Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Original Article
  • Published:

Facile synthesis of acrylamide derivative copolymers with side urethane groups for systematic variation of the thermoresponsive behavior


A simple method to finely control the thermoresponsive properties of polymers over a wide range of temperatures is to enhance the versatility of the thermoresponsive polymers. One such useful technique is the radical copolymerization of two types of monomers with similar copolymerization reactivities, which allows the hydrophilicity/hydrophobicity balance in the polymer structure to be easily tuned. In this study, we focused on a urethane-containing monomer as the key compound, which can be easily obtained by the reaction between an isocyanate and a hydrophilic precursor monomer containing a hydroxy group. A variety of urethane-embedded acrylamide monomers with different alkyl side chains (ethyl: EtUAAm, n-butyl: BuUAAm, and n-hexyl: HexUAAm) were synthesized from 2-hydroxyethylacrylamide (HEAAm) and alkyl isocyanates. Copolymers of HEAAm and EtUAAm with different compositions were prepared by reversible addition-fragmentation chain transfer (RAFT) polymerization. The obtained copolymer with a high urethane composition (>67%) exhibited a lower critical solution temperature (LCST)-type thermoresponse in water due to the hydrophobic interaction and hydrogen bonding derived from the urethane side groups. The response temperature could be widely varied by altering the composition, molecular weight, end groups and alkyl side chains of the urethane monomer.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others


  1. Alarcón CdlH, Pennadam S, Alexander C. Stimuli responsive polymers for biomedical applications. Chem Soc Rev. 2005;34:276–85.

    Article  Google Scholar 

  2. Schmaljohann D. Thermo- and pH-responsive polymers in drug delivery. Adv Drug Deliv Rev. 2006;58:1655–70.

    Article  CAS  PubMed  Google Scholar 

  3. Cook MT, Haddow P, Kirton SB, McAuley WJ. Polymers Exhibiting Lower Critical Solution Temperatures as a Route to Thermoreversible Gelators for Healthcare. Adv Funct Mater. 2021;31:2008123.

    Article  CAS  Google Scholar 

  4. Constantinou AP, Wang L, Wang S, Georgiou TK. Thermoresponsive block copolymers of increasing architecture complexity: a review on structure–property relationships. Polym Chem. 2023;14:223–47.

    Article  CAS  Google Scholar 

  5. Bergbreiter DE, Case BL, Liu Y-S, Caraway JW. Poly(N-isopropylacrylamide) Soluble Polymer Supports in Catalysis and Synthesis. Macromolecules. 1998;31:6053–62.

    Article  CAS  Google Scholar 

  6. Kanaoka S, Yagi N, Fukuyama Y, Aoshima S, Tsunoyama H, Tsukuda T, et al. Thermosensitive Gold Nanoclusters Stabilized by Well-Defined Vinyl Ether Star Polymers:  Reusable and Durable Catalysts for Aerobic Alcohol Oxidation. J Am Chem Soc. 2007;129:12060–1.

    Article  CAS  PubMed  Google Scholar 

  7. Lokuge I, Wang X, Bohn PW. Temperature-Controlled Flow Switching in Nanocapillary Array Membranes Mediated by Poly(N-isopropylacrylamide) Polymer Brushes Grafted by Atom Transfer Radical Polymerization. Langmuir. 2007;23:305–11.

    Article  CAS  PubMed  Google Scholar 

  8. Zhang M, Vora A, Han W, Wojtecki RJ, Maune H, Le ABA, et al. Dual-Responsive Hydrogels for Direct-Write 3D Printing. Macromolecules. 2015;48:6482–8.

    Article  CAS  Google Scholar 

  9. Halperin A, Kröger M, Winnik FM. Poly(N-isopropylacrylamide) Phase Diagrams: Fifty Years of Research. Angew Chem Int Ed. 2015;54:15342–67.

    Article  CAS  Google Scholar 

  10. Bütün V, Armes SP, Billingham NC. Synthesis and aqueous solution properties of near-monodisperse tertiary amine methacrylate homopolymers and diblock copolymers. Polymer. 2001;42:5993–8.

    Article  Google Scholar 

  11. Xia Y, Burke NAD, Stöver HDH. End Group Effect on the Thermal Response of Narrow-Disperse Poly(N-isopropylacrylamide) Prepared by Atom Transfer Radical Polymerization. Macromolecules. 2006;39:2275–83.

    Article  CAS  Google Scholar 

  12. Lang X, Patrick AD, Hammouda B, Hore MJA. Chain terminal group leads to distinct thermoresponsive behaviors of linear PNIPAM and polymer analogs. Polymer. 2018;145:137–47.

    Article  CAS  Google Scholar 

  13. Katsumoto Y, Kubosaki N. Tacticity Effects on the Phase Diagram for Poly(N-isopropylacrylamide) in Water. Macromolecules. 2008;41:5955–6.

    Article  CAS  Google Scholar 

  14. Nishi K, Hiroi T, Hashimoto K, Fujii K, Han Y-S, Kim T-H, et al. SANS and DLS Study of Tacticity Effects on Hydrophobicity and Phase Separation of Poly(N-isopropylacrylamide). Macromolecules. 2013;46:6225–32.

    Article  CAS  Google Scholar 

  15. Hirano T, Miki H, Seno M, Sato T. Effect of polymerization conditions on the syndiotactic-specificity in radical polymerization of N-isopropylacrylamide and fractionation of the obtained polymer according to the stereoregularity. Polymer. 2005;46:5501–5.

    Article  CAS  Google Scholar 

  16. Li X, ShamsiJazeyi H, Pesek SL, Agrawal A, Hammouda B, Verduzco R. Thermoresponsive PNIPAAM bottlebrush polymers with tailored side-chain length and end-group structure. Soft Matter. 2014;10:2008–15.

    Article  CAS  PubMed  Google Scholar 

  17. Ida S, Toyama Y, Takeshima S, Kanaoka S. Thermoresponsive core cross-linked star-shaped poly(N-isopropylacrylamide) for reversible and controlled aggregation of nanoscale molecular units. Polym J. 2020;52:359–63.

    Article  CAS  Google Scholar 

  18. Sharker KK, Takeshima S, Toyama Y, Ida S, Kanaoka S, Yusa S-i. pH- and thermo-responsive behavior of PNIPAM star containing terminal carboxy groups in aqueous solutions. Polymer. 2020;203:122735.

    Article  CAS  Google Scholar 

  19. Terao K, Masahiro A, Nagase M, Takeshima S, Ida S, Kanaoka S. Temperature-Induced Nanostructure Formation Behavior of Core Cross-Linked Star-Shaped Poly(N-isopropylacrylamide) in Water. Macromolecules. 2023;56:5635–41.

    Article  CAS  Google Scholar 

  20. Feil H, Bae YH, Feijen J, Kim SW. Effect of Comonomer Hydrophilicity and Ionization on the Lower Critical Solution Temperature of N-isopropylacrylamide Copolymers. Macromolecules. 1993;26:2496–500.

    Article  CAS  Google Scholar 

  21. Takei YG, Aoki T, Sanui K, Ogata N, Okano T, Sakurai Y. Temperature-responsive bioconjugates. 2. Molecular design for temperature-modulated bioseparations. Bioconjugate Chem. 1993;4:341–6.

    Article  CAS  Google Scholar 

  22. Park J-S, Kataoka K. Precise Control of Lower Critical Solution Temperature of Thermosensitive Poly(2-isopropyl-2-oxazoline) via Gradient Copolymerization with 2-Ethyl-2-oxazoline as a Hydrophilic Comonomer. Macromolecules. 2006;39:6622–30.

    Article  CAS  Google Scholar 

  23. Ida S, Kawahara T, Fujita Y, Tanimoto S, Hirokawa Y. Thermoresponsive Properties of Copolymer Gels Induced by Appropriate Hydrophilic/Hydrophobic Balance of Monomer Combination. Macromol Symp. 2015;350:14–21.

    Article  CAS  Google Scholar 

  24. Ida S, Nishisako D, Fujiseki A, Kanaoka S. Thermoresponsive properties of polymer hydrogels induced by copolymerization of hydrophilic and hydrophobic monomers: comprehensive study of monomer sequence and water affinity. Soft Matter. 2021;17:6063–72.

    Article  CAS  PubMed  Google Scholar 

  25. Miyazaki H, Kataoka K. Preparation of polyacrylamide derivatives showing thermo-reversible coacervate formation and their potential application to two-phase separation processes. Polymer. 1996;37:681–5.

    Article  CAS  Google Scholar 

  26. Sugihara S, Kanaoka S, Aoshima S. Thermosensitive Random Copolymers of Hydrophilic and Hydrophobic Monomers Obtained by Living Cationic Copolymerization1. Macromolecules. 2004;37:1711–9.

    Article  CAS  Google Scholar 

  27. Komatsu S, Asoh T-A, Ishihara R, Kikuchi A. Facile preparation of degradable thermoresponsive polymers as biomaterials: Thermoresponsive polymers prepared by radical polymerization degrade to water-soluble oligomers. Polymer. 2017;130:68–73.

    Article  CAS  Google Scholar 

  28. Bivigou-Koumba AM, Kristen J, Laschewsky A, Müller-Buschbaum P, Papadakis CM. Synthesis of Symmetrical Triblock Copolymers of Styrene and N-isopropylacrylamide Using Bifunctional Bis(trithiocarbonate)s as RAFT Agents. Macromol Chem Phys. 2009;210:565–78.

    Article  CAS  Google Scholar 

  29. Sun B, Lin Y, Wu P, Siesler HW. A FTIR and 2D-IR Spectroscopic Study on the Microdynamics Phase Separation Mechanism of the Poly(N-isopropylacrylamide) Aqueous Solution. Macromolecules. 2008;41:1512–20.

    Article  CAS  Google Scholar 

  30. Willcock H, O’Reilly RK. End Group Removal and Modification of RAFT Polymers. Polym Chem. 2010;1:149–57.

    Article  CAS  Google Scholar 

Download references


This work was partially supported by the Japan Society for the Promotion of Science through a Grant-in-Aid for Scientific Research (JP19K05602), for which the authors are grateful.

Author information

Authors and Affiliations


Corresponding authors

Correspondence to Shohei Ida or Shokyoku Kanaoka.

Ethics declarations

Conflict of interest

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Ida, S., Hashiguchi, R., Murai, Y. et al. Facile synthesis of acrylamide derivative copolymers with side urethane groups for systematic variation of the thermoresponsive behavior. Polym J (2024).

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • DOI:


Quick links