Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Efficient generation of neutral and charged biexcitons in encapsulated WSe2 monolayers


Higher-order correlated excitonic states arise from the mutual interactions of excitons, which generally requires a significant exciton density and therefore high excitation levels. Here, we report the emergence of two biexcitons species, one neutral and one charged, in monolayer tungsten diselenide under moderate continuous-wave excitation. The efficient formation of biexcitons is facilitated by the long lifetime of the dark exciton state associated with a spin-forbidden transition, as well as improved sample quality from encapsulation between hexagonal boron nitride layers. From studies of the polarization and magnetic field dependence of the neutral biexciton, we conclude that this species is composed of a bright and a dark excitons residing in opposite valleys in momentum space. Our observations demonstrate that the distinctive features associated with biexciton states can be accessed at low light intensities and excitation densities.


The strong Coulomb interaction in two-dimensional transition metal dichalcogenide (TMDCs) crystals, arising from reduced dielectric screening in the atomically thin limit, significantly modifies the optical properties of these materials and gives rise to pronounced excitonic effects1. The Coulomb attraction between electrons and holes in these systems leads to the formation of tightly bound excitons, which causes a reduction in the optical band gap by a large fraction of an electron volt and yields very short intrinsic radiative lifetimes2,3,4,5. Both trion (charged exciton) and biexciton (exciton molecule) states have been observed in TMDCs6,7,8. Here we report on the characterization of a second biexciton species in monolayer WSe2, in addition to the previously observed species7, which we identify as the neutral and negatively charged biexciton (four-particle and five-particle) states, respectively. In our high-quality samples produced using encapsulation in hexagonal boron nitride (hBN), local inhomogeneities and nonradiative decay channels in the monolayer semiconductor are strongly reduced. As a consequence, the emission of the neutral and charged biexciton is observed at an excitation density three orders of magnitude lower than in previous reports. By comparing the emission of the different exciton species under strong magnetic fields and as a function of doping level, we deduce that the neutral biexciton is formed predominantly from the combination of a dark (spin-forbidden) and bright (spin-allowed) exciton residing in opposite valleys in momentum space. Our observations provide new understanding of many-body excited states in 2D semiconductors and open a path for utilizing the features of biexcition states for quantum and optoelectronic applications at low light intensities.

The lowest lying interband transition in monolayer tungsten compounds of the TMDC family has been identified as spin-forbidden9. The exciton associated with the lower conduction band therefore, to first order, does not emit light; it is referred to as a dark exciton. The existence of dark excitons strongly influences the optical properties of the material, including the photoluminescence (PL) quantum efficiency at low temperatures10, the ultranarrow linewidth of the PL emission along the in-plane direction11, the efficient coupling to surface plasmon polaritons12, and the large tip-induced enhancement of the PL13. Because the dark exciton has a lifetime that is orders of magnitude longer than the bright exciton at low temperature14, the steady-state density of dark excitons can be much higher than that of bright excitons for continuous-wave excitation. Correspondingly, the diffusion length of the dark exciton is also enhanced. When a dark exciton approaches another exciton, the two excitons can interact to form a biexciton (Fig. 1a). Therefore, the formation of biexcitons via the long-lived dark exciton states is much more likely than through two short-lived bright excitons. Here we report the observation of a neutral and charged biexciton composed of both bright and dark excitons.

Fig. 1
figure 1

Observation of a biexciton composed of a bright (spin-allowed) and a dark (spin-forbidden) exciton. a Schematic of biexciton formation in real space. Because the dark exciton (XD, dark blue) has a total spin of 1, it has a much longer radiative lifetime and therefore a much higher density than the bright exciton (X0, light blue), which has a total spin of zero. A biexciton (XX, green circle) can form as a bright and a dark exciton approach one another. b Representation of the biexciton in momentum space. c Photoluminescence (PL) spectra of an encapsulated WSe2 monolayer sample for different excitation intensities. All spectra are normalized to the X0 peak. A new peak (green shading) emerges at high excitation levels and is attributed to biexciton emission. The XX peak is located at 1.703 eV, 20 meV below the X0 peak. The XD peak at 1.681 eV is identified by examining its distinct radiation pattern. Other peaks are discussed in the main text. d Power dependence of the emission of different excitonic species. Datapoints and errorbars are results of pseudoVoigt fits to the raw spectra. The XX peak grows superlinearly with incident intensity with an exponent of 1.96. In contrast, the X0 and XD peaks have exponents of 1.22 and 1.03, respectively


Observation of biexcitons in the charge-neutral regime

We observe the evidence of a biexciton in our high-quality encapsulated WSe2 samples (see Methods). In these samples, the defect density of the TMDC is reduced by about two orders of magnitude (5 × 1010 cm−2) by exfoliating flux-grown crystals. The observed bright exciton linewidth (FWHM 4.5 meV at 20 K) is approaching the radiative limit15. In the low-temperature PL spectrum, the spin-allowed bright exciton emission appears at 1.723 eV (Fig. 1c). Emission from the spin-forbidden dark exciton with a linewidth of only 0.8 meV and an out-of-plane dipole radiation pattern (Supplementary Fig. 1) is observed at 1.681 eV, in agreement with previous reports11,12. As the excitation power is increased, a new peak emerges at 1.703 eV, lying 20 meV below the bright exciton peak. Compared to the emission of the bright and dark exciton species, which rise nearly linearly with laser intensity, the new peak increases approximately quadratically. A power-law fit of the emission yields an exponent of 1.96 ± 0.03 (Fig. 1d). The quadratic intensity dependence suggests that the peak arises from a few-body state formed from two excitons, each exhibiting a concentration growing linearly with intensity (Supplementary Note 2). The new biexciton peak, we should note, is observed for rather weak continuous wave (cw) excitation, with an irradiance of 1.4 × 103 W/cm2, more than three orders of magnitude lower than in typical experiments employing pulsed laser excitation7. The asymmetric peak Xi, lying 32 meV below X0, and the series of peaks around 1.665 eV have been attributed to indirect (momentum-dark) excitons16. The lower-lying emission peaks also originate from the WSe2 sample, but have an unknown origin and are beyond the scope of this work.

Spin and valley configuration of the biexciton

In the following, we focus on identifying the composition of the newly observed biexciton state. Regarding the spin degree of freedom, biexcitons can be classified as composed of dark–dark, dark–bright, and bright–bright exciton components. (Here we assume the electron and hole of the constituent excitons remain in the same band when forming a biexciton.) The emission energy of the biexciton precludes it from being composed of two dark excitons, as this would require a negative binding energy. The bright–bright configuration is unlikely to occur given our experimental conditions: At the greatest applied laser intensity, we estimate an upper limit of 52 μm−2 of bright excitons in the steady state, for a 2-ps lifetime of the bright exciton5 and assuming a 100% conversion efficiency from absorbed photons to bright excitons. This density is smaller than the dark exciton density at our lowest excitation level, as the dark exciton has a lifetime more than 50 times longer than the bright species, as reported by Robert et al.14 and confirmed in our sample. The low density of bright excitons renders the bright–bright biexciton much less likely to form. (A simple kinetic model is presented in Supplementary Note 3 to describe the biexciton formation process.) We therefore conclude that the observed biexciton is a combination of one bright and one dark exciton (Fig. 1b). This assignment is further supported by the magnetic field and doping dependences of the biexciton emission, as discussed below.

To investigate the biexciton valley configuration further, we apply a strong out-of-plane magnetic field, which acts to break the valley degeneracy. As a magnetic field along the normal direction of the sample shifts the conduction and valence bands in the different valleys in opposite directions, the exciton peaks are split into pairs17,18,19 associated with their valley index. Since the dark exciton has a total spin angular momentum of 1, its Zeeman splitting is larger than that of the bright exciton14 with its vanishing total spin. As the emission of the biexciton results from its bright component, leaving behind a dark exciton in the final state, the biexciton emission energy is given by the bright exciton emission energy reduced by the biexciton binding energy ΔXX (see Methods). Neglecting any difference in magnetic field dependence of the (small) biexciton binding energy ΔXX, we predict within our picture that the XX peak should exhibit the same g-factor as the bright exciton. This agrees with our experimental observations: X0 and XX have g-factors of 4.4 ± 0.5 and 4.6 ± 0.5, respectively, while XD has a g-factor of 9.6 ± 0.5 (Fig. 2a).

Fig. 2
figure 2

Zeeman splitting and non-equilibrium distribution of biexciton emission. a A strong out-of-plane magnetic field splits most emission peaks into pairs. The splitting of XX is similar to that of the X0 feature (g-factor 4.4 ± 0.5), whereas the splitting of the XD feature is larger because of its non-zero spin. b The ratios of amplitudes of the fitted low-energy branch (LEB) and high-energy branch (HEB) of the emission spectra. Unlike the XD pair, the XX emission pair exhibits inverted populations between the HEB and LEB. The LEB/HEB ratio of the XX pair is similar to that of X0/XD. The error bars for X0, XD, and XX are conservative estimates. c A diagram of the biexciton intervalley configuration as probed through the PL measurements in a magnetic field. The B-field splits the bright (light blue) and dark (dark blue) exciton into pairs according to their valley index (K, K′). Analysis of the PL intensities shows that the biexciton is composed of excitons from different valleys

The distribution of the exciton population between the different branches of the Zeeman-split pairs will, in thermal equilibrium, follow a Boltzmann distribution. This suggests that even for a partially thermalized system, which starts from equal populations when degenerate, the low-energy branch (LEB) of the pair should have a larger population, and thus emit more light, than the high-energy branch (HEB). This relation is satisfied for the pairs of dark excitons and most of the features seen in the PL. However, for the bright exciton pair, the emission intensity is comparable, and in some conditions inverted. Such an unusual distribution might arise from the efficient intervalley scattering between two conduction bands of same spin (see Supplementary Note 4 for a detailed discussion). More importantly, the emission intensity from the biexciton pair is also observed to be inverted, with an inversion even more pronounced than for the bright exciton. This observation suggests the biexciton to be composed of a bright and a dark exciton residing in opposite valleys. In the intervalley configuration (Fig. 2c), the dark component in the HEB (LEB) of the biexciton is associated with the LEB (HEB) of the dark exciton17. We expect that the rate of biexciton formation should scale as the product of the constituent exciton densities, that is \(\propto \rho _{{\mathrm {X}}^{\mathrm{D}}{\mathrm{,L(H)}}} \cdot \rho _{{\mathrm {X}}^{\mathrm{0}}{\mathrm{,H(L)}}}\). If the density of biexcitons ρXX,H(L) is much smaller than that of bright excitons, after being normalized to their lifetimes, the biexciton density will scale in the same fashion (see Supplementary Note 2). With the experimentally observed larger population of the dark exciton in the LEB, an intervalley configuration of the biexciton leads naturally to an inverted distribution for the biexciton emission. More quantitatively, the LEB/HEB ratio of the biexciton pair should be close to the quotient of the ratios observed in the bright and dark exciton pairs, a result consistent with our experimental findings at different magnetic fields (Fig. 2b).

The fact that the intervalley configuration of the biexciton is favored over other configurations can be understood in terms of energetics. The intravalley configuration—bright and dark excitons residing in the same valley—needs to involve two holes sharing the same valence band, which costs extra energy as Pauli blocking forces the second hole to occupy a higher momentum/energy state (the footprint of an exciton in momentum space can be approximated by the inverse of the exciton Bohr radius of about 1 nm). Another possible configuration would be that of a biexciton composed of a direct and an indirect exciton—two electrons are located in different bands of the same valley, but with the two holes in opposite valleys. This configuration costs extra exchange energy, which should be about 10 meV as inferred from the peak separation between the two negatively charged trions20,21. Within our experiment, we cannot, however, exclude potential contributions from Q point indirect excitons22.

Distinguishing neutral and negatively charged biexcitons

Finally, we are able to elucidate the relationship between the newly observed and the previously reported biexciton7 by tuning the static carrier density in the material (Fig. 3a). In the low excitation regime, the emission spectra agree well with those reported in the literature: the bright and dark excitons are observed in the intrinsic regime while different types of trions emerge in the n-doped and p-doped regimes20,21. Unlike the bright exciton state, which extends to finite doping levels with an asymmetric gate dependence, the dark exciton is strictly limited to the intrinsic regime. Under stronger excitation conditions (~4 × 103 W cm−2), the biexciton peak at 1.703 eV appears, and its emission is also restricted to the intrinsic regime. The doping dependence therefore confirms that this newly observed XX peak results from a neutral biexciton formed by a bright and a dark exciton, as it appears only in the doping regime where both types of excitons coexist (Fig. 3b).

Fig. 3
figure 3

Doping dependence of the PL emission of neutral and charged biexcitons. a Gate dependence map of the PL intensity above the onset for observing both biexciton species (I0 = 4 × 103 W cm−2). The intrinsic regime is characterized by the strong emission from XD. In the n-doped and p-doped regimes, trions and other species emerge. The XX peak at 1.703 eV is only observed in the intrinsic regime, indicating a neutral biexciton composed of a neutral X0 and XD. Another peak with superlinear power dependence is observed at 1.671 eV, 52 meV below X0. It is assigned to a charged biexciton state, as it appears only in the low n-doped regime. b Normalized PL intensity of the exciton species relevant for the formation of biexcitons as a function of doping level. The neutral biexciton (green) emission is limited to the intrinsic regime, in which XD (dark blue) is observed, showing the important role of XD in the formation of XX. The XX emission (dark red) is strongest in the low n-doped regime, where X0 (light blue), XD and the two X species coexist (light red, only lower X shown for clarity)

Under strong excitation conditions, the emission of another biexciton is observed in our spectra, which exhibits a superlinear power dependence with an emission strength scaling with the pump laser intensity as I1.56 (Supplementary Fig. 2). This peak lies 52 meV below the bright exciton and has been reported in the literature7. However, this biexciton only appears at the crossover from the intrinsic to the n-doped regime (Fig. 3b), suggesting that it is a negatively charged biexciton XX, formed from a trion and a neutral exciton, as opposed to its earlier assignment as a neutral biexciton7. In contrast to the negatively charged trions, no fine features can be resolved in the XX peak at this stage. If no more than one electron/hole resides in any band, there should be two spin-valley configurations for XX. Due to the conduction band splitting, we expect the energetically favored configuration to be two holes in opposite valence band valleys, two electrons in opposite lower conduction band valleys and one electron in the higher conduction band. Because the valence band splitting is much larger—about 400 meV—no positively charged biexciton (XX+) emission would be observed. Since the XX peak appears most prominently at relatively low doping levels, we can rule out the possibility of it being related to a plasmon coupled exciton23. With respect to the two negatively charged trions, the XX has a binding energy of 14 or 21 meV, in agreement with theoretical calculations24.


The identification of neutral and charged biexcitons resolves the discrepancy of the biexciton binding energy found between previous experiments and theories: as calculated, the biexciton binding energy is indeed smaller than the trion binding energy due to the form of the screened Coulomb potential in two-dimensional TMDCs24,25,26,27,28. The 20-meV binding energy also matches that of the neutral biexciton in MoSe2 monolayers observed by Hao et al. using two-dimensional coherent spectroscopy8 and of WSe2 in pump-probe spectroscopy29, even though both works describe bright–bright excitons, which would suggest the biexciton binding energy is only weakly sensitive to the spin configuration of the two constituent excitons.

In conclusion, we have observed neutral and charged biexciton species in monolayer WSe2 crystals encapsulated in hBN through their clear emission signatures. We have established that the neutral biexciton is composed of pairs of excitons located in opposite valleys, one of which is a long-lived dark species. Our observations deepen the understanding of the intrinsic optical properties of two-dimensional TMDCs and provides a new route to access the optical response associated with biexciton species under conditions of modest excitation.



Single crystals were grown by sealing W powder, 99.999% purity, and Se shot, 99.999% purity, in an evacuated quartz ampoule with excess Se as the flux. Subsequently, the ampoule was heated to 1000 °C for 2 days and cooled to 450 °C at a rate of 0.85 °C h−1. The crystals were removed, centrifuged, and annealed at 250 °C for 2 days to remove excess Se. Encapsulated monolayers of WSe2 were then prepared from these single crystals by a dry stamping technique30, with all materials exfoliated on Si/SiO2 substrates. In order to contact the WSe2 film, two few-layer graphene strips were picked up by an hBN flake, followed by the monolayer WSe2. Finally, a bottom (Ar/O2 cleaned) hBN crystal and a thin layer of graphite were picked up to act as the backgate for controlling doping and screening the effects of the SiO2. Contact was made to the graphite leads and backgate by etching with CHF3 and making edge contact using Cr/Pd/Au film deposition (2/25/50 nm).


In all but the magnetic field experiments, the samples were mounted in a continuous flow optical cryostat and cooled with liquid helium to temperatures of 15 K. PL spectra were taken with an imaging spectrometer after 640 nm cw laser excitation. We note that for laser excitation at shorter wavelengths (e.g., 532 nm), we observed photodoping of the sample starting at moderate power levels. Spectra on bare hBN were taken to verify that all features in Fig. 1b originate from the WSe2 sample. Magnetic field measurements were conducted at the National High Magnetic Field Laboratory, at sample temperatures of 10 K and cw laser excitation at 660 nm. The PL spectra were fitted with a series of psedudoVoigt lineshapes to obtain the emission intensity (area) as a function of the relevant experimental parameters.

Biexciton binding energy

The binding energy Δ of the neutral biexciton is obtained from the relation for energy conservation in the formation and radiative decay of the biexciton species: \(E_{{\mathrm{X}}^{\mathrm{0}}} + E_{{\mathrm{X}}^{\mathrm{D}}} - {\mathrm{\Delta }}\) = \(\hbar \omega _{{\mathrm{XX}}} + E_{{\mathrm{X}}^{\mathrm{D}}}\). Here we consider a biexciton formed from a pair of bright and dark excitons and assume that the final state after radiative decay is a dark exciton in its ground state. It follows that the biexciton binding energy is directly related to experimentally observable emission energies through Δ = \(E_{{\mathrm{X}}^{\mathrm{0}}} - \hbar \omega _{{\mathrm{XX}}}\).

Data availability

The data supporting the plots within this paper and other findings of this study are available from the corresponding author upon request.


  1. Wang, G. et al. Excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 90, 21001 (2018).

    Article  Google Scholar 

  2. He, K. et al. Tightly bound excitons in monolayer WSe2. Phys. Rev. Lett. 113, 026803 (2014).

    ADS  Article  CAS  PubMed  Google Scholar 

  3. Ye, Z. et al. Probing excitonic dark states in single-layer tungsten disulfide. Nature 513, 214–218 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  4. Chernikov, A. et al. Exciton binding energy and nonhydrogenic rydberg series in monolayer WS2. Phys. Rev. Lett. 113, 076802 (2014).

    ADS  Article  CAS  PubMed  Google Scholar 

  5. Robert, C. et al. Exciton radiative lifetime in transition metal dichalcogenide monolayers. Phys. Rev. B 93, 205423 (2016).

    ADS  Article  CAS  Google Scholar 

  6. Mak, K. F., He, K., Shan, J. & Heinz, T. F. Control of valley polarization in monolayer MoS2 by optical helicity. Nat. Nanotechnol. 7, 494–498 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  7. You, Y. et al. Observation of biexcitons in monolayer WSe2. Nat. Phys. 11, 477–482 (2015).

    CAS  Article  Google Scholar 

  8. Hao, K. et al. Neutral and charged inter-valley biexcitons in monolayer MoSe2. Nat. Commun. 8, 15552 (2017).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  9. Zhang, X. X. et al. Magnetic brightening and control of dark excitons in monolayer WSe2. Nat. Nanotechnol. 12, 883–888 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  10. Zhang, X.-X., You, Y., Zhao, S. Y. F. & Heinz, T. F. Experimental evidence for dark excitons in monolayer WSe2. Phys. Rev. Lett. 115, 257403 (2015).

    ADS  Article  CAS  PubMed  Google Scholar 

  11. Wang, G. et al. In-plane propagation of light in transition metal dichalcogenide monolayers: optical selection rules. Phys. Rev. Lett. 119, 047401 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  12. Zhou, Y. et al. Probing dark excitons in atomically thin semiconductors via near-field coupling to surface plasmon polaritons. Nat. Nanotechnol. 12, 856–860 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  13. Park, K. D., Jiang, T., Clark, G., Xu, X. & Raschke, M. B. Radiative control of dark excitons at room temperature by nano-optical antenna-tip Purcell effect. Nat. Nanotechnol. 13, 59–64 (2018).

    ADS  CAS  Article  PubMed  Google Scholar 

  14. Robert, C. et al. Fine structure and lifetime of dark excitons in transition metal dichalcogenide monolayers. Phys. Rev. B 96, 155423 (2017).

    ADS  Article  Google Scholar 

  15. Ajayi, O. A. et al. Approaching the intrinsic photoluminescence linewidth in transition metal dichalcogenide monolayers. 2D Mater. 4, 031011 (2017).

    Article  CAS  Google Scholar 

  16. Lindlau, J. et al. Identifying optical signatures of momentum-dark excitons in transition metal dichalcogenide monolayers. Preprint at (2017).

  17. Aivazian, G. et al. Magnetic control of valley pseudospin in monolayer WSe2. Nat. Phys. 11, 148–152 (2015).

    CAS  Article  Google Scholar 

  18. Li, Y. et al. Valley splitting and polarization by the zeeman effect in monolayer MoSe2. Phys. Rev. Lett. 113, 266804 (2014).

    ADS  Article  CAS  PubMed  Google Scholar 

  19. Macneill, D. et al. Breaking of valley degeneracy by magnetic field in monolayer MoSe2. Phys. Rev. Lett. 114, 037401 (2015).

    ADS  Article  CAS  PubMed  Google Scholar 

  20. Plechinger, G. et al. Trion fine structure and coupled spin-valley dynamics in monolayer tungsten disulfide. Nat. Commun. 7, 12715 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  21. Courtade, E. et al. Charged excitons in monolayer WSe2: experiment and theory. Phys. Rev. B 96, 085302 (2017).

    ADS  Article  Google Scholar 

  22. Zhang, C. et al. Probing critical point energies of transition metal dichalcogenides: surprising indirect gap of single layer WSe2. Nano Lett. 15, 6494–6500 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  23. Van Tuan, D., Scharf, B., Zutić, I. & Dery, H. Marrying excitons and plasmons in monolayer transition-metal dichalcogenides. Phys. Rev. X 7, 041040 (2017).

    Google Scholar 

  24. Kylänpää, I. & Komsa, H. P. Binding energies of exciton complexes in transition metal dichalcogenide monolayers and effect of dielectric environment. Phys. Rev. B 92, 205418 (2015).

    ADS  Article  CAS  Google Scholar 

  25. Zhang, D. K., Kidd, D. W. & Varga, K. Excited biexcitons in transition metal dichalcogenides. Nano Lett. 15, 7002–7005 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  26. Mayers, M. Z., Berkelbach, T. C., Hybertsen, M. S. & Reichman, D. R. Binding energies and spatial structures of small carrier complexes in monolayer transition-metal dichalcogenides via diffusion Monte Carlo. Phys. Rev. B 92, 161404(R) (2015).

    ADS  Article  CAS  Google Scholar 

  27. Kidd, D. W., Zhang, D. K. & Varga, K. Binding energies and structures of two-dimensional excitonic complexes in transition metal dichalcogenides. Phys. Rev. B 93, 125423 (2016).

    ADS  Article  CAS  Google Scholar 

  28. Szyniszewski, M., Mostaani, E., Drummond, N. D. & Fal’ko, V. I. Binding energies of trions and biexcitons in two-dimensional semiconductors from diffusion quantum Monte Carlo calculations. Phys. Rev. B 95, 081301(R) (2017).

    ADS  Article  Google Scholar 

  29. Steinhoff, A. et al. Biexciton fine structure in monolayer transition metal dichalcogenides. Preprint at (2018).

  30. Castellanos-Gomez, A. et al. Deterministic transfer of two-dimensional materials by all-dry viscoelastic stamping. 2D Mater. 1, 011002 (2014).

    Article  CAS  Google Scholar 

Download references


The authors thank Timothy Berkelbach and Ting Cao for fruitful discussions. The spectroscopic studies were supported by the Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division, under Contract DE-AC02-76SF00515 for the magnetic field measurements and by the Gordon and Betty Moore Foundation’s EPiQS Initiative through Grant no. GBMF4545 for analysis. Sample preparation was supported by the National Science Foundation MRSEC program through Columbia in the Center for Precision Assembly of Superstratic and Superatomic Solids (DMR-1420634). L.W. acknowledges support by the Alexander von Humboldt Foundation. Y.J., Z.L. and D.S. acknowledge support from the US Department of Energy (DE-FG02-07ER46451) for magneto-photoluminescence measurements performed at the National High Magnetic Field Laboratory, which is supported by the NSF Cooperative Agreement no. DMR-1157490 and the State of Florida.

Author information

Authors and Affiliations



Z.Y., L.W. and T.F.H. conceived the project. D.R., A.A. and B.K. grew the WSe2 crystals and prepared encapsulated and backgated samples. K.W. and T.T. produced the hBN crystals. Z.Y., L.W., E.Y.M., Y.J., X.Z. and M.D. conducted the measurements. Z.Y. and L.W. analyzed the data. Z.Y., L.W. and T.F.H. wrote the manuscript with input from all authors.

Corresponding author

Correspondence to Tony F. Heinz.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ye, Z., Waldecker, L., Ma, E.Y. et al. Efficient generation of neutral and charged biexcitons in encapsulated WSe2 monolayers. Nat Commun 9, 3718 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing