The ever-increasing demands for advanced lithium-ion batteries have greatly stimulated the quest for robust electrodes with a high areal capacity. Producing thick electrodes from a high-performance active material would maximize this parameter. However, above a critical thickness, solution-processed films typically encounter electrical/mechanical problems, limiting the achievable areal capacity and rate performance as a result. Herein, we show that two-dimensional titanium carbide or carbonitride nanosheets, known as MXenes, can be used as a conductive binder for silicon electrodes produced by a simple and scalable slurry-casting technique without the need of any other additives. The nanosheets form a continuous metallic network, enable fast charge transport and provide good mechanical reinforcement for the thick electrode (up to 450 µm). Consequently, very high areal capacity anodes (up to 23.3 mAh cm−2) have been demonstrated.
Utilization of Li-ion chemistry to store the energy electrochemically can address the ever-increasing demands from both portable electronics and hybrid electrical vehicles1,2,3,4. Such stringent challenges on the battery safety and lifetime issues require high-performance battery components, with most of the focus being on electrodes or electrolytes with novel nanostructures and chemistries5,6,7,8,9,10. However, equally important is the development of electrode additives, which are required to maintain the electrode’s conductive network and mechanical integrity.
Traditionally, electrode additives are made of dual components based on a conductive agent (i.e. carbon black, CB) and a polymeric binder11,12. While the former ensures the charge transport throughout the electrode, the latter mechanically holds the active materials and CB together during cycling. Although these traditional electrode additives have been widely applied in Li-ion battery technologies13, they fail to perform well in high-capacity electrodes, especially those displaying large volume changes14. This is because the polymeric binder is not mechanically robust enough to withstand the stress induced during lithiation/delithiation, leading to severe disruption of the conducting networks. This results in rapid capacity fade and poor lifetime.
This issue can be solved by employing a conductive binder to accommodate the large volume change of the electrodes15. This strategy not only ensures good mechanical adhesion of the active materials to the conductive agent but also decreases the inactive volume/mass of the electrode, leading to improved battery performance. Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonic acid) (PEDOT:PSS)15, polyaniline16 and polypyrrole17 etc.18,19 have demonstrated inherent electronic/ionic conductivity in the Li+-containing electrolyte and capability in preserving the mechanical integrity of large-capacity materials, such as silicon (Si, CSP = ~3500 mAh g−1) anodes. However, while several novel conductive binders have been reported for Si-based anodes20,21, their achievable areal capacity, which should be more emphasized in practical cases, is generally low (<4 mAh cm−2)22,23. Revisiting the electrode areal capacity (C/A = C/M × M/A, where C/M is the specific capacity (mAh g−1) of the electrode and M/A is its mass loading (mg cm−2)) implies that one has to increase the M/A of the Si-based anodes (while retaining high specific capacity). This, in turn, requires the formation of a thick electrode using the commercially available technology to cast the conductive-binder/Si-based slurry. Unfortunately, this has proven to be quite difficult, as the critical cracking thickness (CCT), determined by the viscosity and surface tension of the slurry, etc.24, greatly limits the electrodes’ achievable M/A. This is especially true in the reported conductive polymer solutions, where either concentration (or viscosity) of the solution is fairly low or the capillary pressure in the slurry drying process is too high14,15. This means that developing an aqueous solution of conductive-binder with a high concentration (and thus, high viscosity), and achieving high M/A (or C/A) Si-based anodes, are quite important and urgent.
Here we show that the goals outlined above can be simultaneously achieved by using MXene nanosheets as a new class of conductive binder to fabricate high-M/A Si/MXene anodes without any additional polymer or CB. MXenes are an emerging class of two-dimensional (2D) materials produced by selectively etching the A-group element (typically Al or Ga) from the parent MAX phase25,26,27. The as-obtained MXene can be expressed in a general formula Mn+1XnTx, where M represents an early transition metal, X is C and/or N, Tx stands for various surface functionalities such as –OH, –O, and/or –F, and n = 1, 2, or 328,29,30. We take advantage of the excellent mechanical properties of the nanosheets to facilitate the formation of thick electrodes while their high conductivity yields a conducting network, which can efficiently distribute charge. We demonstrate two types of MXene inks, titanium carbide (Ti3C2Tx) and carbonitride (Ti3CNTx) as the conductive binder for producing high C/A nanoscale Si/MXene anodes. We also show graphene-wrapped Si microparticles embedded in the Ti3C2Tx network enable much higher M/A with C/A compared to other Si/conductive binder systems.
Results and discussion
MXene ink characterization
We start by describing the synthesis of Ti3C2Tx (MX-C) and Ti3CNTx (MX-N). After etching the MAX precursors (Supplementary Fig. 1a, b) in hydrochloric acid-lithium fluoride solution31,32, multilayered MXenes, with a certain degree of delamination (Supplementary Fig. 1c, d)32, were obtained. Upon vigorous manual shaking of the MXene/water suspension, the clay-like m-MXenes further swelled and delaminated into MX-C and MX-N flakes, forming concentrated aqueous inks. The viscous feature of the MX-C ink is shown in Fig. 1a. Both MX-C/MX-N inks are made of clean flakes with a hexagonal atomic structure (Fig. 1b, c and Supplementary Fig. 2a,b), agreeing with previous reports12,31. The atomic force microscopy and height profiles (Supplementary Fig. 2c) suggest these nanosheets are predominantly single-layered. These two types of inks possess a similar concentration (~25 mg mL−1), and the mean flake size is in the range of 2.1–2.8 µm in both cases (Fig. 1d).
As mentioned above, the CCT of Si-based anode is directly related to the viscosity of the slurry24. Therefore, the rheological behaviours of MXene aqueous inks, together with a reference sample made of traditional dual-component additives (PAA/carbon black, CB) dispersed in water, were evaluated. All specimens (with the same solid concentration) demonstrate non-Newtonian characteristics and shear-thinning (pseudoplastic) behaviour33; and the apparent viscosity (η, Pa·s) decreases with shear rate (γ, s−1), as demonstrated in Fig. 1e. Such behaviour can be well modelled using the Ostwald-de Wael power law:
where k and n are the consistency and shear-thinning index, respectively34. The empirical parameters of the studied suspensions are summarized in Supplementary Table 1. The apparent viscosity in the MX-C ink is one and two orders of magnitude higher than that of the MX-N ink and PAA/CB-water, respectively. In addition, the viscoelastic properties of the inks, in particular, storage and loss moduli, are important. These can be used to investigate regions of linear elastic deformation, yield points and sample fluidization, and give insight into the energetics of the sample network35. The storage and loss moduli in these viscoelastic materials were plotted as a function of strain, showing much higher storage and loss modulus in MX-C, followed by MX-N and substantially higher than the PAA/CB-water system (Fig. 1f). Such a rheological behaviour in the MXene inks should facilitate the formation of thick Si/MXene electrodes, as will be discussed below.
Electrode fabrication and characterization
Commercial Si powders, namely, nanoscale Si (nSi, CSP = ~3500 mAh g−1, size ~80 nm, Supplementary Fig. 3a) and graphene-wrapped Si (Gr-Si, CSP = ~2000 mAh g−1, superstructure size ~10 µm, Supplementary Fig. 3b–d), were chosen as models for high-capacity materials.
Si powders were ground with MXene aqueous inks to give concentrated, homogenous and viscous slurry, which can be coated onto Cu foil using an industry-compatible slurry-casting technique without adding any polymeric binders or CB (Fig. 2a, Table 2 and Fig. 4). Importantly, the excellent rheological properties of MXene inks, including high viscosity, storage modulus and loss modulus enable a thick coating of the slurry (up to 650 and 2100 µm for the nSi and Gr-Si, respectively, as shown in Fig. 2b and Supplementary Table 3). In the wet slurry, the ultrathin MXene nanosheets distribute randomly and further form a continuous network while wrapping the Si particles. Upon evaporation, the capability of the nanosheet network to assimilate stress and the excellent mechanical strength of MXene nanosheets enable the formation of mechanically robust electrodes36, as shown in Fig. 2c. Indeed, the maximum achievable film thickness is dependent on the viscosity of the MXene ink; increasing the MXene ink concentration (or viscosity) results in thicker films (Supplementary Fig. 5). In other words, the rheological properties of the MXene ink greatly influence the electrode’s structural stability. The surface of the dried electrodes remains smooth with thickness up to ~350 µm before cracking first occurs (Supplementary Table 3), yielding a CCT much larger than the achievable thickness with traditional binders (<100 µm)14,15,17,19,21,22. Top-down and cross-sectional scanning electron microscopy (SEM) images with energy-dispersive X-ray mapping confirm that the nSi particulates are uniformly wrapped by the MX-C skeleton (Fig. 2d, e, Supplementary Fig. 6). No phase changes of the active materials are observed during the slurry processing, as indicated by Raman spectra (Supplementary Fig. 7) and X-ray diffraction (XRD, Supplementary Fig. 8). The nSi/MX-N exhibits a similar porous morphology as that of nSi/MX-C (Supplementary Fig. 9). On the other hand, the Gr-Si/MX-C showcases a hierarchical nano-/macro-structure, in which the Gr-Si pseudo-spherical superstructures (~10 µm) are uniformly coated with robust MX-C nanosheets (Fig. 2f and Supplementary Fig. 10). Such a morphology provides extensive free volume that allows the expansion of the nanoscale Si during the electrochemical processes, which will be discussed below.
Electrical and mechanical characterization
To achieve high thickness and so high C/A, the Si-based anodes should possess high conductivity and mechanical toughness to ensure efficient charge transport and structural stability, respectively37. Previous studies revealed that the electrical conductivity issue becomes more severe in high M/A electrodes, which limit the rate capability of the electrode38. Here we employ MXenes to solve this issue. We performed electrical measurements on a range of Si/MXene electrodes as well as reference samples (see Supplementary Methods). Figure 3a reveals that by adding 30 wt% MXene to the Si, the conductivity has been improved roughly by ×1200 times for the nSi/MX-C (3448 S m−1), ×120 times for the nSi/MX-N (336 S m−1) and ×250 times for the Gr-Si/MX-C (5333 S m−1) compared to their respective traditional systems (nSi/PAA/CB and Gr-Si/PAA/CB with 70:15:15 in weight ratio). The conductivity of nSi/MX-C (70:30, σ = 3448 S m−1) was also much higher than that of nSi/CB/PAA (55:30:15, σ = 9.8 S m−1), nSi/CB/CMC (70:15:15, σ = 2.5 S m−1) and nSi/PEDOT:PSS (70:30, σ = 1909 S m−1), demonstrating the advantage of MXene in enhancing the electrical conductivity of the electrode (Fig. 3a). Moreover, the nSi/MX-C electrode conductivity scales with MX-C mass fraction (Mf) and can be explained in the frame of percolation theory (Supplementary Fig. 11). Importantly, the high electrical conductivity in the nSi/MX-C and Gr-Si/MX-C electrodes can be well maintained upon repeatedly bending even in a twisted configuration (Fig. 3b), indicating the robust nature inherited from the pure MX-C film (Supplementary Fig. 12). We note this is significant as the composite electrodes (nSi/MX-C and Gr-Si/MX-C) combine high M/A, an advanced electron transport network and mechanical flexibility, holding great promise for future wearable power sources.
To further demonstrate the mechanical reinforcement provided by MXene nanosheets, the mechanical properties of Si/MXene composites (such as nSi/MX-C and Gr-Si/MX-C, nSi/MX-N), nSi/PAA/CB as well as pure MXene electrodes (MX-C, MX-N) were evaluated and compared by measuring the stress-strain curves of the corresponding vacuum-filtrated films. This is justified by the roughly similar morphologies of the samples fabricated by the two methods (Supplementary Fig. 13). The tensile toughness (area under the stress-strain curve) is of particular interest and has been improved by ×40 and ×15 in the nSi/MX-C and Gr-Si/MX-C, respectively from the traditional electrode (nSi/PAA/CB) at the equivalent composition (Si Mf = 70 wt%), as shown in Fig. 3c, d. Even though the toughness and Young’s modulus in the Si/MXene composites are lower than the pure MXene films, as expected they are higher than the traditional binder system. This allows a substantial improvement of the CCT, whose magnitude depends on the mechanical properties of the deposited materials24. Consequently, mechanically robust electrodes with thickness up to 350 µm for the Gr-Si/MX-C are produced. This is much higher than the achievable thickness in the traditional binder systems. In addition, it’s worth noting that the dried composite films cannot be peeled off from the Cu substrate, indicative of a strong adhesion force in the Cu/composite interface.
We note that other 2D conductive binders, in particular graphene, graphene oxide and reduced graphene oxide, typically suffer from either low ink concentration39,40, or poor mechanical strength of the network41, or un-scalable, lengthy procedures42,43,44, which greatly limit the achievable electrode mass loadings and areal capacities44. The superiority of concentrated MXene aqueous inks over traditional dual-component electrode additives can be attributed to the excellent electrical and mechanical properties of MXene nanosheets as well as the high ink viscosity. As a result, a simple slurry-casting technique leads to the formation of extremely thick electrodes free from any other post-treatments or complicated procedures. In the Si/MXene electrodes, the metallic conductivity of both MX-C and MX-N enables fast electron transport45, and thus allows reversible electrochemical reactions and high-rate performance. Furthermore, the continuous MXene network results in effective mechanical reinforcement, allowing the production of thick electrodes and potentially preserving the structural integrity of the entire electrode upon cycling. This means that the dual-functionalized MXene network should render the Si/MXene composites with good Li+ storage performance, as discussed below.
Electrochemical characterization of nSi/MXene anodes
We begin by investigating the electrochemical responses of nSi/MX-C electrodes. The dQ/dV and galvanostatic charge-discharge (GCD) profiles of nSi/MX-C electrodes (with various compositions) indicate curves that are typical for Si (Supplementary Fig. 14a and Fig. 15a–e). All electrodes show a high first Coulombic efficiency (CE) of 81–84% (Supplementary Fig. 14b). The specific capacity per nSi mass (C/MSi) at different current densities suggests that by adding 30 wt% MX-C conductive binder, both the rate capability (Fig. 4a) and Si electrochemical utilization are maximized, approaching the theoretical capacity (dashed line, nSi = ~3500 mAh g−1, Supplementary Fig. 16). Therefore, 30 wt% MXene was chosen in all Si/MXene composites. To probe the potentially achievable capacities of nSi, asymmetric charging-discharging was performed on the nSi/MX-C (Mf = 30 wt%, MSi/A = 0.9 mg cm−2); the composite was lithiated slowly (1/20 C) then delithiated at different rates (from 1/20 to 1 C). Figure 4b shows representative asymmetric GCD curves with specific capacities presented in the inset. Almost theoretical values are achieved and maintained up to 5 A g−1, suggesting that the high-rate response is enabled by the MX-C conductive network. Such an efficient continuous network also facilitates the production of high MSi/A electrodes (Fig. 4c, left panel and Supplementary Fig. 17), resulting in a C/A as high as 12.2 mAh cm−2 (Fig. 4c, right panel). The C/A of nSi/MX-C electrodes scales linearly with MSi/A over the entire thickness regime, leading to high C/MSi (~3200 mAh g−1, dashed line) agreeing quite well with Fig. 4b. This indicates that even in the high MSi/A electrodes, almost theoretical capacities have been achieved due to the presence of MX-C conductive binder.
The cycling stabilities of nSi/MX-C electrodes with various MSi/A were measured at 0.3 A g−1 (Fig. 4d). While the high MSi/A electrode shows a relatively rapid capacity decay, reasonably stable capacities are achieved in the electrodes with low-medium range MSi/A (Fig. 4d and Supplementary Fig. 18). For example, the capacity retention in the MSi/A = 0.9 mg cm−2 is 84% after 50 cycles, in sharp contrast to 50% in the nSi/CB/PAA (70:15:15, MSi/A = 0.8 mg cm−2, Fig. 4d). The nSi/MX-C also outperforms other Si/conductive agent/binder electrodes, such as nSi/CB/CMC (70:15:15), nSi/PEDOT:PSS (70:30) and nSi/graphene (70:30) in cycling performance at a similar MSi/A (Fig. 4d and Supplementary Fig. 19). While the phase separation of Si from CB and/or PAA occurs upon repeated volume expansion/contraction. MXene nanosheets well wrap the Si particles, forming a point-to-plane contact and improving the electrochemical performance, unlike the point-to-point contact between the nSi and CB particles. The MXene skeleton conformally attaches to Si particles during repeated expanding/shrinking of the latter, which guarantees a better electron transport path, as demonstrated in Supplementary Fig. 20. Post-cycling SEM images suggest that the continuous MX-C scaffold has been preserved in the medium MSi/A electrode (Fig. 4e and Supplementary Fig. 21) but is disrupted in the high MSi/A electrode due to the large volume change (Supplementary Fig. 22). The degradation of Li metal inside the cell is also part of the reason for the relatively poor cyclability of the MSi/A = 3.8 mg cm−2 electrode (see Supplementary Fig. 22b). To further study the long-term stability of the MSi/A = 0.9 mg cm−2 electrode, a rapid charge/discharge rate was applied. The reasonable stability, coupled with high CE over 280 cycles (Fig. 4f and Supplementary Fig. 23a), can be credited to the synergistic effect between the high-capacity Si particles and the continuous MX-C network. Such a synergistic effect is not confined to MX-C; indeed any other viscous ink composed of concentrated, conductive MXene nanosheets should work as an efficient conductive binder. As a quick example, the nSi/MX-N anode delivers an initial capacity of 1602 mAh g−1 at 1.5 A g−1 and maintains 1106 mAh g−1 after 70 cycles (Fig. 4f and Supplementary Fig. 23b). The inferior cycling performance of nSi/MX-N anode can be possibly attributed to its lower fracture energy (toughness) compared to that of nSi/MX-C (Fig. 3d), by which the latter can assimilate the stress/tension induced by Si volume changes more efficiently. Moreover, the less thermodynamically stable and less conductive MX-N network is more prone to degradation. Despite that the cycling performance of nSi/MXene electrodes are quite comparable to other reported Si/conductive binder systems, as seen in Supplementary Table 4.
Performance of Gr-Si/MX-C anode
To further improve the electrode M/A, and thus C/A, we used microsized Gr-Si particles as active materials. GCD profiles (Fig. 5a and Supplementary Fig. 24a–d) of Gr-Si/MX-C electrodes with various compositions reveal typical curves for Si46. The first CE in these electrodes is reasonably high (81–83%, Supplementary Fig. 24e), suggesting the lithiation/delithiation processes are reversible. The rate performance suggests that 30 wt% MX-C is capable of maximizing the specific capacity at various current densities (Supplementary Fig. 25). In addition, increasing the MX-C Mf gradually not only boosts the utilization of Gr-Si to the theoretical value (CSP = ~2000 mAh g−1, the dashed line in Supplementary Fig. 25c) but will also dramatically improve the mechanical properties of the electrode, according to previous findings on carbon nanotubes37. Thus, Gr-Si/MX-C electrodes, with MGrSi/A ranging from 1.3 to 13 mg cm−2, were fabricated at a constant composition (MX-C Mf = 30 wt%). The first GCD profiles of these Gr-Si/MX-C electrodes are shown in Fig. 5b, suggesting a high first CE (81–83%). The C/A values scale linearly with MGrSi/A and give a specific capacity per Gr-Si (C/MGrSi) as high as 1850 mAh g−1. The cycling performance of these electrodes is also MGrSi/A-dependent, being fairly stable in the MGrSi/A = 3.3 mg cm−2 electrode (C/A = ~5 mAh cm−2, Fig. 5c) while less stable in the MGrSi/A = 13 mg cm−2 electrode. This sharp discrepancy can be majorly attributed to the non-infinite supply of Li as well as the possible disruption of the MX-C continuous network in the thick electrode (Supplementary Fig. 26). On the other hand, intact MX-C nanosheets are well preserved and uniformly cover the Gr-Si superstructures in the MGrSi/A = 3.3 mg cm−2 electrode, as demonstrated in Fig. 5d, e.
Comparison with published data
To demonstrate the advantage of high areal capacity Si/MXene composites for high-energy Li-ion batteries, we compared the C/A in this work to other reported Si/conductive-binder systems. The C/A of Si/MXene composites exceeds the literature results, which are generally lower than 4 mAh cm−2 (Fig. 5f and Supplementary Table 4)14,17,18,20,21,22. The C/A of reported Si/conductive-binder systems is typically limited by the MActive/A (<2 mg cm−2). Even with a high MActive/A (~4 mg cm−2), graphite-Si/conductive-binder electrodes display a much lower C/A than the results reported here due to the excessive graphite content in the electrodes21,47. The ultrahigh C/A of the Si/MXene electrodes can be attributed to the advanced electrode architecture; (1) the viscous nature of the MXene aqueous ink enables the formation of thick composite electrodes (thus high MAcitve/A) using a simple/scalable manufacturing process; (2) the high aspect ratio and metallic conductivity of MXene nanosheets endow the composite electrodes with mechanical robustness, high strength and excellent conductivity, facilitating fast electron transport; (3) the continuous MXene scaffold efficiently accommodates the volume change and stress induced by the Si lithiation/delithiation, and boosts the utilization of active materials. Indeed, the thickness changes are ~34% in nSi/MX-C and ~20% in Gr-Si/MX-C, suggesting 30 wt% of the MX-C nanosheet network has effectively accommodated the volume change induced by 70 wt% of Si particles (Supplementary Fig. 27).
We note that producing high MActive/A electrodes is of technological significance; it not only delivers a higher C/A to the electrode but also decreases the mass portion of inactive components, such as current collector (Cu foil for anode side) and separator. Consequently, the cell-level performance of the anode, which includes the mass of Cu foil (MCu-foil/A = 9 mg cm−2), electrode and half of the separator (MSeparator/A = 2 mg cm−2), can be improved significantly (Fig. 5g). Taking this into consideration, we calculated the true performance of our electrodes along with other reported Si/conductive-binder systems according to:
The C/MTotal was plotted versus the corresponding MActive/A, as shown in Fig. 5h. This comparison clearly suggests that our electrodes exhibit much higher specific capacities on the cell level, highlighting the advantages of MXene viscous inks over other conductive binders. For example, the nSi/MX-C electrode showcases a C/MTotal = 790 mAh g−1 at MSi/A = 3.8 mg cm−2, while the Gr-Si electrode demonstrates 815 mAh g−1 at MGrSi/A = 13 mg cm−2. Importantly, our results are quite close to the theoretical limit (dashed lines in Fig. 5h) for all samples, indicating that almost full utilization of Si active materials has been reached at our highest MAcrive/A electrode. Moreover, the shape of the Gr-Si/MX-C electrode is instructive; the theoretical curve (blue dashed line) nearly saturates at high MGrSi/A > 14 mg cm−2. In other words, even if we further increase the electrode thickness, the C/MTotal of the Gr-Si/MX-C anode will only increase marginally. This means that the electrode architecture has allowed us to reach the absolute maximum C/MTotal possible for the Gr-Si material used.
In summary, the efficient utilization of 2D MXene nanosheets as a new class of conductive binder for high volume-change Si electrodes is of fundamental importance to the electrochemical energy storage field. The continuous network of MXene nanosheets not only provides sufficient electrical conductivity and free space for accommodating the volume change issue but also well resolves the mechanical instability of Si. Therefore, the combination of viscous MXene ink and high-capacity Si demonstrated here offers a powerful technique to construct advanced nanostructures with exceptional performance. Of equal importance is that the formation of these high-mass-loading Si/MXene electrodes can be achieved by means of a commercially compatible, slurry-casting technique, which is highly scalable and low cost, allowing for large-area production of high-performance, Si-based electrodes for advanced batteries. Considering that more than 30 MXenes are already reported, with more predicted to exist, there is certainly much room for further improving the electrochemical performance of such electrodes by tuning the electrical, mechanical and physicochemical properties of this exciting 2D MXene family.
MXene ink preparation
MXene viscous ink was prepared as follows: 15 mL of deionized (DI) water was added to the as-etched, multilayered MXene (Ti3C2Tx or Ti3CNTx), followed by vigorous shaking by hand/vortex machine for 15 min. Then the mixture was centrifuged at 3500 rpm for 30 min. The top 80% supernatant was collected and centrifuged at 5000 rpm for 30 min. After decanting the supernatant, the sediment was re-dispersed in 15 mL of DI water by vigorous shaking for 10 min, resulting in viscous MXene ink denoted as MX-C (Ti3C2Tx) and MX-N (Ti3CNTx), respectively. A detailed description of the preparation of multilayered MXenes can be found in Supplementary Methods.
Electrodes were prepared via a slurry-casting method using MXene viscous aqueous ink without the addition of any other conductive additives or polymeric binder. Typically, nanosized silicon powders, nSi, (or graphene-wrapped Si, Gr-Si, Angstron Materials) were mixed with MX-C ink and ground into a uniform slurry before casting onto Cu foil using a doctor blade. After drying at ambient conditions for 2 h, electrodes were punched (12 mm in diameter) and vacuum-dried at 60 °C for 12 h to remove residual water. The MXene Mf in the electrodes (ranging from 5 to 40 wt%) was controlled by changing the mass ratio of Si powders to MXene during the slurry preparation. In addition, electrodes with different mass loadings (M/A) were obtained by changing the height of doctor blade (150–2100 µm) when casting a slurry with 30 wt% of MXene. The resultant electrodes possessed various thicknesses and thus various mass loadings and were denoted as nSi/MX-C (or Gr-Si/MX-C). We also similarly fabricated nSi/MX-N electrodes by mixing nSi powder with the MX-N viscous aqueous ink. The mass fraction of MX-N Mf in the electrodes was 30 wt%. Detailed compositions and thicknesses of the Si/MXene electrodes can be found in Supplementary Tables 2 and 3, respectively (Supplementary Methods).
The rheological properties of MXene inks, as well as the reference sample, were studied on the Anton Paar MCR 301 rheometer. Morphologies and microstructure of the Si/MXene electrodes were examined by SEM, Raman spectroscopy and XRD. The electrical conductivity of the electrodes was measured using a four-point probe technique. The mechanical properties of the electrodes were measured on a Zwick Z0.5 Pro-Line Tensile Tester (100N Load Cell). A detailed description of characterization can be found in Supplementary Methods.
The electrochemical performance of the Si/MXene electrodes was evaluated in the half-cell configuration (2032-type, MTI Corp.). The coin cells were assembled inside an Ar-filled glove box with Si/MXene paired with Li metal disc. A unit of 1 M lithium hexafluorophosphate (LiPF6) in ethylene carbonate/diethyl carbonate/fluoroethylene carbonate (3:6:1 in v/v/v, BASF) was selected as the electrolyte. GCD tests were performed within 0.005–1.2 V on a potentiostat (VMP3, BioLogic). For the post-mortem analysis, the cycled cells were carefully disassembled inside the glove box and rinsed with dimethyl carbonate. A detailed description of the electrochemical characterization can be found in Supplementary Methods.
The data sets generated during and/or analyzed during the current study are available from the corresponding authors on reasonable request.
Wang, X. et al. High-density monolith of N-doped holey graphene for ultrahigh volumetric capacity of Li-ion batteries. Adv. Energy Mater. 6, 1502100 (2016).
Zhang, C. J. et al. Enabling flexible heterostructures for Li-ion battery anodes based on nanotube and liquid-phase exfoliated 2D gallium chalcogenide nanosheet colloidal solutions. Small 13, 1701677 (2017).
Zhang, C. J. et al. Liquid exfoliation of interlayer spacing-tunable 2D vanadium oxide nanosheets: High capacity and rate handling Li-ion battery cathodes. Nano Energy 39, 151–161 (2017).
Zhang, C. J. et al. Layered orthorhombic Nb2O5@Nb4C3Tx and TiO2@Ti3C2Tx hierarchical composites for high performance Li-ion batteries. Adv. Funct. Mater. 26, 4143–4151 (2016).
Liu, Y. et al. Liquid phase exfoliated MoS2 nanosheets percolated with carbon nanotubes for high volumetric/areal capacity sodium-ion batteries. ACS Nano 10, 8821–8828 (2016).
Hu, L. et al. Thin, flexible secondary Li-ion paper batteries. ACS Nano 4, 5843–5848 (2010).
Poizot, P., Laruelle, S., Grugeon, S., Dupont, L. & Tarascon, J. M. Nano-sized transition-metal oxides as negative-electrode materials for lithium-ion batteries. Nature 407, 496–9 (2000).
Zheng, H., Jiang, K., Abe, T. & Ogumi, Z. Electrochemical intercalation of lithium into a natural graphite anode in quaternary ammonium-based ionic liquid electrolytes. Carbon 44, 203–210 (2006).
Abellán, P. et al. Probing the degradation mechanisms in electrolyte solutions for Li-ion batteries by in situ TEM. Nano Lett. 14, 1293–1299 (2014).
Gogotsi, Y. What nano can do for energy storage. ACS Nano 8, 5369–71 (2014).
Zhang, C. J. et al. Synthesis and electrochemical properties of niobium pentoxide deposited on layered carbide-derived carbon. J. Power Sources 274, 121–129 (2015).
Du, F. et al. Environmental friendly scalable production of colloidal 2D titanium carbonitride MXene with minimized nanosheets restacking for excellent cycle life lithium-ion batteries. Electrochim. Acta 235, 690–699 (2017).
Nitta, N., Wu, F., Lee, J. T. & Yushin, G. Li-ion battery materials: present and future. Mater. Today 18, 252–264 (2014).
Wu, M. et al. Toward an ideal polymer binder design for high-capacity battery anodes. J. Am. Chem. Soc. 135, 12048–12056 (2013).
Higgins, T. M. et al. A commercial conducting polymer as both binder and conductive additive for silicon nanoparticle-based lithium-ion battery negative electrodes. ACS Nano 10, 3702–3713 (2016).
Wu, H. et al. Stable Li-ion battery anodes by in-situ polymerization of conducting hydrogel to conformally coat silicon nanoparticles. Nat. Commun. 4, 1943 (2013).
Xun, S., Xiang, B., Minor, A., Battaglia, V. & Liu, G. Conductive polymer and silicon composite secondary particles for a high area-loading negative electrode. J. Electrochem. Soc. 160, A1380–A1383 (2013).
Kim, S.-M. et al. Poly(phenanthrenequinone) as a conductive binder for nano-sized silicon negative electrodes. Energy Environ. Sci. 8, 1538–1543 (2015).
Wu, M. et al. Manipulating the polarity of conductive polymer binders for Si-based anodes in lithium-ion batteries. J. Mater. Chem. A 3, 3651–3658 (2015).
Chen, Z. et al. A three-dimensionally interconnected carbon nanotube-conducting polymer hydrogel network for high-performance flexible battery electrodes. Adv. Energy Mater. 4, 1400207 (2014).
Zhao, H. et al. Conductive polymer binder for high-tap-density nanosilicon material for lithium-ion battery negative electrode application. Nano Lett. 15, 7927–7932 (2015).
Park, S. J. et al. Side-chain conducting and phase-separated polymeric binders for high-performance silicon anodes in lithium-ion batteries. J. Am. Chem. Soc. 137, 2565–2571 (2015).
Magasinski, A. et al. Toward efficient binders for Li-ion battery Si-based anodes: Polyacrylic acid. ACS Appl. Mater. Interfaces 2, 3004–3010 (2010).
Du, Z. et al. Enabling aqueous processing for crack-free thick electrodes. J. Power Sources 354, 200–206 (2017).
Anasori, B. et al. Two-dimensional, ordered, double transition metals carbides (MXenes). ACS Nano 9, 9507–9516 (2015).
Naguib, M. et al. Two-dimensional transition metal carbides. ACS Nano 6, 1322–31 (2012).
Anasori, B., Lukatskaya, M. R. & Gogotsi, Y. 2D metal carbides and nitrides (MXenes) for energy storage. Nat. Rev. Mater. 2, 16098 (2017).
Naguib, M. et al. Two-dimensional nanocrystals produced by exfoliation of Ti3AlC2. Adv. Mater. 23, 4248–53 (2011).
Zhang, C. J. et al. Oxidation stability of colloidal two-dimensional titanium carbides (MXenes). Chem. Mater. 29, 4848–4856 (2017).
Zhang, C. et al. Synthesis and charge storage properties of hierarchical niobium pentoxide/carbon/niobium carbide (MXene) hybrid materials. Chem. Mater. 28, 3937–3943 (2016).
Lipatov, A. et al. Effect of synthesis on quality, electronic properties and environmental stability of individual monolayer Ti3C2 MXene flakes. Adv. Electron. Mater. 2, 1600255 (2016).
Alhabeb, M. et al. Guidelines for synthesis and processing of two-dimensional titanium carbide (Ti3C2Tx MXene). Chem. Mater. 29, 7633–7644 (2017).
Zhang, C. et al. Highly porous carbon spheres for electrochemical capacitors and capacitive flowable suspension electrodes. Carbon 77, 155–164 (2014).
Hatzell, K. B. et al. Composite manganese oxide percolating networks as a suspension electrode for an asymmetric flow capacitor. ACS Appl. Mater. Interfaces 6, 8886–8893 (2014).
Barwich, S., Coleman, J. N. & Möbius, M. E. Yielding and flow of highly concentrated, few-layer graphene suspensions. Soft Matter 11, 3159–3164 (2015).
Lipatov, A. et al. Elastic properties of 2D Ti3C2Tx MXene monolayers and bilayers. Sci. Adv. 4, eaat0491 (2018).
Liu, Y. et al. Electrical, mechanical and capacity percolation leads to high performance MoS2/nanotube composite lithium ion battery electrodes. ACS Nano 10, 5980–5990 (2016).
Ling, Z. et al. Quantifying the role of nanotubes in nano:nano composite supercapacitor electrodes. Adv. Energy Mater. 8, 1702364 (2017).
Paton, K. R. et al. Scalable production of large quantities of defect-free few-layer graphene by shear exfoliation in liquids. Nat. Mater. 13, 624–30 (2014).
Varrla, E. et al. Turbulence-assisted shear exfoliation of graphene using household detergent and a kitchen blender. Nanoscale 6, 11810–11819 (2014).
Shan, C. et al. Graphene oxides used as a new “dual role” binder for stabilizing silicon nanoparticles in lithium-ion battery. ACS Appl. Mater. Interfaces 10, 15665–15672 (2018).
Zhang, W. et al. Facile synthesis of binder-free reduced graphene oxide/silicon anode for high-performance lithium ion batteries. J. Power Sources 312, 216–222 (2016).
Botas, C., Carriazo, D., Zhang, W., Rojo, T. & Singh, G. Silicon-reduced graphene oxide self-standing composites suitable as binder-free anodes for lithium-lon batteries. ACS Appl. Mater. Interfaces 8, 28800–28808 (2016).
Zhou, M. et al. High-performance silicon battery anodes enabled by engineering graphene assemblies. Nano Lett. 15, 6222–6228 (2015).
Zhang, C. J. et al. Transparent, flexible, and conductive 2D titanium carbide (MXene) films with high volumetric capacitance. Adv. Mater. 29, 1702678 (2017).
Choi, S., Kwon, T., Coskun, A. & Choi, J. W. Highly elastic binders integrating polyrotaxanes for silicon microparticle anodes in lithium ion batteries. Science 357, 279–283 (2017).
Zhao, H., Du, A., Ling, M., Battaglia, V. & Liu, G. Conductive polymer binder for nano-silicon/graphite composite electrode in lithium-ion batteries towards a practical application. Electrochim. Acta 209, 159–162 (2016).
The authors acknowledge the SFI-funded AMBER research centre (SFI/12/RC/2278) and the Advanced Microscopy Laboratory for the provision of their facilities. We thank Joao Coelho for performing the XRD tests, Hannah Nerl for TEM imaging and Dermot Daly for SEM discussion. J.N.C. thanks Science Foundation Ireland (SFI, 11/PI/1087) for funding. V.N. thanks the European Research Council (StG 2DNanocaps and 3D2D print) and Science Foundation Ireland (PIYRA) for funding. We also acknowledge Prof. Patrice Simon, Dr. Patrick Rozier and Dr. Zifeng Lin (CIRIMAT, Université de Toulouse, Toulouse Cedex 9, France), and Prof. Matthias E. Möbius (Trinity College Dublin, Ireland) for the useful discussions. We also thank the support from SFI I-Form centre.
The authors declare no competing interests.
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Zhang, C.(., Park, SH., Seral‐Ascaso, A. et al. High capacity silicon anodes enabled by MXene viscous aqueous ink. Nat Commun 10, 849 (2019). https://doi.org/10.1038/s41467-019-08383-y
This article is cited by
Nature Communications (2023)
Journal of Electronic Materials (2023)
Nature Reviews Materials (2022)
Nature Communications (2022)
Nature Reviews Chemistry (2022)