Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Design principles of chiral carbon nanodots help convey chirality from molecular to nanoscale level


The chirality of (nano)structures is paramount in many phenomena, including biological processes, self-assembly, enantioselective reactions, and light or electron spin polarization. In the quest for new chiral materials, metallo-organic hybrids have been attractive candidates for exploiting the aforementioned scientific fields. Here, we show that chiral carbon nanoparticles, called carbon nanodots, can be readily prepared using hydrothermal microwave-assisted synthesis and easily purified. These particles, with a mean particle size around 3 nm, are highly soluble in water and display mirror-image profile both in the UV–Vis and in the infrared regions, as detected by electronic and vibrational circular dichroism, respectively. Finally, the nanoparticles are used as templates for the formation of chiral supramolecular porphyrin assemblies, showing that it is possible to use and transfer the chiral information. This simple (and effective) methodology opens up exciting opportunities for developing a variety of chiral composite materials and applications.


Chirality is a symmetry description for any object, ranging from molecules to macroscopic items, that is not super-imposable on its mirror image. This geometric property is inherent in nature, as evidenced from homochiral proteins, nucleic acids and (poly)saccharides, which are also able to interact stereospecifically in a variety of biological events1,2. The appeal in understanding the physical, chemical and biological properties of chirality goes back to first observing optical activity in quartz (in 1811)3. However, the field of “art of chirality” started with Louis Pasteur that made the connection between chirality and optical activity with his remarkable experiments on tartaric acid crystals (in 1848)4,5. Subsequently, it was found that most biomolecules (proteins, nucleic acids, and saccharides) are chiral and, also to take advantage of their chiral recognition, admirable achievements have been made on the enantioselective synthesis of small molecules6. Almost two decades ago, the first inorganic chiral nanoparticles (NPs) were reported, employing stabilizing chiral ligands (glutathione) for gold nanoclusters7. While most studies are focused on metal nanoclusters (gold and silver), this approach has been extended to semiconductor nanocrystals, magnetic NPs and other nanostructures8,9,10,11,12,13,14,15,16. Chiroptical effects in metal and semiconductor NPs can be observed, besides the aforementioned interaction of the achiral nanoparticle with chiral molecules, by preparing inorganic nanostructures with chiral shape, achiral NPs that interact in a chiral configuration or NPs that possess intrinsically chiral cores8,9,10,11,12,13,14,15,16,17,18,19,20,21. Immense progress, in preparing and understanding nanoscale chiroptical materials, has been achieved and novel concepts and nanomaterials have opened up potential applications in catalysis, optics and biosensing, to name a few8,9,10,11,12.

The concept of introducing chirality in graphene quantum dots was recently applied by covalently attaching chiral moieties to their edges22,23. Although this elegant approach has produced graphene-based materials capable of interacting with cells22 or other molecules23 depending on the stereoisomer of the attached moieties, a novel methodology is needed to fully combine carbon nanomaterials with chiroptical properties. In this context, a one-step synthetic approach (that avoids cutting down of larger graphene sheets or carbon nanotubes and subsequent coupling with chiral molecules), capable of producing chiral carbon nanoforms with tunable optoelectronic properties, would be ideal. Herein, we report the synthesis of chiral carbon nanodots (CNDs), carbon nanoparticles characterized by sizes below 10 nm and fascinating fluorescence properties24,25,26. Additionally, they possess finer properties such as inexpensive and safe nature, and therefore could substitute the conventional semiconductor NPs, generally considered superior fluorescent materials27,28,29.

Herein we report a synthetic approach for preparing CNDs that exhibit chirality. The carbon dots are prepared through a multi-component microwave-assisted hydrothermal synthesis and we study their (chiro)optical properties. We also show that CNDs can form supramolecular complexes with chromophores (porphyrins) and that the chirality can be transferred, which highlights the emergence of novel possibilities.

Results and discussion

Design and synthesis

Carbon nanodots are generally considered carbon nanoparticles with a nanoscale carbon core covered by surface functional groups, such as carboxylic acids, alcohols, or amines27,28,29,30,31. Normally, these carbon nanoparticles can be prepared either by “top-down” cutting of larger carbon nanostructures or through “bottom-up” approaches, like one-step multi-component synthesis32,33. Especially the latter can make use of the different reactivity of the employed precursors, leading to the formation of defined and properly designed core and surface. For example, using bottom-up microwave-assisted hydrothermal synthesis, starting from abundant and non-expensive precursors such as arginine and ethylenediamine (EDA), it has been possible to readily prepare small and highly-fluorescent carbon nanodots34. Carbon-13 nuclear magnetic resonance, cyclic voltammetry, and chemical reactivity experiments unambiguously showed that arginine leads mostly to the formation of the core, while EDA is mainly responsible for the amino-rich surface34,35,36. However, during the hydrothermal microwave-assisted synthesis, as expected37, L-arginine undergoes racemization or consumption, resulting in achiral carbon nanodots (Supplementary Figure 1). We reasoned that, by appropriate choice of the surface precursor, i.e., a chiral diamine that retains chirality at high temperatures in water, chiral carbon dots could be prepared.

Chiral carbon dots were therefore prepared via microwave-assisted hydrothermal synthesis by using arginine, as the core precursor, and (R,R)- or (S,S)-1,2-cyclohexanediamine (CHDA)38, as the chiral surface precursors (Fig. 1). In the process of microwave heating (see Methods section for details), the solution changed color from transparent to dark brown as a result of the formation of nanodots. Large carbon nanoparticles were removed by filtration and the yellow filtrate was dialyzed against milli-Q water. The obtained nanodots, named CNDs-R or CNDs-S, are soluble in water (and other commonly employed polar organic solvents). For comparison, the achiral carbon dots prepared using arginine and ethylenediamine are named CNDs-EDA.

Fig. 1

Design and synthesis of chiral carbon nanodots. Chiral CNDs were synthesized starting from (R,R)- or (S,S)-1,2-cyclohexanediamine and arginine, under hydrothermal microwave-assisted conditions (240 °C, 70–110 psi, 200 W for 180 s)

Morphological and structural characterization

The structure and the composition of CNDs-R and -S were determined by FT-IR spectroscopy and X-ray photoelectron spectroscopy (XPS), while morphological information were obtained by atomic force microscopy (AFM). As expected, the two chiral carbon nanodots show the same morphological and structural features (Fig. 2 and Supplementary Figures 24).

Fig. 2

Morphological and structural characterization of CNDs-R and CNDs-S. a Tapping mode AFM (4.4 × 4.4 μm) from a drop-cast CNDs-R aqueous solution on a mica substrate (scale bar, 1 μm), inset is the height profile along the dashed line; b three-dimensional close-up AFM image (0.5 × 0.5 μm) of CNDs-R; c size histogram with curve fit using a Gaussian model; d FT-IR spectrum of CNDs-S; e XPS survey spectrum of CNDs-S showing the C1s, N1s, and O1s (deconvoluted spectra are in Supplementary Figure 4, *from Au substrate Au4d3, Au4d5, and Au4p)

AFM images show the CNDs-R round shape and size of 2.64 ± 0.89 nm (FWHM: 2.09), comparable to the achiral CNDs-EDA34 (Fig. 2a–c and Supplementary Figure 2).

The CNDs-S FT-IR spectrum (Fig. 2d and Supplementary Figure 3) shows the presence of many functional groups, similar to the CNDs prepared using achiral EDA as amine precursor. Absorptions at 1174 and 1107 cm−1 can be attributed to C–O–C bonds, while absorptions at 1386, 1353, and 1342 cm−1 confirmed the presence of C–O bonds. Moreover, the absorption peaks at 1646, 1703, and 1766 cm−1 were indicative of C=O bonds, whereas the broad peak centered at 3350 cm−1 revealed O–H/N–H bonding. In addition, C–N/C=N/C=C (1491, 1470, and 1452 cm−1) functional groups can be identified, while peaks at 2935 and 2859 cm−1 can be related to the C–H bond stretching vibrations.

From the full-scan XPS spectrum of CNDs-R (Fig. 2e) C, N, O were detected (C1s at 286.2 eV, N1s at 400.6 eV and O1s at 532.3 eV). The atomic percentage for C, N, O are as follows: 65.9, 23.7, 10.4, respectively. To determine the C and N configurations in the CNDs-S, a detailed peak fitting analysis was performed, and the surface components are in good agreement with the observations from FT-IR experiments. The C1s spectrum of CNDs-S can be deconvoluted into five surface components corresponding to C=C at 284.8 eV (5.1%), C–C, and C–H at 285.8 eV (20.2%), C–O/C–N at 286.7 eV (56.8%), C=O/C=N at 288.5 eV (5.7%), as well as O–C=O at 289.6 eV (12.2%) (Supplementary Figure 4). The N1s spectrum of CNDs-S can be deconvoluted into four peaks centered at 398.7 (7.1%), 399.9 (25.7%), 400.9 (52.9%), and 401.9 (14.3%) eV corresponding to C=N, NH2, C–N–C, and N–C3 respectively. The presence of primary (and secondary) amino groups was confirmed by a positive Kaiser test, with an estimated value of 795 μmol g−1 of amino groups, which is in accordance to XPS measure.

Therefore, FT-IR and XPS measurements show that the surface of chiral nanodots contains similar multiple oxygen and nitrogen functional groups when compared to achiral CNDs-EDA, but with different contents.

Photophysical and (chiro)optical properties

The UV–Vis absorption spectra of CNDs-S and CNDs-R reveal two peaks at around 270 and 330 nm, which are related to the electron transitions from π (or n) to π* of C=C and C=O (Fig. 3a). The successful conferring of chirality from (R,R)- or (S,S)-CHDA to the carbon nanodots was confirmed by electronic circular dichroism (ECD) spectroscopy (Fig. 3b). The ECD spectrum of CNDs-R aqueous solution presents two negative Cotton effects at 260 and 320 nm, in accordance with the UV absorption bands (Fig. 3a). In the case of CNDs-S, inversion of the ECD signal was observed and indeed two positive Cotton effects at 260 and 320 nm were detected. In additional experiments we have prepared CNDs using various molar ratios of (R,R)- or (S,S)-CHDAs and the corresponding circular dichroism spectra showed that the optical activity of CNDs is dependent on the optical purity of the amine precursor (Supplementary Figure 5).

Fig. 3

Photophysical and (chiro)optical characterization of CNDs-S and CNDs-R. Experiments performed in water at 298 K. a UV–Vis spectra of CNDs-S (red line) and CNDs-R (black line); b ECD spectra of CNDs-S (red line) and CNDs-R (black line); c FL emission spectra (at different excitation wavelengths) of CNDs-R (same emission profiles and intensities were observed for CNDs-S); d FDCD for CNDs-S (red circles), CNDs-R (black circles) and fluorescein (empty squares), measured using the experimental conditions reported in the Supplementary Methods, at the angle θ = 15°

The fluorescence (FL) properties of the CNDs-S and CNDs-R show a broad emission peak at 425 nm when excited at the optimal excitation wavelength (350 nm) (Fig. 3c and Supplementary Figure 6). The fluorescence peak shifts from 419 to 466 nm when the excitation wavelength changes from 320 to 440 nm, with a slight excitation-dependent emission profile. These data reveal the different surface functional groups of CNDs-S and CNDs-R, compared to achiral CNDs-EDA. Indeed, the nanodot surface affects the FL properties since it determines the trapping of excitons under excitation. Furthermore, relative fluorescence quantum yields (FLQYs) were determined to be 20% and long average FL lifetimes were measured, around 8 ns for both CNDs-S and -R (double-exponential fit showed a short τ1 = 1.2 ns and a long τ2 = 11 ns component, Supplementary Figure 7 and Supplementary Table 1).

The chirality of the ground and excited states of CNDs was then probed through the detection of luminescence. The chirality of the ground state of CNDs was investigated through the fluorescence detection of circular dichroism (FDCD) by exciting the sample with circularly polarized light and measuring the fluorescence intensity. Opposite FDCD signals were measured for the two CNDs enantiomers. FDCD was measured for excitation wavelengths above 280 nm (Fig. 3d). Their opposite sign agrees with the opposite chirality observed in the electronic circular dichroism spectra. This result was not affected by fluorescence polarization effects or by polarized scattering; indeed, the differential fluorescence collected at the symmetric angle (θ = −15°) show the same spectral features (Supplementary Figure 8) and the contribution from the elastic scattering of CND was so low (i.e., the measured value of the excess scattered intensity in the visible wavelength range is almost comparable with pure solvent) that the longpass filter rejected it completely. Even placing an analyzer at the magic angle, despite the increased noise, did not change the spectral response. The negligible fluorescence polarization effects in the FDCD spectra can be led back to the long average fluorescence lifetime, which was about 8 ns for both CNDs (see Supplementary Figure 7 and Supplementary Table 1). During this time, the small size of CNDs allows for rotations fast enough to depolarize fluorescence emission (measured steady-state anisotropy = 0.03). Unfortunately, circularly polarized luminescence (CPL) spectra did not show any detectable chiroptical signal and thus no information about the excited state of the dots were obtained.

The wide emission spectral range of CNDs, extending above 600 nm, is constituted by different emission bands depending on the excitation wavelength (Fig. 3c). This occurrence indicates that CNDs possess many different dipoles absorbing light from UV to visible, which give rise to detectable fluorescence only if excited above 280 nm. As a consequence, chirality is observed in the deep UV region of the differential absorption spectrum with smaller and smaller amplitude at larger wavelength where the differential fluorescence signal becomes detectable.

Finally, chirality in CNDs was investigated by vibration circular spectroscopy (VCD), a differential absorption of left and right circularly polarized IR light, which was previously employed in chirally capped metal NPs to obtain structural information9. The VCD spectra of aqueous CNDs-S and CNDs-R solutions show a mirror image relationship (Fig. 4a and Supplementary Figure 9), with stronger bands centered at around 1600 cm−1 and at slightly above 1350 cm−1. To extract structural information from the VCD spectra, the latter were simulated using different conformations of various cyclohexanediamine fragments (Supplementary Methods, density functional theory (DFT) calculations). DFT calculations on fragments, rather than entire molecules, were found appropriate when a suitable portion of the molecule was selected39 and consequently we focused on CHDA derivatives. As evidenced by simulated VCD spectra of the optimized structures (Fig. 4b), the stronger signals appear to be arising from primary amine N–H and cyclohexane C–H bending vibrational modes. Possibly the band around 1600 cm−1 has also contributions from C=O (amide) functional groups (Supplementary Figure 10). Though the system is simplified, these calculations are able to account for the strongest signals observed in the experimental VCD spectra and further support the notion of a chiral shell carbon nanoparticle, with the chirality originating from the CHDAs moieies incorporated on the carbon dots.

Fig. 4

Comparison between experimental and calculated VCD spectra. a Experimental VCD spectra in water at 298 K of CNDs-S (red line) and CNDs-R (black line); b simulated VCD spectra obtained from DFT calculations of the cyclohexanediamine fragments (performed using the B3PW91 functional and a 6–31 G** basis set, water PCM solvation) with the insets showing the main displacement vectors for the computed chiral fragments

Templating supramolecular assemblies

In order to investigate if it is possible to transfer the chiral information from the CNDs-S and CNDs-R to other molecules, we probed their non-covalent interactions with porphyrins, which are known to form donor-acceptor complexes with CNDs40,41. Porphyrins, square planar aromatic systems comprising 18 π electrons, are known for their structural robustness, absorption and emission properties and vast supramolecular chemistry.42,43,44 Moreover, porphyrin chemistry has advanced significantly so that the electronic and optical properties can be fine-tuned by shaping their periphery45,46. In addition, functionalization at the porphyrin periphery with charged substituents, gives access to water-soluble porphyrins, while maintaining the hydrophobic character of the macrocyclic core. This dichotomy can be exploited to drive the tendency of the porphyrins to self-assemble in aqueous solution and to modulate their aggregation onto other templates, inducing predefined architectures47,48,49. Furthermore, they are ECD silent, but binding to chiral molecules induces an ECD signal in their absorbance region, which can be regarded as a specific spectroscopic signature of the chirality of the “host” molecule50.

In order to establish electrostatic interactions with the amino groups around the CNDs-S or CNDs-R in aqueous solutions, we focused on the tetranionic meso-tetrakis(4-sulfonatophenyl)porphyrin (H2TSPP4-). Moreover, the partially protonated form (H4TSPP2-, pKa = 4.8), being a zwitterionic molecule, is known to form both face-to-face (H-type, λmax = 420 nm) and edge-to-edge (J-type, λmax = 490 nm) aggregates51,52,53,54,55. These supramolecular aggregation processes are based on hierarchical self-assembly showing different thermodynamically and kinetically controlled paths, closely related to medium properties and experimental conditions (such as concentration, pH, and ionic strength)56,57,58. One of the most intriguing (and controversial) property of H4TPPS2- aggregates is their unpredictable chirality. H4TSPP2- aggregates should form a racemic mixture, exhibiting no optical activity59, however traces of chiral contaminants shift the 1:1 racemate equilibrium towards preferential chiral aggregates. To date only a few studies have been performed on the induction of preferential chirality to H4TSPP2- aggregates using chiral molecules as templates58,60. Here we report the effect of chiral CNDs as inducer of chirality and controller of the size of H4TSPP2- aggregates (Fig. 5a). A challenging aspect in these systems is the possibility of modulating the structure and properties of the final aggregates.

Fig. 5

CNDs-S or CNDs-R as templates for chiral supramolecular aggregates. Experiments performed in water at 298 K. a Schematic representation of CNDs-R acting as chiral template after pH decrease trigger (purple = free base porphyrin, green = protonated porphyrin); b UV–Vis spectra of CNDs (black line) and CNDs + HnTSPPm- solutions at different pHs (H2TSPP4- concentration = 6.0 μM); c ECD spectra of CNDs-S (red line) and CNDs-R (black line), both in the presence of H4TSPP2- (6.0 μM) at pH = 2.5

The addition of tetranionic H2TSPP4- to a solution of CNDs-S or CNDs-R (at pH = 9.0) presents spectroscopic evidences of interaction, i.e., a hypochromic effect (H ~35%) and a slight broadening of the Soret band (Fig. 5b, red line). Since the surface of the CNDs is covered with amino groups, by changing the pH should be possible to tune the charge on the CNDs and therefore adjust the interactions with the porphyrin. Indeed, when decreasing the pH (from 9.0 to 6.5), we observ an intense hypochromic effect (H ~75%) and the splitting of the Soret band of the H2TPPS4- (one more intense band at ~400 nm and the other at ~419 nm) (Fig. 5b, purple line). This experiment indicates the important role played by electrostatic interactions, indeed at pH 6.5 the porphyrin is still mainly tetranionic, whilst the positive charges on CNDs increase.

Then, in order to induce the formation of H4TSPP2- aggregates, we further decreased the pH (to 2.5, using hydrochloric acid) of the solutions of H2TSPP4-•CNDs-R complex. The UV–Vis spectrum shows the complete formation of H-type and J-type H4TSPP2- aggregates in less than 1 h (Fig. 5b, green line). The ECD band of the carbon nanodots decreases and two small induced bisignated ECD bands (centered at 420 and 490 nm) appear in the porphyrin aggregates absorption region (Fig. 5c, black line). Mirror image ECD spectra were acquired for the H2TSPP4-•CNDs-S complex (Fig. 5c, red line). The low intensity of the induced ECD signals of H4TSPP2- aggregates might be due to a weak efficiency in transferring the chiral information from the CNDs to the porphyrin aggregates, owing to the decrease of the ECD bands of the carbon nanodots, at acidic pH. However, the size and the intensity of the communication of porphyrin aggregates also affects the ECD intensity and, indeed, resonance light scattering (RLS) measurments showed the formation of shorter porphyrin aggregates in the presence of CNDs (Supplementary Figure 11).


We report here on the design, synthesis and characterization of chiral carbon nanodots. We demonstrate that the chirality is conferred, through a hydrothermal bottom-up microwave assisted synthesis, by using arginine and trans-cyclohexanediamine. The obtained carbon nanodots possess similar size, morphological and photophysical properties to the previously reported CNDs. However, most importantly, they possess chirality that resulted in CNDs-S and CNDs-R. The chirality was investigated in their ground states and in the UV–Vis and IR regions. ECD spectroscopy show two mirror image profiles, also evidenced by their VCD spectra. Additionally, the origin of chirality is ascribed to the presence of numerous cyclohexanediamine moieties around the carbon-based amorphous core. Finally, the chirality was successfully transferred from the CNDs, through electrostatic interactions, to tetranionic porphyrins, inducing formation of chiral aggregates.

Although we believe that these findings will open up various possibilities and applications for carbon-based dots, there are also many possibilities to achieve this. In order to accomplish even further advances in catalysis, biology and nanotechnology, it might be necessary to prepare chiral assemblies of carbon dots or self-assembly of chiral supra-particles (as already achieved for semiconductor NPs61,62), decreasing the band gap63, exploiting quantum confinement effects64,65 or interacting differently with biological membranes22, to name a few. Such advancements could be fulfilled using properties reported here, and exploring new ones. Differently to other attempts at preparing chiral carbon nanoparticles66,67,68, the rationale brought forward in the present work, accompanied by proper purification and extensive investigation of the chirality, could be extended for preparing other types of carbon dots. By using our approach, chirality could be conferred from different chiral molecules69 to different core precursors70. For example, by using citric acid instead of arginine (and keeping CHDAs as chiral precursors) we have obtained, yet again, chiral carbon dots that display mirror-like images in the circular dichroism spectra, but possess different absorption and emission properties when compared to the arginine-based CNDs (Supplementary Figure 12). Therefore, future work should be directed at preparing and tailoring chiral carbon dots according to specific needs and applications.


Material synthesis

Chiral CNDs were obtained via microwave irradiation (CEM Discover-SP) of an aqueous solution of l-Arginine (Arg, Fluorochem, M03558) and (R,R)- or (S,S)-1,2-cyclohexanediamine (CHDA, Sigma Aldrich, 346721 and 346713). Typically, Arg (87.0 mg), (R,R)- or (S,S)-CHDA (57.0 mg) and milli-Q water (100.0 μL) were heated at 240 °C, 70–110 psi and 200 W for 180 s. In the process of microwave heating, the color changed from yellow to dark brown as a result of the formation of CNDs. The reaction mixture was then diluted with a few milliliters of water and the solution was filtered through a 0.1 μm microporous membrane separating a deep yellow solution that was dialyzed against pure water through a dialysis membrane for 2 days. The aqueous solution was then lyophilized giving a brownish solid (CNDs-R: 20.5 mg; CNDs-S: 22.0 mg).

Chiral supramolecular assemblies

CND stock solution was prepared by dissolving 1.9 mg in 2.5 mL of ultrapure water (the pH of the solution was 9). The porphyrin selected for our study is the tetranionic meso-tetrakis(4-sulfonatophenyl)porphyrin (H2TSPP4-). The stock solution of porphyrin was prepared by dissolving a small amount of solid in ultrapure water at pH = 7, in order to obtain a concentration about 2 × 10−4 M, checked by spectrophotometer Jasco V-630 using ε = 4.8 × 10–5 M–1 cm–1 at λ = 413 nm. The sample solutions were obtained by mixing the CND and H2TSPP4- solutions at pH = 6.5. After 30 min incubation, the pH was decreased to 2.5 in order to induce the formation of aggregates.

Material characterization

Fourier-transform Infrared (FT-IR) spectra (KBr) were recorded on a Perkin Elmer 2000 spectrometer. Atomic force microscopy (AFM) images were obtained with a Nanoscope IIIa, VEECO Instruments. X-ray photoemission spectroscopy (XPS) spectra were measured on a SPECS Sage HR 100 spectrometer.

UV–Vis spectra were recorded on a PerkinElmer Lambda 35 UV–Vis spectrophotometer. Fluorescence spectra were recorded on a Varian Cary Eclipse fluorescence spectrophotometer. Time-resolved and differential fluorescence set-ups are detailed in the Supplementary Methods (and Supplementary Figure 13). Fluorescence time decay curve was fitted according to Supplementary Equation 1. ECD spectra were recorded using Jasco J-810. Resonance light scattering (RLS) measurements were acquired using a spectrophotometer FL11 Jobin Yvon Horiba. Vibrational circular dichroism (VCD) spectra were recorded on a Bruker PMA 50 accessory coupled to a Tensor 27 Fourier transform infrared spectrometer.

DFT calculations

The geometry optimizations, vibrational frequencies, infrared absorption and VCD intensities were performed by DFT. The calculations were performed using the B3PW91 functional and a 6–31 G** basis set (water PCM solvation).

Data availability

The authors declare that the main data supporting the findings of this study are available within the article and its Supplementary Information file. Additional data are available from the corresponding authors upon request.


  1. 1.

    Wagnière, G. H. On Chirality and the Universal Asymmetry: Reflections on Image and Mirror Image. (Verlag Helvetica Chimica Acta, 2007).

  2. 2.

    Blackmond, D. G. The origin of biological homochirality. Cold Spring Harb. Perspect. Biol. 2, a002147–a002147 (2010).

    PubMed  PubMed Central  Article  Google Scholar 

  3. 3.

    Barron, L. D. Molecular Light Scattering and Optical Activity. (Cambridge University Press, Cambridge, 2004).

  4. 4.

    Pasteur, L. Recherches sur les relations qui peuvent exister entre la forme crystalline, la composition chimique et le sens de la polarisation rotatoire. Ann. Chim. Phys. 24, 442–459 (1848).

    Google Scholar 

  5. 5.

    Gal, J. Pasteur and the art of chirality. Nat. Chem. 9, 604–605 (2017).

    CAS  PubMed  Article  Google Scholar 

  6. 6.

    Carreira, E. M. & Kvaerno, L. Classics in Stereoselective Synthesis. (Wiley, Weinheim, 2008).

  7. 7.

    Schaaff, T. G., Knight, G., Shafigullin, M. N., Borkman, R. F. & Whetten, R. L. Isolation and selected properties of a 10.4 kDa gold: glutathione cluster compound. J. Phys. Chem. B 102, 10643–10646 (1998).

    CAS  Article  Google Scholar 

  8. 8.

    Noguez, C. & Garzón, I. L. Optically active metal nanoparticles. Chem. Soc. Rev. 38, 757–771 (2009).

    CAS  PubMed  Article  Google Scholar 

  9. 9.

    Gautier, C. & Bürgi, T. Chiral gold nanoparticles. ChemPhysChem 10, 483–492 (2009).

    CAS  PubMed  Article  Google Scholar 

  10. 10.

    Ben-Moshe, A., Maoz, B. M., Govorov, A. O. & Markovich, G. Chirality and chiroptical effects in inorganic nanocrystal systems with plasmon and exciton resonances. Chem. Soc. Rev. 42, 7028–7041 (2013).

    CAS  PubMed  Article  Google Scholar 

  11. 11.

    Kumar, J., Thomas, K. G. & Liz-Marzán, L. M. Nanoscale chirality in metal and semiconductor nanoparticles. Chem. Commun. 52, 12555–12569 (2016).

    CAS  Article  Google Scholar 

  12. 12.

    Ma, W. et al. Chiral inorganic nanostructures. Chem. Rev. 117, 8041–8093 (2017).

    CAS  PubMed  Article  Google Scholar 

  13. 13.

    Durán Pachón, L. et al. Chiral imprinting of palladium with cinchona alkaloids. Nat. Chem. 1, 160–164 (2009).

    PubMed  Article  Google Scholar 

  14. 14.

    Häkkinen, H. The gold–sulfur interface at the nanoscale. Nat. Chem. 4, 443–455 (2012).

    PubMed  Article  Google Scholar 

  15. 15.

    Ostovar, S. et al. Through-space transfer of chiral information mediated by a plasmonic nanomaterial. Nat. Chem. 7, 591–596 (2015).

    Article  Google Scholar 

  16. 16.

    Farrag, M., Tschurl, M. & Heiz, U. Chiral gold and silver nanoclusters: preparation, size selection, and chiroptical properties. Chem. Mater. 25, 862–870 (2013).

    CAS  Article  Google Scholar 

  17. 17.

    Govorov, A. O. et al. Chiral nanoparticle assemblies: circular dichroism, plasmonic interactions, and exciton effects. J. Mater. Chem. 21, 16806–16818 (2011).

    CAS  Article  Google Scholar 

  18. 18.

    Wang, Y., Xu, J., Wang, Y. & Chen, H. Emerging chirality in nanoscience. Chem. Soc. Rev. 42, 2930–2962 (2013).

    CAS  PubMed  Article  Google Scholar 

  19. 19.

    Yang, H., Coombs, N. & Ozin, G. A. Morphogenesis of shapes and surface patterns in mesoporous silica. Nature 386, 692–695 (1997).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Jung, J. H., Ono, Y., Hanabusa, K. & Shinkai, S. Creation of both right-handed and left-handed silica structures by sol−gel transcription of organogel fibers comprised of chiral diaminocyclohexane derivatives. J. Am. Chem. Soc. 122, 5008–5009 (2000).

    CAS  Article  Google Scholar 

  21. 21.

    Gao, P. X. et al. Conversion of zinc oxide nanobelts into superlattice-structured nanohelices. Science 309, 1700–1704 (2005).

    ADS  CAS  PubMed  Article  Google Scholar 

  22. 22.

    Suzuki, N. et al. Chiral graphene quantum dots. ACS Nano 10, 1744–1755 (2016).

    CAS  PubMed  Article  Google Scholar 

  23. 23.

    Vázquez-Nakagawa, M., Rodríguez-Pérez, L., Herranz, M. A. & Martín, N. Chirality transfer from graphene quantum dots. Chem. Commun. 52, 665–668 (2015).

    Article  Google Scholar 

  24. 24.

    Sun, Y.-P. et al. Quantum-sized carbon dots for bright and colorful photoluminescence. J. Am. Chem. Soc. 128, 7756–7757 (2006).

    CAS  PubMed  Article  Google Scholar 

  25. 25.

    Georgakilas, V., Perman, J. A., Tucek, J. & Zboril, R. Broad family of carbon nanoallotropes: classification, chemistry, and applications of fullerenes, carbon dots, nanotubes, graphene, nanodiamonds, and combined superstructures. Chem. Rev. 115, 4744–4822 (2015).

    CAS  PubMed  Article  Google Scholar 

  26. 26.

    Lim, S. Y., Shen, W. & Gao, Z. Carbon quantum dots and their applications. Chem. Soc. Rev. 44, 362–381 (2015).

    CAS  PubMed  Article  Google Scholar 

  27. 27.

    Baker, S. N. & Baker, G. A. Luminescent carbon nanodots: emergent nanolights. Angew. Chem. Int. Ed. 49, 6726–6744 (2010).

    CAS  Article  Google Scholar 

  28. 28.

    Hola, K. et al. Carbon dots—emerging light emitters for bioimaging, cancer therapy and optoelectronics. Nano Today 9, 590–603 (2014).

    CAS  Article  Google Scholar 

  29. 29.

    Cayuela, A., Soriano, M. L., Carrillo-Carrión, C. & Valcárcel, M. Semiconductor and carbon-based fluorescent nanodots: the need for consistency. Chem. Commun. 52, 1311–1326 (2016).

    CAS  Article  Google Scholar 

  30. 30.

    Hutton, G. A. M., Martindale, B. C. M. & Reisner, E. Carbon dots as photosensitisers for solar-driven catalysis. Chem. Soc. Rev. 46, 6111–6123 (2017).

    CAS  PubMed  Article  Google Scholar 

  31. 31.

    Essner, J. B., Kist, J. A., Polo-Parada, L. & Baker, G. A. Artifacts and errors associated with the ubiquitous presence of fluorescent impurities in carbon nanodots. Chem. Mater. 30, 1878–1887 (2018).

    CAS  Article  Google Scholar 

  32. 32.

    Park, Y., Yoo, J., Lim, B., Kwon, W. & Rhee, S.-W. Improving the functionality of carbon nanodots: doping and surface functionalization. J. Mater. Chem. A 4, 11582–11603 (2016).

    CAS  Article  Google Scholar 

  33. 33.

    LeCroy, G. E. et al. Functionalized carbon nanoparticles: syntheses and applications in optical bioimaging and energy conversion. Coord. Chem. Rev. 320–321, 66–81 (2016).

    Article  Google Scholar 

  34. 34.

    Arcudi, F., Đorđević, L. & Prato, M. Synthesis, separation, and characterization of small and highly fluorescent nitrogen-doped carbon nanoDots. Angew. Chem. Int. Ed. 55, 2107–2112 (2016).

    CAS  Article  Google Scholar 

  35. 35.

    Carrara, S., Arcudi, F., Prato, M. & De Cola, L. Amine-rich nitrogen-doped carbon nanodots as a platform for self-enhancing electrochemiluminescence. Angew. Chem. Int. Ed. 56, 4757–4761 (2017).

    CAS  Article  Google Scholar 

  36. 36.

    Rizzo, C. et al. Nitrogen-doped carbon nanodots-Ionogels: preparation, characterization, and radical scavenging activity. ACS Nano 12, 1296–1305 (2018).

    CAS  PubMed  Article  Google Scholar 

  37. 37.

    Bada, J. L. in Chemistry and Biochemistry of the Amino Acids. 399–414 (Springer, Netherlands, 1985).

    Chapter  Google Scholar 

  38. 38.

    Bennani, Y. L. & Hanessian, S. trans-1,2-Diaminocyclohexane derivatives as chiral reagents, scaffolds, and ligands for catalysis: applications in asymmetric synthesis and molecular recognition. Chem. Rev. 97, 3161–3196 (1997).

    CAS  PubMed  Article  Google Scholar 

  39. 39.

    Yang, G. & Xu, Y. in Electronic and Magnetic Properties of Chiral Molecules and Supramolecular Architectures, Vol 298 (eds Naaman, R., Beratan, D. N. & Waldeck, D.) 189–236 (Berlin, Heidelberg, 2011).

  40. 40.

    Arcudi, F. et al. Porphyrin antennas on carbon nanodots: excited state energy and electron transduction. Angew. Chem. Int. Ed. 56, 12097–12101 (2017).

    CAS  Article  Google Scholar 

  41. 41.

    Cadranel, A. et al. Screening supramolecular interactions between carbon nanodots and porphyrins. J. Am. Chem. Soc. 140, 904–907 (2018).

    CAS  PubMed  Article  Google Scholar 

  42. 42.

    Beletskaya, I., Tyurin, V. S., Tsivadze, A. Y. A. Y., Guilard, R. & Stern, C. Supramolecular chemistry of metalloporphyrins. Chem. Rev. 109, 1659–1713 (2009).

    CAS  PubMed  Article  Google Scholar 

  43. 43.

    Martínez-Díaz, M.-V. V., de la Torre, G. & Torres, T. Lighting porphyrins and phthalocyanines for molecular photovoltaics. Chem. Commun. 46, 7090–7108 (2010).

    Article  Google Scholar 

  44. 44.

    Babu, S. S. & Bonifazi, D. Self-organization of polar porphyrinoids. ChemPlusChem 79, 895–906 (2014).

    CAS  Article  Google Scholar 

  45. 45.

    Li, L.-L. & Diau, E. W.-G. Porphyrin-sensitized solar cells. Chem. Soc. Rev. 42, 291–304 (2013).

    CAS  PubMed  Article  Google Scholar 

  46. 46.

    Urbani, M., Grätzel, M., Nazeeruddin, M. K. & Torres, T. Meso-substituted porphyrins for dye-sensitized solar cells. Chem. Rev. 114, 12330–12396 (2014).

    CAS  PubMed  Article  Google Scholar 

  47. 47.

    Schick, G. A., Schreiman, I. C., Wagner, R. W., Lindsey, J. S. & Bocian, D. F. Spectroscopic characterization of porphyrin monolayer assemblies. J. Am. Chem. Soc. 111, 1344–1350 (1989).

    CAS  Article  Google Scholar 

  48. 48.

    Medforth, C. J. et al. Self-assembled porphyrin nanostructures. Chem. Commun. 0, 7261–7277 (2009).

    CAS  Article  Google Scholar 

  49. 49.

    Romeo, A. et al. Kinetic control of chirality in porphyrin J-aggregates. J. Am. Chem. Soc. 136, 40–43 (2014).

    CAS  PubMed  Article  Google Scholar 

  50. 50.

    D’Urso, A., Fragalà, M. E. & Purrello, R. From self-assembly to noncovalent synthesis of programmable porphyrins’ arrays in aqueous solution. Chem. Commun. 48, 8165–8176 (2012).

    Article  Google Scholar 

  51. 51.

    Ribó, J. M., Crusats, J., Farrera, J.-A. & Valero, M. L. Aggregation in water solutions of tetrasodium diprotonated meso-tetrakis(4-sulfonatophenyl)porphyrin. J. Chem. Soc. Chem. Commun. 7, 681–682 (1994).

    Article  Google Scholar 

  52. 52.

    Maiti, N. C., Ravikanth, M., Mazumdar, S. & Periasamy, N. Fluorescence dynamics of noncovalently linked porphyrin dimers, and aggregates. J. Phys. Chem. 99, 17192–17197 (1995).

    CAS  Article  Google Scholar 

  53. 53.

    Akins, D. L., Zhu, H.-R. & Guo, C. Aggregation of tetraaryl-substituted porphyrins in homogeneous solution. J. Phys. Chem. 100, 5420–5425 (1996).

    CAS  Article  Google Scholar 

  54. 54.

    Koti, A. S. R., Taneja, J. & Periasamy, N. Control of coherence length and aggregate size in the J-aggregate of porphyrin. Chem. Phys. Lett. 375, 171–176 (2003).

    ADS  CAS  Article  Google Scholar 

  55. 55.

    Koti, A. S. R. & Periasamy, N. Self-assembly of template-directed J-aggregates of porphyrin. Chem. Mater. 15, 369–371 (2003).

    CAS  Article  Google Scholar 

  56. 56.

    Castriciano, M. A., Romeo, A., Villari, V., Micali, N. & Scolaro, L. M. Structural rearrangements in 5,10,15,20-tetrakis(4-sulfonatophenyl)porphyrin J-aggregates under strongly acidic conditions. J. Phys. Chem. B 107, 8765–8771 (2003).

    CAS  Article  Google Scholar 

  57. 57.

    Micali, N. et al. From fractal to nanorod porphyrin J-aggregates. Concentration-induced tuning of the aggregate size. J. Phys. Chem. B 110, 8289–8295 (2006).

    CAS  PubMed  Article  Google Scholar 

  58. 58.

    Castriciano, M. A., Romeo, A., Zagami, R., Micali, N. & Scolaro, L. M. Kinetic effects of tartaric acid on the growth of chiral J-aggregates of tetrakis(4-sulfonatophenyl)porphyrin. Chem. Commun. 48, 4872–4874 (2012).

    CAS  Article  Google Scholar 

  59. 59.

    D’Urso, A., Randazzo, R., Lo Faro, L. & Purrello, R. Vortexes and nanoscale chirality. Angew. Chem. Int. Ed. 49, 108–112 (2010).

    Article  Google Scholar 

  60. 60.

    Randazzo, R., Mammana, A., D’Urso, A., Lauceri, R. & Purrello, R. Reversible “Chiral Memory” in ruthenium tris(phenanthroline)-anionic porphyrin complexes. Angew. Chem. Int. Ed. 47, 9879–9882 (2008).

    CAS  Article  Google Scholar 

  61. 61.

    Yeom, J. et al. Chiral templating of self-assembling nanostructures by circularly polarized light. Nat. Mater. 14, 66–72 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  62. 62.

    Zhou, Y. et al. Biomimetic hierarchical assembly of helical suprapartcles from chiral nanoparticles. ACS Nano 10, 3248–3256 (2016).

    CAS  PubMed  Article  Google Scholar 

  63. 63.

    Ding, H., Yu, S.-B., Wei, J.-S. & Xiong, H.-M. Full-color light-emitting carbon dots with a surface-state-controlled luminescence mechanism. ACS Nano 10, 484–491 (2016).

    CAS  PubMed  Article  Google Scholar 

  64. 64.

    Wang, L. et al. Gram-scale synthesis of single-crystalline graphene quantum dots with superior optical properties. Nat. Commun. 5, 5357 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  65. 65.

    Yuan, F. et al. Engineering triangular carbon quantum dots with unprecedented narrow bandwidth emission for multicolored LEDs. Nat. Commun. 9, 2249 (2018).

    ADS  PubMed  PubMed Central  Article  Google Scholar 

  66. 66.

    Deka, M. J. & Chowdhury, D. Chiral carbon dots and their effect on the optical properties of photosensitizers. RSC Adv. 7, 53057–53063 (2017).

    CAS  Article  Google Scholar 

  67. 67.

    Li, F. et al. Highly fluorescent chiral N-S-doped carbon dots from cysteine: affecting cellular energy metabolism. Angew. Chem. Int. Ed. 57, 2377–2382 (2018).

    CAS  Article  Google Scholar 

  68. 68.

    Hu, L. et al. Chiral evolution of carbon dots and the tuning of laccase activity. Nanoscale 10, 2333–2340 (2018).

    CAS  PubMed  Article  Google Scholar 

  69. 69.

    He, X., Wang, Y., Jiang, H. & Zhao, L. Structurally well-defined sigmoidal gold clusters: Probing the correlation between metal atom arrangement and chiroptical response. J. Am. Chem. Soc. 138, 5634–5643 (2016).

    CAS  PubMed  Article  Google Scholar 

  70. 70.

    Ehrat, F. et al. Tracking the source of carbon dot photoluminescence: aromatic domains versus molecular fluorophores. Nano Lett. 17, 7710–7716 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

Download references


This work was supported by the University of Trieste, INSTM, AXA Research Fund, the Spanish Ministry of Economy and Competitiveness MINECO (project CTQ2016-76721-R), Diputación Foral de Gipuzkoa program Red (101/16) and ELKARTEK bmG2017 (Ref: Elkartek KK-2017/00008, BOPV resolution: 8 Feb 2018). R.P. and A.D. thank MIUR for financial support “Piano della Ricerca di Ateneo 2016–2018 linea di intervento 2”. We would like to thank Dr. Jatish Kumar (CIC biomaGUNE), Prof. Lorenzo di Bari (Università di Pisa) and Prof. Marcella Bonchio (Università di Padova) for helpful discussions.

Author information




L.Ð., F.A. and M.P. conceived and coordinated the project. L.Ð. and F.A. designed and performed the experiments and wrote the manuscript, with input from all the authors. A.D. and R.P. contributed to the experimental design and obtained the CD data. M.C. contributed with the scale-up preparation of the materials. N.M. contributed with the FDCD experiments. T.B. contributed with the VCD experiments. M.P. oversaw the research, co-wrote the manuscript and secured the funding.

Corresponding authors

Correspondence to Luka Ðorđević, Francesca Arcudi or Maurizio Prato.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ðorđević, L., Arcudi, F., D’Urso, A. et al. Design principles of chiral carbon nanodots help convey chirality from molecular to nanoscale level. Nat Commun 9, 3442 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing