The liquid and glass states of metal–organic frameworks (MOFs) have recently become of interest due to the potential for liquid-phase separations and ion transport, alongside the fundamental nature of the latter as a new, fourth category of melt-quenched glass. Here we show that the MOF liquid state can be blended with another MOF component, resulting in a domain structured MOF glass with a single, tailorable glass transition. Intra-domain connectivity and short range order is confirmed by nuclear magnetic resonance spectroscopy and pair distribution function measurements. The interfacial binding between MOF domains in the glass state is evidenced by electron tomography, and the relationship between domain size and Tg investigated. Nanoindentation experiments are also performed to place this new class of MOF materials into context with organic blends and inorganic alloys.
Metal–organic frameworks (MOFs), or networked structures of inorganic nodes connected by organic ligands, are flexible materials1,2 that can be broadly separated into two classes according to their porosity. Those that contain high internal surface areas are of intense interest for gas separations and catalysis3,4,5,6, while dense MOF materials are investigated for their potential in other applications, e.g., conduction and magnetism7,8,9.
The zeolitic imidazolate framework (ZIF) family of MOFs contains structures of tetrahedral Mn+ nodes, (M = e.g., Zn, Co, Li, B, Ni, Mg) linked through the N atoms of imidazolate ligands10,11,12. Several members, e.g. ZIF-4-Zn, have been observed to possess accessible melting temperatures (Tm) between 400 and 600 °C13. The melting process proceeds via a dissociation–association mechanism of Zn-N coordination bonding and associated ligand switching between Zn2+ centres14. This becomes sub-nanosecond at Tm, in a manner analogous to the switching between hydrogen bonds in liquid water.
Such liquid states will be of particular intrigue in the development of alternatives to solid-state compounds for industrial-scale gas sorption and separations, due to the better handling and ease of installation compared to their classical solid-state counterparts15. Additionally, the intrinsic instabilities of microcrystalline MOF structures often preclude processing into the physical forms and bodies required by industry16,17. Solution casting techniques combine the processability of organic polymers with selective MOF additives18, though drop-casting, fibre drawing or melt spinning of single-component MOF liquid states would circumvent chemical compatibility concerns.
Cooling of (strongly associated) MOF liquids from above Tm results in a family of melt-quenched glasses chemically different from the inorganic, organic and metallic glass categories known at present. Accordingly, the formation of the liquid and glass phases of MOFs has recently emerged as a new area in an ever-expanding field13,14,19,20,21,22. The reactivity of these ‘MOF liquids’ has not yet been studied. Possibilities also exist in the production of novel MOF glasses, given the potential to incorporate multiple, designed chemical functionalities within a single glass, or in the creation of hybrid equivalents of alloys, blends and ceramics. Progress in the preparation of crystalline materials containing multiple inorganic or/and organic functionalities within a single framework structure has already been made23,24. These multivariate MOFs25,26 arise from the interaction of several chemical components during solvothermal or mechanochemical synthesis, though not in the liquid state.
Here we are interested in how a MOF liquid behaves when combined with a secondary MOF component and the fundamental possibilities that this may afford in new materials' discovery. Specifically, we hypothesize that this may result in the formation of a glass containing interlocking MOF domains. Motivated by the concept of forming this type of material, which we term ‘MOF blends’, we investigated the high temperature reactions within mixtures of ZIF-4 [M(Im)2] and ZIF-62 [Zn(Im)1.75(bIm)0.25] (M = Co2+, Zn2+, Im: C3H3N2−, bIm: C7H5N2−). Previously, it has been observed that, upon heating, both ZIF-4-Zn and ZIF-4-Co undergo a transition to a high-density amorphous phase and a dense crystal on heating to 300 °C and 450 °C, respectively. The zinc framework melts at 550 °C, unlike the dense cobalt crystal, which remains intact until thermal decomposition at ca. 570 °C. ZIF-62 remains in the room temperature crystalline state until liquid formation at 410 °C13,27.
Differential scanning calorimetry
Samples of ZIF-4-Zn and ZIF-62 were synthesized and evacuated according to previously reported solvothermal procedures (Fig. 1a)27,28,29. A physical mixture of the two frameworks in equal weight portions, hereby referred to as (ZIF-4-Zn)(ZIF-62)(50/50), was prepared by ball-milling to ensure sample homogeneity (see Methods). Differential scanning calorimetric (DSC) experiments were then performed up to 590 °C in an argon atmosphere, beyond which thermal decomposition of the liquid state occurred. The first endothermic feature at 225 °C is coincident with a mass loss of ca. 9% and ascribed to desolvation. As expected, two endothermic features belonging to the respective melting points of ZIF-62 and ZIF-4-Zn (445 °C and 580 °C, respectively) were noted, identical to those recorded from pure samples (Fig. 1b)13. The melting enthalpy of ZIF-62 was recorded as ca. 3 kJ mol−1. Quenching after isothermal treatment for 2 min at 590 °C yielded a glassy, amorphous product (Supplementary Figure 1).
Re-heating of this amorphous sample revealed a single glass transition, glass transition temperature (Tg) = 306 °C (Fig. 1b, blue solid line), whereas two separate features at 292 °C (ZIF-4-Zn) and 318 °C (ZIF-62) would have been anticipated13. A physical mixture of the two glasses formed separately yielded the expected two Tgs (Supplementary Figures 2 and 3). Such a markedly different, single value is indicative of liquid phase mixing, as is also the case in e.g. metallic glasses30, inorganic oxides and phosphates31, or miscible polymer blending in organics32. We name the blend produced (ZIF-4-Zn)0.5(ZIF-62)0.5. The ability to tailor Tg was explored through analysis of a further set of (ZIF-4-Zn)1−x(ZIF-62)x mixtures. The results from DSC experiments on the glasses formed upon quenching the liquids from 590 °C (Supplementary Figure 4) show a composition-dependent shift in Tg (Fig. 1c). The increase in Tg with increasing ZIF-62 content follows a linear relation, analogous to the trends observed in binary organic mixtures exhibiting mass additivity behaviour (∆Tg = 0) e.g. poly(1,3-trimethylene adipate) and poly(vinyl methyl ether)32.
In order to facilitate the use of electron microscopy as a characterization technique for the blended glass, a physical mixture of ZIF-4-Co and ZIF-62, hereby referred to as (ZIF-4-Co)(ZIF-62)(50/50), was analysed. A pure sample of ZIF-4-Co was synthesized by following prior literature33. As expected27, it possesses a stable amorphous region from 325 to 500 °C (Supplementary Figure 5), before the expected recrystallization to a dense ZIF at ca. 510 °C. No melting above this temperature is observed. DSC experiments on (ZIF-4-Co)(ZIF-62)(50/50) confirmed these transitions, along with the expected Tm of ZIF-62 (Fig. 1d). Quenching of the sample from 425 °C, i.e. a region containing amorphous ZIF-4-Co and liquid ZIF-62, yielded a glass (Supplementary Figure 6). A subsequent DSC of the quenched glass again demonstrated a single Tg, at ca. 300 °C (Supplementary Figure 7), despite the fact that it was formed from an interaction between an amorphous solid and a liquid. A second measurement using a slower heating rate again yielded only one Tg (Supplementary Figure 1). Differences between (ZIF-4-Co)0.5(ZIF-62)0.5 and (ZIF-4-Zn)0.5(ZIF-62)0.5 are perhaps expected to be small, given the very high viscosities for both ZIF-4-Zn and ZIF-62 reported previously14,34.
Small-angle X-ray scattering (SAXS) has previously been used to reveal information on the pore surface and characteristics of MOF-535, HKUST-136 and monitor particle evolution and growth in situ37,38. Combined with wide-angle X-ray scattering (WAXS), it provides a powerful tool that has also been used to study the collapse of some MOFs to amorphous states21.
The temperature-resolved WAXS profile of ZIF-62 (Fig. 2a) shows consistent Bragg diffraction from the sample, which reduces in intensity and then disappears at ca. 340 °C upon gradual formation of the liquid state. Decomposition of this MOF liquid is then evidenced at ca. 550 °C by the emergence of several Bragg features at relatively large q values. The temperature-resolved WAXS profile of (ZIF-4-Co)0.5(ZIF-62)0.5 (Fig. 2b) contains a region in which amorphous ZIF-4-Co and the ZIF-62 liquid are co-existent, between ca. 340 °C and ca. 400 °C. Recrystallization of amorphous ZIF-4-Co to a dense phase is then observed. These observations are broadly consistent with the DSC results presented in Fig. 1, though these differ because of the dissimilar temperature–time profiles of the two experiments.
The decay in SAXS signal at room temperature was extracted from the three-dimensional, variable temperature plot of the SAXS intensity ISAXS for ZIF-62 and follows power law behaviour of the form q−α, where α = 3.9 (Supplementary Figure 9). At ca. 440 °C, a decrease to α = 3.4 is observed, consistent with the formation of rougher internal surfaces upon melting. Computation of the volume-weighted fraction of the particles (Supplementary Figure 9) shows an initial expansion in particle radii from 5 nm at the point of melting, which is consistent with interfacial particle coalescence. The radii then drop drastically and the volume fraction tends to zero, as homogeneous melting of the sample occurs. The increase in particle size at ca. 460 °C then marks the onset of gradual thermal decomposition.
The variable temperature plot of the SAXS intensity ISAXS for (ZIF-4-Co)(ZIF-62)(50/50) (Fig. 2c) was also fitted and displays a lower initial value of α = 3.66, consistent with the presence of different internal pore structures and particle sizes within the ball-milled mixture of MOFs. This value increases to 4 on heating to 340 oC when ZIF-4-Co amorphizes, before decreasing to 3.1 due to both recrystallization of ZIF-4-Co and melting of ZIF-62. The volume-weighted fraction of the particles also reveals that the distribution of particle scatterers is much broader in the initial instance, consistent with the inhomogeneity in sample composition. Like ZIF-62, the particles disappear rapidly upon liquid formation at 340 °C. The broad distribution of particles that starts to appear at ca. 450 °C is ascribed to the known formation of crystallites of a dense ZIF from ZIF-4-Co at these higher temperatures (Fig. 2d).
Liquid-state 1H nuclear magnetic resonance (NMR) was carried out by digesting samples of (ZIF-4-Co)(ZIF-62)(50/50) and (ZIF-4-Co)0.5(ZIF-62)0.5 (produced by quenching from 445 °C) in a mixture of deuterium chloride (DCl; 35%)/deuterium oxide (D2O; 100 µL) and DMSO-d6 (500 µL) (Supplementary Figure 10). Resonances in both spectra are fairly broad, arising from the substantial paramagnetic broadening induced by the presence of Co2+, predominantly in an octahedral complex coordinated by either H2O or dimethyl sulphoxide (DMSO)39 giving the metal centre a likely electronic arrangement of t2g5eg2 and three unpaired electrons40. This prevents the integration of most of the aromatic signals of the imidazolate ligands. Both NCHNIm and NCHNbIm peaks are, however, well resolved in the 9–9.7 ppm high-field region and are used to determine the Im:bIm ligand concentration ratios; values of 1:0.076 ± 0.010 and 1:0.054 ± 0.015 are obtained for (ZIF-4-Co)(ZIF-62)(50/50) and (ZIF-4-Co)0.5(ZIF-62)0.5, respectively (Supplementary Figure 10). Within error, these values are both in agreement with the expected 1:0.066 stoichiometric ratio. Additionally, in the glass sample, a second resolved peak of the bIm ligand (CHCNbIm) can be integrated relative to NCHN in Im, giving a 1:0.12 ± 0.01 ratio (expected integration from stoichiometry is 1:0.13), confirming that any loss of ligand in the amorphization process is negligible and/or below the detection limit of NMR. The absence of impurity peaks in the 7–9 ppm region indicates minimal decomposition of imidazolates during digestion/amorphization.
The chemical structure of the blend was probed through synchrotron neutron and X-ray total scattering. Whereas the X-ray structure factor S(Q) of (ZIF-4-Co)(ZIF-62)(50/50) contained Bragg diffraction, that of (ZIF-4-Co)0.5(ZIF-62)0.5, as expected, did not. This rules out small regions of crystallinity in the latter (Fig. 3a). After appropriate data corrections (see Methods section), the data were converted to the corresponding pair distribution functions (PDFs) (Fig. 3b), which are weighted histograms of the atom pair distances present in both samples. Interatomic distances at 1.3, 2, 3, 4 and 6 Å were common between both crystal and blend samples, consistent with previous conclusions on near-identical short-range order between crystal and glass ZIFs14.
Above this distance, oscillations at high r were present from the crystalline mixture (ZIF-4-Co)(ZIF-62)(50/50), though the PDF of (ZIF-4-Co)0.5(ZIF-62)0.5 was relatively featureless. A dual-phase refinement in PDFGUI41 of the PDF for (ZIF-4-Co)(ZIF-62)(50/50) was performed in the range 1–15 Å, confirming the presence of both crystalline phases (Fig. 3b inset). Neutron total scattering was also carried out on a deuterated sample of (ZIF-4-Co)0.5(ZIF-62)0.5 (Supplementary Figures 11 and 12). The expected C-D peak below 1 Å was not visible in the PDF, due to the sample containing a higher hydrogen content than expected. Above this distance and below 6 Å, the PDF was similar to those previously reported for deuterated Zn(Im)2 polymorphs42.
To probe the evolution in domain structure or size upon heating, synchrotron X-ray diffraction data were collected on a sample of (ZIF-4-Co)0.5(ZIF-62)0.5 heated from room temperature to 460 °C (Fig. 3c). The first sharp diffraction peak in the S(Q) varied little in intensity or position. While the second and third peaks also remained approximately invariant on heating, some ‘flattening’ of features at high Q values occurred upon heating above 300 °C. This temperature corresponds to the Tg of (ZIF-4-Co)0.5(ZIF-62)0.5, and the flattening is consistent with formation of a more liquid-like state. The peak in the D(r) at r = 1.3 Å, which only contains contributions from C-C and C-N pairs and no contributions from pairs involving Co or Zn, remained constant in intensity and position (Fig. 3d). Those peaks arising mainly from M-N1 (‘B’~2 Å), M-C (‘C’~3 Å), M-N2 (‘D’~4 Å) and M-M (‘E’~6 Å) correlations, however, were observed to undergo a reduction in intensity upon heating. The intensity recovered upon cooling back to ambient temperature, showing that no permanent change in short-range order had taken place.
To investigate the suitability of transmission electron microscopy as a characterization technique for MOF glasses, pure samples of crystalline ZIF-62, (ZIF-4-Co)(ZIF-62)(50/50) and (ZIF-4-Co)0.5(ZIF-62)0.5 were investigated by electron energy loss spectroscopy (EELS, Fig. 4a, Supplementary Figures 13 and 14). The K (1s) ionization edges for C and N atoms exhibited high-intensity π* peak features, which are a signature of conjugated heterocycles and consistent with the π* signature previously reported for EELS of molecular imidazole43. These observations demonstrated that the ligands were not damaged under the selected electron beam conditions used. A sample of (ZIF-4-Co)0.5(ZIF-62)0.5 was subsequently investigated using annular dark field (ADF) scanning transmission electron microscopy (STEM) exhibiting thickness and atomic number contrast and EELS and X-ray energy dispersive spectroscopy (EDS) for chemical mapping at similar or lower electron beam exposures.
EELS performed on a single shard of the glass (Fig. 4a) clearly showed the presence of Co and Zn (Fig. 4b) along with an interfacial region. EDS was performed to yield more insight into the domain structure and interfacial bonding present in the glass particles too thick for EELS analysis (Fig. 4b, c). These revealed a more extended network exhibiting relatively sharp interfaces between Co and Zn domains. Domain sizes were observed ranging from 200 nm to >1 µm in width. This is markedly different to (ZIF-4-Co)(ZIF-62)(50/50), where separate particles of each framework, without domain mixing, were located (Supplementary Figure 15). In STEM analyses, the electron probe is transmitted through the sample, resulting in EELS and EDS signals that arise from the entire volume through the three-dimensional sample. As a result, these two-dimensional analyses alone were not sufficient to fully characterize the interfaces between the lamellar domains of Co and Zn MOFs. Two-dimensional interface regions with mixed signal composition are not distinguishable from single-phase compositional domains overlapping along the electron beam direction.
EDS tomography was performed in order to address this uncertainty and to characterize the sharpness of the interface between the Co- and Zn-containing regions (Fig. 5). A single-piece shard of (ZIF-4-Co)0.5(ZIF-62)0.5 was located that contained two large domains of predominantly Co and Zn, respectively. At the interface, there were two regions (labelled 1 and 2 in Fig. 5) characteristic of heterogeneous mixing between the Co and Zn phases and exhibiting a similar interlocked microstructure as those observed in Fig. 4b, c. Inspection of the tomographic reconstruction volumes at these features revealed that, at feature 1, the Co protrusion is present in a region with negligible Zn content. At feature 2, both Co and Zn were found in the same three-dimensional region, suggesting some minor homogeneous mixing. While some regions of the three-dimensional interface exhibited micro-scale mixing of Co and Zn, the majority were segregated into single-metal domains within an interlocked network microstructure.
Nanoindentation has previously been used to probe the Young’s moduli, E, of crystalline and amorphous MOFs44, though it often results in significant differences between the identified values and those gained from computational studies. The Young’s moduli provides a descriptor of the stiffness of a structure under strain and is highly dependent on the molecular structure. Nanoindentation experiments were thus performed on two independent samples of (ZIF-4-Co)0.5(ZIF-62)0.5. The existence of both constituent phases in a single glass monolith, in domain sizes smaller than the indenter tip, was confirmed by the consistency across measurements of E. Average values of E (7.5 ± 0.5 GPa and 7.1 ± 0.4 GPa, Fig. 6a) were recorded from the load–displacement data (Fig. 6b) of indentations on polished glass monoliths (Fig. 6a inset) between 100 nm and 500 nm. These values lie roughly intermediate between the upper bound of that expected for organic polymers and the lower bound for inorganic glasses (Fig. 6c).
The blend is of comparable pycnometric density to single-phase samples of aZIF-4-Co and the ZIF-62 glass13,27, though it exhibits less compliant behaviour under the indenter tip. The increase in E relative to the pure samples (aZIF-4-Co, E = 6.6 GPa and ZIF-62 glass, E = 6.1 GPa) is ascribed to the isothermal treatment of 2 min above Tm, which is necessary for blend formation. This is similar to the increase in E from quenching a ZIF-62 liquid from Tm (E = 6.6 GPa) and 572 °C (E = 8.8 GPa)13. It should also be noted that the relatively poor agreement between calculated and experimental values of E for MOFs has been ascribed to various factors including the large surface effects from small single crystals or monoliths, structural defects and macroscale sample cracking45. The prior values of E reported for aZIF-4-Co were gained from non-coalesced single-crystal samples, and the extent of defects in all three systems has not been the subject of investigation.
We have demonstrated that the two MOF liquids derived from ZIF-4-Zn and ZIF-62 can be blended or alloyed together. The resultant melt-quenched glass shows a single Tg, the position of which can be controlled according to the sample composition. The resultant glass structure was probed through electron microscopic measurements on a glass derived from ZIF-4-Co and ZIF-62, finding heterogeneous domain formation. Binding between the domains was investigated using electron tomography, showing regions of homogeneous Co and Zn concentration—indicative of liquid–liquid reactivity. The absence of complete homogeneous mixing is in this instance ascribed to the high viscosity of both molten phases. The interfacial binding of the separate MOF domains to one another is entirely consistent with the observed mechanism of MOF melting, which proceeds via imidazolate dissociation from a M2+ centre, and subsequent association of a different imidazolate ligand. We therefore ascribe the domain interlocking mechanism to ligand ‘swapping’ between the liquid MOF phase and amorphous solid, resulting in the heterometallic MOF glasses shown14. Similar heterogeneous structures are also found in SiO2-Al2O3 glasses, where SiO2-rich domains are embedded within Al2O3-rich phases46.
The relationship between domain size and Tg was investigated through the synthesis of two further (ZIF-4-Co)(ZIF-62)(50/50) samples with both larger and smaller initial particle sizes. The first sample was formed through light grinding of ZIF-62 and ZIF-4-Co in a mortar and pestle and compared to a second sample, where the two crystalline frameworks were ball-milled for 20 min together (as opposed to the 5 min used initially). EDS experiments provided qualitative support for the differences in domain sizes of each component using these three different methods of sample preparation (Supplementary Figure 15). Furthermore, DSC experiments confirmed that the sample formed through light grinding contained two distinct Tgs (Supplementary Figures 16 and 17), while that formed by ball-milling for a longer time (Supplementary Figure 18) possesses only one, in a near identical position to the original blend sample (ca. 300 °C).
The binary MOF blend formed and characterized here belongs to the compatible polymer blend category, due to the chemically compatible interactions between the two components and the observation of a single glass transition47. A mixture of two chemically incompatible MOF liquids would therefore be expected give rise to an immiscible blend with two or more Tgs. The results will prove important in understanding the possibilities afforded by the glass and liquid states of MOFs, demonstrating that blended materials containing two or more MOFs can be produced. We have also shown that the reactivity of the liquid MOF state may be utilized in binding to other MOF components and that the Tg of MOF glasses may be tailored according to blend composition.
All crystalline samples studied here crystallize in the Pbca space group, with cell volumes of 4342 Å3, 4280 Å3 and 4466 Å3 for ZIF-4-Zn, ZIF-4-Co and ZIF-62, respectively. The preparation of mixed samples was done in 0.5 g quantities. For example, for a 50/50 ratio mixture, 0.25 g of each MOF was placed in a 10 ml stainless steel jar, along with 2 × 7 mm diameter stainless steel balls. The mixture was then milled for 5 min (or, to produce a finer particle size for one control sample, for 20 min) in a Retsch MM400 grinder mill operating at 25 Hz. Powder X-ray diffraction patterns of both ball-milled mixtures are shown in Supplementary Information, demonstrating the lack of amorphization.
Differential scanning calorimetry
DSC characterizations were conducted using a Netzsch STA 449 F1 instrument in platinum crucibles at a 10 °C min−1 heating rate. The simultaneous DSC–thermogravimetric analysis in Supplementary Figure 5 was performed using a TA instruments Q-600 series differential scanning calorimeter, with the sample (~7 mg) held on an aluminium pan under a continuous flow of dry Ar gas. The data were obtained using a heating rate of 10 °C min−1. Tgs were determined by the method described elsewhere48.
X-ray powder diffraction
Data were collected with a Bruker-AXS D8 diffractometer using Cu Kα (λ = 1.540598 Å) radiation and a LynxEye position sensitive detector in Bragg–Brentano parafocussing geometry.
Combined SAXS and WAXS
X-ray data were collected at the I22 beamline at the Diamond Light Source, UK (λ = 0.9998 Å, 12.401 keV). The SAXS detector was positioned at a distance of 9.23634 m from the sample as calibrated using a 100 nm period Si3N4 grating (Silson, UK), giving a usable Q range of 0.0018–0.18 Å−1. The WAXS detector was positioned at a distance of 0.16474 m from the sample as calibrated using a standard CeO2 sample (NIST SRM 674b, Gaithersburg, USA), giving a usable Q range of 0.17–4.9 Å−1. Samples were loaded into 1.5 mm diameter borosilicate capillaries under argon inside a glovebox and sealed with Blu-tac and Para-film to prevent the ingress of air. Samples were heated using a Linkam THMS600 capillary stage (Linkam Scientific, UK) from room temperature to 600 °C at 10 °C min−1. Simultaneous SAXS/WAXS data were collected every 1 °C. Data were reduced to one dimensional using the DAWN package49,50 and standard reduction pipelines51. Values for the power law behaviour of the samples were found using the power law model of SASView 4.1.152. Data were fitted over the range 0.003 ≤ q ≤ 0.005 Å−1. Particle size distributions were calculated using the McSAS package53,54, a minimal assumption Monte Carlo method for extracting size distributions from small-angle scattering data. Data were fitted over the range 0.002 ≤ q ≤ 0.18 Å−1 with a sphere model.
NMR samples were prepared by digesting ~8 mg of sample in 100 μL of 35 wt% DCl in D2O (purchased from Sigma Aldrich, 99% deuterated) then dissolved in 500 μL of DMSO-d6 (purchased from Sigma Aldrich, 99.9% deuterated). All 1H NMR spectra were recorded on a Bruker Avance III 400 MHz spectrometer.
Total scattering measurements
X-ray data were collected at the I15-1 beamline at the Diamond Light Source, UK (λ = 0.161669 Å, 76.7 keV). A sample of (ZIF-4-Co)(ZIF-62)(50/50), and a small amount of the (ZIF-4-Co)0.5(ZIF-62)0.5 sample used in the neutron total scattering experiment were loaded into borosilicate glass capillaries of 1.17 mm (inner) diameter. Data on the samples, empty instrument and capillary were collected in the region of ∼0.4 < Q <~ 26 Å−1. Corrections for background, multiple scattering, container scattering, Compton scattering and absorption were performed using the GudrunX program55,56. Variable temperature measurements were performed using an identical set-up, though the capillaries were sealed with araldite. Data were taken upon heating at 25 °C, 100 °C, 200 °C, 280 °C and then in 10 °C steps to 340 °C. Further data were collected in 20 °C intervals to 460 °C, before cooling and a final data set taken at room temperature. Data were corrected using equivalent measurements taken from an empty capillary heated to identical temperatures. Published structures for ZIF-4-Co and ZIF-62 were used to refine data in PDFGUI10,33. The values U11, U22 and U33 were set to 0.003 Å2 and constrained to be isotropic. Cross-diagonal terms were set to 0, and data beyond 15 Å were not fitted because of the lack of intensity. The final Rw value was 0.34, due to some disordering in the initial mixture introduced by ball-milling.
Deuterated samples of ZIF-4-Co and ZIF-62 were prepared by equimolar replacement of the hydrogenated benzimidazole and imidazole in their respective syntheses, by the deuterated equivalents, supplied by the ISIS Deuteration Facility. A glass sample of (ZIF-4-Co)0.5(ZIF-62)0.5 was then produced as reported in the manuscript. Data were measured at room temperature using the NIMROD diffractometer at ISIS57. A sample was placed into an 8-mm diameter thin-walled vanadium can, and data from an empty vanadium can, empty instrument, 8 mm V-5.14% Nb rod was used to correct the data in the Gudrun software55.
Pycnometric measurements were carried out using a Micromeritics Accupyc 1340 helium pycnometer. The typical mass used was 200 mg; the values quoted are the mean and standard deviation from a cycle of 10 measurements.
Electron microscopy and spectroscopy
STEM data were acquired using an FEI Osiris microscope equipped with a high-brightness X-FEG electron source and operated at 80 kV. The beam convergence was set to 11.0 mrad. EELS was acquired using a post-column Gatan Enfinium spectrometer. A 2.5 mm entrance aperture was selected, defining a collection semiangle of 19.4 mrad. Spectra were acquired in dual EELS mode: electrons undergoing no inelastic scattering (the zero loss peak) and those undergoing low energy losses were recorded with a fast acquisition time (0.0001 s) and nearly simultaneously electrons undergoing inelastic scattering at element-specific core loss ionization edges were recorded at longer exposures times (100 ms exposure at C and N K edges and 500 ms at Co and Zn L23 edges). Probe currents in this electron optical configuration were typically <150 pA. X-ray EDS was acquired using a ‘Super-X’ EDS detector system with four detectors mounted symmetrically about the optic axis of the microscope (200 ms per pixel). For all spectroscopic data, images were also simultaneously recorded on ADF detectors. These images contain atomic number and thickness contrast, giving structural information in parallel with the chemical mapping obtained in the EELS and EDS data. For EDS tilt-series tomography, EDS spectrum images were acquired from −70° to 70° in 10° increments.
Data were processed using Hyperspy58, an open-source software coded in Python. For EELS data, the spectra were first aligned to the ZLP, initially by shifting the maximum intensity channel to zero followed by cross-correlation-based sub-pixel alignment. Spikes due to X-rays striking the charge-coupled device detector were removed using a routine that automatically identified outlying high-intensity pixels and performed interpolation in the spectral region after removal of the spike. Independent component analysis was likewise performed in Hyperspy. For tilt-series tomography, Zn and Co chemical maps were initially combined for alignment of the tilt-series image-stack. In order to correct for detector shadowing as a function of tilt angle, the chemical maps were re-normalized to maintain constant integrated intensities at all tilts. This procedure was based on the constant total quantity of Zn and Co in the particle recorded within the field of view at all tilt angles. The combined Zn and Co image-stack was aligned using Scikit-Image, an open-source image processing software coded in Python, first using cross-correlation, and then the tilt axis was subsequently aligned by applying shifts and rotations to minimize artefacts in back projection reconstructions. The alignments were then applied to each of the Zn and Co tilt series. A compressed sensing reconstruction algorithm coded in MATLAB (Mathworks) was then used to perform the final independent reconstructions of the Zn and Co tilt series. Broadly, compressed sensing tomography approaches make use of prior knowledge of the sparsity of the signal undergoing reconstruction in a particular transform domain (the sparsity is given as the number of non-zero intensities) in order to recover high-fidelity tomographic reconstructions from highly undersampled tilt-series data59,60. This compressed sensing tomography implementation used three-dimensional total generalized variation61 regularization for the sparsity constraint in conjunction with a real-space projection operator from the Astra toolbox62 and using the primal-dual hybrid gradient method63 to solve the reconstruction problem. Reconstructions were further processed in ImageJ and FEI Avizo software for visualization. The total particle shape recovered in the tomographic reconstruction was used to threshold the volume to remove spurious signals due to noise in the reconstruction volume outside the particle sub-volume. No further processing was applied to the intensities within the particle.
The Young’s modulus (E) of the samples was measured using an MTS Nanoindenter XP at ambient conditions. Samples were mounted in an epoxy resin and polished using increasingly fine diamond suspensions. Indentation experiments were performed under the dynamic displacement controlled mode, at a constant strain rate of 0.05 s−1. All tests were conducted using a three-sided pyramidal (Berkovich) diamond indenter tip, to a maximum surface penetration depth of 500 nm. The load–displacement data collected were analysed using the Oliver and Pharr method64. A Poisson’s ratio of 0.2 was used, in accordance with prior studies on ZIF materials65.
The data that support the findings of this study are available from the corresponding author upon request.
Carrington, E. J. et al. Solvent-switchable continuous-breathing behaviour in a diamondoid metal–organic framework and its influence on CO2 versus CH4 selectivity. Nat. Chem. 9, 882–889 (2017).
Schneemann, A. et al. Flexible metal-organic frameworks. Chem. Soc. Rev. 43, 6062–6096 (2014).
Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, 974–986 (2013).
Banerjee, D. et al. Metal-organic framework with optimally selective xenon adsorption and separation. Nat. Commun. 7, 11831 (2016).
Mason, J. A. et al. Methane storage in flexible metal-organic frameworks with intrinsic thermal management. Nature 527, 357–361 (2015).
Yoon, J. W. et al. Selective nitrogen capture by porous hybrid materials containing accessible transition metal ion sites. Nat. Mater. 16, 526–531 (2017).
Tominaka, S. et al. Topochemical conversion of a dense metal-organic framework from a crystalline insulator to an amorphous semiconductor. Chem. Sci. 6, 1465–1473 (2015).
Lorusso, G. et al. A dense metal-organic framework for enhanced magnetic refrigeration. Adv. Mater. 25, 4653–4656 (2013).
Sun, L., Campbell, M. G. & Dinca, M. Electrically conductive porous metal-organic frameworks. Angew. Chem. Int. Ed. Engl. 55, 3566–3579 (2016).
Banerjee, R. et al. High-throughput synthesis of zeolitic imidazolate frameworks and application to CO2 capture. Science 319, 939–943 (2008).
Zhang, J. P., Zhang, Y. B., Lin, J. B. & Chen, X. M. Metal azolate frameworks: from crystal engineering to functional materials. Chem. Rev. 112, 1001–1033 (2012).
Horike, S., Kadota, K., Itakura, T., Inukai, M. & Kitagawa, S. Synthesis of magnesium ZIF-8 from Mg(BH(4))(2). Dalton. Trans. 44, 15107–15110 (2015).
Bennett, T. D. et al. Melt-quenched glasses of metal-organic frameworks. J. Am. Chem. Soc. 138, 3484–3492 (2016).
Gaillac, R. et al. Liquid metal-organic frameworks. Nat. Mater. 16, 1149–1154 (2017).
Giri, N. et al. Liquids with permanent porosity. Nature 527, 216–220 (2015).
Chen, Y. et al. Shaping of metal–organic frameworks: from fluid to shaped bodies and robust foams. J. Am. Chem. Soc. 138, 10810–10813 (2016).
Sumida, K. et al. Sol–gel processing of metal–organic frameworks. Chem. Mater. 29, 2626–2645 (2017).
Seoane, B. et al. Metal-organic framework based mixed matrix membranes: a solution for highly efficient CO2 capture? Chem. Soc. Rev. 44, 2421–2454 (2015).
Umeyama, D., Horike, S., Inukai, M., Itakura, T. & Kitagawa, S. Reversible solid-to-liquid phase transition of coordination polymer crystals. J. Am. Chem. Soc. 137, 864–870 (2015).
Chen, W. Q. et al. Glass formation of a coordination polymer crystal for enhanced proton conductivity and material flexibility. Angew. Chem. Int. Ed. Engl. 55, 5195–5200 (2016).
Bennett, T. D. et al. Hybrid glasses from strong and fragile metal-organic framework liquids. Nat. Commun. 6, 8079 (2015).
Zhao, Y., Lee, S.-Y., Becknell, N., Yaghi, O. M. & Angell, C. A. Nanoporous transparent MOF glasses with accessible internal surface. J. Am. Chem. Soc. 138, 10818–10821 (2016).
Fukushima, T. et al. Solid solutions of soft porous coordination polymers: fine-tuning of gas adsorption properties. Angew. Chem. Int. Ed. Engl. 49, 4820–4824 (2010).
Panda, T. et al. Mechanical alloying of metal-organic frameworks. Angew. Chem. Int. Ed. Engl. 56, 2413–2417 (2017).
Cadman, L. K. et al. Compositional control of pore geometry in multivariate metal-organic frameworks: an experimental and computational study. Dalton Trans. 45, 4316–4326 (2016).
Zhang, Y. B. et al. Introduction of functionality, selection of topology, and enhancement of gas adsorption in multivariate metal organic framework-177. J. Am. Chem. Soc. 137, 2641–2650 (2015).
Bennett, T. D. et al. Thermal amorphization of zeolitic imidazolate frameworks. Angew. Chem. Int. Ed. Engl. 50, 3067–3071 (2011).
Wharmby, M. T. et al. Extreme flexibility in a zeolitic imidazolate framework: porous to dense phase transition in desolvated ZIF-4. Angew. Chem. Int. Ed. Engl. 54, 6447–6451 (2015).
Gustafsson, M. & Zou, X. D. Crystal formation and size control of zeolitic imidazolate frameworks with mixed imidazolate linkers. J. Porous Mater. 20, 55–63 (2013).
Mattern, N. et al. Structural behavior of CuxZr100-x metallic glass (x=35-70). J. Non Cryst. Solids 354, 1054–1060 (2008).
Fulchiron, R., Belyamani, I., Otaigbe, J. U. & Bounor-Legare, V. A simple method for tuning the glass transition process in inorganic phosphate glasses. Sci. Rep. 5, 8369 (2015).
Kalogeras, I. M. & Brostow, W. Glass transition temperatures in binary polymer blends. J. Polym. Sci. Pol. Phys. 47, 80–95 (2009).
Tian, Y. Q. et al. Two polymorphs of cobalt(II) imidazolate polymers synthesized solvothermally by using one organic template N,N-dimethylacetamide. Inorg. Chem. 43, 4631–4635 (2004).
Qiao, A. et al. A metal-organic framework with ultrahigh glass-forming ability. Sci. Adv. 4, eaao6827 (2018).
Tsao, C. S. et al. Characterization of pore structure in metal-organic framework by small-angle X-ray scattering. J. Am. Chem. Soc. 129, 15997–16004 (2007).
Klimakow, M., Klobes, P., Thünemann, A. F., Rademann, K. & Emmerling, F. Mechanochemical synthesis of metal-organic frameworks: a fast and facile approach toward quantitative yields and high specific surface areas. Chem. Mater. 22, 5216–5221 (2010).
Cravillon, J. et al. Fast nucleation and growth of ZIF-8 nanocrystals monitored by time-resolved in situ small-angle and wide-angle X-ray scattering. Angew. Chem. Int. Ed. Engl. 50, 8067–8071 (2011).
Goesten, M. G. et al. Small-angle X-ray scattering documents the growth of metal-organic frameworks. Catal. Today 205, 120–127 (2013).
Magnell, K. R. & Reynolds, W. L. Complexes of cobalt(II) with chloride and thiocyanate ions in dimethyl sulfoxide. Inorg. Chim. Acta 6, 571–574 (1972).
Housecroft, C. E. & Sharpe, A. G. Inorganic Chemistry 3rd edn (Pearson Education Limited, UK, 2008).
Farrow, C. L. et al. PDFfit2 and PDFgui: computer programs for studying nanostructure in crystals. J. Phys. Condens. Matter 19, 335219 (2007).
Bennett, T. D. et al. Structure and properties of an amorphous metal-organic framework. Phys. Rev. Lett. 104, 115503 (2010).
Apen, E., Hitchcock, A. P. & Gland, J. L. Experimental studies of the core excitation of imidazole, 4,5-dicyanoimidazole, and S-triazine. J. Phys. Chem. 97, 6859–6866 (1993).
Tan, J. C. & Cheetham, A. K. Mechanical properties of hybrid inorganic-organic framework materials: establishing fundamental structure-property relationships. Chem. Soc. Rev. 40, 1059–1080 (2011).
Hobday, C. L. et al. A computational and experimental approach linking disorder, high-pressure behavior, and mechanical properties in UiO frameworks. Angew. Chem. Int. Ed. Engl. 55, 2401–2405 (2016).
Zhang, Y. F., Hu, L. N., Liu, S. J., Zhu, C. F. & Yue, Y. Z. Sub-T-g enthalpy relaxation in an extremely unstable oxide glass and its implication for structural heterogeneity. J. Non Cryst. Solids 381, 23–28 (2013).
Alemán, J. V. et al. Definitions of terms relating to the structure and processing of sols, gels, networks, and inorganic-organic hybrid materials (IUPAC Recommendations 2007). Pure Appl. Chem. 79, 1801–1829 (2007).
Yue, Y. Z. Characteristic temperatures of enthalpy relaxation in glass. J. Non Cryst. Solids 354, 1112–1118 (2008).
Basham, M. et al. Data Analysis WorkbeNch (DAWN). J. Synchrotron Radiat. 22, 853–858 (2015).
Filik, J. et al. Processing two-dimensional X-ray diffraction and small-angle scattering data in DAWN 2. J. Appl. Crystallogr. 50, 959–966 (2017).
Pauw, B. R., Smith, A. J., Snow, T., Terrill, N. J. & Thünemann, A. F. The modular small-angle X-ray scattering data correction sequence. J. Appl. Crystallogr. 50, 1800–1811 (2017).
SasView v4.1 (The SasView Project, 2017).
Pauw, B. R., Pedersen, J. S., Tardif, S., Takata, M. & Iversen, B. B. Improvements and considerations for size distribution retrieval from small-angle scattering data by Monte Carlo methods. J. Appl. Crystallogr. 46, 365–371 (2013).
Bressler, I., Pauw, B. R. & Thünemann, A. F. McSAS: software for the retrieval of model parameter distributions from scattering patterns. J. Appl. Crystallogr. 48, 962–969 (2015).
Soper, A. K. GudrunN and GudrunX: Programs for Correcting Raw Neutron and X-Ray Diffraction Data to Differential Scattering Cross Section. Technical Report RAL-TR-2011-2013 (Rutherford Appleton Laboratory, Didcot, UK, 2011).
Soper, A. K. & Barney, E. R. Extracting the pair distribution function from white-beam X-ray total scattering data. J. Appl. Crystallogr. 44, 714–726 (2011).
Bowron, D. T. et al. NIMROD: the Near and InterMediate Range Order Diffractometer of the ISIS second target station. Rev. Sci. Instrum. 81, 033905 (2010).
de la Peña, F. et al. hyperspy: HyperSpy v.1.0.1 (2016).
Saghi, Z. et al. Three-dimensional morphology of iron oxide nanoparticles with reactive concave surfaces. a compressed sensing-electron tomography (CS-ET) approach. Nano Lett. 11, 4666–4673 (2011).
Leary, R., Saghi, Z., Midgley, P. A. & Holland, D. J. Compressed sensing electron tomography. Ultramicroscopy 131, 70–91 (2013).
Bredies, K., Kunisch, K. & Pock, T. Total generalized variation. Siam J. Imaging Sci. 3, 492–526 (2010).
van Aarle, W. et al. The ASTRA toolbox: a platform for advanced algorithm development in electron tomography. Ultramicroscopy 157, 35–47 (2015).
Chambolle, A. & Pock, T. A first-order primal-dual algorithm for convex problems with applications to imaging. J. Math. Imaging Vis. 40, 120–145 (2011).
Oliver, W. C. & Pharr, G. M. Measurement of hardness and elastic modulus by instrumented indentation: advances in understanding and refinements to methodology. J. Mater. Res. 19, 3–20 (2004).
Tan, J. C., Bennett, T. D. & Cheetham, A. K. Chemical structure, network topology, and porosity effects on the mechanical properties of Zeolitic Imidazolate Frameworks. Proc. Natl. Acad. Sci. USA 107, 9938–9943 (2010).
T.D.B. would like to thank the Royal Society for a University Research Fellowship, and L.L. and N.J.B. acknowledge EPSRC studentships. C.W.A. acknowledges the Royal Society for funding. C.Z. acknowledges the financial support from China Scholarship Council and the Elite Research Travel Scholarship from the Danish Ministry of Higher Education and Science. We acknowledge the provision of synchrotron access to beamlines I15-1 (EE171151) and I22 (NT18236-1) at the Diamond Light Source, Rutherford Appleton Laboratory UK. The authors thank Jiayan Zhang for assistance for a DSC measurement. This work benefited from the use of the SasView application, originally developed under NSF Award DMR-0520547. SasView also contains code developed with funding from the EU Horizon 2020 programme under the SINE2020 project Grant No. 654000. Experiments at the ISIS Pulsed Neutron and Muon Source (on the NIMROD instrument) were supported by a beam-time allocation from the Science and Technology Facilities Council, on proposal RB1720006. S.M.C. acknowledges the Henslow Research Fellowship and Girton College, Cambridge. S.M.C. and P.A.M. acknowledge funding from the European Research Council under the European Union’s Seventh Framework Program (No. FP7/2007-2013)/ERC Grant Agreement No. 291522-3DIMAGE. C.-B.S. acknowledges support from the Leverhulme Trust project Breaking the non-convexity barrier, EPSRC grant EP/M00483X/1, EPSRC centre EP/N014588/1 and from CHiPS (Horizon 2020 RISE project grant). R.T. acknowledges funding from EPSRC grant EP/L016516/1 for the Cambridge Centre for Analysis. R.T. and C.-B.S. also acknowledge the Cantab Capital Institute for the Mathematics of Information.
The authors declare no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Longley, L., Collins, S.M., Zhou, C. et al. Liquid phase blending of metal-organic frameworks. Nat Commun 9, 2135 (2018). https://doi.org/10.1038/s41467-018-04553-6
This article is cited by
Molecule-based nonlinear optical switch with highly tunable on-off temperature using a dual solid solution approach
Nature Communications (2020)
Metal-organic framework crystal-glass composites
Nature Communications (2019)
Metal-organic framework glasses with permanent accessible porosity
Nature Communications (2018)