Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Evolution of thiolate-stabilized Ag nanoclusters from Ag-thiolate cluster intermediates


The synthesis of atomically precise thiolate-stabilized silver (Ag) nanoclusters is the subject of intense research interest, yet the formation mechanism of such nanoclusters remains obscure. Here, electrospray ionization mass spectrometry is successfully applied to monitor the reaction intermediates formed during the sodium-borohydride-reduction of silver 4-tert-butylbenzenethiolate (AgSPh-tBu). We demonstrate a unique evolution route to thiolate-stabilized Ag nanoclusters mediated by Ag-thiolate clusters. The Ag-thiolate clusters form in the initial stage of reduction contain tens of Ag atoms and similar number of ligands, and they are transformed into Ag17(SPh-tBu)123− and Ag44(SPh-tBu)304− nanoclusters in the later reduction process. The number of Ag atoms in the Ag-thiolate clusters determines the reaction path to each final nanocluster product. A similar mechanism is found when silver 2,4-dimethylbenzenethiolate (AgSPhMe2) is used as precursor. This mechanism differs markedly from the long-established bottom-up evolution process, providing valuable new insights into the synthesis of metal nanoclusters.


The synthesis of atomically precise metal nanoclusters has attracted tremendous research interest in recent years due to their unique physicochemical properties1,2,3,4 which lead to end applications in catalysis2,5,6, bioimaging7,8, sensors9,10, and many other areas. Amongst atomically precise metal nanoclusters, thiolate-stabilized gold (Au) and silver (Ag) nanoclusters have been the most widely investigated5,11,12,13,14,15,16. Although Au and Ag have similar atom radii and share a face-centered cubic (fcc) structure in crystalline materials, these metals have distinct differences in the types of thiolate-stabilized nanoclusters they form. For a single aliphatic thiol, atomically precise Au nanoclusters with a wide range of sizes can be synthesized, including Au1917, Au2018, Au2419, Au2520,21, Au3822,23, Au6824, and Au14425. In contrast, for thiolate-stabilized Ag nanoclusters there is a far more rigid relationship between thiolate ligands and nanocluster sizes26,27. For each aromatic thiol, generally only a single atomically precise Ag nanocluster is formed26,28,29,30.

The evolution process of thiolate-stabilized Au25 nanoclusters from Au-thiolate precursors was recently studied by Xie et al. and a stepwise bottom-up formation process involving Au(I)-SR monomers and oligomers was developed31. However, the formation mechanism of atomically precise thiolate-stabilized Ag nanoclusters from Ag-thiolate precursors is not known, motivating a detailed investigation.

Herein, we demonstrate the successful identification of intermediates in the evolution process of atomically precise thiolate-stabilized Ag nanoclusters by electrospray ionization mass spectrometry (ESI-MS), thereby allowing the establishment of a unique evolution mechanism. As shown in Fig. 1, instead of forming monomers or oligomers followed by bottom-up evolution process as reported for Au nanoclusters31, the reduction of the Ag-thiolate complex precursor, silver 4-tert-butylbenzene-thiolate (AgSPh-tBu), generates discrete Ag-thiolate clusters containing tens of Ag atoms and similar number of thiolate ligands (i.e., a similar Ag:thiolate composition to the Ag-thiolate precursor). It’s worth mentioning that the Ag-thiolate precursor can be regarded as Ag(I)-thiolate complex with an infinite chain length and takes the form of insoluble light yellow flakes30. In contrast, the intermediate clusters can be regarded as a Ag-thiolate complex with a finite chain length. The intermediate clusters are subsequently transformed to thiolate-stabilized Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304 nanoclusters through ligand dissociation and size focusing as the reduction proceeded. Further analysis of Ag atom numbers contained in the intermediate clusters reveals that the number of Ag atoms determines the reaction path to the final products. It should be mentioned that in a previous report, the bulky ligand SPh-tBu was found to stabilize only Ag17(SPh-tBu)123 rather than both Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304, as is reported in the present study28. Our findings indicate that the size (number of Ag atoms) in the intermediate Ag-thiolate clusters plays a critical role in the reaction routes to the different thiolate-stabilized nanoclusters with the same capping ligand.

Fig. 1

Schematic illustration of the evolution process. Thiolate-stabilized Ag nanoclusters were obtained through sodium-borohydride-reduction of AgSPh-tBu precursor. Discrete Ag-thiolate clusters were captured by ESI-MS as the key intermediates in the evolution process


Synthesis of Ag nanoclusters

In a typical reaction, 20 mg of AgNO3 (0.12 mmol) was dissolved in 10 mL of acetonitrile, and the resulting solution was added dropwise into a solution of 100 µL of HSPh-tBu (0.60 mmol) in 20 mL of acetonitrile under vigorous stirring. A light yellow AgSPh-tBu precipitate was formed immediately. The suspension was kept for several minutes before 10 mg of NaBH4 (0.26 mmol) powder was added into the reaction mixture under vigorous stirring. When the solution turned clear and colorless, 10 mL of methanol was added to promote the reduction by providing active hydrogen. Thiolate-stabilized Ag nanoclusters were obtained within 15 min at room temperature. UV–Vis absorption spectroscopy (Fig. 2b) identified characteristic absorption peaks of thiolate-stabilized Ag44 species14,27, while ESI-MS results confirmed the formation of two different stable products: Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304 (Fig. 2a and Supplementary Fig. 1).

Fig. 2

Characterizations of final products. a Negative-mode ESI-MS and b UV–Vis absorption spectrum of the final reaction product. Species with m/z larger than 4000 can also be assigned to Ag44(SPh-tBu)304− and its fragments. See Supplementary Fig. 1 for more detailed analysis

Capture of reaction intermediates by ESI-MS

Attention was subsequently focused on the evolution of thiolate-stabilized Ag nanoclusters during the reduction of the Ag-thiolate complexes. Preliminary attempts to identify the reaction intermediates under the original reaction conditions by ESI-MS were unsuccessful due to the high temperature in the ESI-MS instrument (source temperature: 40 °C, desolvation temperature: 120 °C), which caused the reaction to proceed to completion very quickly. Some small peaks for the intermediates could be detected (Supplementary Fig. 2), though it was impossible to systematically follow the evolution and disappearance of the intermediates due to the fast reaction kinetics. To suppress the reduction kinetics of the system, we replaced the methanol (10 mL) by 5 mL of methanol containing 2.5 mg of NaOH. In the reaction without NaOH, the pH of the reaction mixture was measured to be 9.3, while by adding NaOH, the solution pH was adjusted to above 14 (out of range of the pH meter). Under such new reaction conditions, the intermediates formed from the AgSPh-tBu precipitate could be successfully captured by ESI-MS and they showed perfect coincidence with the small peaks captured under the former reaction conditions (Supplementary Fig. 3). However, it is worth mentioning that the final products, Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304 were less stable under these new reaction conditions since their evolution was accompanied by slight etching, as evidenced by the appearance of some miscellaneous small peaks in Fig. 3g.

Fig. 3

Time-dependent ESI-MS spectra. The spectra show the evolution of atomically precise thiolate-stabilized Ag nanoclusters in the reaction solution. The rectangles highlight the evolution of the final products, Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304. The capture started as soon as the methanol was added and the reaction time in each panel was a 0 min, b 2 min, c 4 min, d 7 min, e 10 min, f 15 min and g 25 min

Analysis of ESI-MS spectra

The entire evolution process of the Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304 products is captured in the negative-mode ESI-MS spectra shown in Fig. 3. If the evolution of these products occurred by a stepwise bottom-up process (typical for Au nanoclusters)31, then lower molecular weight intermediates should be consumed with time. However, all low molecular weight species (m/z < 1000) identified in Fig. 3a, d can be assigned to inorganic ions, such as Na+ and NO3, in the reaction mixture (Supplementary Fig. 4). Instead, a series of peaks with a −3 charge and a characteristic Ag isotopic pattern was observed in the m/z 2000–5000 region. A straightforward relationship is apparent between these species and the two final products Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304. As the reaction proceeded, the signals for the two final products intensified whilst signals for the species formed early in the reaction were attenuated, leading to a conclusion that these species are key reaction intermediates. Ag17(SPh-tBu)123 and Ag44(SPh-tBu)304 were also found to evolve with different speeds, suggesting two separate routes to these products. As shown in Fig. 3, Ag17(SPh-tBu)123 (Fig. 3a, d) evolved more quickly than Ag44(SPh-tBu)304 (Fig. 3c, g). Accordingly, we were able to distinguish two sets of intermediates, one for each final product. Note that attempts were also made to detect positively charged or neutral intermediates during the reaction. Except for species associated with inorganic ions in the low molecular weight range, no obvious signals corresponding to reaction intermediates could be found (Supplementary Fig. 5).

The intermediate clusters leading to Ag17(SPh-tBu)123 have m/z 2000–2800 and become detectable almost immediately after the reaction initiated. Detailed analyses of peaks in Fig. 3a are shown in Supplementary Figs. 6-9. Selected peak positions and their assignments are listed in Supplementary Table 1. These intermediates, denoted here as intermediate Ag-thiolate clusters, have a general formula Ag n (SPh-tBu) n x , where 0 ≤ x ≤ 4. The number of Ag atoms in these intermediate clusters falls in the range of 22–34. They have a Ag:thiolate ratio similar to the Ag-thiolate complex precursor (Ag:thiolate = 1:1) and they are negatively charged due to the reduction by NaBH4. Intermediate Ag-thiolate clusters leading to the formation of Ag44(SPh-tBu)304 have m/z 2800–5000, and contain 35–57 Ag atoms (Fig. 3c, Supplementary Figs. 10, 11 and Supplementary Table 2). Thus, the number of Ag atoms in the intermediate Ag-thiolate clusters has a strong influence on the final products. In this case, Ag-thiolate clusters containing 22–34 Ag atoms will be transformed to Ag17(SPh-tBu)123, whilst those with 35–57 Ag atoms will lead to the formation of Ag44(SPh-tBu)304. The initially formed Ag-thiolate clusters with polydisperse size (different Ag atom number in clusters) will ‘size-focus’ to their corresponding stable atomically precise thiolate-stabilized Ag nanoclusters later in the reaction. This process is also accompanied by reduction of Ag(I) to Ag(0), which will enhance the metal–metal interaction between Ag atoms in the clusters and result in simultaneous thiolate ligand dissociation.

Evolution process of Ag nanoclusters

To allow better understanding of the transformation from the intermediate Ag-thiolate clusters to the final products (atomically precise thiolate-stabilized Ag nanoclusters), we defined the value M = nm+l to represent the degree of reduction of each intermediate Ag-thiolate cluster (also known as the valence electron count in nanoclusters)32, where n is the number of Ag atoms, m is the number of thiolate ligands and l is the number of units of negative charge on the cluster, respectively. As described in Supplementary Fig. 12, for the Ag-thiolate complex precursor (before the reducing agent was added), M = 0 (since n = m, l = 0). When the precursor was dissolved and transformed to the intermediate Ag-thiolate clusters, M increased due to the reduction. For the intermediate Ag-thiolate clusters, calculation of M was based on the general formula Ag n (SPh-tBu) n−x , where 0 ≤ x ≤ 4. M falls in the range of 3 to 7. At this stage of reaction, the intermediate Ag-thiolate clusters contained a large amount of Ag(I) ions and showed similar composition to the Ag-thiolate complex (intermediate Ag-thiolate clusters can be regarded as slightly reduced Ag-thiolate complex with a limited chain length, in which some of the Ag(I) were reduced to Ag(0) to give negatively charged clusters). Accordingly, we denote the intermediates as intermediate Ag-thiolate clusters. In a system with a strong reducing power (NaBH4 and methanol), the Ag-thiolate clusters with relatively small M were unstable and were further reduced to species with larger M, e.g., Ag17 (Ag17(SPh-tBu)123, M = 8) and Ag44 (Ag44(SPh-tBu)304, M = 18). Note that we could not identify any species with M in the range of 8 to 18. We hypothesized that the intermediate species with M larger than 8 were highly reactive, and they were transformed to Ag44(SPh-tBu)304 before they could be captured by ESI-MS. This can be rationalized by a shell closing phenomenon wherein clusters with M = 8, 18, 34, etc have higher stability than the others32.

TEM observation of intermediates

Transmission electron microscopy (TEM) was applied to monitor the intermediates at the very beginning of the reduction reaction. After addition of NaBH4 to the reaction mixture containing the AgSPh-tBu precipitate, the yellow turbid solution turned clear and colorless. A sample was taken and subjected to TEM analysis. Figure 4 shows a representative TEM image of the sample, revealing nanoparticles with a mean size of 1.24 ± 0.18 nm. Ag44, the main product in our reaction system, has been reported to have a core diameter of ~1.2 nm14,27,32. The perfect coincidence in size lends supports to the earlier conclusion from the ESI-MS data that the discrete nanoparticles formed in this stage (i.e., intermediate Ag-thiolate clusters) are the intermediates in the formation of Ag17(SPh-tBu)123− and Ag44(SPh-tBu)304−.

Fig. 4

Particle size of intermediates. TEM image of the intermediates obtained after NaBH4 addition to the reaction mixture, when the mixture became clear and colorless. Scale bar: 20 nm. The overlaid inset shows a particle size histogram and the corresponding Gaussian fit

Control experiment through a bottom-up process

The final products of this reaction, Ag17(SPh-tBu)123− and Ag44(SPh-tBu)304−, were not particularly stable, as evidenced by the color fading of the reaction mixture (to colorless) over several hours if the solution was kept in air at room temperature under constant stirring (please refer to Supplementary Note 1 for more details concerning the stability of Ag44 and Ag17). ESI-MS showed that the colorless species in solution were Ag-thiolate monomers and oligomers, amongst which Ag(SPh-tBu)2 and Ag5(SPh-tBu)6 had the highest abundance (Supplementary Fig. 13). This mixture of Ag-thiolate monomers and oligomers served as a perfect precursor to investigate the possibility of synthesizing Ag17(SPh-tBu)123− and Ag44(SPh-tBu)304− via a bottom-up process simply by adding a small amount of NaBH4 to induce a reduction reaction. However, upon addition of 10 mg of NaBH4 to the colorless mixture, none of the absorption features of thiolate-stabilized Ag nanoclusters were observed. Instead, a broad peak corresponding to the localized surface plasmon resonance (SPR) of large Ag nanoparticles (typically with particle size above 3 nm) was observed (Supplementary Fig. 14a). This data were further verified by TEM measurements, where irregular Ag nanospheres of particle size larger than 3 nm were clearly seen in the representative TEM images (Supplementary Fig. 14b). This experiment demonstrates conclusively that it is not possible to obtain thiolate-stabilized Ag nanoclusters such as Ag17(SPh-tBu)123− and Ag44(SPh-tBu)304− via a bottom-up process under the experimental conditions used in this study.

Experiments using 2,4-dimethylbenzenethiol (HSPhMe2)

To test the validity of the aforementioned Ag nanocluster evolution process, an analogous set of experiments were performed using a different thiolate ligand, HSPhMe2. HSPhMe2 has been reported to stabilize Ag25 nanoclusters, thus it was of interest to see if nanoclusters of this particular size could be formed through Ag-thiolate cluster intermediates26. ESI-MS experiments showed that at the early stage of the reaction, the intermediate Ag-thiolate clusters were formed (detected by a series of products with −3 charge), which in turn served as key intermediates during the evolution process of thiolate-stabilized Ag nanoclusters (Supplementary Figs. 15, 16). Multiple thiolate-stabilized Ag nanoclusters were detected as products (Supplementary Fig. 17). Interestingly, the main final products were Ag26(SPhMe2)192− and Ag44(SPhMe2)304−, but no signals corresponding to Ag25(SPhMe2)18 were detected26. The two products Ag26(SPhMe2)192−and Ag44(SPhMe2)304− evolved simultaneously, thus it was difficult to identify the intermediate Ag-thiolate clusters leading to each product. However, the overall evolution of the Ag26(SPhMe2)192− and Ag44(SPhMe2)304− products was similar to that presented in Fig. 2 for Ag17(SPh-tBu)123− and Ag44(SPh-tBu)304−, which provides a sufficient evidence to suggest a similar evolution process. Ag17 nanoclusters were also detected during the evolution process of Ag26(SPhMe2)192− and Ag44(SPhMe2)304−, and they were disappeared as the reaction proceeded (Supplementary Figs. 15 and 18). Considering the different ESI-MS fragment patterns of Ag44 capped by SPhMe2 (Supplementary Fig. 17c and 17d) and Ag44 capped by SPh-tBu (Fig. 2a and Supplementary Fig. 1), we conclude that Ag17 and Ag44 were formed in the presence of each thiolate capping ligand, though their stabilities differ. Furthermore, some capping ligands can generate unique thiolate-stabilized Ag nanoclusters, such as Ag26(SPhMe2)192−.


Previous studies have shown atomically precise Ag44 nanoclusters are inert and do not “seed” the synthesis of larger thiolate-stabilized Ag nanoclusters, whereas Au25 nanoclusters could seed larger nanoclusters when the analogous reaction was performed14. Our results offer a highly plausible explanation for the non-seeding properties of Ag nanoclusters, since the evolution of Ag44 nanoclusters is based on a process from discrete Ag-thiolate cluster intermediates, a pathway that prevents the growth of larger nanoclusters. Conversely, Au25 nanoclusters are formed through a stepwise bottom-up process31, providing the distinct possibility for Au25 to react with other Au-thiolate monomers to create larger nanoclusters.

Recently, thiolate-stabilized Ag nanoparticles containing 136 and 374 Ag atoms have been successfully synthesized33, demonstrating potential for the synthesis of larger thiolate-stabilized Ag nanoclusters. Results of this study demonstrate that the final size of the Ag nanoclusters is determined by the size of intermediate Ag-thiolate clusters. Accordingly, if larger intermediate Ag-thiolate clusters could be generated during the reaction, then it should be possible to obtain larger Ag nanoclusters at the end of the reaction. However, all the Ag-thiolate clusters we detected by ESI-MS contained less than 60 Ag atoms. Structure of the AgSPh-tBu complex precursor (the initial yellow precipitate obtained before NaBH4 addition) may help to understand this limitation. As shown in Supplementary Fig. 19, the AgSPh-tBu complex consisted of particles with size of only 1–2 nm, very similar to that of the intermediate Ag-thiolate clusters (Fig. 4). These data suggest that the size of the assembled particles in the AgSPh-tBu precursor complex may directly relate to the number of Ag numbers in the intermediate Ag-thiolate clusters.

To summarize, we demonstrate that the synthesis of atomically precise thiolate-stabilized Ag nanoclusters by chemical reduction of Ag-thiolate complex precursors proceeds via an evolution process involving Ag-thiolate cluster intermediates. These intermediate clusters contain tens of Ag atoms and a similar number of thiolate ligands, and they were transformed to Ag nanoclusters of well-defined size through thiolate dissociation and size-focusing as the reduction reaction proceeds. Furthermore, the number of Ag atoms in the intermediate Ag-thiolate clusters determines the reaction pathway and final size of the thiolate-stabilized Ag nanoclusters. Our findings significantly advance the understanding of the formation mechanism of atomically precise Ag nanoclusters, and hint at efficient routes towards Ag nanoclusters of different (e.g., larger) sizes.



4-tert-butylbenzenethiol (HSPh-tBu) and 2,4-dimethylbenzenethiol (HSPhMe2) were purchased from Aladdin Chemistry Co. Ltd. Sodium borohydride (NaBH4, 99.99%, metal basis) was purchased from Sigma-Aldrich. Methanol, acetonitrile, and NaOH were obtained from local suppliers and used without further purification.

Synthesis of thiolate-stabilized Ag nanoclusters

In a typical reaction, 20 mg of AgNO3 (0.12 mmol) was dissolved in 10 mL of acetonitrile, and the resulting solution was added dropwise into a solution of 100 µL of HSPh-tBu (0.60 mmol) in 20 mL of acetonitrile under vigorous stirring. A light yellow AgSPh-tBu precipitate was formed. 10 mg of NaBH4 (0.26 mmol) powder was added into the reaction mixture under vigorous stirring, and the stirring continued for several minutes. When the solution turned clear and colorless, 10 mL of methanol was added to promote the reduction. Thiolate-stabilized Ag nanoclusters were obtained within 15 min at room temperature.

Capture of intermediate species

In the above synthesis, the 10 mL methanol was replaced with 5 mL of methanol solution containing 2.5 mg of NaOH. All other conditions were unchanged.

UV–visible absorption spectroscopy

Solution-phase absorption spectra were recorded using standard 1 cm path length quartz cuvettes on a Hitachi UV-3900 spectrophotometer.

Transmission electron microscope (TEM)

TEM images were obtained using a JEOL-2100F microscope operating at an accelerating voltage of 200 kV. Samples were dispersed on hydrophilic carbon films for analysis.

Electrospray ionization mass spectrometry (ESI-MS)

All mass spectrometry data were collected on a Xevo G2-S quadrupole time-of-flight mass spectrometer (Waters, Milford, USA) equipped with an ESI source and operated in both positive and negative ionization mode. Instrumental parameters were as follows: capillary voltage: 2.5 kV, sample cone voltage: 15 V, extraction cone voltage: 3.0 V, collision energy: 0 eV, cone gas flow rate: 30 L/h, desolvation gas flow rate: 800 L/h, source temperature: 40 °C, and desolvation temperature: 120 °C. The scan range was from 50 to 7000 Da. Data acquisition, handling, and instrument control were performed by using UNIFI.

Data availability

All relevant data are available from the corresponding author on request.


  1. 1.

    Jin, R. Atomically precise metal nanoclusters: stable sizes and optical properties. Nanoscale 7, 1549–1565 (2015).

    ADS  Article  PubMed  CAS  Google Scholar 

  2. 2.

    Ott, L. S. & Finke, R. G. Transition-metal nanocluster stabilization for catalysis: a critical review of ranking methods and putative stabilizers. Coord. Chem. Rev. 251, 1075–1100 (2007).

    Article  CAS  Google Scholar 

  3. 3.

    Guo, S. & Wang, E. Noble metal nanomaterials: controllable synthesis and application in fuel cells and analytical sensors. Nano Today 6, 240–264 (2011).

    Article  CAS  Google Scholar 

  4. 4.

    Jin, R., Zeng, C., Zhou, M. & Chen, Y. Atomically precise colloidal metal nanoclusters and nanoparticles: fundamentals and opportunities. Chem. Rev. 116, 10346–10413 (2016).

    Article  PubMed  CAS  Google Scholar 

  5. 5.

    Li, G. & Jin, R. Atomically precise gold nanoclusters as new model catalysts. Acc. Chem. Res. 46, 1749–1758 (2013).

    Article  PubMed  CAS  Google Scholar 

  6. 6.

    Fang, J. et al. Recent advances in the synthesis and catalytic applications of ligand-protected, atomically precise metal nanoclusters. Coord. Chem. Rev. 322, 1–29 (2016).

    Article  CAS  Google Scholar 

  7. 7.

    Zhang, L. & Wang, E. Metal nanoclusters: New fluorescent probes for sensors and bioimaging. Nano Today 9, 132–157 (2014).

    ADS  Article  CAS  Google Scholar 

  8. 8.

    Liu, C.-L. et al. Insulin-directed synthesis of fluorescent gold nanoclusters: preservation of insulin bioactivity and versatility in cell imaging. Angew. Chem. Int. Ed. 50, 7056–7060 (2011).

    Article  CAS  Google Scholar 

  9. 9.

    Lin, C.-A. J. et al. Synthesis of fluorescent metallic nanoclusters toward biomedical application: recent progress and present challenges. J. Med. Biol. Eng. 29, 276–283 (2009).

    CAS  Google Scholar 

  10. 10.

    Luo, Z., Zheng, K. & Xie, J. Engineering ultrasmall water-soluble gold and silver nanoclusters for biomedical applications. Chem. Commun. 50, 5143–5155 (2014).

    Article  CAS  Google Scholar 

  11. 11.

    Qian, H., Zhu, M., Wu, Z. & Jin, R. Quantum sized gold nanoclusters with atomic precision. Acc. Chem. Res. 45, 1470–1479 (2012).

    Article  PubMed  CAS  Google Scholar 

  12. 12.

    Joshi, C. P., Bootharaju, M. S. & Bakr, O. M. Tuning properties in silver clusters. J. Phys. Chem. Lett. 6, 3023–3035 (2015).

    Article  PubMed  CAS  Google Scholar 

  13. 13.

    Tsukuda, T. Toward an atomic-level understanding of size-specific properties of protected and stabilized gold clusters. Bull. Chem. Soc. Jpn. 85, 151–168 (2012).

    Article  CAS  Google Scholar 

  14. 14.

    Desireddy, A. et al. Ultrastable silver nanoparticles. Nature 501, 399–402 (2013).

    ADS  Article  PubMed  CAS  Google Scholar 

  15. 15.

    Yang, H. et al. All-thiol-stabilized Ag44 and Au12Ag32 nanoparticles with single-crystal structures. Nat. Commun. 4, 2422 (2013).

    Article  PubMed  Google Scholar 

  16. 16.

    Jadzinsky, P. D., Calero, G., Ackerson, C. J., Bushnell, D. A. & Kornberg, R. D. Structure of a thiol monolayer-protected gold nanoparticle at 1.1 A resolution. Science 318, 430–433 (2007).

    ADS  Article  PubMed  CAS  Google Scholar 

  17. 17.

    Wu, Z., MacDonald, M. A., Chen, J., Zhang, P. & Jin, R. Kinetic control and thermodynamic selection in the synthesis of atomically precise gold nanoclusters. J. Am. Chem. Soc. 133, 9670–9673 (2011).

    Article  PubMed  CAS  Google Scholar 

  18. 18.

    Zhu, M., Qian, H. & Jin, R. Thiolate-protected Au20 clusters with a large energy gap of 2.1 eV. J. Am. Chem. Soc. 131, 7220–7221 (2009).

    Article  PubMed  CAS  Google Scholar 

  19. 19.

    Zhu, M., Qian, H. & Jin, R. Thiolate-protected Au24(SC2H4Ph)20 nanoclusters: superatoms or not? J. Phys. Chem. Lett. 1, 1003–1007 (2010).

    Article  CAS  Google Scholar 

  20. 20.

    Akola, J., Walter, M., Whetten, R. L., Haekkinen, H. & Groenbeck, H. On the structure of thiolate-protected Au25. J. Am. Chem. Soc. 130, 3756–3757 (2008).

    Article  PubMed  CAS  Google Scholar 

  21. 21.

    Zhu, M., Aikens, C. M., Hollander, F. J., Schatz, G. C. & Jin, R. Correlating the crystal structure of a thiol-protected Au25 cluster and optical properties. J. Am. Chem. Soc. 130, 5883–5884 (2008).

    Article  PubMed  CAS  Google Scholar 

  22. 22.

    Donkers, R. L., Lee, D. & Murray, R. W. Synthesis and isolation of the molecule-like cluster Au38(PhCH2CH2S)24. Langmuir 20, 1945–1952 (2004).

    Article  CAS  Google Scholar 

  23. 23.

    Qian, H., Eckenhoff, W. T., Zhu, Y., Pintauer, T. & Jin, R. Total structure determination of thiolate-protected Au38 nanoparticles. J. Am. Chem. Soc. 132, 8280–8281 (2010).

    Article  PubMed  CAS  Google Scholar 

  24. 24.

    Dass, A. Mass spectrometric identification of Au68(SR)34 molecular gold nanoclusters with 34-electron shell closing. J. Am. Chem. Soc. 131, 11666–11667 (2009).

    Article  PubMed  CAS  Google Scholar 

  25. 25.

    Qian, H. & Jin, R. Controlling nanoparticles with atomic precision: the case of Au144(SCH2CH2Ph)60. Nano Lett. 9, 4083–4087 (2009).

    ADS  Article  PubMed  CAS  Google Scholar 

  26. 26.

    Joshi, C. P., Bootharaju, M. S., Alhilaly, M. J. & Bakr, O. M. [Ag25(SR)18]: The “Golden” Silver Nanoparticle. J. Am. Chem. Soc. 137, 11578–11581 (2015).

    Article  PubMed  CAS  Google Scholar 

  27. 27.

    Bakr, O. M. et al. Silver nanoparticles with broad multiband linear optical absorption. Angew. Chem. Int. Ed. 48, 5921–5926 (2009).

    Article  CAS  Google Scholar 

  28. 28.

    Wickramasinghe, S. et al. M3Ag17(SPh)12nanoparticles and their structure prediction. J. Am. Chem. Soc. 137, 11550–11553 (2015).

    Article  PubMed  CAS  Google Scholar 

  29. 29.

    Yan, J. et al. Total structure and electronic structure analysis of doped thiolated silver [MAg24(SR)18]2- (M=Pd, Pt) clusters. J. Am. Chem. Soc. 137, 11880–11883 (2015).

    Article  PubMed  CAS  Google Scholar 

  30. 30.

    AbdulHalim, L. G. et al. Ag29(BDT)12(TPP)4: a tetravalent nanocluster. J. Am. Chem. Soc. 137, 11970–11975 (2015).

    Article  PubMed  CAS  Google Scholar 

  31. 31.

    Luo, Z. et al. Toward understanding the growth mechanism: tracing all stable intermediate species from reduction of Au(I)-thiolate complexes to evolution of Au25 nanoclusters. J. Am. Chem. Soc. 136, 10577–10580 (2014).

    Article  PubMed  CAS  Google Scholar 

  32. 32.

    Harkness, K. M. et al. Ag44(SR)30 4-: a silver-thiolate superatom complex. Nanoscale 4, 4269–4274 (2012).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  33. 33.

    Yang, H. et al. Plasmonic twinned silver nanoparticles with molecular precision. Nat. Commun. 7, 12809 (2016).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

Download references


T.Z. is grateful for financial support from the National Key Projects for Fundamental Research and Development of China (2017YFA0206904, 2017YFA0206900, 2016YFB0600901), the Ministry of Science and Technology of China (2014CB239402), the National Natural Science Foundation of China (51772305, 51572270, U1662118), the Strategic Priority Research Program of the Chinese Academy of Sciences (XDB17000000), the Royal Society-Newton Advanced Fellowship (NA170422), the International Partnership Program of Chinese Academy of Sciences (GJHZ1819), the Young Elite Scientist Sponsorship Program by CAST (YESS), and the Youth Innovation Promotion Association of the CAS.

Author information




T.Z. and Y.C. conceived the idea and design the experiments. T.Z. supervised the project. Y.C. carried out the experiments and characterizations. Y.C., J.P., and Z.D. performed the ESI-MS tests. Y.C., G.I.N.W., and T.Z. wrote the manuscript. J.G., R.S., Q.Y., L.W., C.T., and J.X. discussed the results and commented on the manuscript.

Corresponding author

Correspondence to Tierui Zhang.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Cao, Y., Guo, J., Shi, R. et al. Evolution of thiolate-stabilized Ag nanoclusters from Ag-thiolate cluster intermediates. Nat Commun 9, 2379 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing