Stepwise control of host–guest interaction using a coordination polymer gel

Abstract

Precise control of host–guest interaction as seen in biological processes is difficult to achieve with artificial systems. Herein we have exploited the thermodynamic benefits of a system in equilibrium to achieve controlled stepwise release and capture of cyclodextrin (guest) using a coordination polymer (Mg-CP) as the host and temperature as the stimulus. Since temperature is not a precision stimulus for artificial host–guest interaction, the present system is a distinct prototype that manifests temperature-controlled natural host–guest interaction. The described coordination polymeric host system, when incorporated into a hydrogel matrix, provides a microenvironment that facilitates the stepwise release of α-CD in response to temperature variation within a quasi-solid state. The work demonstrated here may pave the way towards thermally controlled delivery and monitoring of otherwise spectroscopically silent molecules such as cyclodextrins.

Introduction

Ever since the postulation of the lock and key concept by Emil Fischer in 18941, a myriad of studies have been reported in the area of host–guest interactions, aiming at understanding the mechanism behind enzymatic action in biological systems. Most of the enzymatic processes such as synthesis of peptides, degradation of various metabolites, synthesis and hydrolysis of adenosine triphosphate, etc. proceed in a stepwise fashion and with absolute control2. Several of these natural systems are precisely controlled by external or internal stimuli; however, designing such artificial stimuli-responsive systems remains a challenging task3. Owing to its instant delivery at a specific location and control via different wavelengths and intensities, light is arguably the most attractive physical stimulus for artificial systems4,5,6,7. However, although heat is not considered as a stimulus with precisional control3,8, natural host–guest processes are mainly controlled by heat. Since equilibrium constants of host–guest interactions are constant at a particular temperature, change of temperature of a system at chemical equilibrium may change the equilibrium constant, followed by the shifting of the equilibrium towards a direction to undo the change according to Le Châtelier’s principle9. Temperature can therefore take advantage of the thermodynamic benefits of host–guest equilibrium10,11 and be exploited to demonstrate the formation (capture) or dissociation (release) of a host–guest complex in a stepwise manner. An ideal host system with multiple guests that facilitates temperature-controlled stepwise release–capture process is shown in Fig. 112,13,14,15. This strategy may further help us in developing thermoresponsive smart materials16,17, for example, a drug delivery system similar to the concept of magic bullet propounded by Ehrlich18, which can be programmed for drug delivery as well as drug re-uptake or clearance from the blood stream essential for tackling issues like drug resistance and side-effects.

Fig. 1
figure1

Temperature-controlled host–guest systems. Schematic representation of an ideal temperature controlled formation and dissociation of multiple guests (cyclodextrins) from a host (coordination polymer) in a stepwise manner

Cyclodextrins (CDs) are known to be an excellent host for the host–guest interaction with hydrophobic guest molecules19. CDs have therefore been widely exploited as hydrophobic drug-delivery vehicles as well as in the design of functional supramolecular polymers20,21. Recently, CDs have also been recognized as potent drug molecules for treating fatal neurodegenerative disorders like Niemann–Pick type C and as anti-obesity dietary fibres for flushing out fat from high cholesterol diets22,23. However, a suitable delivery system for easy, detectable and controlled stepwise release of CDs in solution as well as in soft solid-state devices is yet to be realized. This is because, unlike other organic molecules, CDs are optically transparent and their release and binding profiles cannot be identified using common spectroscopic techniques such as absorption or fluorescence. Nevertheless, by virtue of their inherent chirality, CDs offer the possibility to follow their binding-release isotherms via induced circular dichroism (ICD) spectroscopy24,25. For this purpose, a light absorbing moiety possessing accessible binding motifs is required. In this regard, several hydrophobic organic molecules such as azobenzene, adamantane, bipyridine, etc. have been used that bind with CDs21. If such moieties can be organized over a one-dimensional (1-D) coordination polymer (CP) (Fig. 1), the system may reversely accept and release CDs in solution upon application of an appropriate stimulus. While CDs are known to be the host in almost all cases, reports on their use as guest are rare26. Therefore, the present system is a rare example where CDs behave as the guest in a host–guest molecular interaction.

According to a report by Yaghi and co-workers, MOF-74-based structure, composed of a chiral infinite rod-shaped magnesium or zinc oxide cluster and dioxidoterephthalate-based organic linkers, forms a non-interpenetrated framework27. The ligand has a carboxylic acid motif with an ortho-positioned hydroxy group, as in salicylic acid. The observed structure can probably be restricted along the crystallographic b axis, if the organic strut contains the metal-binding functionalities on one end. Such a design leads to a polymer brush-like structure, with the organic linkers organized along the infinite metal oxide chain as reported in the case of infinite CPs of calcium, manganese, cadmium, zirconium, lanthanides, etc.28. With this idea in mind, we prepared an organic ligand (AzSA) with a hydrophobic azobenzene core and a metal-binding salicylic acid moiety.

Herein we have designed a CP-based host, with azobenzene side appendages, which exhibits temperature responsive host–guest interaction with CDs not only in the solution state but also in the quasi-solid (hydrogel) state. Using the aforesaid system, we have been able to demonstrate a stepwise release and capture profile of CD guests from the CP backbone.

Results

Synthesis and characterization of host polymer

The magnesium-based CP, Mg-CP was synthesized via solvothermal reaction of azobenzene salicylic acid, AzSA, with Mg(NO3)2•6H2O in high boiling solvent such as N,N-diethylformamide (DEF) (Fig. 2a) and characterized using various spectroscopic and analytical techniques (Fig. 2 and Supplementary Fig. 1). Coordination of the carboxylic acid and hydroxyl groups in AzSA to the MgO-based inorganic cluster was confirmed by the absence of the free O-H stretching band (2500–3300 cm−1) in its Fourier transform infrared (FT-IR) spectrum (Fig. 2b). The unsymmetric nature of the bidentate bridging mode of coordination with additional bridging was corroborated by the difference between asymmetric and symmetric stretching frequencies of the carbonyl group that increased from 217 cm−1 in AzSA to 223 cm−1 in Mg-CP (Fig. 2c)29. Thermogravimetric analysis confirmed the superior thermal stability of Mg-CP over the ligand AzSA. The thermal decomposition of the 1-D CP was found to start around 300 °C, whereas the ligand (AzSA) starts to decompose around 200 °C. Moreover, a residual weight (42%) equivalent to the amount of Mg-O present in Mg-CP remained even >700 °C (Fig. 2d). The phenolic –OH proton, which is otherwise exchangeable in CD3OD can be visualized in the 1H NMR spectrum of AzSA due to strong intramolecular hydrogen bonding. The absence of the phenolic–OH peak in the 1H nuclear magnetic resonance (NMR) spectrum of Mg-CP confirmed the coordination of the ligand with Mg2+. Broadening of the peaks in the aromatic region and the presence of coordinated DEF solvent molecules were also evident from the 1H NMR spectrum of Mg-CP (Fig. 2e). No changes were observed in the ultraviolet (UV)–visible absorption spectrum of Mg-CP even on prolonged 365 nm UV irradiation (Supplementary Fig. 2). There can be two potential reasons behind this observation; first, the coordination of an azobenzene ligand in a CP or a MOF backbone may lead to the loss of its photoisomerization properties30,31,32. Second, owing to the presence of an electron-donating hydroxy group at the para position to the azobenzene functionality, the system may undergo very fast cistrans reverse isomerization33.

Fig. 2
figure2

Synthesis and characterization of Mg-CP. a Reagents and conditions for the synthesis of the coordination polymer Mg-CP from organic ligand AzSA. Schematic representation of coordination modes in Mg-CP. Blue and magenta represent magnesium and oxygen atoms, respectively. b FT-IR spectra of AzSA and Mg-CP showing changes in the region corresponding to O-H stretching and the asymmetric and symmetric stretching frequencies of the carbonyl bond. c Expanded portion of the region (1750–1400 cm−1), showing the differences in the asymmetric and symmetric stretching bands of the carbonyl bond. d TGA of Mg-CP and AzSA. e 1H NMR spectra of Mg-CP (blue) and AzSA (red) (500 MHz, CD3OD)

The Mg-CP when prepared from DEF resulted in the formation of a CP gel (Fig. 3). The critical gelation concentration was found to be 4 mg mL−1 (Fig. 3a; for details, see Supplementary Methods). The gel was found to be thermally irreversible and its non-linear rheological behaviour was confirmed by the amplitude sweep studies (Fig. 3b). The xerogel obtained from Mg-CP was further characterized by FT-IR and 1H NMR spectroscopy. Wide-angle X-ray scattering (WAXS) analysis (Fig. 3c) of the Mg-CP xerogel powder revealed intense diffraction peaks indicating a highly crystalline columnar hexagonal (Colh)  structure, with d-spacing ratios of d, d/√3, d/√4, d/√7 and d/√9. From the first diffraction peak of Mg-CP (d100 = 19.45 Å), the hexagonal lattice parameter a, was estimated as 22.45 Å, which in turn provides the information about the diameter of the columnar stacks in Mg-CP xerogel powder (Fig. 3d)34. The diameter determined from WAXS is in good agreement with the distance of ~24 Å, reported for Zn2+-osalazine-based MOF [Zn 2 (Olz)] (Fig. 3d), which is isostructural to its magnesium anlogue35. The distances between the parallel and antiparallel organic struts of AzSA were estimated to be 6.8 and 3.4 Å, respectively, by comparing with the crystal structure of Zn 2 (Olz) (Fig. 3d). Whereas the WAXS pattern of AzSA matches well with a layered structure similar to its ammonium salt (Supplementary Fig. 3). Transmission electron microscopic images of Mg-CP fibres (Fig. 4a and Supplementary Fig. 4) revealed highly crystalline nature of a closely packed and ordered (d = 3.6 Å) structure corresponding to a columnar hexagonal lattice as looked along the b axis (Fig. 3d). A selected area electron diffraction pattern corroborating the single crystalline nature was obtained from the larger agglomerates of Mg-CP fibres (Fig. 4b).

Fig. 3
figure3

Gelation behaviour of Mg-CP and structural analysis of the xerogel. a Photographs showing the gelation of Mg-CP at the critical gelation concentration (4 mg mL−1). b Non-linear rheological response (amplitude sweep) of Mg-CP gel. c WAXS analysis of Mg-CP and AzSA. d Schematic representation of the molecular arrangement of columnar hexagonal (CoIh) packing of Mg-CP polymeric strands and the calculated lattice parameter. Blue arrows represent coordinated solvent molecules

Fig. 4
figure4

Transmission electron microscopic analysis of Mg-CP fibres. a High-resolution TEM image of Mg-CP fibres. Scale bar, 10 nm. b Single-crystalline SAED pattern obtained from the agglomerates of Mg-CP fibres. Scale bar, 5 nm−1

Host–guest interaction with cyclodextrins in solution

The host–guest interaction of the CDs with Mg-CP as well as its organic precursor AzSA (Supplementary Figs 5-7) was studied in solution state. The intrinsic chirality of CDs allowed us to monitor the binding interactions using a circular dichroism spectrophotometer. A positive ICD band at 355 nm corresponding to the π–π* transition and a small negative band at 440 nm corresponding to n–π* transition (Fig. 5a) indicate the binding of α-cyclodextrin (α-CD) with Mg-CP and AzSA. The hydrophobic azobenzene core resides inside the CD cavity with its electronic transition moment parallel to the CD axis36. The intensity of the ICD signals at 355 nm was found to be two-fold higher for Mg-CP as compared to AzSA when titrated with 3.5 and 4.5 equivalents of α-CD, respectively (Supplementary Fig. 6a,b). A detailed titration plot of the two systems shows that the ICD response was more consistent in the case of Mg-CP as compared to AzSA (Supplementary Figs 6c and 7). The ICD spectrum of Mg-CPβ-CD was similar to that of Mg-CPα-CD, suggesting similar orientation of AzSA stalks inside the β-CD cavity. The interaction of γ-CD with Mg-CP and AzSA was found to be rather weak. The ICD spectrum of Mg-CPγ-CD was recorded at a temperature below the room temperature (15 °C) and consisted of a broad positive signal in the range of 350–500 nm (Fig. 5a).

Fig. 5
figure5

Induced circular dichroism (ICD) capture–release studies of CD complexes of Mg-CP. a ICD spectra of Mg-CP in presence of α-, β- and γ-CDs. b Temperature-dependent ICD spectra of Mg-CPα-CD. Inset shows the changes in the intensity of the ICD band at 355 nm on heating (magenta) and cooling (blue) a solution of Mg-CPα-CD in water between 20 and 90 °C. c Stepwise temperature-controlled quantitative capture of α-CD by an aqueous solution of Mg-CP. Concentration of Mg-CP is 0.06 mg mL−1 and that of α-, β- and γ-CD is 1 × 10−3 M

On increasing the temperature of an aqueous solution of α-CD encapsulated Mg-CP (Mg-CPα-CD) in the range 20–90 °C, a steady decrease in the intensity of the ICD signal at 355 and 440 nm was observed. This decrease in intensity correlates to the release of the α-CD from Mg-CP via temperature-induced decomplexation (Fig. 5b). The release and capture profiles of α-CD from Mg-CP followed identical pathways and no hysteresis was observed during heating or cooling cycles (inset, Fig. 5b). Similar thermally controlled host–guest complexation was obtained for the α-CD complex of AzSA (AzSAα-CD) (Supplementary Fig. 8). The thermal stability of both the inclusion complexes was determined by monitoring the decrease in intensity of the absorption band at 350/355 nm with respect to the increase in temperature (Supplementary Fig. 6d). The Mg-CPα-CD was found to be thermally more stable than AzSAα-CD, which is in agreement with our previous observations (Supplementary Fig. 6a, b). Mg-CPα-CD was therefore chosen as the model system for demonstrating temperature-controlled capture and release of CDs from the host network. By changing the temperature of Mg-CPα-CD solution, the amount of α-CD captured or released could be quantitatively controlled. A temperature dependent capture profile is shown in Fig. 5c.

Thermally controlled host–guest interaction

One of the most relevant properties of any ideal remotely controlled systems is to dodge the process of point capture or point release. For instance, a high dosage of a drug is often administered at an initial point of treatment and may be repeated at a later stage or the dosage may be lowered after several hours or days. This drug administration protocol cannot be precisely controlled and is not free from side effects. In order to address this problem, scientists have tried to develop efficient methods for continuous and controlled drug delivery for prolonged time periods or throughout the whole course of the treatment37. Most of the stimuli-responsive drug delivery systems reported in literature does not show any capture or release of drug molecules in absence of a stimulus. A gradual and continuous release or capture process starting at a particular point is generally observed upon the application of a particular stimulus, which in most cases cannot be further delayed, controlled or reversed5.

It has not yet been demonstrated that temperature-dependent capture–release processes can be achieved in a stepwise and reversible manner, with specific control over the amount of guest molecules captured or released. By controlling the cooling rate from 15 to 5 °C min−1, we demonstrate that the binding rates of α-CD to Mg-CP could be controlled from rapid to moderate to slow rates (Fig. 6a). The system also showed reversible binding and release of α-CD from the CP over several heating–cooling cycles (Fig. 6b). In line with the conventions of a system in thermodynamic equilibrium, the equilibrium constant or the ratio of the α-CD encapsulated sites to that of the free sites present in Mg-CP and the amount of free α-CD molecules present in solution remains constant at a particular temperature. Further, the ratio of bound to free α-CD could also be kept constant for any desired duration of time. As a result, the ICD signal of Mg-CPα-CD remains constant at a particular temperature, which is an inherent property of this host–guest complex. Therefore, by increasing or decreasing the temperature at regular intervals, a definite amount of α-CD can be released or captured by the Mg-CP in a reversible and stepwise fashion (Fig. 6c). This property also allowed the release or capture of α-CD in different instalments by adjusting the temperature of the solution. This host–guest complex thus manifests itself to be programmable on an increasing or decreasing temperature scale. Any desired release or capture profile may be obtained by controlling the host–guest ratio at a particular temperature for any desired amount of time. The ICD signal was found to be constant at 20 °C, even after 1 h (Fig. 6d).

Fig. 6
figure6

Stepwise and reversibly controlled release and capture of α-CD by Mg-CP in solution state. a Temperature-dependent binding of α-CD by Mg-CP with cooling rate of the solution from 15 to 5 °C min−1. Non-linear fit to the observed data points are also represented. b Thermally reversible binding (blue) and release (yellow) of α-CD by Mg-CP. c Stepwise release and capture of α-CD by Mg-CP. The arrows represent the specific changes in the temperature. d A two-step capture profile of α-CD from Mg-CP. The ICD signal remains stable at a particular temperature for the desired amount of time. The plot on the right shows no release of α-CD from Mg-CP at 20°C even after 1 h. Concentration of Mg-CP is 0.06 mg mL−1 and that of α-CD is 1 × 10−3 M for all experiments

In order to study the feasibility of temperature-controlled release and capture of α-CD in the solid state, temperature-dependent changes in the ICD spectrum of Mg-CPα-CD was investigated in a film prepared from an aqueous solution of Mg-CPα-CD over a quartz substrate (Supplementary Fig. 9). The positive and negative ICD signals were found to be red shifted to 392 nm and 470 nm, respectively, due to the aggregation of Mg-CPα-CD in the solid state. No detectable changes were observed in the ICD spectrum upon heating or cooling the sample, confirming that the rigid phase does not favour the dynamics of the host–guest self-assembly process and hence a fluid or soft phase is essential. For example, synthetic hydrogels efficiently mimic the salient features of extracellular matrices as well as help in the creation of three-dimensional cellular microenvironments38,39. These materials trap a large amount of water in the quasi-solid state40 and behave as an ideal system to study temperature-controlled host–guest interactions in a restricted environment. Mg-CPα-CD was therefore incorporated into a polyacrylamide hydrogel (Fig. 7a–c). The yellow colour of the obtained soft material confirmed the incorporation of Mg-CPα-CD within the gel matrix. The hybrid gel was found to be highly mouldable, flexible and transparent (Fig. 7b). No noticeable change in the CD spectrum of the pristine hydrogel was observed upon heating and cooling between 20 and 80 °C (Fig. 7d). Specifically, the CD intensity at 350 nm and 420 nm corresponding to Mg-CPα-CD remained constant with respect to the changes in the temperature of the gel (Supplementary Fig. 10). The ICD spectrum of Mg-CPα-CD incorporated inside the hydrogel matrix (Fig. 7e) recorded at different temperatures was different from that of the complex in solution (Fig. 5a). The nature of the ICD spectrum is decided by a set of rules proposed by Harata and Kodaka initially for CD inclusion complexes and generalized later for chiral macrocycles34. These rules state that (i) any electronic transition that is polarized parallel or perpendicular to the axis of the macrocyclic host gives a positive and negative ICD signal, respectively; (ii) on movement of the chromophore from inside of the macrocycle cavity to outside, keeping the direction of the electronic transition moment unaltered, the sign of ICD is reversed; (iii) when a chromophore remains outside, just near the narrow rim of the CD, the intensity of the ICD signal is greater when compared to being positioned just outside of the wider rim; and (iv) the intensity of an ICD signal due to an electronic transition polarized perpendicular to the macrocycle axis is −1/2 of that when the transition is polarized in the parallel direction and the sign of the ICD signal changes at 54.7°. In the solution state, according to rules (i) and (iv), Mg-CPα-CD shows a positive ICD signal (due to π–π* transition) and a negative signal (due to n–π* transition). However, in the hydrogel matrix, the incorporated Mg-CPα-CD shows a broad negative ICD signal, corresponding to both π–π* and n–π* transitions, in accordance with rules (i), (iii) and (iv). The changes may be attributed to the complex positioning of the Mg-CPα-CD polymer strands and free α-CD close to one another in the gel, in a haphazard fashion, as opposed to the larger inter-strand distance in solution, where electronic interactions are minimal. In order to prove the stability of Mg-CPα-CD inside the polymer hydrogel matrix, leaching of the complex into water from a xerogel strip at room temperature was monitored at 355 nm (Supplementary Fig. 11a). The ICD spectrum of the aqueous phase matched that of Mg-CPα-CD complex in solution (Supplementary Fig. 11b).

Fig. 7
figure7

Stepwise and reversibly controlled release and capture of α-CD by Mg-CP in quasi-solid state. a Photograph of the polyacrylamide hydrogel. b Photograph of Mg-CPα-CD incorporated into the polyacrylamide hydrogel. c A pictorial representation of Mg-CPα-CD in the polyacrylamide hydrogel. d Temperature-dependent changes in the ICD spectra of the polyacrylamide hydrogel. e Temperature-dependent changes in the ICD spectra of the Mg-CPα-CD entrapped polyacrylamide hydrogel. Changes in the ICD spectrum at 350 and 420 nm are represented by magenta and cyan lines, respectively. f Stepwise release profile of α-CD from Mg-CP monitored at 350 and 420 nm in the hydrogel at different temperatures. g Reversible binding (black arrow) and release (blue arrow) of α-CD from Mg-CP incorporated into the hydrogel

On heating the gel sample, the ICD signal is completely reversed according to rule (ii). Temperature-dependent ICD spectrum of Mg-CPα-CD trapped inside the hydrogel matrix was monitored at 350 and 420 nm (Fig. 7e and Supplementary Fig. 12), corresponding to the major ICP bands of Mg-CP in solution. Contrary to the solution-state ICD spectrum (Fig. 5b, inset), a clear hysteresis was observed between the heating and cooling cycles of Mg-CPα-CD when incorporated into the polymer hydrogel. This observation indicates that, although α-CD molecules were released from the Mg-CP on heating, they were not readily available to recapture the free azobenzene sites on cooling. Temperature-dependent swelling and de-swelling of the polymer hydrogel promotes a lag phase between these binding and release processes, leading to the observed hysteresis, similar to the hysteresis loop in the gas adsorption profile of soft porous crystals41. Akin to the solution state, the ICD signal could be consistently modulated by maintaining the hydrogel at a particular temperature. A stepwise release profile of α-CD from the Mg-CP could also be demonstrated (Fig. 7f) as in solution. The temperature-dependent ICD spectrum of the polymer hydrogel, monitored at 350 and 420 nm (Supplementary Fig. 10), where no perceptible changes was observed, substantiates that the differences observed above originate solely from the host–guest interactions involving α-CD and Mg-CP. The system was also found to maintain its high reversibility for several heating and cooling cycles in the quasi-solid state (Fig. 7g).

Discussion

Moving away from the conventional approach, in the present study, CDs have been used as guests for a CP Mg-CP. The water-soluble CP having CD-binding azobenzene-based side appendages possess a greater affinity and high selectivity towards various CDs as compared to its organic precursor. The Mg-CPα-CD precisely perform quantitative capture–release process using temperature as stimulus. The chemistry discussed herein reaps the thermodynamic benefits of a system in chemical equilibrium and may have potential impact in designing systems for controlled delivery of stealth drug molecules, such as CDs.

Methods

Stepwise CD capture and release experiments

Temperature-controlled stepwise capture and release of α-CD was performed in the time course measurement mode. Relative changes in ICD signal intensity was monitored at a particular wavelength (corresponding to π–π* transition) with respect to time. In all samples, 90 μL of Mg-CP (2 mg mL−1) was added to a 3 mL solution of α-CD (1 × 10−3 M) in water. The temperature of the solution was manually changed using the thermostat between specific temperature ranges (e.g. from 80 to 70 °C → from 80 to 20 °C, Fig. 5c). Considering the maximum achieved ICD signal as 100%, the amount of α-CD captured was determined. The temperature of the thermostat was reduced manually between 90 and 20 °C, varying the rate from 5 to 15 °C min−1, to obtain Fig. 6a. The experiment was repeated at least three times to confirm our observation. When the solution was cooled and heated with a particular rate, in repeated cycles, Fig. 6b was obtained. When the temperature of the solvent was kept constant for a particular time interval (5 min) during the cooling or heating process, the ICD signal versus time showed a plateau-like behaviour (Fig. 6c). For the experiments in the hydrogel state, a hydrogel/Mg-CP/α-CD composite was prepared inside a quartz quevette by adding 750 μL of an aqueous solution of Mg-CP (0.26 mg mL−1) to 750 μL of an aqueous solution of α-CD (4.33 mg mL−1). To the resulting solution, 1.5 mL of 40% stock solution of acrylamide/bisacrylamide was added followed by 300 μL of 10% ammonium persulphate solution. The resulting mixture was vigorously whisked to prevent the formation of air bubbles. Subsequently, 50 μL of tetramethylethylenediamine solution was added to control the rate of the polymerization process. A total of 3 mL of the above solution was left undisturbed for ~1 h in a quartz cuvette to obtain a transparent pale yellow hydrogel. The circular dichroism spectral intensities at required constant temperatures were measured and plotted against time for monitoring the CD capture–release processes.

Data availability

All relevant data are available in the article as well as in the supplementary information files and from the authors on reasonable request.

References

  1. 1.

    Koshland, D. E. The key-lock theory and the induced fit theory. Angew. Chem. Int. Ed. 33, 2375–2378 (1995).

    Article  Google Scholar 

  2. 2.

    Alberts, B. et al. Molecular Biology of the Cell, 4th edn, (Garland Science, New York, 2002).

    Google Scholar 

  3. 3.

    Mura, S., Nicolas, J. & Couvreur, P. Stimuli-responsive nanocarriers for drug delivery. Nat. Mater. 12, 991–1003 (2013).

    ADS  Article  PubMed  CAS  Google Scholar 

  4. 4.

    Rwei, A. Y., Wang, W. & Kohane, D. S. Photoresponsive nanoparticles for drug delivery. Nano Today 10, 451–467 (2015).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  5. 5.

    Linsley, C. S. & Wu, B. M. Recent advances in light-responsive on demand drug-delivery systems. Ther. Deliv. 8, 89–107 (2017).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  6. 6.

    Alvarez-Lorenzo, C., Bromberg, L. & Concheiro, A. Light-sensitive intelligent drug delivery systems. Photochem. Photobiol. 85, 848–859 (2009).

    Article  PubMed  CAS  Google Scholar 

  7. 7.

    Khaletskaya, K. et al. Integration of porous coordination polymers and gold nanorods into core-shell mesoscopic composites toward light-induced molecular release. J. Am. Chem. Soc. 135, 10998–11005 (2013).

    Article  PubMed  CAS  Google Scholar 

  8. 8.

    Mano, J. F. Stimuli-responsive polymeric systems for biomedical applications. Adv. Eng. Mater. 10, 515–527 (2008).

    Article  CAS  Google Scholar 

  9. 9.

    Fernandez-Prini, R. Le Châtelier’s principle and the prediction of the effect of temperature on solubilities. J. Chem. Educ. 59, 550–552 (1982).

    Article  CAS  Google Scholar 

  10. 10.

    Connors, K. A. The stability of cyclodextrin complexes in solution. Chem. Rev. 97, 1325–1357 (1997).

    Article  PubMed  CAS  Google Scholar 

  11. 11.

    Bohne, C. Supramolecular dynamics. Chem. Soc. Rev. 43, 4037–4050 (2014).

    Article  PubMed  CAS  Google Scholar 

  12. 12.

    Nagata, S., Kokado, K. & Sada, K. Metal–organic framework tethering PNIPAM for ON–OFF controlled release in solution. Chem. Commun. 51, 8614–8617 (2015).

    Article  CAS  Google Scholar 

  13. 13.

    Meng, X., Gui, B., Yuan, D., Zeller, M. & Wang, C. Mechanized azobenzene-functionalized zirconium metal-organic framework for on-command cargo release. Sci. Adv. 2, e1600480 (2016).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  14. 14.

    Diring, S. et al. Light responsive metal–organic frameworks as controllable CO-releasing cell culture substrates. Chem. Sci. 8, 2381–2386 (2017).

    Article  PubMed  CAS  Google Scholar 

  15. 15.

    Kahn, J. S., Freage, L., Enkin, N., Garcia, M. A. A. & Willner, I. Stimuli-responsive DNA-functionalized metal-organic frameworks (MOFs). Adv. Mater. 29, 1602782 (2017).

    Article  CAS  Google Scholar 

  16. 16.

    Haraguchi, K. & Takehisa, T. Nanocomposite hydrogels: a unique organic–inorganic network structure with extraordinary mechanical, optical, and swelling/de-swelling properties. Adv. Mater. 14, 1120–1124 (2002).

    Article  CAS  Google Scholar 

  17. 17.

    Maggini, L., Liu, M., Ishida, Y. & Bonifazi, D. Anisotropically luminescent hydrogels containing magnetically-aligned MWCNTs-Eu(III) hybrids. Adv. Mater. 25, 2462–2467 (2013).

    Article  PubMed  CAS  Google Scholar 

  18. 18.

    Strebhardt, K. & Ullrich, A. Paul Ehrlich’s magic bullet concept: 100 years of progress. Nat. Rev. Cancer 8, 473–480 (2008).

    Article  PubMed  CAS  Google Scholar 

  19. 19.

    Crini, G. Review: a history of cyclodextrins. Chem. Rev. 114, 10940–10975 (2014).

    Article  PubMed  CAS  Google Scholar 

  20. 20.

    Harada, A. Cyclodextrin-based molecular machines. Acc. Chem. Res. 34, 456–464 (2001).

    Article  PubMed  CAS  Google Scholar 

  21. 21.

    Chen, G. & Jiang, M. Cyclodextrin-based inclusion complexation bridging supramolecular chemistry and macromolecular self-assembly. Chem. Soc. Rev. 40, 2254–2266 (2011).

    Article  PubMed  CAS  Google Scholar 

  22. 22.

    Abi-Mosleh, L., Infante, R. E., Radhakrishnan, A., Goldstein, J. L. & Brown, M. S. Cyclodextrin overcomes deficient lysosome-to-endoplasmic reticulum transport of cholesterol in Niemann-Pick type C cells. Proc. Natl. Acad. Sci. USA 106, 19316–19321 (2009).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  23. 23.

    Artiss, J. D., Brogan, K., Brucal, M., Moghaddam, M. & Jen, K. L. The effects of a new soluble dietary fiber on weight gain and selected blood parameters in rats. Metabolism 55, 195–202 (2006).

    Article  PubMed  CAS  Google Scholar 

  24. 24.

    Miyauchi, M., Takashima, Y., Yamaguchi, H. & Harada, A. Chiral supramolecular polymers formed by host–guest interactions. J. Am. Chem. Soc. 127, 2984–2989 (2005).

    Article  PubMed  CAS  Google Scholar 

  25. 25.

    Liao, X. et al. Photoresponsive pseudopolyrotaxane hydrogels based on competition of host–guest interactions. Angew. Chem. Int. Ed. 49, 4409–4413 (2010).

    Article  CAS  Google Scholar 

  26. 26.

    Wang, J., Zhang, Y.-M., Zhang, X.-J., Zhao, X.-J. & Liu, Y. Light-controlled [3]pseudorotaxane based on tetrasulfonated 1,5-dinaphtho-32-crown-8 and α-cyclodextrin. Asian J. Org. Chem. 4, 244–250 (2015).

    Article  CAS  Google Scholar 

  27. 27.

    Deng, H. et al. Large-pore apertures in a series of metal-organic frameworks. Science 336, 1018–1023 (2012).

    ADS  Article  PubMed  CAS  Google Scholar 

  28. 28.

    Rosi, N. L. et al. Rod packings and metal-organic frameworks constructed from rod-shaped secondary building units. J. Am. Chem. Soc. 127, 1504–1518 (2005).

    Article  PubMed  CAS  Google Scholar 

  29. 29.

    Deacon, G. B. & Phillips, R. J. Relationships between the carbon-oxygen stretching frequencies of carboxylato complexes and the type of carboxylate coordination. Coord. Chem. Rev. 33, 227–250 (1980).

    Article  CAS  Google Scholar 

  30. 30.

    Mukhopadhyay, R. D., Praveen, V. K. & Ajayaghosh, A. Photoresponsive metal–organic materials: exploiting the azobenzene switch. Mater. Horiz. 1, 572–576 (2014).

    Article  CAS  Google Scholar 

  31. 31.

    Mukhopadhyay, R. D., Praveen, V. K., Hazra, A., Maji, T. K. & Ajayaghosh, A. Light driven mesoscale assembly of a coordination polymeric gelator into flowers and stars with distinct properties. Chem. Sci. 6, 6583–6591 (2015).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  32. 32.

    Mukhopadhyay, R. D., Vedhanarayanan, B. & Ajayaghosh, A. Creation of “rose petal” and “lotus leaf” effects on alumina by surface functionalization and metal-ion coordination. Angew. Chem. Int. Ed. 56, 16018–16022 (2017).

    Article  CAS  Google Scholar 

  33. 33.

    Bandara, H. M. D. & Burdette, S. C. Photoisomerization in different classes of azobenzene. Chem. Soc. Rev. 41, 1809–1825 (2012).

    Article  PubMed  CAS  Google Scholar 

  34. 34.

    Kline, M. A. et al. Extremely strong tubular stacking of aromatic oligoamide macrocycles. Chem. Sci. 6, 152–157 (2015).

    Article  PubMed  CAS  Google Scholar 

  35. 35.

    Levine, D. J. et al. Olsalazine-based metal-organic frameworks as biocompatible platforms for H2 adsorption and drug delivery. J. Am. Chem. Soc. 138, 10143–10150 (2016).

    Article  PubMed  CAS  Google Scholar 

  36. 36.

    Balan, B., Sivadas, D. L. & Gopidas, K. R. Interaction of pyromellitic diimide derivatives with β-cyclodextrin and anthracene-appended β-cyclodextrin: rim binding vs inclusion complexation. Org. Lett. 9, 2709–2712 (2007).

    Article  PubMed  CAS  Google Scholar 

  37. 37.

    Mitragotri, S., Burke, P. A. & Langer, R. Overcoming the challenges in administering biopharmaceuticals: formulation and delivery strategies. Nat. Rev. Drug Discov. 13, 655–672 (2014).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  38. 38.

    Cushing, M. C. & Anseth, K. S. Hydrogel cell cultures. Science 316, 1133–1134 (2007).

    Article  PubMed  CAS  Google Scholar 

  39. 39.

    Caliari, S. R. & Burdick, J. A. A practical guide to hydrogels for cell culture. Nat. Methods 13, 405–414 (2016).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  40. 40.

    Wang, Q. et al. High-water-content mouldable hydrogels by mixing clay and a dendritic molecular binder. Nature 463, 339–343 (2010).

    ADS  Article  PubMed  CAS  Google Scholar 

  41. 41.

    Horike, S., Shimomura, S. & Kitagawa, S. Soft porous crystals. Nat. Chem. 1, 695–704 (2009).

    Article  PubMed  CAS  Google Scholar 

Download references

Acknowledgements

A.A. is grateful to Department of Science and Technology (DST), Government of India for a J. C. Bose Fellowship (SB/S2/JCB-11/2014). R.D.M. and G.D. are thankful to Council of Scientific and Industrial Research (CSIR), Government of India for research fellowships. We thank Mr. Kiran Mohan, Dr. J. D. Sudha and Dr. E. Bhoje Gowd of CSIR-NIIST for TEM, rheology and WAXS measurements, respectively.

Author information

Affiliations

Authors

Contributions

R.D.M. undertook the synthesis of molecules and performed studies. G.D. helped in ICD measurements and hydrogel preparation. A.A. and R.D.M. designed the experiments. All the authors analysed the data, discussed the results, wrote and commented on the manuscript. A.A. was responsible for the overall project concept, direction and coordination.

Corresponding author

Correspondence to Ayyappanpillai Ajayaghosh.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Mukhopadhyay, R.D., Das, G. & Ajayaghosh, A. Stepwise control of host–guest interaction using a coordination polymer gel. Nat Commun 9, 1987 (2018). https://doi.org/10.1038/s41467-018-04303-8

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.