Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Original Article
  • Published:

Revisit of crystal orientation in a vulcanizate of natural rubber under planar elongation

Abstract

The orientation of the crystalline lattice formed as a consequence of strain-induced crystallization (SIC) was revisited for a natural rubber (NR) sheet undergoing planar elongation by being stretched in one direction while keeping the other dimension unchanged. For this purpose, two-dimensional wide-angle X-ray diffraction patterns were measured by changing the inclination angle of the incident X-ray beam to the specimen sheet. The intensity of the reflection from the (120) plane of the orthorhombic crystal increased with increasing inclination angle from the normal direction of the specimen sheet; this result indicated that the orientation of the (120) planes was parallel to the surface of the specimen sheet. Moreover, the intensity of the (200) plane reflection reached a maximum at a slightly inclined angle from the normal of the specimen surface. WAXD measurements were also conducted using different X-ray wavelengths (0.06, 0.10, and 0.15 nm) to evaluate the inclined angle of the ac plane with respect to the surface of the specimen. By changing the X-ray wavelength, the distribution of reciprocal lattice points was altered such that the inclined angle of the incident X-ray beam to the specimen sheet needed to be changed to meet the diffraction condition. The inclined angle at the maximum intensity of the (200) reflection increased as a function of the X-ray wavelength. Based on this result, the preferential orientation of the ac planes was determined, whereby the ac plane was not completely parallel to the surface of the specimen sheet but was slightly inclined by 6.4°. Thus, a dual orientational state was deduced. Therefore, the preferential orientation of the ac plane was nearly parallel to the surface of the specimen sheet, with the inclined angle ranging from 6.4° to 19.6° within the volume of the specimen irradiated by the incident X-ray beam.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. Trabelsi S, Albouy P-A, Rault J. Stress-Induced Crystallization around a Crack Tip in Natural Rubber. Macromolecules. 2002;35:10054–61.

    Article  CAS  Google Scholar 

  2. Rublon P, Huneau B, Saintier N, Beurrot S, Leygue A, Verron E, et al. In situ synchrotron wide-angle X-ray diffraction investigation of fatigue cracks in natural rubber. J Synchrotron Rad. 2013;20:105–9.

    Article  Google Scholar 

  3. Osumi R, Yasui T, Tanaka R, Mai T-T, Takagi H, Shimizu N, et al. Impact of Strain-Induced Crystallization on Fast Crack Growth in Stretched cis-1,4-Polyisoprene Rubber. ACS Macro Lett. 2022;11:747–52.

    Article  CAS  PubMed  Google Scholar 

  4. Tsunoda K, Kitamura Y, Urayama K. Transition of rupture mode of strain crystallizing elastomers in tensile edge-crack tests. Soft Matter. 2023;19:1966–76. https://doi.org/10.1039/d3sm00060e

    Article  CAS  PubMed  Google Scholar 

  5. Kitamura Y, Okada K, Masunaga H, Hikosaka M. Role of strain rate in the strain-induced crystallization (SIC) of natural and synthetic isoprene rubber. Polym J. 2019;51:221–6.

    Article  CAS  Google Scholar 

  6. Katz JR. Röntgenspektrographische Untersuchungen Am Gedehnten Kautschuk Und Ihre Mögliche Bedeutung Für Das Problem Der Dehnungseigenschaften Dieser Substanz. Naturwissen-schaften. 1925;19:410–6.

    Article  Google Scholar 

  7. Bunn CW. Molecular structure and rubber-like elasticity I. The crystal structures of β gutta-percha, rubber and polychloroprene. Proc Roy Soc A. 1942;180:40–66.

    CAS  Google Scholar 

  8. Nyburg SC. A Statistical Structure for Crystalline Rubber. Acta Cryst. 1954;7:385–92.

    Article  CAS  Google Scholar 

  9. Benedetti E, Corradini P, Pedone C. Conformational isomorphism in crystalline 1,4-cis-polyisoprene. Eur Polym J. 1975;11:585–7.

    Article  CAS  Google Scholar 

  10. Natta G, Corradini P. Über die Kristallstrukturen des 1,4-cis-Polybutadiens und des 1,4-cis-Polyisoprens. Angew Chem. 1956;68:615.

    Article  CAS  Google Scholar 

  11. Tosaka M, Senoo K, Sato K, Noda M, Ohta N. Detection of fast and slow crystallization processes in instantaneously-strained samples of cis-1,4-polyisoprene. Polymer. 2012;53:864–72.

    Article  CAS  Google Scholar 

  12. Brüning K, Schneider K, Roth SV, Heinrich G. Kinetics of Strain-Induced Crystallization in Natural Rubber Studied by WAXD: Dynamic and Impact Tensile Experiments. Macromolecules. 2012;45:7914–9.

    Article  Google Scholar 

  13. Candau N, Chazeau L, Chenal J-M, Gauthier C, Ferreira J, Munch E, et al. Strain induced crystallization and melting of natural rubber during dynamic cycles. Phys Chem Chem Phys. 2015;17:15331–8.

    Article  CAS  PubMed  Google Scholar 

  14. Chen X, Meng L, Zhang W, Ye K, Xie C, Wang D, et al. Frustrating strain-induced crystallization of natural rubber with biaxial stretch”. ACS Appl Mater Interfaces 2019;11:47535–44.

    Article  CAS  PubMed  Google Scholar 

  15. Zhou W, Meng L, Lu J, Wang Z, Zhang W, Huang N, et al. Inducing uniform single-crystal like orientation in natural rubber with constrained uniaxial stretch. Soft Matter. 2015;11:5044–52.

    Article  CAS  PubMed  Google Scholar 

  16. Oono R, Miyasaka K, Ishikawa K. Crystallization kinetics of biaxially stretched natural rubber. J Polym Sci: Polym Phys Ed. 1973;11:1477–88.

    CAS  Google Scholar 

  17. Beurrot S, Huneau B, Verron E In Constitutive models for rubber VII: Proceedings of the 7th European conference on constitutive models for rubber, ECCMR, Dublin, Ireland, 20-23 Sept 2011. CRC/Taylor & Francis, Boca Raton. Jerrams S, Murphy N (eds). 2011:23–28.

  18. Toki S, Sics I, Ran S, Liu L, Hsiao BS, Murakami S, et al. New Insights into Structural Development in Natural Rubber during Uniaxial Deformation by In Situ Synchrotron X-ray Diffraction. Macromolecules. 2002;35:6578–84.

    Article  CAS  Google Scholar 

  19. Toki S, Fujimaki T, Okuyama M. Strain-induced crystallization of natural rubber as detected real-time by wide-angle X-ray diffraction technique. Polymer. 2000;41:5423–9.

    Article  CAS  Google Scholar 

  20. Murakami S, Senoo K, Toki S, Kohjiya S. Structural development of natural rubber during uniaxial stretching by in situ wide angle X-ray diffraction using a synchrotron radiation. Polymer. 2002;43:2117–20.

    Article  CAS  Google Scholar 

  21. Miyamoto Y, Yamao H, Sekimoto K. Crystallization and melting of polyisoprene rubber under uniaxial deformation. Macromolecules. 2003;36:6462–71.

    Article  CAS  Google Scholar 

  22. Tosaka M, Murakami S, Poompradub S, Kohjiya S, Ikeda Y, Toki S, et al. Orientation and Crystallization of Natural Rubber Network As Revealed by WAXD Using Synchrotron Radiation. Macromolecules. 2004;37:3299–309.

    Article  CAS  Google Scholar 

  23. Toki S, Sics I, Hsiao BS, Tosaka M, Poompradub S, Ikeda Y, et al. Probing the Nature of Strain-Induced Crystallization in Polyisoprene Rubber by Combined Thermomechanical and In Situ X-ray Diffraction Techniques. Macromolecules. 2005;38:7064–73.

    Article  CAS  Google Scholar 

  24. Tosaka M, Kawakami D, Senoo K, Kohjiya S, Ikeda Y, Toki S, et al. Crystallization and Stress Relaxation in Highly Stretched Samples of Natural Rubber and Its Synthetic Analogue. Macromolecules. 2006;39:5100–5.

    Article  CAS  Google Scholar 

  25. Zhao B, Tian N, Liu Y, Yan T, Zhou W, Li L, et al. Strain-induced crystallization of natural rubber with high strain rates. J Polym Sci: Part B: Polym Phys. 2012;50:1630–7.

    Article  CAS  Google Scholar 

  26. Che J, Burger C, Toki S, Rong L, Hsiao BS, Amnuaypornsri S, et al. Crystal and Crystallites Structure of Natural Rubber and Peroxide-Vulcanized Natural Rubber by a Two-Dimensional Wide-Angle X-ray Diffraction Simulation Method. II. Strain-Induced Crystallization versus Temperature-Induced Crystallization. Macromolecules. 2013;46:4520–8.

    Article  CAS  Google Scholar 

  27. Gros A, Tosaka M, Huneau B, Verron E, Poompradub S, Senoo K. Dominating factor of strain-induced crystallization in natural rubber. Polymer. 2015;76:230–6.

    Article  CAS  Google Scholar 

  28. Candau N, Chazeau L, Chenal J-M, Gauthier C, Munch E. A Comparison of the Abilities of Natural Rubber (NR) and Synthetic Polyisoprene Cis-1,4 Rubber (IR) to Crystallize under Strain at High Strain Rates. Phys Chem Chem Phys. 2016;18:3472–81.

    Article  CAS  PubMed  Google Scholar 

  29. Albouy P-A, Vieyres A, Pérez-Aparicio R, Sanséau O, Sotta P. The impact of strain-induced crystallization on strain during mechanical cycling of cross-linked natural rubber. Polymer. 2014;55:4022–31.

    Article  CAS  Google Scholar 

  30. Beurrot-Borgarino S, Huneau B, Verron E, Rublon P. Strain-induced crystallization of carbon black-filled natural rubber during fatigue measured by in situ synchrotron X-ray diffraction. Int J Fatigue. 2013;47:1–7.

    Article  CAS  Google Scholar 

  31. Poompradub S, Tosaka M, Kohjiya S, Ikeda Y, Toki S, Sics I, et al. Mechanism of strain-induced crystallization in filled and unfilled natural rubber vulcanizates. J Appl Phys. 2005;97:103529.

    Article  Google Scholar 

  32. Toki S, Burger C, Hsiao BS, Amnuaypornsri S, Sakdapipanich J, Tanaka Y. Multi-Scaled Microstructures in Natural Rubber Characterized by Synchrotron X-Ray Scattering and Optical Microscopy. J Polym Sci: Part B: Polym Phys. 2008;46:2456–64.

    Article  CAS  Google Scholar 

  33. Tanaka R, Yasui T, Kitamura Y, Tsunoda K, Takagi H, Shimizu N, et al. Application of Strained Natural Rubber at High Temperatures. ACS Appl Polym Mater. 2024;6:2799–806.

  34. Mai T-T, Yasui T, Tanaka R, Masunaga H, Kabe T, Tsunoda K, et al. Unraveling Non-Uniform Strain-Induced Crystallization Near a Crack Tip in Natural Rubber. Adv Sci. 2024;11:2307741.

Download references

Acknowledgements

This study was financially supported by JST CREST (Grant No. JPMJCR2091). The WAXD experiments were performed at Photon Factory, KEK, Japan (under the Approval No. 2020G512 and 2020G516) and SPring-8, JASRI, Japan (under the Approval No. 2023A7213).

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Shinichi Sakurai.

Ethics declarations

Conflict of interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Tanaka, R., Yasui, T., Takagi, H. et al. Revisit of crystal orientation in a vulcanizate of natural rubber under planar elongation. Polym J 56, 753–763 (2024). https://doi.org/10.1038/s41428-024-00910-z

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41428-024-00910-z

Search

Quick links