Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Design and application of volatilizable solid additives in non-fullerene organic solar cells


Most of the high-performance organic solar cells are fabricated with the assistance of high-boiling-point solvent additives to optimize their charge transport properties; this has adverse effects on the OSCs’ stability and reproducibility in large-scale production. Here, we design volatilizable solid additives by considering the molecular structure feature of an acceptor–donor–acceptor-type non-fullerene acceptor. The application of solid additives can enhance the intermolecular π–π stacking of the non-fullerene acceptor and thus facilitate the charge transport properties in the active layers, leading to improved efficiencies of OSCs. Importantly, devices fabricated using volatilizable solid additives exhibit higher stability and reproducibility when compared with the OSCs processed with solvent additives. Our results not only demonstrate an approach of applying volatilizable solid additives to benefit the large-scale production of OSCs but also provide a potential direction for designing specific solid additives for different active layers.


Organic solar cells (OSCs) have desirable advantages in that they are low cost, flexible and lightweight1,2,3,4, and their power conversion efficiencies (PCEs) have rapidly increased in recent years5,6,7,8,9. As charge generation, transport and recombination in bulk-heterojunction (BHJ) OSCs are highly dependent on the nanoscale morphology of active layers, a few processing methods such as use of solvent additives and thermal/vapor annealing were developed to control the blend morphology. Solvent additives such as 1,8-diiodooctane (DIO)10,11, diphenyl ether12 and 1-phenylnaphthalene13 have dominant advantages for improving photovoltaic performance but have been shown to be unfavorable for the devices’ stability and reproducibility14,15,16,17,18.

Recently, non-fullerene (NF) acceptors, especially small molecular acceptors comprising acceptor–donor–acceptor (A–D–A) structures, have gradually replaced fullerene acceptors, with PCEs above 13% having been achieved19,20,21,22,23,24,25. Unlike fullerene derivatives, the A–D–A acceptors have planar conjugated backbones and bulky alkyl chains substituted on their central units. Since the side chains have strong steric hindrance to impede ordered intermolecular stacking, the π-orbital overlaps, which offer charge transport channels, are mainly formed between the terminal groups of two adjacent A–D-A molecules26,27. In addition to considering the phase separation, domain size and purity in active layers, enhancing the intermolecular π-π stacking morphology is crucial to the facilitation of charge transport for A–D–A acceptors. Presently, the morphology optimization of NF-based blend films empirically follows the methods originally developed in fullerene-based blends, and both the advantages and disadvantages of the latter have been inherited. Considering the unique intermolecular packing features of the A–D–A acceptors, exploring a method that optimizes blend morphology while maintaining good device stability and reproducibility is crucial for further development of OSCs.

Herein, we present a method of directly enhancing the intermolecular π–π interaction by introducing volatilizable solid additives (SAs) in NF OSCs. We synthesize SA-1 with a similar chemical structure to that of the end-groups of an A–D–A acceptor IT-4F25. A film casted from the solution of equimolar IT-4F and SA-1, in which SA-1 volatilizes after thermal annealing (TA) at 140 °C, exhibits enhanced π–π stacking, leading to significantly improved electron mobility in comparison to the IT-4F film processed without SA-1. In OSC devices based on a fluorinated conjugated polymer (PBDB-TF) and IT-4F, the addition of SA-1 contributes to the optimization of the morphology of active layers, leading to the PCE increasing from 12.2 to 13.8%, which is comparable to the results using DIO as an additive28. More attractively, the devices processed with SA-1 show good tolerance to thickness variation of the active layer and exhibited good reproducibility and stability. We propose a working mechanism for this kind of additives by applying seven analogues of SA-1 with different volatility in NF OSCs. Furthermore, we have shown that the application of SA-1 can effectively improve the photovoltaic performance of NF OSCs based on different active layers.


Design, synthesis and characterization of the solid additives

As illustrated in Fig. 1a, we designed eight SA-x (x = 1 to 8) to have similar chemical structures to those of the end-groups of IT-4F, expecting that the SA-x had good miscibility with IT-4F molecules. The SA-x can be easily synthesized by some low-cost compounds through the Knoevenagel condensation reaction (Supplementary Note 1) and have good solubility in commonly used solvents such as dichloromethane, chloroform and chlorobenzene. We measured the fundamental physicochemical properties of the SA-x by taking SA-1 as an example. As illustrated in Supplementary Fig. 1, in chloroform solution, SA-1 exhibits an absorption peak at 370 nm with an extinction coefficient of 3.1 × 104 M−1 cm−1. The molecular configurations and molecular energy levels of SA-1 are calculated by density functional theory (DFT) and provided in Supplementary Figs 2 and 3.

Fig. 1

Chemical structures. a Chemical structures of eight designed solid additives, SA-x. b Chemical structures of the polymer donor PBDB-TF and the acceptor IT-4F

Application of SA-1 as an SA in OSCs

OSC devices were fabricated using a conventional device structure of indium tin oxide/poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate)/PBDB-TF29: IT-4F/poly[(9,9-bis(3′-((N,N-dimethyl)-N-ethylammonium)-propyl)-2,7-fluorene)-alt-2,7-fluorene)-alt-2,7-(9,9-dioctylfluorene)]dibromide (PFN-Br)30/Al, where the PBDB-TF and IT-4F (their molecular structures are illustrated in Fig. 1b) work as a donor and an acceptor, respectively. Different amounts of SA-1 were added into the solution of PBDB-TF:IT-4F before film coating. Thermal annealing of the active film at 140 °C for 10 min was performed after the film coating. Detailed experimental procedures are provided in the methods section.

We first fabricated the PBDB-TF:IT-4F-based device processed without any additive, which exhibits a maximum PCE of 12.2% with an open-circuit voltage (Voc) of 0.89 V, a short-circuit current density (Jsc) of 19.0 mA cm−2, and a fill factor (FF) of 0.72 (Fig. 2a and Table 1). When the mole ratio of IT-4F:SA-1 was drastically changed from 1:0.05 to 1:3, as shown in Fig. 2b and summarized in Supplementary Table 1, both the Jsc and FF first rose and then descended, whereas the Voc decreases with an increase in SA-1 content and the corresponding JV and EQE curves are plotted in Supplementary Fig. 4. As a result, the optimal device was obtained when 17.3 wt.% SA-1 was used with respect to IT-4F (the mole ratio of IT-4F:SA-1 was 1:1); it had a Jsc of 20.6 mA cm−2, an FF of 0.77 and a Voc of 0.87 V, leading to a very good PCE of 13.8%. It should be noted that all the devices had over 13% PCEs when the weight ratio of SA-1 ranged from 8 to 25 wt.%. Fig. 2c displays the external quantum efficiency (EQE) curves of the device processed without additives and the optimal device. It is very clear that the addition of SA-1 leads to the enhancement of EQE values in the region of 400–800 nm, especially in 500–750 nm, thereby contributing to the improved Jsc. The calculated integral current densities are 18.7 and 20.1 mA cm−2 for the devices processed with or without SA-1, respectively; these results are in good agreement with the Jsc values obtained from the JV measurements.

Fig. 2

Device performance. a JV curves and the histogram of PCE for PBDB-TF:IT-4F-based devices with/without SA-1. Thermal annealing of the active films at 140 °C for 10 min was performed. b Device parameters of PBDB-TF:IT-4F devices as a function of the mole ratios of IT-4F:SA-1 or the weight ratio of SA-1 incorporated into the casting solution (error bars show standard deviation from the mean). c EQE curves of the corresponding devices. d PCEs of the devices based on PBDB-TF:IT-4F processed with or without SA-1 under various active layer thicknesses (the horizontal error bars represent the standard deviation of the thicknesses and the vertical error bars show standard deviation from the mean). e, the thermal stability of OSC devices processed with or without SA-1 (error bars show standard deviation from the mean). f The long-term storage stability of OSC devices processed with or without SA-1 (error bars show standard deviation from the mean)

Table 1 The effect of SA-1 on the photovoltaic parameters of devices based on different active layers

Then, we fabricated the optimal OSCs with active layer thicknesses varying from 100 to 400 nm and studied the impact of the SA-1 on the device stability. As illustrated in Fig. 2d and Supplementary Table 2, when the thickness increased to approximately 400 nm, the PCEs of OSCs fabricated without using SA-1 sharply dropped to 6.9% while PCEs above 12% remained for the OSCs fabricated by including SA-1, which will benefit the large-scale fabrication of OSCs through roll-to-roll printing technology12,31,32. Furthermore, we investigated the long-term thermal stability of the optimal OSCs. As demonstrated in Fig. 2e, after 300 h of annealing at 140 °C, the devices fabricated with SA-1 yielded PCEs of around 11.5%, while those processed without SA-1 had PCEs lower than 10%. We also studied the long-term storage stability of the devices (encapsulated in a N2-filled glovebox), and PCEs of 12.5% were maintained after storage for 1500 h (Fig. 2f). These results suggest that the use of SA-1 in the active layer not only enhances the device’s photovoltaic performance but also provides benefits of good long-term thermal and storage stability.

To clarify the effect of TA, we fabricated the as-cast PBDB-TF:IT-4F and PBDB-TF:IT-4F+SA-1 devices for comparison. As demonstrated in Supplementary Fig. 5, the as-cast device exhibits a PCE of 11.6%, a Jsc of 18.7 mA cm−2 and an FF of 0.69. When 17.3 wt.% SA-1 was added, the PBDB-TF:IT-4F-based device without TA shows a lower PCE of 11.1% with a Jsc of 20.2 mA cm−2 and an FF of 0.61. The photovoltaic parameters of SA-1 processed devices under different TA temperatures were also investigated (Supplementary Table 4).

We ascribed the simultaneous enhancement of Jsc and FF in OSCs to the improved charge transport properties in the blend films processed with SA-1. Therefore, we first measured the electron mobilities of blend films through the space charge limited current (SCLC) method33 with an electron-only device structure. As showed in Supplementary Fig. 6a and summarized in Supplementary Table 5, the electron mobility of the IT-4F+SA-1/TA film is 1.4 × 10−3 cm2 V−1 s−1, which is approximately one order of magnitude higher than that of the IT-4F/TA film (2.0 × 10−4 cm2 V−1 s−1). The electron mobilities of the PBDB-TF:IT-4F blend films with different treatments were also measured. The electron mobility of as-cast film shows no obvious improvement after adding SA-1, while the electron mobility of SA-1-added film was improved from 1.4 × 10−4 to 1.3 × 10−3 cm2 V−1 s−1 after TA. Photo-induced charge-carrier extraction in linearly increasing voltage (photo-CELIV) measurements were also conducted34. The photo-CELIV mobility (Supplementary Fig. 6d) of PBDB-TF:IT-4F+SA-1/TA film (1.2 × 10−4 cm2 V−1 s−1) is also higher than both the PBDB-TF:IT-4F+SA-1 film (6.8 × 10−5 cm2 V−1 s−1) and the PBDB-TF:IT-4F/TA film (7.6 × 10−5 cm2 V−1 s−1). Furthermore, compared with those of the device processed without SA-1, the bimolecular recombination was more suppressed in the SA-1-processed device (Supplementary Fig. 7).

Influence of SAs on blend morphology

As is known, the optical properties of organic semiconductors have a strong connection with the aggregation behavior in solid films35,36. First, as depicted in Fig. 3a, the UV-vis absorption spectra of the films at different conditions were measured. When comparing the SA-1-added and the SA-1-added/TA films, the characteristic absorption peaks of SA-1 in shortwave region vanish after TA. For the polymer PBDB-TF/TA film, the use of SA-1 affects the absorption coefficient slightly. For the IT-4F+SA-1/TA film, the absorption peak red-shifts about 14 nm with increased absorption coefficient approximately 7% when compared with the as-cast IT-4F film, which should be ascribed to the enhanced intermolecular π–π interaction of IT-4F. Detailed optical properties of PBDB-TF, IT-4F and blend films under different treatments are summarized in Supplementary Table 6. As exhibited in Fig. 3b, a similar phenomenon can be observed in the PBDB-TF:IT-4F-based blend film, i.e. that SA-1 has the obvious effect of enhancing intermolecular ππ interaction on IT-4F rather than the polymer donor.

Fig. 3

The influence of SA-1 on the intermolecular interaction and the film morphology. Absorption spectra with absorption coefficients of (a) PBDB-TF, PBDB-TF/TA, PBDB-TA+SA-1, and PBDB-TF+SA-1/TA films; b IT-4F, IT-4F/TA, IT-4F+SA-1, and IT-4F+SA-1/TA films; c blend, blend/TA, blend+SA-1, and blend+SA-1/TA films. d The corresponding X-ray diffraction patterns and that of SA-1 film without TA. e The corresponding AFM height images  (A specified scale bar is used for the image of PBDB-TF+SA-1 film)

Then, we measured the X-ray diffraction (XRD) patterns of the donor, acceptor, and the blend films processed with different conditions. As indicated in Fig. 3c, the diffraction peaks of the SA-1 film made through the solution process are sharp and intense, indicating that SA-1 has high crystallinity. The annealed IT-4F film processed without SA-1 (blue line) exhibits two weak diffraction peaks at 2-Theta of 5.5° and 26°, corresponding to a d100-spacing value of 15.9 Å and a d010-spacing value of 3.4 Å, which are stronger than those of the as-cast IT-4F film (black line). By adding an equimolar ratio of SA-1 into the solution for making the IT-4F film, the characteristic diffraction peaks of SA-1 cannot be distinguished, suggesting that it is well miscible with IT-4F. Interestingly, the d010 peak of IT-4F, which should be ascribed to intermolecular π–π interaction, can be significantly enhanced in the IT-4F+SA-1/TA film. For the blend film, the use of SA-1 also enhances the (010) diffraction peak of IT-4F. For the PBDB-TF/TA film, the use of SA-1 has a litter influence on its crystallinity. For the blend/TA film, it shows an enhanced (010) peak by using SA-1. To further study the crystallinity of the films, we carried out the 2D GIWAXS measurements. The 2D GIWAXS patterns and the corresponding intensity profiles in the out-of-plane (OOP) and in-plane directions are provided in Supplementary Fig. 8. For the IT-4F-based films with different treatments, the IT-4F+SA-1/TA film shows a pronounced (010) peak in the OOP direction, suggesting more ordered molecular stacking.

We then investigated the effect of SA-1 on phase separation morphology in the surfaces of the films using atomic force microscopy (AFM). The as-cast films processed without SA-1 show smooth and uniform surfaces (Fig. 3d). The corresponding mean-square surface roughness (Rq) values are slightly increased after TA at 140 °C for 10 min. The as-cast film of the equimolar mixture of IT-4F and SA-1 has a smooth surface, although the neat SA-1 has a very poor film formation property. When the content of SA-1 further increases (IT-4F:SA-1, mol:mol = 1:2 or 1:3), some tiny aggregations of SA-1 appear, while most of the film is still quite smooth (Supplementary Fig. 9). In the as-cast PBDB-TF+SA-1 film (wt/wt = 100:17.3), SA-1 forms large crystals with a high Rq of 59.2 nm, but the film still shows normal morphology in the zoom without crystals. For the as-cast PBDB-TF:IT-4F blend film, the nanoscale phase-separation morphology can be maintained after adding the same content of SA-1, which could be ascribed to the good miscibility of SA-1 and IT-4F. After TA, the Rq of the IT-4F+SA-1/TA film is 0.83 nm, which is higher than that of the IT-4F/TA film (0.32 nm). The large crystals of SA-1 on the surface of PBDB-TF films disappeared with a slightly higher Rq than the as-cast PBDB-TF film observed. From the transmission electron microscopy (TEM) image, there is no any hollow observed for the blend+SA-1/TA film. We find the film thickness dropped approximately 10 nm after treated with TA (Supplementary Fig. 10), suggesting more condensed molecular arrangement in the blend.

Proposed working mechanism of SAs

Based on the photovoltaic characterizations, absorption spectra, as well as XRD and AFM results, we speculate the role of the SA-1 on affecting photovoltaic properties of the PBDB-TF:IT-4F blend as demonstrated in Fig. 4a. During the spin-coating process, SA-1 can be well mixed with IT-4F and they may act as small bridges to enhance the π-stacking between the two IT-4F molecules. During the TA process, SA-1 is removed from the film, leaving more room for the self-assembly of IT-4F and forming a more condensed and ordered molecular arrangement, which makes it possible for a strong π–π interaction among IT-4F molecules. As a result, even if the Voc is slightly reduced caused by the changes of morphologies, the photovoltaic properties of the blend film can be significantly improved by using SA-1 as the additive. In this process, the donor matrix acts as a limit to the excessive movement of IT-4F molecules, which helps to maintain the good bi-continuous interpenetrating networks. To verify the proposed mechanism, we first studied the volatility of SA-1 by the detailed thermogravimetric analysis (TGA) and solution absorption before and after its volatilization. Then, we applied SA-1 in other efficient NF OSCs and investigated the volatility of the other seven small molecular materials (SA-x, x = 2 to 8) as illustrated in Fig. 1a and used them as solid additive for device fabrication, respectively.

Fig. 4

Proposed mechanism of volatilizable SAs. a Schematic diagram of working mechanism of SAs. b Photographs of spin-coated films of eight SAs. Then the films were thermal annealed at 140 °C for 10 min

First, we measured the TGA at different conditions. As shown in the Supplementary Fig. 11a, we changed the heating rates of 1, 10 and 20 °C min−1 and SA-1 shows different Td (5% weight loss) of 209, 241 and 263 °C, and the weight loss starts from around 180 °C. We think the volatilization of SA-1 is a slow process, therefore, we hold the heating temperature of 140, 150, 160 and 180 °C for 2 h. We can find a clear weight loss at 140 °C, implying the SA-1 have volatility at 140 °C. The increasing temperature will accelerate the volatilization of SA-1 significantly. After the measurement, we found the SA-1 on the top of crucible, suggesting it is not decomposed. We then put the SA-1 powder and made a thin SA-1 film (about 40 nm) on the silicon substrates and observed their changes under thermal annealing. We found that the SA-1 film gradually changed over time and totally vanished 2 min later, and the substrate became clean (Supplementary Fig. 11e). However, the SA-1 powder showed really little change. The AFM images and photos of SA-1 film with or without TA are shown in Supplementary Fig. 12. Furthermore, we measured the solution absorption spectra of PBDB-TF:IT-4F blend with different weight ratio of SA-1 and the solution of chloroform-dissolved films under different conditions to confirm that SA-1 could leave totally from the active layer after TA at 140 °C (Supplementary Fig. 13). Furthermore, Fourier transform infrared (FT-IR) spectra was also applied to confirm the volatilization of SA-1 from the blend film (Supplementary Fig. 14).

To further verify this mechanism, we applied the SA-1 in other efficient NF OSCs by using different polymers and A–D-A acceptors, including PBDB-TCl:IT-4F, PBTA-TF:IT-M, PBDB-TF:IT-2F, PBDB-T:ITIC, PBDB-T:ITCC and J52:IEICO (the chemical structures are shown in Supplementary Fig. 15). The J − V curves of these devices processed with or without SA-1 are provided in Supplementary Fig. 16, and the detailed photovoltaic parameters are summarized in Table 1. Clearly, the addition of SA-1 in different systems can simultaneously enhance Jsc and FF values of the devices; this is very similar to the phenomenon observed in PBDB-TF:IT-4F-based devices. Impressively, a maximum PCE of 14.2% was recorded for the PBDB-TCl:IT-4F-based OSCs, which is comparable to the result obtained by using DIO as a solvent additive in our recent work37.

As illustrated in Fig. 4b, these small molecular materials (SA-x) possess different volatilities (Supplementary Figs 17 and 18) in the spin-coated solid films. For instance, after TA at 140 °C for 10 min, the neat films of SA-1, SA-2, SA-3 and SA-4 can be completely removed while many residues remained in the films of SA-5 and SA-6. For the SA-7 and SA-8 films, there was no obvious change after TA. As presented in Table 2 and Supplementary Fig. 19, the PBDB-TF:IT-4F-based OSC devices fabricated with SA-2, SA-3 or SA-4 exhibit good PCE around 13.6%, which is comparable to that of the device fabricated with SA-1. However, the photovoltaic properties of the devices with the other four additives are obviously lower, especially for the devices processed with SA-7 and SA-8. We also found that the film thickness of PBDB-TF:IT-4F blend processed with SA-2, SA-3 or SA-4 decreased approximately 10 nm after TA, which is similar to that observed in the blend film processed with SA-1, while the thicknesses of the blend film processed with other four additives were almost unchanged after TA. Therefore, we can conclude that SA-1, SA-2, SA-3 and SA-4 exhibit similar functions for improving photovoltaic performance of the PBDB-TF:IT-4F-based OSCs, whereas the other four materials are not appropriate because of their weaker volatilities.

Table 2 Photovoltaic parameters for PBDB-TF:IT-4F based devices with different SAs incorporated into the casting solution

The superiority of SAs compared with solvent additives

We fabricated the PBDB-TF:IT-4F-based device using the most widely used solvent additive DIO. As presented in Supplementary Table 7, the devices using DIO as additive followed by TA can achieve comparable PCE to that of the SA-1-processed OSCs. However, as illustrated in Fig. 5a, b, when the active layer films have been treated with 24 h-standing before TA, the devices fabricated using DIO exhibit lower PCE (9.3 ± 1.3%) and poor reproducibility. From the AFM images in Fig. 5c, we can see that the aged film processed with DIO exhibits large aggregations with an Rq of 41.9 nm, due to the slow evaporation of residual DIO in the storage period. By contrast, the aged film with SA-1 still exhibits smooth and uniform morphology, and the resulting devices fabricated using SA-1 still have good device performance (PCE of 13.2 ± 0.3%). Benefiting from the intrinsic nature of solid additive, the OSCs processed with SA-1 exhibit better morphological stability than those with residual DIO, and the former contribute to higher yield and reproducibility in large-scale production.

Fig. 5

The advantages of SAs over solvent additives. a J − V curves of OSCs fabricated by aged films using DIO or SA-1. b The histogram of PCE for aged devices with DIO or SA-1. c AFM height image and 3D images of PBDB-TF:IT-4F films with DIO or SA-1, for which the casted active layer was annealed after 24 h standing. d Photo-stability of PBDB-TF:IT-4F-based devices with DIO or SA-1 (encapsulated in air, AM 1.5 radiation to illumination of 100 mW cm−2 for 130 h)

Additionally, we investigated the stability of the optimal OSCs fabricated with SA-1 or DIO under illumination in air. After illumination for 130 h (encapsulated, AM 1.5 radiation to illumination of 100 mW cm−2), the device fabricated with SA-1 delivered a PCE of 12.0% and showed better stability than the device with DIO (Fig. 5d).

According to the literature, the photovoltaic performance of OSCs processed with DIO is greatly affected by the volume of addition, which is typically below 5% or even 0.5% (v/v) and needs be carefully controlled6,20,21,22. However, as mentioned above, the devices can maintain their good performances when the content of SA-1 varies in a large range, from 8 to 25 wt.%. These advantages of volatilizable SAs, including better morphological stability, illumination stability and insensitivity to the amount of additive, will be beneficial for the future industrial application of OSCs.


In conclusion, we report a method of applying volatilizable SAs to enhance photovoltaic performance of NF OSCs based on A–D–A-type acceptors. By considering the molecular structure of the NF acceptor IT-4F, we designed and synthesized a volatilizable solid additive SA-1, which can be well mixed with IT-4F and volatilized by TA. The intermolecular π–π interaction and charge transport properties of IT-4F can be significantly enhanced since the more condensed and ordered molecular arrangement after the SA-1 volatilized from the active layer, which contributes to the enhancement of Jsc and FF of the optimal OSCs. Furthermore, the device fabricated by using SA-1 possesses better device stability and reproducibility than the most widely used solvent additive, DIO. We also demonstrate that some of the SA-x, which have similar volatility to that of SA-1, can also be effective for achieving high-efficient devices, whereas SA-1 can be a general additive in varied active layers for improving the photovoltaic performance of NF OSCs. Our results suggest that using volatilizable SAs is an alternative and potential method of making OSCs more competitive in future industrialization and that designing specific additives for different active materials will be a promising direction in the photovoltaic field.


Device fabrication and testing

The conventional OSC devices were fabricated and characterized by using a device structure of ITO/PEDOT:PSS)/active layer/PFN-Br/Al, where PEDOT:PSS and PFN-Br served as the hole-transport layer and electron-transport layer, respectively. The cleaned ITO glasses were treated by UV-ozone for 15 min before about 20 nm thick of PEDOT:PSS was spin-coated. Then the ITO substrate were placed in an oven for 15 min at 150 °C. The active layer, PBDB-TF:IT-4F blend was dissolved in chlorobenzene (CB) solvent at a polymer weight concentration of 11 mg mL−1, and the donor: acceptor ratio was kept at 1:1. SA-x of the same concentration was also dissolved in CB. After adding SA-x, the blend solution was stirred for more than 20 min. After the blend solution were spin-coated onto ITO glasses, TA for 10 min at 140 °C was utilized to optimize the morphology of active layer. Then the electron-transport layer of PFN-Br (about 5 nm) was coated on the top of active layer at 3000 rpm for 30 s. Finally, about 90 nm of Al with an area of 4.0 mm2 were deposited onto the active layer under high vacuum. The preparation of the other devices based on PBDB-TCl:IT-4F, PBTA-TF:IT-M, PBDB-TF:IT-2F, PBDB-T:ITIC, PBDB-T:ITCC and J52:IEICO were the same as the procedures discussed above. Except for the spin-coating of PEDOT:PSS, the other the processes were all carried out in an nitrogen-filled glovebox. The J−V measurement was performed via the solar simulator (SS-F5-3A, Enlitech) along with AM 1.5 G spectra whose intensity was calibrated by the certified standard silicon solar cell (SRC-2020, Enlitech) at 100 mW cm−2. The external quantum efficiency (EQE) data were obtained by using the solar-cell spectral-response measurement system (QE-R, Enlitech). The devices for examining the storage stability and light stability were fabricated by using a structure of ITO/ZnO/active layer/MoO3/Al. AM 1.5 G spectrum at 100 mW cm−2 along with a National Institute of Metrology, China calibrated reference cell was used to measure the OSCs. As shown in the Supplementary Fig. 20, the best OSC device was sent to the National Institute of Metrology, China (NIM), to make a certification by using an area of 3.78 mm2. The confirming PCE was 13.7% with a Voc of 0.88 V, a Isc of 0.77 mA and an FF of 0.765.

Morphology characterization

AFM images were obtained by a Nanoscope V AFM on tapping mode. For the films with SA-1, 17.3 wt.% of SA-1 with respect to PBDB-TF or IT-4F were added in each blend solution before spin-coating. All the film samples with or w/o SA-1 were spin-coated from the respective solutions onto ITO-PEDOT:PSS substrate. X-ray diffraction (XRD) patterns were collected using a Rigaku D/max 2500 X-ray diffractometer and the samples were prepared on Si substrates by drop-casting. The GIWAXS data were obtained on a XEUSS SAXS/WAXS SYSTEM (XENOCS, FRANCE) at the National Center for Nanoscience and Technology (NCNST, Beijing).

Synthesis of SA-1 and other solid additives

The detailed synthesis routes can be found in the Supplementary Notes 1 to 8. The NMR data, elemental and mass analysis of all the modulators are included as Supplementary Figs 21 to 44.

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.


  1. 1.

    Yu, G., Gao, J., Hummelen, J. C., Wudl, F. & Heeger, A. J. Polymer photovoltaic cells: enhanced efficiencies via a network of internal donor-acceptor heterojunctions. Science 270, 1789–1791 (1995).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Li, G., Zhu, R. & Yang, Y. Polymer solar cells. Nat. Photon 6, 153–161 (2012).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Dou, L. et al. 25th anniversary article: a decade of organic/polymeric photovoltaic research. Adv. Mater. 25, 6642–6671 (2013).

    CAS  Article  PubMed  Google Scholar 

  4. 4.

    Lu, L. et al. Recent advances in bulk heterojunction polymer solar cells. Chem. Rev. 115, 12666–12731 (2015).

    CAS  Article  PubMed  Google Scholar 

  5. 5.

    Xu, X. et al. Highly efficient ternary-blend polymer solar cells enabled by a nonfullerene acceptor and two polymer donors with a broad composition tolerance. Adv. Mater. 29, 1704271 (2017).

    Article  Google Scholar 

  6. 6.

    Fei, Z. et al. An alkylated indacenodithieno[3,2-b]thiophene-based nonfullerene acceptor with high crystallinity exhibiting single junction solar cell efficiencies greater than 13% with low voltage losses. Adv. Mater. 30, 1705209 (2018).

    Article  Google Scholar 

  7. 7.

    Li, M. M. et al. Benzo[1,2-b: 4,5-b’]dithiophene (BDT)-based small molecules for solution processed organic solar cells. J. Mater. Chem. A 3, 4765–4776 (2015).

    CAS  Article  Google Scholar 

  8. 8.

    Nian, L. et al. 11% efficient ternary organic solar cells with high composition tolerance via integrated near-IR sensitization and interface engineering. Adv. Mater. 28, 8184–8190 (2016).

    CAS  Article  PubMed  Google Scholar 

  9. 9.

    Deng, D. et al. Fluorination-enabled optimal morphology leads to over 11% efficiency for inverted small-molecule organic solar cells. Nat. Commun. 7, 13740 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  10. 10.

    He, Z. et al. Single-junction polymer solar cells with high efficiency and photovoltage. Nat. Photon. 9, 174–179 (2015).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Lee, J. K. et al. Processing additives for improved efficiency from bulk heterojunction solar cells. J. Am. Chem. Soc. 130, 3619–3623 (2008).

    CAS  Article  PubMed  Google Scholar 

  12. 12.

    Choi, H. et al. Small-bandgap polymer solar cells with unprecedented short-circuit current density and high fill factor. Adv. Mater. 27, 3318–3324 (2015).

    CAS  Article  PubMed  Google Scholar 

  13. 13.

    Zhao, J. B. et al. Efficient organic solar cells processed from hydrocarbon solvents. Nat. Energy 1, 15027 (2016).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Tremolet de Villers, B. J. et al. Removal of residual diiodooctane improves photostability of high-performance organic solar cell polymers. Chem. Mater. 28, 876–884 (2016).

    CAS  Article  Google Scholar 

  15. 15.

    Zhao, W. et al. Environmentally friendly solvent-processed organic solar cells that are highly efficient and adaptable for the blade-coating method. Adv. Mater. 30, 1704837 (2018).

    Article  Google Scholar 

  16. 16.

    Turkovic, V. et al. Long-term stabilization of organic solar cells using hindered phenols as additives. Acs Appl. Mater. Interfaces 6, 18525–18537 (2014).

    CAS  Article  PubMed  Google Scholar 

  17. 17.

    Liao, H.-C. et al. Additives for morphology control in high-efficiency organic solar cells. Mater. Today 16, 326–336 (2013).

    CAS  Article  Google Scholar 

  18. 18.

    Park, K. H., An, Y., Jung, S., Park, H. & Yang, C. The use of an n-type macromolecular additive as a simple yet effective tool for improving and stabilizing the performance of organic solar cells. Energy Environ. Sci. 9, 3464–3471 (2016).

    CAS  Article  Google Scholar 

  19. 19.

    Lin, Y. et al. An electron acceptor challenging fullerenes for efficient polymer solar cells. Adv. Mater. 27, 1170–1174 (2015).

    CAS  Article  PubMed  Google Scholar 

  20. 20.

    Bin, H. et al. Non-fullerene polymer solar cells based on alkylthio and fluorine substituted 2D-conjugated polymers reach 9.5% efficiency. J. Am. Chem. Soc. 138, 4657–4664 (2016).

    CAS  Article  PubMed  Google Scholar 

  21. 21.

    Li, Z. et al. Donor polymer design enables efficient non-fullerene organic solar cells. Nat. Commun. 7, 13094 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  22. 22.

    Baran, D. et al. Reduced voltage losses yield 10% efficient fullerene free organic solar cells with >1 V open circuit voltages. Energy Environ. Sci. 9, 3783–3793 (2016).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  23. 23.

    Liu, Y. et al. Exploiting noncovalently conformational locking as a design strategy for high performance fused-ring electron acceptor used in polymer solar cells. J. Am. Chem. Soc. 139, 3356–3359 (2017).

    CAS  Article  PubMed  Google Scholar 

  24. 24.

    Zhu, J. et al. Naphthodithiophene-based nonfullerene acceptor for high-performance organic photovoltaics: effect of extended conjugation. Adv. Mater. 30, 1704713 (2018).

    Article  Google Scholar 

  25. 25.

    Zhao, W. et al. Molecular optimization enables over 13% efficiency in organic solar cells. J. Am. Chem. Soc. 139, 7148–7151 (2017).

    CAS  Article  PubMed  Google Scholar 

  26. 26.

    Han, G., Guo, Y., Song, X., Wang, Y. & Yi, Y. Terminal π–π stacking determines three-dimensional molecular packing and isotropic charge transport in an A–π–A electron acceptor for non-fullerene organic solar cells. J. Mater. Chem. C. 5, 4852–4857 (2017).

    CAS  Article  Google Scholar 

  27. 27.

    Hou, J., Inganas, O., Friend, R. H. & Gao, F. Organic solar cells based on non-fullerene acceptors. Nat. Mater. 17, 119–128 (2018).

    ADS  CAS  Article  PubMed  Google Scholar 

  28. 28.

    Fan, Q. et al. Synergistic effect of fluorination on both donor and acceptor materials for high performance non-fullerene polymer solar cells with 13.5% efficiency. Sci. Chi. Chem. 61, 531–537 (2018).

    CAS  Article  Google Scholar 

  29. 29.

    Zhang, M., Guo, X., Ma, W., Ade, H. & Hou, J. A large-bandgap conjugated polymer for versatile photovoltaic applications with high performance. Adv. Mater. 27, 4655–4660 (2015).

    CAS  Article  PubMed  Google Scholar 

  30. 30.

    Huang, F., Wu, H. B., Wang, D., Yang, W. & Cao, Y. Novel electroluminescent conjugated polyelectrolytes based on polyfluorene. Chem. Mater. 16, 708–716 (2004).

    CAS  Article  Google Scholar 

  31. 31.

    Li, W. T., Yan, L., Zhou, H. X. & You, W. A general approach toward electron deficient triazole units to construct conjugated polymers for solar cells. Chem. Mater. 27, 6470–6476 (2015).

    CAS  Article  Google Scholar 

  32. 32.

    Zhang, G. et al. High-performance ternary organic solar cell enabled by a thick active layer containing a liquid crystalline small molecule donor. J. Am. Chem. Soc. 139, 2387–2395 (2017).

    CAS  Article  PubMed  Google Scholar 

  33. 33.

    Kokil, A., Yang, K. & Kumar, J. Techniques for characterization of charge carrier mobility in organic semiconductors. J. Polym. Sci. B-Polym. Phys. 50, 1130–1144 (2012).

    ADS  CAS  Article  Google Scholar 

  34. 34.

    Juska, G., Arlauskas, K., Viliunas, M. & Kocka, J. Extraction current transients: new method of study of charge transport in microcrystalline silicon. Phys. Rev. Lett. 84, 4946–4949 (2000).

    ADS  CAS  Article  PubMed  Google Scholar 

  35. 35.

    Lee, J. et al. Two-dimensionally extended π-conjugation of donor–acceptor copolymers via oligothienyl side chains for efficient polymer solar cells. Macromolecules 48, 1723–1735 (2015).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Liu, P. et al. Effect of fluorine content in thienothiophene-benzodithiophene copolymers on the morphology and performance of polymer solar cells. Chem. Mater. 26, 3009–3017 (2014).

    ADS  Article  Google Scholar 

  37. 37.

    Zhang, S., Qin, Y., Zhu, J. & Hou, J. A chlorinated polymer donor enables over 14% efficiency in polymer solar cells. Adv. Mater. 30, 1800868 (2018).

    Article  Google Scholar 

Download references


J.H. would like to acknowledge the financial support from the financial support from National Natural Science Foundation of China (21835006, 91633301 and 51673201), the Chinese Academy of Science (XDB12030200, KJZD-EW-J01). H.Y. thanks the financial support from the National Natural Science Foundation of China (21805287) and the Youth Innovation Promotion Association CAS (No. 2018043). We acknowledge Dr. Jianqi Zhang and Prof. Zhixiang Wei from National Center for Nanoscience and Technology (NCNST) for assistance with the GIWAXS measurements.

Author information




R.Y. fabricated and characterized the devices and carried out the detailed characterizations. H. Yao designed and synthesized the solid additives and non-fullerene acceptor. J.Z. synthesized some solid additives. Y.Q. and Y.C. carried out the device certification. S.L. synthesized the polymer donor. L.H. carried out the material characterizations. R.Y., H.Y. and J.H. prepared the manuscript. J.H. and H.Y. supervised and directed this project. All authors discussed the results and commented on the manuscript.

Corresponding authors

Correspondence to Huifeng Yao or Jianhui Hou.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Yu, R., Yao, H., Hong, L. et al. Design and application of volatilizable solid additives in non-fullerene organic solar cells. Nat Commun 9, 4645 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing