Abstract
Topological defects in matter behave collectively to form highly nontrivial structures called topological textures that are characterised by conserved quantities such as the winding number. Here we show that an epitaxial ferroelectric square nanoplate of bismuth ferrite subjected to a large strain gradient (as much as 10^{5} m^{−1}) associated with misfit strain relaxation enables five discrete levels for the ferroelectric topological invariant of the entire system because of its peculiar radial quadrant domain texture and its inherent domain wall chirality. The total winding number of the topological texture can be configured from − 1 to 3 by selective nonlocal electric switching of the quadrant domains. By using angleresolved piezoresponse force microscopy in conjunction with local winding number analysis, we directly identify the existence of vortices and antivortices, observe pair creation and annihilation and manipulate the net number of vortices. Our findings offer a useful concept for multilevel topological defect memory.
Similar content being viewed by others
Introduction
Topological defects are singularities such as vortices in real, momentum and complexphase spaces^{1,2,3}. Topological defects are unstable in terms of their own energy, but they are created by other constraints such as given boundary conditions and systemspecific symmetry^{4}. The topological concept has been broadly applied to a variety of subjects and has led to novel physical phenomena such as the quantum Hall effect and the topological insulator^{5} based on the topology of the quantum mechanical wave function, i.e., the orbital degree of freedom in solids. Magnetic vortices and skyrmions are also topological objects that are relevant to the spin degree of freedom^{6,7,8}. The remaining fundamental degree of freedom that has been relatively rarely explored concerns the lattice in crystalline solids. Despite the identification of electric vortex structures^{9,10,11,12,13,14,15,16,17,18,19,20,21}, electric switching of competing vortex textures with deterministic configurability of the topological number remains experimentally unconfirmed. Therefore, the study of configurable topological defects in electrically polarised media such as a ferroelectric presents an opportunity for a complete understanding of the universal topological features in matter.
In this study, we explore the role of an inhomogeneous strain field as a mechanism for topological defects in ferroelectrics. Elastically deformed lattice in an inhomogeneous strain state is coupled with the ferroelectric property through the mechanoelectric effect^{22,23,24}. Nevertheless, the straingradientinduced effect has been overlooked as an origin of topological ferroelectric textures, because the polarisation induced by macroscopic bending is negligible relative to the typical value of spontaneous ferroelectric polarisation. However, recent advances in nanoscale characterisation have led to the discovery that large strain gradients are often present in epitaxial films relaxed from misfit strains^{23,24}, selfassembled nanostructures^{25}, dislocations^{26}, domain and twin walls^{2}, and morphotropic phase boundaries^{27,28}. The challenge at hand, therefore, is to demonstrate ferroelectric materials subjected to significantly large inhomogeneous strains to clamp nontrivial textures and facilitate interphase switching. Direct observation and analysis of electric vortices in the context of the topological winding number in such curved lattices can provide an unprecedented view of ferroelectrics.
In the following results, we study how to stabilise, observe and control the ferroelectric topological textures in the epitaxial square nanoplate of bismuth ferrite subjected to a large strain gradient. The piezoresponse vector map of the ferroelectric nanoplate is obtained by angleresolved piezoresponse force microscopy (PFM) and the positions of the vortices and antivortices are determined by winding number calculation based on the piezoresponse vector map. In addition, the effect of inhomogeneous strain in the ferroelectric nanoplate on nontrivial topological texture formation is investigated by phase field simulation. Finally, we show that the total winding number of the topological texture can be modulated by selective domain switching.
Results
Emergence of a radial quadrant domain structure
Selfassembled BiFeO_{3} (BFO) nanoplates were synthesized by pulsed laser deposition using a composite target mixing BFO with cobaltferrite spinel (see Methods section for the details). BFO has a rhombohedral structure with a large spontaneous ferroelectric polarisation (almost 100 μC cm^{−2}) along a pseudocubic <111> direction in bulk^{29} and weakly strained epitaxial films^{30,31}. The largearea topographic image (Fig. 1a) shows the emergence of protruding square BFO plates with a typical lateral size of approximately 300 nm. Outofplane (OOP) and inplane (IP) PFM images reveal that a quadrant domain structure emerges on the BFO nanoplates (Fig. 1b, c). This unusual domain structure is attributed to the anisotropic mechanical boundary condition, i.e., the bottom of the BFO nanoplate is compressively strained while the other side and top faces experience no external stress. Quantitative analysis of the strain relaxation using Xrays and theoretical understanding based on phase field simulation will be discussed later in this study.
In the asgrown state, outward/upward polarisations are stabilised in most quadrant domain areas, but slim buffer domains with inward/downward polarisations are identified in the form of a cross. The electric poling over a square region by a positively biased tip switches the upward polarisation to the downward direction (Fig. 1d). Interestingly, this OOP switching is accompanied by the reversal of IP piezoresponse. The clamping of OOP and IP components suggests that each quadrant is subject to ferroelastic elongation along <111> and the poling gives rise to 180° ferroelectric switching along the rhombohedral axis. The switched configuration can be reversed to the original upward/outward state, as demonstrated by the reverse poling (Fig. 1e). Similar quadrant textures are commonly observed in almost all nanoplates regardless of differences in the lateral size and shape, which indicates the stability of the quadrant domain textures.
Detailed intrastructure of a quadrant domain texture
One of the greatest challenges in ferroelectric defect studies is to devise a direct realspace detection technique that observes the behaviour of electric vortices with nanoscale spatial resolution in a nondestructive manner, particularly when related to mechanical deformation. Angleresolved PFM was used to construct IP piezoresponse vector map (Fig. 2). The inplane PFM technique can distinguish only the perpendicular component to the cantilever, because it relies on the torsional vibration mode of the cantilever. The inplane piezoresponse vector can be determined by using several highresolution PFM images acquired in a quasiidentical region with different tip orientation angles, respectively. We carried out trigonometric curve fitting to determine the amplitude and phase shift of the sinusoidal fit function per position and mapped out the piezoresponse vector spatially.
We successfully visualised the piezoresponse vector distribution, thereby disclosing detailed features on an emergent radial quadrant domain structure (Fig. 3). The second and fourth quadrant ferroelastic domains of the rhombohedral BFO were split into a quadrant domain and a thin buffer domain with forming a 180° charged domain wall, respectively. At the ferroelectric domain walls, not only does the polarisation rotate to avoid uncompensated charge density, but the amplitude of polarisation is reduced to avoid imposing a significant energy cost for rotating the polarisation away from the easy axis in the lattice^{32}. According to the locations of the buffer domains on the second and fourth quadrants, the measured nanoplate corresponds to the type 2 configuration (as will be addressed later) that contains two vortices at the ferroelectric domain walls and a single antivortex at the centre. Scanning transmission electron microscopy (TEM) of a crosssection of a nanoplate underpins the outward/upward quadrant polarisations and the downward buffer domain (Supplementary Fig. 5). Although the PFM vector map provides a useful insight into ferroelectric domain structures under the assumption that piezoresponse vector has a linear correlation with electric polarisation, we should be cautiously aware of the limitation. For example, it has been reported that 180° domain walls can generate a lateral piezoreponse due to a topographical slope at the domain boundary caused by opposite deformations on the neighbouring up and down polarised domains^{33}. We are not sure how largely the effect is involved in our case, and thus, it is desirable to interpret the detailed feature of the domain walls based on theoretical supports through topological analysis and phase field simulation.
Topological winding number analysis
We analysed the measured vector map by calculating local winding numbers to identify the precise positions of the vortices (Fig. 3d). The winding number is a topological quantity that counts the singularities in vector fields and is defined in a twodimensional space by contour integration of the variation of the vector direction along a given closed loop^{1,2,34}; it is an integer that indicates the net number of singularities inside the loop, so the number is preserved in continuous deformations. The integral over a large enclosed space is equivalent to the total sum of all individual local winding numbers for small areas that comprise the large space (Supplementary Fig. 1). This conservation property ensures that the topological number of an entire system is determined only by the boundary condition and does not vary, regardless of any interior configuration.
We tiled small edge sharing loops and calculated local winding numbers (see the Methods section for the details). As a result, two vortices and a single antivortex were clearly identified. A single vortex point was found on each 180° charged domain wall. The antivortex was detected at the central merging point of the twoin/twoout domain configuration. The net sum of the vortex points in this asgrown state was + 1 and this net value was equal to the total winding number calculated along a large closed loop near the edge of BFO nanoplate. We emphasise that the topological point affects not only the small loop area but also its farfield configuration globally; it can be easily verified that any other larger loops that only enclose a vortex result in the same winding number. Any random noise in the angle distribution from measurement artefacts and/or intrinsic incoherent fluctuations hardly destroys the robust topological nature.
Phase field simulation
Although the nontrivial topological texture consumes considerable energy in terms of mutual interactions among electric dipoles, their inevitable presence is due to a larger energy gain in another degree of freedom, namely the elastic energy. To reveal the origin of the radial quadrant domain structure, we calculate the inhomogeneous strain distribution in a nanoplate as illustrated in Fig. 4a by phase field simulations (see methods for details). As the bottom interface is constrained while the other five surfaces are stressfree, the mechanical boundary condition gives rise to the distribution of shear strain ε_{ xz } or ε_{ yz } as shown in Fig. 4b. Owing to the electrostrictive interaction q_{1313}ε_{ xz }P_{ x }P_{ z } and q_{2323}ε_{ yz }P_{ y }P_{ z } with q_{ ijkl } as the electrostrictive coefficients, the quadrant domains will be induced. After including the effect of depolarisation field, a domain pattern shown in Fig. 4c is obtained. The polarisation vectors on the top surface is demonstrated in Fig. 4d, which agrees well with the experimental observation in Fig. 3c. Therefore, the spontaneous rhombohedral deformation of BFO (rhombohedral angle ~ 0.6°)^{35}, combined with the specific distribution of shear strains caused by the mechanical boundary conditions of a nanoplate, leads to the formation of a quadrant ferroelastic domain structure in which each quadrant domain is elastically elongated along an outward <111> axis.
As shown in Supplementary Fig. 2a, the gradients of normal strains are largest at the four corners and the polarisations therein are enforced to be upward by the flexoelectric interactions^{24,36}. Thus, the depolarisation field can only flip down the polarisation in the middle part, and the buffer domains are created in the vicinity of ferroelastic walls.
Domain wall chirality and topological domain textures
Under the elastic constraints, ferroelectric polarisation values are assigned to the quadrant domains. A ferroelastic quadrant domain can have two variant ferroelectric polarisations harmonised with each <111> elongation axis. In the asgrown state, upward/outward radial polarisations are stabilised and encounter electric frustration in the central region, thereby leading to nontrivial topological textures with a total winding number of + 1. A buffer ferroelectric domain with an inward/downward polarisation is built on one side of a ferroelastic domain wall to reduce the depolarisation energy, as indicated by the dark grey boxes in Fig. 5a. One end of the 180° domain wall between a buffer domain and a quadrant domain is terminated at an edge where a strong strain gradient is present. The different strain states in both sides of the domain wall deviates the inplane polarisation interangle between two neighbouring ferroelectric domains from 180°, pinning the domain wall chirality at the edge because IP polarisations in the domain wall should rotate gradually along an acute angle.
We note that a single (anti)vortex must exist at a point at which two different chiral domain walls are encountered. Although the nanoscale vortex itself is energetically unstable, the existence cannot be avoided topologically between two end points clamped to have mutually opposite chiralities. This vortex is expected to be readily movable between the two end points, potentially offering an isolated quasiparticle carrying energy along the onedimensional chain. The observed vortex in the second quadrant (on the upper left) in Fig. 3d was located away from the symmetric position, suggesting a vortex formed by the domain wall chirality is less massive between the pinning ends and thus the location is vulnerable to influence from strain variations and/or uncontrolled perturbations.
The existence of buffer ferroelectric domains and the diversity of their locations create more abundance in possible topological textures (Fig. 5b, c). In the asgrown state in which ferroelectric polarisations in the quadrant domains are restricted outward (simultaneously upward), we can classify all 16 possible configurations into four types according to the locations of the buffer domains on one side of each red ferroelastic wall. However, the total winding number in the asgrown state is still + 1, because any buffer domain between two quadrant domains equally outward does not affect the total winding number (Supplementary Fig. 3). All the four types of buffer domain arrangements in the asgrown state can be stabilised by phase field simulations (Fig. 5b).
Nonlocal domain switching and buffer domains control
The central region of the BFO nanoplate can be electrostatically unstable due to the same polarity of the electric dipoles merging at the centre. Because of electrical frustration, unexpected complex domain structures are easily created alongside pair creations by an electrical writing at the centre of the nanoplate. To avoid touching the central region with the biased tip and minimise lowlying excitations, we used a nonlocal domain switching technique. When we apply a dc bias to switch the electric polarisation on the corner of a ferroelastic domain, as described in Fig. 6a, the entire region of a ferroelastic domain is switched in addition to the electrically written area. In the nanoplate structure, the domain wall energy is comparable to the bulk energy because of the large surfacetovolume ratio. Therefore, the entire region of a ferroelastic domain is switched instead of creating a domain wall. This nonlocal switching offers a useful pathway into domain switching minimising artificial pair creations at the sensitive centre area leading to the minimum states. Figure 6b demonstrates our nonlocal domain switching process in a deterministic way. We applied dc − 4 V to the bottom electrode and scanned the corner part that was approximately 100 nm from the central area using a grounded tip. The electrical writing size was 400 × 400 nm, drawing 128 lines at a tip speed of 400 nm s^{–1}, including the corner region. We recognised the nanoplate region using the deflection error simultaneously acquired during the poling, which clearly indicated the boundary of the BFO nanoplate in real time. After nonlocal domain switching, PFM was measured to check the switching effect. We performed nonlocal domain switching at each corner of the BFO nanoplate one by one in a clockwise direction. Eventually, the entire ferroelastic domains were switched to downward/inward polarisation from upward/outward polarisation.
Using nonlocal domain switching, we can control the existence or nonexistence of the buffer domain and its location, which offers a useful pathway into manipulation of the total winding number. For example, we consider an initial domain structure with two neighbouring upward quadrant domains with a downward buffer domain placed on the left side of the ferroelastic wall between them (Fig. 6c). The right ferroelastic quadrant domain that does not contain the buffer domain is switched first and the left ferroelastic domain is switched later. This sequence causes all relevant regions to have downward polarisations without creating a buffer domain. However, the reversal of the switching order leaves a buffer domain on the right side of the ferroelastic wall between quadrant domains that are otherwise the same. These multiple states can be understood on the basis of the competition between the depolarisation energy gain and the domain wall energy loss. The first domain switching causes positive and negative bound charges at the surface. In this case, the depolarisation energy is already stable without regard to the buffer domain, so the switching forms a single ferroelectric domain in the corresponding quadrant without creating a buffer domain. As for the second domain switching, bound charges of the same polarity are located at the surface, so the existence of a buffer domain helps to reduce such unstable depolarisation energy.
Configuration of the topological winding number
We demonstrate that the system’s total winding number can be configured artificially by electric fields. As the net winding number of topological defects is invariable for any continuous deformations of the order parameter, we should introduce a catastrophic transformation such as 180° polarisation switching of quadrant domain(s) to modify the total winding number. The total winding number of a BFO nanoplate relies on the relative arrangement of the quadrant and buffer domains. Provided that the polarisations of two neighbouring quadrant domains point outward (Supplementary Fig. 3), the partial winding number calculations along a line segment from a point in the first quadrant domain to another point in the second quadrant domain are equally 1/4 (i.e. the angle of polarisation is finally increased by 90°) irrespective of the presence of a buffer domain. In the asgrown state, all quadrant domains point outward, so the total winding number is + 1 without regard to different buffer domain formations. On the contrary, if one points outward and the other points inward, the presence of a buffer domain between them increases the winding number by + 1 compared with the absent case. Using this rule, we inspected all possible domain configurations and found total winding numbers ranging from − 1 to 3.
We list each of the domain configurations eligible for the BFO nanoplate and classify them into five levels of topological invariants from a single antivortex to three vortices (Supplementary Fig. 4). Several representative configurations were chosen with four more total winding numbers in addition to the + 1 winding number of the asgrown states among the 1296 possible textures; these configurations are experimentally demonstrated in Fig. 7. The selective domain switching technique without invoking unintended pair creations was essential to stabilise the quasiground state. Remarkably, we found that electrical poling on the corner region (less than a quarter of a single quadrant area) resulted in the reversal of the corresponding quadrant domain while inhibiting the production of a new domain wall. The nonlocal domain reversal provides a tremendous advantage by switching not only selective quadrant domains but also writing or erasing buffer domains deterministically by managing the switching sequence (see the schematics in the righthand side column of Fig. 7), enabling us to realise all the possible configurations in principle.
We verify that interior modifications are unrelated to the total winding number. Figure 8 exhibits an excited state with vortexantivortex pair creations. When all polarisations point inward without buffer domains, the central region becomes highly frustrated with competing local textures. Small electric perturbations easily induce new small domains via unintended pair creations. In the winding number map, many vortex–antivortex pairs are clearly identified near the conjugate small domains, but the total winding number remains + 1 because of the topology.
Evaluation of strain relaxation
These exotic domain textures and switching behaviour are attributed to the radial strain relaxation from the residual compressive strain (as much as − 0.6% at the interface with edge dislocations; see Supplementary Fig. 5). Although the threedimensional strain relaxation is complicated with the delicate features involved in spontaneous rhombic deformation, we obtained experimental hints regarding strain relaxation with the use of various diffraction techniques. The diffusive feature of the asymmetric peaks observed in Xray reciprocal space maps (RSMs) is a clear signature of gradual strain relaxation (Supplementary Fig. 6). The broadening of the diffraction peak was also analysed with a WilliamsonHall plot and the inhomogeneous strains were quantitatively determined to be 0.60% and 0.46% for the OOP and IP lattice parameters, respectively (Supplementary Fig. 7a). Furthermore, the grazing incidence geometry enabled direct investigation of the dependence of the IP lattice parameter on the xray penetration depth (Supplementary Fig. 7b and c). These structural characterisations complementarily suggest that the compressive strain is almost relaxed within the 60 nmthick nanoplates, resulting in a strain gradient whose order of magnitude is 10^{5} m^{−1}. In addition, we note that the strain gradient has a crucial role in the upward selfpolarisation in the quadrant domains via the flexoelectric effect^{36}, because normal BFO films on the Pr_{0.5}Ca_{0.5}MnO_{3} (PCMO) bottom electrode have been downward.
Discussion
Our demonstration by using the unique visualisation approach and the winding number analysis not only offers a useful concept for multilevel topological defect memory, but also provides an avenue into straingradientmediated clamping of topological ferroelectric textures and nonlocal switching among symmetryprotected quantised states. The findings of this study also offer useful insights into electric pair creation, electric frustration and programmable charged domain walls. Of obvious future interest is an examination of the dynamic motion of the topological vortices along the chiral domain walls for energy efficient information technology: electric topological defectronics.
Methods
Growth of composite thin films
BFOCoFe_{2}O_{4} (BFOCFO) composite thin films were synthesised by pulsed laser deposition using a single target composed of Bi_{1.1}FeO_{3} (65 atomic %) and CFO (35 atomic %). The selfassembled nanoplate structures of BFOCFO were grown on (001) LaAlO_{3} (LAO) substrates with a bottom electrode that comprised a ~ 4 nmthick PCMO layer. Growths were made at 630 °C in an oxygen environment of 100 mTorr. A KrF excimer pulsed laser (λ = 248 nm) was used at a frequency of 7 Hz to create a laser fluence of 0.8 J cm^{–}^{2} on the target surface. After the growths were completed, the samples were cooled to room temperature at a rate of 10 °C min^{–1} in an oxygen environment of 500 Torr to minimise the current leakage of BFO.
Angleresolved PFM technique
The surface topography and ferroelectric domains of BFO nanoplates were investigated with a scanning probe microscope (Bruker MultiMode V equipped with a Nanoscope controller V). PFM measurements were performed at a scanning rate of 3 μm s^{−1} using Ptcoated Si conductive tips (MikroMasch, NSC35) applying an ac driving voltage of 2 V_{pp} at a frequency 10 kHz in ambient conditions. In this study, all PFM images plot the real part piezoresponse signal, i.e., amplitude × cos(phase). In the OOP PFM images, the bright (dark) contrast represents upward (downward) polarisation. In the IP PFM images, the bright (dark) contrast indicates the IP piezoresponse vector pointing to [010] ([0–10]) when a cantilever is oriented towards [−100]. IP PFM exploits the torsional motion of the cantilever to sense the IP oscillations of the sample underneath. The IP PFM signal depends on the sample orientation with respect to the cantilever (i.e., the IP PFM signal is proportional to the projected component of the IP piezoresponse vector on the axis perpendicular to the cantilever). It was necessary to align these PFM images to correct pixel misalignment from an asymmetric tip shape and/or the tipdrift issue in nanoscale measurements. Several specific positions, including the domain walls and the corners of the nanoplates, were selected as reference points to determine the coordinate conversion matrices among the images. After this alignment, each position has tiporientationdependent IP PFM signals. Although a data pixel has a physical size of 3 × 3 nm, the signals in a single position for the vector maps are prepared by averaging over a 15 × 15 nm area to improve statics, considering our instrument resolution and sensitivity, and thus pair creations with a separation of less than the average distance are hardly detected. We also used finer 9 × 9 nm averaging for the angle maps to calculate the local winding number with 3by3 (27 × 27 nm) loops.
Winding number calculation
The vortex—a spatially confined object—has a core region with a discontinuous order parameter. Despite the singularity, the existence of a vortex affects the farfield region, where the order parameter changes slowly in space. Therefore, the presence of a vortex can be determined by measuring the variance of the order parameter such as the orientation of ferroelectric polarisation (θ) on any closed contour that encloses the vortex core. Mathematically, the winding number n in twodimensional space is defined by the contour integral of an orientation change Δθ of two neighbouring IP ferroelectric polarisations along a given loop divided by 2π. The winding number gives information regarding the net number of vortices and antivortices enclosed by the loop. For example, if a large closed loop encloses a pair of vortex and antivortex points with opposite winding numbers in a uniform farfield configuration of polarisation, the total winding number for the entire enclosed area is 0. We performed such winding number calculation as follows:
where θ is measured anticlockwise from the [100] direction. We assume that θ is continuous everywhere, except for vortex or antivortex points, and we used a condition of Δθ < 180° to determine the angle rotation direction. We tiled 3 × 3pixel square loops on angle maps that shared the boundaries, to calculate the local winding number at each loop. A pixel of the angle maps includes an average IP PFM direction of a 9 × 9 nm area. Such a small loop has the advantage of measuring the precise position of each vortex or antivortex core.
Phase field simulation
In the phase field simulations, we introduce both polarisation, P_{ i }(i = 1–3), and oxygen octahedral tilt order parameters, θ_{ i }(i = 1–3), to describe the domain structures in BFO. The total free energy density includes the contributions from the Landau bulk free energy, gradient energy, elastic energy and electrostatic energy:
where α_{ ij }, α_{ ijkl }, β_{ ij }, β_{ ijkl } and t_{ ijkl } are the coefficients of the Landau polynomial under stressfree boundary conditions, g_{ ijkl } and κ_{ ijkl } are the gradient energy coefficients, x_{ i } is the spatial coordinate, c_{ ijkl } is the elastic stiffness tensor, ε_{ ij } and \(\varepsilon _{kl}^0\) are the total strain and eigenstrain, respectively, E_{ i } is the electric field, ε_{0} is the permittivity of free space, and κ_{ b } is the background dielectric constant. The eigenstrain is related to the order parameters through \(\varepsilon _{ij}^0 = h_{ijkl}P_kP_l + \lambda _{ijkl}\theta _k\theta _l + \varepsilon _{ij}^{{\mathrm{lattice}}}\), where λ_{ ijkl } and h_{ ijkl } are coupling coefficients, and \(\varepsilon _{ij}^{{\mathrm{lattice}}}\) is eigenstrain caused by lattice parameter mismatch between BFO and the substrate. The current simulations use the parameters from Ref. ^{37}, and a more comprehensive thermodynamic potential for BFO is available at Ref. ^{38}.
To describe the mechanical boundary conditions of BFO nanoplates, the system consists of three types of materials, i.e., BFO, air and substrate. BFO possesses nonzero polarisation and the polarisation in the air and substrate is zero. The elastic stiffness of the air is zero and we assume that the elastic stiffness of the substrate is the same as BFO. Temporal evolution of the order parameter is described by the timedependent Ginzburg–Landau equation, \(\partial P_i{\mathrm{/}}\partial t =  L_P\left( {\delta F{\mathrm{/}}\delta P_i} \right)\) and \(\partial \theta _i{\mathrm{/}}\partial t =  L_\theta \left( {\delta F{\mathrm{/}}\delta \theta _i} \right)\), which is solved numerically using the semiimplicit Fourier spectral method^{39}. Periodic boundary conditions are applied along three directions, and a spectral iterative perturbation method is used to solve the mechanical and electrostatic equilibrium conditions^{40}. Taking the lattice parameter of the substrate as the reference, \(\varepsilon _{ij}^{{\mathrm{lattice}}}\)can be calculated as \(\varepsilon _{ij}^{{\mathrm{lattice}}} = \frac{{0.3965  0.3821}}{{0.3821}} = 3.8\%\). To consider the effect of the depolarisation field along the outofplane direction, we calculate the average polarisation \(\bar P_3 = \frac{{\mathop {\sum}\nolimits_{i = 1}^n {P_3} }}{n}\), and the depolarisation electric field \(E_3 =  \frac{{\bar P_3}}{{\varepsilon _b\varepsilon _0}} + E_{{\mathrm{ex}}}\), where E_{ex} is the extra electric field caused by other factors such as the flexoelectric effect and its magnitude is tuned to obtain the domain structures similar to experiments.
The whole system grid is 128Δx × 128Δx × 60Δx with Δx = 0.38 nm, with 128Δx × 128Δx × 24Δx for the substrate and 64Δx × 64Δx × 12Δx for the BFO island. In the calculation of strain distributions, the order parameter P_{ i } and θ_{ i } are maintained at zero. Thus, the distribution of strain is caused by the relaxation of the nanoplate rather than by the BFO domain structures.
Highangle annular darkfield scanning TEM
To gain more insight into the depth profile of the BFO nanoplate, we performed TEM for a crosssectional view of a nanocomposite thin film. As shown in Supplementary Fig. 5a, a lowmagnification darkfield TEM image clearly revealed that a nanoplate with a lateral size of ~ 300 nm has a thickness of approximately 60 nm and a very thin PCMO layer that uniformly covers the substrate as a bottom electrode. CFO clusters were also seen around the nanoplate with relatively weak contrast in this Zcontrast image. To determine the epitaxial relationships among the nanoplate, the PCMO, and the substrate, we obtained highangle annular darkfield (HAADF) images at the interfacial region of the central nanoplate (Supplementary Fig. 5b). The 4 nmthick PCMO conducting layer was coherently deposited on LAO, that is, the IP lattice parameter of the PCMO was exactly matched with the substrate. However, the BFO nanoplate turned out to be partially relaxed at the initial stage, which created edge dislocations at the interface with the PCMO (red arrows in figure). The edge dislocations appear regularly with an interval of ~ 10 nm (~ 25 unit cells) along the interface at the measured central region. Accordingly, the IP lattice parameter of BFO at the central region is found to be relaxed to 3.94 Å, because the lattice expands by 1/25 from the lattice parameter (3.789 Å) of LAO. The origin of the regular edge dislocations that emerging at an interval of ~ 10 nm is inferred from a large lattice mismatch between the BFO and LAO substrate (~ 4.4% compressive strain compared with the lattice parameter of bulk BFO). Although a significant fraction of the strain is relaxed near the substrate, a compressive strain of ~ 0.6% remains and relaxes gradually across the BFO from the bottom to the top of the nanoplate. Furthermore, atomicscale HAADF scanning TEM (STEM) images taken from the left, middle and right areas of the plate allowed us to check the local ferroelectric polarisation (Supplementary Fig. 5ce), which could be identified by a relative Fe ion displacement with respect to the Bi cage. As the Fe ion of BFO drags the oxygen anions, which were unseen in our measurements, the position of the Fe ion enabled us to presume the negative centre of a unit cell. The observed Fe ion shifts led us to the conclusion that the local polarisations on the left and right areas were upward and outward. Meanwhile, the Fe offcentring at the middle area was downward, and the magnitude was less than those of the outer areas. These observations showed good agreement with the radial quadrant domain structure verified by the angleresolved PFM. For the crosssectional observation on the BFO nanoplate, the specimens were prepared by a dualbeam focused ion beam system (JIB4601F, JEOL, Japan). To protect the BFO plates and CFO films, an amorphous carbon layer was deposited on the top surface before ion beam milling. A Ga^{+} ion beam with an acceleration voltage of 30 kV was used to fabricate the thin TEM lamella. To minimise the surface damages induced by Ga^{+} ion beam milling, the sample was further milled with an Ar^{+} ion beam (PIPS II, Gatan, USA) with an acceleration voltage of 0.8 kV for 15 min. Zcontrast HAADF STEM images were taken with a scanning transmission electron microscope (JEM2100F, JEOL) at 200 kV with a spherical aberration corrector (CEOS GmbH, Germany). The optimum size of the electron probe was approximately 0.9 Å. The collection semiangles of the HAADF detector were adjusted from 80 to 220 mrad to exploit the largeangle elastic scattering of electrons for clear Zsensitive images. The raw images obtained were processed with a Wiener filter with a local window to reduce background noise (HREM Research Inc., Japan).
Xray diffraction
RSMs: Xray diffraction measurements were carried out at beamline 3 A of the Pohang Light Source with a wavelength of 0.9428 Å. To investigate the lattice parameters in detail, we measured RSMs around the asymmetric crystallographic peaks of randomly distributed ~ 60 nmthick nanoplates in a BFOCFO composite film grown on an LAO substrate. As shown in Supplementary Fig. 6, two distinct BFO phases (R and T) with significantly different caxis lattice parameters were detected on both (104) and (114) RSMs. By analysing the two RSMs, we determined the pseudocubic symmetry of each phase and lattice parameters. The peaks of our main interest RBFO have diffusive shapes with their tails pointed toward smaller IP reciprocal positions, indicating the existence of significant strain relaxation within the nanoplates. In particular, we observed a more prominent diffusive feature in the (114) RSM than the (104) RSM and inferred that a more welldefined strain gradient appears along the [HHL] crystallographic axis.
Williamson–Hall plots: The inhomogeneous strain distribution within nanoplates was measured quantitatively in the context of the Williamson–Hall plot^{41,42}. First, we performed longitudinal θ–2θ scans for OOP (00L) peaks up to the fifth order and collected diffraction patterns of the IP (H00) peaks using grazing incidence geometry. We then examined the evolution of the peak broadenings depending on the order (H or L) of the peaks. The broadness of the diffraction peaks can be influenced by the sizebroadening (β_{L}) effect (e.g., film thickness) and the strainbroadening (β_{e}) effect (e.g., a strain gradient along the longitudinal direction). These two effects can be distinguished by their different dependences on the Bragg angle θ, i.e. \(\beta _{\rm L}\sim \frac{{0.9\lambda }}{{t\cos \theta }}\) and \(\beta _e\sim 4\varepsilon _{\rm I}\tan \theta\), where λ is the wavelength of an incident Xray beam, t stands for the film thickness and ε_{I} represents the SD of the strain distribution known as inhomogeneous strain. By combining the two broadenings in a linear regime, the intrinsic line broadening (β) of diffraction peaks can be written as \(\beta \cos \theta \sim 4\varepsilon _{\rm I}\sin \theta + \frac{{0.9\lambda }}{t}\). Accordingly, the Williamson–Hall plot (\(\beta \cos \theta\) vs. \(4\sin \theta\)) gives information regarding the inhomogeneous strain from the slope and the film thickness from the intercept. The values of ε_{ I } for the caxis and aaxis lattice parameters were determined to be 0.0060 and 0.0046, respectively (Supplementary Fig. 7a). The linear fitting lines in the plot were constrained in such a way that they intersected at an identical point at θ = 0. From the intercept, the film thickness is determined to be ~ 60 nm, which is consistent with the TEM crosssectional image.
Grazing incidence XRD: A variation of the IP lattice parameter was directly measured as a function of the probing depth (d_{p}) by using the grazing incidence geometry (Supplementary Fig. 7b). The penetration depth of the X ray is nearly proportional to the incidence angle μ, according to \(d_p = \lambda {\rm sin}\mu {\mathrm{/}}4\pi \beta ^ \ast\), where the effective imaginary part of reflective index β* was set to be the BFO value (4.3 × 10^{−7})^{43}. The depth profile shows that the lateral strain (ε_{ xx } and ε_{ yy }) is rapidly relaxed near the surface (Supplementary Fig. 7c). To explain the observed strain depth profile, the strain ε(z) was written as \(\varepsilon (z) =  \varepsilon _1 + \varepsilon _0e^{\alpha z}\) where ε_{1}, ε_{0} and α are coefficients, and z is the distance from the substrate. We fit the average strain model \(\left\langle \varepsilon \right\rangle _{d_p} = \frac{1}{{d_p}}{\int}_0^{d_p} {\varepsilon (t  z{\prime}){\rm d}z{\prime}}\) to the experimental data, where t denotes the film thickness (60 nm) and the variable of integration z′ measures from the top surface. The coefficients ε_{1}, ε_{0} and α were determined to be 0.0043, 2.6 × 10^{−9} and 0.24 nm^{−1}, respectively. The fitting was well matched with an R^{2} value of 0.9874. We thus estimate the average strain gradient across the entire BFO nanoplate \(\left\langle {\frac{{d\varepsilon }}{{dz}}} \right\rangle _t\) as 0.8 × 10^{5} m^{−1}, which agrees well with the inhomogeneous strain.
Data availability
The authors declare that the data supporting the findings of this study are available within the paper and its Supplementary Information files. Additional data are available from the corresponding author upon reasonable request.
References
Mermin, N. D. The topological theory of defects in ordered media. Rev. Mod. Phys. 51, 591–648 (1979).
Seidel, J. (Ed.) Topological Structures in Ferroic Materials. (Springer International Publishing, 2016).
Skyrme, T. H. R. A unified field theory of mesons and baryons. Nucl. Phys. 31, 556–569 (1962).
Gregg, J. M. Exotic domain states in ferroelectrics: searching for vortices and skyrmions. Ferroelectrics 433, 74–87 (2012).
Qi, X.L. & Zhang, S.C. The quantum spin Hall effect and topological insulators. Phys. Today 63, 33–38 (2010).
Mühlbauer, S. et al. Skyrmion lattice in a chiral magnet. Science 323, 915–919 (2009).
Yu, X. Z. et al. Realspace observation of a twodimensional skyrmion crystal. Nature 465, 901–904 (2010).
Milde, P. et al. Unwinding of a skyrmion lattice by magnetic monopoles. Science 340, 1076–1080 (2013).
Lin, S.Z. et al. Topological defects as relics of emergent continuous symmetry and Higgs condensation of disorder in ferroelectrics. Nat. Phys. 10, 970–977 (2014).
Yadav, A. K. et al. Observation of polar vortices in oxide superlattices. Nature 530, 198–201 (2016).
Tang, Y. L. et al. Observation of a periodic array of fluxclosure quadrants in strained ferroelectric PbTiO_{3} films. Science 348, 547–551 (2015).
Balke, N. et al. Enhanced electric conductivity at ferroelectric vortex cores in BiFeO_{3}. Nat. Phys. 8, 81–88 (2012).
Vasudevan, R. K. et al. Exploring topological defects in epitaxial BiFeO_{3} thin films. ACS Nano 5, 879–887 (2011).
Jia, C.L., Urban, K. W., Alexe, M., Hesse, D. & Vrejoiu, I. Direct observation of continuous electric dipole rotation in fluxclosure domains in ferroelectric Pb(Zr, Ti)O_{3}. Science 331, 1420–1423 (2011).
McQuaid, R. G. P., McGilly, L. J., Sharma, P., Gruverman, A. & Gregg, J. M. Mesoscale fluxclosure domain formation in singlecrystal BaTiO_{3}. Nat. Commun. 2, 404 (2011).
Schilling, A. et al. Domains in ferroelectric nanodots. Nano Lett. 9, 3359–3364 (2009).
Naumov, I. I., Bellaiche, L. & Fu, H. Unusual phase transitions in ferroelectric nanodisks and nanorods. Nature 432, 737–740 (2004).
Nahas, Y. et al. Discovery of stable skyrmionic state in ferroelectric nanocomposites. Nat. Commun. 6, 8542 (2015).
Wu, C. M. et al. Controllability of vortex domain structure in ferroelectric nanodot: fruitful domain patterns and transformation paths. Sci. Rep. 4, 3946 (2014).
Hong, Z. et al. Stability of polar vortex lattice in ferroelectric superlattices. Nano Lett. 17, 2246–2252 (2017).
Xue, F. et al. Switching the curl of polarization vectors by an irrotational electric field. Phys. Rev. B 94, 100103 (2016).
Morozovska, A. N. et al. Flexocoupling impact on size effects of piezoresponse and conductance in mixedtype ferroelectric semiconductors under applied pressure. Phys. Rev. B 94, 174101 (2016).
Catalan, G. et al. Flexoelectric rotation of polarization in ferroelectric thin films. Nat. Mater. 10, 963–967 (2011).
Lee, D. et al. Giant flexoelectric effect in ferroelectric epitaxial thin films. Phys. Rev. Lett. 107, 057602 (2011).
Chen, Z., Huang, G., Trase, I., Han, X. & Mei, Y. Mechanical selfassembly of a strainengineered flexible layer: wrinkling, rolling, and twisting. Phys. Rev. Appl. 5, 017001 (2016).
Nagarajan, V. et al. Misfit dislocations in nanoscale ferroelectric heterostructures. Appl. Phys. Lett. 86, 192910 (2005).
Borisevich, A. Y. et al. Atomicscale evolution of modulated phases at the ferroelectric–antiferroelectric morphotropic phase boundary controlled by flexoelectric interaction. Nat. Commun. 3, 775 (2012).
Chu, K. et al. Enhancement of the anisotropic photocurrent in ferroelectric oxides by strain gradients. Nat. Nanotechnol. 10, 972–979 (2015).
Lebeugle, D., Colson, D., Forget, A. & Viret, M. Very large spontaneous electric polarization in BiFeO_{3} single crystals at room temperature and its evolution under cycling fields. Appl. Phys. Lett. 91, 022907 (2007).
Kim, D. H., Lee, H. N., Biegalski, M. D. & Christen, H. M. Effect of epitaxial strain on ferroelectric polarization in multiferroic BiFeO_{3} films. Appl. Phys. Lett. 92, 012911 (2008).
Daumont, C. et al. Strain dependence of polarization and piezoelectric response in epitaxial BiFeO_{3} thin films. J. Phys. Condens Matter 24, 162202 (2012).
Lee, D. et al. Mixed BlochNéelIsing character of 180° ferroelectric domain walls. Phys. Rev. B 80, 060102 (2009).
Morozovska, A. N., Eliseev, E. A., Bravina, S. L. & Kalinin, S. V. Resolutionfunction theory in piezoresponse force microscopy: Wall imaging, spectroscopy, and lateral resolution. Phys. Rev. B 75, 174109 (2007).
Huang, F.T. & Cheong, S.W. Aperiodic topological order in the domain configurations of functional materials. Nat. Rev. Mater. 2, 17004 (2017).
Wang, J. et al. Epitaxial BiFeO_{3} multiferroic thin film heterostructures. Science 299, 1719–1722 (2003).
Jeon, B. C. et al. Flexoelectric effect in the reversal of selfpolarization and associated changes in the electronic functional properties of BiFeO_{3} thin films. Adv. Mater. 25, 5643–5649 (2013).
Xue, F., Gu, Y., Liang, L., Wang, Y. & Chen, L.Q. Orientations of lowenergy domain walls in perovskites with oxygen octahedral tiles. Phys. Rev. B 90, 220101 (2014).
Karpinsky, D. V. et al. Thermodynamic potential and phase diagram for multiferroic bismuth ferrite (BiFeO_{3}). NPJ Comput. Mater. 3, 20 (2017).
Chen, L.Q. & Shen, J. Applications of semiimplicit Fourierspectral method to phase field equations. Comput. Phys. Commun. 108, 147–158 (1998).
Zhang, J. et al. Threedimensional phasefield simulation of domain structures in ferroelectric islands. Appl. Phys. Lett. 92, 122906 (2008).
Williamson, G. K. & Hall, W. H. Xray line broadening from filed aluminium and wolfram. Acta Metall. 1, 22–31 (1953).
Catalan, G., Noheda, B., McAneney, J., Sinnamon, L. J. & Gregg, J. M. Strain gradients in epitaxial ferroelectrics. Phys. Rev. B 72, 020102 (2005).
Parratt, L. G. Surface studies of solids by total reflection of xrays. Phys. Rev. 95, 359–369 (1954).
Acknowledgements
This work was supported by the National Research Foundation (NRF) Grant funded by the Korean Government via the Creative Research Initiative Center for Lattice Defectronics (2017R1A3B1023686) and the Center for Quantum Coherence in Condensed Matter (2016R1A5A1008184). Xray studies were carried out at the Pohang Accelerator Laboratory. This work was also supported by the Global Frontier R&D Program on Center for Hybrid Interface Materials (HIM) funded by the Ministry of Science, ICT & Future Planning (2013M3A6B1078872). The work at Penn State was supported by the U.S. Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering under Award FG0207ER46417 (F.X. and L.Q.C.) and by the Penn State MRSEC, Center for Nanoscale Science, under the award NSF DMR1420620 (F.X.).
Author information
Authors and Affiliations
Contributions
K.E.K. and C.H.Y. conceived and designed the project. K.E.K. and S.J. prepared samples. K.E.K., S.J. and K.C. measured and analysed the angleresolved PFM with the winding number calculation. J.H.L and T.Y.K. performed structural analysis by Xray diffraction. G.Y.K. and S.Y.C. carried out STEM. F.X. and L.Q.C. performed phase field simulation. K.E.K., R.R. and C.H.Y. led manuscript preparation with contributions from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kim, KE., Jeong, S., Chu, K. et al. Configurable topological textures in strain graded ferroelectric nanoplates. Nat Commun 9, 403 (2018). https://doi.org/10.1038/s41467017028135
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467017028135
This article is cited by

Electricfieldinduced multiferroic topological solitons
Nature Materials (2024)

Absence of critical thickness for polar skyrmions with breaking the Kittel’s law
Nature Communications (2023)

Polar Solomon rings in ferroelectric nanocrystals
Nature Communications (2023)

Phase field modeling of topological magnetic structures in ferromagnetic materials: domain wall, vortex, and skyrmion
Acta Mechanica (2023)

Ferroelectric domainwall logic units
Nature Communications (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.