Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Broadband achromatic optical metasurface devices


Among various flat optical devices, metasurfaces have presented their great ability in efficient manipulation of light fields and have been proposed for variety of devices with specific functionalities. However, due to the high phase dispersion of their building blocks, metasurfaces significantly suffer from large chromatic aberration. Here we propose a design principle to realize achromatic metasurface devices which successfully eliminate the chromatic aberration over a continuous wavelength region from 1200 to 1680 nm for circularly-polarized incidences in a reflection scheme. For this proof-of-concept, we demonstrate broadband achromatic metalenses (with the efficiency on the order of 12%) which are capable of focusing light with arbitrary wavelength at the same focal plane. A broadband achromatic gradient metasurface is also implemented, which is able to deflect wide-band light by the same angle. Through this approach, various flat achromatic devices that were previously impossible can be realized, which will allow innovation in full-color detection and imaging.


Wavelength dispersion is a key characteristic of optical materials, which always plays an important role in designing optical components and systems. In most dielectrics like glasses, the index of refraction decreases with the longer wavelength, which is called normal chromatic dispersion1. Utilizing such materials, refractive lenses will perform larger focal lengths and prisms will deflect at a smaller angle for longer wavelength. Such chromatic aberration significantly degrades the performance of full-color optical applications, such as in communication, detection, imaging, displaying etc. Taking the refractive lenses as an example, complete elimination of chromatic aberration at three and four wavelengths is accomplished by integrating several materials arranged into a single component to achieve the same focal length, which are termed as apochromatic and superachromatic lens2, respectively. Although successful, this strategy adds weight, complexity and cost to optical systems, which greatly limits their usage.

In contrast to the traditional bulk optical elements, metasurfaces3,4,5,6 provide a new perspective on flexibly shaping the electromagnetic field7 by manipulating its phase, amplitude as well as polarization at will via a compact and easy-of-fabrication system. Such promising approaches prove their great features and functionality in a variety of applications, such as nonlinear dynamics8, light beam shaping9,10,11, highly dimensional holographic images12,13,14,15, polarization control and analysis16,17,18, invisible cloak carpet19 etc. In addition to the compact dimension, the main distinction between metalenses (planar lenses based on metasurfaces) and traditional optical lenses is the integrated functionality that allows the achievement of specific characteristics such as multispectral20, dual-functional21 and off-axis focusing22. Recent works reported the dielectric metasurfaces for metalens with high numerical aperture (NA) and optical planar camera with monochromatic aberrations that are comparable with the commercial products, presenting their potential prospect in real applications23, 24. However, these proposed metasurface devices still exhibit large chromatic aberration, which is mainly attributed to following fundamental properties: the resonant phase dispersion of the building blocks used in metasurfaces, the intrinsic dispersion in used materials, as well as the different phase accumulation through light propagation in free space with various wavelengths. Many works have shown that optical metasurfaces working in a relatively broad wavelength bandwidth can be achieved25,26,27,28,29,30. However, in these reports the optical performance of resonant elements in the metasurfaces is unchanged in a broad bandwidth and this is insufficient for the suppression of chromatic aberration.

Up to now, several pioneering works have realized multi-wavelength achromatic metalenses that are capable of eliminating the chromatic aberration at several discrete wavelengths31,32,33,34,35,36,37. Very recently, there has been a successful demonstration of an achromatic metalens which is able to suppress the chromatic effect over a 60-nm bandwidth in the visible38. However, although continuous, the working bandwidth (about 11.4% of the central wavelength) is still not broad enough for practical purposes and there is still lack of an effective design rule for unit elements in achromatic metasurface devices. Therefore, much work remains to be done in order to accomplish a broadband achromatic flat optical component working over a continuous bandwidth because of the abrupt phase change from the resonant unit elements. In this work, we employ the integrated-resonant unit element in metasurfaces with smooth and linear phase dispersion combining with geometric phase to design broadband achromatic flat optical components. For the proof of concept, achromatic converging metalenses and beam deflector with gradient metasurfaces are demonstrated that are valid at will within a broad infrared (IR) bandwidth from wavelength of 1200 to 1680 nm. The broadband achromatic metasurface devices based on our approach greatly innovate a complete class of designs in full-color light manipulation and imaging and push them forward to the practical applications.


Phase requirement of broadband achromatic metalens

As the most basic and important functional element, converging lens plays a crucial role in various optical systems. The typical distribution of phase retardation for a metalens follows:

$$\varphi \left( {R,\lambda } \right) = - \left[ {2{\rm{\pi }}\left( {\sqrt {{R^2}{\rm{ + }}{f^2}} - f} \right)} \right]\frac{{\rm{1}}}{\lambda }$$

where \(R{\rm{ = }}\sqrt {x_0^2{\rm{ + }}y_0^2} \) is the distance from arbitrary position (x 0, y 0) on the metalens to the center and f is the focal length. To realize a broadband achromatic metalens (BAML), which is schematically shown in the right side of Fig. 1a, such phase retardation with a fixed focal length is exactly required in a wide range of wavelength. Generally, for the case of working wavelength \({{\lambda }} \in \left\{ {{{{\lambda }}_{{\rm{min}}}},\quad {{{\lambda }}_{{\rm{max}}}}} \right\}\), with λ min and λ max being the boundaries of the interested wavelength band, the phase in Eq. 1 can be re-written as:

$${\varphi _{{\rm{Lens}}}}\left( {R,\lambda } \right) = \varphi \left( {R,{\lambda _{{\rm{max}}}}} \right){\rm{ + \Delta }}\varphi \left( {R,\lambda } \right)$$


$$\Delta \varphi \left( {R,\lambda } \right) = - \left[ {2\pi \left( {\sqrt {{R^2} + {f^2}} - f} \right)} \right]\left( {\frac{1}{\lambda } - \frac{1}{{{\lambda _{{\rm{max}}}}}}} \right)$$
Fig. 1

Achromatic metalens. a Schematic for chromatic (left) and achromatic (right) metalenses. In the case of chromatic metalens, the focal length is changed as the incident wavelength is switched, resulting in a rainbow-like focal line when it is illuminated by a light source with continuously changed wavelength. The focal point will become a single spot for the case of BAML with optimized phase compensation. b Phase profile for a BAML at arbitrary wavelength of λ {λ min, λ max}

The BAML can only be realized once these two key phase characteristics are exactly satisfied simultaneously; therefore, the designed phase of BAML can be accordingly divided into two components. The former part in Eq. 2, φ(R, λ max), is considered as a basic phase profile, which is only related with λ max and is independent to the working wavelength λ. Such phase profile can be acquired by exploiting the geometric phase as the phase modulation in each metalens unit element. The geometric phase, also called Berry phase, is produced from the rotation of the resonant elements in metasurface with a circularly-polarized incidence39. The produced phase modulation only depends on the orientation of scattered elements, which can therefore work as the solution for the wavelength-independent phase modulation. In contrary, the latter part in Eq. 2, Δφ(R, λ), is a function of working wavelength and presents a linear relation with 1/λ, which is considered as the phase difference between various incident wavelengths. Such phase difference can be obtained by suitably designing the phase response of each unit element of the metalens, which must also exhibit the phase dispersion owning a linear relation with 1/λ, in consistent with Δφ (R, λ). Since the mechanism of this resonant phase response is completely different from the geometric phase, these two parts of phase won’t disturb with each other, but can be simply merged together.

It should be mentioned that an additional phase shift φ shift(λ) can be introduced to optimize the phase compensation effect from the specially designed metalens, since such phase shift won’t affect the focusing property of the metalens34, as shown in Fig. 1b. Then, the phase profile of the achromatic metalens is changed to

$$\varphi' _{{\rm{Lens}}} \left( {R,\lambda } \right) = - \left[ {2\pi \left( {\sqrt {{R^2} + {f^2}} - f} \right)} \right]\frac{1}{\lambda } + {\varphi _{{\rm{shift}}}}(\lambda )$$

The phase difference consequently becomes \({\rm{\Delta }}\varphi '\left( {R,\lambda } \right) = {\rm{\Delta }}\varphi \left( {R,\lambda } \right){\rm{ + }}{\varphi _{{\rm{shift}}}}\left( \lambda \right)\). To maintain the linear relation with 1/λ, φ shift(λ) has to match the form as φ shift (λ) = α/λ + β, with \(\alpha = \chi \frac{{{\lambda _{{\rm{max}}}}{\lambda _{{\rm{min}}}}}}{{{\lambda _{{\rm{max}}}} - {\lambda _{{\rm{min}}}}}}\) and \(\beta = - \chi \frac{{{\lambda _{{\rm{min}}}}}}{{{\lambda _{{\rm{max}}}} - {\lambda _{{\rm{min}}}}}}\), where χ denotes the largest additional phase shift between λ min and λ max at the central position of the BAML. It is the key parameter in the design of BAML, especially for the determination of the diameter of BAML. How to design special unit elements to compensate the phase difference at corresponding position is subsequently the crucial issue. Here, for a proof-of-concept demonstration, the working wavelength is chosen in the commonly used telecom region, i.e., {λ min, λ max}→{1200, 1680 nm}.

Design of integrated-resonant unit elements

In our design, the basic building blocks of the BAML are metallic nano-rods (MNRs) and their assemblies, coupled MNRs. The metal-dielectric-metal structural configuration (insets in Fig. 2) is implemented to access a cavity-like resonance so as to enhance the operating efficiency of metasurfaces40, 41. Generally, a single MNR is able to support multiple plasmonic resonances, such as the fundamental dipolar mode and various high order modes. An abrupt phase shift usually occurs when these plasmonic resonances are excited, which does not fit the requirement of smooth and linear phase difference Δφ′(R, λ) (Supplementary Fig. 1). In contrast, the phase distribution between these resonances exhibits a smooth trend with a nearly linear profile against 1/λ. Since such state is fall in between the two strong resonant modes, it could be termed as an integrated-resonant state. In addition, such integrated-resonant features provide a promising method to slickly compensate the phase difference for BAML. Moreover, since the produced phase compensation owns a linear relation with of 1/λ, the BAML will naturally be achieved at any wavelength within the working bandwidth as long as the largest phase difference Δφ′(R, λ min) is exactly compensated by the designed unit elements.

Fig. 2

Phase profile of integrated-resonant unit elements based on coupled nano-rods. a, c, e RCP-to-LCP polarization conversion efficiency (red curves), phase profile (blue curves) and (b, d, f) electric field distribution (color mapping) of integrated-resonant unit elements. Each unit element with 550 nm periods along x and y axes consists of one or several gold MNRs with fixed thickness 30 nm. The MNRs stand on a SiO2/Au substrate with varying gap size, length and width are optimized to achieve various phase compensation between λ min and λ max (Supplementary Tables 1 and 2). The thickness of dielectric spacer SiO2 is 60 nm. Gray region and black arrows remark the range of working bandwidth of BAML and positions of resonant modes, respectively

Due to linear relation of the phase distribution, the slope S in the phase spectrum can be directly obtained as \(S = C{\rm{/}}\left( {\frac{1}{{{{\it{\lambda }}_{R{\rm{1}}}}}}} \right) - \left( {\frac{1}{{{{\it{\lambda }}_{R{\rm{2}}}}}}} \right)\), where λ R1 and λ R2 are the resonant wavelengths of the MNR, and C is a constant. This indicates that the slope of the phase profile can be tuned via tuning the wavelength distance between two resonances. Therefore, one can effectively steer the phase compensation δ(λ) provided by the integrated-resonant unit elements composed of MNRs or coupled MNRs, which obeys \(\delta \left( \lambda \right) = S\left( {\frac{1}{\lambda } - \frac{1}{{{\lambda _{{\rm{max}}}}}}} \right) = C\left( {\frac{1}{\lambda } - \frac{1}{{{\lambda _{{\rm{max}}}}}}} \right){\rm{/}}\left( {\frac{1}{{{\lambda _{R1}}}} - \frac{1}{{{\lambda _{R2}}}}} \right)\). The largest phase compensation produced by these unit elements between λ min and λ max therefore becomes \(\delta = C\left( {\frac{1}{{{\lambda _{{\rm{min}}}}}} - \frac{1}{{{\lambda _{{\rm{max}}}}}}} \right){\rm{/}}\left( {\frac{1}{{{\lambda _{R1}}}} - \frac{1}{{{\lambda _{R2}}}}} \right)\), which can be directly utilized to cover the largest phase difference Δφ′(R, λ min) required at any position in BAML.

For the case of slight slope S corresponding to the small phase compensation, a single MNR with large aspect ratio is utilized, in which the fundamental dipole mode and high order mode are excited. When the wavelengths of these two plasmonic modes are tuned far away from each other, the small phase compensation is realized. The detail information of the single MNR structure with large aspect ratio can be found in Supplementary Fig. 2. To improve the operating efficiency, multiple MNRs are integrated within an integrated-resonant unit element. Following this approach, the smallest phase compensation, also a key parameter for determining the size of BAML, can be achieved at around 30˚, as shown in Fig. 2a. The electric field distributions at the wavelengths corresponding to the dipole mode and second order plasmonic mode are respectively plotted in Fig. 2b.

The larger phase compensation can be acquired by decreasing the difference between two resonant wavelengths of the MNR. With the aspect ratio of the MNR decreasing, the dipole mode along its short axis can be excited instead of the second order plasmonic modes, being the nearest resonant mode from the dipole mode along the long axis. With the wavelength distance between these two modes shrinking, larger phase compensation is obtained. As shown in Fig. 2c, two dipole modes can be evidently observed in the operation efficiency spectrum, in which 120˚ phase compensation is realized. The electric field distributions at these two resonant wavelengths are shown in Fig. 2d, which obviously indicates their identities.

It will turn into another issue when the phase compensation is larger than 150˚ in such integrated-resonant MNRs, in that case steering the relation between two resonances is insufficient, and one more resonance is necessary to be introduced into the working wavelength region. However, it is quite challenging to exhibit three resonances within the concerning wavelength band using single MNR. Therefore, a compound structure composed of two perpendicularly aligned MNRs with different lengths and widths is utilized to introduce the third plasmonic resonant mode. Assuming that the second resonant wavelength λ R2 located near the middle of resonant wavelength region {λ R1, λ R3}, the slopes of phase spectrum of two wavelength regions {λ R1, λ R2} and {λ R2, λ R3} can be close to \({S_{21}}{\rm{ = }}{C_{21}}{\rm{/}}\left( {\frac{1}{{{\lambda _{R1}}}} - \frac{1}{{{\lambda _{R2}}}}} \right)\sim{S_{32}}{\rm{ = }}{C_{32}}{\rm{/}}\left( {\frac{1}{{{\lambda _{R2}}}} - \frac{1}{{{\lambda _{R3}}}}} \right)\), assuming C 21C 32 = C. Thus, the entire phase slope S can be expressed as \(S \sim 2C{\rm{/}}\left( {\frac{1}{{{\lambda _{R1}}}} - \frac{1}{{{\lambda _{R3}}}}} \right)\), which can theoretically be two times larger than the single MNR case. Figure 2e presents the case of 210˚ phase compensation between λ min and λ max after structural optimization with three resonances. The corresponding electric field distributions are also provided to recognize which individual MNR these resonances belonging to, as shown in Fig. 2f. Based on this approach, the largest phase compensation can reach to even 360°, with a fairly good efficiency at most wavelengths (Supplementary Fig. 3). In fact, the phase compensation can be further increased by introducing more resonances to the integrated-resonant unit element, which will enable a BAML with larger size (Supplementary Fig. 10).

Characterizations of the BAML

Employing the proposed policy, a broadband achromatic converging metalens with numerical aperture (NA) = 0.268 is designed and demonstrated. Figure 3a shows the optical image of the fabricated metalens, which has a diameter of 55.55 μm and designed focal length of 100 μm. This metalens was fabricated using standard electron beam lithography (see Methods section for details). The measured focal spots show the highly symmetric profiles, performing a good ability on light convergence in designed BAML. The focal spot at the middle of the working wavelength range, 1500 nm, is presented as an example in Fig. 3b. Figure 3c presents the zoom-in scanning electron microscope (SEM) image, in which a set of integrated-resonant MNRs with accurate gap sizes are observed. To capture the light intensity distribution, a couple of optical components including an IR objective and an IR coupled charge device (CCD) are moved together along the propagation direction of reflected light at different x–y planes (see Supplementary Fig. 7 for details of measurement setup). The right-hand circular polarization (RCP) to left-hand circular polarization (LCP) light intensity profiles on xz plane is subsequently obtained from stitching all captured images together. Figure 3d shows that the measured and simulated light intensity profiles along the cross section plane are in a good agreement with each other. As theoretical predication, the focal length keeps almost unchanged while incident wavelength varies, indicating the realization of a broadband achromatic converging property in near-IR region.

Fig. 3

Verification of achromatic converging metalens. a Optical image of fabricated metalens with NA = 0.268. b Measured light intensity of focal spot at incident wavelength λ = 1500 nm. c Zoom-in scanning electron microscope (SEM) image of fabricated metalens. More images and design details can be found in the Supplementary Note 3. d Experimental (top row) and numerical (bottom row) intensity profiles of BAML along axial planes at various incident wavelengths

For optical characteristics of the designed metalens, the focal lengths vs. incident wavelength of both achromatic and chromatic metalenses are measured. Figure 4a shows the results of three achromatic metalenses with different NA values, which exhibits unchanged focal length with varied incident wavelength. These results confirmed again that the designed BAML is able to focus the incident light at the same focal plane in a continuous and wide range of wavelength (~33.3% of the central wavelength). Such perfect achromatic property can be realized from metalens with various NA values. To the best of our knowledge, this is the state-of-the-art demonstration of an achromatic metalens, which is able to completely eliminate the chromatic effect over the broadest wavelength range at continuously changed steps. In contrast to the BAML, the focal length of chromatic metalenses (which is designed and fabricated using Berry phase based metasurfaces) strongly depends on the incident wavelength. For comparison, the phase distributions of chromatic metalenses are designed for similar NA values with the achromatic ones at the longest wavelength in the interested wavelength range (Supplementary Note 4). The obvious chromatic aberration can be observed with evident focal length enlarging as the wavelength decreasing in all three metalenses, shown in Fig. 4b.

Fig. 4

Performance of broadband achromatic metalens. Measured and simulated focal length of a BAML with various NA values and b chromatic metalenses. Measured c FWHM and d operation efficiency at corresponding focal plane as a function of wavelength. The efficiency is defined as the ratio of light intensity from the focal spot at corresponding focal plane to the light intensity reflected by a metallic mirror with the same pixel sizes. The error bars present the length of distance from the focal plane where the intensity of focal spot remains the maximum value in measurements

To further examine the working performance of designed BAML, full-width at half-maximum (FWHM) and operating efficiency are measured at near-IR region, as shown in Figs. 4c and 4d. The FWHM, which is defined as the beam waist of the normalized light intensity at 0.5, is estimated by fitting the measured light intensity along the focal line with Gaussian function. All measured FWHM are located at the range of 1.5λ~2λ that are nearly diffraction-limited. The maximum focusing efficiency of 8.4, 12.44 and 8.56% were measured for BAML with NA = 0.217, 0.268 and 0.324, respectively. The focusing efficiency drops at the boundaries of measured wavelength region is due to the lower polarization conversion efficiency of utilized unit elements at λ min and λ max. Though the efficiency spectrum shows some fluctuations in the operating wavelength range, which is the inevitable corollary from the introduction of the integrated-resonant unit elements, the average working efficiency can be further increased by replacing the material components with dielectrics or further optimizing the structural configuration42, 43.

Design and characterizations of the broadband achromatic gradient metasurface

Generally, our design principle can be used to realize various flat optical components without chromatic effect like the broadband achromatic gradient metasurface (BAGMS). The design of a BAGMS to deflect a normally incident light by the same angle in a broad wavelength range is demonstrated (Fig. 5a). The building blocks are the same as those used in the above achromatic metalens, and the orientation of each unit element is designed to obey the required phase distribution:

$$\varphi \left( {x,\lambda } \right){\rm{ = }} - \frac{{2\pi }}{\lambda }x\sin {\theta _{\rm{d}}}$$

where x is the spatial coordinate and θ d is the reflected angle of anomalous beam, namely the LCP light beam reflection with RCP incidence. To realize the phase requirement for deflecting light with the same θ d at different incident wavelengths, the specially designed unit elements with proper orientation are implemented to compensate the phase difference Δφ (x, λ), as shown in Fig. 5b. The detailed information of design is shown in Supplementary Note 5. As predicted, all the LCP light reflected angles are kept almost unchanged when the incident wavelength is changed from 1200 to 1650 nm, showing a broadband achromatic performance in anomalous beam deflection (see Fig. 5c). It is further experimentally verified by capturing the scattering light through a slight focus (see Supplementary Fig. 8 for the optical measurement). Figure 5d presents the SEM image of the fabricated sample. As shown in Fig. 5e, the beam spot keeps in the center of CCD while the incident wavelength changed, presenting a good agreement with the numerical simulation. The anomalous reflected LCP beam can only be observed with cross-polarized component, which is also verified by changing the polarization state from detection.

Fig. 5

Broadband achromatic gradient metasurfaces. a Schematic of beam deflection with BAGMS. All anomalously deflected angles are the same when the incident wavelength is changed. b Phase distribution for a BAGMS at different incident wavelengths. The Δφ(x, λ) represents the phase difference between λ min and λ max at certain surface position. c Simulated intensity of RCP-to-LCP scattering light vs. angle of reflection at various incident wavelengths. The angle of reflection keeps at around 22.26˚ when the incident wavelength is changed from 1200 to 1650 nm. d SEM image of fabricated BAGMS. e (Left) Experimentally captured CCD images of RCP-to-LCP scattering light from the BAGMS. The intensities are normalized by the maximum value in each image. (Right) Cross section of normalized scattering light intensity along the central line of each corresponding CCD image for RCP-to-LCP (navy curves) and RCP-to-RCP (olive curves) components


Compared with the flat optical devices using the strong resonance based unit elements, our design employs the integrated-resonant unit elements that enable the achromatic ability in a continuously broad wavelength band. Theoretically, the BAML with very high NA can also be realized with our design principle. For example, a BAML with NA as high as 0.86 is achieved with a smaller dimension (see Supplementary Fig. 9). Although the feature size of achromatic metalenses with a fixed NA is limited by the largest phase compensation, namely the largest additional phase shift χ, it can be further increased through structural optimization by introducing more resonances/resonators into the integrated-resonant unit elements (Supplementary Note 8). We also would like to emphasize that the proposed design principle is not only valid to the reflective metasurface devices but can also be employed for metasurface devices in a transmission scheme if one can successfully introduce transparent integrated-resonant unit elements into the devices. One of the promising candidates is high-index dielectric metasurfaces, where multiple Fabry-Pérot resonances are realized because they can be regarded as truncated cross-sectional waveguides44. The versatility in the selective change of phase distribution and control of chromatic dispersion is beneficial for the development of specific functionalities like opposite phase dispersion and phase mismatch in nonlinear optical cavity that are difficult to be accomplished from bulky chromatic systems.

In summary, achromatic metasurface devices which can suppress the chromatic aberration in a wide wavelength range with continuous bandwidth are demonstrated. Through exploiting geometric phase combining with phase compensation from specially designed integrated-resonant unit elements, the metasurfaces can provide the exact phase profile as the ideal requirement for broadband achromatic flat optical devices like converging metalens and metasurface deflector. Although demonstrations in the near-IR regime, the working wavelength of proposed achromatic metasurface devices can be further pushed into the visible light by using aluminum or all-dielectric based unit elements as the building blocks. Our design paves an innovate class to control the phase dispersion at will and it will greatly advance the development of innovative metadevices in full color control to reach real practical applications.


Sample Fabrication

A 150-nm-thick Au mirror and a 3-nm-thick Cr were first deposited on a Si substrate by e-gun evaporator. A 60-nm-thick SiO2 dielectric spacer is then deposited by using plasma-enhanced chemical vapor deposition (PECVD). A 100-nm-thick ZEP520A layer is consequently spin coated at 5000 rpm on the prepared substrate and then bake on a hot plate for 2 min at 180 °C. Subsequently, an Espacer layer is spin coated at 1500 rpm on the ZEP520A layer. Espacer is an organic polymer with high conductivity to reduce the positional error during the e-beam exposure process. An e-beam writing system at the acceleration voltage of 100 keV with 100 pico-ampere of current is used. The structural profile of metasurfaces is defined by the e-beam exposure and development process. The final sample will be obtained after the 3-nm-thick Cr and 30-nm-thick Au deposition and lift-off process.

Numerical simulation

All numerical simulations were performed by using the commercial software Computer Simulation Technology (CST) Microwave Studio. For the design of unit elements, a unit cell boundary condition is employed for the simulation of reflection spectra and phase profile in an array configuration. For simplicity, perfect matched layer (PML) and periodic boundary conditions are respectively used for x and y direction for the simulation of metalenses; that is, cylindrical lenses are simulated to simply evaluate the focal length of each metalens. In the case of gradient metasurfaces, PML is employed as the boundary condition for all boundaries to mimic a free space for far-field scattering simulation. The refractive index of SiO2 is obtained from ref. 45. The permittivity of gold in the near-IR regime is described by the Lorentz–Drude model with three times damping constant larger than the bulky material.

Data availability

The data that support the findings of this study are available from the authors on reasonable request, see author contributions for specific data sets.


  1. 1.

    Hecht, E. Optics (Addison Wesley, 3, 1997).

  2. 2.

    Pedrotti, F. L. & Pedrotti, L. S. Introduction to Optics (Prentice-Hall, 1987).

  3. 3.

    Zhang, L., Mei, S., Huang, K. & Qiu, C.-W. Advances in full control of electromagnetic waves with metasurfaces. Adv. Opt. Mater. 4, 818–833 (2016).

    CAS  Article  Google Scholar 

  4. 4.

    Arbabi, A., Horie, Y., Bagheri, M. & Faraon, A. Dielectric metasurfaces for complete control of phase and polarization with subwavelength spatial resolution and high transmission. Nat. Nano 10, 937–943 (2015).

    CAS  Article  Google Scholar 

  5. 5.

    Yu, N. & Capasso, F. Flat optics with designer metasurfaces. Nat. Mater. 13, 139–150 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  6. 6.

    Minovich, A. E. et al. Functional and nonlinear optical metasurfaces. Laser Photon. Rev 9, 195–213 (2015).

    Article  Google Scholar 

  7. 7.

    Pu, M. et al. Catenary optics for achromatic generation of perfect optical angular momentum. Sci. Adv. 1, e1500396 (2015).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  8. 8.

    Lysenko, O., Bache, M., Olivier, N., Zayats, A. V. & Lavrinenko, A. Nonlinear dynamics of ultrashort long-range surface plasmon polariton pulses in gold strip waveguides. ACS Photon. 3, 2324–2329 (2016).

    CAS  Article  Google Scholar 

  9. 9.

    Chen, X., Zhang, Y., Huang, L. & Zhang, S. Ultrathin metasurface laser beam shaper. Adv. Opt. Mater. 2, 978–982 (2014).

    CAS  Article  Google Scholar 

  10. 10.

    Walther, B. et al. Spatial and spectral light shaping with metamaterials. Adv. Mater. 24, 6300–6304 (2012).

    CAS  Article  PubMed  Google Scholar 

  11. 11.

    Liu, H. et al. Twisted focusing of optical vortices with broadband flat spiral zone plates. Adv. Opt. Mater. 2, 1193–1198 (2014).

    ADS  Article  Google Scholar 

  12. 12.

    Wen, D. et al. Helicity multiplexed broadband metasurface holograms. Nat. Commun. 6, 8241 (2015).

    Article  PubMed  PubMed Central  Google Scholar 

  13. 13.

    Huang, L. et al. Broadband hybrid holographic multiplexing with geometric metasurfaces. Adv. Mater. 27, 6444–6449 (2015).

    CAS  Article  PubMed  Google Scholar 

  14. 14.

    Huang, Y.-W. et al. Aluminum plasmonic multicolor meta-hologram. Nano. Lett. 15, 3122–3127 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  15. 15.

    Wang, L. et al. Grayscale transparent metasurface holograms. Optica 3, 1504–1505 (2016).

    Article  Google Scholar 

  16. 16.

    Li, L. et al. Plasmonic polarization generator in well-routed beaming. Light Sci. Appl 4, e330 (2015).

    CAS  Article  Google Scholar 

  17. 17.

    Wu, P. C. et al. Versatile polarization generation with an aluminum plasmonic metasurface. Nano. Lett. 17, 445–452 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  18. 18.

    Chen, W. T. et al. Integrated plasmonic metasurfaces for spectropolarimetry. Nanotechnology 27, 224002 (2016).

    ADS  Article  PubMed  Google Scholar 

  19. 19.

    Ni, X., Wong, Z. J., Mrejen, M., Wang, Y. & Zhang, X. An ultrathin invisibility skin cloak for visible light. Science 349, 1310–1314 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  20. 20.

    Khorasaninejad, M. et al. Multispectral chiral imaging with a metalens. Nano. Lett. 16, 4595–4600 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  21. 21.

    Chen, X. et al. Dual-polarity plasmonic metalens for visible light. Nat. Commun. 3, 1198 (2012).

    Article  PubMed  PubMed Central  Google Scholar 

  22. 22.

    Khorasaninejad, M., Chen, W. T., Oh, J. & Capasso, F. Super-dispersive off-axis meta-lenses for compact high resolution spectroscopy. Nano Lett. 16, 3732–3737 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  23. 23.

    Khorasaninejad, M. et al. Metalenses at visible wavelengths: Diffraction-limited focusing and subwavelength resolution imaging. Science 352, 1190–1194 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  24. 24.

    Arbabi, A. et al. Miniature optical planar camera based on a wide-angle metasurface doublet corrected for monochromatic aberrations. Nat. Commun. 7, 13682 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  25. 25.

    Huang, L. et al. Dispersionless phase discontinuities for controlling light propagation. Nano Lett. 12, 5750–5755 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  26. 26.

    Li, Z., Palacios, E., Butun, S. & Aydin, K. Visible-frequency metasurfaces for broadband anomalous reflection and high-efficiency spectrum splitting. Nano Lett. 15, 1615–1621 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  27. 27.

    Liu, L. et al. Broadband metasurfaces with simultaneous control of phase and amplitude. Adv. Mater. 26, 5031–5036 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  28. 28.

    Jiang, S.-C. et al. High-efficiency generation of circularly polarized light via symmetry-induced anomalous reflection. Phys. Rev. B 91, 125421 (2015).

    ADS  Article  Google Scholar 

  29. 29.

    High, A. A. et al. Visible-frequency hyperbolic metasurface. Nature. 522, 192–196 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  30. 30.

    Wu, P. C. et al. Broadband wide-angle multifunctional polarization converter via liquid-metal-based metasurface. Adv. Opt. Mater. 5, 1600938 (2017).

    Article  Google Scholar 

  31. 31.

    Khorasaninejad, M. et al. Achromatic metasurface lens at telecommunication wavelengths. Nano. Lett. 15, 5358–5362 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  32. 32.

    Wang, P., Mohammad, N. & Menon, R. Chromatic-aberration-corrected diffractive lenses for ultra-broadband focusing. Sci. Rep. 6, 21545 (2016).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  33. 33.

    Zhao, Z. et al. Multispectral optical metasurfaces enabled by achromatic phase transition. Sci. Rep. 5, 15781 (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  34. 34.

    Aieta, F., Kats, M. A., Genevet, P. & Capasso, F. Multiwavelength achromatic metasurfaces by dispersive phase compensation. Science 347, 1342–1345 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  35. 35.

    Arbabi, E., Arbabi, A., Kamali, S. M., Horie, Y. & Faraon, A. Multiwavelength polarization-insensitive lenses based on dielectric metasurfaces with meta-molecules. Optica 3, 628–633 (2016).

    CAS  Article  Google Scholar 

  36. 36.

    Hu, J., Liu, C.-H., Ren, X., Lauhon, L. J. & Odom, T. W. Plasmonic lattice lenses for multiwavelength achromatic focusing. ACS Nano 10, 10275–10282 (2016).

    CAS  Article  PubMed  Google Scholar 

  37. 37.

    Deng, Z.-L., Zhang, S. & Wang, G. P. Wide-angled off-axis achromatic metasurfaces for visible light. Opt. Express 24, 23118–23128 (2016).

    ADS  Article  PubMed  Google Scholar 

  38. 38.

    Khorasaninejad, M. et al. Achromatic metalens over 60 nm bandwidth in the visible and metalens with reverse chromatic dispersion. Nano Lett. 17, 1819–1824 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  39. 39.

    Kang, M., Feng, T., Wang, H.-T. & Li, J. Wave front engineering from an array of thin aperture antennas. Opt. Express 20, 15882–15890 (2012).

    ADS  Article  PubMed  Google Scholar 

  40. 40.

    Sun, S. et al. High-Efficiency Broadband anomalous reflection by gradient meta-surfaces. Nano Lett. 12, 6223–6229 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  41. 41.

    Pors, A. & Bozhevolnyi, S. I. Plasmonic metasurfaces for efficient phase control in reflection. Opt. Express 21, 27438–27451 (2013).

    ADS  Article  PubMed  Google Scholar 

  42. 42.

    Pu, M. et al. Spatially and spectrally engineered spin-orbit interaction for achromatic virtual shaping. Sci. Rep. 5, 9822 (2015).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  43. 43.

    Zheng, G. et al. Metasurface holograms reaching 80% efficiency. Nat. Nano 10, 308–312 (2015).

    CAS  Article  Google Scholar 

  44. 44.

    Arbabi, A., Horie, Y., Ball, A. J., Bagheri, M. & Faraon, A. Subwavelength-thick lenses with high numerical apertures and large efficiency based on high-contrast transmitarrays. Nat. Commun. 6, 7069 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  45. 45.

    Ghosh, G. Dispersion-equation coefficients for the refractive index and birefringence of calcite and quartz crystals. Opt. Commun. 163, 95–102 (1999).

Download references


We acknowledge financial support from National Key R&D Program of China (2016YFA0202103,2017YFA0303700), National Natural Science Foundation of China (No. 11674167, 11621091, and 11322439), Ministry of Science and Technology, Taiwan (Grant No. MOST-105–2745-M-002-005-ASP) and Academia Sinica (Grant No. AS-103-TP-A06). They are also grateful to National Center for Theoretical Sciences, NEMS Research Center of National Taiwan University, National Center for High-Performance Computing, Taiwan, and Research Center for Applied Sciences, Academia Sinica, Taiwan for their supports. T.L. thanks the support from Dengfeng Project B of Nanjing University.

Author information




S.M.W. and P.C.W. developed the theoretical aspects, performed the numerical design and optical measurement, data analysis and wrote the manuscript; V.C.S. performed the sample preparation and data analysis; Y.C.L. and C.H.C. carried out the simulation; J.W.C. and S.H.L. fabricated the samples; J.C. and B.B.X. built up the optical system for measurement; C.H.K. analyze the data; T.L., S.N.Z. and D.P.T. organized the project, designed experiments, analyzed the results, and prepare the manuscripts. All authors discussed the results and commented on the manuscript.

Corresponding authors

Correspondence to Shuming Wang, Tao Li, Shining Zhu or Din Ping Tsai.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wang, S., Wu, P.C., Su, VC. et al. Broadband achromatic optical metasurface devices. Nat Commun 8, 187 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing