Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Hydrodeoxygenation of water-insoluble bio-oil to alkanes using a highly dispersed Pd–Mo catalyst


Bio-oil, produced by the destructive distillation of cheap and renewable lignocellulosic biomass, contains high energy density oligomers in the water-insoluble fraction that can be utilized for diesel and valuable fine chemicals productions. Here, we show an efficient hydrodeoxygenation catalyst that combines highly dispersed palladium and ultrafine molybdenum phosphate nanoparticles on silica. Using phenol as a model substrate this catalyst is 100% effective and 97.5% selective for hydrodeoxygenation to cyclohexane under mild conditions in a batch reaction; this catalyst also demonstrates regeneration ability in long-term continuous flow tests. Detailed investigations into the nature of the catalyst show that it combines hydrogenation activity of Pd and high density of both Brønsted and Lewis acid sites; we believe these are key features for efficient catalytic hydrodeoxygenation behavior. Using a wood and bark-derived feedstock, this catalyst performs hydrodeoxygenation of lignin, cellulose, and hemicellulose-derived oligomers into liquid alkanes with high efficiency and yield.


Decreasing petroleum deposits combined with conversely climbing global demand and environmental concern makes it critical to develop fuel and chemical production processes based on renewable resources1. Lignocellulosic biomass, including cellulose, hemicellulose, and lignin, is the most abundantly available and cost-effective carbon reservoir that can be used to produce renewable fuel and high added-value chemicals2. Compared with biomass fractionation, which requires extensive pre-treatment and following hydrolysis, flash pyrolysis is a cheaper process for the production of upgradable bio-oil from lignocellulose, and offers potential for lignin utilization3, 4. However, the bio-oil also contains high oxygen content (up to 60 wt%) and necessitates further catalytic upgrading, preferably via hydrodeoxygenation (HDO), before use in hydrocarbon fuel or chemical production5. The water soluble fraction of bio-oil mainly involves carbohydrates that could be catalytically converted into hydroxymethylfurfural6, 7, levulinic acid8, and monofunctional hydrocarbons9, 10; these platform chemicals can be further converted to hydrocarbons via HDO. By comparison, the water-insoluble bio-oil (WIBO) often contains a large variety of products derived from lignin, cellulose, and hemicellulose in the form of oligomers with molecular weight up to 5000 Da5. The complexity of WIBO composition and the chemical inertness of the oligomers present therefore pose a great challenge for any HDO catalyst.

In recent years, bifunctional metal-acid catalysts have been developed, showing high efficiency in HDO reaction for hydrocarbon fuel production from lignin11,12,13,14,15,16,17. Lercher and co-workers have made important contributions on the design of an efficient combination of metal-catalyzed hydrogenation and acid-catalyzed deoxygenation for highly selective HDO of phenols to cyclohexanes11, 15. Both the Dyson and Leitner groups have made impressive progress on the development of high performance catalyst for the HDO of lignin-derived phenols using combinations of metal nanoparticles and acidic ionic liquids8, 17. In spite of the growing number of metal-acid combinations, the successful productions of alkanes using these bifunctional metal-acid catalysts have been mostly used for single-component lignin-derived monomers. The conversion of lignin into alkanes has been realized in a rare case via a two-step process, involving catalytic cleavage of the C–O–C bonds and subsequent hydrogenolysis/hydrogenation18. Very recently, the production of alkanes, with mass yield up to 28.1 wt%, was reported via HDO from raw lignocellulose containing cellulose, hemicellulose, and lignin by using a Pd/NbOPO4 bifunctional catalyst. However, the mass yield of alkyl cyclohexanes converted from lignin was only up to 5.1 wt%19. Efficient HDO requires the design and synthesis of a bifunctional catalyst containing active metal and both Brønsted and Lewis acid sites. Recent reports showed that atomically dispersed metal may demonstrate higher activity and efficiency compared with nanoparticles in heterogeneous reactions20,21,22. It is also believed increased Brønsted acid sites favor increasing alkane selectivities16, 23, and additional Lewis acid sites may help catalyze the reaction through initial binding of the oxygenated substrates and subsequent cleavage of the C–O linkages19.

Herein, we present a highly dispersed Pd–Mo catalyst that encompasses a combination of highly dispersed Pd and ultrafine Mo phosphate nanoparticles on silica (Pd/m–MoO3–P2O5/SiO2), in which m represents mixed-valent Mo. In batch reaction, this catalyst exhibits high activity (99%) for the catalytic HDO of phenol to cyclohexane in very mild conditions (383 K, 1 MPa). Furthermore, it shows good re-usability in continuous flow reaction conditions for 419 h. Characterization studies show that the efficient HDO ability may originate from the cooperative effects between highly dispersed Pd, high Brønsted and Lewis acid sites. By feeding wood and bark-derived WIBO containing large amounts of lignocellulosic oligomers, the catalyst not only completely converts phenolic monomers to cyclohexanes, but also achieves HDO of lignin, cellulose, and hemicellulose-derived oligomers into cyclohexanes, hexane, and pentane in 13.4, 5.1, and 7.4 wt%, respectively, with total mass yield up to 29.6 wt% and carbon yield up to 46.3%.


Catalysts synthesis and characterizations

The solid catalyst, Pd/m–MoO3–P2O5/SiO2, was prepared using a wet-impregnation method (see “Methods” for preparation). Transmission electron microscopy (TEM) image of the Pd/m–MoO3–P2O5/SiO2 (Supplementary Fig. 1) shows ultrafine, electron-rich m–MoO3–P2O5 nanoparticles supported on an amorphous SiO2 support. A high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) image (Fig. 1a) shows these ultrafine m–MoO3–P2O5 nanoparticles with high coverage and size of 2.8 ± 1.0 nm (inset, Fig. 1a). Inductively coupled plasma mass spectrometry (ICP-AES) analysis showed a Mo:P molar ratio of ca. 1:1 (Supplementary Table 1), which is consistent with Energy Dispersive X-ray spectroscopy (EDXS) data (Supplementary Fig. 2). Aberration-corrected annular bright-field (ABF) scanning transmission electron microscope image (Fig. 1b) and corresponding HAADF-STEM image (Fig. 1c) clearly show that the m–MoO3–P2O5 nanoparticles do not form a crystalline lattice. Together with powder X-ray diffractogram (PXRD) data (Supplementary Fig. 3), these results suggest that the m–MoO3–P2O5 nanoparticles are crystallographically disordered. Elemental mapping revealed that Mo and P are well dispersed throughout individual m–MoO3–P2O5 nanoparticles. The structure of the m–MoO3–P2O5 nanoparticles was further investigated with the help of multinuclear solid-state nuclear magnetic resonance (NMR) spectroscopy. The 31P solid-state magic angle spinning (MAS) NMR spectrum of a sample of the Pd/m–MoO3–P2O5/SiO2 exhibits a single resonance centered at δ = –5.5 ppm (Supplementary Fig. 4), the 31P chemical shift matches that of a MoO3–P2O5 glass with Mo:P molar ratio ca. 124, 25. A strong absorption band at ca. 966 cm−1 in the Raman spectrum (Supplementary Fig. 5) can be assigned to a terminal ν(Mo=O) in a MoO6 octahedra25. The data suggest that this glassy structure consists of chains of inter-connected PO4 tetrahedra and MoO6 octahedra linked via Mo–O–P bridges.

Fig. 1

Characterizations of the Pd/m–MoO3–P2O5/SiO2 catalyst. a HAADF-STEM image of Pd/m–MoO3–P2O5/SiO2. Inset shows the size distribution of the nanoparticles. Scale bar equals 20 nm. b Aberration-corrected ABF scanning transmission electron microscope image and c corresponding HAADF-STEM image of Pd/m–MoO3–P2O5/SiO2. Scale bars equal 5 nm. d STEM-EDS elemental mapping results for Pd/m–MoO3–P2O5/SiO2, showing a homogeneous distribution of Mo and P elements within nanoparticles and highly dispersed Pd. Scale bar equals 3 nm

X-ray absorption fine structure analysis

In addition to Mo and P elements, ICP-AES (Supplementary Table 1) and EDXS (Supplementary Fig. 2) data also show the presence of Pd in Pd/m–MoO3–P2O5/SiO2 (0.48 wt% from ICP-AES). The Pd signal is highly dispersed according to elemental mapping studies (Fig. 1d), and that the absence of Bragg diffraction of Pd from PXRD (Supplementary Fig. 3), these suggest Pd is presented in very small size. Due to the similar atomic number of Pd and Mo, it is difficult to distinguish Pd using the intensity information in the HAADF-STEM image. To understand the coordination environment and chemical states of Pd in Pd/m–MoO3–P2O5/SiO2, X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies were carried out. For clear comparison, Pd/m–MoO3–P2O5/SiO2 is labeled as reduced catalyst, and corresponding H2 treating precursor is labeled as oxidized catalyst. The Mo K-edge XANES spectrum for reduced catalyst shows a notable shoulder peak (denoted as a) in the pre-edge region (Fig. 2a) as MoO3, suggesting the formation of strongly distorted MoO6 octahedra having Mo=O bond26, in good agreement with the Raman results. The average valence of the Mo ions in the reduced catalyst is estimated to be ca. 5.5 using the linear relation between the Mo oxidation state and the energy position of feature b27, indicating the possible existence of mixed-valent Mo5/6+ oxide states. The Pd K-edge XANES spectrum is found to exhibit two well-defined features including a shoulder peak c and a doublet peak (d and e) at the white line (Fig. 2d); our XANES simulation reveals that the shoulder peak c can be considered to be the fingerprint of Pd2+ in square planar coordination, while the intensity of feature e is higher for Pd ions in distorted octahedral coordination than for the square planar coordination (Fig. 2g), consistent with XANES results in the literature28. Therefore, this implies that the Pd is highly dispersed in the framework of m–MoO3–P2O5/SiO2 via a combination of square planar and distorted octahedral configurations, with an averaged oxidation state between Pd2+ and Pd3+. This is in agreement with recently reported strategy of stabilizing single Pt atoms on a support interface by adopting a proper coordination22. The presence of m–MoO3–P2O5/SiO2 matrix may offer an ideal interface to stabilize Pd with high dispersion.

Fig. 2

XAFS characterization of the local coordination of Mo/Pd atoms in Pd/m–MoO3–P2O5/SiO2 catalyst. a The experimental Mo K-edge XANES spectra and b EXAFS Fourier transforms of the reduced catalyst, oxidized catalyst, and references. c Comparison of the WTs for the k 3-weighted Mo K-edge EXAFS signals for the high coordination shells in oxidized catalyst and reduced catalyst. d The experimental Pd K-edge XANES spectra and e EXAFS Fourier transforms of reduced catalyst, oxidized catalyst, and references. f Comparison of the WTs for the k 3-weighted Pd K-edge EXAFS signals for the high coordination shells in oxidized catalyst and reduced catalyst. g The theoretical XANES spectra calculated with the depicted square planer (PdO-P42/mmc) and distorted octahedral (PdO-I4/mmm and LaPdO3-Pbnm) structures. h Schematic representation of structural modulation due to the production of oxygen vacancies in the oxygen network by H2 reduction. The vertical dashed lines are drawn to guide the eye

The structural change of Pd/m–MoO3–P2O5/SiO2 during H2 treatment was also investigated. Interestingly, except for the peak intensity decrease for the Pd–O nearest-neighbor (NN) coordination shells, the two higher shell peaks at distances of 2.5 and 3.5 Å. The Pd K-edge EXAFS Fourier transform of reduced catalyst (Pd/m–MoO3–P2O5/SiO2) display a dramatic intensity increase and a radial shift to lower R direction, as compared to oxidized catalyst (Fig. 2e); similar phenomenon is shown for the Mo K-edge EXAFS results (Fig. 2b). Meanwhile, complementary wavelet transform (WT) EXAFS analysis29 reveals strong WT maxima at about 7.0 and 9.5 Å–1, which can be, respectively, associated with the Pd–P/Si and Pd–Pd/Mo scatterings (see Supplementary Fig. 6), at a distance of around 2.55 Å surrounding Pd atoms in reduced catalyst, in marked contrast to the WT maxima distribution in oxidized catalyst (Fig. 2f); slight change is observed for the Mo K-edge WT (Fig. 2c). Those results suggest that more oxygen vacancies are produced by H2 reduction in the oxide network of reduced catalyst, which may cause the collapse of the PdO6 octahedra by breaking the bridging oxygen atoms with the neighbor polyhedrons. A least-squares curve-fitting analysis was carried out for the multiple coordination shells of Mo and Pd (Supplementary Figs. 710 and Supplementary Tables 2 and 3). The coordination numbers of the Pd–O bonding in the first NN coordination sphere for reduced catalyst (oxidized catalyst) is estimated to be 4.9 (5.6) at a distance of 2.02 (2.03) Å, evidencing the transformation of the Pd–O bonding from a distorted octahedral to a square planer coordination. Simultaneously, the number of Pd/Mo atoms in the second NN coordination sphere of Pd in the reduced catalyst is estimated to be 1.5 at a distance of 2.80 Å, much larger than that of 0.4 in the oxidized catalyst, strongly signaling the presence of Pd–Pd/Mo atoms. By EXAFS analysis it is difficult to distinguish Mo from Pd; the data suggest a probability of both Pd–Mo and Pd–Pd neighbors after reduction, as schematically shown in Fig. 2h using density functional theory (DFT) calculations. The data do allow us to conclude there is an absence of large Pd particles, implying a high dispersion for the Pd atoms (further discussions are shown in Supplementary Note 1 and Supplementary Figs. 1113). Thus, XAFS data indicate that there are significant oxygen vacancy sites present in close vicinity of Mo and highly dispersed Pd in Pd/m–MoO3–P2O5/SiO2.

Studies of the activity and stability of the catalyst

Phenol HDO in a batch reactor was initially chosen as a model reaction to evaluate the catalytic activity of Pd/m–MoO3–P2O5/SiO2. The total mass of Pd was kept constant in order to benchmark other catalyst systems (Supplementary Table 1). The reaction process using Pd/m–MoO3–P2O5/SiO2 catalyst (Fig. 3a and Supplementary Fig. 14) shows an increase in cyclohexane selectivity and a decrease in cyclohexanol selectivity. In comparison, Pd/SiO2 catalyst only delivered hydrogenated products (cyclohexanone and cyclohexanol) and subsequent dehydration was not observed (Supplementary Fig. 14). These results suggest that in the case of Pd/m–MoO3–P2O5/SiO2 catalyst, phenol is initially hydrogenated to cyclohexanol catalyzed by Pd, which is followed by dehydration of cyclohexanol catalyzed by m–MoO3–P2O5 and further hydrogenation of cyclohexene to yield cyclohexane catalyzed by Pd. Via a comparison of product selectivity at near identical conversion level (Fig. 3b), the Pd/m–MoO3–P2O5/SiO2 catalyst exhibited a much higher cyclohexane selectivity (81%) compared with catalysts without m–MoO3–P2O5, indicating its high dehydration ability is due to the presence of m–MoO3–P2O5. We have compared the performance of Pd/m–MoO3–P2O5/SiO2 for the HDO of phenol to a series of state-of-art bifunctional metal-acid catalysts (Supplementary Table 4). Overall Pd/m–MoO3–P2O5/SiO2 demonstrates higher phenol conversions, with better cyclohexane selectivity at a lower temperature and lower H2 pressure than any of other catalyst systems. The catalyst was re-used and showed no obvious deactivation after five cycles (Fig. 3c), showing its stability under batch reaction conditions. In order to investigate stability under more industrially related conditions, Pd/m–MoO3–P2O5/SiO2 was evaluated under continuous flow condition at 433 K, 1 MPa H2 with flow rate of 10 cm3 (STP)min–1, weight hour space velocity (WHSV) = 0.18 h–1. The results show that there is some degree of deactivation (phenol conversion from 84.2 to 77.2%) but stable cyclohexane selectivity (from 68.2 to 68.8%) in the 32-h test (Fig. 3d), exhibiting higher cyclohexanol selectivity and stability than those in recent report under similar conditions (cyclohexane yield decrease from 52 to 28% in 4 h)17. The spent catalyst shows no obvious change (Supplementary Figs. 15, 16). The Mo and Pd K-edge XANES and EXAFS spectra are also given for the spent catalyst, exhibiting no obvious changes in the local structure around Mo and Pd atoms (Supplementary Fig. 17). The deactivation was mainly due to carbonaceous deposition (Supplementary Fig. 18). To evaluate re-use ability, Pd/m–MoO3–P2O5/SiO2 was evaluated under continuous flow conditions (453 K, 1 MPa H2 with WHSV of 0.085 h−1). As shown in Supplementary Fig. 19, after it was deactivated (phenol conversion from >99 to 69.0%, cyclohexanol selectivity from 98.3 to 90.4%) in 135 h, the spent catalyst was calcined at 673 K for 5 h to remove the carbonaceous deposition and re-used for another two runs. The result shows that the initial performance could be substantially recovered, with phenol conversion of >99% (1st run), 94.5% (2nd run), and 94.0% (3rd run), respectively, and cyclohexane selectivity of 98.3% (1st run), 98.4% (2nd run), and 96.7% (3rd run), respectively, and a similar deactivation trend was observed. This good re-usability ensures a long-term reaction efficiency (maintaining phenol conversion >60% and cyclohexane selectivity >90%) in three runs for over 419 h without obvious catalyst leaching (Supplementary Table 1).

Fig. 3

Catalytic performance on HDO of phenol. a Time dependence of the phenol conversion and cyclohexanol selectivity using Pd/m–MoO3–P2O5/SiO2 and Pd/SiO2 catalysts in batch reactions. Reaction conditions: phenol (0.195 mmol), catalyst (including 0.00045 mmol Pd), decalin (7 mL), 383 K, 1 MPa H2; reaction mixture stirred at 800 rpm. b Comparison of product selectivity of different catalysts at identical conversion level at 383 K, 1 Mpa H2 in batch reaction. Reaction conditions: phenol (0.195 mmol), catalyst (including 0.00045 mmol Pd), decalin (7 mL), reaction mixture stirred at 800 rpm. c Stability test of Pd/m–MoO3–P2O5/SiO2 in batch reaction. Reaction conditions: 383 K, 1 Mpa H2, 0.5 h. d Long-term stability test on the Pd/m–MoO3–P2O5/SiO2 at 433 K, 1 MPa H2 with a weight hourly space velocity of 0.17 h−1 in a continuous flow reaction

Studies of the effects of Brønsted and Lewis acidity on reaction

31P MAS NMR spectrum were recorded following adsorption of the trimethylphosphine oxide (TMPO) probe molecule, giving information about the acid type (Brønsted vs. Lewis), strength and concentration in the materials30. The 31P MAS NMR spectrum (Fig. 4a) of the TMPO-adsorbed on reduced catalyst (Pd/m–MoO3–P2O5/SiO2) exhibits two distinct resonances at 58.0 and 73 ppm, both signals are attributed to the protonation of TMPO by surface Brønsted acid sites with exceptionally high density reaching 0.0138 mmol/m2 (Supplementary Table 5 and Supplementary Fig. 20), which is 2.6-fold higher than a strong acidic zeolite HZSM-5 (Si to Al of 15)31. The reduced catalyst exhibits another new resonance at 45 ppm, which was not observed in oxidized catalyst and could be attributed to Lewis acid with density of 0.0075 mmol/m2. A series of catalysts with different Brønsted acid sites and Lewis acid sites were prepared by the same procedure as the Pd/m–MoO3–P2O5/SiO2 catalyst by varying the molar ratio of P:Mo (Supplementary Table 5). The existence of the Lewis acid site is observed only on catalysts containing Mo species, thus it is most likely linked to oxygen vacancy associated with Mo centers32, which is well consistent with abovementioned XAFS analysis. The formation of oxygen vacancy is observed by temperature programmed reduction (TPR, Supplementary Fig. 21), and could be linked with the reduction of surface oxidation state evidenced by multi-frequency electron paramagnetic resonance (EPR, see Methods, Supplementary Figs. 2224) and by solid-state magnetic susceptibility measurements (Supplementary Fig. 25).

Fig. 4

Surface analyses of Pd/m–MoO3–P2O5/SiO2 catalyst. a Solid-state 31P MAS NMR spectra of TMPO-adsorbed on the oxidized catalyst and reduced catalyst (Pd/m–MoO3–P2O5/SiO2). Inset displayed TMPO molecule. b DRIFTS spectra at 1100–1900 cm−1 obtained over oxidized catalyst and reduced catalyst (Pd/m–MoO3–P2O5/SiO2) in a reaction mixture containing phenol and He at 383 K

We believe that the excellent performance of Pd/m–MoO3–P2O5/SiO2 for HDO may be attributed to cooperative effects between highly dispersed Pd, strong Brønsted acid sites, and Lewis acid sites. The highly dispersed Pd allows for higher hydrogenation activity (Fig. 3a) and enhanced metal atom efficiency compared with Pd/SiO2 (Supplementary Fig. 14), by increasing the number of exposed surface atoms by using very low Pd loading amount of 0.48 wt%. The catalysts with different Brønsted acid sites (Supplementary Table 5) were compared in the dehydration of cyclohexanol (Supplementary Table 6), which is the most important intermediate in the HDO of phenol. Since most of the samples show comparable Brønsted acid strength, respectively, revealed by resonance position of 31P MAS NMR spectrum (except Pd/P2O5/SiO2 (P:Mo = 1:0) which shows weaker Brønsted acid strength), one can look into the correlation between Brønsted acid and dehydration activity. The result shows that only samples containing Brønsted acid sites have activity, suggesting the dehydration is a Brønsted acid-catalyzed process. Specifically, Pd/m–MoO3–P2O5/SiO2 (P:Mo = 1:1, the reduced catalyst shown in the main work) with the most Brønsted acid sites is a more active dehydration catalyst, and also Pd/m–MoO3–P2O5/SiO2 (P:Mo = 2:1) with higher Brønsted acid sites compared with Pd/MoO3/SiO2 (P:Mo = 0:1) has higher dehydration activity (conversion: 25.2 vs. 19.8%), which are consistent with the correlation between the Brønsted acid sites and the dehydration activity16, 23. It is also observed that Pd/P2O5/SiO2 has lower dehydration activity compared with Pd/MoO3/SiO2 (12.8 vs. 19.8%), although its Brønsted acid sites is higher. This could be due to its relatively weaker Brønsted acid strength13. The role of Lewis acid site on phenol conversion was further studied by performing diffuse-reflectance infrared Fourier transform spectroscopy (DRIFTS) upon exposure of the oxidized and reduced catalyst (Pd/m–MoO3–P2O5/SiO2) to a phenol/He mixture at reaction temperature (383 K). In the measurements, the reduced catalyst was first treated with 5% H2/Ar at 383 K before exposed to phenol/He mixture. The DRIFTS spectra of both reduced catalyst and oxidized catalyst (Fig. 4b) show bands at 1597, 1497, 1475, 1352 and 1267 cm–1, which correspond to different vibrational modes of phenoxy species33. Compared with oxidized catalyst, the reduced catalyst shows more pronounced bands at 1684, 2951 and 2874 cm–1 (Fig. 4b, Supplementary Fig. 26), which could be assigned to the v(C=O) and v(C–H) stretching modes, respectively, of adsorbed 2,4-cyclohexadien-1-one tautomer of phenol33, 34. Considering that both the DRIFTS of spectra of oxidized Pd/SiO2 and reduced Pd/SiO2 do not show obvious bands for 2,4-cyclohexadien-1-one (Supplementary Fig. 27), the formation of this compound is more likely promoted by Lewis acid sites (oxygen vacancy associated with Mo centers) on reduced catalyst via tautomerization of phenol. This compound is an important intermediate in the HDO of phenol supported by Priscillat et al. studies33, which could be first hydrogenated to 2-cyclohexen-1-one, then to cyclohexanone and further to cyclohexanol.


Based on the above understanding, efficiency test using Pd/m–MoO3–P2O5/SiO2 for upgrading a WIBO derived from fast pyrolysis of grounded eucalyptus wood chip and bark were carried out. This WIBO sample was a dark red, treacle-like, viscous liquid (Supplementary Fig. 28) with a 47.2 wt% carbon content and a 42.8 wt% oxygen content (Supplementary Table 7). The WIBO contains 13 wt% moisture determined by Karl Fisher method, which mainly derived from the feedstock and also the dehydration reactions during flash pyrolysis treatment35. The content of the WIBO was studied using gas chromatograph-mass spectrometry (GC-MS) (Fig. 5a and Supplementary Fig. 29). The results show the WIBO contains a series of oxygenated monomers involving phenolic compounds such as guaiacol, syringol, and furans (4.7 wt% of total WIBO mass). High-performance liquid chromatography (HPLC) of the water extract of the WIBO (Supplementary Fig. 30) showed no sugar-type monomers before it was hydrolyzed. The remaining mass can be attributed to lignin and sugar oligomers that are undetectable in both GC-MS and HPLC. Gel permeation chromatography (GPC) analysis (Supplementary Fig. 31) verified the presence of oligomers in the WIBO with molecular weight up to 1000 Da and weight average molecular weight (M w) of 401. This M w value is consistent with those reported for wood pyrolysis oils36.

Fig. 5

GC-MS analysis before and after upgrading. a GC-MS analysis of WIBO dissolved in decalin before upgrading. b GC-MS analysis of upgrading product after a batch reaction. Reaction conditions: WIBO (86.2 mg), Pd/m–MoO3–P2O5/SiO2 (170.8 mg), decalin (7 mL), 453 K, 1 MPa H2, 4 h, stirred at 800 rpm. MS detector was off from 6.2 to 9.5 min, and 11.8 to 11.9 min to block decalin and tetralin signals. The overall GC-MS patterns and three enlarged regions are shown. Insets show the images of mixtures before and after upgrading, respectively

HDO of this WIBO was carried out in a batch reactor at 453 K and 1 MPa H2 in the presence of Pd/m–MoO3–P2O5/SiO2 catalyst. Total conversion of the oxygenated monomers was achieved after 4 h (Fig. 5b), with the production of 9.4 wt% total mass yield of liquid alkanes involving 0.9 wt% pentane, 1.2 wt% hexane, and 5.6 wt% C6–C9 cycloalkanes (cyclohexane, methylcyclohexane, ethylcyclohexane, and propylcyclohexane; see Table 1 and Supplementary Fig. 32). Overall a 10.2% carbon yield in the form of cyclohexanes was obtained. This is higher than the maximum carbon yield (5.7%) possible from the lignin-derived monomers present in the WIBO. This indicates that some oligomers in the WIBO were converted into cyclohexanes. The production of pentane and hexane suggests that HDO of cellulose and hemicellulose into alkanes are achieved, which is supported by the earlier literature19. The color of the mixture became lighter after the reaction, serving as another qualitative indicator of the HDO efficiency (inset in Fig. 5a, b). To further increase the mass yield of liquid alkanes, the reaction was carried out at an increased temperature. At 523 K and 1 MPa H2, 29.6 wt% total mass yield and 46.3% total carbon yield of liquid alkanes was achieved after 15 h, the mass yield of cyclohexanes, pentane, and hexane reached 13.4, 7.4 and 5.1 wt%, respectively (see Methods, Table 1, Supplementary Fig. 33). It should be noted that the total carbon yield is comparable to the state-of-art in catalytic performance19, 37, 38. GPC analysis (Supplementary Fig. 34) shows the decrease of oligomers. Although reaction mechanisms for HDO of different classes of oxygenates in bio-oil could be different, these results clearly indicate that the catalyst has a high performance for simultaneous HDO of lignin, cellulose, and hemicellulose-derived oligomers into liquid alkanes.

Table 1 HDO of water-insoluble wood and bark-derived WIBO over Pd/m–MoO3–P2O5/SiO2 catalyst


We report a highly active HDO catalyst comprising highly dispersed Pd and ultrafine Mo phosphate nanoparticles supported on SiO2. This catalyst is 100% effective and is 97.5% selective for HDO of phenol to cyclohexane under mild conditions, showing regeneration ability in long-term continuous flow tests for 419 h with some decrease in catalytic performance after 32 h in a continuous flow reaction. There are cooperative effects between highly dispersed Pd, Brønsted and Lewis acid sites on Pd/m–MoO3–P2O5/SiO2, which shows to be important for the efficient catalytic HDO behavior. Using water-insoluble fraction of wood and bark-derived WIBO, the catalyst showed state-of-art performance for the simultaneous HDO of lignin, cellulose, and hemicellulose-derived oligomers into liquid alkanes with total mass yield of 29.6 wt% under mild condition (523 K, 1 MPa H2). Further work will include mechanistic investigations for HDOs of different classes of oxygenates in bio-oil to fully understand the high efficiency of this catalyst.


Sample preparation

Pd/m–MoO3–P2O5/SiO2 synthesis: (NH4)6Mo7O24•4H2O (0.021 mmol), (NH4)2HPO4 (0.150 mmol), citric acid (0.30 mmol) were dissolved in 0.3 mL of HCl aqueous solution containing PdCl2 (1.5 mg). The mixture was stirred for 1 h and then added dropwise to SiO2 (0.12 g). The obtained glue-like sample was dried in an oven at 397 K overnight and calcined at 773 K in a muffle furnace for 5 h at a rising rate of 5 K/min. The calcined sample, named as Pd/MoO3–P2O5/SiO2, was reduced in H2 at 323 K for 3 h with a flowing rate of 75 cm3/min. The calcined sample changed to a greenish-blue color following reduction. This reduced sample was named Pd/m–MoO3–P2O5/SiO2. The synthesis of Pd/P2O5/SiO2 was similar as for Pd/m–MoO3–P2O5/SiO2, except with no addition of (NH4)6Mo7O24•4H2O. Pd/SiO2 was prepared by dropwise addition of 0.3 mL of prepared PdCl2 solution into SiO2 under strong stirring. The following operations are the same as the one for Pd/m–MoO3–P2O5/SiO2. The fresh catalyst was protected in N2 and quickly prepared as samples for further characterizations and catalytic tests.

High-resolution TEM

HRTEM images were acquired with JEOL JEM-2100F field-emission TEM with an accelerating voltage of 200 kV.

Aberration-corrected TEM

Aberration-corrected TEM was performed on JEOL 200F TEM operated at 200 keV. The attainable spatial resolution of the microscope is 78 pm with a probe spherical-aberration corrector. Both ABF and HAADF were obtained with the illumination semi-angle of 25 mrad and probe current of 100 pA. The dwell time for imaging was set at 10 ms per pixel to ensure desirable signal to noise ratio. The collection angles for the ABF and HAADF images were fixed at 12–25 and 90–250 mrad, respectively. EDXS was performed to locate elemental distribution of Mo, P, and Pd with an SDD-type EDX detector. The attainable energy-resolution of the EDX detector is 130 eV. A higher beam current of 300 pA was used with a longer dwell time of 0.1 ms per pixel repeated for 200 times. Spatial drift was corrected with a simultaneous image collector. Mo L-edge, P K-edge and Pd L-edge were used for elemental mapping.

Power X-ray diffraction

PXRD data were obtained on a PANAnalytical X’Pert Pro diffractometer in reflection mode at 40 kV and 40 mA using Cu Kα radiation.

Raman spectroscopy

Raman spectra were recorded on a Renishaw Raman spectrometer at a laser excitation wavelength of 633 nm.

X-ray absorption data collection and analysis

Mo K-edge and Pd K-edge X-ray absorption spectra were acquired under ambient condition at beamline BL14W1 of Shanghai Synchrotron Radiation Facility (SSRF) using a Si(311) double-crystal monochromator in transmission and fluorescence modes, respectively. The storage ring of SSRF was operated at 3.5 GeV with a maximum current of 250 mA. The energy was calibrated using Mo/Pd foil. While the incident and transmitted X-ray intensities were monitored by using standard ion chambers, the fluorescence signal was detected by using a 7 element Ge detector. To prevent air oxidation, the samples were prepared in a glove box, and they were uniformly mixed with BN powder and pressed to a pellet, which was sealed in a cell holder with Kapton windows for XAFS measurement. The XAFS raw data were background-subtracted, normalized, and Fourier transformed by the standard procedures with the ATHENA program39, 40. Least-squares curve-fitting analysis of the EXAFS χ(k) data was carried out using the ARTEMIS program39 with the theoretical scattering amplitudes, phase shifts, and the photoelectron mean-free path for all paths calculated by ab-initio code FEFF9.0541. The details of curve fitting are discussed in Supplementary Figs. 710 and Supplementary Tables 2 and 3. The Pd K-edge theoretical XANES calculations were carried out with the FDMNES code in the framework of real-space full multiple-scattering scheme using Muffin-tin approximation for the potential41,42,43. The energy-dependent exchange-correlation potential was calculated in the real Hedin-Lundqvist scheme, and then the spectra are convoluted using a Lorentzian function with an energy-dependent width to account for the broadening due both to the core-hole width and to the final state width. Satisfactory convergence for cluster sizes had been achieved.

Density functional theory calculations

The electronic structure calculations were performed using the density functional theory and a plane-wave basis set as implemented in the VASP code44. The electron–ion interaction was treated by the projector-augmented wave method45 with the outmost s, p, and d states as valence orbital. The electron exchange-correlation energy was described by the modified Perdew-Burke-Ernzerhof generalized gradient approximation for solids (PBEsol)46. The kinetic energy cutoff was set to 350 eV, and the Brillouin zone was sampled in Monkhorst-Pack k point meshes with an interpolation grid spacing of 0.04 Å–1 for the 240 atoms supercell, to achieve the total energy convergence of less than 0.001 eV/atom. Structural relaxation was allowed until the force on each atom was <0.01 eV/Å.

Catalysis testing in batch reactions

Phenol (18.4 mg, 0.195 mmol) was added into a stainless steel Parr autoclave (reactor volume, 50 mL) with decalin (7 mL), together with Pd/m–MoO3–P2O5/SiO2 (10.0 mg) and was stirred for 10 min. The autoclave was then sealed, purged with H2 for three times, and then placed under 1 MPa H2 at room temperature. The reaction was carried out at different temperature for a certain time with a stirring speed of 800 rpm. After reaction, the organic product was collected and analyzed by GC-MS. For the re-usability experiments using the Pd/m–MoO3–P2O5/SiO2 catalyst; after each reaction cycle, the spent catalyst was separated by centrifugation and used for the next run.

Catalysis testing in fixed bed reactions

The fixed bed reaction was carried out in a HEL made continuous trickle bed reactor (mode FlowCAT) with both the liquid feed and hydrogen gas passing in downward direction. The Pd/m–MoO3–P2O5/SiO2 catalyst (127 mg) was located in the middle of the tubular reactor with quartz wool plugs on both the sides. Liquid feed was prepared by dissolving phenol in decalin to form a solution of 3.6 mg/mL. The reaction was carried out at 433–453 K (Fig. 3d and Supplementary Fig. 19), 1 Mpa with H2 flow rate of 10 cm3(STP)min–1 and liquid flow rate of 0.05–0.1 mL min–1 (Fig. 3d and Supplementary Fig. 16). The liquid was preheated at the desired reaction temperature before being fed into the reactor. The products were periodically collected from the outlet stream throughout the reaction and were analyzed by GC-MS. WHSV was calculated by dividing the feed flow rate per hour by weight of catalyst. The spent catalyst (32 h-test) was collected and protected in N2, and then quickly prepared as samples for further characterizations. For the re-usability of the Pd/m–MoO3–P2O5/SiO2 catalyst, the spent catalyst was not removed from the reactor but calcined on-site in air at 673 K for 5 h with a flowing rate of 20 cm3/min and then reduced in H2 at 323 K for 3 h with a flowing rate of 75 cm3/min.

GC-MS analysis

GC-MS analysis was conducted by using an Agilent gas chromatograph equipped with an Agilent 19091N-133 column of mode HP-INNOWax with high polarity, 30 m × 250 μm × 0.25 μm connected online to mass spectrometer. The GC oven was programmed as: hold at initial temperature of 313 K for 5 min, ramp at 15 K min–1 to 523 K and hold at 523 K for 5 min. 2-isopropylphenol was used as the internal standard. The peaks were analyzed by comparing the corresponding spectra with those of the NIST 2011 MS library.

WIBO analysis and conversion

The WIBO was derived from fast pyrolysis of grounded eucalyptus wood chip and bark. Wood log (wood chip + bark) was fed directly into pyrolysis reactor in forms of grounded wood and bark. Pyrolysis was carried out at 773 K in absence of oxygen. The produced bio-oil was separated into water-soluble phase and water-insoluble phase. For the WIBO part, the volatile species, mainly lignin-derived monomers, were determined by dissolving 84.0 mg WIBO and 4.03 mg internal standard, 2-isopropylphenol, in 1.5 mL methanol or only WIBO in decalin, and analyzing by GC-MS, as presented in Supplementary Fig. 29 and Fig. 5a. For the analysis of sugar component, 1.038 g WIBO was washed with 30 mL water while stirring at room temperature for 12 h, and the resulting water extraction was analyzed by HPLC, as presented in Supplementary Fig. 30. HPLC analysis was conducted by using a Laserchrom HPLC system equipped with a Aminex HPX 87H 300 × 7.8 column and Refractive Index Detector at 308 K using 0.025 M H2SO4 as the mobile phase with flow rate of 0.6 mL min–1. To hydrolyze oligomers into monomeric sugars, 200 μL concentrated H2SO4 was added into 2 mL upper water solution and heated at 393 K for 1 h. The resultant was also analyzed by HPLC, as presented in Supplementary Fig. 30.

For reaction at 453 K, WIBO (86.2 mg), decalin (7 mL), and Pd/m–MoO3–P2O5/SiO2 (170.8 mg) were added into a stainless steel Parr autoclave (reactor volume of 50 mL) and stirred for 10 min. Then, the autoclave was sealed, purged three times with H2, and placed under 1 MPa H2 at room temperature. The reaction was carried out at 453 K for 4 h with a stirring speed of 800 rpm. After reaction, the organic product was collected and analyzed by GC-MS using an added internal standard, as presented in Supplementary Fig. 32. For reaction at 523 K, 87.2 mg WIBO was used and the other parameters were kept identically. The reaction was carried out at 523 K for 15 h. The reaction products were analyzed by GC-MS, as presented in Supplementary Fig. 33.

The mass of lignin-derived phenols and furans in the WIBO and alkanes in the product were determined by internal standard. The corresponding response factors were determined by analyzing mixtures of those pure, commercial compounds of phenols, furans and alkanes, and internal standard with given weights. Mass yields of alkanes were calculated by the equation: mass of alkanes/mass of dried WIBO input. Carbon yields were calculated by the equation: mass of carbon in alkanes/mass of carbon in the WIBO input.

Gel permeation chromatography

GPC measurements were performed on a Shimadzu LC-20AD instrument using MALLS detector. Two Mixed Bed PSS SDV linear S columns were used in series with tetrahydrofuran (THF) as mobile phase with flowing rate of 1.0 cm3 min–1 at 303 K. The MALLS detector was calibrated using a polystyrene standard. The sample was prepared by dissolving WIBO in THF with 1 wt% concentration and then filtering with 0.20 μm pore size microfilter.

Thermogravimetric analysis (TGA)

TGA measurements were performed on a Mettler Toledo TGA/DSC 1 system. 16.76 mg of sample was heated in a corundum crucible between 423 and 973 K at a heating rate of 5 K/min in a flowing 50% O2/N2 mixture.

TMPO-adsorbed sample preparation for 31P MAS NMR spectroscopy

100 mg of the catalyst was placed in a home-made glass tube, activated at 298 K for 2 h under vacuum (10–1 Pa), mixed with a CH2Cl2 solution containing 0.1 M TMPO under nitrogen, treated by ultrasound for 1 h (for equilibrium), and then the solvent was evacuated under vacuum. Finally, the sample tube was sealed for storage and transferred to Bruker 4 mm ZrO2 rotor with a Kel-F endcap in a glove box under nitrogen atmosphere before NMR spectroscopy measurement.

31P MAS solid-state NMR spectroscopy experiments

Solid-state MAS NMR spectroscopy experiments were carried out using a Bruker Avance III 400WB spectrometer at room temperature. To remove the effect of proton spins on quantitative 31P spectra (i.e., Fig. 4a), a strong radio frequency field (B) is usually applied at the resonance frequency of the non-observed abundant spins (1H herein), which contribute to the coupling of both spin species. The high power decoupling was thus used for the quantitative 31P analysis. Considering the long relaxation time of 31P nuclei in NMR spectroscopy experiment, 30° pulse with 1.20 μs width and 15 s delay time. The radiofrequency for decoupling was 59 kHz. The spectral width was 400 ppm, from 200 to −200 ppm. The number of scanning was 800 and spinning frequency was 10 kHz. The 31P chemical shifts were reported relative to 85% aqueous solution of H3PO4, with NH4H2PO4 as a secondary standard (0.81 ppm). The quantitative analysis of adsorbed TMPO molecules was then calculated according to the calibration line established by running standard samples with various adsorbed TMPO concentration47, 48. On the other hand, for samples without adsorbing TMPO (Supplementary Fig. 4), the 1H- 31P cross-polarization was used.

Surface area measurements

Specific surface areas were analyzed by Micromeritics Tristar II. The samples were measured for the N2 adsorption and desorption at 77 K. Before each measurement, the samples were first in-situ degassed overnight at 110 °C for 12 h.

Electron paramagnetic resonance

Continuous-wave electron paramagnetic resonance (CW-EPR) was carried out in the Centre for Advanced Electron Spin Resonance (CAESR), on two spectrometers and frequencies. X-band measurements (ca. 9.4 GHz) were performed on a Bruker BioSpin EMXmicro spectrometer with a Bruker SHQE-W cylindrical TE011-mode resonator. The temperature was controlled with an Oxford Instruments ITC-503 cryostat and ESR-900 cryostat. W-band measurements (ca. 94 GHz) were performed on a Bruker BioSpin EleXsys E680 spectrometer with a Bruker EN600-1021H cylindrical TE011-mode resonator. The temperature was controlled with an Oxford Instruments ITC-503 cryostat and CF-935O cryostat. For W-band, the microwave frequency was 93.9373 GHz for W-band, microwave power 40 μW, modulation amplitude 10 G, with a sweep of 84 s over 450 mT. For X-band, the microwave frequency was 9.38914 GHz, microwave power 4 mW, modulation amplitude 6 G, with a sweep of 41 s over 80 mT. The field modulation frequency was 100 kHz at both microwave frequencies. Data analysis was performed in Matlab, and EPR simulations employed the EasySpin toolbox49.

In temperature-dependent X-band EPR measurements the sample does not undergo microwave power saturation down to 20 K, while measurements present here were acquired at 85 K. Quantitative X-band CW-EPR measurements determined a total spin concentration of 9.1 × 1016 spins/mg, and double-integration of best-fit W-band simulations shows that the Mo5+ accounts for 80% of EPR-active species. W-band simulations employed a g-strain linewidth model of σ  = 0.0054 and σ || = 0.0079, which the same as at X-band. Simulations uncertainties are estimated in g-values as +/− 0.001 and hyperfine as +/− 5 MHz. Hyperfine values reported as A(95Mo) are those of 95Mo (15.9% natural abundance), while the 97Mo isotope (9.56% natural abundance) is related to 95Mo by the ratio of nuclear g-factors (−0.3734(97Mo)/−0.3657(95Mo)).

For EPR results, at 94 GHz, W-band (Supplementary Fig. 22), a signal consistent with six-coordinate Mo5+ is resolved from oxygen vacancies at g = 2 and donor defects at g = 1.977 with an axial g-matrix of g  = 1.933 and g || = 1.88450. Natural abundance 95/97Mo5+ hyperfine in X-band (Supplementary Fig. 23), 9.4 GHz, point to at least two species in the precursor, which are similar to two of three components in the H2-reduced form, but with about one-fourth overall EPR intensity in the precursor. A third component of reduced catalyst arises as an additional g || feature at g~1.90 and an additional component of hyperfine in the high field A ||(95/97Mo) feature, as demarcated in Supplementary Fig. 24. The W-band sample, aged under air, results in a relative reduction of the g = 1.90 feature, indicating that the corresponding site is likely surface-exposed. Multi-component simulations in Supplementary Fig. 24 also show an increase in g || from the precursor value by Δg of ca. 0.0025 upon reduction, on the trend of increasing ionic ligand character.

Superconducting quantum interference device (SQUID) magnetometry

Magnetic susceptibility measurements of powdered samples of catalyst before and after H2 reduction were carried out using a Quantum Design MPMS-5 SQUID magnetometer at a field of 0.1 T and different temperatures (2–300 K). Accurately weighed samples (ca. 60 mg) were placed into gelatine capsules and then loaded into nonmagnetic plastic straws before being lowered into the cryostat. No corrections were made for the diamagnetic contribution to the magnetic moment due to the excess silica, and it was assumed the paramagnetic contribution originated solely from Mo5+ present in the sample, as determined by ICP-MS. Hence, a total magnetic susceptibility per Mo is reported. For quick comparison the magnetic susceptibility (per Mo) at 2 K, for catalyst before and after reduction is 6.73 × 10–4 and 1.19 × 10–3 cm3 mol−1, respectively, demonstrating the formation of more Mo5+ in the catalyst after H2 reduction.

Temperature programmed reduction

TPR was performed on Micromeritics AutoChem II 2920 using a flow of H2 in N2 (10%, 50 mL min–1) ramping from 309 to 1073 K at a rate of 5.0 °K min–1.

Diffuse-reflectance infrared Fourier transform spectroscopy

DRIFT spectroscopy studies were performed using a Bruker Tensor 27 spectrometer fitted with a high-sensitivity MCT detector (with resolution of 4 cm−1) and a diffuse IR heated chamber equipped with ZnS window. The reduced catalyst (Pd/m–MoO3–P2O5/SiO2) and reduced Pd/SiO2 with mass of 20 mg were pre-treated in the presence of 5% H2 in Ar at 383 K for 1 h. The oxidized catalyst and oxidized Pd/SiO2 (PdO/SiO2) with a mass of 20 mg were pre-treated in air at 573 K for 1 h and then cooled down to 383 K. The ZnS window was kept being heated to avoid phenol condensation. After the pre-treatments, the background was scanned in the presence of He at 383 K and then the spectra were collected in the presence of phenol/helium mixture at 383 K. The background and spectra were recorded at a resolution of 4 cm−1 with 128 accumulation scans.

Data availability

Data that support the findings of this study are available within the article (and its Supplementary Information files) and from the corresponding authors on reasonable request.


  1. 1.

    Huber, G. W., Iborra, S. & Corma, A. Synthesis of transportation fuels from biomass: chemistry, catalysts, and engineering. Chem. Rev. 106, 4044–4098 (2006).

    CAS  Article  PubMed  Google Scholar 

  2. 2.

    Corma, A., Iborra, S. & Velty, A. Chemical routes for the transformation of biomass into chemicals. Chem. Rev. 107, 2411–2502 (2007).

    CAS  Article  PubMed  Google Scholar 

  3. 3.

    Czernik, S. & Bridgwater, A. V. Overview of applications of biomass fast pyrolysis oil. Energy Fuels 18, 590–598 (2004).

    CAS  Article  Google Scholar 

  4. 4.

    Bridgwater, A. V. Catalysis in thermal biomass conversion. Appl. Catal. A 116, 5–47 (1994).

    CAS  Article  Google Scholar 

  5. 5.

    Mohan, D., Pittman, C. U. & Steele, P. H. Pyrolysis of wood/biomass for bio-oil: a critical review. Energy Fuels 20, 848–889 (2006).

    CAS  Article  Google Scholar 

  6. 6.

    Roman-Leshkov, Y., Chheda, J. N. & Dumesic, J. A. Phase modifiers promote efficient production of hydroxymethylfurfural from fructose. Science 312, 1933–1937 (2006).

    ADS  CAS  Article  PubMed  Google Scholar 

  7. 7.

    Huber, G. W., Chheda, J. N., Barrett, C. J. & Dumesic, J. A. Production of liquid alkanes by aqueous-phase processing of biomass-derived carbohydrates. Science 308, 1446–1450 (2005).

    ADS  CAS  Article  PubMed  Google Scholar 

  8. 8.

    Mehdi, H. et al. Integration of homogeneous and heterogeneous catalytic processes for a multi-step conversion of biomass: from sucrose to levulinic acid, gamma-valerolactone, 1,4-pentanediol, 2-methyl-tetrahydrofuran, and alkanes. Top. Catal. 48, 49–54 (2008).

    CAS  Article  Google Scholar 

  9. 9.

    Kunkes, E. L. et al. Catalytic conversion of biomass to monofunctional hydrocarbons and targeted liquid-fuel classes. Science 322, 417–421 (2008).

    ADS  CAS  Article  PubMed  Google Scholar 

  10. 10.

    Vispute, T. P., Zhang, H. Y., Sanna, A., Xiao, R. & Huber, G. W. Renewable chemical commodity feedstocks from integrated catalytic processing of pyrolysis oils. Science 330, 1222–1227 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  11. 11.

    Zhao, C., Kou, Y., Lemonidou, A. A., Li, X. & Lercher, J. A. Highly selective catalytic conversion of phenolic bio-oil to alkanes. Angew. Chem. Int. Ed. 48, 3987–3990 (2009).

    CAS  Article  Google Scholar 

  12. 12.

    Zhao, C. & Lercher, J. A. Upgrading pyrolysis oil over Ni/HZSM-5 by cascade reactions. Angew. Chem. Int. Ed. 51, 5935–5940 (2012).

    CAS  Article  Google Scholar 

  13. 13.

    Yan, N., Yuan, Y., Dykeman, R., Kou, Y. & Dyson, P. J. Hydrodeoxygenation of lignin-derived phenols into alkanes by using nanoparticle catalysts combined with Bronsted acidic ionic liquids. Angew. Chem. Int. Ed. 49, 5549–5553 (2010).

    CAS  Article  Google Scholar 

  14. 14.

    Xia, Q. N. et al. Pd/NbOPO4 multifunctional catalyst for the direct production of liquid alkanes from aldol adducts of furans. Angew. Chem. Int. Ed. 53, 9755–9760 (2014).

    CAS  Article  Google Scholar 

  15. 15.

    Zhao, C., He, J. Y., Lemonidou, A. A., Li, X. B. & Lercher, J. A. Aqueous-phase hydrodeoxygenation of bio-derived phenols to cycloalkanes. J. Catal. 280, 8–16 (2011).

    CAS  Article  Google Scholar 

  16. 16.

    Wang, L. et al. Mesoporous ZSM-5 zeolite-supported Ru nanoparticles as highly efficient catalysts for upgrading phenolic biomolecules. ACS Catal. 5, 2727–2734 (2015).

    CAS  Article  Google Scholar 

  17. 17.

    Luska, K. L., Migowski, P., El Sayed, S. & Leitner, W. Synergistic interaction within bifunctional ruthenium nanoparticle/SILP catalysts for the selective hydrodeoxygenation of phenols. Angew. Chem. Int. Ed. 54, 15750–15755 (2015).

    CAS  Article  Google Scholar 

  18. 18.

    Yan, N. et al. Selective degradation of wood lignin over noble-metal catalysts in a two-step process. ChemSusChem 1, 626–629 (2008).

    CAS  Article  PubMed  Google Scholar 

  19. 19.

    Xia, Q. et al. Direct hydrodeoxygenation of raw woody biomass into liquid alkanes. Nat. Commun. 7, 11162 (2016).

    ADS  Article  PubMed Central  PubMed  Google Scholar 

  20. 20.

    Liu, P. X. et al. Photochemical route for synthesizing atomically dispersed palladium catalysts. Science 352, 797–801 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  21. 21.

    Qiao, B. et al. Single-atom catalysis of CO oxidation using Pt1/FeOx. Nat. Chem. 3, 634–641 (2011).

    CAS  Article  PubMed  Google Scholar 

  22. 22.

    Zhang, B. et al. Stabilizing a platinum1 single-atom catalyst on supported phosphomolybdic acid without compromising hydrogenation activity. Angew. Chem. Int. Ed. 55, 8319–8323 (2016).

    CAS  Article  Google Scholar 

  23. 23.

    Zhang, W. et al. Hydrodeoxygenation of lignin-derived phenolic monomers and dimers to alkane fuels over bifunctional zeolite-supported metal catalysts. ACS Sustainable Chem. Eng. 2, 683–691 (2014).

    CAS  Article  Google Scholar 

  24. 24.

    Santagneli, S. H. et al. Structural studies of NaPO3-MoO3 glasses by solid-state nuclear magnetic resonance and raman spectroscopy. J. Phys. Chem. B 111, 10109–10117 (2007).

    CAS  Article  PubMed  Google Scholar 

  25. 25.

    Koudelka, L. et al. Structural study of PbO-MoO3-P2O5 glasses by Raman and NMR spectroscopy. J. Non-Crystal. Solids 357, 2816–2821 (2011).

    ADS  CAS  Article  Google Scholar 

  26. 26.

    Wang, H. et al. In operando X-ray absorption fine structure studies of polyoxometalate molecular cluster batteries: polyoxometalates as electron sponges. J. Am. Chem. Soc. 134, 4918–4924 (2012).

    CAS  Article  PubMed  Google Scholar 

  27. 27.

    Ressler, T., Wienold, J., Jentoft, R. E. & Neisius, T. Bulk structural investigation of the reduction of MoO3 with propene and the oxidation of MoO2 with oxygen. J. Catal. 210, 67–83 (2002).

    CAS  Article  Google Scholar 

  28. 28.

    Eyssler, A. et al. On the dtate of Pd in perovskite-type oxidation catalysts of composition A(B, Pd)O3±δ(A=La, Y; B=Mn, Fe, Co). Chem. Mater. 24, 1864–1875 (2012).

    CAS  Article  Google Scholar 

  29. 29.

    Funke, H., Scheinost, A. C. & Chukalina, M. Wavelet analysis of extended X-ray absorption fine structure data. Phys. Rev. B 71, 094110 (2005).

    ADS  Article  Google Scholar 

  30. 30.

    Zheng, A., Huang, S. J., Liu, S. B. & Deng, F. Acid properties of solid acid catalysts characterized by solid-state 31P NMR of adsorbed phosphorous probe molecules. Phys. Chem. Chem. Phys. 13, 14889–14901 (2011).

    CAS  Article  PubMed  Google Scholar 

  31. 31.

    Zhao, Q. et al. Discernment and quantification of internal and external acid sites on zeolites. J. Phys. Chem. B 106, 4462–4469 (2002).

    CAS  Article  Google Scholar 

  32. 32.

    Prasomsri, T., Shetty, M., Murugappan, K. & Román-Leshkov, Y. Insights into the catalytic activity and surface modification of MoO3 during the hydrodeoxygenation of lignin-derived model compounds into aromatic hydrocarbons under low hydrogen pressures. Energy Environ. Sci. 7, 2660–2669 (2014).

    CAS  Article  Google Scholar 

  33. 33.

    de Souza, P. M. et al. Role of keto intermediates in the hydrodeoxygenation of phenol over Pd on oxophilic supports. ACS Catal. 5, 1318–1329 (2015).

    Article  Google Scholar 

  34. 34.

    de Souza, P. M. et al. Effect of zirconia morphology on hydrodeoxygenation of phenol over Pd/ZrO2. ACS Catal. 5, 7385–7398 (2015).

    Article  Google Scholar 

  35. 35.

    Bridgwater, A. V. Review of fast pyrolysis of biomass and product upgrading. Biomass Bioenergy 38, 68–94 (2012).

    CAS  Article  Google Scholar 

  36. 36.

    Ingram, L. et al. Pyrolysis of wood and bark in an auger reactor: physical properties and chemical analysis of the produced bio-oils. Energy Fuels 22, 614–625 (2008).

    MathSciNet  CAS  Article  Google Scholar 

  37. 37.

    Routray, K., Barnett, K. J. & Huber, G. W. Hydrodeoxygenation of pyrolysis oils. Energy Tech. 4, 1–15 (2016).

    Article  Google Scholar 

  38. 38.

    Nolte, M. W., Zhang, J. & Shanks, B. H. Ex situ hydrodeoxygenation in biomass pyrolysis using molybdenum oxide and low pressure hydrogen. Green Chem. 18, 134–138 (2016).

    Article  Google Scholar 

  39. 39.

    Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using. IFEFFIT J. Synchrotron Rad. 12, 537–541 (2005).

    CAS  Article  Google Scholar 

  40. 40.

    Koningsberger, D. C. & Prins, R. X-Ray Absorption: Principles, Applications, Techniques of EXAFS, SEXAFS, and XANES (John Wiley and Sons, 1988).

  41. 41.

    Rehr, J. J. & Albers, R. C. Theoretical approaches to X-ray absorption fine structure. Rev. Mod. Phys. 72, 621–654 (2000).

    ADS  CAS  Article  Google Scholar 

  42. 42.

    Joly, Y. X-ray absorption near-edge structure calculations beyond the muffin-tin approximation. Phys. Rev. B 63, 125120 (2001).

    ADS  Article  Google Scholar 

  43. 43.

    Bunau, O. & Joly, Y. Self-consistent aspects of X-ray absorption calculations. J. Phys. Condens. Matter 21, 345501 (2009).

    CAS  Article  PubMed  Google Scholar 

  44. 44.

    Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    ADS  CAS  Article  Google Scholar 

  45. 45.

    Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).

    ADS  CAS  Article  Google Scholar 

  46. 46.

    Perdew, J. P. et al. Restoring the density-gradient expansion for exchange in solids and surfaces. Phys. Rev. Lett. 100, 136406 (2008).

    ADS  Article  PubMed  Google Scholar 

  47. 47.

    Peng, Y. K. et al. Trimethylphosphine-assisted surface fngerprinting of metal oxide nanoparticle by 31P solid-state NMR: a zinc oxide case study. J. Am. Chem. Soc. 138, 2225–2234 (2016).

    CAS  Article  PubMed  Google Scholar 

  48. 48.

    Kreissl, H. T. et al. Niobium oxides: correlation of acidity with structure and catalytic performance in sucrose conversion to 5-hydroxymethylfurfural. J. Catal. 338, 329–339 (2016).

    CAS  Article  Google Scholar 

  49. 49.

    Stoll, S. & Schweiger, A. EasySpin, a comprehensive software package for spectral simulation and analysis in EPR. J. Magn. Reson. 178, 42–55 (2006).

    ADS  CAS  Article  PubMed  Google Scholar 

  50. 50.

    Louis, C. & Che, M. EPR investigation of the coordination sphere of Mo5+ ions on thermally reduced silica-supported molybdenum catalysts prepared by the grafting method. J. Phys. Chem. 91, 2875–2883 (1987).

    CAS  Article  Google Scholar 

Download references


H.D. thanks SCG Chemicals Co., Ltd and SCG Packaging Co., Ltd for funding. J.D. acknowledges support from the National Natural Science Foundation of China (Grant No. 11605225) and the Jianlin Xie Foundation of the Institute of High Energy Physics, Chinese Academy of Sciences. Q.W. and J.F. thank State Key Laboratory of Chemical Resource Engineering for funding. W.K.M. is supported by the UK EPSRC 281 (EP/L011972/1, grant to CAESR, the Centre for Advanced Spin Resonance). A.F.R.K. and J.-C.B. thank SCG Chemicals Co., Ltd for funding. A.F.R.K. thanks Wadham College Oxford for a RJP Williams Junior Research Fellowship. We also thank Hefei Light Source and Shanghai Light Source for use of the instruments. We thank Dr Nicholas H. Rees for performing the solid-state NMR spectroscopy; Drs Ashley Shepherd and Robert Jacobs for their help with TPR and BET measurements, Dr Yang He, Jinglu Huang, and Qu Chen for their comments on TEM results, Drs Yufei Song and Wei Chen for their valuable discussion on sample characterizations.

Author information




H.D. conceived the idea, designed and carried out the synthesis, characterizations and catalytic reactions, analyzed the data and wrote the manuscript. J.D. and D.C. performed XAFS data analysis and DFT calculation. X.G. performed DRIFTS measurement. Y.-K.P. prepared the samples for TMPO-adsorbed 31P NMR measurement and analyzed the data. W.C. performed the XAFS measurement and data analysis. T.I. initiated the idea, provided WIBO and discussion. W.K.M. performed the EPR measurement and data analysis. M.-J.L. analyzed the XAFS data. N.Y. performed GPC measurement. A.F.R.K. performed the SQUID measurement and data analysis. Y.W. performed XAFS measurement. X.Z. performed the XAFS measurement. S.J. assisted with TEM characterization. Q.W. and J.F. helped with DRIFTS measurement. J.-C.B. assisted in regulating the experiments and discussion. H.C. designed DRIFTS measurement and discussed results. Y.L. provided the resources for TEM characterization and XAFS measurement. S.C.E.T. and D.O.H. supervised the project, helped design the experiments, analyzed the data and wrote the manuscript. All the authors commented on the manuscript and have given approval to the final version of the manuscript.

Corresponding authors

Correspondence to Shik Chi Edman Tsang or Dermot O’Hare.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Duan, H., Dong, J., Gu, X. et al. Hydrodeoxygenation of water-insoluble bio-oil to alkanes using a highly dispersed Pd–Mo catalyst. Nat Commun 8, 591 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing