Two-dimensional perovskites have emerged as more intrinsically stable materials for solar cells. Chemical tuning of spacer organic cations has attracted great interest due to their additional functionalities. However, how the chemical nature of the organic cations affects the properties of two-dimensional perovskites and devices is rarely reported. Here we demonstrate that the selection of spacer cations (i.e., selective fluorination of phenethylammonium) affects the film properties of two-dimensional perovskites, leading to different device performance of two-dimensional perovskite solar cells (average n = 4). Structural analysis reveals that different packing arrangements and orientational disorder of the spacer cations result in orientational degeneracy and different formation energies, largely explaining the difference in film properties. This work provides key missing information on how spacer cations exert influence on desirable electronic properties and device performance of two-dimensional perovskites via the weak and cooperative interactions of these cations in the crystal lattice.
Two-dimensional (2D) organic–inorganic hybrid perovskites (OIHPs), with a perspective of combining properties of both inorganic frameworks and versatile organics towards creating functional hybrid materials, have been studied since the 1980s1,2,3,4,5,6,7,8,9. The inorganic framework can empower the 2D OIHPs with desirable properties such as high charge carrier mobility along the sheet-like inorganic framework4, and the layered structure of such 2D OIHPs enables appreciable tunability in quantum confined properties (e.g., band gap, exciton binding energy) by varying the thickness of the inorganic layer10,11,12. As to the organics, a variety of conjugated molecule based ammoniums have been incorporated into 2D OIHPs, including oligothiophenes13, acenes14,15,16, and fullerenes17. Depending upon the energy levels and band gaps, these conjugated organics can contribute to light absorption and emission, and/or facilitate charge transfer between the organic and the inorganic framework13,14,15,16,18,19,20,21. Given the vast design space for both organic and inorganic frameworks, more “exotic” functions have also been envisioned with 2D OIHPs, including singlet fission, up conversion, among others8,13,18,22,23.
The lead halide-based 2D OIHPs, which have a general formula of (RNH3)2MAn–1PbnX3n+1, have attracted much attention as alternative photovoltaic materials because of their improved stability24,25,26,27,28,29,30,31,32. However, these 2D layered perovskites, having the insulating organic cations separating these inorganic slabs, tend to adopt an orientation where these inorganic slabs would be aligned in parallel to the substrate. This would significantly hinder the charge transport in the vertical direction and result in a lower efficiency9,28,32. However, 2D OIHP solar cells have recently been demonstrated with significant high efficiency via a couple of methods such as hot-casting28 and using additives25,31,33,34,35, due to presumably achieved vertical alignment of the inorganic slabs. Perhaps due to the easy accessibility of simple aliphatic ammoniums (e.g., butylammonium, C4H9-NH3+, BA), most 2D OIHP based solar cells of high efficiency have employed them as spacer cations25,28,31. However, these aliphatic ammoniums are electrically insulating and not light absorbing. Ideally, one would like to replace such aliphatic ammoniums with functional organics, for example, conjugated oligomers that would absorb a complementary portion of the solar spectrum to that of the inorganic framework. This improved light absorption could potentially increase the current of 2D OIHP based solar cells and further boost their efficiency. In fact, large conjugated oligomers (e.g., tetrathiophene, acenes) have been successfully incorporated into 2D OIHPs, yet only with the n = 1 phase8,13,16. For 2D OIHPs with n = 2–5, which are much more relevant to photovoltaic applications, we are not aware of any successful attempts incorporating large conjugated oligomers. Nevertheless, progress has been made with 2D OIHPs based on spacer cations with single aromatic rings, such as phenethylammonium (C6H5–CH2CH2–NH3+, PEA)24,27,33,36, 2-thiophenemethylammonium34, 3-bromobenzylammonium35, among others. Yet, most of these studies relied on special additives such as NH4SCN, MACl, etc. to achieve a high efficiency. Thus, chemical tuning of these spacer cations and its impact on the structure of 2D OIHPs as well as the device performance of related solar cells become an interesting yet under-explored direction.
Here we show that selectively monofluorinating PEA at different positions of the aromatic moiety (benzene in this case) can significantly affect the photovoltaic device efficiency of these 2D OIHPs (n = 4). Monofluorination of PEA is perhaps the smallest perturbation to the PEA-based spacer cations, which should not significantly change the molecule size or add additional optoelectronic functionalities. While we observe over 10% photovoltaic efficiency when 3-fluorophenethylammonium (mF1PEA) or 4-fluorophenethylammonium (pF1PEA) is used as the organic cation in 2D OIHP based solar cells, the efficiency of solar cells based on 2-fluorophenethylammonium (oF1PEA) is less than 1%. We find the observed difference in efficiency can be explained by considering three key properties of the 2D OIHP films: phase distribution, surface morphology and crystal orientation. To further understand how the organic cation would affect the structure of these 2D OIHPs, we analyze single crystals of 2D OIHPs (n = 1) with these fluorinated PEA cations and disclose that all crystals have a similar inorganic framework structure, yet very different organic cation packing arrangements. Specifically, the crystals with high orientational disorder of the organic cations yield poor device performance. Combined with density functional theory (DFT) calculations, we find the differences in formation energies of these compounds correlate well with variations in packing and disorder of the spacer cations. It appears that having a more favorable formation energy and less crystallographic disorder are beneficial for the device performance of these 2D OIHP based solar cells.
Photovoltaic device performance
We chose lead iodide based 2D OIHPs with a nominal n = 4 average composition (Fig. 1a) as the active layer for our solar cells with a p-i-n planar structure28,37. Four structurally-related large organic cations were employed to construct the 2D OIHPs: PEA, oF1PEA, mF1PEA, and pF1PEA (Fig. 1b, Supplementary Figure 1). Although these cations do not directly contribute to charge transport or light absorption by themselves38,39,40, they significantly influence the photovoltaic device performance. For example, we achieved an optimized efficiency of 7.67% with small hysteresis for devices with PEA (Fig. 1c, Supplementary Figure 2, 3 and Supplementary Table 1–3). This efficiency is comparable to or higher than literature values (for the cells fabricated without special processing conditions such as hot-casting or using additives)24,27 and consistent with our External Quantum Efficiency (EQE) measurement (Supplementary Figure 4 and Supplementary Note 1). When mF1PEA or pF1PEA were used instead of PEA, all key device characteristics—open circuit voltage (Voc), short circuit current (Jsc) and fill factor (FF)—were noticeably improved, resulting in higher efficiency values (over 10%) (Supplementary Figure 3 and Supplementary Table 1). However, if oF1PEA was employed, the photovoltaic device showed very poor efficiency values (less than 1%). We observed certain hysteresis in our 2D OIHP based solar cells (Supplementary Figure 2 and Supplementary Table 1), which could be ascribed to trap states or ion migration41,42,43,44,45. Nevertheless, all devices maintained consistent efficiency under constant illumination and at maximum power point (Fig. 1d).
Characterizations of 2D OIHP Films
We first characterized the absorption of each film to investigate the differences in light absorption and film composition, which could account for the observed difference in device performance. For each film, we observed several excitonic peaks (Fig. 2a), corresponding to a distribution of perovskite phases with different n. This observation indicates that there are multiple perovskite phases in these 2D OIHP films having a nominal n = 446,47,48,49. However, there are subtle differences when comparing these absorption spectra. For example, the absorbance of n = 1 phase in pF1PEA based 2D OIHP is weaker than the corresponding n = 1 phase in other 2D OIHPs in this series, while the 3D perovskite absorption in mF1PEA or pF1PEA based 2D OIHP was stronger than those in PEA and oF1PEA 2D OIHPs. These results indicate that the relative distribution of 2D phases having different n values in each film is different. Nevertheless, the overall light absorption of each film is similar in terms of the intensity and peak position, thus the light absorption cannot be the key reason to explain the large performance difference in photovoltaic devices.
We further conducted photoluminescence (PL) of each film from both back (glass) side and front (air) side as shown in Fig. 2b, c. For PEA, mF1PEA or pF1PEA based 2D OIHP, PL signals from 2D phases with different n values are clearly visible when excited from the substrate side (i.e., back side) (Fig. 2b). However, when excited from the air side (i.e., front side), signals from these 2D phases (n = 1, 2, 3, etc.) are much weaker, and the spectrum is essentially dominated by the PL from the 3D perovskite phase (Fig. 2c). We note that, when excited from the air side, the emission peaks for the 3D perovskite phases in our 2D OIHPs are slightly blue shifted when compared to the emission of normal 3D perovskites at 770 nm (Supplementary Figure 5). It may be caused by the slight twisting of the 3D crystal lattice (the twisted Pb-I-Pb angle) due to the presence of 2D phases which may impose a large internal strain in the formation of mixed perovskite films30,50. A blue shift of 3D phase was also observed previously when the ratio of PbI2 and MAI was changed, which may also occurs here51. However, when excited from the glass side, we observed much different emission peaks from 733 to 765 nm in the case of PEA, mF1PEA and pF1PEA 2D OIHP films (Fig. 2b). These emission peaks for “3D” perovskites are asymmetric and have significant blue-shifts due to the PL from 3D phase blended with the significant emission from large n phases. These observations indicate in PEA, mF1PEA, or pF1PEA based 2D OIHP films, a vertical phase distribution of multiple 2D OIHP phases occurs, where phases having smaller n values dominate on the glass side of the substrate while phases with larger n or 3D appear more on the air side. As suggested by others, this sequential phase distribution could benefit energy transfer (and/or charge transfer) across the film and lead to high device performance (Supplementary Figure 6a)37,46,47,48,49,52. However, for oF1PEA 2D OIHP, we only observed a strong and dominating emission peak from the 3D perovskite phase for both back side and the front side excitation (Fig. 2b, c), and these two emission spectra for oF1PEA 2D OIHP are almost identical. This suggests that the front side (i.e., air side) and back side (i.e., glass side) of the oF1PEA OIHP film are similar in terms of composition—both contain a significant amount of 3D perovskite phases, with 2D phases randomly mixed within. This scenario, i.e., a random phase distribution, would allow the 2D phases in the oF1PEA OIHP film to efficiently transfer their energy to large n phases and eventually to 3D phases. However, this random phase distribution in the oF1PEA 2D OIHP film would also result in charge trapping at the small band gap phases (schematically shown in Supplementary Figure 6b) and lower the Jsc and FF of the corresponding photovoltaic device. We believe this is one of the reasons to account for the extremely poor photovoltaic device performance of 2D OIHP based on oF1PEA.
To further verify the proposed phase distribution, we conducted transient absorption (TA) measurements on all four 2D OIHP films. Samples were pumped from the glass side at the wavelength of the absorption of the particular n = 1 phase for each 2D OIHP film. Upon excitation, at very early stage (1 ps), we observed strong bleach signal of small n phases (n = 1 or 2) and relatively weak bleach signal from 3D or large n components in the case of PEA, mF1PEA, and pF1PEA based 2D OIHP films (Fig. 2d–g). In contrast, oF1PEA 2D OIHP film shows strong bleach signal for 3D phase signal and relatively weak bleach signal for 2D phases (Fig. 2e). These results support our claim that for PEA, mF1PEA, and pF1PEA based 2D OIHP films, 2D phases with small n dominate the composition on the glass side whereas for oF1PEA, there is a significant amount of 3D phases on the glass side. The dynamics for each 2D OIHP sample also support the corresponding energy transfer mechanisms (Supplementary Figure 7 and Supplementary Note 2). The proposed phase distribution and energy transfer were further supported by characterizations of time of flight secondary ion mass spectrometry (ToF-SIMS, Supplementary Figure 8 and Supplementary Note 3) and ultraviolet photoelectron spectroscopy (UPS, Supplementary Figure 9, Supplementary Table 4 and Supplementary Note 4).
We next investigated the film surface morphology by scanning electron microscope (SEM) (Fig. 3). While PEA 2D OIHP film is quite uniform with some visible pinholes, the oF1PEA 2D OIHP film is very rough and discontinuous. This undesirable surface morphology of the oF1PEA 2D OIHP film could lead to partially shorting of the device or bad contact between the electrodes (including interfacial layers) and the perovskite film, leading to inferior device performance (e.g., low Voc, FF). In contrast, both mF1PEA and pF1PEA 2D OIHP films are uniform without pinholes, a surface morphology conducive to the high device performance we achieved. Probing the surface roughness with atomic force microscopy (AFM) also shows a similar trend (Supplementary Figure 10), with mF1PEA and pF1PEA films show the smallest roughness (less than 20 nm). Overall, we observed the consistent relationship between the surface morphology and device performance.
In addition to phase distribution and surface morphology, crystal orientation was also reported to be an important factor that can remarkably affect the device performance due to the anisotropic nature of 2D OIHPs28,53,54. To investigate the crystal orientation, we performed grazing incidence wide angle X-ray scattering (GIWAXS) on each sample. GIWAXS can elucidate all directions of orientation and we conducted incident angle-dependent experiment to probe different depth from the surface of the film55 (Fig. 4 and Supplementary Figure 11). A lower X-ray incident angle GIWAXS experiment, for example, 0.18°, allows the acquisition of the diffraction data from the top few nanometers of the 2D OIHP films (Fig. 4, left column), whereas a higher incident angle, for example, 1°, probes deeper into the bulk of a film (Fig. 4, right column)56,57,58. First, as a whole, our GIWAXS data for PEA, mF1PEA or pF1PEA based 2D OIHP films clearly show strong, sharp and discrete Bragg spots, indicating a highly orientated film in each case (see Supplementary Figure 11 for full GIWAXS patterns)59,60,61,62,63. On the other hand, the oF1PEA 2D OIHP film exhibits diffraction rings, suggesting no preferred orientation of crystallites28. This observation is also consistent with the film X-ray diffraction pattern (Supplementary Figure 12, 13 and Supplementary Discussion 1). Therefore, the smaller crystallites in the oF1PEA 2D OIHP film must be randomly distributed without a particularly preferred orientation. This random crystal orientation would hinder the charge transport across the film, further explaining the low device performance (e.g., low Jsc and FF). Second, we investigate the presence of unique 2D OIHP signatures in the GIWAXS patterns in all 2D OIHP films in this study. Venkatesan et al. have shown that 2D OIHP films exhibit diffraction peaks less than 10 nm−1 because the spacings associated with the low-Q peaks are only possible when the larger cations are present in the system64. Similar to their findings, at the incident angle = 0.18°, the oF1PEA (Fig. 4b) and mF1PEA (Fig. 4c) 2D OIHP films show clear signals for the n = 1 2D phase around Qz = 4 nm−1, as indicated by the white arrows and indices. The oF1PEA 2D OIHP film has an additional peak around Qz = 4.8 nm−1, which can be assigned to n = 3 (Fig. 4b, orange arrow and index). In sharp contrast, when probed at the same 0.18° incident angle, we do not observe any uniquely 2D OIHP peaks (no clear spots or arcs located at Q < 10 nm−1) in the PEA (Fig. 4a) and pF1PEA (Fig. 4d) 2D OIHP films. This observation of unique low-Q features in GIWAXS directly corroborates with the XRD findings where oF1PEA and mF1PEA 2D OIHP films show low 2θ peaks (Supplementary Figure 13 and Supplementary Discussion 1).
Finally, to understand the vertical distribution of these 2D phases in the 2D OIHP films, we probed all these films with higher incident angle (1°, Fig. 4e–h). Interestingly, under this condition, the PEA (Fig. 4e) and pF1PEA (Fig. 4h) 2D OIHP films do show 2D OIHP peaks at Q < 10 nm−1. In fact, such 2D OIHP peaks in the case of the mF1PEA 2D OIHP film (Fig. 4g) are now even stronger at this higher incident angle. While a few peaks for the pF1PEA 2D OIHP film (Fig. 4h, red arrows) could not be assigned to known 2D phases (n < 4), these peaks are still at a Q < 10 nm−1, suggesting that there might be larger n 2D phases (e.g., n = 4). The stronger intensity of 2D OIHP patterns in PEA, mF1PEA, and pF1PEA 2D OIHP films under higher incident angle indicate that there exists a mixture of 2D phases of different n values, and their concentrations are higher towards the back of the films. On the other hand, the oF1PEA 2D OIHP film (Fig. 4f) exhibits no obvious changes when probing at the higher angle, indicating that oF1PEA 2D OIHP film has a more random phase distribution. These results from GIWAXS for 2D OIHP with different cations strongly agrees with the different phase distribution probed by the prominent PL spectra as discussed earlier (Fig. 2b, c).
The presence of more 2D phases on the surface of mF1PEA 2D OIHP than other studied 2D OHIPs in this work, as indicated by the GIWAXS data (Fig. 4), also helps explain the relatively higher stability of mF1PEA 2D OIHP solar cell than pF1PEA, PEA, and the widely studied BA based 2D OIHP solar cells. As shown in Supplementary Figure 14, when the un-encapsulated devices were stocked under ambient condition (relative humidity around 45%), mF1PEA base 2D OIHP solar cells showed the best stability, while others showed lower stability.
Orientational disorder from single crystal analysis
To further understand how different organic cations impact the structure and texture of these 2D OIHP films, we grew single crystals of 2D OIHPs (n = 1) with each of these four different cations (Supplementary Figure 15), following a procedure previously reported (details in Methods section)65. Though each 2D OIHP film analyzed in this study contains multiple phases (e.g., n = 1, 2, 3, 4, etc.), we chose to synthesize and study single crystals of the n = 1 phase for two reasons. First, the n = 1 phase is the fundamental building unit towards larger n number 2D phases (n = 2, 3, 4, etc.). Only containing the [PbI6] octahedra and the large cation (i.e., no methylammonium), the crystal structure of the n = 1 phase allows us to focus on the interaction between these inorganic octahedra and organic cations. Second, the n = 1 phase can be reliably grown as a pure single crystal with the least amount of dynamic disorder of organic cations or with lamellar disorder; therefore, the analyzed structure can serve as the structural input for density functional calculations.
Single crystal structural models reveal that all three monofluorinated PEA (i.e., oF1PEA, mF1PEA, and pF1PEA) based 2D crystals are composed of sheets of corner-sharing [PbI6] octahedra that are separated by the organic cations (Fig. 5b-d, f-h, Supplementary Table 5, Supplementary Table 6 and Supplementary Discussion 2), similar to that seen in the PEA2PbI4 2D crystal previously reported (Fig. 5a, e)38. Two of the 2D OIHP crystals, pF1PEA2PbI4 and mF1PEA2PbI4, are isostructural to their Sn analogs (4-FPEA)2SnI4 and (3-FPEA)2SnI466, while oF1PEA2PbI4 adopts a lower symmetry structure (space group P\(\bar 1\)) owing to a different packing motif of the organic molecules in the interlayer gallery. The location of the fluorine atom on the PEA (ortho, meta, para) leads to changes in the packing of the bulky organic cations relative to one another with varying degrees of structural disorder. For instance, the packing of pF1PEA2PbI4 has the cations within the interlayer gallery facing the same direction in a co-aligned fashion (Fig. 5d, h), which is consistent with the Sn-analogue reported earlier66,67. The structure is fully ordered with no split atomic sites, indicating registry between neighboring layers is retained throughout the structure67. On the other hand, mF1PEA2PbI4 has a different packing motif: within a single layer of the organic interlayer gallery, neighboring aromatic moieties are rotated relative to one another to generate a herringbone configuration (Fig. 5c). Another significant difference between mF1PEA2PbI4 and pF1PEA2PbI4 is the presence of split equatorial iodine atomic positions and consequentially a splitting of the ammonium groups on the mF1PEA cations; attribution of this disorder and a logical construction of the idealized configuration is described in the Supplementary Information (Supplementary Figure 16). This disorder is similar to that observed in (3-FPEA)2SnI466 where the splitting of sites was attributed to loss of registry between inorganic sheets within the material. Lastly, oF1PEA2PbI4 has yet another packing motif that is similar to PEA2PbI4. Within the organic interlayer gallery, the organic cations in the top layer are co-aligned facing the same direction (Fig. 5b), but the neighboring bottom-most layer cations are then rotated ~90° relative to the top-most layer (Fig. 5f). Additionally, the crystal structure of oF1PEA2PbI4 reveals a lack of ordering of the organic bilayer perpendicular to the planes (Supplementary Figure 17, 18). This is different from PEA2PbI4, which does have ordering of the organic cations. This indicates that oF1PEA2PbI4 has the most orientational disorder of the three monofluorinated PEA based 2D crystals. Therefore, we propose that during the film formation of the oF1PEA based 2D OIHP film, the lack of ordering of the organic bilayer would cause the formation of small crystal domains and may also play a part in why the film morphology and subsequent device performance was so drastically lower than either PEA, pF1PEA, or mF1PEA 2D OIHP films. We will further quantify this difference through the formation energy difference conducted by DFT calculation (vide infra).
The analyzed structures of n = 1 2D crystals allowed us to conduct DFT calculations of the formation energies of these n = 1 2D OIHPs (i.e., the total energy difference between the final perovskite structure and the starting aryl-ammonium iodide and lead iodide)27. Details of DFT calculation parameters are shown in Supplementary Note 5. The relative formation energies are shown in Fig. 6 and Supplementary Table 7. For mF1PEA2PbI4 and pF1PEA2PbI4, their formation energies are close, and more favorable towards the formation of the n = 1 2D crystal than that of PEA2PbI4; in contrast, the formation energy of oF1PEA2PbI4 is the least favorable. Indeed, the trend of the calculated formation energy is consistent with the quality of crystals (e.g., the crystal size and visible defects) we obtained (pF1PEA2PbI4 ≈ mF1PEA2PbI4 > PEA2PbI4 » oF1PEA2PbI4, Supplementary Figure 15). This trend also follows the trend observed in the structural transition enthalpy determined by differential scanning calorimetry (DSC) reported by Li et al.65, indicating that this simulated formation energy trend is in agreement with experiments. In addition, the relatively unfavorable formation energy of oF1PEA2PbI4 can also lead to the most disordered crystal structure among these four crystals, which—again—agrees with the single crystal structure discussed earlier. Finally, this formation energy trend also matches the device performance we observed. Therefore, we propose that this different formation energy is likely what leads to the different film properties in our study in three aspects. First, with a more favorable formation energy (e.g., pF1PEA2PbI4 in Fig. 6), it is relatively easy to form large domains and results in a more compact film. For the unfavorable formation energy of oF1PEA2PbI4, there is an orientational degeneracy of the dipole formed by the fluorine substitution, leading to crystallographic disorder; as such, macroscopic defects are more likely to form and lower the device performance. Second, it has been reported that the driving force to form 2D OIHP with smaller n value is larger27. We propose that during the film formation following our fabrication procedure, the back side (i.e., glass side) of the film was heated first and quickly accumulated with the formation of the phase with small n values. Because of the formation of small n phases, the stoichiometric ratio of the precursor would shift to a phase with an even larger n value. As a result, the ordered phase distribution with small n value phase at the bottom (glass side) and larger n value phase on the top (air side) were formed. In the case of oF1PEA2PbI4, the formation energy is less favorable than those of the rest, which could hinder the quick formation small n phase at the early stage. As a result, the unfavorable disordered phase distribution would occur in the oF1PEA 2D OIHP film. Third, the small crystal domain and random orientation in oF1PEA 2D OIHP films, caused by the unfavorable formation energy and highly disordered crystal structure, would further hinder the device performance. In addition, it is worth noticing that the inorganic frameworks (i.e., the Pb-I layer) in these crystals are almost identical (e.g., bond length, Pb-I-Pb angle, etc., Supplementary Table 8). Therefore, the main difference among these crystals must be from the packing of the organic layers (i.e., packing between PEA or F1PEA). For 2D OIHP phases with a higher n value where the only difference is increasing the thickness of the inorganic slab, the organic spacer layers would retain the same orientational preferences due to the shapes of the fluorinated molecules, even with slight differences in octahedral tilting; therefore, we propose that the trends in formation energy of n = 1 phases are representative of all compounds with n > 1. Furthermore, given the only difference among these cations is the substitution position of the fluorine (or no fluorine in the case of PEA), we believe that the noncovalent interaction, for example, dipole interaction between these large cations, will highly influence the film properties and therefore, result in different device performance.
In summary, we discovered that the photovoltaic device performance of 2D OIHPs can be significantly impacted by the spacer cation chemistry and packing, as established by a seemly negligible change in the position of monofluorination on the PEA cation. In the studied series of 2D OIHP films (PEA, oF1PEA, mF1PEA, and pF1PEA), the pF1PEA based 2D OIHP showed the highest efficiency of over 10%, followed by mF1PEA (over 10%), PEA (over 7%), and oF1PEA (less than 1%). Through an orchestra of experiments, we have identified possible causes to account for the observed difference in device performances. First, all these films contain multiple 2D phases (n = 1, 2, 3, 4, etc.) and 3D phases, yet the distribution of these phases are different for each 2D OIHP film in this study. While three OIHP films (PEA, mF1PEA and pF1PEA) show more or less a vertical phase distribution where the small n phases accumulated near the substrate and 3D phases near the surface of the film, the oF1PEA OIHP film only shows a rather random distribution of 2D phases. Second, the surface of oF1PEA OIHP film is very rough and discontinuous, which is undesirable for solar cells. Third, the crystallites in the oF1PEA OIHP film are small and randomly distributed without particularly preferred orientation.
Taking one step further, the single crystal structures of related n = 1 2D OIHPs and DFT calculation establish the rules for packing of these substituted organic cations; such packing results in various degrees of orientational order and disorder, depending upon the nature of the organic cations, as predicted by the formation energy. These differences could be caused by the organic cation interactions (e.g., dipole–dipole interactions), which is likely the fundamental reason for the observed photovoltaic device differences among these different PEA cations based 2D OIHP films.
Furthermore, our study offers an example where chemical modification of organic cations, device performance, film morphology and crystallography are integrated to derive the structure-properties relationships. Such relationships—where weak yet cooperative interactions can still yield macroscopic differences in performance—provide a guide for the design of materials with desirable properties for functional devices. We note cations with single benzene ring like PEA lack the coveted optoelectronic functionalities; however, this work still provides valuable insight to the future design of more complex conjugated cations to achieve desirable properties for a variety of applications including photovoltaics24,34,35, light emitting13,48,49, transistors4,66, spin electronics68, etc. We believe future design of organic cations and understanding the intermolecular interactions associated with these organics, will play an essential role in further development of these 2D OIHP materials.
Synthesis of MAI, PEAI, oF1PEAI, mF1PEAI, and pF1PEAI
Eleven milliliter unstabilized hydroiodic acid (HI) (57 wt% in water, Sigma-Aldrich) was purified using a 0.36 M tributyl phosphate solution in chloroform, following a previous reported procedure24. Then the as-prepared HI was dropped into a cold 10 mL methylamine solution (40 wt% in water, Sigma-Aldrich) under stirring. The crude product was obtained by slowly evaporating the solvent under reduced pressure. Then the white precipitate was dissolved and recrystallized in ethanol and washed with ethyl ether. The product was dried under vacuum overnight.
Five milliliter phenethylammonium (Alfa Aesar, 99%) or 2-fluorophenethylamine (Acros Organics, 97%) or 3-fluorophenethylamine (Alfa Aesar, 97%) or 4-fluorophenethylamine (Sigma-Aldrich, 99%) was diluted with 5 mL ethanol. As-purified HI was dropped into an ice-cold amine solution under stirring. The crude product was precipitated during the process. Ethyl ether was then added into the solution to further precipitate the ammonium product. Then the white precipitate was re-dissolved and recrystallized with ethanol, and lastly washed with ethyl ether. The products were dried under vacuum overnight.
Deposition of perovskite films
For 2D OIHP films, the precursor solution was made by dissolving PEAI (or oF1PEAI, mF1PEAI, pF1PEAI), MAI and PbI2 (99.9985%, from Alfa Aesar) in dimethylformamide (DMF) (from Sigma-Aldrich) with the molar ratio of PEAI:MAI:PbI2 = 2:3:4 and the mixture was stirred for at least 60 min. The concentration of Pb2+ was 1 M for the precursor solution used to prepare the OIHP films for all characterizations except for TA measurement, where the precursor solution adopted a concentration of 0.5 M for Pb2+. The 2D OIHP film was spin-coated at 5000 rpm for 20 s from the precursor solution on a substrate (glass substrates for XRD and optical characterizations; poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) coated indium doped tin oxide (ITO) substrates for solar cells, SEM and AFM; Si wafer for ToF-SIMS; PEDOT:PSS coated Si wafer for GIWAXS) and then the resulting film was quickly transferred to a hot plate at desired temperature (65 °C for pF1PEA and 40 °C for the rest) to anneal 30 s. The spin-coating process was done in an ambient condition with a relative humidity around 10–45%.
For 3D OIHP (MAPbI3), film was deposited by one-step anti-solvent extraction approach. The perovskite precursor solution was prepared by dissolving 461 mg PbI2 and 159 mg MAI in 700 mL DMF and 78 µL dimethyl sulfoxide (DMSO). Then the MAPbI3 precursor solution was spun onto the substrate (glass for XRD and optical characterizations) at 2000 rpm for 2 s and 4000 rpm for 20 s, the sample was drop-casted with 0.3 mL toluene at 8 s of the second-step spin-coating. Subsequently, the sample was annealed at 65 °C for 10 min and 100 °C for 10 min
Device fabrication and characterization
Glass substrates coated with patterned ITO (Thin Film Devices, Inc with a resistivity of 20 Ω □−1) were ultrasonicated in deionized water, acetone, and 2-proponal for 15 min each sequentially. The substrates were dried under a stream of nitrogen and subjected to the treatment of UV-Ozone for 15 min. PEDOT:PSS in water (Clevios™ P VP AI 4083 from Heraeus) filtered by 0.45 µm polyvinylidene difluoride (PVDF) filter was then spun cast onto cleaned ITO substrates at 4000 rpm for 60 s and then baked at 130 °C for 15 min in air to give a thin film with a thickness of 40 nm. Then the perovskite film was coated on top of the PEDOT:PSS as previously mentioned. After cooling down, the [6,6]-phenyl C61 butyric acid methyl ester (PCBM) was spin-coated on top at 2000 rpm for 30 s from a PCBM solution in chloroform with a concentration of 13.3 mg mL−1 in a N2 filled glovebox. The film was heated at 80 °C for 15 min. After cooling down, a bathophenanthroline solution in ethanol with a concentration of 0.7 mg mL−1 was spin-coated on PCBM layer at 4000 rpm for 30 s. Then 70 nm aluminum was thermally evaporated as the metal electrode at a base pressure of 2 × 10–6 mbar. The active area was 0.13 cm2, controlled by a shadow mask.
Device characterization was carried out under AM 1.5 G irradiation with the intensity of 100 mW cm−2 (Oriel 91160, 300 W) calibrated by a NREL certified standard silicon cell in a nitrogen filled glovebox. Current density versus voltage (J–V) curves were recorded with a Keithley 2400 digital source meter. The scan rate is 50 mV s−1 and dwell time is 0.1 s. For oF1PEA, mF1PEA, pF1PEA based 2D OIHP solar cells, no preconditioning were performed while for PEA based 2D OIHP solar cell, light soaking for 10 min was performed before testing. External quantum efficiency (EQE) was detected under monochromatic illumination (Oriel Cornerstone 260 1/4 m monochromator equipped with Oriel 70613NS QTH lamp), and the calibration of the incident light was performed with a monocrystalline silicon diode (Model No.: Newport 71580).
The photoluminescence of OIHP thin films on glass slides was measured using a Horiba Scientific Fluorolog-3 spectrofluorometer. The excitation wavelength was 450 nm. The absorption of OIHP thin films on glass slides was obtained with a Shimadzu UV-2600 spectrophotometer.
All transient absorption experiments were conducted with a 45 fs, 4 mJ Coherent Libra with a 1 kHz repetition rate. Approximately 1.5 mJ of the 800 nm fundamental was focused into a 4 m long tube filled with argon gas to generate a visible continuum. The continuum pulse was then passed through an all-reflective 4 F setup, which was based on a 1200 g mm−1 grating and 20 cm focal length mirror. A motorized slit at the Fourier plane was used to filter the desired portion of the spectrum. The spectrally filtered pulses had 5 nm widths and 250 fs durations. Pulse energies were controlled with a rotational neutral density filter.
Continuum probe pulses were generated in a sapphire window and relayed to the sample with reflective optics. The spot size of the probe was adjusted to match the 200 µm spot size of the pump. The pump fluence was 2.9 × 1013 photons cm−2 (10 µJ cm−2) unless indicated otherwise below. Signal detection was accomplished with a CMOS array detector that was synchronized to the 1 kHz repetition rate of the laser system. In transient absorption experiments, the signals were averaged over 30 scans of the delay line and a total of 6000 differences were collected at each delay point.
For SEM and AFM imaging, films of the OIHPs were deposited on a PEDOT:PSS covered ITO substrate. SEM images were obtained by a Hitachi S-4700 cold cathode field emission SEM. AFM images were obtained by Asylum Research MFP3D Atomic Force Microscope.
The GIWAXS patterns were collected at beamline 7.3.3 at the Advanced Light Source in Lawrence Berkeley National Laboratory69. The incident X-ray energy was 10 keV while the detector was a Pilatus 2 M. The patterns were corrected, axis-labeled, and colored as shown using Igor Pro and a modified version of the NIKA package70.
Devices of the OIHPs were fabricated following the same procedures for solar cell performance characterization except that Cu was used as the top electrode instead of Al. Un-encapsulated devices were kept in a desiccator with saturate K2CO3 to maintain a relative humidity around 45%.
Single crystal growth
To synthesize the single crystals, 26.4 mg PbI2 and 28.6 mg PEAI (for oF1PEAI, mF1PEAI or pF1PEAI, 30.7 mg ammonium iodide was used) were dissolved in 57 wt% stabilized HI (Alfa Aesar) at 95 °C. 1.5 mL HI was needed to fully dissolve pF1PEAI, and for the rest, 1 mL was enough. This difference is likely due to the different formation energy of these perovskites. The solution was slowly cooled down at 1 °C h−1 to room temperature. The solids were filtered and washed with plenty of ethyl ether.
Further information on experimental design is available in the Nature Research Reporting Summary linked to this article.
A reporting summary for this Article is available as a Supplementary Information file. The source data underlying Supplementary Figure 3 and Supplementary Table 1 are provided as a Source Data file. The single crystal results are available in The Cambridge Crystallographic Data Center: oF1PEA2PbI4: 1893383 [https://doi.org/10.5517/ccdc.csd.cc21k6wq]; mF1PEA2PbI4: 1893384 [https://doi.org/10.5517/ccdc.csd.cc21k6xr]; pF1PEA2PbI4: 1893385 [https://doi.org/10.5517/ccdc.csd.cc21k6ys]; idealized supercell of oF1PEA2PbI4: 1893474 [https://doi.org/10.5517/ccdc.csd.cc21k9tr]; idealized supercell of mF1PEA2PbI4: 1893475 [https://doi.org/10.5517/ccdc.csd.cc21k9vs]. All relevant data are available from the authors.
Shi, E. et al. Two-dimensional halide perovskite nanomaterials and heterostructures. Chem. Soc. Rev. 47, 6046–6072 (2018).
Tamotsu, I. & Yusei, M. In situ X-ray observation on the intercalation of weak interaction molecules into perovskite-type layered crystals (C9H19NH3)2PbI4 and (C10H21NH3)2CdCl4. Bull. Chem. Soc. Jpn 59, 563–567 (1986).
Calabrese, J. et al. Preparation and characterization of layered lead halide compounds. J. Am. Chem. Soc. 113, 2328–2330 (1991).
Kagan, C. R. et al. Organic-inorganic hybrid materials as semiconducting channels in thin-film field-effect transistors. Science 286, 945–947 (1999).
Mitzi, D. B., Feild, C. A., Harrison, W. T. A. & Guloy, A. M. Conducting tin halides with a layered organic-based perovskite structure. Nature 369, 467–469 (1994).
Dolzhenko, Y. I., Inabe, T. & Maruyama, Y. In situ X-ray observation on the intercalation of weak interaction molecules into perovskite-type layered crystals (C9H19NH3)2PbI4 and (C10H21NH3)2CdCl4. Bull. Chem. Soc. Jpn 59, 563–567 (1986).
Straus, D. B. & Kagan, C. R. Electrons, excitons, and phonons in two-dimensional hybrid perovskites: connecting structural, optical, and electronic properties. J. Phys. Chem. Lett. 9, 1434–1447 (2018).
Saparov, B. & Mitzi, D. B. Organic–inorganic perovskites: structural versatility for functional materials design. Chem. Rev. 116, 4558–4596 (2016).
Hu, J., Yan, L. & You, W. Two-dimensional organic–inorganic hybrid perovskites: a new platform for optoelectronic applications. Adv. Mater. 30, 1802041 (2018).
Stoumpos, C. C. et al. Ruddlesden–Popper hybrid lead iodide perovskite 2D homologous semiconductors. Chem. Mater. 28, 2852–2867 (2016).
Tanaka, K. & Kondo, T. Bandgap and exciton binding energies in lead-iodide-based natural quantum-well crystals. Sci. Technol. Adv. Mater. 4, 599–604 (2003).
Dou, L. et al. Atomically thin two-dimensional organic–inorganic hybrid perovskites. Science 349, 1518–1521 (2015).
Chondroudis, K. & Mitzi, D. B. Electroluminescence from an organic−inorganic perovskite incorporating a quaterthiophene dye within lead halide perovskite layers. Chem. Mater. 11, 3028–3030 (1999).
Ema, K., Inomata, M., Kato, Y., Kunugita, H. & Era, M. Nearly perfect triplet–triplet energy transfer from Wannier excitons to naphthalene in organic–inorganic hybrid Quantum-well materials. Phys. Rev. Lett. 100, 257401 (2008).
Braun, M., Tuffentsammer, W., Wachtel, H. & Wolf, H. C. Tailoring of energy levels in lead chloride based layered perovskites and energy transfer between the organic and inorganic planes. Chem. Phys. Lett. 303, 157–164 (1999).
Passarelli, J. V. et al. Enhanced out-of-plane conductivity and photovoltaic performance in n = 1 layered perovskites through organic cation design. J. Am. Chem. Soc. 140, 7313–7323 (2018).
Kikuchi, K., Takeoka, Y., Rikukawa, M. & Sanui, K. Fabrication and characterization of organic–inorganic perovskite films containing fullerene derivatives. Colloids Surf. A 257-258, 199–202 (2005).
Jemli, K. et al. Two-dimensional perovskite activation with an organic luminophore. ACS Appl. Mater. Interfaces 7, 21763–21769 (2015).
Era, M., Morimoto, S., Tsutsui, T. & Saito, S. Organic–inorganic heterostructure electroluminescent device using a layered perovskite semiconductor (C6H5C2H4NH3)2PbI4. Appl. Phys. Lett. 65, 676–678 (1994).
Hattori, T., Taira, T., Era, M., Tsutsui, T. & Saito, S. Highly efficient electroluminescence from a heterostructure device combined with emissive layered-perovskite and an electron-transporting organic compound. Chem. Phys. Lett. 254, 103–108 (1996).
Mitzi, D. B., Chondroudis, K. & Kagan, C. R. Organic–inorganic electronics. IBM J. Res. Dev. 45, 29–45 (2001).
Chen, Y. et al. 2D Ruddlesden–Popper perovskites for optoelectronics. Adv. Mater. 30, 1703487 (2018).
Mase, K., Okumura, K., Yanai, N. & Kimizuka, N. Triplet sensitization by perovskite nanocrystals for photon upconversion. Chem. Commun. 53, 8261–8264 (2017).
Smith, I. C., Hoke, E. T., Solis-Ibarra, D., McGehee, M. D. & Karunadasa, H. I. A layered hybrid perovskite solar-cell absorber with enhanced moisture stability. Angew. Chem. Int. Ed. 53, 11232–11235 (2014).
Zhang, X. et al. Stable high efficiency two-dimensional perovskite solar cells via cesium doping. Energy Environ. Sci. 10, 2095–2102 (2017).
Cao, D. H., Stoumpos, C. C., Farha, O. K., Hupp, J. T. & Kanatzidis, M. G. 2D homologous perovskites as light-absorbing materials for solar cell applications. J. Am. Chem. Soc. 137, 7843–7850 (2015).
Quan, L. N. et al. Ligand-stabilized reduced-dimensionality perovskites. J. Am. Chem. Soc. 138, 2649–2655 (2016).
Tsai, H. et al. High-efficiency two-dimensional Ruddlesden–Popper perovskite solar cells. Nature 536, 312–314 (2016).
Grancini, G. et al. One-Year stable perovskite solar cells by 2D/3D interface engineering. Nat. Commun. 8, 15684 (2017).
Wang, Z. et al. Efficient ambient-air-stable solar cells with 2D–3D heterostructured butylammonium-caesium-formamidinium lead halide perovskites. Nat. Energy 2, 17135 (2017).
Zhou, N. et al. Exploration of crystallization kinetics in quasi two-dimensional perovskite and high performance solar cells. J. Am. Chem. Soc. 140, 459–465 (2018).
Etgar, L. The merit of perovskite’s dimensionality: can this replace the 3D halide perovskite? Energy Environ. Sci. 11, 234–242 (2018).
Xinqian, Z. et al. Orientation regulation of phenylethylammonium cation based 2D perovskite solar cell with efficiency higher than 11%. Adv. Energy Mater. 8, 1702498 (2018).
Lai, H. et al. Two-dimensional Ruddlesden–Popper perovskite with nanorod-like morphology for solar cells with efficiency exceeding 15%. J. Am. Chem. Soc. 140, 11639–11646 (2018).
Yang, R. et al. Oriented quasi-2D perovskites for high performance optoelectronic devices. Adv. Mater. 30, 1804771 (2018).
Jian, Q. et al. Aligned and graded type‐II Ruddlesden–Popper perovskite films for efficient solar cells. Adv. Energy Mater. 8, 1800185 (2018).
Yan, L. et al. A general post-annealing method enables high-efficiency two-dimensional perovskite solar cells. ACS Appl. Mater. Interfaces 10, 33187–33197 (2018).
Du, K.-Z. et al. Two-dimensional Lead(II) halide-based hybrid perovskites templated by acene alkylamines: crystal structures, optical properties, and piezoelectricity. Inorg. Chem. 56, 9291–9302 (2017).
Knutson, J. L., Martin, J. D. & Mitzi, D. B. Tuning the band gap in hybrid tin iodide perovskite semiconductors using structural templating. Inorg. Chem. 44, 4699–4705 (2005).
Xu, Z., Mitzi, D. B., Dimitrakopoulos, C. D. & Maxcy, K. R. Semiconducting perovskites (2-XC6H4C2H4NH3)2SnI4 (X=F, Cl, Br): steric interaction between the organic and inorganic layers. Inorg. Chem. 42, 2031–2039 (2003).
Snaith, H. J. et al. Anomalous hysteresis in perovskite solar cells. J. Phys. Chem. Lett. 5, 1511–1515 (2014).
Shao, S. et al. Elimination of the light soaking effect and performance enhancement in perovskite solar cells using a fullerene derivative. Energy Environ. Sci. 9, 2444–2452 (2016).
Unger, E. L. et al. Hysteresis and transient behavior in current–voltage measurements of hybrid-perovskite absorber solar cells. Energy Environ. Sci. 7, 3690–3698 (2014).
Eames, C. et al. Ionic transport in hybrid lead iodide perovskite solar cells. Nat. Commun. 6, 7497 (2015).
Tress, W. et al. Understanding the rate-dependent J–V hysteresis, slow time component, and aging in CH3NH3PbI3 perovskite solar cells: the role of a compensated electric field. Energy Environ. Sci. 8, 995–1004 (2015).
Williams, O. F. et al. Energy transfer mechanisms in layered 2D perovskites. J. Chem. Phys. 148, 134706 (2018).
Liu, J., Leng, J., Wu, K., Zhang, J. & Jin, S. Observation of internal photoinduced electron and hole separation in hybrid two-dimensional perovskite films. J. Am. Chem. Soc. 139, 1432–1435 (2017).
Yuan, M. et al. Perovskite energy funnels for efficient light-emitting diodes. Nat. Nanotechnol. 11, 872–877 (2016).
Wang, N. et al. Perovskite light-emitting diodes based on solution-processed self-organized multiple quantum wells. Nat. Photonics 10, 699 (2016).
Zhao, J. et al. Strained hybrid perovskite thin films and their impact on the intrinsic stability of perovskite solar cells. Sci. Adv. 3, eaao5616 (2017).
Wang, Q. et al. Large fill-factor bilayer iodine perovskite solar cells fabricated by a low-temperature solution-process. Energy Environ. Sci. 7, 2359–2365 (2014).
Wang, J. et al. Engineered directional charge flow in mixed two-dimensional perovskites enabled by facile cation-exchange. J. Phys. Chem. C 121, 21281–21289 (2017).
Chen, A. Z. et al. Origin of vertical orientation in two-dimensional metal halide perovskites and its effect on photovoltaic performance. Nat. Commun. 9, 1336 (2018).
Xu, Z. et al. Phase transition control for high performance Ruddlesden–Popper perovskite solar cells. Adv. Mater. 30, 1707166 (2018).
Baker, J. L. et al. Quantification of thin film crystallographic orientation using X-ray diffraction with an area detector. Langmuir 26, 9146–9151 (2010).
Rivnay, J., Mannsfeld, S. C. B., Miller, C. E., Salleo, A. & Toney, M. F. Quantitative determination of organic semiconductor microstructure from the molecular to device scale. Chem. Rev. 112, 5488–5519 (2012).
Renaud, G., Lazzari, R. & Leroy, F. Probing surface and interface morphology with grazing incidence small angle X-ray scattering. Surf. Sci. Rep. 64, 255–380 (2009).
Singh, M. A. & Groves, M. N. Depth profiling of polymer films with grazing-incidence small-angle X-ray scattering. Acta Crystallogr. A 65, 190–201 (2009).
Guerra, V. L. P. et al. Implications of TiO2 surface functionalization on polycrystalline mixed halide perovskite films and photovoltaic devices. J. Mater. Chem. A 3, 20811–20818 (2015).
Moore, D. T. et al. Direct crystallization route to methylammonium lead iodide perovskite from an ionic liquid. Chem. Mater. 27, 3197–3199 (2015).
Zhang, W. et al. Ultrasmooth organic–inorganic perovskite thin-film formation and crystallization for efficient planar heterojunction solar cells. Nat. Commun. 6, 6142 (2015).
Huang, W., Huang, F., Gann, E., Cheng, Y.-B. & McNeill, C. R. Probing Molecular and crystalline orientation in solution-processed perovskite solar cells. Adv. Funct. Mater. 25, 5529–5536 (2015).
Soe, C. M. M. et al. Room temperature phase transition in methylammonium lead iodide perovskite thin films induced by hydrohalic acid additives. ChemSusChem 9, 2656–2665 (2016).
Venkatesan, N. R., Labram, J. G. & Chabinyc, M. L. Charge-carrier dynamics and crystalline texture of layered Ruddlesden–Popper hybrid lead iodide perovskite thin films. ACS Energy Lett. 3, 380–386 (2018).
Li, T., Dunlap-Shohl, W. A., Han, Q. & Mitzi, D. B. Melt processing of hybrid organic–inorganic lead iodide layered perovskites. Chem. Mater. 29, 6200–6204 (2017).
Mitzi, D. B., Dimitrakopoulos, C. D. & Kosbar, L. L. Structurally tailored organic−inorganic perovskites: optical properties and solution-processed channel materials for thin-film transistors. Chem. Mater. 13, 3728–3740 (2001).
Kikuchi, K., Takeoka, Y., Rikukawa, M. & Sanui, K. Structure and optical properties of lead iodide based two-dimensional perovskite compounds containing fluorophenethylamines. Curr. Appl. Phys. 4, 599–602 (2004).
Long, G. et al. Spin control in reduced-dimensional chiral perovskites. Nat. Photonics 12, 528–533 (2018).
Alexander, H. et al. A SAXS/WAXS/GISAXS beamline with multilayer monochromator. J. Phys. Conf. Ser. 247, 012007 (2010).
Ilavsky, J. Nika: software for two-dimensional data reduction. J. Appl. Crystallogr. 45, 324–328 (2012).
J.Hu, L.Y., and W.Y. are supported by the National Science Foundation (DMR-1728921) and UNC Research Opportunities Initiative (ROI) through the Center of Hybrid Materials Enabled Electronic Technology. M.M.N., H.A., Y.L., X.X., and J.Huang are also supported by the same UNC Research Opportunities Initiative (ROI). The SEM image, AFM image and UPS analysis in this work was performed in part at the Chapel Hill Analytical and Nanofabrication Laboratory, CHANL. ToF-SIMS analysis was performed in part at the Analytical Instrumentation Facility (AIF) at North Carolina State University. Both CHANL and AIF are members of the North Carolina Research Triangle Nanotechnology Network, RTNN, which is supported by the National Science Foundation, Grant ECCS-1542015, as part of the National Nanotechnology Coordinated Infrastructure, NNCI. J.Hu and W.Y. want to thank Sara Wehlin and Professor Gerald Meyer (UNC-Chapel Hill) for assistance with PL measurements. S.J.S. is supported by the National Science Foundation (No. DGE-1633587). The GIWAXS data was acquired at beamline 7.3.3 at the Advanced Light Source (ALS) in Lawrence Berkeley National Laboratory, which is supported by the U.S. Department of Energy (No. DE-AC02-05CH11231). Experimental support was provided at the ALS by beamline scientists C. Zhu and A. Liebman-Pelaez. Work at Colorado State University was supported by the grant DE-SC0016083 funded by the U.S. Department of Energy, Office of Science. J.R.N. acknowledges support from Research Corporation for Science Advancement through a Cottrell Scholar Award and the A.P. Sloan Foundation for assistance provided from a Sloan Research Fellowship. This work utilized the RMACC Summit supercomputer, which is supported by the National Science Foundation (awards ACI-1532235 and ACI-1532236), the University of Colorado Boulder and Colorado State University. The RMACC Summit supercomputer is a joint effort of the University of Colorado Boulder and Colorado State University. J.R.N. gratefully acknowledges the support of NVIDIA Corporation with the donation of the Tesla K40 GPU used for this research. Z.C. is supported by the China Scholarship Council (CSC, File No. 201706175063) and National Science Foundation of China (NSFC, project NO. 51503075). N.Z., O.F.W., Z.G., and A.M.M. are supported by National Science Foundation (CHE-1763207).
The authors declare no competing interests.
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hu, J., Oswald, I.W.H., Stuard, S.J. et al. Synthetic control over orientational degeneracy of spacer cations enhances solar cell efficiency in two-dimensional perovskites. Nat Commun 10, 1276 (2019). https://doi.org/10.1038/s41467-019-08980-x
This article is cited by
Stabilization of 3D/2D perovskite heterostructures via inhibition of ion diffusion by cross-linked polymers for solar cells with improved performance
Nature Energy (2023)
Phase-pure two-dimensional layered perovskite thin films
Nature Reviews Materials (2023)
Carbonized polymer dots enhanced stability and flexibility of quasi-2D perovskite photodetector
Light: Science & Applications (2022)
Discovery of Pb-free hybrid organic–inorganic 2D perovskites using a stepwise optimization strategy
npj Computational Materials (2022)
Direct drop-casting synthesis of all-inorganic lead and lead-free halide perovskite microcrystals for high-performance photodetectors
Nano Research (2022)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.