Abstract
The synthesis of polymers with on-demand sequence structures is very important not only for academic researchers but also for industry. However, despite the existing polymerization techniques, it is still difficult to achieve copolymer chains with on-demand sequence structures. Here we report a dually switchable and controlled interconvertible polymerization system; in this system, two distinct orthogonal polymerizations can be selectively switched ON/OFF independent of each other and they can be interconverted promptly and quantitatively according to external stimuli. Thus, the external stimuli can manipulate the insertion of distinct monomers into the resulting copolymer chains temporally, spatially, and orthogonally, allowing the on-demand precise arrangement of sequence structures in the resulting polymers. This dually switchable and interconvertible polymerization system provides a powerful tool for synthesizing materials that are not accessible by other polymerization methods.
Similar content being viewed by others
Introduction
The precise incorporation of monomers into the resulting polymer chains, forming sequence-controlled polymers, is a major challenge for modern polymer chemistry1,2,3,4,5,6,7,8,9,10,11,12,13. In molecular biology, the key processes are well executed by proteins and DNA—natural sequenced polymers with remarkable functions such as catalysis, molecular recognition, and data storage1. Precise sequence regulation of synthetic polymers may develop polymer materials with next-generation performance and functions. The first sequence-controlled polymer was prepared by sequential addition of monomers through peptide coupling or other coupling reactions during solid-supported step polymerization in 196314. Recently, Liu and colleagues9, and O’Reilly and colleagues15 have elegantly developed a DNA-templated synthesis methodology for synthetic polymers, i.e., using DNA as a template and translating its sequence into synthetic polymers. Johnson et al. have reported the click synthesis of unimolecular macromolecules by an iterative exponential growth strategy, wherein the chain length, sequence, and stereo-configuration can be precisely defined. However, they are unable to produce high molecular weights and are generally time intensive. For chain polymerizations, the precise sequence regulation is more difficult given the intrinsic mechanism. However, despite the difficulty, Pfeifer and Lutz16 proposed robust strategy for synthesizing sequence-controlled polymers via the timed addition of kinetically fast monomers. Sawamoto and colleagues17,18 designed a template initiator with different functional groups, which can recognize different monomers through molecular interactions. Hawker and colleagues6, and Hillmyer and colleagues19 have prepared sequence-controlled polymers using ring-opening polymerization, etc. Although the developed methods have proved to be very effective for regulating the sequence structure, it is still very difficult to achieve copolymer chains with on-demand sequence structures, especially when diverse monomers are all present in one pot simultaneously; moreover, many advanced polymeric architectures (e.g., symmetrically gradient, gradient block, and other periodic copolymers) that are expected to possess special physical properties are still synthetically intractable1,2,4,20,21,22,23. Recently, the use of stimuli to selectively start or suspend polymerization processes has attracted considerable attention, providing a very powerful tool for regulating polymerization20,24,25,26,27,28,29,30,31,32,33,34. Such switchable polymerization methods not only allow for the synthesis of polymers with controlled molecular weights but also provide opportunities to operate polymerizations temporally, spatially, and orthogonally35,36,37,38,39,40,41,42. For examples, Fors and colleagues31, and Kamigaito and colleagues43 reported a strategy that combines radical polymerization and cationic polymerization mechanisms in a one-pot setup, and switching the monomer selectivity provides an opportunity to control sequence of methyl acrylates and vinyl ethers or vinyl acetates. Boyer and colleagues35, and Zhu and colleagues44 have proposed a concept to use temperature to manipulate the polymer structure. Boyer and colleagues35 also has reported an interesting method to prepare block copolymer by two orthogonal polymerizations using different wavelengths. Therefore, switchable polymerization will be a promising and powerful means for regulating the sequence structure of polymer chains.
Here we propose a dually switchable and controlled interconvertible polymerization system involving an anionic ring-opening polymerization (AROP), which only polymerizes cyclic monomers and a photoinduced electron transfer–reversible addition–fragmentation chain transfer (PET-RAFT) polymerization that is highly selective to vinyl monomers. Both the AROP and PET-RAFT polymerization can be selectively switched ON/OFF independent of each other using external stimuli, and a single trithiocarbonate unit can not only simultaneously control the AROP and PET-RAFT polymerization but also make them interconvert promptly and quantitatively on demand, as shown in Fig. 1. Therefore, the dually switchable polymerization system can polymerize cyclic monomers and vinyl monomers temporally, spatially, and orthogonally by heating or light irradiation, thus precisely manipulating the incorporations of monomers into the resulting polymer chains, forming copolymers with on-demand sequence structures.
Results
Switch ON/OFF of AROP and PET-RAFT polymerization
Nishikubo and colleagues45–47 found that quaternary onium salts could catalyze the AROP of cyclic thiirane monomers using thioester, thiourethane and trithiocarbonate as initiators. Here we found that the AROP of thiirane monomers using trithiocarbonate as the initiator was highly temperature dependent (Supplementary Figure 1), having a high apparent activation energy (Eaapp) of 100.87 kJ mol−1. At high temperatures ( > 50 °C) the AROP of thiiranes proceeded smoothly, whereas at 20 °C the polymerization did not occur even after 48 h, as shown in Supplementary Figure 1. This result suggested that the polymerization could be easily toggled between ON and OFF by heating and cooling. The S,S′-bis(α,α′-dimethyl-α″-acetic acid) trithiocarbonate (BDMAT)-mediated AROP of 2-(phenoxymethyl) thiirane (POMT) in the presence of quaternary onium salts was performed at 50 °C, as shown in Fig. 2a. After 1 h of reaction, the POMT conversion reached 21%. However, when the reaction temperature quickly decreased to room temperature (20 °C), the BDMAT-mediated AROP stopped immediately. Subsequently, the polymerization could restart by increasing the reaction temperature to 50 °C and could be suspended by rapid cooling. At each polymerization step, the produced polymers had controlled molecular weights and narrow polydispersity (Supplementary Figure 2). Therefore, the AROP of thiiranes could be easily switched between ON and OFF via heating and cooling, as shown Fig. 2a. This reason is that BDMAT-mediated AROP involved the slow formation of alkyl thiolate catalyzed by quaternary onium salts, as well as a fast attack of alkyl thiolate to trithiocarbonate followed by rearrangement. The formation of alkyl thiolate is a reversible process and higher temperatures favored the catalyst to overcome the energy barrier, thus opening the ring of the thiiranes.
On the other hand, trithiocarbonates are efficient chain transfer agents to control RAFT polymerization. Recently, Boyer and colleagues29,30,35,44,48,49,50,51,52,53,54,55,56 have developed a PET-RAFT polymerization method using a series of photocatalysts in response to different wavelength to control the free radical polymerization of vinyl monomers. The PET-RAFT polymerization of N,N-dimethylacrylamide (DMA) occurred under irradiation and stopped as soon as the irradiation was removed. Subsequently, the polymerization could be restarted rapidly by applying irradiation again. Therefore, the BDMAT-mediated PET-RAFT polymerization could be easily switched between ON and OFF, as shown in Fig. 2b.
Synthesis of ABA and BAB triblock copolymers in one pot
If the photocatalyst, quaternary onium salt, trithiocarbonate, vinyl monomer, and cyclic thiirane monomer were present in one pot simultaneously, neither the PET-RAFT polymerization of the vinyl monomer nor the AROP of the cyclic thiirane monomer occurred in the absence of irradiation or heating. When the polymerization system was irradiated with light, the photocatalyst was activated to polymerize vinyl monomers via PET-RAFT, whereas the AROP of thiirane monomers was dormant. On removing the irradiation and heating the polymerization system, the AROP was switched on, while the PET-RAFT polymerization was switched OFF. Further, trithiocarbonate unit could be switched to mediate the AROP from mediating the PET-RAFT polymerization when the AROP was started and the PET-RAFT polymerization was stopped. In addition, it could be switched back to regulate PET-RAFT polymerization when the heating was stopped and irradiation was applied to the system. Thus, the external stimuli could not only switch both AROP and PET-RAFT polymerization between ON and OFF but also make the polymerizations interconvert easily.
To verify the hypothesis, we chose Ir(ppy)3 as the photocatalyst for the PET-RAFT polymerization and tetraphenylphosphonium chloride (TPPCl) as the catalyst for the AROP (see experiment details in Supplementary Methods). When Ir(ppy)3, TPPCl, BDMAT, DMA, and POMT were all present at once, we first subjected the polymerization system to heating followed by irradiation (Fig. 3a). Under heating without irradiation, the AROP was switched ON, as shown in Fig. 3b. The POMT conversion reached 12% and 72% in 1 and 4.5 h (Supplementary Figures 3 and 4), respectively. A linear increase in ln([M]0/[M]) with reaction time was observed (Fig. 3c). In the UV–vis spectra, the absorption peak of trithiocarbonate shifted to 438 from 453 nm, because its neighboring units changed into POMT units (see Supplementary Figure 6). We used 1H–nuclear magnetic resonance (NMR) to trace the polymerization. It was very obvious that the signals attributed to polymer of POMT (PPOMT) gradually strengthened with increasing heating time, and that no peaks corresponding to polymer of DMA (PDMA) were present (Fig. 3f and Supplementary Figures 3 and 4), indicating that none of the DMA was consumed under heating. The polymers obtained under heating showed unimodal size exclusion chromatography (SEC) curves and controlled molecular weights (Fig. 3d, e). Subsequently, the mixture was rapidly cooled to room temperature and exposed to a 5-W blue light-emitting diode (LED). 1H-NMR results showed that the AROP of POMT stopped as soon as the heating was suspended. Under irradiation, Ir(ppy)3 was activated to trigger the PET-RAFT polymerization of DMA, giving a 62% monomer conversion after 5 h irradiation (Fig. 3b and Supplementary Figure 5). For the PET-RAFT polymerization, a linear relationship between ln([M]0/[M]) and reaction time, and between Mn and DMA conversion was observed, illustrating that this polymerization could be well controlled using trithiocarbonate-containing PPOMT as the macro-RAFT agent (Fig. 3c). Based on the 1H-NMR spectra, none of POMT was consumed under irradiation. In the UV–vis spectra, the absorption peak of trithiocarbonate shifted from 438 to 433 nm, because the neighboring units of trithiocarbonate changed from POMT into DMA units (Supplementary Figure 6). In addition, the proton signal intensity of PPOMT remained unchanged under irradiation, whereas the signal intensity of DMA appeared and strengthened with increasing the irradiation time (Fig. 3g), forming an ABA-type triblock copolymer containing two PPOMT segments and one PDMA segment with average 62 DMA units and 72 POMT units in one polymer chain. The Fourier infrared (FI-IR) spectra were also consistent with NMR analysis (Supplementary Figure 7). The above results indicated that the AROP and PET-RAFT polymerizations could be switched ON or OFF independent of each other, and that the AROP could be easily converted into the PET-RAFT polymerization when the external stimulus was changed from heating to irradiation. Further, the AROP and PET-RAFT polymerization showed highly selective monomer discrimination, which allowed a single propagating chain to selectively polymerize cyclic monomers and vinyl monomers on demand.
Second, we subjected the polymerization system to irradiation followed by heating. Under irradiation without heating, the PET-RAFT polymerization was activated and DMA started to polymerize. As irradiation time increased, the signal intensity of the peak corresponding to DMA and Mn value of the produced PDMA gradually increased and no peaks were observed for POMT (Supplementary Figures 8, 9, and 10). Subsequently, after the external stimulus was changed from irradiation to heating, the AROP of POMT was activated, whereas the PET-RAFT polymerization of DMA was suspended immediately (Supplementary Figures 8, 9, and 11). As heating time increased, the signals corresponding to POMT became stronger. The linear plots of ln([M]0/[M]) as a function of reaction time and Mn as a function of monomer conversion were also observed for both heating and irradiation (Supplementary Figure 8). According to 1H-NMR results, on an average, 77 DMA units and 74 POMT units were copolymerized into the polymer chain with a BAB triblock structure (Supplementary Figure 9). The above results demonstrated that there was no interference between the PET-RAFT and AROP, and that they could be interconverted promptly and quantitatively according to the external stimulus (heating or irradiation). Further, the polymerization could be switched back and forth on demand between AROP and PET-RAFT polymerization based on on demand by changing the external stimulus. The unique characteristics of this polymerization strategy will provide more powerful and precise controls of the polymer sequence structure.
Synthesis of multiblock copolymers in one pot
Multiblock copolymers possess special physical properties compared to common block copolymers23,57, but their synthesis is synthetically intractable2. Based on the above dually switchable system, multiblock copolymers could be prepared simply by subjecting the polymerization system to multiple rounds of heating followed by irradiation, such that vinyl and cyclic monomers were all present in one pot at once (Fig. 4a), e.g., the polymerization of DMA and POMT in the presence of BDMAT, TPPCl, and Ir(ppy)3 (see experiment details in Supplementary Methods). First, the AROP of POMT was started by heating the polymerization system to 60 °C and 23% of the POMT was converted to PPOMT with a trithiocarbonate unit in the middle of the PPOMT chain after 1 h, forming homo-PPOMT with Mn = 3.5 kDa (Fig. 4b, c and Supplementary Figure 12). After quickly cooling the system to room temperature and exposing it to a blue LED, the PET-RAFT polymerization of DMA was activated, while the AROP of POMT was suspended. Up to 25% of the DMA monomer was consumed in 2.5 h, forming a triblock copolymer containing two PPOMT blocks on either side of a DMA block, with Mn = 7.3 kDa (Fig. 4b, c and Supplementary Figure 12). Subsequently, the AROP of POMT wasrestarted by applying heat and removing the irradiation and another 22% of the POMT monomer was inserted into the block copolymer chain in 0.67 h, forming a pentablock copolymer having three PPOMT segments and two PDMA segments, with Mn = 11.2 kDa. Then, multiple rounds of heating followed by irradiation were alternatively applied continuously, to from heptablock, nonablock, and undecablock copolymers (Fig. 4b, c and Supplementary Figure 12). All the copolymers showed unimodal SEC curves and had controlled molecular weights. After three cycles of the PET-RAFT polymerization and AROP, an undecablock copolymer with six PPOMT blocks and five PDMA blocks was formed. Due to the similar conversion of both monomers during the cycles, each block had a similar length. Each block of PPOMT included ~ 14 units, whereas each block of PDMA included ~ 15 units (Supplementary Figure 12). During the synthesis of multiblock copolymers, the orthogonality of AROP and PET-RAFT was also confirmed by a controlled experiment (Supplementary Figures 13 and 14). To further verify the formation of the produced multiblock copolymers via this switchable polymerization system, we performed DSC analysis of the resulting undecablock copolymer. Generally, the Tg of PPOMT is 9 °C, whereas that of PDMA is 112 °C (Supplementary Figure 15). In DSC curve of the ABA triblock copolymer, two Tgs were observed (Supplementary Figure 16a), demonstrating microphase separation of long blocks in the resulting copolymer. Interestingly, the DSC curve of the resulting undecablock copolymer had only one broad Tg around 46 °C (Supplementary Figure 16b), which may have resulted from that no ordered structures or nanophase separation of nearly pure PPOMT or nearly pure PDMA segments was formed due to the short block length of PPOM or PDMA in the resulting polymer.
In this dually switchable and interconvertible polymerization system, the block numbers of the copolymer could be controlled by varying the number of cycles: one cycle resulted in the formation of a triblock copolymer, and two, three, four, and five cycles led to the formation of pentablock, heptablock, nonablock, and undecablock copolymers, respectively. The chain length for each block could be easily regulated by the irradiation and heating time. Thus, by simply varying the irradiation and heating time, a symmetrically gradient block copolymer (PPOMT30-b-PDMA8-b-PPOMT18-b-PDMA19-b-PPOMT9-b-PDMA34-SC( = S)-PDMA34-b-PPOMT9-b-PDMA19-b-PPOMT18-b-PDMA8-b-PPOMT30), which has so far been synthetically intractable, was easily obtained (Fig. 4d–f). For this long copolymer chain, the PPOMT blocks at both ends were the longest (30 POMT units) and the gradient decreased toward the middle (9 POMT units); further, the length of the DMA block gradient decreased from the middle (68 DMA units) to the ends (8 DMA unit). In the DSC curves (Supplementary Figure 17), two distinct glass transition intervals (7–28 °C, 71–82 °C), which were close to those of the homopolymers of PPOMT and PDMA, were observed; these were attributed to the long POMT blocks at both ends and long DMA block in the middle, respectively. Furthermore, very broad Tg range between 28 °C and 67 °C was observed, which corresponded to the broad phase containing mixed short PPOMT blocks and PDMA blocks sandwiched between long PPOMT blocks and PDMA blocks. The overall glass transition temperature range was 75 °C, which was similar to those of typical gradient copolymers58.
Synthesis of heptablock quadricopolymer in one pot
The dually switchable and interconvertible polymerization system showed broad monomer applicability, high efficiency, and no interference between the PET-RAFT polymerization and AROP. New monomers 2-methylthiirane (MT) and N-isopropyl acrylamide (NIPAM) were tested, and the results demonstrated that only MT was polymerized on heating, whereas only NIPAM was polymerized with blue light. Furthermore, there was no any consumption of both MT and NIPAM without light or heat, confirming the orthogonality of MT and NIPAM (Fig. 5a and Supplementary Figures 18 and 19). Therefore, multiblock copolymers with more diverse block structures could be easily prepared by sequential addition of comonomers and sequential heating followed by irradiation, e.g., the comonomers MT and NIPAM were first added into a polymerization tube, both MT monomer conversion and NIPAM monomer conversion reached ~ 100% after applying 12 h of heating followed by 15 h of irradiation, forming a triblock copolymer with two PMT blocks and one PNIPAM block, as shown in Fig. 5a, b; subsequently, the comonomers POMT and DMA were injected into the polymerization tube. On further heating for 12 h followed by irradiation for 15 h, a heptablock quadricopolymer with two PMT blocks, two PNIPAM blocks, two PPOMT blocks, and one PDMA block was formed (Fig. 5a,b). Based on the 1H-NMR and 13C–NMR spectra (Supplementary Figures 20 and 21), all four starting monomers were present in the resulting heptablock copolymer. SEC data (Fig. 5c) further demonstrated the controlled behavior during polymerization.
Advanced sequence control by programmed heating and irradiation
The sequences in biomacromolecules have a vital role in the development, functioning, and reproduction of all living organisms. The ability to construct highly organized sequence-controlled synthetic macromolecules would be a significant breakthrough with potential applications in many fields, including nanomedicine and nanotechnology1,4. However, the most developed strategies can only couple one building block at a time, and in many cases, they require protection/deprotection of the growing oligomer chains. Therefore, these strategies are expensive and time consuming, and only achieve a partial sequence control2,3. This dually switchable polymerization system proposed in the present study provides versatile means to precisely manipulate the sequence structure of the resulting polymers. As shown in Fig. 6a–c and Supplementary Figure 22, using the well-designed program of heating combined with intermittent irradiation, the DMA unit could be precisely inserted into the PPOMT chain by simply irradiating the polymerization tube (see experiment details in Supplementary Methods). The length of each PPOMT segment could be controlled by the heating time. The location of the DMA unit in the PPOMT chain could be tuned by the irradiation time. The amount of the DMA and the length of the DMA and POMT in the co-segment could be regulated by the irradiation time and amount of Ir(ppy)3. Similarly, using a tailored program of continuous irradiation combined with intermittent heating, the POMT unit could be precisely inserted into the PDMA chain by simply heating the polymerization tube. The position of the POMT units in the PDMA chain could also be manipulated by the heating time; the number of the DMA units could be controlled by the heating time and amount of TPPCl added (Fig. 6d–f and Supplementary Figure 23). Therefore, we could precisely insert the DMA units into the PPOMT chain at any position simply via irradiation and insert the POMT units into the PDMA chain at any position simply by heating (Fig. 6).
Moreover, the proposed method is versatile, simple, and flexible. The program of heating and irradiation could be well-designed on demand, and hence the resulting copolymers with advanced sequence structures could be obtained. The sequence structure depends on the designed program of heating and irradiation and not on reactivity of the monomers. Therefore, to synthesize triblock copolymer PPOMT block-b-copolymer block-b-PDMA block, we should use the program of sequential heating, heating integrated with irradiation, and irradiation on the polymerization system, whereas to synthesize the triblock copolymer PPOMT block-b-PDMA block-b-copolymer block, we should use the program of sequential heating, irradiation, and heating integrated with irradiation on the polymerization system (see experiment details in Supplementary Methods). As shown in Fig. 7a–c and Supplementary Figure 24, the triblock copolymer PPOMT block-b-copolymer block-b-PDMA block was obtained when the program of sequential heating, heating integrated with irradiation, and irradiation was applied to the polymerization system. As shown in Fig. 7d–f and Supplementary Figure 25, the copolymers had multiple blocks of PPOMT, PDMA, and copolymer of POMT and DMA when multiple rounds of heating, heating integrated with irradiation, and irradiation were applied to the polymerization system. The location and length of the PPOMT blocks, PDMA blocks, and copolymer blocks of POMT and DMA could be well tuned.
Discussion
We design a dually switchable and controlled interconvertible polymerization system involving the AROP and PET-RAFT polymerization to obtain sophisticated microstructures; in this system, the AROP and PET-RAFT polymerization could be reversibly activated/inactivated rapidly and quantitatively according to the external stimuli. Further, the AROP and PET-RAFT polymerization could be fast interconverted and they show a highly selective monomer discrimination. Therefore, the well-designed program of heating and irradiation results in the synthesis of copolymers with a tailored composition, chain length, and on-demand sequence structure. Moreover, many other functional dithioesters and trithiocarbonates are also found to be suitable for this polymerization system, as well as diverse functional monomers; thus, a wide range of functionalities along the copolymer backbones with controlled physico-chemical properties could be incorporated in this system, leading to the formation of highly ordered materials with unique functions and properties. Therefore, the dually switchable and interconvertible polymerization system paves the way for the synthesis of a new class of macromolecules with on-demand sequence structures for a wide range of applications including nanostructured materials, polymeric phase separation, single-chain folding, and drug delivery.
Methods
Polymerization via heating followed by irradiation
DMA (891 mg, 9 mmol), POMT (1494 mg, 9 mmol), BDMAT (25.5 mg, 0.09 mmol), photocatalyst (27 µL, 15 p.p.m.), and TPPCI (11 mg, 0.03 mmol) were dissolved in DMAc to obtain 6 mL solution, which was further transferred into a glass tube with rubber plug. After three freeze–pump–thaw cycles, the tube was sealed and immersed in an oil bath at 60 °C. After suitable time interval, polymerization solution was taken out by injector. Conversions of POMT were calculated by 1H-NMR spectra. After 4.5 h heating (conversion of POMT reaching 72%), the tube was quickly cooled to room temperature and irradiated by 5 W blue LED strip. Similarly, after suitable time interval, polymerization solution was taken out by injector and conversions of DMA were calculated by 1H-NMR spectra. All the reaction mixtures at different reaction time were precipitated into diethyl ether several times and the products as light yellow solids were obtained after dried in vacuum.
Polymerization via irradiation followed by heating
DMA (891 mg, 9 mmol), POMT (1494 mg, 9 mmol), BDMAT (25.5 mg, 0.09 mmol), photocatalyst (27 µL, 15 p.p.m.), and TPPCI (11 mg, 0.03 mmol) were dissolved in DMAc to obtain 6 mL solution, which was further transferred into a glass tube with rubber plug. After three freeze–pump–thaw cycles, the tube was sealed and irradiated by 5 W blue LED strip. After suitable time interval, polymerization solution was taken out by injector and the conversions of DMA were calculated by 1H-NMR spectra. After 2.5 h irradiation (conversion of DMA reaching 77%), turn off the light source and the tube was immersed in an oil bath at 60 °C. Similarly, after suitable time interval, polymerization solution was taken out by injector and the conversions of POMT were calculated by 1H-NMR spectra. All the reaction mixtures at different reaction times were precipitated into diethyl ether several times and the products as light yellow solids were obtained after dried in vacuum.
Synthesis of multiblock copolymers
DMA (891 mg, 9 mmol), POMT (1494 mg, 9 mmol), BDMAT (20.1 mg, 0.072 mmol), photocatalyst (45 µL, 25 p.p.m.), and TPPCI (11 mg, 0.03 mmol) were dissolved in DMAc to obtain 6 mL solution, which was further transferred into a glass tube with rubber plug. After three freeze–pump–thaw cycles, the tube was sealed and immersed in an oil bath at 60 °C. After conversion of POMT reaching 23%, the tube was quickly cooled to room temperature and irradiated by 5 W blue LED strip. Similarly, after conversion of DMA reaching 25%, the light was turned off and the tube was immersed into oil bath at 60 °C again. After conversion of POMT reaching 46%, the tube was cooled to room temperature and irradiated by blue LED strip again. Then after conversion of DMA reaching 49%, the light was turned off and the tube was immersed into oil bath at 60 °C for the third time. After conversion of POMT reaching 70%, the tube was cooled to room temperature and irradiated by blue LED strip. All the reaction mixtures at different reaction time were precipitated into diethyl ether several times and the products as light yellow solids were obtained after dried in vacuum.
Data availability
The data that support the findings of this study are available within the article and its Supplementary Information File or from the corresponding author upon reasonable request.
References
Lutz, J. F., Ouchi, M., Liu, D. R. & Sawamoto, M. Sequence-controlled polymers. Science 341, 1238149 (2013).
Engelis, N. G. et al. Sequence-controlled methacrylic multiblock copolymers via sulfur-free RAFT emulsion polymerization. Nat. Chem. 9, 171–178 (2017).
Hibi, Y., Ouchi, M. & Sawamoto, M. A strategy for sequence control in vinyl polymers via iterative controlled radical cyclization. Nat. Commun. 7, 11064 (2016).
Lutz, J. F. Polymer chemistry: a controlled sequence of events. Nat. Chem. 2, 84–85 (2010).
Edwardson, T. G. W., Carneiro, K. M. M., Serpell, C. J. & Sleiman, H. F. An efficient and modular route to sequence-defined polymers appended to DNA. Angew. Chem. Int Ed. 53, 4567–4571 (2014).
Gutekunst, W. R. & Hawker, C. J. A general approach to sequence-controlled polymers using macrocyclic ring opening metathesis polymerization. J. Am. Chem. Soc. 137, 8038–8041 (2015).
Ji, Y. X. et al. Sequence-controlled polymers with furan-protected maleimide as a latent monomer. Angew. Chem. Int Ed. 56, 2328–2333 (2017).
Chen, Z., Lichtor, P. A., Berliner, A. P., Chen, J. C. & Liu, D. R. Evolution of sequence-defined highly functionalized nucleic acid polymers. Nat. Chem. 10, 420–427 (2018).
Niu, J., Hili, R. & Liu, D. R. Enzyme-free translation of DNA into sequence-defined synthetic polymers structurally unrelated to nucleic acids. Nat. Chem. 5, 282–292 (2013).
Ida, S., Terashima, T., Ouchi, M. & Sawamoto, M. Selective radical addition with a designed heterobifunctional halide: a primary study toward sequence-controlled polymerization upon template effect. J. Am. Chem. Soc. 131, 10808–10809 (2009).
Zhang, Z., You, Y. Z., Wu, D. C. & Hong, C. Y. Syntheses of sequence-controlled polymers via consecutive multicomponent reactions. Macromolecules 48, 3414–3421 (2015).
Porel, M., Thornlow, D. N., Phan, N. N. & Alabi, C. A. Sequence-defined bioactive macrocycles via an acid-catalysed cascade reaction. Nat. Chem. 8, 591–597 (2016).
Barnes, J. C. et al. Iterative exponential growth of stereo- and sequence-controlled polymers. Nat. Chem. 7, 810–815 (2015).
Merrifield, R. B. Solid phase peptide synthesis .1. Synthesis of a tetrapeptide. J. Am. Chem. Soc. 85, 2149–2154 (1963).
Milnes, P. J. et al. Sequence-specific synthesis of macromolecules using DNA-templated chemistry. Chem. Commun. 48, 5614–5616 (2012).
Pfeifer, S. & Lutz, J. F. A facile procedure for controlling monomer sequence distribution in radical chain polymerizations. J. Am. Chem. Soc. 129, 9542–9543 (2007).
Ida, S., Ouchi, M. & Sawamoto, M. Template-assisted selective radical addition toward sequence-regulated polymerization: lariat capture of target monomer by template initiator. J. Am. Chem. Soc. 132, 14748–14750 (2010).
Ida, S., Ouchi, M. & Sawamoto, M. Designer template initiator for sequence regulated polymerization: systems design for substrate-selective metal-catalyzed radical addition and living radical polymerization. Macromol. Rapid Comm. 32, 209–214 (2011).
Zhang, J. H., Matta, M. E. & Hillmyer, M. A. Synthesis of sequence-specific vinyl copolymers by regioselective ROMP of multiply substituted cyclooctenes. Acs Macro Lett. 1, 1383–1387 (2012).
Teator, A. J., Lastovickova, D. N. & Bielawski, C. W. Switchable polymerization catalysts. Chem. Rev. 116, 1969–1992 (2016).
Arriola, D. J., Carnahan, E. M., Hustad, P. D., Kuhlman, R. L. & Wenzel, T. T. Catalytic production of olefin block copolymers via chain shuttling polymerization. Science 312, 714–719 (2006).
Ouchi, M., Badi, N., Lutz, J. F. & Sawamoto, M. Single-chain technology using discrete synthetic macromolecules. Nat. Chem. 3, 917–924 (2011).
Eagan, J. M. et al. Combining polyethylene and polypropylene: Enhanced performance with PE/iPP multiblock polymers. Science 355, 814–816 (2017).
Treat, N. J. et al. Metal-free atom transfer radical polymerization. J. Am. Chem. Soc. 136, 16096–16101 (2014).
Leibfarth, F. A., Mattson, K. M., Fors, B. P., Collins, H. A. & Hawker, C. J. External regulation of controlled polymerizations. Angew. Chem. Int Ed. 52, 199–210 (2013).
Chen, M. et al. Logic-controlled radical polymerization with heat and light: multiple-stimuli switching of polymer chain growth via a recyclable, thermally responsive gel photoredox catalyst. J. Am. Chem. Soc. 139, 2257–2266 (2017).
Chen, M., Yang, B. P. & Chen, C. L. Redox-controlled olefin (co)polymerization catalyzed by ferrocene-bridged phosphine-sulfonate palladium complexes. Angew. Chem. Int Ed. 54, 15520–15524 (2015).
Dadashi-Silab, S., Doran, S. & Yagci, Y. Photoinduced electron transfer reactions for macromolecular syntheses. Chem. Rev. 116, 10212–10275 (2016).
Shanmugam, S., Xu, J. T. & Boyer, C. Light-regulated polymerization under near-infrared/far-red irradiation catalyzed by bacteriochlorophyll a. Angew. Chem. Int Ed. 55, 1036–1040 (2016).
McKenzie, T. G. et al. Beyond Traditional RAFT: Alternative Activation of Thiocarbonylthio Compounds for Controlled Polymerization. Advanced Science 3, 1500394 (2016).
Kottisch, V., Michaudel, Q. & Fors, B. P. Photocontrolled interconversion of cationic and radical polymerizations. J. Am. Chem. Soc. 139, 10665–10668 (2017).
Kottisch, V., Michaudel, Q. & Fors, B. P. Cationic polymerization of vinyl ethers controlled by visible light. J. Am. Chem. Soc. 138, 15535–15538 (2016).
Magenau, A. J. D., Strandwitz, N. C., Gennaro, A. & Matyjaszewski, K. Electrochemically mediated atom transfer radical polymerization. Science 332, 81–84 (2011).
Fors, B. P. & Hawker, C. J. Control of a living radical polymerization of methacrylates by light. Angew. Chem. Int Ed. 51, 8850–8853 (2012).
Fu, C. K., Xu, J. T. & Boyer, C. Photoacid-mediated ring opening polymerization driven by visible light. Chem. Commun. 52, 7126–7129 (2016).
Niu, J. et al. Engineering live cell surfaces with functional polymers via cytocompatible controlled radical polymerization. Nat. Chem. 9, 537–545 (2017).
Aydogan, C., Kutahya, C., Allushi, A., Yilmaz, G. & Yagci, Y. Block copolymer synthesis in one shot: concurrent metal-free ATRP and ROP processes under sunlight. Polym. Chem. 8, 2899–2903 (2017).
Broderick, E. M. et al. Redox control of a ring-opening polymerization catalyst. J. Am. Chem. Soc. 133, 9278–9281 (2011).
Biernesser, A. B., Li, B. & Byers, J. A. Redox-controlled polymerization of lactide catalyzed by bis(imino)pyridine iron bis(alkoxide) complexes. J. Am. Chem. Soc. 135, 16553–16560 (2013).
P’Pool, S. J. & Schanz, H. J. Reversible inhibition/activation of olefin metathesis: a kinetic investigation of ROMP and RCM reactions with Grubbs’ catalyst. J. Am. Chem. Soc. 129, 14200–14212 (2007).
Liu, B., Cui, D. M. & Tang, T. Stereo- and temporally controlled coordination polymerization triggered by alternating addition of a Lewis acid and base. Angew. Chem. Int Ed. 55, 11975–11978 (2016).
Poelma, J. E., Fors, B. P., Meyers, G. F., Kramer, J. W. & Hawker, C. J. Fabrication of complex three-dimensional polymer brush nanostructures through light-mediated living radical polymerization. Angew. Chem. Int Ed. 52, 6844–6848 (2013).
Aoshima, H., Uchiyama, M., Satoh, K. & Kamigaito, M. Interconvertible living radical and cationic polymerization through reversible activation of dormant species with dual activity. Angew. Chem. Int Ed. 53, 10932–10936 (2014).
Li, N. et al. Temperature programed photo-induced RAFT polymerization of stereo-block copolymers of poly(vinyl acetate). Polym. Chem.-Uk 8, 6024–6027 (2017).
Kameyama, A., Murakami, Y. & Nishikubo, T. Novel sequence-ordered polymers by transformation of polymer backbone: quantitative and regioselective insertion of thiiranes into poly(S-aryl thioester). Macromolecules 32, 1407–1412 (1999).
Nagai, A., Koike, N., Kudo, H. & Nishikubo, T. Controlled thioacyl group transfer (TAGT) polymerization of cyclic sulfide: novel approach to AB diblock copolymers by the combination of RAFT and TAGT polymerizations. Macromolecules 40, 8129–8131 (2007).
Kudo, H., Sato, K. & Nishikubo, T. Controlled insertion reaction of thiirane into carbamothioate: novel synthesis of well-defined polysulfide. Macromolecules 43, 9655–9659 (2010).
Shanmugam, S., Xu, J. T. & Boyer, C. Photocontrolled living polymerization systems with reversible deactivations through electron and energy transfer. Macromol. Rapid Comm. 38, 1700143 (2017).
Xu, J. T., Jung, K., Atme, A., Shanmugam, S. & Boyer, C. A robust and versatile photoinduced living polymerization of conjugated and unconjugated monomers and its oxygen tolerance. J. Am. Chem. Soc. 136, 5508–5519 (2014).
Shanmugam, S., Xu, J. T. & Boyer, C. Exploiting metalloporphyrins for selective living radical polymerization tunable over visible wavelengths. J. Am. Chem. Soc. 137, 9174–9185 (2015).
Shanmugam, S. & Boyer, C. Stereo-, temporal and chemical control through photoactivation of living radical polymerization: synthesis of block and gradient copolymers. J. Am. Chem. Soc. 137, 9988–9999 (2015).
Xu, J. T. et al. Synthesis of discrete oligomers by sequential PET-RAFT single-unit monomer insertion. Angew. Chem. Int Ed. 56, 8376–8383 (2017).
Xu, J. T., Shanmugam, S., Fu, C. K., Aguey-Zinsou, K. F. & Boyer, C. Selective photoactivation: from a single unit monomer insertion reaction to controlled polymer architectures. J. Am. Chem. Soc. 138, 3094–3106 (2016).
Shanmugam, S., Xu, J. T. & Boyer, C. Utilizing the electron transfer mechanism of chlorophyll a under light for controlled radical polymerization. Chem. Sci. 6, 1341–1349 (2015).
Corrigan, N., Shanmugam, S., Xu, J. T. & Boyer, C. Photocatalysis in organic and polymer synthesis. Chem. Soc. Rev. 45, 6165–6212 (2016).
Shanmugam, S. & Boyer, C. POLYMER SYNTHESIS Organic photocatalysts for cleaner polymer synthesis. Science 352, 1053–1054 (2016).
Bates, F. S. et al. Multiblock polymers: panacea or Pandora’s box? Science 336, 434–440 (2012).
Kim, J., Mok, M. M., Sandoval, R. W., Woo, D. J. & Torkelson, J. M. Uniquely broad glass transition temperatures of gradient copolymers relative to random and block copolymers containing repulsive comonomers. Macromolecules 39, 6152–6160 (2006).
Acknowledgements
We acknowledge funding support from the National Key R&D Program of China (2017YFA0205601), the National Natural Science Foundation of China (Grant Numbers 51625305, 21704095, 21774113, and 21525420) and the Foundamental Research Funds for the Central Universities (WK9110000004).
Author information
Authors and Affiliations
Contributions
Y.Z.Y. and C.Y.H. conceived the project and directed the experiment. Z.Z. conducted the polymerizations and polymer characterization, and L.X., T.Y.Z., D.C.W., and C.Y.H. performed the data analysis. Z.Z., C.Y.H., D.C.W., and Y.Z.Y. wrote the paper. All the authors discussed the results and contributed to the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, Z., Zeng, TY., Xia, L. et al. Synthesis of polymers with on-demand sequence structures via dually switchable and interconvertible polymerizations. Nat Commun 9, 2577 (2018). https://doi.org/10.1038/s41467-018-05000-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-05000-2