Article | Open | Published:

# Bioinspired 3D structures with programmable morphologies and motions

## Abstract

Living organisms use spatially controlled expansion and contraction of soft tissues to achieve complex three-dimensional (3D) morphologies and movements and thereby functions. However, replicating such features in man-made materials remains a challenge. Here we report an approach that encodes 2D hydrogels with spatially and temporally controlled growth (expansion and contraction) to create 3D structures with programmed morphologies and motions. This approach uses temperature-responsive hydrogels with locally programmable degrees and rates of swelling and shrinking. This method simultaneously prints multiple 3D structures with custom design from a single precursor in a one-step process within 60 s. We suggest simple yet versatile design rules for creating complex 3D structures and a theoretical model for predicting their motions. We reveal that the spatially nonuniform rates of swelling and shrinking of growth-induced 3D structures determine their dynamic shape changes. We demonstrate shape-morphing 3D structures with diverse morphologies, including bioinspired structures with programmed sequential motions.

## Introduction

Nature has inspired researchers to develop shape-morphing materials that can replicate the functions of native soft tissues1,2. Such materials have applications in soft robotics, programmable matter, bioinspired engineering, and biomimetic manufacturing1,2,3,4,5,6,7,8,9,10,11,12. Existing approaches use swellable hydrogels3,4,5,6,7,8,13, shape-memory polymers14,15, and liquid crystalline elastomers16,17,18 with fabrication methods, such as photopatterning4,6,7,8,11, self-folding7,11,19,20, and three-dimensional (3D) printing5,15. These approaches have been used to build various self-shaping 3D structures, including those with complex 3D morphologies of living organisms4,5, but reproducing their movements has not been fully achieved1,2,21.

A promising approach in this regard is to use spatially controlled in-plane growth (expansion and contraction) of hydrogel sheets to form 3D structures via out-of-plane deformation (non-Euclidean plates)3,4. Because bending is energetically less expensive than stretching in a thin sheet, the internal stresses developed by nonuniform in-plane growth are released by out-of-plane deformation3,4. This approach defines 3D shapes with Gaussian curvatures22,23 and is uniquely capable of creating 3D structures with curved geometries, often seen in biological organisms but difficult to achieve by other methods4,5. Living organisms, ranging from plants to marine invertebrates, use such approaches (e.g., differential growth) for fundamental biological processes, including morphogenesis, complex growth and movement, and adaptation to environments3,4,5,13,24,25,26,27,28,29,30,31,32,33,34. With the physical properties of hydrogels similar to those of soft tissues7,12,33, this approach thus has great potential for creating bioinspired 3D structures4. In particular, the ability to spatially and temporally control the local in-plane growth could offer a new strategy to create dynamic 3D structures that can mimic the continuously deforming motions of living organisms1,2. However, dynamic growth-induced 3D motions of non-Euclidean plates remain largely unexplored3,4. Previous theoretical and experimental studies have mainly focused on the formation of 3D shapes at equilibrium states3,4,35,36,37, but their dynamic behavior at metastable states during shape transition is not well understood. Furthermore, the principle has been demonstrated for various 3D shapes3,4,37, but achieving nonaxisymmetric 3D structures with complex morphologies remains to be further studied34,35,36.

Here we show an approach named digital light 4D printing (DL4P) that creates dynamic 3D structures with programmed morphologies and motions (Fig. 1a). This approach encodes temperature-responsive 2D hydrogels with spatially and temporally controlled growth (expansion and contraction) functions Ω, or target metrics, which transforms the hydrogels into prescribed 3D structures and programs their motions. Previous studies of differential growth-induced 3D shaping have mostly formed single 3D shapes either at the swelled or the shrunk state3,4,5,38. In contrast, our temperature-responsive hydrogels with phototunable degrees and rates of swelling and shrinking allow us to define target 3D shapes at both the swelled and shrunk states. In particular, the ability to control the rates uniquely enables a new strategy for programming growth-induced 3D motions. This method simultaneously prints multiple 3D structures with custom design (using digital light projection grayscale lithography) from a single precursor solution in a one-step process within 60 s and is thus highly scalable. Taking advantage of our phototunable hydrogels and the flexible 2D printing method for 3D material programming (e.g., without the need for multiple physical masks or nozzles), we established simple yet versatile design rules and the concept of modularity for creating complex 3D structures with diverse morphologies4, including ray-inspired structures with programmed motions. To investigate the dynamic growth-induced motions, we introduced a concept of dynamic target metrics and developed a dynamic theoretical model based on the concept. Our experimental and theoretical studies reveal that the spatially nonuniform rates of swelling and shrinking of growth-induced 3D structures determine their dynamic shape changes. Furthermore, the swelling and shrinking rates of our hydrogels are phototunable and thus locally programmable. The ability to spatially control the rates of shape changes allows us to fabricate dynamic 3D structures with programmed sequential motions, as previously demonstrated with photopatterned hydrogels responsive to different molecular inputs (e.g., DNA molecules with different sequences) and those with different thicknesses8. Such ability is critical for implementing complex functions but challenging to attain with global external stimuli (e.g., temperature)8. This work introduces a 3D fabrication method with the advantages of traditional (scalable) and additive (customizable) manufacturing for fabricating soft devices with programmed 3D morphologies and motions.

## Results

### Hydrogels with phototunable material properties

Our DL4P approach relies on the ability to prepare temperature-responsive hydrogels with continuously varying compositions and thus material properties (e.g., degrees and rates of swelling and shrinking) from a single precursor solution through photopolymerization and crosslinking within 60 s (Fig. 1). The modulation of the material properties is based on the temporal control of polymerization and crosslinking reactions using two types of crosslinkers with different lengths by light exposure time tex. The phototunability provides a flexible means to encode the hydrogels with spatially and temporally controlled growth (swelling and shrinking), which can be used to program the formation of 3D structures and their motions.

The precursor solution consists of N-isopropylacrylamide (NIPAm), N,N′-methylene bisacrylamide (BIS; short-chain crosslinker), and poly(ethylene glycol) diacrylate (PEGDA; long-chain crosslinker). For an equimolar concentration of crosslinkers, crosslinking with PEGDA forms gels faster than with BIS, due to longer distances between the crosslinking points of PEGDA (Supplementary Figures 1, 2)39. The BIS- and PEGDA-crosslinked hydrogels swell and shrink in different degrees (Fig. 1b, c, Supplementary Figure 1).

### Shape-morphing 3D structures with axisymmetric metrics

To validate our DL4P approach and demonstrate its accuracy, we created well-defined geometric 3D structures with axisymmetric metrics (Fig. 2a–k). In contrast to previous studies, which mostly form 3D shapes at either the swelled or the shrunk state3,4,5, our approach can define the target 3D shapes at both the swelled (Ω > 1)and the shrunk (Ω < 1) states. The equilibrium 3D shape is selected from the competition between bending ($$E_{\mathrm{B}} \sim {t_{\mathrm{h}}}^3$$, where th is the thickness of a sheet) and stretching (Eth) energies3,38. As the thickness decreases, the hydrogel sheet thus converges to the stretch-free configuration that fully follows the target metric38. However, the actual metric adopted by experimental 3D structures differs from the target metric, because of a finite-thickness bending energy36,38. The structure at the shrunk state can thus yield a 3D shape closer to the theoretical configuration described by the target metric than one at the swelled state. In addition, the use of hydrogels at the shrunk state is beneficial for practical applications, for example, because of their enhanced mechanical properties and the formation of target shapes under physiological conditions (T = 37 °C) for potential biomedical applications44. We thus designed Ω for target shapes at the shrunk state.

We created spherical cap, saddle, and cone structures with constant Gaussian curvature K > 0, K < 0, and K = 0, respectively (Fig. 2a–c). We formed these structures by encoding hydrogels (400 μm in thickness) with Ω shown in Fig. 2g (see Supplementary Notes 13 for the theoretical model). The resulting structures agree quantitatively with the theoretical structures, reflecting the accuracy of our approach (Fig. 2d–f, Supplementary Note 3). For example, the experimentally measured K of the spherical cap and saddle structures are 0.0464 mm−2 and −0.0727 mm−2, which match well with the theoretically calculated K of 0.0468 mm−2 and −0.0722 mm−2, respectively. The cone structures constructed with different exponents α in Ω have the programmed value of the vertex angle β (β = sin−1α) (Fig. 2h, Supplementary Note 3). We further verified our approach by creating Enneper’s minimal surfaces (Fig. 2i, j) using Ω(r) = c[1 + (r/R)2(n′–1)]2, where r is a radial position and c, R, and n′ are constants (Fig. 2k)4. As expected, the growth functions with different n′ induce Enneper’s surfaces with the targeted number of wrinkles n′ (Fig. 2i–k, Supplementary Figure 5, Supplementary Movie 1).

The created structures reversibly transform between prescribed 3D shapes at the swelled and shrunk states in response to temperature change (Fig. 2a–c, j). The 3D structures at the swelled state adopt new metrics, determined by the areal swelling ratios (Fig. 1c) and the growth functions designed for the target shapes at the shrunk state. Because of the inverse relationship between the areal swelling and shrinking ratios (Fig. 1b, c), 3D shapes with K > 0 (e.g., spherical cap in Fig. 2a, right) at the shrunk state in general transform to 3D shapes with K< 0 at the swelled state (e.g., saddle-like shape in Fig. 2a, left) and vice versa (Fig. 2b).

In addition to determining Ω for a target 3D shape (Fig. 2a, c, Supplementary Note 3), we can predict the 3D shape for a given Ω (Fig. 2l, Supplementary Note 4). To validate the predictive power of the model, we considered a growth function in the form Ω(r) = c[1 + (r/R′)2]α−1, where R′ = aR and a and α are constants (Fig. 2l–n, Supplementary Note 4). The theoretical model predicts 3D shapes that consist of a spherical cap-like shape with a smooth gradient in K in the central region and a cone-like shape (K = 0) in the outer region (Fig. 2l, Supplementary Note 4). The experimental structures agree well with the theoretical predictions (Fig. 2l–n, Supplementary Figure 6). For example, the base angle γ of the experimental structures decreases with α, following the predictions (Fig. 2n, Supplementary Note 4). The examples in Fig. 2 illustrate the accuracy and sensitivity of our approach. Small changes in Ω can induce substantial changes in the resulting 3D shapes (e.g., Fig. 2i–k, Supplementary Figure 5)38.

### Design rules for creating complex 3D structures

We next sought to establish design rules for creating nonaxisymmetric 3D structures with diverse morphologies (Fig. 3). Our schemes involve the combination and transformation of target metrics and the concept of modularity. As they are implemented in the metric space, these schemes require design rules for how to interface metrics4. We thus introduced the concepts of linkers and transitional components at the interfaces of metrics. The radial and azimuthal combinations of growth functions yield hybrid 3D structures with alternating features of the functions along the r (Fig. 3a, b) and θ (Fig. 3c) directions, respectively, where θ is an angular position. For example, the radial combination of Ω1 for a spherical cap and Ω2 for a saddle shape induces a structure with K > 0 and K < 0 in the central and outer regions, respectively (Fig. 3a, Supplementary Figure 7). Another example is a hybrid structure that combines a spherical cap and a cone (Fig. 3b). The azimuthal combination of Ω1 (5° < θ < 85° and 185° < θ < 265°) and Ω2 (95° < θ < 175° and 275° < θ < 355°) shown in Fig. 3d yields a structure with alternating features of Ω1 and Ω2 along θ (Fig. 3c). We introduced a linear linker with a form ΩL = (Ω– Ω2)θθ + Ω2 with Δθ = 10° at the interfaces of Ω1 and Ω2 to make Ω continuous, as sharp discontinuities in Ω can cause stress accumulation and thereby shape distortion (e.g., hybrid Ω without linkers or linkers with θ = 5°, Supplementary Figure 8).

Transforming axisymmetric Ω into a function of θ in the form Ω(rθ) = c(θ)Ω(r/(a(θ)R)) leads to nonaxisymmetric structures with varying morphologies along θ (Fig. 3e–l). c(θ) scales Ω along θ. Therefore, transforming Ω(r) = c(r/R)Ωmin for a modified excess cone (Supplementary Figure 9)45,46 with c(θ) = c0cos2(), where Ωmin and L are constants, forms a shape with alternating K > 0 and K < 0 and a programmed number of nodes n′ = 2L (Fig. 3e–i, Supplementary Figure 9, Supplementary Movie 2). The resulting structures with 4 (L = 2) and 6 (L = 3) nodes are shown in Fig. 3e, f, respectively. The structures have the same number of nodes at the swelled and shrunk states (Fig. 3e–h). On the other hand, a(θ) in Ω(rθ) = cΩ(r/(a(θ)R)) scales Ω along r. This transformation defines the boundary of structures, while maintaining the functional form and thereby the shape along r. Transforming Ω for a saddle shape with $$a(\theta ) = \sqrt {1 + \left( {b^2 - 1} \right)\sin ^{2}\theta }$$ thus forms an elongated elliptical saddle structure with an aspect ratio of 1/b (0 < b < 1) (Fig. 3j, Supplementary Figure 10); an elongated saddle structure with an aspect ratio of 2 (b = 0.5) is shown in Fig. 3j. Interestingly, the directions of the principal curvatures at the center of the saddle structure align with the major and minor axes of the ellipse, suggesting that this configuration is an embedding of the lowest bending energy of the target metric. Furthermore, adding periodicity into Ω with $$a\left( \theta \right) = \sqrt {1 + \left( {b^2 - 1} \right)\sin ^2(L\theta) }$$ modulates the number of nodes n′ = 2L along θ. Using this transformation, we could form spherical cap and saddle-like structures with a targeted number of legs (Fig. 3k, l, Supplementary Figure 11). The examples in Fig. 3 show the versatility of our approach in creating diverse 3D morphologies. These structures can be further used as a building block for multimodular 3D structures (Fig. 4).

### Multimodular 3D structures

The modular assembly of target metrics can create 3D structures with broad morphological and functional diversity (Fig. 4, Supplementary Figure 12)4. However, there is an intrinsic problem in assembling modules in the metric space4. Each module can randomly adopt the direction of deformation (e.g., upward or downward)4 or the orientation with respect to other modules due to the symmetric nature of metrics. Thus, a multimodular Ω can in general form multiple different conformations presumably with the same elastic energy (as shown in previous work4 and Supplementary Figure 12). To tackle this problem, we introduced the concept of transitional components, designed to control the direction of deformation and the orientation of modular components (Fig. 4a–j). A saddle-like structure with K< 0 (e.g., Figs. 2b, 3j) has the principle curvatures with the same sign along its parallel edges. We thus postulated that modular components with K > 0 that share the parallel edges of a saddle-like structure (K < 0), or a parallel transitional component (e.g., small circles with dashed white lines in Fig. 4f–i), would deform in the same direction as the parallel edges. On the other hand, modular components with K > 0 that share the perpendicular edges of a saddle-like structure (K < 0), or a perpendicular transitional component (e.g., large circles with dashed white lines in Fig. 4f–i), would deform in the opposite directions. Figure 4a–d shows examples of multimodular structures with directional control, where the arrows indicate the programmed orientation of each module. Placing the parallel and perpendicular transitional components between modules (indicated by the small and large circles with white dashed lines in Fig. 4f–i, respectively) led to the multimodular structures with designed morphologies (Fig. 4a–d). In contrast, the modules in a control structure without transitional components tend to deform in the same direction, implying slight variations in shrinkage through the thickness; the variations make a specific direction energetically favorable for all modules (Fig. 4e, j).

The design rules established in this work (Figs. 3, 4) offer simple yet versatile ways to build complex 3D structures without the need for extensive computation. To demonstrate this capability, we fabricated ray-inspired 3D structures that replicate the key morphological features of stingrays, including the pectoral fins with K < 0 (Fig. 4k–n)21,47. We designed multimodular structures based on the reconstructed 3D images, K, and swimming motions of stingrays (Fig. 4k, l, Supplementary Figure 13)21,47. The growth functions for the body and the pectoral fins were designed and merged with linear linkers (Fig. 4l), using the design rules shown in Figs. 3, 4a–j (Supplementary Note 5). For example, the module for the body structure with the linkers was used as a transitional component that controls the orientation of the left and right pectoral fins with respect to the body and thus synchronizes their motions (Supplementary Figure 14). Furthermore, the ray-inspired structures were designed to produce different types of oscillatory flapping motions in response to temperature cycles (between 31.5 °C and 33.5 °C), mimicking those of stingrays (Supplementary Movies 3, 4).

### Dynamic behavior of growth-induced 3D structures

We next explored how growth-induced 3D structures transform their shapes (Fig. 5). To elucidate the underlying mechanism of the shape evolution, we introduced the concept of dynamic target metrics (Fig. 5a–e). To verify this concept, we used a spherical cap structure shown in Fig. 2a as our model system. Figure 5a shows the shape evolution of a spherical cap. Despite its simple shapes at equilibrium (swelled and shrunk states), the structure undergoes complex shape transformations. Our results reveal that the spatially nonuniform rates of swelling and shrinking of growth-induced 3D structures determine their dynamic shape changes as described below.

To understand the dynamic behavior, we first measured AT/A0 of homogeneous hydrogels (i.e., hydrogel disks uniformly crosslinked by tex) as a function of time t during cooling (Fig. 5b). The measurements indicate that the swelling rates decrease with tex (as shown in Fig. 1d), reflecting the difference in the rate of diffusion of water through the hydrogels with different densities (supporting the mechanism in Fig. 1). The crossover of AT/A0 of hydrogels prepared with short and long tex at around 30–35 min (indicated by the dashed black line in Fig. 5b) implies how growth-induced structures transform between shapes with K > 0 and K < 0 (e.g., Figs. 2a–c, j, 5a).

To quantitatively describe the shape evolution, we next constructed dynamic calibration curves (AT/A0 as a function of tex at times t) using AT/A0 shown in Fig. 5b (Fig. 5c, Supplementary Figure 15), analogous to the static calibration curves (Fig. 1b, c). The dynamic calibration curves show how the local areas created with tex in 3D structures swell (or shrink) with t. AT/A0(tex) changes from the static calibration curve at the shrunk state (i.e., AT/A0(tex) at t = 0 min in Fig. 5c) to the static calibration curve at the swelled state (Supplementary Figure 15). We can then determine how Ω for a 3D shape evolves with t (dynamic growth function or target metric Ωt) from Ω at t = 0 min (i.e., Ω at the shrunk state), using the dynamic calibration curve AT/A0(tex) at t.

Having established the procedure to determine Ωt, we applied the concept of dynamic target metrics to investigate the shape evolution of the spherical cap structure (Fig. 5a). We determined Ωt for the spherical cap (Fig. 5d, e, Supplementary Figure 16) from its static growth function (shown in Fig. 2g), using the dynamic calibration curves (shown in Fig. 5c, Supplementary Figure 15). Ωt shows how the metric of the spherical cap changes with time and thus how the structure changes its shape (Fig. 5d, e, Supplementary Figures 16, 17). During this transition, Ωt undergoes complex transformations, forming hybrid elliptic and hyperbolic metrics (Fig. 5d, e) and thus inducing hybrid 3D shapes (Fig. 5a, Supplementary Figure 18). The spatially nonuniform kinetics of swelling produces hybrid Ωt with a minimum at (r/R)min at t of 20–40 min (as indicated by dashed black lines in Fig. 5e and Supplementary Figure 18). Ωt at r/R < (r/R)min and r/R > (r/R)min represents the spherical cap-like shape in the center (K> 0) and the wrinkles in the edge (K< 0), respectively. The functional form of Ωt (e.g., sharp change in the gradient of Ωt at r/R> (r/R)min) reflects how Ωt forms wrinkles, reminiscent of Enneper’s surfaces (Fig. 2i–k, Supplementary Figure 5).

To demonstrate that Ωt predicts the dynamic shape change, we quantified the shape evolution of the spherical cap structure at 0–40 min and compared it with our theoretical model (Fig. 5f–h, Supplementary Figures 18–20). We characterized the dynamic shapes by Gaussian curvature of the spherical cap-like shape in the center Ksc (Fig. 5f), the location of the shape transition between the spherical cap-like shape (K > 0) and the wrinkles (K< 0) (ρ/Rs)tr, where ρ is the radial coordinate of the 3D structure and Rs is the radius of the structure (Fig. 5g, Supplementary Figures 18, 19), and the number and amplitude of wrinkles (Fig. 5h, Supplementary Figure 20). The experimentally measured Ksc decreases with time and the spherical cap-like shape gradually disappears at around 40 min (K → 0), matching well with Ksc obtained from Ωt (Fig. 5f). The measured (ρ/Rs)tr decreases with time (i.e., shifts toward the center of the structure), showing a good agreement with (ρ/Rs)tr calculated from (r/R)min (using Supplementary Equation 8 in Supplementary Note 2). The shift of (ρ/Rs)tr (or (r/R)min) results in the decrease in the region of the spherical cap-like shape and the increase in the region of the wrinkles.

Furthermore, our theoretical model describes how the number of the wrinkles decreases with time while their amplitude increases (as shown in Fig. 5a and Supplementary Figure 18). To understand how the structure forms the wrinkles, we fitted Ω = c/[1 + (r/(aR))2]+ [1 + (r/R)n]2 − 1 to Ωt, where the first and second terms in Ω represent the spherical cap-like shape (as shown in Fig. 2g) and the wrinkles (a functional form of Enneper’s surfaces in Fig. 2k), respectively, and c, a, and n are constants. The results show that n decreases with time, suggesting that the decrease in n results in the decrease in the number of the wrinkles and the increase in their amplitude (Fig. 5h, Supplementary Figure 20), as observed in Enneper’s surfaces with different n′ (Fig. 2i–k, Supplementary Figure 5)4,37. The dynamic K maps theoretically calculated from Ωt reflect the experimentally observed shape transformations (Supplementary Figure 21).

To further demonstrate that Ωt can predict the dynamic behavior of growth-induced 3D structures, we replicated the dynamic shapes of the spherical cap using Ωt (Fig. 5i). Because the full range of Ωt is not accessible by our material systems, we rescaled Ωt to the experimentally accessible range of Ω (Fig. 5j). The replicated structures reproduce the key signatures of the shape evolution, including the formation of wrinkles and their shape changes (e.g., increase in the amplitude of wrinkles, decrease in their number, and gradual disappearance of the spherical cap-like shape in the center) (Fig. 5i). The discrepancy in the detailed shapes (e.g., enhanced wrinkles) is attributed to the use of normalized Ωt. Moreover, this approach that uses Ωt for 3D shaping provides new pathways for creating complex 3D structures. This approach offers rich sources to design complex 3D shapes, difficult to access with current theories (e.g., wrinkle formation)35, and to understand how differential in-plane growth translates to 3D shapes. Manufacturing complex 3D structures, such as those shown in Fig. 5i, is difficult and expensive to achieve by other methods.

### Dynamic 3D structures with programmed sequential motions

Another important finding is that the swelling and shrinking rates of our hydrogel systems are phototunable and thus locally programmable. To demonstrate the ability to control the speed of shape change, we created saddle structures with an identical shape but different speeds of shape transformation (Fig. 6a, b, Supplementary Figure 22). To create these structures, we designed Ωfast and Ωslow with the same functional form (Ω for a saddle shape shown in Fig. 2g) but in different Ω ranges: Ωslowfast = C, where C is a constant and C > 1 (Fig. 6c). The growth (swelling and shrinking) rates decrease with tex and thus with Ω (Fig. 1d, Supplementary Figure 23), but a 3D shape is determined by the relative growth (not by the absolute values of Ω). We can therefore program the speed of shape transformation without changing 3D shapes by controlling the range of Ω (e.g., the maximum and minimum values of Ω) but maintaining the relative growth (e.g., Ω(r/R)/Ωmin, where Ωmin is a constant). As designed, the structure with Ωfast transforms its shape faster than the structure with Ωslow (Fig. 6a, b, Supplementary Figure 22). The dynamic K maps theoretically calculated from the dynamic growth functions describe the experimentally observed shape transformations with different speeds (Fig. 6b, Supplementary Figure 22). Within the structures (Fig. 6a, b), due to the difference in the range of Ω, the central regions (r/R ~ 0; low range Ω) transform faster than the edge regions (r/R ~ 0.4; high range Ω), also seen in the dynamic K maps (Fig. 6b, Supplementary Figure 22). The same trend is observed in the spherical cap structure (Fig. 5a), in which the edge region (low range Ω) transforms faster than the central region (high range Ω) (Supplementary Figure 21).

The ability to spatially control the rate of shape transformation allows us to create dynamic 3D structures with programmed sequential motions, difficult to achieve with global external stimuli8. As a demonstration, we fabricated a ray-inspired 3D structure with programmed sequential motions (Fig. 6d, e, Supplementary Figures 24, 25). The structure consists of modules for the body (K > 0), front wings (K < 0), and rear wings (K < 0) (Supplementary Figure 24). The front and rear wings were designed to transform fast and slowly, respectively, and thereby be sequentially actuated in response to temperature change (Fig. 6d, e). As designed, the front wings transform first from a shape with Kc < 0 to Kc > 0 (around 5 min), gradually lifting the rear wings, while the rear wings slowly transform (e.g., Kc < 0 up to 10 min) and flap after 20 min (Fig. 6d, Supplementary Movie 5). Moreover, we can control the oscillatory motions (e.g., amplitude and frequency) by modulating temperature cycles (Supplementary Figure 25). The theoretically calculated dynamic K maps for each module illustrate the experimentally observed sequential motions (Fig. 6e).

## Discussion

Living organisms often achieve 3D morphologies and movements by using spatially patterned and temporally controlled expansion and contraction of continuously deformable soft tissues. Our approach that uses the spatially and temporally controlled growth for programming 3D shapes and their motions, possibly with a large number of degrees of freedom, could thus create dynamic 3D structures that mimic the morphologies and motions of living organisms and thus, potentially, their functions. The ability to program growth-induced 3D shapes and motions could potentially transform the way we design and fabricate soft engineering systems, such as soft robots, actuators, and artificial muscles. The concept is applicable to other programmable materials. The 2D printing approach for 3D material programming represents a scalable and customizable 3D manufacturing technology, potentially integrable with biological systems1,2,7,21,30 and existing 2D fabrication methods and devices for multifunctionalities and broader applications48.

## Methods

### Preparation of precursor solutions

The precursor solutions for pNIPAm crosslinked with BIS and PEGDA were prepared by dissolving NIPAm (0.4 g), BIS (0.5 mol% of NIPAm), PEGDA with an average molecular weight (MW) of ~700 g mol−1 (0.125 mol% of NIPAm), and diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (PBPO) (0.15 mol% of NIPAm) in 1 mL aqueous solutions (1:3 ratio of water and acetone by volume). The precursor solutions for pNIPAm crosslinked with BIS were prepared by dissolving NIPAm (0.2 g), BIS (0.25–5.0 mol% of NIPAm), and PBPO (0.3 mol% of NIPAm) in 1 mL aqueous solutions (1:3 ratio of water and acetone). The precursor solutions for pNIPAm crosslinked with PEGDA were prepared by dissolving NIPAm (0.2 g), PEGDA (1.0–10.0 mol% of NIPAm), and PBPO (0.3 mol% of NIPAm) in 1 mL aqueous solutions (1:3 ratio of water and acetone). All materials were purchased from Sigma-Aldrich and used as received.

### Creation of shape-morphing 3D structures

Projection lithography cells were prepared by placing a polydimethylsiloxane (PDMS) spacer with a thickness of 400 μm on a PDMS substrate. After purging with nitrogen to reduce the effects of oxygen on photopolymerization, the precursor solutions were introduced into the cells. The cells were then covered with a glass coverslip (150 µm in thickness). The precursor solutions were then programmed with growth functions (or target metrics) Ω by spatially and temporally controlled ultraviolet (UV) light (dynamic light projection grayscale lithography).

Shape-morphing 3D structures were created using DL4P. 2D structures that define the boundary of target structures were designed using 3ds Max (Autodesk). Growth functions Ω designed for target 3D shapes were converted into 2D maps of light exposure times using the calibration curves of the areal swelling and shrinking ratios versus light exposure time (Fig. 1b, c) with a custom-made MATLAB (MathWorks) code. The growth functions define local AT/A0 of 2D structures. Stereolithography (STL) files were generated that contain the information of the 2D maps of light exposure times. The precursor solutions were polymerized and crosslinked by spatially and temporally controlled UV light using a digital light processing (DLP) projector (Vivitek D912HD) with the STL files (dynamic light projection lithography). After polymerization and crosslinking, the 2D hydrogel structures were detached from the cell and immediately washed with acetone, isopropyl alcohol (IPA), and water for three times to remove unreacted monomers, crosslinkers, and photoinitiators, and suppress photopolymerization and crosslinking reactions. To achieve the target 3D shapes at the equilibrium swelled state, the hydrogel structures were immersed in water at 4 °C for 72 h, while exchanging the water every 12 h, and then at 25 °C for 2 h in a temperature controlled water bath. To induce the target 3D shapes at the equilibrium shrunk state, the temperature of the water was slowly increased to 35 °C. Food color dyes were introduced into hydrogel structures for imaging. Hydrogel structures without dyes are transparent at equilibrium states.

### Measurement of areal swelling and shrinking ratios

Homogeneous pNIPAm hydrogel disks with a diameter of 5 mm (i.e., hydrogel disks formed with constant Ω) were prepared by DL4P. The hydrogel disks were uniformly exposed to UV light over the entire disks with light exposure times of 8–70 s. The areas of the hydrogel disks at the swelled state A25 were measured at 25 °C. The areas of the hydrogel disks at the shrunk state A35 were measured at 35 °C. The areal swelling and shrinking ratios are defined as A35/A0 and A25/A0, respectively, where A0 is the area of as-prepared hydrogel disks. The hydrogel disks were used to generate the calibration curves of the areal swelling and shrinking ratios versus light exposure time (Fig. 1b, c, Supplementary Figure 1). This process induces essentially no or little variation of swelling and shrinking through the thickness and thus does not induce bending of homogeneous hydrogel disks.

### Measurement of mechanical properties and gel points

The dynamic mechanical properties of hydrogels at the swelled state were measured using a rheometer (DHR-2, TA Instruments) with a 20-mm plate geometry. Hydrogel disks with a diameter of 20 mm were used. The shear storage modulus G′ and loss modulus G″ were measured by frequency sweeps of 0.01–100 rad s−1 at an oscillatory strain of 1%. The hydrogel disks with a storage shear modulus larger than 20 Pa were used for the measurements of the swelling and shrinking ratios (Fig. 1b, c, Supplementary Figure 1).

The gel points of hydrogels crosslinked with single crosslinkers were measured by the method of Winter and Chambon (Supplementary Figure 2)49,50. Hydrogel disks with a diameter of 20 mm were prepared with single crosslinkers (BIS and PEGDA; 1 mol% of NIPAm in precursor solutions) with different light exposure times (BIS-crosslinked hydrogels: 4, 8, 12 and 16 s; PEGDA-crosslinked hydrogels: 1, 2, 3 and 4 s). The hydrogel disks that form stable hydrogels after washing with acetone and IPA were used for the measurements. G′ and G″ were measured by frequency sweeps of 0.1–15 Hz at an oscillatory strain of 0.1% using the rheometer with a 20-mm plate geometry. To determine the gel points, tanδ = G″/G' were plotted as a function of frequency. At the gel point, tanδ = G″/G' has a constant value over the frequency sweep (Supplementary Figure 2)49,50.

### Reconstruction of 3D images and Gaussian curvatures

The 3D images and Gaussian curvatures K of experimentally created 3D structures were constructed based on the spin image 3D recognition method51. 2D images of the 3D structures were captured from different angles by taking images while rotating the structures. 3D images were then reconstructed from the 2D images and converted into STL files using 3ds Max. The reconstructed 3D images with K were constructed using MATLAB with the STL files (Fig. 2d–f, l, Supplementary Figure 6).

## Data availability

The data that support the findings of this study are available within the paper and its Supplementary Information and from the corresponding author upon reasonable request.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## References

1. 1.

Kim, S., Laschi, C. & Trimmer, B. Soft robotics: a bioinspired evolution in robotics. Trends Biotechnol. 31, 287–294 (2013).

2. 2.

Rus, D. & Tolley, M. T. Design, fabrication and control of soft robots. Nature 521, 467–475 (2015).

3. 3.

Klein, Y., Efrati, E. & Sharon, E. Shaping of elastic sheets by prescription of non-Euclidean metrics. Science 315, 1116–1120 (2007).

4. 4.

Kim, J., Hanna, J. A., Byun, M., Santangelo, C. D. & Hayward, R. C. Designing responsive buckled surfaces by halftone gel lithography. Science 335, 1201–1205 (2012).

5. 5.

Gladman, A. S., Matsumoto, E. A., Nuzzo, R. G., Mahadevan, L. & Lewis, J. A. Biomimetic 4D printing. Nat. Mater. 15, 413–418 (2016).

6. 6.

Wu, Z. L. et al. Three-dimensional shape transformations of hydrogel sheets induced by small-scale modulation of internal stresses. Nat. Commun. 4, 1586 (2013).

7. 7.

Jamal, M. et al. Bio-origami hydrogel scaffolds composed of photocrosslinked PEG bilayers. Adv. Healthc. Mater. 2, 1142–1150 (2013).

8. 8.

Cangialosi, A. et al. DNA sequence–directed shape change of photopatterned hydrogels via high-degree swelling. Science 357, 1126–1130 (2017).

9. 9.

Pikul, J. H. et al. Stretchable surfaces with programmable 3D texture morphing for synthetic camouflaging skins. Science 358, 210–214 (2017).

10. 10.

Shepherd, R. F. et al. Multigait soft robot. Proc. Natl Acad. Sci. USA 108, 20400–20403 (2011).

11. 11.

Jamal, M., Zarafshar, A. M. & Gracias, D. H. Differentially photo-crosslinked polymers enable self-assembling microfluidics. Nat. Commun. 2, 527 (2011).

12. 12.

Jeon, S.-J., Hauser, A. W. & Hayward, R. C. Shape-morphing materials from stimuli-responsive hydrogel hybrids. Acc. Chem. Res. 50, 161–169 (2017).

13. 13.

Kuksenok, O. & Balazs, A. C. Modeling the photoinduced reconfiguration and directed motion of polymer gels. Adv. Funct. Mater. 23, 4601–4610 (2013).

14. 14.

Lendlein, A., Jiang, H., Junger, O. & Langer, R. Light-induced shape-memory polymers. Nature 434, 879–882 (2005).

15. 15.

Ge, Q. et al. Multimaterial 4D printing with tailorable shape memory polymers. Sci. Rep. 6, 31110 (2016).

16. 16.

Iamsaard, S. et al. Conversion of light into macroscopic helical motion. Nat. Chem. 6, 229–235 (2014).

17. 17.

Ware, T. H., McConney, M. E., Wie, J. J., Tondiglia, V. P. & White, T. J. Voxelated liquid crystal elastomers. Science 347, 982–984 (2015).

18. 18.

White, T. J. & Broer, D. J. Programmable and adaptive mechanics with liquid crystal polymer networks and elastomers. Nat. Mater. 14, 1087–1098 (2015).

19. 19.

Na, J.-H. et al. Programming reversibly self-folding origami with micropatterned photo-crosslinkable polymer trilayers. Adv. Mater. 27, 79–85 (2015).

20. 20.

Liu, Y., Shaw, B., Dickey, M. D. & Genzer, J. Sequential self-folding of polymer sheets. Sci. Adv. 3, e1602417 (2017).

21. 21.

Park, S.-J. et al. Phototactic guidance of a tissue-engineered soft-robotic ray. Science 353, 158–162 (2016).

22. 22.

O’Neill, B. Elementary Differential Geometry (Academic Press, New York, 1997).

23. 23.

do Carmo, M. P. Differential Geometry of Curves and Surfaces (Dover Publications, New York, 2016).

24. 24.

Forterre, Y., Skotheim, J. M., Dumais, J. & Mahadevan, L. How the Venus flytrap snaps. Nature 433, 421–425 (2005).

25. 25.

Goriely, A. & Ben Amar, M. Differential growth and instability in elastic shells. Phys. Rev. Lett. 94, 198103 (2005).

26. 26.

Dervaux, J. & Ben Amar, M. Morphogenesis of growing soft tissues. Phys. Rev. Lett. 101, 068101 (2008).

27. 27.

Liang, H. & Mahadevan, L. Growth, geometry, and mechanics of a blooming lily. Proc. Natl Acad. Sci. USA 108, 5516–5521 (2011).

28. 28.

Studart, A. R. Biologically inspired dynamic material systems. Angew. Chem. Int. Ed. 54, 3400–3416 (2015).

29. 29.

Käpylä, E., Delgado, S. M. & Kasko, A. M. Shape-changing photodegradable hydrogels for dynamic 3D cell culture. ACS Appl. Mater. Interfaces 8, 17885–17893 (2016).

30. 30.

Nawroth, J. C. et al. A tissue-engineered jellyfish with biomimetic propulsion. Nat. Biotechnol. 30, 792–797 (2012).

31. 31.

Roche, E. T. et al. Soft robotic sleeve supports heart function. Sci. Transl. Med. 9, eaaf 3925 (2017).

32. 32.

Ko, H. & Javey, A. Smart actuators and adhesives for reconfigurable matter. Acc. Chem. Res. 50, 691–702 (2017).

33. 33.

Ionov, L. Biomimetic hydrogel-based actuating systems. Adv. Funct. Mater. 23, 4555–4570 (2013).

34. 34.

van Rees, W. M., Vouga, E. & Mahadevan, L. Growth patterns for shape-shifting elastic bilayers. Proc. Natl Acad. Sci. USA 114, 11597–11602 (2017).

35. 35.

Klein, Y., Venkataramani, S. & Sharon, E. Experimental study of shape transitions and energy scaling in thin non-Euclidean plates. Phys. Rev. Lett. 106, 118303 (2011).

36. 36.

Dias, M. A., Hanna, J. A. & Santangelo, C. D. Programmed buckling by controlled lateral swelling in a thin elastic sheet. Phys. Rev. E 84, 036603 (2011).

37. 37.

Na, J.-H., Bende, N. P., Bae, J., Santangelo, C. D. & Hayward, R. C. Grayscale gel lithography for programmed buckling of non-Euclidean hydrogel plates. Soft Matter 12, 4985–4990 (2016).

38. 38.

Sharon, E. & Efrati, E. The mechanics of non-Euclidean plates. Soft Matter 6, 5693–5704 (2010).

39. 39.

Bowman, C. N. & Kloxin, C. J. Toward an enhanced understanding and implementation of photopolymerization reactions. AIChE J. 54, 2775–2795 (2008).

40. 40.

Zhou, H. & Johnson, J. A. Photo‐controlled growth of telechelic polymers and end‐linked polymer gels. Angew. Chem. Int. Ed. 52, 2235–2238 (2013).

41. 41.

Chen, M., Zhong, M. & Johnson, J. A. Light-controlled radical polymerization: mechanisms, methods, and applications. Chem. Rev. 116, 10167–10211 (2016).

42. 42.

Pan, X. et al. Mechanism of photoinduced metal-free atom transfer radical polymerization: experimental and computational studies. J. Am. Chem. Soc. 138, 2411–2425 (2016).

43. 43.

44. 44.

Kamata, H., Akagi, Y., Kayasuga-Kariya, Y., Chung, U. & Sakai, T. “Nonswellable” hydrogel without mechanical hysteresis. Science 343, 873–875 (2014).

45. 45.

Müller, M. M., Amar, M. B. & Guven, J. Conical defects in growing sheets. Phys. Rev. Lett. 101, 156104 (2008).

46. 46.

Seffen, K. A. Fundamental conical defects: the d-cone, its e-cone, and its p-cone. Phys. Rev. E 94, 013002 (2016).

47. 47.

Blevins, E. L. & Lauder, G. V. Rajiform locomotion: three-dimensional kinematics of the pectoral fin surface during swimming by freshwater stingray Potamotrygon orbignyi. J. Exp. Biol. 215, 3231–3241 (2012).

48. 48.

Xu, S. et al. Assembly of micro/nanomaterials into complex, three-dimensional architectures by compressive buckling. Science 347, 154–159 (2015).

49. 49.

Winter, H. H. & Chambon, F. Analysis of linear viscoelasticity of a crosslinking polymer at the gel point. J. Rheol. 30, 367–382 (1986).

50. 50.

Rodd, A. B., Cooper-White, J., Dunstan, D. E. & Boger, D. V. Gel point studies for chemically modified biopolymer networks using small amplitude oscillatory rheometry. Polymer 42, 185–198 (2001).

51. 51.

Johnson, A. E. & Hebert, M. Using spin images for efficient object recognition in cluttered 3D scenes. IEEE Trans. Pattern Anal. Mach. Intell. 21, 433–449 (1999).

## Acknowledgements

We thank C. Kim, S. Koh, H. F. Tibbals, A. Aghamohammadi, and M. Khorrami for discussion.

## Author information

### Affiliations

1. #### Department of Materials Science and Engineering, University of Texas at Arlington, 501 West First Street, Arlington, TX, 76019, USA

• Amirali Nojoomi
• , Kwan Lee
•  & Kyungsuk Yum
2. #### Department of Mechanical and Aerospace Engineering, University of Texas at Arlington, 500 West First Street, Arlington, TX, 76019, USA

• Hakan Arslan

### Contributions

A.N. and K.Y. conceived the project and designed the experiments. A.N. and H.A. performed the experiments. A.N, H.A., K.L. and K.Y. analyzed the data. A.N. and K.Y. wrote the manuscript. All authors discussed data and contributed to the writing of the manuscript.

### Competing interests

The authors declare no competing interests.