Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Direct conversion of CO and H2O into liquid fuels under mild conditions


Although enormous progress has been made in C1 chemistry and CO2 conversion in recent years, it is still a challenge to develop new carbon resource transformation protocols especially those lead to the production of liquid fuels with high selectivity under mild conditions (e.g., under low temperature and using benign solvent). Herein, we present a novel and energy-efficient catalytic route to directly transform CO and H2O to liquid fuels (i.e., liquid hydrocarbons) at low temperature (≤200 °C) in aqueous phase (i.e., in a benign solvent), in which H2O served as both hydrogen source and solvent for the liquid fuel production. The key to the catalytic process is the construction of a highly efficient tandem catalyst Pt-Mo2C/C + Ru/C, which can directly convert CO and H2O in aqueous phase to liquid hydrocarbons with a production rate of 8.7 mol-CH2- molRu−1 h−1 and selectivity up to 68.4% of C5+ hydrocarbons at 200 °C.


Conversion of CO2 into value-added chemicals or fuels offers a promising alternative to reduce anthropogenic emissions of CO2, providing an attractive strategy for carbon recycling. However, it is still a challenge to obtain liquid fuels via direct conversion of CO2 due to the high thermodynamic stability of CO2 and coupling barrier of C–C bonds. CO, as a key intermediate in CO2 conversion, has attracted extensive attention during past decades. It has been demonstrated recently that direct conversion of CO2 to CO with nearly 100% selectivity via solar-driven photocatalytic or electro-reduction processes1,2,3. Furthermore, CO2 splitting to CO production (2CO2 = 2CO + O2) via plasma technologies has attracted considerable attention, especially in industry4. Hence, these new technologies could potentially provide abundant source of CO (from CO2) for large-scale CO utilizations in industry. Moreover, large amount of industrial flue gases with CO as main component have been generated from converter gas, blast furnace gas, and electric furnace gas in the iron and steel industry every day, in which the hydrogen content is extremely low (<5%). Some of the gases contain around 70% CO or more by volume. Unfortunately, most of these gases were used for direct burning as fuels, and part of them were even emitted directly into the atmosphere. As a matter of fact, the transformation of CO has always been regarded a core process in current C1 chemical industry5,6,7. Tremendous research efforts have been devoted to the conversion of syngas (i.e., a mixture of CO and H2) to designated products with high selectivity in the past decades8,9,10,11,12,13,14,15,16. Two well-known reactions, i.e., water-gas-shift (WGS)17 and Fischer-Tropsch synthesis (FTS)7, play a crucial role for the transformation of CO in coal or natural-gas based industry and ammonia synthesis industry18. In the WGS reaction, CO is combined with H2O (steam) to produce H2 and CO2. In the FTS reaction, CO is combined with H2 to produce liquid hydrocarbons, which is a promising technology to replace the petroleum-based processes due to rapid growth of energy demand and the high oil price19,20. Although the coal-to-liquid (CTL) technology has been industrially used in different countries, the process remains cost-intensive as it needs a multi-step process to get a suitable H2/CO ratio (~2) required for the FTS reaction. New catalytic systems have been reported, aiming at using coal-based syngas with low H2/CO ratio. For example, Bao et al.12 reported that olefins could be produced from syngas with H2/CO ratio equal or lower than one over a tandem catalyst of Zn–Cr and SAPO-34 at high temperature (400 °C). However, hydrogen gas is usually required for the CO conversion through the conventional FT reaction. Hence, direct transformation of CO without addition of hydrogen gas becomes one urgent demand for the COx resource utilization. Meanwhile, water has been used as a cheap and environmentally friendly solvent in industrial chemical processes, which may facilitate the WGS reactions under mild conditions. If we can develop a reaction process that can directly convert CO and H2O into liquid fuels, it will be a key advance for the COx resource utilization.

$${\mathrm{CO}} + {\mathrm{H}}_{\mathrm{2}}{\mathrm{O}} \to {\mathrm{fuels}} + {\mathrm{CO}}_2$$

Aiming to achieve this goal, we report here an energy-efficient catalytic route to directly convert CO and H2O into liquid fuels at low temperatures (≤200 °C) in aqueous phase, in which H2O served as both hydrogen source and solvent. Obviously, H2 is needed for the efficient transformation of CO via FTS. For FTS reactions with low H2/CO ratios (for example, 0.7), water has sometimes been added into the feed to promote water gas shift reaction and thus to get a high H2/CO ratio required for FTS21. In our previous work22,23,24, we demonstrated that FTS reactions could be achieved in aqueous phase by Ru- or Co-based nanoparticle catalysts at low temperatures (<200 °C. Note that in this process, H2O was used as a solvent only for FTS, and we can call them aqueous-phase FTS processes (APFTS). However, there is no report yet about the reaction between CO and water to produce liquid fuels. It will be interesting to see if H2O can serve as a hydrogen provider (without adding extra H2 gas) to react with CO for producing liquid hydrocarbons.

Indeed, H2 gas could be generated from H2O through WGS. However, the WGS reactions normally occur in gas phase. Thus, to successfully design a chemical process for direct conversion of CO and H2O to liquid hydrocarbons, we will need (i) high performance of the WGS catalytic system that can work in aqueous-phase, and (ii) efficient coupling of WGS and FTS reactions in aqueous phase. The whole chemical process with reaction thermodynamics can be illustrated as the followings:

$${\mathrm{CO}} + {\mathrm{H}}_{\mathrm{2}}{\mathrm{O}} \to {\mathrm{H}}_2 + {\mathrm{CO}}_2\quad \quad {\mathrm{WGS}}$$
$$\Delta H^\theta = - 41\,{\mathrm{kJ}}\,{\mathrm{mol}}^{ - 1},\quad \Delta G^\theta = - 28\,{\mathrm{kJ}}\,{\mathrm{mol}}^{ - 1}$$
$${\mathrm{CO}} + {\mathrm{2H}}_2 \to {\mathrm{H}}_{\mathrm{2}}{\mathrm{O}} + \left( { - {\mathrm{CH}}_2 - } \right)\quad \quad {\mathrm{FTS}}$$
$$\Delta H^\theta < -\!\! 200\,{\mathrm{kJ}}\,{\mathrm{mol}}^{ - 1},\quad \Delta G^\theta < -\!\! 142\,{\mathrm{kJ}}\,{\mathrm{mol}}^{ - 1}$$
$${\mathrm{3CO}} + {\mathrm{H}}_{\mathrm{2}}{\mathrm{O}} \to {\mathrm{2CO}}_2 + \left( { - {\mathrm{CH}}_2 - } \right)$$
$$\Delta H^\theta {\mathrm{ < }} -\!\! 282\,{\mathrm{kJ}}\,{\mathrm{mol}}^{ - 1},\quad \Delta G^\theta {\mathrm{ < }} -\!\! 198\,{\mathrm{kJ}}\,{\mathrm{mol}}^{ - 1}$$

Clearly, the combined process of WGS and FTS (Eq. 4) in aqueous phase, termed as aqueous-phase CO to liquid (APCOTL), is thermodynamically feasible. However, from the kinetics point of view, the mismatch of the WGS and FTS reaction rates in the APCOTL process may lead to unsuccessful coupling of those two reactions and thus failure to produce liquid hydrocarbons. For instance, if the hydrogen production rate is too slow, there will be no driving force for the CO conversion to hydrocarbon25. Therefore, proper matching of the two reaction rates is the key for the successful design of APCOTL processes.

Thus, we designed a tandem catalyst Pt-Mo2C/C + Ru/C (i.e., a simple mixture of Pt-Mo2C/C and Ru/C), which has proper matching of the reaction rates between WGS and FTS reactions in aqueous-phase. The designed catalytic system exhibited superior activity for direct conversion of CO and H2O to liquid hydrocarbons with high selectivity. The reaction temperature was 200 °C, much lower than that of conventional FTS and WGS processes. To the best of our knowledge, this is the first report of direct conversion of CO and H2O to liquid hydrocarbons.



The Pt-Mo2C/C catalyst was prepared through impregnation followed by a modified temperature-programmed reduction (TPR) method. The Ru/C catalyst was obtained through the conventional impregnation method. The tandem Pt-Mo2C/C + Ru/C catalyst was prepared by mixing Pt-Mo2C/C with Ru/C. For comparison, an integrated catalyst PtRu-Mo2C/C (i.e., the Pt, Ru, and Mo alloy supported on carbon) was prepared by co-impregnating Ru, Pt, Mo precursors over active carbon before the TPR treatment.

Catalytic performance

In order to test whether the synthesized catalysts have APCOTL activity, we evaluated the catalysts in aqueous phase with pure CO as a gas-phase feed (3.0 MPa CO) at 150 °C. It was reported that molybdenum carbide supported noble metal catalysts were very active for WGS26,27. As H2O could be effectively activated on molybdenum carbide at a relatively low temperature, the WGS reaction could achieve higher reactivity than those in previous reports28 even below 150 °C. Indeed, we found that using the Pt-Mo2C/C catalyst for CO in water, the only products were H2 and CO2 without any hydrocarbons (Table 1, entry 1 and 2). The WGS rate by Pt-Mo2C/C was 55.3 molCO2 molPt−1 h−1 at 150 °C and increased to 77.3 molCO2 molPt−1 h−1 at 200 °C, indicating this WGS catalyst was not only active in gas-phase, but also active in aqueous-phase. With the syngas (CO + H2) (3.0 MPa syngas, Table 1, entry 3) in aqueous phase, no hydrocarbons were detected for the Pt-Mo2C/C catalyst. The absence of hydrocarbons in the product suggested that the Pt-Mo2C/C catalyst was not able to transform the produced H2 and CO into liquid hydrocarbons. Obviously, the Pt-Mo2C/C catalyst was active for WGS, but not active for the APFTS reaction. We evaluated the activity of Ru/C with the syngas CO and H2 in aqueous phase (Table 1, entry 4). As expected, Ru/C showed good activity for hydrocarbon formation, indicating that it is a good catalyst for FTS in aqueous phase. Interestingly, the WGS rate by Pt-Mo2C/C (Table 1, entry 2) was about 8 times higher than that of FTS by Ru/C, with 1:2 CO/H2 as the feed (Table 1, entry 4).

Table 1 Catalytic performance of aqueous-phase CO conversion with different catalysts

To design an effective APCOTL process, our first thought was to integrate all the active catalytic components (i.e., Pt, Mo2C and Ru) into a single integrated catalyst, as usually composite catalysts showed good catalytic performance due to the alloying or interfacial effect29,30. Therefore, we prepared the RuPt-Mo2C/C (molar ratio of Ru/Pt = 2.5) alloy catalyst by co-impregnation methods. When RuPt-Mo2C/C was used in the reaction with pure CO as the feed in water (Table 1, entry 5), we did observe the formation of liquid hydrocarbons. It is expected that the formation of hydrocarbons is due to the FTS reaction by Ru, after the WGS process by Pt-Mo2C. Thus, we described the overall reaction rate for the hydrocarbon formation based on the amount of Ru. The production rate of hydrocarbons was 2.2 mol-CH2- molRu−1 h−1 by RuPt-Mo2C/C (Table 1, entry 5), with 46.7% selectivity towards C5+ hydrocarbons and 29.7% selectivity for the C2–4 hydrocarbons. Therefore, the integrated catalyst RuPt-Mo2C/C indeed converted CO and water into liquid fuels. This integrated catalyst has not been reported before. Moreover, the reaction was conducted at a relatively low reaction temperature 200 °C.

We soon noticed that the WGS rate by RuPt-Mo2C/C was 42.2 molCO2 molPt−1 h−1 at 200 °C, and was lower than that of Pt-Mo2C/C (77.3 molCO2 molPt−1 h−1). Meanwhile, the FTS activity of RuPt-Mo2C/C was lower than that of Ru/C (2.2 vs 9.1 mol-CH2- molRu−1 h−1). Perhaps, during the preparation of the integrated catalyst, mutual interactions between the Ru and Pt-Mo2C components reduced the efficiency of each component. Therefore, we simply mixed Pt-Mo2C/C and Ru/C to obtain a tandem catalyst Pt-Mo2C/C + Ru/C (molar ratio of Ru/Pt = 2.5), to eliminate the undesired alloying or interfacial effect introduced by integrated catalysts. We evaluated the APCOTL activity of the tandem catalyst. A typical GC spectrum of the liquid products by the tandem catalyst for CO in water (reaction temperature: 200 °C) is shown in Fig. 1. Clearly, the production of a series of hydrocarbons was resolved (from C4 to C30 hydrocarbons), and the formation of methane to C7 hydrocarbons was observed in the gas-phase products (see Supplementary Figure 1), the distribution of the hydrocarbon is well consistent with the ASF product distribution for typical FTS reaction (Supplementary Figure 2). The production rate of hydrocarbons was 8.7 mol-CH2- molRu−1 h−1 at 200 °C (Table 1, entry 6), about four times higher than that of RuPt-Mo2C/C. Moreover, it was comparable to the activity of Ru-based AFTS catalysts under syngas condition (Supplementary Table 1). Meanwhile, low selectivity for the undesired product methane was observed (11.4%). More importantly, the selectivity to C5+ hydrocarbons increased dramatically to 68.7%, suggesting the success of the simple mixing method. The concentration of CO and H2 monitored at different reaction time is also reported (Supplementary Figure 3).

Fig. 1

GC spectrum of the liquid products. The product was collected in the cyclohexane phase obtained on Pt-Mo2C/C + Ru/C catalysts for pure CO and H2O conversion at 200 °C. The labeled Cn on the graph represents an alkane with n C numbers, and Cn-O represents alcohol with corresponding carbon number. e.g., C5-O stands for pentanol

It should be noted that there was an optimum mixing ratio between Pt-Mo2C/C and Ru/C. When the molar ratio of Ru to Pt was higher or lower than 2.5, the activity for the hydrocarbon formation decreased (Supplementary Table 2). Based on these results, it can be concluded that WGS and FTS processes could be effectively coupled to produce liquid fuels using a tandem catalytic system of Pt-Mo2C/C and Ru/C. The balanced kinetic control (i.e., proper matching of the reaction rates between WGS and FTS reactions) is the key for the outstanding performance of the tandem catalyst. With the development of this direct APCOTL process, intensive capital and energy consumption can be reduced in current FTS technology. For example, the tandem catalyst Pt-Mo2C/C + Ru/C can possess excellent activity for the conversion of syngas with low H2/CO ratio, avoiding the use of separate WGS units.

Structural characterization

Why did the tandem catalyst Pt-Mo2C/C + Ru/C show better performance of hydrocarbon formation for the APCOTL process than the integrated catalyst RuPt-Mo2C/C? In the following, we will answer this question by analyzing catalytic structures and mechanisms. X-ray diffraction (XRD, see Fig. 2a) of Pt-Mo2C/C and RuPt-Mo2C/C showed that the crystal phase of molybdenum carbide was pure β-Mo2C (hexagonal compact phase). For Pt-Mo2C/C, the weak diffraction peaks associated with Pt crystallites indicated the high dispersion of small-size Pt nanoparticles. Moreover, Pt-Mo2C/C exhibited excellent stability even under hot aqueous environment as it maintained its crystal structure after being treated in aqueous phase at 250 °C for 2 h under a CO atmosphere (see Supplementary Figure 4). For Ru/C, the broad and weak peaks at 43o and 25o were assigned to Ru crystallites and active carbon, respectively, indicating that Ru nanoparticles with small particle size were highly dispersed over carbon. Fourier transformed X-ray adsorption fine structure spectrum (EXAFS) at Pt L3-edge of Pt-Mo2C/C fitted with Pt-Pt and Pt-Mo coordination shell (see Fig. 2b and Supplementary Table 3) implied that the average coordination number of Pt-Pt shell was 6.3 ± 1.2, much smaller than that of bulk Pt (with coordination number of 12), indicating that small Pt nanoparticles were formed and well dispersed over Mo2C. The average coordination number of Pt-Mo shells was 2.6 ± 0.2, confirming strong interaction between Pt and Mo2C. The EXAFS spectrum at Pt L3-edge of RuPt-Mo2C/C catalyst (Fig. 2c) suggested possible formation of Pt-Ru alloys. Electronic characteristic of the catalyst surfaces was examined by the X-ray photoelectron spectroscopy (XPS), as shown in Fig. 2d. For Pt-Mo2C/C and RuPt-Mo2C/C, a Mo 3d5/2 signal associated with molybdenum carbide at 228.0 eV was detected, indicating the formation of molybdenum carbide. Ru/C showed a peak at 280.2 eV that was ascribed to metallic Ru, indicating that Ru was reduced under the synthetic conditions. For RuPt-Mo2C/C, the peak of metallic Ru was shifted to lower energies by 0.2 eV as compared to that of Ru/C, suggesting the electronic structure of Ru in RuPt-Mo2C/C was modulated either by Mo2C or Pt. On the other hand, the binding energies of Pt in Pt-Mo2C/C and RuPt-Mo2C/C were shifted to higher energies by 0.6 and 0.55 eV, respectively, compared to that of pure metallic Pt (71.2 eV). These shifts in binding energy of Pt implied the formation of electron deficient Pt species in Pt-Mo2C/C and RuPt-Mo2C/C, which could have a major impact on its reactivity26.

Fig. 2

XRD, EXAFS and XPS analyses of different catalysts. a XRD patterns of the different catalysts; b, c Pt L3-edge EXAFS profiles and fits of fresh catalysts: b for the Pt-Mo2C/C and c for the RuPt-Mo2C/C; d XPS spectra of different catalysts

The above results suggested that the chemical environment and electronic structure of Ru in RuPt-Mo2C/C catalyst was significantly modified by integrating with Pt and Mo2C, which may have led to the decreased performance of FTS. The structural details were further studied by high-angle annular dark-field scanning TEM (HAADF-STEM) and energy dispersive X-ray (EDX) analysis.

As shown in Fig. 3a and Supplementary Figure 5, for Ru/C, Ru nanoparticles with 1.5–2.0 nm in size were highly dispersed on the carbon support, consistent with the XRD result. For Pt-Mo2C/C, the HAADF-STEM image correlated with elemental mapping results clearly showed good dispersion of Pt nanoparticles with mainly 1–3 nm in size on the Mo2C particles (Fig. 3b, c and Supplementary Figure 6), consistent with the XRD and EXAFS results. For RuPt-Mo2C/C, the RuPt alloy nanoparticles with 3–7 nm in size were observed (see Fig. 3d, e and Supplementary Figure 7), consistent with the EXAFS observation. Combined with the EXAFS and XPS results, we deduced that the alloy structure of RuPt nanoparticles was in highly dispersed state on the surface of Mo2C in RuPt-Mo2C/C. This implied that for RuPt-Mo2C/C, the mutual interaction between metallic components changed the chemical environment and thus the electronic structure of Ru and Pt, leading to decreased WGS activity and thus decreased FTS activity compared to the tandem catalyst. In order to verify the influence of intermetallic interactions on the electronic structure, temperature-programmed desorption analysis of CO (CO-TPD) was employed on Ru/C, Pt-Mo2C/C and RuPt-Mo2C/C, respectively (see Supplementary Figure 8). The TPD profiles clearly indicated that the desorption temperature of CO on the integrated catalyst was nearly 20 °C higher than that of Pt-Mo2C/C and Ru/C, demonstrating a much stronger CO binding on the RuPt surfaces than the Ru surfaces. This could be an important reason for the decreased activity of RuPt-Mo2C/C for the coupled WGS and FTS processes. Comparing the catalytic performances of Pt-Mo2C/C + Ru/C and RuPt-Mo2C/C, we can conclude that the spatial arrangement of the two metallic components (i.e., Pt and Ru) is pivotal for the construction of APCOTL. Introduction of Ru at the atomic scale to form alloys with Pt can weaken the synergistic effect of the coupled WGS and FTS reactions, and thus modulate the overall reaction kinetics. Only by balanced kinetic control, optimal performance of the APCOTL reaction could be reached. We also tested the stability of the catalyst. Clearly, beside a drop in activity in the first round, the tandem catalyst is relatively stable (Supplementary Figure 9 and 10).

Fig. 3

Structure characterization of different catalysts. HAADF-STEM images of Ru/C (a), Pt-Mo2C/C (b, c) and RuPt-Mo2C/C catalysts (d, e, f), and corresponding EDX elemental mapping images of the Pt-Mo2C/C (c) and RuPt-Mo2C/C catalysts (f): C (red), Mo (yellow), Pt (blue) and Ru (orange); the particles in c and f corresponding to those in the red frame of b and e. The scale bars of a, b and d, e correspond to 20 nm, and the scale bars of c and f correspond to 2 nm


We developed a tandem catalytic system for direct conversion of CO and H2O into liquid hydrocarbons in aqueous phase (an APCOTL process) at a low temperature. By modulating the composition and structure of catalysts, high formation rate of liquid hydrocarbons (up to 8.7 mol-CH2- molRu−1 h−1) was obtained by the tandem catalyst Pt-Mo2C/C + Ru/C (molar ratio of Ru/Pt = 2.5) at 200 °C. More importantly, the selectivity for C5+ products as major components of liquid fuels could reach to nearly 70%. Meanwhile, the aqueous-phase CO conversion could reduce the energy consumption for fuel production. Our present work paves the way to establish efficient and sustainable chemical processes for the utilization of COx resources, shedding light on the design of heterogeneous bimetallic catalysts for hydrogen or fuel production in chemical industry.


Catalyst preparation

The Pt-Mo2C/C catalyst on active carbon was synthesized via incipient wetness impregnation. Briefly, an aqueous solution containing appropriate amount of ammonium paramolybdate (Sinopharm, (NH4)6Mo7O24·4H2O, 0.68 g) and chloroplatinic acid (Aldrich, H2PtCl6, 0.19 M, 2 mL) were mixed with the activated carbon (2 g) and then kept stirring for 12 h in the air at room temperature. The sample was then put into the vacuum freeze dryer overnight to remove water. The resulting precursor was exposed to hydrogen with the flow rate of 40 mL min−1, and heated to 400 °C at 10 °C min−1, holding at this temperature for 1 h, then to 700 °C at 1 °C min−1 and holding it for 3 h. Prior to exposure to air, the catalysts were treated in a flow of 0.5% O2/N2 overnight at room temperature. The RuPt-Mo2C/C catalyst was synthesized using the same procedure, except the adding of aqueous solution of ruthenium trichloride hydrate (Aldrich, RuCl3·xH2O, 0.19 M). Ru/C was prepared by impregnating processed carbon with RuCl3·xH2O solution, subsequent drying at 120 °C. Then the sample was transferred to a tubular furnace and reduced at 300 °C for 1 h with the H2 flow rate of 30 mL min−1. The loading of Ru was measured to be 4.1% by inductively coupled plasma atomic emission spectrometry (ICP).

Catalyst characterization

The detailed element content in the catalysts was determined by ICP using a PROFILE SPEC. All of the catalysts were dissolved by aqua regia at 100 °C for 12 h.

X-ray diffraction patterns were collected on a Rigaku D/MAX-PC 2500 powder X-ray diffractometer, using Cu Kα radiation with scanning angle (2Ѳ) from 20o to 70o. The accelerating voltage and current were 40 kV and 100 mA, respectively.

The phases of components were identified based on JCPDS standard cards. The X-ray photoelectron spectroscopy measurements were conducted on an Axis Ultra Imaging Photoelectron Spectrometer equipped with Al Ka (1486.7 eV) quartz monochrometer source. The freshly prepared catalysts were transferred to the measurement chamber without exposure to air. The binding energy was corrected by setting active carbon sp2 C 1s of 284.5 eV as the reference.

High-angle annular dark-field scanning TEM and EDX mapping measurements were carried out on a FEI Talos 200 A field-emission transmission electron microscope operating at 200 kV accelerating voltage using Cu TEM grids.

The XAFS spectra of Pt L3 edge (11564 eV) was collected at 1W1B beamline of Beijing Synchrotron Radiation Facility (BSRF). The beam was tuned by the Si (111) double-crystal monochromators. The energies were calibrated according to the absorption edge of pure Pt foil. All samples were pressed into solid pellets and sealed with Kapton film in the protection of N2 atmosphere before testing. The XAFS data were recorded under fluorescence mode by lytle detector. All collected spectra were processed and analyzed using Athena and Artemis program within the Ifeffit package31. For the X-ray absorption near edge structure analysis, the experimental absorption coefficients as the function of energies were processed by background subtraction and normalization procedure, and reported as “normalized intensity”. Pt foil and PtO2 bulk materials were used as the references. For the extended X-ray absorption fine structure analysis, Fourier transformed data in R space were analyzed by applying metallic Pt model for the Pt-Pt or Pt-Ru shell, respectively. The passive electron factors, S02, were determined by fitting the experimental data of Pt foil and fixing the Pt-Pt coordination number (CN) to be 12, and then fixed for further analysis of the measured samples. The parameters describing the electronic properties (e.g., correction to the photoelectron energy origin, E0) and local structure environment including CN, bond distance (R) and Debye Waller factor (σ2) around the absorbing atoms were allowed to vary during the fitting process. The fitted ranges for k and R spaces (k2 weighted) were k = 2.8−10.0 Å−1 and R = 1.6−3.2 Å.

CO-temperature-programmed desorption experiments were carried out in a fixed-bed reactor and detected by mass spectrometer (MS, AMETEK quadruple mass spectrometer). In total, 100 mg catalyst was reduced by H2 (30 ml min−1) at 300 °C for 1 h and then cooled down to room temperature in He flow. After exposure to CO for 30 min, the catalyst was switched to He exposure until the baseline of the CO signal leveled off. Finally, the temperature was increased to 400 °C at 10 °C min−1, and the mass signal of 28 was monitored.

Catalyst activity measurements

The reactions were carried out in a stainless steel autoclave (120 mL) typically at 200 °C and 3 MPa CO (the authoclave contains 4% Ar as the internal standard for online gas chromatography analysis) for 7 h. The catalysts were used without pretreatment. For each reaction, 0.20 g catalyst and 60 ml water were put into the reactor, and stirred at 800 r min−1. After each reaction, the gas-phase products were analyzed by Agilent 7820 A that was equipped with a thermal conductivity detector (TCD) and a flame ionization detector (FID). Porapark Q and 5 Å molecular sieves packed column were connected to TCD to detect the permanent gases including H2, CO2, CO, CH4 and Ar, while Al2O3 capillary column were connected to FID to analyze gaseous C1–C7 hydrocarbons. The liquid phase products were first extracted by 10 mL cyclohexane, followed by stirring at 150 °C for 1 h. The resulting solution was layered by the oil and water phase. The oil phase was qualitatively analyzed by GC-MS (Agilent 7890 A GC with HP-5 capillary column and 5975 MS) and quantified by GC (Agilent 7820 A, HP-5 capillary column) using decalin as an internal standard. Agilent 7820 A equipped with an INNOWAX capillary column was used to quantify the aqueous phase product. The FTS activity was calculated by adding all the hydrocarbon products in gas phase, water phase and oil phase. Since CO2 was resulted from the WGS reaction, the WGS activity was calculated in terms of the amount of CO2.

Data availability

The authors declare that the data supporting the findings of this study are available within the paper and its supplementary information files.


  1. 1.

    Yan, C. et al. Coordinatively unsaturated nickel–nitrogen sites towards selective and high-rate CO2 electroreduction. Energ. Environ. Sci. 11, 1204–1210 (2018).

    CAS  Article  Google Scholar 

  2. 2.

    Pan, Y. et al. Design of single-atom Co-N5 catalytic site: a robust electrocatalyst for CO2 reduction with nearly 100% CO selectivity and remarkable stability. J. Am. Chem. Soc. 140, 4218–4221 (2018).

    CAS  Article  Google Scholar 

  3. 3.

    Niu, K. et al. A spongy nickel-organic CO2 reduction photocatalyst for nearly 100% selective CO production. Sci. Adv. 3, e1700921 (2017).

    ADS  Article  Google Scholar 

  4. 4.

    Snoeckx, R. & Bogaerts, A. Plasma technology-a novel solution for CO2 conversion. Chem. Soc. Rev. 46, 5805–5863 (2017).

    CAS  Article  Google Scholar 

  5. 5.

    Tang, P., Zhu, Q., Wu, Z. & Ma, D. Methane activation: the past and future. Energy Environ. Sci. 7, 2580–2591 (2014).

    CAS  Article  Google Scholar 

  6. 6.

    Zhang, Q. H., Cheng, K., Kang, J. C., Deng, W. P. & Wang, Y. Fischer–Tropsch catalysts for the production of hydrocarbon fuels with high selectivity. ChemSusChem 7, 1251–1264 (2014).

    Google Scholar 

  7. 7.

    Khodakov, A. Y., Chu, W. & Fongarland, P. Advances in the development of novel cobalt Fischer-Tropsch catalysts for synthesis of long-chain hydrocarbons and clean fuels. Chem. Rev. 107, 1692–1744 (2007).

    CAS  Article  Google Scholar 

  8. 8.

    Zhai, P. et al. Highly tunable selectivity for syngas-derived alkenes over zinc and sodium-modulated Fe5C2 catalyst. Angew. Chem. Int. Ed. 55, 9902–9907 (2016).

    CAS  Article  Google Scholar 

  9. 9.

    Zhao, B. et al. Direct transformation of syngas to aromatics over Na-Zn-Fe5C2 and hierarchical HZSM-5 tandem catalysts. Chem 3, 323–333 (2017).

    CAS  Article  Google Scholar 

  10. 10.

    Galvis, H. M. T. et al. Supported iron nanoparticles as catalysts for sustainable production of lower olefins. Science 335, 835–838 (2012).

    ADS  Article  Google Scholar 

  11. 11.

    Prieto, G. et al. Design and synthesis of copper-cobalt catalysts for the selective conversion of synthesis gas to ethanol and higher alcohols. Angew. Chem. Int. Ed. 53, 6397–6401 (2014).

    CAS  Article  Google Scholar 

  12. 12.

    Jiao, F. et al. Selective conversion of syngas to light olefins. Science 351, 1065–1068 (2016).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Zhong, L. et al. Cobalt carbide nanoprisms for direct production of lower olefins from syngas. Nature 538, 84–87 (2016).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Kang, J. C. et al. Mesoporous zeolite-supported ruthenium nanoparticles as highly selective Fischer-Tropsch catalysts for the production of C5–C11 isoparaffins. Angew. Chem. Int. Ed. 50, 5200–5203 (2011).

    CAS  Article  Google Scholar 

  15. 15.

    Peng, X. et al. Impact of hydrogenolysis on the selectivity of the Fischer-Tropsch synthesis: diesel fuel production over mesoporous zeolite-Y-supported cobalt nanoparticles. Angew. Chem. Int. Ed. 54, 4553–4556 (2015).

    CAS  Article  Google Scholar 

  16. 16.

    Cheng, K. et al. Direct and highly selective conversion of synthesis gas into lower olefins: design of a bifunctional catalyst combining methanol synthesis and carbon-carbon coupling. Angew. Chem. Int. Ed. 55, 4725–4728 (2016).

    CAS  Article  Google Scholar 

  17. 17.

    Gokhale, A. A., Dumesic, J. A. & Mavrikakis, M. On the mechanism of low-temperature water gas shift reaction on copper. J. Am. Chem. Soc. 130, 1402–1414 (2007).

    Article  Google Scholar 

  18. 18.

    Galvis, H. M. T. & de Jong, K. P. Catalysts for production of lower olefins from synthesis gas: a review. ACS Catal. 3, 2130–2149 (2013).

    Article  Google Scholar 

  19. 19.

    Takeshita, T. & Yamaji, K. Important roles of Fischer–Tropsch synfuels in the global energy future. Energy Policy 36, 2773–2784 (2008).

    Article  Google Scholar 

  20. 20.

    Van de Loosdrecht, J. et al. Providing fundamental and applied insights into Fischer–Tropsch catalysis: Sasol–Eindhoven University of Technology Collaboration. ACS Catal. 6, 3840–3855 (2016).

    Article  Google Scholar 

  21. 21.

    Pendyala, V. R. R. et al. Fischer-Tropsch synthesis: attempt to tune FTS and WGS by alkali promoting of iron catalysts. Appl. Catal. A-Gen. 389, 131–139 (2010).

    Article  Google Scholar 

  22. 22.

    Xiao, C. X. et al. Aqueous-phase Fischer–Tropsch Synthesis with a Ruthenium nanocluster catalyst. Angew. Chem. Int. Ed. 120, 758–761 (2008).

    Article  Google Scholar 

  23. 23.

    Wang, H. et al. Platinum-modulated cobalt nanocatalysts for low-temperature aqueous-phase Fischer–Tropsch synthesis. J. Am. Chem. Soc. 135, 4149–4158 (2013).

    CAS  Article  Google Scholar 

  24. 24.

    Li, W. Z. et al. Chemical insights into the design and development of face-centered cubic ruthenium catalysts for Fischer-Tropsch synthesis. J. Am. Chem. Soc. 139, 2267–2276 (2017).

    CAS  Article  Google Scholar 

  25. 25.

    Ojeda, M. et al. CO activation pathways and the mechanism of Fischer–Tropsch synthesis. J. Catal. 272, 287–297 (2010).

    CAS  Article  Google Scholar 

  26. 26.

    Lin, L. et al. Low-temperature hydrogen production from water and methanol using Pt/alpha-MoC catalysts. Nature 544, 80–83 (2017).

    ADS  CAS  Article  Google Scholar 

  27. 27.

    Yao, S. Y. et al. Atomic-layered Au clusters on α-MoC as catalysts for the low-temperature water-gas shift reaction. Science 357, 389–393 (2017).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    Schweitzer, N. M. et al. High activity carbide supported catalysts for water gas shift. J. Am. Chem. Soc. 133, 2378–2381 (2011).

    CAS  Article  Google Scholar 

  29. 29.

    Fu, Q. et al. Interface-confined ferrous centers for catalytic oxidation. Science 328, 1141–1144 (2010).

    ADS  CAS  Article  Google Scholar 

  30. 30.

    Agarwal, N. et al. Aqueous Au-Pd colloids catalyze selective CH4 oxidation to CH3OH with O2 under mild conditions. Science 358, 223–227 (2017).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2005).

    CAS  Article  Google Scholar 

Download references


This work was financially supported by the National Key R&D Program of China (2017YFB0602200) and Natural Science Foundation of China (21725301, 91645115, 21821004, 21872104, 21673273, 21872163). The XAS experiments were conducted at the Beijing Synchrotron Radiation Facility (BSRF) and Shanghai Synchrotron Radiation Facility (SSRF).

Author information




D.M. designed the study. Y.X. and J.L. performed most of the reactions and sample characterization. W.L. synthesized part of the catalysts. W.L. and J.X. carried out the X-ray structure characterization and analysis. Y.L. and X.L. performed the electron-microscopy characterization. D.M., Y.X., Z.Y., and Y.C. wrote the paper. The other authors provided reagents, performed some of the experiments and revised the paper.

Corresponding authors

Correspondence to Zhen Yin, Yong Cao or Ding Ma.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal Peer Review Information: Nature Communications thanks Jairton Dupont, and other anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Xu, Y., Li, J., Li, W. et al. Direct conversion of CO and H2O into liquid fuels under mild conditions. Nat Commun 10, 1389 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing