Studying defect formation and evolution in MethylAmmonium lead Iodide (MAPbI3) perovskite layers has a bottleneck in the softness of the matter and in its consequent sensitivity to external solicitations. Here we report that, in a polycrystalline MAPbI3 layer, Pb-related defects aggregate into nanoclusters preferentially at the triple grain boundaries as unveiled by Transmission Electron Microscopy (TEM) analyses at low total electron dose. Pb-clusters are killer against MAPbI3 integrity since they progressively feed up the hosting matrix. This progression is limited by the concomitant but slower transformation of the MAPbI3 core to fragmented and interconnected nano-grains of 6H-PbI2 that are structurally linked to the mother grain as in strain-relaxed heteroepitaxial coupling. The phenomenon occurs more frequently under TEM degradation whilst air degradation is more prone to leave uncorrelated -oriented 2H-PbI2 grains as statistically found by X-Ray Diffraction. This path is kinetically costlier but thermodynamically favoured and is easily activated by catalytic species.
There is a general consensus in referring to organic–inorganic hybrid perovskites, with particular focus on MAPbI3, as soft matter. The degrees of freedom of the organic cations inside the inorganic Pb–I cage and their bonding to the anions create a crystal-liquid duality1,2 that makes the lattice dynamically rearranging at the local scale during short lapses of time. The structure is indeed measured as average response of the material. Implications of this dynamic disorder have been already envisaged on the carrier transport3, on the self-healing of lattice defects4 and on order-disorder lattice transition with temperature1,5.
Similarly related to the dynamic nature of the ionic interaction, lattice instability rises substantial concerns on the material reliability for long-lasting operation6.
In the MAPbI3 lattice, the attitude of the methylammonium cations (MA+) to dynamically interact with external agents (species, electric fields and light)7 reduces the perovskite durability with augmented vulnerability at the tetragonal to cubic phase transition8. Although the lattice engineering of different kinds of perovskite has been producing significant improvements by mixing cations and anions of different nature9,10,11, the pioneering MAPbI3 is still deserving top records in Photovoltaics and is indeed worthy of further effort12,13.
In reasoning about MAPbI3 stabilising solutions, the focus has been going with progressively more strength towards the preservation of the grain surfaces via treatments14,15, extra-molecules or additives16,17,18,19,20,21,22. Grain shells are sites for lattice instability and dynamic generation of defects. Nitrogen, largely used as inert species in the experimental setup8,11,12,23,24,25, has been recently demonstrated to have a beneficial role in assisting a temperature-induced recovery of intrinsic MAPbI3 lattice disorder at the grain shell and in stabilising under-coordinated cations (Pb2+, MA+) through van der Waals interactions26.
A thorough knowledge of the local defect formation and evolution inside a MAPbI3 matrix was for a long time limited by the material damage caused by the use of high-dose electron beams as probe. They can create artefacts or provide misleading information. Most of the literature was conscious of that and a long silence was covering new insights. The first light was shed by Rothmann et al.27 that used a very low electron dose rate (~1 e−/Å2s) for transmission electron microscopy (TEM) analyses. In that paper, for the first time, the transition from tetragonal to cubic lattice arrangement in thin polycrystalline MAPbI3 layers was investigated with interesting insights drawn on the existence of reversible twinned domains. Very recently, a second paper has been published based on TEM analyses28, providing a detailed description of single-crystal MAPbI3 degradation to PbI2 via I−- and MA+-related defects formation and volatile species release.
The applicability of polycrystalline MAPbI3 layers to technology indeed demands special care on the transformation at the grain boundaries (GBs) and at all the exposed surfaces in respect to the volume, since defects formation and their further evolution pilot the whole perovskite to a progressive and irreversible transition to PbI2. The kind of defects, their location and evolution, their eventual passivation, their optical behaviour are topics of increasing interest.
Starting from the pioneering papers on TEM, in our paper we afford the issue of surface defect formation in polycrystalline MAPbI3 films by in situ TEM investigation at low total electron dose unveiling breakthroughs on: a clustering phenomenon of Pb-based defects at the MAPbI3 grain surfaces; their motion without bias and their progressive enlargement during time at the expenses of MAPbI3 GBs; the antagonistic formation of PbI2 and its structural coupling with the MAPbI3 mother grain that produces a textured nano-fragmentation as in a relaxed heteroepitaxy. The described phenomena are similarly observed in thin and thick samples (40–150 nm), with clustering more pronounced in samples with high surface to volume ratio.
As a bridge towards degradation under ambient conditions, we feature similar investigations on identical samples exposed to humid air to draw a general paradigm on the role of defects formation and evolution, and on the convenience of PbI2 to arrange along 2H or 6H stacking during MAPbI3 degradation.
Thirdly, a lighting up phenomenon of Pb-clustering that is blocked by PbI2 formation is disclosed and paves the way to frame advanced stabilisation actions that can inhibit formation of defects at the GBs.
Degradation by Pb-clustering
A set of 40-nm thick perovskite layers was deposited at 70 °C by sequential sublimation of PbI2 and methylammonium iodide (MAI) directly on a Cu carbon-coated grid. The thickness was chosen to enhance the response under low total electron dose condition. Immediately after deposition, the Cu carbon-coated grid was loaded into the vacuum chamber of the TEM and analysed. To set up the proper acquisition conditions, we moved from the protocol developed by Rothmann et al.27 that defines proper electron dose rate and energy needed to preserve, at least for short-acquisition times, the initial structure of the material. To keep low the total energy dose per frame, we set up the acquisition time at 200 kV as low as 4 s in the 40-nm thick layer at dose rate of ~1 e−/Å2s. We further implemented the protocol by on purpose switching off the beam between two consecutive acquisitions in order to reduce material–beam interactions during time. Thereby, frames were acquired for 4 s each, along 1500 s of net exposure (excluding the time with the beam off). Our first intent is understanding the roles of e-beam and vacuum since the early stages of interaction.
Figure 1 shows a collection of images acquired during time. The first image represents the sample in fresh conditions. The layer is made of grains reciprocally matching along the GBs with diameter in the range 50–200 nm. Despite of the low deposition temperature used (70 °C), no pin-holes were found on the surface. The same was achieved on FTO/TiO2 substrates. The surface of the grains is smooth and uniform. Some grains are dark as a result of highly scattering crystallographic planes, in Bragg conditions with respect to the e-beam. Those planes specifically identify the tetragonal phase of MAPbI3 without any PbI2 contribution, as will be focused by the further discussion of data. Average compositional inhomogeneities are excluded on the basis of diffraction and chemical analyses.
During subsequent acquisition, the boundaries between adjacent grains (GBs) are being progressively modified. A net change is detected after 12 s from the sample loading. The circled regions in Fig. 1b–d highlights, in fact, small and dark grains located at the (preferentially triple) GBs that grow during time. While growing, they move along the GBs leaving behind empty spaces (holes) that are white in the image. The final size of clusters is in the diameter range 10–15 nm. The process is sketched in Fig. 1f. The nano-grains at the GBs are Pb-clusters as testified by the EDX spectra acquired in scanning mode and shown in Fig. 1e (light blue profile). Although the beam size is comparable with the Pb-cluster size, contributions from the surrounding matrix cannot be fully avoided. This indeed produces a small iodine peak in the profile. The reference spectrum is instead taken far from the GBs inside the grain (red curve) and has indeed intense I-related peaks. Quantification of the Pb–I ratio into the grain is beyond the scope of this analysis and would require specific protocol. EDX was instead on purpose used to certify the initially unknown composition of the clusters formed at the interfaces. Pb-clusters are not observed in fresh non-irradiated samples left under vacuum per days and then quickly irradiated for image acquisition for 4 s.
The increasing size of the Pb-clusters and the formation of holes at the GBs during time in a starting compact layer imply that MAPbI3 is feeding the process and that, in concomitance, volatile species, containing iodine, are formed29. Although high reactivity between iodine and lead species at equilibrium in bulk conditions is expected, the observed iodine release and Pb clustering are, on the contrary, surface phenomena. In addition, vacuum conditions unbalance the local equilibrium towards the progressive volatilisation of species that leaves Pb atoms to easily aggregate on the surfaces. The preferential location of the Pb-clusters at the (triple) GBs reinforces the pivotal role of the surface and a reduced barrier for the overall process.
An extreme case is shown in Fig. 1g, taken by leaving, after analyses, the sample for two days under vacuum with the e-beam off. The image was taken in a fresh area of the sample. We believe that the oversize of some clusters in the image is initially triggered by electron exposure (even at low dose, low magnification) and supplied by long-lasting pumping in vacuum. It is, in fact, expected that vacuum speeds up the kinetics of the process11, and indeed our protocol included to switch the e-beam off among two acquisitions. Above the specific conditions that trigger Pb-defects formation (water, light, etc.), they are expected to aggregate with similar dynamics as under vacuum, thus preferring GBs for the high-lattice disorder26,30, and with similar effects on the MAPbI3 integrity. As a matter of fact, similar structural dynamics were previously observed for MAPbI3 degradation under vacuum and air conditions using X-rays as probe for analyses31,32. Nonetheless, Pb-nanoclusters do not necessarily leave a measurable trace of them in conventional diagnostics (e.g., X-ray diffraction (XRD)) due to their small size and large dispersion.
Degradation by nano-fragmentation
It has been observed that the progression of the MAPbI3 to Pb goes to saturation after ~120 s from loading, producing Pb-cluster with size of a few nanometres (10–15 nm). They do not notably evolve during time. This transformation path is limited by a concomitant but slower second transition mechanism. This second stage is described in Fig. 2.
After ~100 seconds from loading, the grains’ core starts radically changing its structure. The changes are gradual during time with final state reached after ~850 s. The plan-view TEM image shown in Fig. 2a, taken in the same region as the images in Fig. 1, is well representative of the final state of this second stage of transformation. In the image, the grains, whose boundaries are not still changed from their starting configuration (see Fig. 1), are inside fragmented in small nano-grains (schematic in Fig. 2b) that creates roughening at the surface (further discussion in the next sections). On the contrary, the peripherical Pb-clusters, still located at the GBs, have size and position mostly unmodified as mapped in Fig. 1 at t = 120 s. Their further evolution was indeed blocked by the transformation of the whole grains.
To describe the changes occurring inside the grains during time, Fig. 2c–f show a sequence of electron diffraction patterns (EDPs) taken during time in the area of the sample shown in Fig. 2a. The starting arrangement of the lattice is provided in Fig. 2c wherein specific rings of the tetragonal phase (the two most intense labelled with the blue arrows) are easily associated to planes of the (110/001) family. The main planes of this family are represented in the schematic of Fig. 2b, together with the associated plane spacing: 0.627 and 0.314 nm for the (110)/(002) and the (220)/(004) planes, respectively. PbI2 is fully absent in the starting pattern. During relatively short laps of time, we observe a progressive transfer of intensity from the original perovskite spots at position d = 0.314 nm towards a close contribution from PbI2 at d = 0.317 nm. See Fig. 2d as representative of the phenomenon after 100 s of beam exposure (25th frame). The transition causes the (220/004) perovskite ring to get shaded contours (Fig. 2d). It is to notice that the consequent outbreak of doublets involves each perovskite contribution, as visible in Fig. 2e and as further elucidated through Fig. 3. It is additionally noteworthy that the transition leaves unchanged the direction of the Q vector in the reciprocal space (i.e., the ED). The final PbI2 has the 6H33,34 lattice symmetry, univocally identified by the brilliant contributions at d = 0.317 nm, as shown in Fig. 2f. Correspondently, the vanishing of the internal specific ring of the MAPbI3 (110/002: d = 0.314 nm) traces a final full conversion within 850 s. A transition to 6H-PbI2 (R-3m) was similarly observed by Chen et al.28 on single-crystal MAPbI3 samples. The authors describe this phase change as occurring through an intermediate transition characterised by I species leaving the perovskite lattice with consequent formation of superstructures (I- and subsequently MA-deficient). The marking features for this transient transformation to PbI2 were not observed on our 40-nm thick layer. Instead, the coincidence of the final state in our polycrystalline layers and in single crystals28 denotes a similar transition path of the MAPbI3 core. Besides core transition, polycrystalline layers, that are better suited for applications, demand special care on the transformation at the GBs and surfaces that is the main focus of our investigation.
In this respect, we found that the transition of the grain core to 6H-PbI2 has blocked further visible evolution of the Pb nano-clusters formed during the first stage from loading. We thus argue that the transition from MAPbI3 to Pb is in competition with the one from MAPbI3 to PbI2. Both of them occur with release of mass. We additionally unveil that PbI2 and Pb-clusters can share a boundary (plan-view image in Fig. 2a) without necessarily interacting or merging or further evolving into a unique phase.
We spent further effort in studying the origin of the preferential phase transition of the grain core to 6H-PbI2. We start reconsidering in more details the MAPbI3–PbI2 doublet alignments, as those shown in the large area ED in Fig. 3a and taken after 200 s of beam exposure (some doublets are circled in white and light blue). We notice that main MAPbI3 spots in the large area diffraction can be framed by squares (light blue) that are concentric with similar slightly inner squares of PbI2 (dark yellow), with corners and half-edges occupied by doublets. Each inner square univocally identifies the −441/841/−481 zone axis (crystallographic directions) of the 6H-PbI2 since it is not expected in other polymorphisms. The identification of this zone axis as belonging to 6H-PbI2 is pivotal for data interpretation: misleading conclusions can arise by the incorrect attribution of the diffraction spots therein to MAPbI3 that instead has planes at 0.314 nm and not at 0.317 nm. By discrete rotation of this coupled squares, the whole patterns can be represented. This implies that all the MAPbI3 grains inside the analysed area of the sample change in similar 6H-PbI2 grains. A difference is introduced by the initial rotational degree of freedom of the MAPbI3 grains along the growth axis perpendicular to the sample surface.
The local EDPs taken on a MAPbI3 grain before transformation (Fig. 3b) and on the corresponding PbI2 grain after transition (Fig. 3d), locally reveal how (004/220) planes of the perovskite transform into (0–14/−114) planes of the by-product though the whole core. Those planes are aligned during transition as encountered in heteroepitaxial growths35,36,37,38. During transition, the single spots are smeared due to the nano-fragmentation of the matrix. This induces a broadening of the intensity distribution for size effects. Structure simulations in Fig. 3c, e show the atomic distribution and the relationship between atoms along the experimental zone axis and highlight a noteworthy similarity between MAPbI3 and 6H-PbI2. Moving from one phase to the other implies just a little change in the atomic configuration as shown in Fig. 3g, h. Note, in particular, the octahedron alignment in the two structures with respect to what occurs in the 2H lattice (Fig. 3f). It is indeed intuitive that 6H formation is kinetically favoured.
Dark-field (DF) images were acquired during time selecting diagnostic diffraction spots. Figure 4 shows the staring (a) and the end (b) states in a sampled area that are representative of the whole sample behaviour. The circled area in the inset of the figure indicates the size of the objective aperture used for DF. The structural alignment of the two materials (doublet) allowed collecting information on the starting and end-states in the same sampled area by keeping fixed the slit position in the EDP. To read the image, bright areas in DF have the selected (inside the slit area) crystallographic planes in Bragg condition with respect to the beam. On this basis, we identify a starting large uniform grain of MAPbI3 with random contours. After full transition to PbI2, (~820 s), that is signed by the disappearance of the inner ring of perovskite at d = 0.627 nm, the grains break into nano-aggregates of 6H-PbI2. This results in a dotted black and white contrast at the nano-scale due to the fragmentation of the starting unique MAPbI3 platform into slightly misaligned aggregates (slight zone axis tilt). This morphological transition is represented in the schematic of Fig. 4c. The preserved alignment of the PbI2 planes to those of the starting mother MAPbI3, occurring inside a window of tolerability within the zone axis spread, is often encountered after strain relaxation in heteroepitaxial growths35.
Degradation under air condition and its relation with TEM degradation
A cross-link to the in-air degradation pathway was done through a focused experiment. To this purpose, a MAPbI3 layer grown on a Cu-grid in the same deposition run as done for the sample TEM-degraded, was left in ambient air condition at 50–60% RH. After 5 days in air the sample colour fully tuned to yellow, providing a feedback of the occurred transition to PbI2. Then, it was loaded into the TEM chamber and analysed under low-dose condition. Figure 5 compares the end-states reached through the two degradation paths. Both end states correspond to pure PbI2. Figure 5a shows grains structurally fragmented, as discussed in Fig. 4, whose contours are invariant with respect to the starting perovskite grains. As a difference, the sample aged in air (Fig. 5b) has a layered architecture of  oriented sliced grains (c-axis oriented). This path is likely piloted by the presence of ambient water molecules that have a high capability to infiltrate the initial perovskite grains and to act as catalysts on the production of volatile species11,25,26,31. The in-air degradation is slower than in TEM degradation to allow water infiltration and release processes11.
It has produced, among the allowed polymorphisms, the one indicated in the literature as the most stable at room temperature39,40, namely the 2H (http://rruff.geo.arizona.edu/AMS/amcsd.php)41. The identification of the layered sequence of atoms in the sliced grains as following the P-3m1 (2H) arrangement is feasible on the basis of the selected area EDP in Fig. 5c. It was taken on a grain of the transformed material, as that shown in Fig. 5b, but is representative of most of the grain structure.
The EDP has a peculiarity that distinguishes this from the 6H polytype pattern. The peculiarity resides in the internal spots at plane distance of 0.395 nm. They are not expected in the 6H polymorphism (http://rruff.geo.arizona.edu/AMS/amcsd.php). The same planes could be found in 4H and 6R lattices, but with less intensity (2–3%Imax). Their dominance was statistically excluded on the basis of the large area XRD data that will be discussed in the next section. Moreover, 4H and 6R polytypes have twinned octahedron sequence around the c-axis, quite dissimilarly to what occurs in the MAPbI3 lattice.
Although in the sample aged in air most of the grains are sliced along the (001) planes of the 2H structure that are parallel to the substrate, some other grains were less frequently found with the same zone axis as encountered during degradation at the TEM. To disentangle about this concomitance, large area XRD patterns were acquired and analysed to provide larger statistics on the lattice arrangement of the degradation products. To this purpose, different samples were prepared on glass substrates for large area X-ray analysis (1 cm × 1 cm) and measured after full degradation under ambient air plus eventual heating in the range 30–120 °C. Temperature was used to accelerate the degradation path8,26. The summarising scenario is shown in Fig. 6a–d. For a better figure readabiity, we clarify that the XRD patterns were taken in symmetric configuration and this implies that the peaks therein must be associated to planes lying parallel to the sample surface (Fig. 6b). We found that most of the samples exhibited a degradation path towards 2H-PbI2, as shown in Fig. 6a by the intense peak at 2θ = 12.67° and in agreement with the results in Fig. 5b, c. The result is independent of the temperature applied for degradation, indeed we do not discriminate the samples on the basis of their history but rather on the basis of their final state. We called this path A. We point out that, even though the peak at 2θ = 12.67° can be exhibited by other polymorphisms, the cross correlation with the TEM pattern (Figs. 5c and 6e, inner hexagon) allows a discrimination in favour of the 2H arrangement of the Pb–I octahedra (moreover, 2H is the most stable at RT). By Fig. 6a we further draw that inclusions of 6H-PbI2 can be formed, as testified by the small peak detected at 2θ = 28.23° ((104)-type planes, see figure 4c). This peak is not present in the 2H-PbI2 pattern (see simulations in Fig. 6e). In some other MAPbI3 samples, less statistically encountered, a predominance of the 6H polytype over the 2H can be found as shown in Fig. 6c. This countertrend is represented by the major relative intensity of the (104) peak of the 6H-PbI2 over the (002) peak of the 2H polymorphism. This degradation path was called B. It is interesting to notice the unusual shape of this diagnostic peak centred at 2θ = 28.23°: it is broad at the basis as expected for a mixture of polymorphisms (that could include the 4H) that share a common architecture in stacking rather than in separated grains. 6H inclusions in the frame of a 2H matrix is shown in Fig. 6d inside an in-air-degraded sample. 6H inclusions can be recognised by the peculiar texture, according to Figs. 2 and 4, as further confirmed by specific selected area diffraction as the one shown in Fig. 3d (squared diffraction). Figure 6e shows instead the selected area EDP of a 2H-PbI2 grain with its peculiar double-hexagonal arrangement of spots (real and simulated). This pattern is easily distinguishable from a similar 6H-PbI2 hexagonal configuration wherein instead the inner hexagon at d = 3.95 angstrom is missed (Fig. 6e, right panel).
We summarise that, under air condition and whatever the temperature used, the most convenient path for degradation of pure MAPbI3 is towards the 2H polymorphism of PbI2. In the large statistics, 6H-PbI2 grains can be found with lower probability.
Degradation in thick layers
To more closely meet technological requrements, 150-nm thick layers of MAPbI3 were grown on Cu C-coated grids simply by scaling up the deposit time. Scaling up the thickness is also used to frame the transition mechanisms in a more general paradigm. Due to the thickness, the acquisition time for TEM and ED was extended to 8 s/frame to improve the image quality. The total dose of electrons was low enough to not induce damage or artefacts at least in the first acquisition frames, as clearly stated in ref. 42. Similarly to what found in the thin layer, the fresh thick sample is free from visible Pb clusters. It is made of large well-matching grains in the range of diameter 200–500 nm. In this sample, the surface/volume ratio is reduced compared to the 40-nm thick sample wherein the grain diameter is instead in the range 50–200 nm. Pb-clustering and hole formation at the GBs and surfaces is observed during the initial transformation step. Data are shown in Fig. 7b after an exposure time of 40 s (total dose = 40 e−/A2). The phenomenon of Pb-clustering in thick MAPbI3 layers deposited by solution processing was preliminarily reported in our previous publication. Figure 7c shows, in addition, a phenomenon of neighbouring hole merging at the GBs during electron exposure as similarly observed in ref. 42 on MAPbI3 layers deposited over Cu-grids by solution processing. In the statistics, hole merging can locally produce a detaching along a row of grains as shown in Fig. 7d, e. The similarity in the grain detaching over different deposition techniques sheds light on the phenomenon being uncorrelated with the specific growth method. Instead, differences in thickness, grain size, surface grain curvature or the presence of eventual contamination from the preparation procedure could introduce differences from sample to sample. Figure 7e and its EDP in the inset additionally highlight a transformation of the MAPbI3 grains towards PbI2 through the formation of doublets similarly to what found in thin layers. A full transition is recorded, in that area of the sample, after ~1400 s of electron exposure (total dose ~1400 e−/Å2).
Similarly to what observed in the thin layers, Pb clustering and hole formation are the fastest processes that compete with the slower transformation of the grain core to PbI2. Likely triggered at the surfaces, the transition proceeds with time to entirely transform the volume. The time to complete the transition, that was estimated in ~850 s for the 40-nm thick layer, is expanded by a factor ∼2 in the 150-nm thick MAPbI3 layer. Discrepancies of the degradation time from scaling with thickness could be related to the electron mean free path affecting the energy transferred to the material/unit volume. In addition, thickness related relaxation of strain could impact on the transformation dynamics and therefore further effort is needed to disclose the detail of the core transition. Above this further refinement, the two-step degradation pathway is a general paradigm.
We draw the paradigm on a two-step transformation pathway of MAPbI3 layers : Pb-clustering and phase transition to PbI2. The paradigm is validated in the range of thickness from 40 to 150 nm but it could be further extended up to 300 nm.
The full description is provided by time-resolved experiments done at the TEM under mild (1 e−/A2 s and short-acquisition time) and intermitting e-beam conditions in order to limit the effect of the electron dose and exposure on the material structure.
Pb-clustering is a surface phenomenon that can occur in evaporated as well as in solution deposited layers under external perturbation. It arises from aggregation of Pb-related defects left at the boundary of MAPbI3 grains after volatile species release as occurs in any kind of dissociation process. Perturbation of equilibrium can be triggered by electron irradiation, even at low dose, in conjunction with morphological inhomogeneities (e.g., grain curvature, triple GBs, and thinned boundaries) and/or local stoichiometric inhomogeneities. High-grain curvature and/or small grain size, promoting Pb atomic diffusion and aggregation, can even lead to oversize clustering, in thin layers. The description of progressive MAPbI3 consumption, preferentially at the GBs, by Pb aggregation also frames the detaching phenomenon observed in our work and in the literature42.
The effect of the Pb-clustering on the grain surfaces is dramatic in progressively feeding on the hosting matrix. It can occur with similar consequences under any other kind of external perturbation that creates volatile species and defects or an atomic gradient, i.e., under action of environmental species, electric field, light and temperature. Pb-clusters migration without any applied electric field addresses a catalytic action of the clusters in collecting lead atoms from the disordered MAPbI3 boundaries. Pb aggregation could even occur in a complete device architecture as boundaries are created with the ETL and HTL layers. Ionic migration under operation, unbalancing the local atomic equilibrium, could similarly and indirectly promote Pb-aggregation.
Pb-clustering is limited by the concomitant but slower transformation of the core of the MAPbI3 grains to PbI2. This implies that Pb/PbI2 is more stable than Pb/MAPbI3 interfaces. Phase transition of the MAPbI3 grain core to PbI2 is a time-dependent process that deserves further focused investigation. It was here explored by in situ (TEM) and ex situ experiments (XRD). MAPbI3 core progressively converts into 6H-PbI2 in the TEM-transformed sample; 2H-PbI2 is instead generated under air conditions. 6H-PbI2 has a higher structural affinity to MAPbI3 and this allows transforming one structure to the other by small atomic adjustments (plus MA–I release), similarly to what occurs in heteroepitaxial couplings. The process results in a fragmentation of each original perovskite grain into an array of PbI2 nano-domains sharing a common zone axis (i.e., same planes parallel to the grain surface). We can, indeed, argue that this transition is kinetically favoured. The transition to 2H is instead costlier and thus needs to be activated by catalytic species such as water molecules. In the statistics, nevertheless, 6H inclusions into a 2H-dominant matrix can be even found after degradation under air conditions. In the light of those findings, a convenience in piloting a partial transition of MAPbI3 towards the 6H polymorphism is drawn based on their allowed lattice coupling that addresses the use of a thin conformal coverage of 6H-PbI2 to protect the surface of each perovskite grain. On the opposite, degradation to 2H-PbI2 produces sliced domains not structurally connected to the MAPbI3 mother grain, thus excluding the possibility of a conformal coverage.
Controlled surface passivation by 6H-PbI2 could be explored to preserve the grain core and/or mitigate dynamic disorder at the grain surfaces. This would additionally limit Pb-defects clustering at the periphery of the grains.
Finally, the extended timescale for degradation by scaling-up the layer thickness of the MAPbI3 layer reinforces the role of the surface to volume ratio and suggests the total electron dose (e−/cm2) normalised to the grain thickness as a more comprehensive parameter to merge data from different laboratories in a unique benchmark curve for degradation.
Perovskite layer growth
MAPbI3 layers were grown on a Cu carbon-covered grid by sequential deposition of PbI2 and MAI via physical sublimation from powders43 at a base pressure of ~2 × 10−2 mbar with the crucibles taken at 350 °C and 150 °C, respectively. The procedure allowed avoiding solvent use and skipping any sample preparation for TEM analyses that would modify the structure of the material, with special regards to the preservation of the organic components. A first set of samples was 40-nm thick. A second batch of 150-nm thick layers was grown on Cu-grids simply by prolonging the deposition time and used to frame the role of the surfaces in samples that can be applied to devices. Although we were forced to double the acquisition time during TEM analyses and indeed the total e-dose per frame to allow reliable imaging, the overall description of the sample modification was consistent to what observed in the thin layers such to draw a unique paradigm for the material evolution during time. In both layers (40 and 150 nm thick) no evidence of average stoichiometric discrepancy from the MAPbI3 composition is found by diffraction and chemical analyses. Large area samples were similarly grown on glass substrates (20 samples) to allow statistical evaluations on the phase transition under air conditions by XRD analyses
Transmission electron microscopy
TEM analyses were done in plan-view using a JEOL JEM 2010F microscope operating at 200 kV. The illumination parameters were chosen in order to reduce the dose rate to ~1 e−/Å2 s. Exposure time per frame acquired were 4 and 8 s for the 40- and 150-nm thick layers, respectively. In most cases, frames were sequentially acquired (as the ones in Fig. 1) for time-resolved experiments. In specific experiments, the beam was, on purpose, interrupted between two consecutive images (beam intermittence) such to explore eventual phenomena triggered by the beam exposure further evolving after the beam in switched off. Electron Diffraction pattern (EDPs) series were also acquired with the same protocol.
Scanning transmission electron microscopy images were acquired at 200 kV in scanning mode using a high-angle annular dark field detector in Z-contrast configuration
XRD patterns were collected by using a D8Discoved (Bruker AXS) diffractometer equipped with a high precision goniometer (0.0001Å), a thin film attachment (long soller slits) and a Cu-K α source (instrumental broadening 0.07°). Probed area = 0.2 cm2.
The data that support the findings of this study are available from the corresponding author upon request.
Deretzis, I. et al. Spontaneous bidirectional ordering of CH3NH3PbI3 in lead iodide perovskites at room temperature: The origins of the tetragonal phase. Sci. Rep. 6, 24443 (2016).
Miyata, K., Atallah, T. L. & Zhu, X.-Y. Lead halide perovskites: crystal-liquid duality, phonon glass electron crystals, and large polaron formation. Sci. Adv. 3, e1701469 (2017).
Huang, H. Ferroelectric photovoltaics. Nat. Photon. 4, 134–135 (2010).
Ceratti, D. R. et al. Self-healing inside APbBr3 halide perovskite crystals. Adv. Mater. 30, 1706273 (2018).
Deretzis, I. & La Magna, A. Exploring the orthorhombic–tetragonal phase transition in CH 3 NH 3 PbI 3: the role of atom kinetics. Nanoscale 9, 5896–5903 (2017).
Rong, Y. et al. Challenges for commercializing perovskite solar cells. Science 361, 1214 (2018).
Deretzis, I. et al. Stability and degradation in hybrid perovskites: is the glass half-empty or half-full? J. Phys. Chem. Lett. 9, 3000–3007 (2018).
Alberti, A. et al. Revealing a discontinuity in the degradation behaviour of CH3NH3PbI3 during thermal operation. J. Phys. Chem. C 121, 13577–13585 (2017).
Singh, T. & Miyasaka, T. Stabilizing the efficiency beyond 20% with a mixed cation perovskite solar cell fabricated in ambient air under controlled humidity. Adv. Energy Mater. 8, 1700677 (2018).
Saliba, M. et al. Cesium-containing triple cation perovskite solar cells: improved stability, reproducibility and high efficiency. Energy Environ. Sci. 9, 1989–1997 (2016).
Smecca, E. et al. Stability of solution-processed MAPbI3 and FAPbI3 layers. Phys. Chem. Chem. Phys. 18, 13413–13422 (2016).
Holzhey, P. et al., Materials Today https://doi.org/10.1016/j.mattod.2018.10.017 (2018).
Kogo, A., Sanehira, Y., Numata, Y., Ikegami., M. & Miyasaka, T. Amorphous metal oxide blocking layers for highly efficient low-temperature brookite TiO2‐based perovskite solar cells. ACS Appl. Mater. Interfaces 10, 2224–2229 (2018).
Meggiolaro, D. et al. Iodine chemistry determines the defect tolerance of lead-halide perovskite. Energy Environ. Sci. 11, 702 (2018).
Brenes, R. et al. Metal halide perovskite polycrystalline films exhibiting properties of single. Cryst. Joule 1, 155–167 (2017).
Yang, S. et al. Functionalization of perovskite thin films with moisture-tolerant molecules. Nat. Energy 1, 15016 (2016).
Bi, D. et al. High‐performance perovskite solar cells with enhanced environmental stability based on amphiphile‐modified CH3NH3PbI3. Adv. Mater. 28, 2910–2915 (2016).
Huang, G., Wang, C., Zhang, H., Xu, S. & Xu, Q. Healing of defects: an alternative way for passivation of carbon-based mesoscopic perovskite solar cells via hydrophobic ligand coordination. J. Mater. Chem. A 6, 2449–2455 (2018).
Masi, S. et al. Organic gelators as growth control agents for stable and reproducible hybrid perovskite‐based solar cells. Adv. Energy Mater. 7, 1602600 (2017).
Masi, S. et al. Multiscale morphology design of hybrid halide perovskites through a polymeric template. Nanoscale 7, 18956–18963 (2015).
Lu, J. et al. Interfacial benzenethiol modification facilitates charge transfer and improves stability of cm-sized metal halide perovskite solar cells with up to 20% efficiency. Energy Environ. Sci. 11, 1880–1889 (2018).
Jung, M., Shin, T. J., Seo, J., Kim, G. & Seok, S. I. Structural features and their functions in surfactant-armoured methylammonium lead iodide perovskites for highly efficient and stable solar cells. Energy Environ. Sci. 11, 2188 (2018).
Nickel, N. H., Lang, F., Brus, V. V., Shargaieva, O. & Rappich, J. Unraveling the light-induced degradation mechanisms of CH 3 NH 3 PbI 3 perovskite films. Adv. Electron. Mater. 3, 1700158 (2017).
Christians, J. A. et al. Tailored interfaces of unencapsulated perovskite solar cells for >1,000 h operational stability. Nat. Energy 3, 68–74 (2018).
Mannino, G. et al. First evidence of CH3NH3PbI3 optical constant improvement in N2 environment at 40-80°C.Journal. J. Phys. Chem. C 121, 7703–7710 (2017).
Alberti, A. et al. Nitrogen soaking promotes lattice recovery in polycrystalline hybrid perovskites. Adv. Energy Mater. 9, 1803450 (2019).
Rothmann, M. U. et al. Direct observation of intrinsic twin domains in tetragonal CH3NH3PbI3. Nat. Commun. 8, 14547 (2017).
Chen, S. et al. Atomic scale insights into structure instability and decomposition pathway of methylammonium lead iodide perovskite Nature. Nat. Commun. 9, 4807 (2018).
Ciccioli, A. & Latini, A. Thermodynamics and the intrinsic stability of lead halide perovskites CH3NH3PbX3. J. Phys. Chem. Lett. 9, 3756–3765 (2018).
Uratani, H. & Yamashita, K. Charge carrier trapping at surface defects of perovskite solar cell absorbers: a first-principles study. J. Phys. Chem. Lett. 8, 742–746 (2017).
Alberti, A. et al. Similar structural dynamics for the degradation of CH3NH3PbI3 in air and in vacuum. ChemPhysChem 16, 3064–3071 (2015).
Deretzis, I. et al. Atomistic origins of CH3NH3PbI3 degradation to PbI2 in vacuum. Appl. Phy. Lett. 106, 131904 (2015).
Chaudhary, S. K. Lead iodide crystals as input material for radiation detectors. Cryst. Struct. Theory Appl. 1, 21–24 (2012).
Zheng, Z. et al. In situ growth of epitaxial lead iodide films composed of hexagonal single crystals. Mater. Chem. 15, 4555–4559 (2015).
Alberti, A. & La Magna, A. Role of the early stages of Ni-Si interaction on the structural properties of the reaction products. J. Appl. Phys. 114, 164–168 (2013).
Alberti, A., Bongiorno, C., Rimini, E. & Grimaldi, M. G. Critical nickel thickness to form silicide transrotational structures on  silicon. Appl. Phys. Lett. 89, 102105 (2006).
Alberti, A. et al. Low temperature formation and evolution of a 10 nm amorphous Ni–Si layer on  silicon studied by in situ transmission electron microscopy. J. Appl. Phys. 105, 093506 (2009).
Alberti, A. et al. Structural characterization of Ni2Si pseudoepitaxial transrotational structures on  Si. Acta Crystallogr. Sect. B Struct. Sci. 62, 729–736 (2006).
Palosz, B., Steurer, W. & Schulz, H. The structure of PbI, polytypes 2 and 4H: a study of the 2H-4H transition. J. Phys. Condens. Matter 2, 5285–5295 (1990).
Minagawa, T. Common polytypes at low and high temperatures and the 2H-12R transformation. Acta Cryst. A 31, 823 (1975).
Beckmann, P. A. A review of polytypism in lead iodide. Cryst. Res. Technol. 45, 455–460 (2010).
Rothmann, M. U. et al. Structural and chemical changes to CH3NH3PbI3 induced by electron and gallium ion beams. Adv. Mater. 30, 1800629 (2018).
Liu, M., Johnston, M. B. & Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition letter to. Nature 501, 395–398 (2013).
This activity was partially supported by the national project BEYOND NANO Upgrade (CUP G66J17000350007). We want to also acknowledge the bilateral project founded by CNR (Italy) and JSPS (Japan) for supporting the activity on PSC for the years 2018–2019 (CUP B56C18001070005).
The authors declare no competing interests.
Journal peer review information: Nature Communications thanks Mathias Uller Rothmann and Antonio Abate for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Alberti, A., Bongiorno, C., Smecca, E. et al. Pb clustering and PbI2 nanofragmentation during methylammonium lead iodide perovskite degradation. Nat Commun 10, 2196 (2019). https://doi.org/10.1038/s41467-019-09909-0
Frontiers in Chemistry (2020)
Advanced Functional Materials (2020)
The Journal of Physical Chemistry Letters (2020)
The Journal of Physical Chemistry Letters (2020)
General Decomposition Pathway of Organic–Inorganic Hybrid Perovskites through an Intermediate Superstructure and its Suppression Mechanism
Advanced Materials (2020)