Atomically precise fabrication methods are critical for the development of next-generation technologies. For example, in nanoelectronics based on van der Waals heterostructures, where two-dimensional materials are stacked to form devices with nanometer thicknesses, a major challenge is patterning with atomic precision and individually addressing each molecular layer. Here we demonstrate an atomically thin graphene etch stop for patterning van der Waals heterostructures through the selective etch of two-dimensional materials with xenon difluoride gas. Graphene etch stops enable one-step patterning of sophisticated devices from heterostructures by accessing buried layers and forming one-dimensional contacts. Graphene transistors with fluorinated graphene contacts show a room temperature mobility of 40,000 cm2 V−1 s−1 at carrier density of 4 × 1012 cm−2 and contact resistivity of 80 Ω·μm. We demonstrate the versatility of graphene etch stops with three-dimensionally integrated nanoelectronics with multiple active layers and nanoelectromechanical devices with performance comparable to the state-of-the-art.
As next-generation technologies of electronic, photonic, and mechanical devices approach the atomic scale, it is important to develop atomically precise fabrication methods. Among them, etch stops, critical for the vertical integration of nanoelectronic and nanomechanical devices, are created by layering materials with drastically different etch properties and embedded into a structure, allowing for patterning feature sizes, accessing buried layers, or undercutting to create suspended structures. Accordingly, improved fabrication techniques are especially needed in nanoelectronics based on van der Waals (vdW) heterostructures, where two-dimensional (2D) materials are stacked to form electronic devices with nanometer thicknesses1,2,3,4,5. Many of the applications for 2D material heterostructure devices demand out-of-plane integration, contacting multiple active layers, and creating interconnects between the different layers1,2,3,4,5. Examples include 2D material-based integrated circuitry like NAND gates6 or ring oscillator7; devices based on interlayer tunneling like light-emitting diodes (LEDs)8 or tunnel transistors9; and nanoelectromechanical systems (NEMS) like resonators based on atomic membranes10.
In the current state of the art, the relative ease of assembly of vdW heterostructures, which occurs through the sequential pick-up and stamped release of individual atomic layers, contrasts starkly with the difficulty of patterning and electrically addressing each layer in a heterostructure device. As a result, the majority of studies in this field are performed on monolayers or on heterostructures where each layer has been carefully offset so they are accessible for electrical contacts through direct deposition of metal on top or on the exposed edges of individual 2D layers11,12,13,14. The current state-of-the-art method is to use edge contacts where heterostructures are etched through to expose the edges of buried layers of graphene encapsulated in insulating hexagonal boron nitride (hBN), and then metals are evaporated onto the edge to make one-dimensional (1D) contacts13. This method has led to a dramatic improvement in the mobility and quality of electronic devices because it allows contact to electronic layers that are fully encapsulated and thus have a minimum of disorder13,15. However, edge contacts still require careful offsetting of active layer because the etching is not selective so all vertically aligned layers in the heterostructure are exposed simultaneously. A method that combines the superior device behavior of the edge contacts but that simultaneously allows ready patterning of 2D heterostructures from large area continuous sheets and individually addressing of each layer are critical for translating many of the recent demonstrations of this class of devices into scalable technologies.
Here we show methods to fabricate nanostructures and access buried interfaces with the precision of a single atomic layer by using graphene as impermeable etch masks and etch stops16,17. These techniques, which we call GES (graphene etch stops), represent a straightforward method to selectively expose and contact embedded graphene layers within 2D heterostructures. This concept takes advantage of the high chemical selectivity of XeF2, a vapor phase, strong fluorinating agent commonly used as an isotropic etchant for silicon in the microelectromechanical systems (MEMS) industry18. Several 2D materials including hBN and transition metal dichalcogenides, are quickly etched when exposed to XeF216,19,20. In contrast, graphene reacts with XeF2 to form fluorographene (FG)21,22,23,24, a wide band-gap semiconducting monolayer21,22 with composition C4F, in the case that only one side is exposed22. There have been several demonstrations that take advantage of this selectivity to use graphene as an etch mask for shaping MoS216, as a mask to etch underlying silicon25,26,27, and to create a sacrificial release layer to suspend graphene membranes on silicon on insulator17,22. Our innovation has been to apply this etch selectivity to access buried graphene layers embedded within the heterostructures and as masks for patterning the underlying layers. Surprisingly, the embedded contacts, which is composed of FG–metal contacts, lead to room temperature carrier mobilities of 40,000 cm2 V−1 s−1 at carrier density n = 4.0 × 1012 cm−2 and behave as 1D contacts with low contact resistivity of 80 Ω μm, approaching theoretical limits11,28. This capability enables simple and scalable methods to vertically integrate 2D devices through contacting multiple active layers, interlayer vias, and suspended nanostructures, yet maintains the state-of-the-art performance of fully encapsulated 2D devices.
Selective etching by graphene etch stop
Figure 1a illustrates the use of GES to pattern a heterostructure of 2D materials, and Fig. 1b, c are optical images of the same heterostructure before and after exposure to XeF2. The heterostructure is fabricated by stacking individual materials using established polymer-free, aligned transfer techniques11,29. Specifically, the heterostructure is composed of two monolayer graphene flakes, set in a cross-alignment and embedded between hBN layers, then placed on top of a Si/SiO2 (285 nm) substrate. The color corresponds with the thickness of the heterostructure. In Fig. 1b, two graphene layers are not visible because their contrast is completely overwhelmed by the much thicker hBN, but the inset Raman map confirms their positions. As seen in Fig. 1c, after exposure to XeF2 (3 Torr for 30 s at room temperature), the exposed hBN is completely etched, while the graphene layers and the hBN underneath them remain. In Supplementary Note 1, Supplementary Figure 1, and Supplementary Table 1, we show that the same process can be applied to many other 2D material heterostructures as well, including hBN, MoS2, WSe2, and black phosphorus (BP).
To examine the selectivity and resolution limits of GES, we obtained cross-sectional images of the etched heterostructures with a scanning transmission electron microscope (STEM), as shown in Fig. 1d, e. Importantly, the hBN layers under the FG show no etching, indicating that they are protected from the XeF2. Moreover, Fig. 1e shows that the buried layer of graphene (G1) is unaffected by the etch process and there are atomically sharp and clean interfaces between stacked graphene and hBN layers (see also Raman data in Supplementary Figure 2). These results demonstrate that FG maintains the impermeable nature of graphene30,31 through the chemical modification process16,32. In Fig. 1d, at the edge of the etch mask, the underlying hBN has a sub-nanometer slope. These images demonstrate that GES is a self-arresting etch process that enables atomic precision out of plane and nanometer-scale feature sizes without requiring precise control in timing or conditions.
Characteristics of fluorinated graphene etch stops
The self-arresting nature of GES means that it is scalable as well as being atomically precise. Fig. 2a demonstrates this scalability by applying GES to a large area heterostructure array. We patterned large area graphene as etch masks for patterning large area WS2, both grown by chemical vapor deposition (CVD). First, large area continuous graphene was patterned into lines with lithography and oxygen plasma. Two sets of the patterned lines were then sequentially transferred onto large area continuous monolayer WS2 grown by CVD. The second transfer is set perpendicular to the first to form a cross-hatch pattern. After exposure to XeF2, WS2 uncovered by graphene was completely etched, while the region covered by graphene remained under FG (process flow in Supplementary Figure 3 and photoluminescence maps in Supplementary Figure 4). This process of combining prepatterned graphene masks with the selective etch can be repeated to scalably achieve arbitrarily complex heterostructures of layered FG, graphene, and other materials on the wafer-scale patterns, which could not be realized with conventional patterning and etching techniques.
Before examining the application of GES to 2D heterostructure devices, we confirm the structure and electrical properties of FG. Figure 2b shows the Raman spectra of graphene on hBN under increasing exposure to XeF2. Initially, only the G and 2D peak are visible, indicating clean graphene with no defects, as well as one additional peak from the underlying hBN. After exposure to XeF2, the D peak appeared and the 2D peak was suppressed. Both phenomena are a result of the breaking of hexagonal symmetry within the graphene lattice due to the formation of sp3 bonds by bonding of fluorine atoms onto the graphene surface22. Supplementary Figures 5 and 6 show additional structural analyses of X-ray photoelectron spectroscopy (XPS) and TEM and demonstrate that the fluorination condition results in only a sp3-type lattice transition without formation of voids, consistent with the observation that FG acts as an impermeable barrier16. Figure 2c shows the electrical transport through a prefabricated graphene transistor on hBN (device shown in the inset and additional details in Supplementary Figure 7). Before fluorination, the graphene shows mS conductance and gate dependence typical of the linear dispersion in graphene band structure. The device conductance drastically decreased as a function of fluorination time. After 10 s, the device conductance decreased by a factor of 10, while after 30 s, the graphene became insulating with resistance exceeding 60 GΩ. As shown in Supplementary Figure 8, when graphene on hBN is functionalized for longer periods (720 s), it maintained its structure and high resistance for over 2 months in ambient conditions.
Electrical properties of fluorinated graphene contacts
In the rest of the paper, we will explore the application of GES to fabricating electronic and mechanical devices from 2D heterostructures. Two persistent challenges in nanoscale device research are how to minimize the impact of environment on limiting the potentially outstanding electronic mobility of nanomaterials and how to engineer low resistance contacts to nanomaterials. Previous studies have shown that achieving the theoretical limits of performance in graphene devices requires graphene to never come into contact with solvents or polymers and charged impurity scattering to be suppressed by fully encapsulating the samples in hBN13. However, doing this brings a challenge of how to electrically contact the encapsulated graphene layers. In Fig. 3a, we demonstrate the application of GES to electrically contact a buried graphene layer encapsulated in hBN. Using e-beam lithography, electrodes were patterned on top of hBN/G/hBN heterostructure. Then the structure was exposed to XeF2 before metallization. As it is well known, the XeF2 does not attack the polymer. However, within the patterned regions, the top hBN is etched away, locally exposing and fluorinating the buried graphene layer. Electrodes were then deposited through the same polymer mask directly on to the fluorographene regions (1 nm Cr, 30 nm Pd, and 40 nm Au; see Supplementary Figure 9 and Methods for details). Figure 3a shows a cross-sectional high-resolution transmission electron microscope (HR-TEM) image of the FG electrical contact. The lithographic pattern is transferred into the hBN, and the evaporated metal is deposited only on the exposed FG, while the graphene channel under the hBN is never exposed.
Figure 3b shows the field-effect characteristics of a graphene Hall bar device encapsulated by hBN with FG contacts. The mobility was calculated by the Drude model, μ = σ/ne where μ, n, e, and σ are the carrier mobility, carrier density, electron charge, and sheet conductivity, respectively. At high carrier concentration of n = 4.0 × 1012 cm−2, the sheet resistance was 45 Ω per square at room temperature, corresponding to a carrier mobility of 40,000 cm2 V−1 s−1, close to the theoretical limit28. As shown in the inset of Fig. 3b, the mobility drastically increases with decreasing carrier concentrations, as expected from the acoustic-phonon-limited model13,28. On a Hall bar device measured at low temperature T = 1.7 K (Supplementary Figure 10), the low carrier concentration mobility increased to 460,000 cm2 V−1 s−1. This mobility corresponds with a mean free path of 4.6 μm, similar to the channel width of the device so the mobility is likely limited by device dimensions rather than material properties. The device conductance (Ids − Vds) is linear and displayed no hysteresis (Supplementary Figure 11). The contact resistance of the FG to the buried graphene channel was quantified by performing transfer length measurements on the device shown in the inset of Fig. 3c. Figure 3c shows the resistance vs. channel length at different charge concentrations. The contact resistances are extracted from the extrapolated zero-length intercepts to get 21 Ω for holes and 49 Ω for electrons for a 4 μm wide channel. Figure 3d shows the contact resistance vs. carrier concentration from 2.4 K to room temperature. The contact resistance vs. temperature is shown in the Fig. 3d inset. The resistivity is not significantly affected by temperature and can reach a value of 80 Ω∙μm at n = 4.0 × 1012 cm−2, which means absence of the potential barrier at the contact. This is distinct from the graphene devices with surface-contacted metal electrodes, which show temperature dependence of contact resistance due to the potential barrier formed at the contact13. In addition, all the devices display robust chemical and electrical stability. The devices showed no significant change after 1 month, when stored in air (Supplementary Figure 12). Taken together, the outstanding mobility, low contact resistance, and stability from encapsulation make these devices comparable to the state of the art across all metrics (Supplementary Figure 13 and Supplementary Table 2 contain a comparison), while simultaneously being much easier to fabricate due to the self-arresting mechanism of GES. However, these low contact resistances are surprising, especially given the high in-plane resistance of FG measured in Fig. 2b.
To explain the low contact resistance, density functional theory was applied to simulate the interlayer distance and charge distribution at a FG and metal heterointerface. Figure 3e shows the equilibrated structure and local density of states in four different interfaces: either graphene or FG and either Cr or Pd metal (see Supplementary Figure 14 and Methods for simulation details). The 1 nm-thick Cr adhesion layer forms islands, not a continuous film (Supplementary Figure 15), so both Cr and Pd will make direct contact to the FG surface. From a Landauer framework, the factors governing contact resistance are related to the carrier transmission probability T and the number M of conduction modes available12. Transport must occur both from the metal to the graphene under the metal and from the graphene under the metal to the channel region, which have different transmission probabilities. Additionally, the number of graphene conduction modes under the metal is reduced in some cases due to charge transfer doping by the metal. The contact resistance can be improved by achieving a smaller effective metal/graphene coupling length to increase T or by finding metals that lead to high metal-induced doping concentrations to increase M. From the isosurfaces, without fluorine the G–Cr interface shows weak vdW bonding33, and the small orbital overlap leads to low T due to the presence of a tunneling barrier and a large effective coupling distance34. The G–Pd interface shows somewhat more orbital hybridization between the graphene pz and metal d states, consistent with prior results33. Interestingly, when fluorinated the degree of hybridization increases for both metals, particularly for FG–Pd, indicating a reduced coupling length that renders the charge transfer more ballistic and lowering the contact resistance34. Additionally, the fluorine hybridization opens a band gap in graphene, reducing its work function, and inducing a large effective n-type charge transfer doping. The combination of the strong coupling and the enhanced charge transfer doping suggest that the contact resistance is limited by the FG–graphene interface rather than the metal–FG interface, resulting in 1D edge contacts rather than 2D surface contacts. To test this hypothesis, a variable width channel device was fabricated. The contact resistance was linearly proportional to the reciprocal of channel width (Supplementary Figure 16) as expected in 1D contacts. These simulations and measurements show that the dominant contact resistance in the FG-buried devices is at the 1D graphene–FG interface. Similar results have been seen in electrically contacting the sides of etched heterostructures where only the 1D edge of graphene is exposed13. Unlike in 2D surface contacts, this result indicates that the contact resistance of the metallized FG is independent of the contact length and there is no intrinsic lower limit of size. Hence, it should be possible to scale down the size of embedded contacts and vias to nanoscale dimensions without impacting functionality.
Fabrication of three-dimensional (3D) integrated systems from 2D materials
In addition to offering a simpler fabrication process and state-of-the-art device properties, the selective etch stop also enables capabilities that cannot be easily or scalably realized using other techniques. For example, interlayer vias and independently contacting multiple active layers in vertically aligned heterostructures are critical to integrated circuits like NAND gates6, where logic operations are computed by coupling the gates and channels of several transistors in series, and graphene-based multilayered printed circuit boards (PCBs). Similarly, many device applications of 2D heterostructures that rely out-of-plane transport, like vertical PN junctions35, tunnel junctions9, or light emitters based on 2D materials8,36 require the same ability to contact vertically aligned layers separately.
Figure 4 outlines proof-of-concept demonstrations of using GES to fabricate interlayer vias and vertically integrate multiple active layers. First, the GES is a self-arresting process that allows access to multiple buried layers set at different depths within a single etch step. This allows the creation of interlayer vias, which are critical components for integrated circuits, where wiring and devices can operate on more than one plane. Figure 4a is an optical image of a multilayer graphene–hBN heterostructure with interlayer vias fabricated in a single lithography and etch step identical to the one used in Fig. 3 on a single layer. The heterostructure is formed by sequentially stacking three graphene layers, each separated by few-layer hBN. Each graphene layer operates as a separate transistor, and the out-of-plane vias are formed by exposing two layers within a single opening before metallization. Figure 4b is the corresponding transfer curves within each graphene device. In this particular geometry, the layers are offset, so they may all be controlled with the global backgate. The inset of Fig. 4b is the interlayer transport current through the vias vs. interlayer bias, which shows a linear dependence. For example, the total resistance measured from the labeled electrodes, B1–M1, is 1 kΩ at Vg = 0 V, equivalent to the in-plane channel resistance of the graphene. The contact resistance is negligibly small compared with the corresponding channel resistances, demonstrating that GES enables efficient, simple, and selective contacts to vertically offset layers to create low resistance interlayer vias, which could be integrated to the complicated devices such as multilayer PCBs or light emitter based on 2D materials.
The second demonstration takes advantage of the combined high in-plane resistance of FG with the low contact resistance when the FG is metallized. Through sequential patterning and etching steps, GES allows independent contact of multiple active layers that interact to generate device functionality. This allows the creation of 3D integrated circuitry from 2D materials, where, for example, vertically offset encapsulated 2D layers act as both the gate and channel in a transistor, which has been difficult to realize with conventional patterning techniques or 1D edge contacting13 (Supplementary Figure 17). Figure 4c shows the optical image and schematic illustration of a hBN-encapsulated graphene transistor channel with graphene backgate (i.e. two coupled active layers). In the heterostructure, the two graphene sheets are separated by hBN. Key to this demonstration is that the top graphene layer is larger than the bottom layer and fully covers it. In order to access the buried bottom layer, the selective etch process is repeated twice with an oxygen plasma shaping step in between, then lastly depositing electrodes contacting all layers (see Supplementary Figure 18 for the full fabrication process). The high in-plane and vertical resistance of both the top FG and the dielectric hBN allow access to the buried bottom layer without shorting the two layers together. Figure 4d is the transfer curve of the resulting embedded all 2D material field effect transistors, showing that the top graphene channel (G2) can be effectively modulated by the bottom graphene gate (G1). Like the single layer demonstration in Fig. 3, all 2D layers are encapsulated, protecting them from extrinsic disorder and resulting in high carrier mobilities. The two demonstrations above prove that the selective etch process enables interlayer vias and 3D integration of multiple active device layers made entirely of 2D materials, both capabilities that are critical to the development of integrated circuitry from 2D materials.
As a final demonstration of a different kind of vertical integration, a common application of selective etches in MEMS is to suspend mechanically responsive structures. In studies on this, it was shown that graphene can be used as an etch mask for underlying silicon to generate suspended FG membranes17,22. These atomic membranes behave as tensioned mechanical resonators37, useful as low mass chemical sensors or tunable radio frequency filters or oscillators. In Fig. 4e, we show that the same concept can be applied to fabricate suspended graphene NEMS from 2D heterostructures. Figure 4e is an angled scanning electron microscopic (SEM) image of a suspended few-layer graphene membrane clamped by graphite supports. This membrane was fabricated by first creating a heterostructure of narrow few-layer graphene ribbon on 70-nm-thick black phosphorus, with 100 nm thick graphite at either end. The black BP etches far more quickly than other 2D materials when exposed to XeF2 (Supplementary Figure 1 and Supplementary Table 1), allowing it to act as a sacrificial release layer that undercuts the graphene (see fabrication process in Supplementary Figure 19).The resulting FG membrane was fully suspended without wrinkles and contamination in a dry vapor phase process. Figure 4f is the mechanical resonance of the membrane measured using modulated laser optomechanical actuation and dynamic reflection contrast detection10,37 (Supplementary Figures 20 and 21 and Methods). The graphene membrane has a resonant frequency of f1 = 5.24 MHz and quality factor of 255 at room temperature, comparable to state-of-the-art graphene resonators with similar dimensions produced via a wet process or mechanical exfoliation over trenches10,38. Just as XeF2 has found wide applicability in MEMS or NEMS industry as a selective silicon etch, using GES to produce graphene-based resonators has a great potential since the whole process is liquid free and clean. Moreover, this route can produce suspended graphene with much higher aspect ratios and gap depths than with conventional transfer or wet etching techniques.
Taken together, the demonstrations in Fig. 4 show that GES proposed in this work enable advanced fabrication of 3D-integrated electronic and mechanical devices based on 2D materials. Figure 3 shows that the structures will maintain the high mobility and low contact resistances that are currently the state of the art. Figure 1 shows that nanometer scale in-plane features and devices should be possible. Most of the demonstrations above use exfoliated materials, but as shown in Fig. 2a, the scalability of this technique means that all demonstrations will also work on arrays of devices patterned from continuous, large area heterostructures. The self-arresting nature of this process means that precision is not needed to achieve uniformity of devices, a huge benefit in atomically precise electronics. All of these components suggest that the selective etch process is a major capability necessary for the realization of atomically precise, all-2D nanoelectronics as a viable technology, in applications where vertical integration is critical, like integrated circuit logic components (e.g., NAND gates), devices operating through out-of-plane transport (e.g., 2D material tunnel junctions and LEDs), and in 2D nanoelectromechanical systems. Finally, many other materials such as transition metals, silicon, and MBE grown III–V materials are also etched by XeF2, so GES may find broad application for the fabrication of atomically precise devices beyond just 2D materials.
Fabrication of vdW heterostructures
To fabricate the heterostructures, we use a 2D material pick-up technique with similar established methods13,29. Before creating the heterostructure, it is necessary to fabricate a sacrificial transfer substrate. First, a 0.5-mm-thick polydimethylsiloxane (PDMS) droplet is deposited on a microscope glass slide, then cured overnight at 60 °C. At the same time, poly (bisphenol A carbonate, Sigma Aldrich) (PC) dissolved in chloroform is deposited onto a microscope slide glass. The chloroform is allowed to evaporate in air at room temperature, then the remaining PC film is manually peeled off by hand. The peeled-off PC film is placed onto the PDMS, then the entire structure is baked at 170 °C for 15 min to form conformal contact between PC film and PDMS. The resulting transfer substrate is then fixed to a micromanipulator. In parallel, all 2D flakes used for the vdW heterostructures were separately exfoliated onto the SiO2 (285 nm)/Si substrates with the scotch tape method. The thickness or layer number of each material is separately confirmed using a combination of Raman spectroscopy, atomic force microscopy, and optical microscopy. For the first pick-up, it is necessary to start with an extra thick layer of hBN (~20 nm). The PC/PDMS stamp is placed onto the target hBN flake at 70 °C. To increase adhesion strength between PC and hBN, the temperature is then raised to 130 °C. Then PC/PDMS stamp is gradually lifted up during cooling to 70 °C. This process is then repeated to pick up other 2D flakes subsequently at 90 °C. Each 2D piece must be smaller than the top layer of hBN. After stacking, the stacked heterostructure was transferred onto a clean SiO2/Si substrate by releasing the PC film from the PDMS at a higher temperature above 190 °C. Lastly, the PC film was removed by rinsing the sample in chloroform.
Xenon difluoride etching
The XeF2 etcher (Xactix etching system) was used for the selective etching of 2D materials in pulse mode with PXeF2 = 3 Torr at room temperature. The pulse time for etching, i.e., exposure time was set according to the thickness of top layer of hBN, between 30 s, to 2 min. However, it should be noted that the exposure time is not proportional to etch rate because etching stops at the graphene layer.
The e-beam lithography (EBL, TESCAN) was performed to generate patterns to selectively etch the vdW heterostructures. The exposure to the XeF2 gas did not affect the ability to remove the poly (methyl methacrylate) (PMMA) used as an e-beam resist using normal solvents. For fabrication of the devices in Fig. 3, the vdW heterostructure was etched by first patterning the PMMA on top of the heterostructure, then exposing the entire structure to XeF2. The top layers of the heterostructure were etched away exposing the contact area of the embedded graphene, which fluorinated during etching (Supplementary Figure 9). Then metals of Cr/Pd/Au (1 nm/30 nm/40 nm) were deposited using e-beam evaporator (Temescal six pocket e-beam evaporation systems). Finally, lift-off process was performed simply by soaking the samples in acetone.
Sample preparation for TEM
In the TEM images of Supplementary Figures 6 and 15, graphene was grown by CVD following standard recipes described in a previous paper39. The CVD graphene was then transferred onto a TEM grid. PMMA was spin-coated on the as-grown CVD graphene on a copper foil, followed by etching of copper in ammonium persulfate solution. After rinsing in multiple baths of de-ionized (DI) water, the graphene/PMMA film floating on DI water was scooped with the TEM grid. PMMA film was removed by dipping it in acetone. The cross-section TEM specimens in Fig. 1d, e in the main text were prepared using FEI Helios 600i Dualbeam focused ion beam (FIB), using standard lift-out procedures with a final milling step of 2 kV to reduce surface damage. For Fig. 3a, cross-section TEM sample of the encapsulated graphene device was prepared with FIB (JIB-4601F, JEOL).
STEM images in Fig. 1d, e were acquired with a 200 kV aberration-corrected JEOL 2200FS STEM. HR-TEM images in Supplementary Figures 6 and 14 were acquired on a Cs-corrected TEM (JEM-ARM200F, JEOL). The acceleration voltage was fixed at 80 kV to minimize damage of graphene by electron beam irradiation.
Scanning electron microscopy
The SEM images in Fig. 4e of the heterostructure stack on an SiO2 substrate were acquired on a Hitachi S-4700 field-emission gun SEM with 2 kV accelerating voltage. The sample is tilted by 45° with respect to the beam direction. False coloring was added after data acquisition.
Raman measurements in Fig. 2b and Supplementary Figure 8 were acquired on a Renishaw using a 633 nm laser and an 1800 mm−1 grating. To minimize damage of graphene by irradiation of the laser, a power of < 5 mW was used with an acquisition of 60 s.
XPS measurement in Supplementary Figure 5 was acquired using a K-alpha XPS system (Thermo VG, UK). For this measurement, graphene grown by CVD was used. To prevent peak shift by charging effect of the substrate, the CVD graphene was transferred onto Au-coated SiO2 substrate. We utilized monochromated Al as X-ray sources (Al Kα line: 1486.5 eV) and X-ray power of 12 kV and 3 mA. All measurements were carried out in vacuum (P < 5 × 10−9 mbar).
For the temperature-dependent electrical measurements in Fig. 3, the devices were placed on a commercial chip carrier with 32 leads and electrically contacted using aluminum wires with a wedge-wire bonder. Then the devices were loaded into cryostat, with a base temperature of 1 K. Conventional two-point and four-point lock-in measurements were performed using an SR830. For measurement of via and graphene gated devices in Fig. 4, measurements were performed in air at room temperature with a semiconductor parameter analyzer (Keithley 4200).
Two lasers of different wavelengths were focused on the center of the graphene membrane and used to actuate and detect the mechanical resonance. To actuate the membrane, a 623 nm diode laser was modulated electrically. The reflected light of a second 520 nm laser was monitored through the Si-based avalanche photodetector. The modulation frequency was tuned and monitored using a spectrum analyzer to find the resonance frequency. The measurements were performed in an optical cryostat at < 5 μTorr to reduce damping of the membrane.
Simulation of the FG–metal interface
The atomic-scale structure and charge distribution of the interface between metal and FG shown in Fig. 3e and Supplementary Figure 14 was simulated using density functional theory40,41 implemented in VASP42 in conjunction with projected augmented wave43. The generalized gradient approximation of Perdew–Burke–Ernzerhof44 was applied to describe the exchange-correlation functional. An energy cutoff of 350 eV was chosen for the plane wave basis and achieves convergence of the total energy of both Pd and Cr and graphene sheet to within 0.01 eV of the total energy. Geometry optimization allowed relaxation until the forces on each atom were < 0.1 eV/Å. A 64-atom supercell of graphene and 7 layers of Pd (111) (or Cr (111)) were used to describe the metal electrode, which is sufficient to recover bulk-like properties in the interior of the slab. Within GGA-PBE, the graphene lattice constant was 2.47 Å, and in our simulations, the Pd metal electrodes are under 3% compressive strain due to lattice mismatch with the graphene membrane. In each supercell, 20 Å of vacuum is included to avoid interaction between adjacent images in the z-direction. A 4 × 8 × 1 mesh was used to sample the system k-space. Furthermore, graphene or fluorinated graphene was introduced on both sides of the metal to maintain symmetry in the supercells and to avoid spurious introduction of electric fields and dipole moments across the supercell.
The authors declare that all data supporting the findings of this study are available within the paper and its supplementary information files.
Cui, X. et al. Multi-terminal transport measurements of MoS2 using a van der Waals heterostructure device platform. Nat. Nanotechnol. 10, 534–540 (2015).
Novoselov, K. S., Mishchenko, A., Carvalho, A. & Castro Neto, A. H. 2D materials and van der Waals heterostructures. Science 353, aac9439 (2016).
Duong, D. L., Yun, S. J. & Lee, Y. H. van der Waals layered materials: opportunities and challenges. ACS Nano 11, 11803–11830 (2017).
Jariwala, D., Marks, T. J. & Hersam, M. C. Mixed-dimensional van der Waals heterostructures. Nat. Mater. 16, 170–181 (2017).
Frisenda, R. et al. Recent progress in the assembly of nanodevices and van der Waals heterostructures by deterministic placement of 2D materials. Chem. Soc. Rev. 47, 53–68 (2018).
Wang, H. et al. Integrated circuits based on bilayer MoS2 transistors. Nano Lett. 12, 4674–4680 (2012).
Guerriero, E. et al. Gigahertz integrated graphene ring oscillators. ACS Nano 7, 5588–5594 (2012).
Withers, F. et al. Light-emitting diodes by band-structure engineering in van der Waals heterostructures. Nat. Mater. 14, 301–306 (2015).
Britnell, L. et al. Resonant tunnelling and negative differential conductance in graphene transistors. Nat. Commun. 4, 1794 (2013).
van der Zande, A. M. et al. Large-scale arrays of single-layer graphene resonators. Nano Lett. 10, 4869–4873 (2010).
Nagashio, K., Nishimura, T., Kita, K. & Toriumi, A. Contact resistivity and current flow path at metal/graphene contact. Appl. Phys. Lett. 97, 143514 (2010).
Xia, F., Perebeinos, V., Lin, Y., Wu, Y. & Avouris, P. The origins and limits of metal-graphene junction resistance. Nat. Nanotechnol. 6, 179–184 (2011).
Wang, L. et al. One-dimensional electrical contact to a two-dimensional material. Science 342, 614–617 (2013).
Giubileo, F. & Di Bartolomeo, A. The role of contact resistance in graphene field-effect devices. Prog. Surf. Sci. 92, 143–175 (2017).
Gao, Q. & Guo, J. Role of chemical termination in edge contact to graphene. APL Mater. 2, 056105 (2014).
Huang, Y. et al. An innovative way of etching MoS2: characterization and mechanistic investigation. Nano Res. 6, 200–207 (2013).
Robinson, J. T. et al. Graphene strained by defects. ACS Nano 11, 4745–4752 (2017).
Williams, K. R. et al. Etch rates for micromachining processing. J. Microelectromech. S. 5, 256–269 (1996).
Roy, T. et al. Field-effect transistors built from all two-dimensional material components. ACS Nano 8, 6259–6264 (2014).
Zhang, R., Drysdale, D., Koutsos, V. & Cheung, R. Controlled layer thinning and p-type doping of WSe2 by vapor XeF2. Adv. Funct. Mater. 27, 1702455 (2017).
Nair, R. R. et al. Fluorographene: a two-dimensional counterpart of teflon. Small 6, 2877–2884 (2010).
Robinson, J. T. et al. Properties of fluorinated graphene films. Nano Lett. 10, 3001–3005 (2010).
Stine, R., Lee, W. K., Whitener, K. E., Robinson, J. T. & Sheehan, P. E. Chemical stability of graphene fluoride produced by exposure to XeF2. Nano Lett. 13, 4311–4316 (2013).
Kashtiban, R. J. et al. Atomically resolved imaging of highly ordered alternating fluorinated graphene. Nat. Commun. 5, 4902 (2014).
Rangarajan, A., Wood, J., Koepke, J. & Lyding, J. Graphene as an etch mask for silicon. http://hdl.handle.net/2142/72832 (2014).
Fang, C., Shapter, J. G., Voelcker, N. H. & Ellis, A. V. Graphene masks as passivation layers in the electrochemical etching of silicon. J. Mater. Sci. 49, 7819–7823 (2014).
Kim, J., Lee, D. H., Kim, J. H. & Choi, S. H. Graphene-assisted chemical etching of silicon using anodic aluminum oxides as patterning templates. ACS Appl. Mater. Interfaces 7, 24242–24246 (2015).
Hwang, E. H. & Das Sarma, S. Acoustic phonon scattering limited carrier mobility in two-dimensional extrinsic graphene. Phys. Rev. B 77, 115449 (2008).
Pizzocchero, F. et al. The hot pick-up technique for batch assembly of van der Waals heterostructures. Nat. Commun. 7, 11894 (2016).
Bunch, J. S. et al. Impermeable atomic membranes from graphene sheets. Nano Lett. 8, 2458–2462 (2008).
Berry, V. Impermeability of graphene and its applications. Carbon 62, 1–10 (2013).
Liu, Y. et al. Basal plane fluorination of graphene by XeF2 via a radical cation mechanism. J. Phys. Chem. Lett. 6, 3645–3649 (2015).
Ji, X., Zhang, J., Wang, Y., Qian, H. & Yu, Z. A theoretical model for metal–graphene contact resistance using a DFT–NEGF method. Phys. Chem. Chem. Phys. 15, 17883–17886 (2013).
Giovannetti, G. et al. Doping graphene with metal contacts. Phys. Rev. Lett. 101, 026803 (2008).
Lee, C. H. et al. Atomically thin p–n junctions with van der Waals heterointerfaces. Nat. Nanotechnol. 9, 676–681 (2014).
Kim, Y. D. et al. Ultrafast graphene light emitters. Nano Lett. 18, 934–940 (2018).
Chen, C. & Hone, J. Graphene nanoelectromechanical systems. Proc. IEEE 101, 1766–1779 (2013).
Chen, C. et al. Performance of monolayer graphene nanomechanical resonators with electrical readout. Nat. Nanotechnol. 4, 861–867 (2009).
Lee, G.-H. et al. High-strength chemical-vapor-deposited graphene and grain boundaries. Science 340, 1073–1076 (2013).
Hohenberg, P. & Kohn, W. Inhomogeneous electron gas. Phys. Rev. 136, B864–B871 (1962).
Kohn, W. & Sham, L. J. Self-consistent equations including exchange and correlation effects. Phys. Rev. 140, A1133–A1138 (1951).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
This research was primarily supported by the National Science Foundation MRSEC program under NSF Award Number DMR-1720633. Work at Yonsei was funded by Samsung Research Funding & Incubation Center of Samsung Electronics under Project Number SRFC-MA1502-12. Y.L. and P.Y.H. were supported by the Air Force Office of Scientific Research under award number FA9550-7-1-0213; R.G.M acknowledges funding by DOE Basic Energy Sciences under DESC0012649. This work was carried out in part in the Fredrick-Seitz Material Research Laboratory Central Facilities and the Micro and Nano Technology Laboratory at UIUC. K.W. and T.T. acknowledge support from the Elemental Strategy Initiative conducted by the MEXT, Japan and JSPS KAKENHI Grant Numbers JP15K21722.
The authors declare no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Son, J., Kwon, J., Kim, S. et al. Atomically precise graphene etch stops for three dimensional integrated systems from two dimensional material heterostructures. Nat Commun 9, 3988 (2018). https://doi.org/10.1038/s41467-018-06524-3
Nature Materials (2022)
Nature Materials (2020)
Scientific Reports (2019)