of catalysts. To begin with, Zn-based TMNC material (ZnNC) was prepared by thermal treatment of Zn-containing hybrid precursor in an argon atmosphere at 800 °C for 6 h (Supplementary Fig. 1). According to reported works, prolonged higher temperature pyrolysis can result in the vanish of Zn22.
The crystalline structure of ZnNC was investigated using high-power X-ray diffraction (HP-XRD) equipment (Supplementary Fig. 2). The two diffraction peaks of ZnNC at around 26° and 43° can be assigned to the (002) and (100) planes of graphitic carbon. No peaks of metallic Zn and Zn oxide were detected. The structural and chemical compositions of ZnNC were further studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) specific surface area analysis (Supplementary Figs. 3–5). The polyhedral building blocks in ZnNC exhibited an average size of 50 nm and consisted of C, N and Zn elements. Importantly, the element mapping images showed that the C, N and Zn elements are uniformly distributed in ZnNC. The high-resolution scanning transmission electron microscope (STEM) images further confirm the graphitic morphology of ZnNC, with an absence of metal or metal oxide nanoparticles for Zn element.
The XPS technique was further introduced to investigate the detailed chemical compositions of Zn and N species (Supplementary Fig. 6). The two peaks at binding energies of 1021.7 and 1044.8 eV in the high-resolution Zn 2p XPS spectrum belong to Zn 2p3/2 and Zn 2p1/2 of the Zn2+ species. The high-resolution N 1s XPS spectrum confirmed the presence of four different N species, including pyridinic N (398.5 eV), pyrrolic N (400.1 eV), graphitic N (401.0 eV) and oxidized N (404.6 eV)23. The atomic concentrations of the various N species are 2.28 at%, 0.26 at%, 2.34 at% and 0.39 at%, respectively. In relation to pyrrolic N, the content of pyridinic N is significantly higher, which can be attributed to the higher thermal stability of pyridinic N. Generally, uniformly distributed pyridinic N plays an important role in the active sites of TMNC materials, which can stabilize TM atoms in the NC matrix by formation of TM-N bonds.
Active site structure identification
Synchrotron radiation-based X-ray absorption spectroscopy, with high sensitivity to electronic and geometric structures, was adopted for identification of the structure of active sites. Figure 2a shows the K-edge XANES spectrum of ZnNC, with ZnPc and Zn foil as the references. The location of the absorption edge for ZnNC reveals that the oxidation state of the Zn atom is between 0 and + 2. The Fourier-transformed (FT) k3-weighted EXAFS spectrum of ZnNC exhibits a main peak at around 1.47 Å, corresponding to Zn-N coordination. The possibility of Zn-C coordination was excluded by the following XANES spectrum simulation (Supplementary Fig. 7). In contrast to the case of Zn foil, no peak belonging to Zn-Zn bond was detected at around 2.2 Å (Fig. 2b). Based on the position of the absorption edge, the Zn-N2 model structure was proposed as the geometric structure of the ZnNC active sites and was further used to fit the corresponding Fourier transform (FT) k3-weighted EXAFS spectrum in both R and k spaces (Supplementary Table 1). As shown in Fig. 2c, d, the FT k3-weighted EXAFS spectrum of ZnNC can be well fitted, suggesting Zn-N2 configuration as the active sites of ZnNC.
Compared with the EXAFS spectrum, the XANES spectrum is more sensitive and is thus essential for the identification of the structure of active sites. To confirm the structure of the active sites, XANES spectra were further simulated with typical structures of TMNC active sites (Fig. 3). Figure 3a shows the Zn K-edge XANES spectrum of ZnNC and the theoretical XANES spectrum based on the structure of the proposed Zn-N2 model. The calculated spectrum can reproduce identical features and matches well with the experimental results. Compared with the experimental spectrum, the calculated spectra for the structures of Zn-N1C3, Zn-N2C2, Zn-N3C1, Zn-N4 models and ZnO, which exhibit more positive absorption edges, are strikingly different. Although the theoretical spectrum for the structure of the Zn-N3 model shows an adsorption edge similar to that of the experimental spectrum, a corresponding strong feature at around 9677.3 eV interrupts this agreement. In the energy range of 9669–9677 eV, no obvious other models related intensity enhancing was observed in the experimental spectrum, revealing the high homogeneity of Zn-N2 model.
This result is consistent well with the optimized typical structures of Zn active sites (Supplementary Fig. 8). As shown, the configurations of Zn-N1C3, Zn-N2C2, Zn-N3C1, Zn-N3 and Zn-N4 are instable, in which the Zn atoms have struggled out of the nitrogenated carbon matrix planes. The exposed Zn atoms can be easily reduced into metallic Zn by the surrounded adjacent carbon species. Unlike other transition metals, such as Fe and Co, the formed metallic Zn can be further removed steadily via sublimation at high temperature. In this regard, Zn-N2 configuration on the edge sites of the nitrogenated carbon matrix planes exhibits the most stable configuration, which faces the minimum adjacent carbon species and has the most opportunity to survive at high temperature. The following atomic resolution STEM images in Fig. 4c, d further confirmed the sole edge site location of Zn single atoms at the nitrogenated carbon matrixes. No Zn-N1C3, Zn-N2C2, Zn-N3C1, Zn-N3 and Zn-N4 configuration-related location site for Zn single atoms was observed. At the meantime, the nitrogenated carbon matrixes are very small in size, which can provide abundant edge sites for the maximum coordinating of Zn single atoms.
Overall, combining EXAFS with XANES spectra, the structure of the active sites for ZnNC can be confirmed without ambiguity to be the Zn-N2 structure. Structural identification of the active sites is highly beneficial for the analysis of structural activation to determine catalytic behaviours on the surfaces of catalysts.
Theoretical study of the structural activation
Electrochemical reduction of O2 to H2O in aqueous medium via a robust four-electron pathway has been pursued for decades by TMNC catalysts. Active site structural activation for O-O bond stretching in *O2 and *OOH, and O2 adsorption plays an important role in the oxygen reduction process23,24,25.
To obtain fundamental insight into structural activation for oxygen species on Zn-N2 active sites, first-principles DFT calculations were conducted. The Pt(111) surface was also investigated as a reference (Supplementary Fig. 9). Figure 5a shows the optimized gaseous O2 molecule, which exhibits an O-O bond length of 1.21 Å. Figure 5b, c show the optimized configurations of O2 and OOH adsorbed on the Zn-N2 active site. Importantly, the bond lengths for *O2 and *OOH are 1.53 and 1.49 Å, respectively, which are 1.26 and 1.23 times that of the gaseous O2 molecule. The degree of O-O bond stretching of *O2 and *OOH on Zn-N2 active sites is also higher than that on Pt(111). With a higher degree of O-O bond stretching, much easier breaking of O-O bonds can be expected. The higher degree of O-O bond stretching can accelerate the rate of selective four-electron oxygen reduction and suppress the formation H2O2 via an inefficient two-electron pathway.
On the other hand, the O2 adsorption energies on Zn-N2 active sites and Pt(111) are –1.53 and –0.93 eV, respectively (Supplementary Table 2). The high O2 adsorption energy on the Zn-N2 active sites is more favoured by oxygen reduction, which can allow fast reactant supply for the subsequent reaction steps. Although the carbon atoms adjacent pyridinic N are also constantly considered as the active sites, the O2 adsorption energies on the carbon atoms are much lower, leading to a quite sluggish oxygen reduction pathway23. Meanwhile, the oxygen reduction is more efficient at an overpotential of 0.4 V (Supplementary Fig. 10).
According to the identified structure of active sites and the structural activation of oxygen species, we believe that Zn-N2 active sites incorporating ZnNC exhibit favourable catalytic behaviour for oxygen reduction.
Experimental evaluation on ORR catalytic activity
The catalytic behaviours of ZnNCs for oxygen reduction were further evaluated in an oxygen-saturated 0.1 M aq. KOH solution. The contents of Zn in ZnNC, ZnNC-M and ZnNC-L were around 4.03 wt%, 3.68 wt% and 2.81 wt%, respectively (Supplementary Figs 11 and 12). NC and Pt/C were compared under the same conditions (Supplementary Fig. 13). Figure 5e shows the potential dependence of the kinetic current density (Jk) on ZnNC with different Zn concentrations and Pt/C. Jk was calculated using the Koutecky–Levich equation. Without Zn active sites, NC exhibits poor catalytic activity in the potential range of 0.8–1.0 V vs. the reversible hydrogen electrode (RHE). Jk values at 0.85 V for ZnNC-L, ZnNC-M and ZnNC are –1.9, –4.5 and –7.9 mA cm–2, respectively, while that for Pt/C is around –4.3 mA cm–2. Compared with Pt/C, ZnNC exhibits much higher mass activity (Supplementary Fig. 14). Following the increasing Zn concentration, ZnNC demonstrates significantly enhanced catalytic activity towards oxygen reduction. Meanwhile, the decreasing Tafel slopes (81, 55 and 27 mV dec–1) confirm that the corresponding reaction kinetics also become much faster (Supplementary Fig. 15). With a smaller Tafel slope and a more positive half-wave potential (E1/2; 0.857 V), ZnNC exhibits catalytic activity superior to that of other decent catalysts for oxygen reduction reaction8,26,27,28,29,30,31,32 (Supplementary Table 3).
The selectivity of ZnNC was further detected by monitoring the H2O2 yield through rotating ring–disk electrode (RRDE) measurements (Supplementary Fig. 16). By applying a constant potential to the Pt ring, the H2O2 yield for ZnNC was revealed to be 1.35–2.93% in the potential range of 0.5–0.7 V, which was merely half of that for Pt/C (3.16–4.61%). According to the ring and disk current, the electron transfer number (n) of ZnNC was further calculated and found to be 3.97, confirming an efficient four-electron oxygen reduction pathway. The good stability of ZnNC was also demonstrated in the results of a methanol poisoning test and long-term cycling tests in oxygen-saturated 0.1 M aq. KOH solution (Supplementary Fig. 17).
The demonstrated high catalytic activity and selectivity of Zn-N2 active sites for electrochemical reduction of O2 agree well with the theoretical calculations based on the structural activation of *O2 and *OOH. On the other hand, owing to the stronger OH adsorption of Zn-N2 active sites, the theoretical onset potential would be smaller than that of Pt(111). The result is different from the relative performance of ZnNC and Pt/C and requires study in the future.
In summary, Zn-N2 active sites have been achieved and identified by both EXAFS and XANES spectra. Theoretical calculations reveal that the structural activation of oxygen species on Zn-N2 active sites is favoured by the selective oxygen reduction, which is confirmed by the experimental results. This work not only achieves the preparation and identification of Zn-N2 active sites but also provides a regular principle to obtain deep insight into the nature of catalysts for various catalytic applications.
Synthesis of ZnNC
As a typical synthesis, Zn(CH3COO)2 (2 mmol), 2-methylimidazole (8 mmol) and CNT (5 mg) were dissolved in methanol (80 ml). Each mixture was sonicated for 20 min. The above solutions were mixed quickly and aged at ambient conditions for 24 h. The resultant precipitates were collected and dried in an oven under reduced pressure. The collected precursor was annealed at 800 °C for 6 h in an argon atmosphere with a fast argon flow rate of 1.5 L min–1, denoted as ZnNC. Sample synthesized with 15-h thermal treatment was denoted as ZnNC-M. ZnNC etched with 5% HCl for 4 h was denoted as ZnNC-L. For the NC synthesis, trimesic acid (0.1 g) was mixed with dicyandiamide (1.0 g) and annealed under the same conditions as ZnNC.
A field-emission SEM (Nanonova 230, FEI, USA) was used to obtain the SEM images of the samples. A high-resolution TEM (JEM-2100F, JEOL, Japan) was used to get the TEM images of the samples. A high-power X-ray diffractometer (D/MAZX 2500 V/PC, Rigaku, Japan) was applied to obtain the XRD patterns. An X-ray photoelectron spectrometer (K-alpha, Thermo Fisher Scientific, UK) was introduced to conduct the XPS analysis. Nitrogen adsorption–desorption isotherms were used to analyse the specific surface area, using the BET method (BELSORP-max, BEL, Japan). XAFS test was conducted at Pohang Light Source (PLS-II) in Korea.
The catalytic performance was investigated on an electrochemical workstation (Ivium, Netherlands) with a typical three-electrode cell. The counter-electrode and reference electrode were graphite rod and Ag/AgCl (saturated KCl) electrodes, respectively. All the potentials were referenced vs. RHE. The commercial Pt/C was obtained from Alfa Aesar (platinum, nominally 20% on carbon Black HiSPEC 3000). Catalyst (4 mg) and Nafion solution (30 μL, Aldrich Chemical Inc.) were dispersed in 0.5 ml ethanol/isopropyl alcohol solution (1/3, v/v). Catalyst ink was obtained by ultrasonicating the solution for 30 min. Catalyst film for the electrochemical test was formed by dropping the ink (8.32 µL) onto RRDEs (4 mm in diameter). The loading amount of Pt/C and catalysts are 0.2 and 0.5 mg cm–2, respectively (Pt/C: 40 μgPt cm−2; ZnNC: 20 μgZn cm−2). Linear sweep voltammetry was conducted in 0.1 M aq. KOH solution (oxygen saturated). The scan rate and rotation speed were 5 mV s−1 and 1600 r.p.m., respectively. A constant potential of 0.3 V (vs. Ag/AgCl) was applied on the Pt ring. The percentage of HO2 and electron transfer number (n) were calculated by the disc, ring current and Pt ring collection efficiency. The kinetics current was calculated using Koutecky–Levich equation.
The Vienna Ab Initio Simulation Package (VASP) was used to conduct the DFT calculations, employing the Perdew–Burke–Ernzerhof-type gradient-corrected exchange-correlation potential. The cutoff energy for the plane-wave basis set was 630 eV. The ionic potentials were described by projector-augmented wave potentials. The atomic configurations were relaxed with residual forces <0.01 eV Å−1. The Zn K-edge XANES spectra calculations were carried on the optimized atomic structures of ZnNC active sites with the full-potential augmented plane wave+local orbitals method, considering core–hole correction.
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Behrens, M. et al. The active site of methanol synthesis over Cu/ZnO/Al2O3 industrial catalysts. Science 336, 893–897 (2012).
Guo, D. H. et al. Active sites of nitrogen-doped carbon materials for oxygen reduction reaction clarified using model catalysts. Science 351, 361–365 (2016).
Haag, W. O., Lago, R. M. & Weisz, P. B. The active-site of acidic aluminosilicate catalysts. Nature 309, 589–591 (1984).
Jaramillo, T. F. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007).
Norskov, J. K. et al. The nature of the active site in heterogeneous metal catalysis. Chem. Soc. Rev. 37, 2163–2171 (2008).
Shima, S. et al. The crystal structure of [Fe]-hydrogenase reveals the geometry of the active site. Science 321, 572–575 (2008).
Ahn, S. H., Yu, X. W. & Manthiram, A. “Wiring” Fe-Nx-embedded porous carbon framework onto 1D nanotubes for efficient oxygen reduction reaction in alkaline and acidic media. Adv. Mater. 29, 1606534 (2017).
Chen, P. Z. et al. Atomically dispersed iron-nitrogen species as electrocatalysts for bifunctional oxygen evolution and reduction reactions. Angew. Chem. Int. Ed. 56, 610–614 (2017).
Liang, H. W. et al. Molecular metal-Nx centres in porous carbon for electrocatalytic hydrogen evolution. Nat. Commun. 6, 7992 (2015).
Tang, C., Wang, B., Wang, H. F. & Zhang, Q. Defect engineering toward atomic Co-Nx-C in hierarchical graphene for rechargeable flexible solid Zn-Air batteries. Adv. Mater. 29, 1703185 (2017).
Wang, Q. et al. Phenylenediamine-based FeNx/C catalyst with high activity for oxygen reduction in acid medium and its active-site probing. J. Am. Chem. Soc. 136, 10882–10885 (2014).
Chen, Y. J. et al. Isolated single iron atoms anchored on N-doped porous carbon as an efficient electrocatalyst for the oxygen reduction reaction. Angew. Chem. Int. Ed. 56, 6937–6941 (2017).
Li, X. G. et al. Single-atom Pt as co-catalyst for enhanced photocatalytic H2 evolution. Adv. Mater. 28, 2427–2431 (2016).
Zhang, M. L. et al. Metal (hydr)oxides@polymer core-shell strategy to metal single-atom materials. J. Am. Chem. Soc. 139, 10976–10979 (2017).
Zhu, Y. Q. et al. A cocoon silk chemistry strategy to ultrathin N-doped carbon nanosheet with metal single-site catalysts. Nat. Commun. 9, 3861 (2018).
Aijaz, A., Fujiwara, N. & Xu, Q. From metal-organic framework to nitrogen-decorated nanoporous carbons: high CO2 uptake and efficient catalytic oxygen reduction. J. Am. Chem. Soc. 136, 6790–6793 (2014).
Asefa, T. Metal-free and noble metal-free heteroatom-doped nanostructured carbons as prospective sustainable electrocatalysts. Acc. Chem. Res. 49, 1873–1883 (2016).
Jiang, H. L. et al. From metal-organic framework to nanoporous carbon: toward a very high surface area and hydrogen uptake. J. Am. Chem. Soc. 133, 11854–11857 (2011).
Zheng, F. C., Yang, Y. & Chen, Q. W. High lithium anodic performance of highly nitrogen-doped porous carbon prepared from a metal-organic framework. Nat. Commun. 5, 5261 (2014).
Song, P. et al. Zn single atom catalyst for highly efficient oxygen reduction reaction. Adv. Funct. Mater. 27, 1700802 (2017).
Yang, F. et al. Highly efficient CO2 electroreduction on ZnN4-based single-atom catalyst. Angew. Chem. Int. Ed. 57, 12303–12307 (2018).
Yin, P. Q. et al. Single cobalt atoms with precise N-coordination as superior oxygen reduction reaction catalysts. Angew. Chem. Int. Ed. 55, 10800–10805 (2016).
Li, F. et al. Boosting oxygen reduction catalysis with abundant copper single atom active sites. Energy Environ. Sci. 11, 2263–2269 (2018).
Cao, R. et al. Promotion of oxygen reduction by a bio-inspired tethered iron phthalocyanine carbon nanotube-based catalyst. Nat. Commun. 4, 2076 (2013).
Gong, K. P., Du, F., Xia, Z. H., Durstock, M. & Dai, L. M. Nitrogen-doped carbon nanotube arrays with high electrocatalytic activity for oxygen reduction. Science 323, 760–764 (2009).
Cao, B. F. et al. Cobalt molybdenum oxynitrides: synthesis, structural characterization, and catalytic activity for the oxygen reduction reaction. Angew. Chem. Int. Ed. 52, 10753–10757 (2013).
Guan, B. Y., Yu, L. & Lou, X. W. A dual-metal-organic-framework derived electrocatalyst for oxygen reduction. Energy Environ. Sci. 9, 3092–3096 (2016).
Liang, Y. Y. et al. Co3O4 nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. Nat. Mater. 10, 780–786 (2011).
Lin, L., Zhu, Q. & Xu, A. W. Noble-metal-free Fe-N/C catalyst for highly efficient oxygen reduction reaction under both alkaline and acidic conditions. J. Am. Chem. Soc. 136, 11027–11033 (2014).
Mao, S., Wen, Z. H., Huang, T. Z., Hou, Y. & Chen, J. H. High-performance bi-functional electrocatalysts of 3D crumpled graphene-cobalt oxide nanohybrids for oxygen reduction and evolution reactions. Energy Environ. Sci. 7, 609–616 (2014).
Strickland, K. et al. Highly active oxygen reduction non-platinum group metal electrocatalyst without direct metal-nitrogen coordination. Nat. Commun. 6, 7343 (2015).
Wu, Z. Y. et al. Iron carbide nanoparticles encapsulated in mesoporous Fe-N-doped carbon nanofibers for efficient electrocatalysis. Angew. Chem. Int. Ed. 54, 8179–8183 (2015).
This work was supported by the Creative Research Initiative (CRI, 2014R1A3A2069102), the Science Research Center (SRC, 2016R1A5A1009405) and the BK21 Plus (10Z20130011057) program through the National Research Foundation (NRF) of Korea, National Natural Science Foundation of China (21706132) and Natural Science Foundation of Jiangsu Province (BK20160834).
The authors declare no competing interests.
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Li, F., Bu, Y., Han, GF. et al. Identifying the structure of Zn-N2 active sites and structural activation. Nat Commun 10, 2623 (2019). https://doi.org/10.1038/s41467-019-10622-1
This article is cited by
Nano Research (2022)
Engineering unsymmetrically coordinated Cu-S1N3 single atom sites with enhanced oxygen reduction activity
Nature Communications (2020)