Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Light-tuned selective photosynthesis of azo- and azoxy-aromatics using graphitic C3N4


Solar-driven photocatalysis has attracted significant attention in water splitting, CO2 reduction and organic synthesis. The syntheses of valuable azo- and azoxyaromatic dyes via selective photoreduction of nitroaromatic compounds have been realised using supported plasmonic metal nanoparticles at elevated temperatures (≥90 °C); however, the high cost, low efficiency and poor selectivity of such catalyst systems at room temperature limit their application. Here we demonstrate that the inexpensive graphitic C3N4 is an efficient photocatalyst for selective syntheses of a series of azo- and azoxy-aromatic compounds from their corresponding nitroaromatics under either purple (410 nm) or blue light (450 nm) excitation. The high efficiency and high selectivity towards azo- and azoxy-aromatic compounds can be attributed to the weakly bound photogenerated surface adsorbed H-atoms and a favourable N-N coupling reaction. The results reveal financial and environmental potential of photocatalysis for mass production of valuable chemicals.


Azo- and azoxyaromatic compounds are very important and precious precursors for the dye-, electronic-, pigment-, and drug industries1. Traditional industrial syntheses of azo- and azoxy-aromatic compounds are realised by diazotisation (yields >70%). The process is costly and environmentally unfriendly, due to the formation of unstable intermediate diazo compounds and harsh process conditions (involving strict temperature control and the use of corrosive acids)2,3. In a more environmentally friendly approach, azo compounds can be obtained via aerobic oxidation of amines by heterogeneous catalysis, but this requires supported noble metal catalysts or expensive oxidants, which limits large-scale applications4,5.

Heterogeneous photocatalysis shows great potential in driving several important reactions (i.e., water splitting, CO2 reduction, and organic synthesis), and the technology has therefore attracted significant attention over the last decades6,7,8,9,10. Recent development of the graphitic C3N4 (g-C3N4) has further boosted the fundamental research and industrial potential of photocatalysis, as this inexpensive, metal-free material exhibits reasonable catalytic performance and stability under visible light irradiation conditions11,12,13,14,15.

A number of studies have reported on the photoreduction of nitroaromatic compounds, either by inorganic semiconductor photocatalysts or by the supported plasmonic metal nanoparticles (NPs), as shown in (Table 1)16,17,18,19,20,21,22,23,24. The photocatalyst producing azo- or azoxy-compounds at low temperatures typically contains a precious metal. For example, a rhodium containing photocatalyst (SiO2/CdS/Rh) converts nitrobenzene selectively to azoxybenzene under visible light irradiation18. However, in addition to the low efficiency and poor selectivity, the use of the unstable and toxic CdS photocatalyst makes this process unfavourable for industrial applications (Table 1, entry 1). Azobenzene can be successfully synthesised at room temperature (RT) by using a Au supported TiO2 photocatalyst (Table 1, entry 2)19. A recent study has demonstrated that selective photosynthesis of azobenzene can also be realised at elevated temperature (90 °C), by using a cheaper metal (Cu) supported on graphene (Table 1, entry 3)17,20. However, since the nitrobenzene reduction can be initiated at 80 °C without any catalyst (poor activity and selectivity)21, the use of an expensive graphene support in a reaction that is inefficient at RT, affects its commercial potential negatively. In addition, the supported plasmonic metal nanoparticle based photocatalysts (i.e., Au, Ag, and Cu) show a relatively poor efficiency for light absorption compared to their semiconductor counterpart, and the particle size of the metal would have to be controlled strictly to absorb photons with the desired energies25. Instead of azo- and azoxy-compounds, amines, i.e. the fully hydrogenated lower-value products, were reported as the main products in many studies when using conventional semiconductor photocatalysts such as TiO2 and CdS (Table 1, entries 4–6)22,23,24.

Table 1 Possible products formed by photocatalytic reduction of nitroaromatic compounds and comparison of the conversion and selectivity of different photocatalysts

Up to now, it has been challenging to realise efficient photosynthesis of azo- and azoxy-aromatic compounds with controlled selectivity at RT without producing amines. Herein, we show that both azoxybenzene and azobenzene can be synthesised by photoreduction of nitrobenzene with high selectivity using the cheap graphitic C3N4 (g-C3N4, <0.1 $ g−1 on lab-scale) as photocatalyst at RT. The selectivity can be simply controlled by the irradiation wavelength. We estimate the turn over number (TON) to be ~8600 per surface active site (i.e., the two-coordinated N) over the reaction time, suggesting that the process is catalytic.


Lab-scale nitrobenzene conversion

As described in Table 1, the selective conversion of nitrobenzene to azobenzene and azoxybenzene can be controlled by the irradiation wavelength (450 and 410 nm, entry 7 and 8). Surprisingly, an amorphous graphitic C3N4 compound (A-g-C3N4) characterised by a larger specific surface area (112 m2 g−1) compared to that of g-C3N4 (49 m2 g−1) shows a negligible performance in photocatalytic nitrobenzene reduction under similar reaction conditions (Table 1, entry 9).

Under 410 nm irradiation, azobenzene is gradually formed in a two-step reduction reaction; firstly, nitrobenzene is converted to azoxybenzene, which is then subsequently reduced to azobenzene (Fig. 1a). In contrast, azoxybenzene has been found to be the main product throughout the 450 nm irradiation course (Fig. 1b). Under both irradiation conditions, the nitrobenzene reduction can reach high conversion (>95%) with high selectivity (>94%) without the formation of aniline. We estimate that the quantum efficiencies (QE) are 1.4 and 0.4% for the synthesis of azobenzene and azoxybenzene under 410 and 450 nm irradiation, respectively (Supplementary Equations 1 and 2). It should be noted that such QEs are relatively high considering that the reactions involve 6e and 8e charge transfer processes, respectively, to achieve azoxy- and azobenzene. We also observed that the selectivity to aniline remains very low (≤5%) even under UV irradiation until most nitrobenzene molecules (>82%) had been converted (Supplementary Table 1).

Fig. 1

Photocatalytic performance. a, b Photoconversion (Con.) and selectivity (Sel.) of nitrobenzene to azobenzene and azoxybenzene using g-C3N4 under 410 and 450 nm irradiation (lab-scale). c Photoconversion of nitrobenzene to azoxybenzene using g-C3N4 at different starting concentrations under 450 nm irradiation. Reaction conditions: 8 mM nitrobenzene, 10 mM KOH, and 50 mg catalyst in 10 mL isopropanol under N2 atmosphere. d, e Up-scaled reactions with volumes of 800 mL and 80 L, respectively. The nitrobenzene photoconversion tests were performed under solar radiation in Beijing (30/9/2016-2/10/2016, 25-30 °C, 800 mL) and Shenzhen (18/12/2016-5/1/2017, 25–30 °C, 80 L). The starting concentration of nitrobenzene was 8 mM. f, g Conversion and selectivity for the scaled-up tests


The photoconversion of nitrobenzene into the value-added azoxybenzene by using the g-C3N4 photocatalyst shows a huge potential for scaling-up to industrial level, both in terms of the nitrobenzene starting concentration and the reaction volume. As shown in Fig. 1c, the high selectivity and conversion observed at low nitrobenzene concentration (8 mM) are maintained at higher nitrobenzene concentrations (24 and 40 mM) under identical reaction conditions. We observed that prolonged irradiation times are required to reach full conversion (12, 60, and 168 h, for 8, 24, and 40 mM of nitrobenzene, respectively), which may be caused by the reduction of light transmission to the photocatalyst due to the increased light absorption of azoxybenzene.

Figure 1d and e depict the reactions scaled-up in volume (to 0.8 and 80 L corresponding to an 80 and 8000-fold volume increase compared to the lab-scale reactions) performed under solar irradiation (i.e., without the use of artificial light sources). The yellow catalyst suspension gradually turned orange, indicating the formation of azo- and azoxybenzene. The colour change of the liquid caused by the formation of azo- and azoxybenzene was even more obvious after centrifugation. Gas chromatography (GC) analysis reveals that the high selectivity (~ 90%) towards azoxybenzene was achieved for both up-scaled tests (Fig. 1f and g). The solar irradiation favours the formation of the same compound as that formed under blue light irradiation (450 nm, azoxybenzene), which suggests that the reduction of nitrobenzene to azoxybenzene is more favourable than that of the conversion of azoxybenzene to azobenzene. The formation of azobenzene will only take place when nitrobenzene has been fully converted to azoxybenzene. We estimate the QE of the 8000-fold scaled-up test to be 1.9% (see Fig. 1f, g and Supplementary Figs 6 and 7). The higher QE observed for the scaled-up test than that of the lab-scale experiment can be associated to with utilisation of the UV light in the solar spectrum (300–400 nm). We also observed that the conversion increased steadily with irradiation time in both up-scaled experiments with a similar rate (Fig. 1f and g). This suggests a strong photostability of the g-C3N4 and that scaling-up only has a negligible effect on the performance, which most likely allows the reactions to be even further scaled-up for industrial applications. We notice a relatively low conversion (~ 60%) for both scaled-up reactions, which may be caused by the accumulation of azoxybenzene that blocks the light absorption of the g-C3N4 photocatalyst. Further optimisation of the reactor design could possibly solve this technique issue (i.e., by using a flow cell or shorter light path length).

Photoconversion of other nitroaromatic compounds

By tuning the irradiation wavelength of the light sources, we have f`urther demonstrated the versatility of the g-C3N4 catalyst for controlled photoconversion of various nitroaromatic compounds into their corresponding azoxy- or azo-compounds (Table 2). The compounds p,p′-dichloro-, p,p′-dibromo-, and p,p′-iodo- azo- and azoxybenzene can be synthesised with excellent conversion and selectivity from the p-chloro-, p-bromo-, and p-iodo nitrobenzene, respectively (Table 2, entries 1–6). Likewise, the o,o′-dichloro- and m,m′-dichloro- substituted azo- and azoxybenzene can also be selectively synthesised from the corresponding o-chloro nitrobenzene and m-chloro nitrobenzene (Table 2, entries 7–10). Furthermore, the photoconversion of p-nitrotoluene, p-nitroanisole and p-nitrobenzotrifluoride into their corresponding azo- and azoxybenzene can also be achieved with very high conversion and selectivity in a controlled manner (Table 2, entries 11–16). We have also examined the photo-conversion of four di-substituted nitrobenzene precursors (p-Cl, m-F; p-Cl, m-CF3; p-CH3, m-CH3; and p-CF3, m-CF3) (Table 2, entry 17–24). All of these di-substituted nitroaromatic compounds can be converted into their corresponding azo- and azoxy-aromatic products with high selectivity, indicating that more complicated azoxy- and azo-aromatic compounds can be synthesised via this approach. In addition, the photosynthesis of asymmetric azobenzenes can also be realised with a reasonable selectivity (Supplementary Table 6).

Table 2 Photocatalytic reduction of various nitroaromatic compounds to azoxy- (I) and azo- (II) aromatic compounds using the g-C3N4 photocatalyst

Reaction mechanism

We propose that the excellent performance of the g-C3N4 photocatalyst for nitrobenzene photoreductions can be associated with the efficient utilisation of photogenerated electrons for the reduction reaction. This has been revealed by mechanistic studies of the reduction of O2 by using in-situ mass spectrometry (MS, Fig. 2a). Under deaerated conditions, the remaining oxygen that was dissolved in the catalyst-isopropanol suspension was reduced rapidly under 450 nm LED irradiation when using the g-C3N4 photocatalyst, whereas the A-g-C3N4 sample and pristine TiO2 (Degussa Aeroxide® P25) showed much slower rates in O2 depletion. We have further rationalised that such efficient reduction can be linked to the adsorption energy of the surface adsorbed hydrogen atoms (Hads) that was generated by isopropanol oxidation during irradiation, as probed by post-mortem temperature programmed desorption (TPD, Fig. 2b and Supplementary Fig. 12). The pre-irradiated (3 h under reaction-like conditions without nitrobenzene) and subsequently vacuum dried g-C3N4 sample showed no H2 desorption peak. This indicates that Hads is only adsorbed weakly on the catalyst surface, enabling it to react rapidly with the surface adsorbed nitrobenzene to form azo- or azoxy-benzene (Fig. 2c). In contrast, the A-g-C3N4 prepared identically showed two H2 desorption peaks, suggesting a relatively strong adsorption of the photogenerated Hads on A-g-C3N4, which prevents the use of the Hads for efficient reduction reactions. The in-situ X-ray photoelectron spectroscopy analysis (XPS, Supplementary Fig. 13) also confirms that the Hads binds strongly on the A-g-C3N4 surface, resulting in a significant shift of the N1s peak. In contrast, the N1s peak of g-C3N4 remains unchanged upon irradiation, indicating that the Hads only loosely binds to the g-C3N4 surface, thus, making the catalyst ideal for the nitrobenzene reduction (Supplementary Fig. 13). In addition, the N1s peak intensity also remains unchanged, indicating that nitrogen does not leach out from the g-C3N4 catalyst. Furthermore, the g-C3N4 shows a significantly higher photocurrent compared to that of A-g-C3N4, indicating that the charge separation is also promoted by the ordered structure of g-C3N4 (Supplementary Fig. 14).

Fig. 2

Reaction mechanism analysis. a The consumption of dissolved O2 (O2 reduction and isopropanol oxidation) under irradiation using various photocatalysts determined by in-situ MS. A 365 nm LED was used for TiO2 and a 450 nm LED was used for all other tests. b Post-mortem TPD spectra revealing the desorption of Hads from the g-C3N4 and A-g-C3N4 surfaces. The TPD was performed on vacuum dried samples after reaction without adsorption of additional H2. c Scheme of the suggested reaction pathway. The reduction reaction will be hindered if Hads binds strongly to the catalyst. d Reaction path for the photoconversion of nitroaromatic compounds to azoxy-, azo-aromatic compounds, and amines. NBS = Nitrosobenzene, NPH = N-phenylhydroxylamine

We have further explored the orgin behind the high selectivity of the nitroaromatic photoconversion into azoxy- or azo-aromatics by probing the photo reaction of the intermediates (Fig. 2d and Supplementary Table 4). Since all reactions were performed under deaerated conditions, we have ruled out the pathway involving initial reduction to aniline followed by partial oxidation to azo-/azoxy benzene. This has been also confirmed experimentally by a control reaction starting with aniline, where no N-N coupling products were formed under irradiation. According to previous mechanistic studies, nitrobenzene undergoes a gradual photoreduction process during which nitrosobenzene (NBS) and N-phenylhydroxylamine (NPH) are initially formed27,28. The NBS and NPH will then be further reduced to azoxy- and azo-aromatics via path (I) or to amines via path (II). The as-formed azo-aromatics may also get photoreduced into amines via path (III). We have observed that the photoreduction of NBS or of an NBS/NPH mixture (1:1 in molar ratio) results exclusively in the formation of azo- and azoxybenzene (conversion >97%) when g-C3N4 was used as photocatalyst. In contrast, the photoreduction of NBS exhibits a non-selective behaviour when TiO2 was used as photocatalyst ([azobenzene + azoxybenzene]: amine = 44:56). The presence of NPH in the reaction (NBS: NPH = 1:1) further drives the reaction to favour the formation of the amine ([azobenzene + azoxybenzene]: amine = 18:82). Surprisingly, the photoreduction of azobenzene to amine (path III) has been found to be inactive for both g-C3N4 and TiO2. These control experiments suggest that the g-C3N4 photocatalyst facilitates the N−N coupling of NBS and NPH (path I) and inhibits the reduction of NBS and NPH (path II), thus resulting in a high selectively of the nitroaromatic photoconversion into azo- and azoxy-aromatic products. Since the affinity of the aromatic molecules can be enhanced by π−π coupling effect of the tri-s-trazine unit in g-C3N4 29,30, we consider that the photogenerated NBS and NPH are co-adsorbed on the g-C3N4 surface, thus, promoting the N-N coupling for the formation of azo- and azoxycompounds (path I). In contrast, other photocatalysts (i.e., TiO2) without such π–π bonding interaction possibly facilitates the reduction via path (II) to form amines.


The redox potentials of isopropanol/acetone and nitrobenzene/azoxybenzene, respectively, are ~0.1 and −0.8 V as referenced to the standard hydrogen electrode (SHE)31,32. Therefore, the photoexcited e in the conduction band (CB) of g-C3N4 is energetically favourable to initiate the nitrobenzene reduction, as depicted in Fig. 3a. Meanwhile, the isopropanol that serves as the electron donor will be oxidised into acetone, resulting in the formation of two protons and the injection of two electrons into the valence band (VB) to fill the hole (h+). Since previous calculations reveal that the highest occupied molecular orbital (HOMO, equivalent to the VB) of the g-C3N4 mainly originates from the p-orbital of the two-coordinated N atoms, it is reasonable to speculate that the oxidation of isopropanol takes place on these sites (Fig. 3b)33. It should also be noted that the negatively charged surface of g-C3N4 under basic conditions34 is beneficial for the deprotonation of isopropanol, thus, an improved nitrobenzene conversion is expected due to the enhanced isopropanol oxidation.

Fig. 3

Proposed reaction mechanisms. a Energy scheme of the photocatalytic nitrobenzene reduction on g-C3N4. The redox potentials of nitrobenzene (NB) to azoxybenzene plus isopropanol (IP) to acetone (AC), and the CB and VB positions are referenced to the SHE32,33. b and c suggested possible active sites for isopropanol oxidation and nitrobenzene reduction according to calculations. Grey: C, light purple: N, white: structural H, light blue: surface adsorbed H (Hads)

We have further explored the possible active sites for the nitrobenzene reduction reaction by employing semi-empirical MOPAC2016 calculations, to estimate the relative adsorption energies of H pairs (two H atoms) on a model crystalline g-C3N4 structure consisting of two H-bonded strips with 6 melem units (Supplementary Fig. 15). Since the nitrobenzene reduction requires removal of oxygen by two H atoms through the formation of H2O, we have evaluated the relative stability of adsorbed H pairs to see if they will identify any significant sites for the reduction. In general, the H-atom pairs are found to be less stable on the crystalline g-C3N4 surface (∆G H > 0) compared to free H2, which agrees well with our post-mortem TPD results (Supplementary Table 5). The H pairs prefer to be adsorbed close to each other instead of further apart on the same melem unit, and the most stable adsorption sites are found to be the C-N bond adjacent to a bridging N atom (~ 0.5 eV) and the two-coordinated N atoms in the same ring adjacent to the bridging N atoms between melem units (~ 0.9 eV), as indicated in the Fig. 3(c). Therefore, we speculate that these possible hydrogen adsorption sites are the active sites for the nitrobenzene reduction. In addition, we found that the C-N binding configuration upon H adsorption becomes more stable when occurring on the corner melem unit, where it is only 0.1 eV less stable than free H2. This could point to even more highly labile H2 adsorption sites at the edges of the melem strips in real g-C3N4. A list of selected adsorption energies are provided in Supplementary Table 5.

Herein, we report on a photocatalytic strategy for controllable and efficient synthesis of a series of industrially important azo- and azoxy-aromatic compounds from their corresponding nitroaromatic precursors under visible light irradiation at RT. The g-C3N4 photocatalyst facilitates the light driven N-N coupling of the nitroaromatics, and the weakly adsorbed photogenerated Hads atoms contribute to the excellent catalytic performance in the multi-electron transfer process. We anticipate that the possibility of scaling-up the reaction with respect to both concentration and volume, and the use of the inexpensive g-C3N4 photocatalyst makes the reaction attractive for industrial applications.


Sample preparations

The g-C3N4 photocatalyst was synthesised via conventional pyrolysis of urea at 550 °C35, and the A-g-C3N4 sample was obtained by post heating of the g-C3N4 at 630 °C (Supplementary Fig. 1).

Price estimation of the photocatalysts

The prices of photocatalysts listed in Table 1 were estimated according to the catalyst compositions presented in the cited studies (Supplementary Table 2).

Materials characterisations

Transmission electron microscopy (TEM), N2 adsorption-desorption isotherm, X-ray photoelectron spectroscopy (XPS), X-ray diffractometry (XRD), and diffuse reflectance spectrometry (DRS) were used for material characterisation (Supplementary Figs 811 and Supplementary Table 3). In-situ XPS and post-mortem TPD were performed to analyse the oxidation state change of N and the bond strength of the Hads to the catalyst surface under reaction conditions (Supplementary Figs 12 and 13). MS (Supplementary Figs 4 and 5) and gas chromatography (GC) were used to investigate the reaction mechanism.

Photocatalytic process analysis

A home-built vacuum-gas line was used to perform the photocatalytic reactions (Supplementary Figs 2 and 3). GC was used to determine the concentrations of the reactants and the products.


The semi-empirical molecular orbital geometry optimisations were performed in MOPAC2016, all using the PM7 Hamiltonian (Supplementary Fig. 15 and Supplementary Table 5)36. All details can be found in the Supplementary Methods and Supplementary Discussion.

Data availability

The data that support the findings of this study are available from the corresponding author upon request.


  1. 1.

    Egli, R. The Design and Synthesis of Organic Dyes and Pigments (Elsevier, Amsterdam, 1991).

  2. 2.

    Clarke, H. T. & Kirner, W. R. METHYL RED. Org. Synth. 2, 47 (1922).

    Article  Google Scholar 

  3. 3.

    Dabbagh, H. A., Teimouri, A. & Chermahini, A. N. Green and efficient diazotization and diazo coupling reactions on clays. Dyes Pigm. 73, 239–244 (2007).

    CAS  Article  Google Scholar 

  4. 4.

    Grirrane, A., Corma, A. & García, H. Gold-catalyzed synthesis of aromatic azo compounds from anilines and nitroaromatics. Science 322, 1661–1664 (2008).

    ADS  CAS  Article  PubMed  Google Scholar 

  5. 5.

    Acharyya, S. S., Ghosh, S. & Bal, R. Catalytic oxidation of aniline to azoxybenzene over CuCr2O4 spinel nanoparticle catalyst. ACS Sustain. Chem. Eng. 2, 584–589 (2014).

    CAS  Article  Google Scholar 

  6. 6.

    Terrett, J. A., Cuthbertson, J. D., Shurtleff, V. W. & MacMillan, D. W. C. Switching on elusive organometallic mechanisms with photoredox catalysis. Nature 524, 330–334 (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  7. 7.

    Chang, X., Wang, T. & Gong, J. CO2 photo-reduction: insights into CO2 activation and reaction on surfaces of photocatalysts. Energy Environ. Sci. 9, 2177–2196 (2016).

    CAS  Article  Google Scholar 

  8. 8.

    Wang, Q. et al. Scalable water splitting on particulate photocatalyst sheets with a solar-to-hydrogen energy conversion efficiency exceeding 1%. Nat. Mater. 15, 611–615 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  9. 9.

    Schultz, D.M. & Yoon, T.P. Solar Synthesis: Prospects in Visible Light Photocatalysis. Science 343, 6174 (2014).

    Article  Google Scholar 

  10. 10.

    Corrigan, N., Shanmugam, S., Xu, J. & Boyer, C. Photocatalysis in organic and polymer synthesis. Chem. Soc. Rev. 45, 6165–6212 (2016).

    CAS  Article  PubMed  Google Scholar 

  11. 11.

    Wen, J., Xie, J., Chen, X. & Li, X. A review on g-C3N4-based photocatalysts. Appl. Surf. Sci. 391, 72–123 (2017).

    ADS  CAS  Article  Google Scholar 

  12. 12.

    Lau, V. W.-h. et al. Rational design of carbon nitride photocatalysts by identification of cyanamide defects as catalytically relevant sites. Nat. Commun. 7, 12165 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  13. 13.

    Lu, J. et al. Order–disorder transition in a two-dimensional boron–carbon–nitride alloy. Nat. Commun. 4, 2681 (2013).

    PubMed  Google Scholar 

  14. 14.

    Wu, G. et al. Graphitic carbon nitride nanosheet electrode-based high-performance ionic actuator. Nat. Commun. 6, 7258 (2015).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  15. 15.

    Cao, S., Low, J., Yu, J. & Jaroniec, M. Polymeric photocatalysts based on graphitic carbon nitride. Adv. Mater. 27, 2150–2176 (2015).

    CAS  Article  PubMed  Google Scholar 

  16. 16.

    Guo, X., Hao, C., Jin, G., Zhu, H.-Y. & Guo, X.-Y. Copper nanoparticles on graphene support: an efficient photocatalyst for coupling of nitroaromatics in visible light. Angew. Chem. Int. Ed. 53, 1973–1977 (2014).

    CAS  Article  Google Scholar 

  17. 17.

    Zhu, H., Ke, X., Yang, X., Sarina, S. & Liu, H. Reduction of nitroaromatic compounds on supported gold nanoparticles by visible and ultraviolet light. Angew. Chem. Int. Ed. 49, 9657–9661 (2010).

    CAS  Article  Google Scholar 

  18. 18.

    Pal, B., Torimoto, T., Okazaki, K.-I. & Ohtani, B. Photocatalytic syntheses of azoxybenzene by visible light irradiation of silica-coated cadmium sulfide nanocomposites. Chem. Commun. 5, 483–485 (2007).

    Article  Google Scholar 

  19. 19.

    Naya, S.-i, Niwa, T., Kume, T. & Tada, H. Visible-light-induced electron transport from small to large nanoparticles in bimodal gold nanoparticle-loaded titanium (IV) oxide. Angew. Chem. Int. Ed. 53, 7305–7309 (2014).

    CAS  Article  Google Scholar 

  20. 20.

    Ke, X. et al. Selective reductions using visible light photocatalysts of supported gold nanoparticles. Green. Chem. 15, 236–244 (2013).

    CAS  Article  Google Scholar 

  21. 21.

    Gund, S. H., Shelkar, R. S. & Nagarkar, J. M. An efficient catalyst-free and chemoselective synthesis of azobenzenes from nitrobenzenes. RSC Adv. 4, 42947–42951 (2014).

    CAS  Article  Google Scholar 

  22. 22.

    Shiraishi, Y., Togawa, Y., Tsukamoto, D., Tanaka, S. & Hirai, T. Highly efficient and selective hydrogenation of nitroaromatics on photoactivated rutile titanium dioxide. ACS Catal. 2, 2475–2481 (2012).

    CAS  Article  Google Scholar 

  23. 23.

    Gao, W.-Z., Xu, Y., Chen, Y. & Fu, W.-F. Highly efficient and selective photocatalytic reduction of nitroarenes using the Ni2P/CdS catalyst under visible-light irradiation. Chem. Commun. 51, 13217–13220 (2015).

    CAS  Article  Google Scholar 

  24. 24.

    Tanaka, A. et al. Functionalization of a plasmonic Au/TiO2 photocatalyst with an Ag co-catalyst for quantitative reduction of nitrobenzene to aniline in 2-propanol suspensions under irradiation of visible light. Chem. Commun. 49, 2551–2553 (2013).

    CAS  Article  Google Scholar 

  25. 25.

    Langhammer, C., Kasemo, B. & Zorić, I. Absorption and scattering of light by Pt, Pd, Ag, and Au nanodisks: absolute cross sections and branching ratios. J. Chem. Phys. 126, 194702 (2007).

    ADS  Article  PubMed  Google Scholar 

  26. 26.

    Fuldner, S. et al. Green-light photocatalytic reduction using dye-sensitized TiO2 and transition metal nanoparticles. Green. Chem. 12, 400–406 (2010).

    Article  Google Scholar 

  27. 27.

    Maldotti, A. et al. Photochemical and photocatalytic reduction of nitrobenzene in the presence of cyclohexene. J. Photochem. Photobiol. A 133, 129–133 (2000).

    CAS  Article  Google Scholar 

  28. 28.

    Brezová, V., Tarábek, P., Dvoranová, D., Staško, A. & Biskupič, S. EPR study of photoinduced reduction of nitroso compounds in titanium dioxide suspensions. J. Photochem. Photobiol. A 155, 179–198 (2003).

    Article  Google Scholar 

  29. 29.

    Goettmann, F., Fischer, A., Antonietti, M. & Thomas, A. Chemical synthesis of mesoporous carbon nitrides using hard templates and their use as a metal-free catalyst for friedel–crafts reaction of benzene. Angew. Chem. Int. Ed. 45, 4467–4471 (2006).

    CAS  Article  Google Scholar 

  30. 30.

    Goettmann, F., Thomas, A. & Antonietti, M. Metal-free activation of CO2 by mesoporous graphitic carbon nitride. Angew. Chem. Int. Ed. 46, 2717–2720 (2007).

    CAS  Article  Google Scholar 

  31. 31.

    Al-Azri, Z. H. N. et al. The roles of metal co-catalysts and reaction media in photocatalytic hydrogen production: Performance evaluation of M/TiO2 photocatalysts (M=Pd, Pt, Au) in different alcohol–water mixtures. J. Catal. 329, 355–367 (2015).

    CAS  Article  Google Scholar 

  32. 32.

    Gronchi, G., Courbis, P., Tordo, P., Mousset, G. & Simonet, J. Spin trapping in electrochemistry. Non-aqueous electrochemical behavior of nitroso spin traps. J. Phys. Chem. 87, 1343–1349 (1983).

    CAS  Article  Google Scholar 

  33. 33.

    Lau, V. W.-h et al. Low-molecular-weight carbon nitrides for solar hydrogen evolution. J. Am. Chem. Soc. 137, 1064–1072 (2015).

    CAS  Article  PubMed  Google Scholar 

  34. 34.

    Zhu, B., Xia, P., Ho, W. & Yu, J. Isoelectric point and adsorption activity of porous g-C3N4. Appl. Surf. Sci. 344, 188–195 (2015).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Liu, J., Zhang, T., Wang, Z., Dawson, G. & Chen, W. Simple pyrolysis of urea into graphitic carbon nitride with recyclable adsorption and photocatalytic activity. J. Mater. Chem. 21, 14398–14401 (2011).

    CAS  Article  Google Scholar 

  36. 36.

    Stewart, J. J.P. MOPAC2016, Stewart Computational Chemistry (Colorado Springs, CO, USA, 2016) (Last accessed October, 2016).

Download references


R.S. would like to thank the NSFC for financial support (projects number: 21503257 and 21601198). Y.D. would like to thank the Sino-Danish Centre (SDC) for the Ph.D Scholarship. N.L. acknowledges the Villum Foundation Young Investigator Programme (VKR023449) and the Danish National Research Foundation (Carbon Dioxide Activation Centre, DNRF 118). We acknowledge the support from the Carlsberg Foundation, and we would like to thank Dr. Yi Wang, Dr. Yifeng Yun, and Ms. Yiling Bai from Synfuels China Technology Co. Ltd. for the TEM and TPD analysis. We thank Dr. Chao Wang from Shenzhen University for providing space to perform the upscaled reaction.

Author information




Y.D., R.S., and N.L. conceived the studies. Y.D., C.L., and Y.S. synthesised the samples. Y.D. and C.L. performed the photocatalytic tests. Y.D., C.L., N.L., and R.S. carried out the material characterisation. T.L. performed the calculations. J.X., Y.L., H.N., and F.B. were involved in the design of the experiments, the discussion of the results, and the writing up of the manuscript.

Corresponding authors

Correspondence to Nina Lock or Ren Su.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Dai, Y., Li, C., Shen, Y. et al. Light-tuned selective photosynthesis of azo- and azoxy-aromatics using graphitic C3N4 . Nat Commun 9, 60 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links