Abstract
Metal–organic frameworks (MOFs) have so far been highlighted for their potential roles in catalysis, gas storage and separation. However, the realization of high electrical conductivity (>10−3 S cm−1) and magnetic ordering in MOFs will afford them new functions for spintronics, which remains relatively unexplored. Here, we demonstrate the synthesis of a two-dimensional MOF by solvothermal methods using perthiolated coronene as a ligand and planar iron-bis(dithiolene) as linkages enabling a full π-d conjugation. This 2D MOF exhibits a high electrical conductivity of ~10 S cm−1 at 300 K, which decreases upon cooling, suggesting a typical semiconductor nature. Magnetization and 57Fe Mössbauer experiments reveal the evolution of ferromagnetism within nanoscale magnetic clusters below 20 K, thus evidencing exchange interactions between the intermediate spin S = 3/2 iron(III) centers via the delocalized π electrons. Our results illustrate that conjugated 2D MOFs have potential as ferromagnetic semiconductors for application in spintronics.
Similar content being viewed by others
Introduction
The realization of high electrical conductivity and long-range magnetic ordering within a single material is highly appealing to meet the demands for data storage and processing1,2. Typically, ferromagnetic semiconductors are of considerable interest for spintronics (spin electronics) applications3,4,5, where the electronic spins can be modulated by external electrical and magnetic fields to perform logic operations and act as memory. Currently, materials employed as ferromagnetic semiconductors generally comprise inorganic solid compounds like Heusler compounds and dilute magnetic semiconductors4,6,7,8 and organic/molecular film semiconductors9,10,11,12,13,14,15,16. In these inorganic solids, direct metal–metal bonds or indirect interactions among metal atoms mediated by small ligands (such as oxo atoms) enable the long-range electronic communication, which is essential to achieve the electrical conductivity and magnetic ordering4,6,7,8. Nevertheless, their entirely inorganic composition prevents a facile tunability of magnetic and conductive properties due to the lack of both ligand functionalization and structural diversity. In the case of molecular film semiconductors, their electronic and magnetic properties can be tuned to a much higher degree, due to the structural diversities of organic monomers and functional groups that can be employed. Notably, the molecular semiconductors such as vanadium-tetracyanoethylene11 and metal-phthalocyanine12,13,14 have exhibited strong magnetic coupling at high temperature, which are considered as an emerging class of spin transport media with long spin lifetime due to their carbon-based light-atom compositions. Nevertheless, the low mobility and complex transport properties in molecular semiconductors still hinder their practical applications for spintronics.
In contrast, metal–organic frameworks (MOFs) are hybrid porous materials based on crystalline coordination polymers consisting of metal atoms or clusters connected by organic ligands17,18. Their properties and functions can be tuned by varying abundant organic ligands, metal centers and framework geometries, thus enabling their potential in catalysis19, sensing20, gas storage21,22 and separation23, etc. However, it is still challenging to realize magnetic MOF semiconductors. The conventionally reported three-dimensional (3D) MOFs showed extremely low bulk electrical conductivity (10−12 to 10−8 S cm−1)20,24 and weak magnetic coupling due to the large separation of metal centers by multi-atoms, insulating organic ligands, etc. Recent advances disclosed that the incorporation of conducting guests in MOFs could significantly enhance the electrical conductivity25,26. Moreover, immobilizing redox-active ligands with mixed-valences, such as 2,5-dihydroxybenzoquinone, into the backbones of iron(III) complexes could generate long-range charge delocalization and strong magnetic exchange27,28,29, leading to high conductivity (~10−4 to ~0.2 S cm−1) and high-temperature magnetic ordering (Curie temperature even could reach 105 K). In addition, the design of conjugated 2D MOFs by employing planar organic ligands and square-planar metal-complex linkages inducing full delocalization of π-electrons has also led to improved electrical conductivity (>10−3 S cm−1)20,24. These reported 2D MOFs are based on benzene30–32 or triphenylene-derivatives33,34,35,36 with thiol30,31,35,36, hydroxyl33 or amino32,34 groups linked via Ni or Cu metal centers and have been integrated as electrode materials for applications in transistor37, electrocatalysis35,38,39, chemiresistive sensor40 and energy storage41. Despite the magnetic behavior of these 2D MOFs remains unexplored, high delocalization of π-electrons in a 2D plane enables the interaction between charge carriers and localized spins to drive magnetic ordering3,42, which makes conjugated 2D MOFs as intriguing candidates for ferromagnetic semiconductors42,43,44.
In this study, we demonstrate a 2D MOF (PTC-Fe) consisting of polycyclic aromatic hydrocarbon monomer, namely 1,2,3,4,5,6,7,8,9,10,11,12-perthiolated coronene (PTC), as ligand connected by planar iron-bis(dithiolene) linkage enabling full π-d conjugation in a 2D plane. Thus, such 2D MOF is featured with hexagonal lattices and van der Waals layer-stacking structure. Four-probe van der Pauw electrical measurement revealed the room temperature conductivity value of ~10 S cm−1 for bulk compressed pellet. A variable-temperature conductivity measurement displayed a non-linear increase of conductivity with temperature, indicating a typical semiconducting behavior. A density functional theory (DFT) calculation was carried out to estimate the band gap as ~0.2 eV for a monolayer MOF. A variable-temperature magnetic susceptibility measurement as well as 57Fe Mössbauer spectra demonstrated that the PTC-Fe exhibited ferromagnetic ordering within nanoscale magnetic clusters at low temperatures (below ~20 K). Our work highlights conjugated 2D MOFs as a class of conductive materials exhibiting ferromagnetic and semiconducting features for potential spintronics application.
Results
Synthesis and structure
Black polycrystalline PTC-Fe 2D MOFs (Fig. 1a) were synthesized from reaction of 1,2,3,4,5,6,7,8,9,10,11,12-perthiolated coronene (PTC)45 with ammoniacal solutions of iron acetate (Fe(OAc)2) in the mixture of deoxygenated water and dimethylformamide (DMF) heated at 120 °C in a sealed vial for 48 h. The solid product was collected and washed by deoxygenated DMF, dilute hydrochloric acid (0.1 M), water and acetone and dried under vacuum at 100 °C. The attenuated total reflection IR (ATR-IR) spectra of PTC-Fe (Supplementary Fig. 1) displayed that the S-H signals at 2512 cm−1 disappeared in the PTC-Fe, suggesting that the thiol groups in monomer PTC were efficiently coordinated to Fe atoms. Thermogravimetric analysis (TGA) revealed that PTC-Fe decomposed above 300 °C, as evidenced by the pronounced weight losses above this temperature (Supplementary Fig. 2). The nitrogen sorption isotherms were measured at 77 K to evaluate the porosity of PTC-Fe (Supplementary Fig. 3), which showed gas uptake and release during the adsorption and desorption processes. The Brunauer–Emmett–Teller specific surface area was calculated to be 210 ( ± 5) m2/g with the existence of counter ions of NH4+ in the pores.
Powder X-ray diffraction (PXRD) measurements with Co Kα irradiation (λ = 1.79 Å) reveal a highly crystalline structure in PTC-Fe with prominent (100), (200) and (210) peaks at 2θ = 8.8°, 17.6°, and 21.7°, respectively, as shown in Fig. 1b. We simulated several possible stacking arrangements for the layers of PTC-Fe by DFT calculation (Supplementary Fig. 4). The experimentally resolved pattern agrees well with the AB packing model with 25% shifting in X and Y directions between neighboring layers. Thus, the PXRD results combined with the theoretical simulation provide a structural model of PTC-Fe (Fig. 1b and enlarged image shown in Supplementary Fig. 4d), which exhibits a hexagonal pattern within the ab planes and a AB layer stacking along the c direction. The square planar, conjugated iron-bis(dithiolene) linkages extend the π-electron conjugation of coronene in a 2D plane. From the peak at 2θ = 8.8°, we can infer a hexagonal unit cell with a = b = ~11.7 Å. The peak at 2θ = 26.0°, corresponding to the (001) reflection suggests an ordered stacking with an inter-layer distance of ~3.9 Å.
Transmission electron microscopy (TEM) studies provide further evidence of 2D long-range order and layer stacking in PTC-Fe. The TEM images show a non-porous morphology in PTC-Fe (Fig. 1c and Supplementary Fig. 5). In-plane periodicity is determined by selected area electron diffraction (SAED, inset in Fig. 1c), which presents strong polycrystalline diffraction rings. The ring size reveals an ordered network with a = ~1.2 nm cell size. High resolution TEM (HRTEM) images clearly present crystalline domains within a dozen of nanometers (Fig. 1d and Supplementary Fig. 5). Fast Fourier transform (FFT) analysis of a crystalline domain in Fig. 1d further demonstrates a hexagonal structure with a lattice parameter a = b = ~1.2 nm, in excellent agreement with PXRD and DFT results. A cross view of PTC-Fe sample shows the layer-stacking structure with an interlayer distance of ~4 Å (Fig. 1e).
Compositional characterization
Next we investigated the composition of PTC-Fe. X-ray photoelectron spectroscopy (XPS) spectrum discloses the presence of Fe 2p, N 1 s, C 1 s, S 2 s, and S 2p core levels (Supplementary Fig. 6a). The N signal originates from the counter ions of NH4+ balancing the charged system. The high-resolution Fe 2p photoemission spectrum shows two sets of peaks (Supplementary Fig. 6b), with binding energies of 710.9 and 723.9 eV, which are assigned to the 2p3/2 and 2p1/2 levels, respectively, indicating the presence of Fe(III) species. The S 2p peak in the XPS spectrum occurs at a binding energy of ~162 eV. Deconvolution of the S 2p signal generates high-intensity dual peaks at 161.5 and 162.7 eV derived from the Fe–S units, evidencing efficient complexation between Fe ions and thiol groups (Supplementary Fig. 6c). Quantitative analysis of the Fe and S signals provides a Fe:S ratio of ~0.98:4, which is in consistence with the expected PTC-Fe model.
Synchrotron powder X-ray absorption spectroscopy (XAS) was employed to characterize the coordination geometry and iron valence in PTC-Fe (Fig. 2a and Supplementary Methods). As a reference, the known one-dimensional coordination polymer (TTB-Fe)46 comprising 1,2,4,5-tetrathiolbenzene and iron (III), as well as Fe foil, FeO and Fe2O3 inorganic solids were also investigated by XAS. Thus, the Fe K-edge X-ray absorption near edge structure (XANES) spectra of PTC-Fe reveal the same coordination geometry as the TTB-Fe. Figure 2b shows the Fourier transform of the κ-weighted extended X-ray absorption fine structure (EXAFS) spectra of PTC-Fe, as well as Fe2O3 and TTB-Fe as contrast samples. The EXAFS spectra present a predominant peak in PTC-Fe, which is originated from the nearest-neighboring sulfur coordination shell around the Fe atoms. Based on this peak, Fe-S distance was calculated to be ~2.23 Å. Besides this first-shell interaction, the second-shell atomic interactions were also observed, based on which distance of Fe–C of ~3.39 Å was calculated (Supplementary Fig. 7). These bond lengths are very close to those of the contrast sample TTB-Fe, which are well consistent with the iron-bis(dithiolene) geometry. However, another contrast sample Fe2O3 exhibits two predominant peaks at ~1.44 Å and ~2.57 Å, which arise from Fe–O and Fe–Fe bonds, respectively. Therefore, the XANES and EXAFS spectra of PTC-Fe and the contrast experiments provide strong proof on the formation of square planar iron-bis(dithiolene) complexes via the coordination of PTC and Fe ions. Moreover, no metal oxides such as FeO and Fe2O3 were detected in the PTC-Fe.
In order to further investigate the iron coordination geometry, local electronic structure, and magnetic properties, 57Fe Mössbauer spectra were measured between 300 and 5 K (Fig. 2c, d, Supplementary Methods, Supplementary Fig. 8 and Supplementary Table 1). Spectra obtained by cooling down from 300 to 10 K mainly feature a single quadrupole doublet. The isomer shift IS = 0.21 mm/s and quadrupole splitting QS = 2.89 mm/s at T = 300 K are within the range of values typical for Fe(III) complexes with thiolate ligands and square planar coordination geometry47,48, which is in agreement with the anticipated Fe-bis(dithiolene) coordination in PTC-Fe. The intensity asymmetry of the two doublet components is a texture effect reflecting preferred orientation of crystallites in the sample. The d-orbital splitting pattern in square planar ligand environment is known to stabilize an intermediate spin S = 3/2 state for Fe3+, and the large quadrupole splitting reflects the unequal electron population of the Fe 3d orbitals split by the ligand field (valence contribution to the electric field gradient)27,49. The S = 3/2 (intermediate spin) ground state of Fe3+ is a consequence of the square planar coordination geometry, which leads to a pronounced energetic stabilization of the 3dz2 orbital with respect to the dx2−y2 orbital, and the energy of the dz2 orbital is comparable to the energies of the dxy, dxz, and dyz orbitals. Compared with the Fe(III), somewhat larger isomer shifts are expected for square planar Fe(II) complexes with an intermediate spin S = 1. The temperature dependence of IS reflects the usual second-order Doppler shift. A broadened quadrupole doublet (Supplementary Fig. 8) is observed at 10 K; however, at 5 K, the Mössbauer spectrum exhibits magnetic hyperfine splitting suggesting a magnetic ordering transition (Fig. 2d). Furthermore, Mössbauer spectra at low temperature also prove no iron oxides purities in the PTC-Fe.
Electronic structure of PTC-Fe
We measured solid-state UV-Vis spectrum of PTC-Fe (Supplementary Fig. 9). Importantly, the electronic absorption features of PTC-Fe extend well into the near-infrared (NIR) range. Such low-energy electronic excitations are common in highly conjugated organic/metal-organic and conducting polymers26. In order to estimate the electronic band structure of PTC-Fe, DFT calculations were performed (Fig. 3, Supplementary Methods and Supplementary Figs. 10–12). The density of states (DOS) describe the type and the number of states occupied at a certain energy and are essential for determining the carrier concentrations and energy distributions within a semiconductor50. In this respect, we provide the DOS results for both the single layer (Fig. 3a, b, Supplementary Figs. 10, 11) and multilayer of the 2D MOF with AB stacking model (Fig. 3c, d, Supplementary Fig. 12). Spin up, spin down and mixed spin directions have been considered in the DOS calculation. The band structure simulation for the single layer indicates a band gap of ~0.2 eV (Fig. 3a, b), while that for the AB stacking system exhibits a metallic character (Fig. 3c, d). In addition, the single layer and AB stacking models present a band gap of ~0.7 eV and ~1 eV for the spin-up channel, respectively (Fig. 3b, d). However, for spin down channel, a semi-conducting feature remains for single layer while a metallic character is dominantly presented for AB stacking. Layer stacking is believed to narrow the band gap for most of the 2D materials51. In addition, due to the negatively charged structure in PTC-Fe, a compensating cation (NH4+) has been introduced into the cell to avoid electrostatic potential and energy diverge induced by net charge, which could also play a crucial role in narrowing the band gap. Around the Fermi level the dominating states are coming from Fe-d and S-p orbitals (Supplementary Fig. 10a and c). Analysis of the projected density of states (PDOS) near to the Fermi level show a hybridization of the p-orbitals of S and the dyz- and dxz-orbitals of Fe, suggesting that the p-orbitals of the system are delocalized (Supplementary Fig. 10b and d). The bulk materials are expected to be semi-metallic in the ab directions (due to the metal ions and the S atoms) and semiconducting in the c direction due to weak van der Waals interactions.
DC conductivity measurements
The bulk electrical properties of PTC-Fe were determined from pelletized samples with the thickness of ~0.3 mm obtained by pressing powders at ~1 GPa (Inset in Fig. 4a). The I–V curves were measured in the van der Pauw geometry and displayed Ohmic response between –1.0 and +1.0 V (Supplementary Fig. 13), which gave an electrical conductivity of the pellets as high as ~10 S cm-1 at 300 K. This is among the highest values for the thus far reported intrinsically conducting MOF powders (Supplementary Table 2)20,24,32.
The variable-temperature conductivity measurements showed a non-linear increase of conductivity from 20 to 320 K (Fig. 4a), indicating a typical semiconducting feature. The natural logarithm of conductivity (lnσ) plotted versus reciprocal temperature (1/T) is presented in Fig. 4b. The plot shows a linear region over a temperature range of 125–300 K, consistent with a thermally activated transport dominant in this temperature range. The slope of the linear region in Fig. 4b corresponds to the activation energy (Ea), which can be extracted from the following Arrhenius law: σ~exp(Ea/kT), where σ is the conductivity, Ea is the activation energy, k is the Boltzmann constant (8.617 × 10−5 eV/K) and T is the temperature31. The value of Ea was evaluated from the slope of lnσ versus 1/T plot and was calculated as 0.2 eV. As shown in the inset of Fig. 4b, the plot of ln(σ) versus T−1/4 over the temperature region 65–130 K, which is well fitted to the Mott variable range hoping (Mott–VRH) model52. We ascribe this hopping process to the grain boundaries between the crystallites dominating the temperature dependence of conductivity in the bulk polycrystalline pellets, giving rise to apparent semiconducting behavior32.
Magnetic properties of PTC-Fe
Iron-based MOFs [Fe(III)] can exhibit magnetic exchange interactions between neighboring iron atoms through the bridging ligands27,29. In order to probe the magnetic properties of the PTC-Fe, we measured the magnetization using a superconducting quantum interference device-vibrating sample magnetometer (SQUID-VSM) (Fig. 5).
Figure 5a and Supplementary Fig. 14a show the variation of the magnetization with applied magnetic field (H) measured at different temperatures. While at 50 K the magnetization increases linearly with field, as expected for a paramagnetic system, a sigmoidal shape of M(H) below ~20 K signals the onset of ferromagnetism. For temperatures T ≤ 10 K a hysteresis is evident and the hysteresis width increases with decreasing temperature (coercive field ~0.07 T at 5 K). Furthermore, the T-dependent magnetization data (Fig. 5b) feature an increase in M below 20 K and a cusp in the zero-field cooled (ZFC) magnetization near 15 K. Below 15 K the FC and ZFC data diverge. These observations point to nanoscale ferromagnetism with an average blocking temperature of about 15 K53. The evolution of ferromagnetism below ~20 K is in agreement with the variable-temperature magnetic remanence measurements (inset in Fig. 5b). These clues are in accordance with the Mössbauer spectra (Supplementary Fig. 8) where line broadening near 10 K signals the onset of spin freezing on the Mössbauer time scale (~10−8 s), while the broad hyperfine pattern at 5 K verifies that the majority of the sample is in a frozen magnetic state. However, the very broad hyperfine field distribution (Supplementary Fig. 8, bottom) suggests a wide distribution of relaxation times due to a variation in the size of the magnetic nano-domains.
Discussion
To understand the origin of the relatively high-temperature (<20 K) ferromagnetic semiconducting ground state in PTC-Fe, we investigated the magnetic properties of the organic ligand PTC as well as coronene as contrast samples by SQUID. The temperature dependent remanent magnetization plots reveal that the ligand PTC and the building core coronene contribute ignorable magnetic ordering even at 5 K while the coordination complexes comprising PTC and Fe behave ferromagnetism (Supplementary Fig. 15). We then evaluated the spin density distribution in AB-stacking PTC-Fe by DFT calculation (Supplementary Fig. 16), which suggests that the Fe atoms provide the major spins compared with the C and S atoms, associated with localized d electrons44. In this case, Fig. 5c shows the magnetic ground states of the PTC-Fe with unit-cell magnetization, in which the magnetic moments are predominantly localized on the iron atoms. Notably, the magnetic ground state of the system at 0 K will be ferromagnetic if the magnetic exchange energy is positive whereas anti-ferromagnetic if negative. Here, an exchange energy of Eex=1.22 meV (Eex=EAFM—EFM) has been obtained by DFT calculation, further revealing the intrinsic ferromagnetic character of this 2D MOF43,54. The simulated Curie temperature of PTC-Fe is ~16 K by employing Ising model (calculation seen in Supplementary Methods)54, which further supports the SQUID measurements on the magnetic ordering with a blocking temperature of ~15 K (Fig. 5b).
With the preliminary determination of spin distribution, we attempt to further achieve an understanding how the magnetic coupling appears between the localized spins on Fe toms. Given the distance between the neighboring lateral Fe atoms from ~0.54 to ~1.20 nm in PTC-Fe MOF (Fig. 1b and Supplementary Fig. 7), direct exchange between the d orbitals of lateral Fe is relatively weak, and thus cannot be responsible for the strong ferromagnetic coupling between the intralayer Fe atoms. In addition, the layer distance is ~0.38 nm and the distance between the neighboring interlayer Fe atoms is ~0.5 nm, also leading to relatively weak direct exchange interaction. Thus, we propose that the magnetic coupling is induced by indirect exchange interaction14,27,28,29,43,44,55,56. Namely, the localized spin moments of the Fe atoms polarize the delocalized p orbital through exchange interaction. That is because this layer-stacked PTC-Fe MOF comprises of fully conjugated planar structure, enabling strong hybridization between the d/p orbitals of Fe, the coronene core, and the Fe-bis(dithiolene) nodes, which has a critical impact on the magnetic properties of the lattice. DOS plots also indicate that dxz/dyz orbitals of Fe participate in the hybridization of p orbitals (Supplementary Figs. 10 and 12), leading to strong exchange interaction between the localized d orbitals and the p orbitals, and hence ferromagnetic coupling. This indirect exchange through delocalized electrons is consistent with the Zener d-p exchange42,57 or the Ruderman–Kittel–Kasuya–Yosida (RKKY)58,59 exchange mechanism.
In summary, we have synthesized a coronene-based conjugated 2D MOF that exhibits record electrical conductivity of ~10 S cm−1 for bulk compressed pellets at room temperature. The variable-temperature conductivity measurements revealed a typical semiconducting behavior for PTC-Fe. The variable-temperature magnetic susceptibility measurements indicated that PTC-Fe exhibits a ferromagnetic ground state at low temperature resulting from the unique hybridization between the d/p orbitals of Fe, the coronene core, and the Fe-bis(dithiolene) nodes. Our work indicates that endowing 2D MOFs with strongly delocalized π systems can be an effective strategy to develop novel ferromagnetic MOF semiconductors. The possible contribution from the magnetic impurities to the ferromagnetic ordering has been excluded via the combined analysis of XPS, XANES, EXAFS, and 57Fe Mössbauer spectra. It should be noticed that the conductive and magnetic behavior presented here did not rule out the impact of the defects possibly generated from grain boundaries, the crystallite tilting and the edges in the bulk materials60, due to the polycrystalline feature and structural complexity as a result of heterogeneity. In addition, the tuning of the defects generated from the uncoordinated vacancy sites was able to lead to long-range ferromagnetic coupling in MOFs, which have been significantly proved via theoretical and experimental approaches61. Our results hopefully encourage more physical studies on the ferromagnetic and semiconducting properties as well as spintronic applications, relying on the growth of MOF single-crystals or 2D crystalline films with tuned thickness and enlarged crystalline domain size by interfacial synthesis or chemical vapor deposition methods, which remains to be explored.
Methods
Materials
The ligand, 1,2,3,4,5,6,7,8,9,10,11,12-perthiolated coronene (PTC), was synthesized according to our previous reported protocols45. Starting from coronene, 1,2,3,4,5,6,7,8,9,10,11,12-dodecachlorocoronene was prepared by chlorination reaction. Nucleophilic replacement of all peripheral chlorosubstituents was achieved using lithium benzylthiolate at room temperature, which afforded 1,2,3,4,5,6,7,8,9,10,11,12-dodecakis(benzylthio)coronene as a red powder in 62% yield. After reductive cleavage of the protective benzyl groups under Birch conditions using lithium in anhydrous liquid ammonia at −78 °C, the dodecalithiocoronene-1,2,3,4,5,6,7,8,9,10,11,12-dodecathiolate was obtained. The subsequent direct treatment with aqueous hydrogen chloride and hydrogen peroxide afforded persulfurated coronene (PSC) in 61% isolated yield. The reduction of PSC by NaBH4 could afford PTC via the cleavage of S–S bonds.
Synthesis of PTC-Fe 2D MOFs
A degassed solution of 0.014 mmol (10.0 mg) of PTC in 0.5 mL of DMF, 0.1 mL of aqueous ammonia (NH4OH, 6 M), and a degassed solution of anhydrous Fe(OAc)2 (7.5 mg, 0.043 mmol) in 0.5 mL of water were transferred into a 10 ml glass vial and sonicated for 5 min at 0 °C. Then, the vial was sealed and heated at 120 °C in an oven for 48 h, followed by natural cooling to room temperature. The solid product was afterwards collected and washed three times by deoxygenated DMF, dilute HCl (0.1 M), water and acetone. After dried at 100 °C under vacuum for 24 h, ~12 mg of black crystals was obtained and stored in Ar. Anal. Calcd. for [Fe3C24S12]3- •(NH4+)3: C, 32.19; S, 42.92; N, 4.69; H, 1.34. Found: C, 32.41; S, 43.12; N, 4.45; H, 1.68, in which the NH4+ are counter ions to balance the charges in the system.
Conductivity measurements
The solid sample was finely ground and pressed between two Mylar tapes (sample thickness is about 300 μm and the diameter is around 1.2 cm) at ~1 GPa. The Cu wires were contacted on the pellet surface by carbon paint in a glove box. Thus, a four-point contact was placed at the circumference to define a square. The I–V curves of the pellets were measured in van der Pauw geometry under vacuum at varied temperatures (from 20 K to 320 K) using a commercial Lakeshore Hall System.
Magnetic studies
Magnetometry was performed using a SQUID-VSM (Quantum Design). Temperature dependence of the magnetization of the PTC-Fe 2D MOF powder sample was measured in zero-field cooling and field cooling sequence with applied magnetic field of 100 Oe. The magnetic field dependence of magnetization was measured at different temperatures, i.e., 5, 10, 20, 25, and 50 K. Remanent magnetization was measured as a function of temperature in a zero magnetic field, after the sample was cooled down from 350 K to 5 K in a magnetic field of 1000 Oe.
Data availability
The data that support the findings of this study are available from the corresponding author on reasonable request.
References
Dechambenoit, P. & Long, J. R. Microporous magnets. Chem. Soc. Rev. 40, 3249–3265 (2011).
Awschalom, D. D. & Flatté, M. E. Challenges for semiconductor spintronics. Nat. Phys. 3, 153–159 (2007).
Dietl, T. A ten-year perspective on dilute magnetic semiconductors and oxides. Nat. Mater. 9, 965–974 (2010).
Dietl, T. & Ohno, H. Dilute ferromagnetic semiconductors: physics and spintronic structures. Rev. Mod. Phys. 86, 187–251 (2014).
Dietl, T. Ferromagnetic semiconductors. Semicond. Sci. Technol. 17, 377–392 (2002).
Xu, Y., Awschalom, D. D. & Nitta, J. Handbook of Spintronics. Vol. 9, 335–364 (Springer, Netherlands, 2016).
Chadov, S. et al. Tunable multifunctional topological insulators in ternary Heusler compounds. Nat. Mater. 9, 541–545 (2010).
Fedorych, O. M. et al. Magnetic order in semiconducting, ferromagnetic Ga1−xMnxAs. Semicond. Sci. Technol. 19, S492 (2004).
Xiong, Z. H., Wu, D., Vardeny, Z. V. & Shi, J. Giant magnetoresistance in organic spin-valves. Nature 427, 821–824 (2004).
Dediu, V. A., Hueso, L. E., Bergenti, I. & Taliani, C. Spin routes in organic semiconductors. Nat. Mater. 8, 707–716 (2009).
Yoo, J. W. et al. Spin injection/detection using an organic-based magnetic semiconductor. Nat. Mater. 9, 638–642 (2010).
Warner, M. et al. Potential for spin-based information processing in a thin-film molecular semiconductor. Nature 503, 504–509 (2013).
Serri, M. et al. High-temperature antiferromagnetism in molecular semiconductor thin films and nanostructures. Nat. Commun. 5, 3079 (2014).
Dhara, B. et al. Possible room-temperature ferromagnetism in self-assembled ensembles of paramagnetic and diamagnetic molecular semiconductors. J. Phys. Chem. Lett. 7, 4988–4995 (2016).
Tsurumi, J. et al. Coexistence of ultra-long spin relaxation time and coherent charge transport in organic single-crystal semiconductors. Nat. Phys. 13, 994–998 (2017).
Odenthal, P. et al. Spin-polarized exciton quantum beating in hybrid organic–inorganic perovskites. Nat. Phys. 13, 894–899 (2017).
Li, H., Eddaoudi, M., O’Keeffe, M. & Yaghi, O. M. Design and synthesis of an exceptionally stable and highly porous metal-organic framework. Nature 402, 276–279 (1999).
Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, 1230444 (2013).
Zhang, T. & Lin, W. Metal-organic frameworks for artificial photosynthesis and photocatalysis. Chem. Soc. Rev. 43, 5982–5993 (2014).
Stassen, I. et al. An updated roadmap for the integration of metal-organic frameworks with electronic devices and chemical sensors. Chem. Soc. Rev. 46, 3185–3241 (2017).
Eddaoudi, M. et al. Systematic design of pore size and functionality in isoreticular MOFs and their application in methane storage. Science 295, 469–472 (2002).
Murray, L. J., Dinca, M. & Long, J. R. Hydrogen storage in metal-organic frameworks. Chem. Soc. Rev. 38, 1294–1314 (2009).
Li, J.-R., Sculley, J. & Zhou, H.-C. Metal-organic frameworks for separations. Chem. Rev. 112, 869–932 (2012).
Sun, L., Campbell, M. G. & Dincă, M. Electrically conductive porous metal-organic frameworks. Angew. Chem. Int. Ed. 55, 3566–3579 (2016).
Talin, A. A. et al. Tunable electrical conductivity in metal-organic framework thin-film devices. Science 343, 66–69 (2014).
Dhara, B. et al. Increase in electrical conductivity of MOF to billion-fold upon filling the nanochannels with conducting polymer. J. Phys. Chem. Lett. 7, 2945–2950 (2016).
Darago, L. E. et al. Electronic conductivity, ferrimagnetic ordering, and reductive insertion mediated by organic mixed-valence in a ferric semiquinoid metal-organic framework. J. Am. Chem. Soc. 137, 15703–15711 (2015).
Jeon, I.-R., Negru, B., Van Duyne, R. P. & Harris, T. D. A 2D semiquinone radical-containing microporous magnet with solvent-induced switching from T c=26 to 80 K. J. Am. Chem. Soc. 137, 15699–15702 (2016).
DeGayner, J. A. et al. 2D conductive iron-quinoid magnets ordering up to T c=105 K via heterogenous redox chemistry. J. Am. Chem. Soc. 139, 4175–4184 (2017).
Kambe, T. et al. π-Conjugated nickel bis(dithiolene) complex nanosheet. J. Am. Chem. Soc. 135, 2462–2465 (2013).
Huang, X. et al. A two-dimensional π-d conjugated coordination polymer with extremely high electrical conductivity and ambipolar transport behaviour. Nat. Commun. 6, 7408 (2015).
Dou, J.-H. et al. Signature of metallic behavior in the metal-organic frameworks M3(hexaiminobenzene)2 (M=Ni, Cu). J. Am. Chem. Soc. 139, 13608–13611 (2017).
Hmadeh, M. et al. New porous crystals of extended metal-catecholates. Chem. Mater. 24, 3511–3513 (2012).
Sheberla, D. et al. High electrical conductivity in Ni3(2,3,6,7,10,11-hexaiminotriphenylene)2, a semiconducting metal-organic graphene analogue. J. Am. Chem. Soc. 136, 8859–8862 (2014).
Dong, R. et al. Large-area, free-standing, two-dimensional supramolecular polymer single-layer sheets for highly efficient electrocatalytic hydrogen evolution. Angew. Chem. Int. Ed. 54, 12058–12063 (2015).
Clough, A. J. et al. Metallic conductivity in a two-dimensional cobalt dithiolene metal-organic framework. J. Am. Chem. Soc. 139, 10863–10867 (2017).
Wu, G. et al. Porous field-effect transistors based on a semiconductive metal-organic framework. J. Am. Chem. Soc. 139, 1360–1363 (2017).
Miner, E. M. et al. Electrochemical oxygen reduction catalysed by Ni3(hexaiminotriphenylene)2. Nat. Commun. 7, 10942 (2016).
Dong, R. et al. Immobilizing molecular metal dithiolene-diamine complexes on 2D metal-organic frameworks for electrocatalytic H2 production. Chem. Eur. J. 23, 2255–2260 (2017).
Campbell, M. G. et al. Cu3(hexaiminotriphenylene)2: an electrically conductive 2D metal-organic framework for chemiresistive sensing. Angew. Chem. Int. Ed. 54, 4349–4352 (2015).
Sheberla, D. et al. Conductive MOF electrodes for stable supercapacitors with high areal capacitance. Nat. Mater. 16, 220–224 (2016).
Dietl, T. et al. Zener model description of ferromagnetism in zinc-blende magnetic semiconductors. Science 287, 1019–1022 (2000).
Li, W. et al. High temperature ferromagnetism in π-conjugated two-dimensional metal-organic frameworks. Chem. Sci. 8, 2859–2867 (2017).
Chakravarty, C., Bikash Mandal, B. & Sarkar, P. Coronene-based metal-organic framework: a theoretical exploration. Phys. Chem. Chem. Phys. 18, 25277–25283 (2016).
Dong, R. et al. Persulfurated coronene: a new generation of “sulflower”. J. Am. Chem. Soc. 139, 2168–2171 (2017).
Dirk, C. W., Cox, S. D., Wellman, D. E. & Wudl, F. Isolation and purification of benzene-1,2,4,5-tetrathiol. J. Org. Chem. 50, 2395–2397 (1985).
Dirk, C. W. et al. Metal poly(benzodithiolenes). Macromolecules 19, 266–269 (1986).
Sellmann, D., Geck, M. & Moll, M. Transition-metal complexes with sulfur ligands. 62. Hydrogen evolution upon reaction of protons with sulfur-coordinated iron(II) complexes. Investigation of the proton, hydrogen and hydride interactions with iron 1,2-benzenedithiolate complexes. J. Am. Chem. Soc. 113, 5259–5264 (1991).
Roy, N. et al. Molecular and electronic structure of the square planar bis(o-amidobenzenethiolato)iron(III) anion and its bis(o-quinoxalinedithiolato)iron(III) analogue. Inorg. Chem. 47, 10911–10920 (2008).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kuc, A. & Heine, T. The electronic structure calculations of two-dimensional transition-metal dichalcogenides in the presence of external electric and magnetic fields. Chem. Soc. Rev. 44, 2603–2614 (2015).
Wang, Y. et al. Ferromagnetism and crossover of positive magnetoresistance to negative magnetoresistance in Na-doped ZnO. Chem. Mater. 27, 1285–1291 (2015).
Friedländer, S. et al. Linear chains of magnetic ions stacked with variable distance: ferromagnetic ordering with a Curie temperature above 20 K. Angew. Chem. Int. Ed. 55, 12683–12687 (2016).
Zhou, J. & Sun, Q. Magnetism of phthalocyanine-based organometallic single porous sheet. J. Am. Chem. Soc. 133, 15113–15119 (2011).
Lannes, A. et al. Room temperature magnetic switchability assisted by hysteretic valence tautomerism in a layered two-dimensional manganese-radical coordination framework. J. Am. Chem. Soc. 138, 16493–16501 (2016).
Espallargas, G. M. & Coronado, E. Magnetic functionalities in MOFs: from the framework to the pore. Chem. Soc. Rev. 47, 533–557 (2018).
Zener, C. Interaction between the d shells in the transition metals. Phys. Rev. 81, 440–444 (1951).
Coey, J. M. D., Venkatesan, M. & Fitzgerald, C. B. Donor impurity band exchange in dilute ferromagnetic oxides. Nat. Mater. 4, 173–179 (2005). 92005.
Girovsky, J. et al. Long-range ferrimagnetic order in a two-dimensional supramolecular Kondo lattice. Nat. Commun. 8, 15388 (2017).
Fang, Z., Bueken, B., De Vos, D. E. & Fischer, R. A. Defect-engineered metal-organic frameworks. Angew. Chem. Int. Ed. 54, 7234–7254 (2015).
Shen, L. Origin of long-range ferromagnetic ordering in metal-organic frameworks with antiferromagnetic dimeric-Cu(II) building units. J. Am. Chem. Soc. 134, 17286–17290 (2012).
Acknowledgements
This work was financially supported by the ERC Grant on 2DMATER, EU Graphene Flagship, SPP 1928 (COORNET) and the German Science Council. We acknowledge the cfaed (Center for Advancing Electronics Dresden). We also thank Beamline BL14W1 at the Shanghai Synchrotron Radiation Facility (SSRF) for providing the beamtimes to carry out the XAS measurements. We acknowledge Dresden Center for Nanoanalysis (DCN) at TUD and Dr. Petr Formanek (Leibniz Institute for Polymer Research, IPF, Dresden) for the use of facilities, and we like to appreciate Prof. Stuart Parkin, Dr. Binghai Yan, Dr. Reinhard Berger and Mr. Chi Xu for the helpful discussion.
Author information
Authors and Affiliations
Contributions
X.L.F. and R.H.D. conceived and designed the experiments. R.H.D. synthesized the 2D MOFs, and conducted structure, composition and property characterizations. R.H.D. and M.C.W. synthesized the PTC precursors. Z.T.Z., R.H.D. and S.Q.Z. contributed to the magnetic measurements and analysis. Z.T.Z., S.Q.Z., R.H.D., Z.Z. and S.M. contributed to the conductivity measurements and analysis. D.T., Y.S., W.S. and C.F. performed the theoretical simulation of the 2D MOFs. P.A. and C.F. contributed to the Mössbauer spectroscopy measurements. Z.Q.L., R.H.D. and E.Z. carried out the HRTEM measurements. F.L. performed the X-adsorption spectroscopy experiments. R.H.D. and X.L.F. co-wrote the paper. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Dong, R., Zhang, Z., Tranca, D.C. et al. A coronene-based semiconducting two-dimensional metal-organic framework with ferromagnetic behavior. Nat Commun 9, 2637 (2018). https://doi.org/10.1038/s41467-018-05141-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-05141-4
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.