Light amplified oxidative stress in tumor microenvironment by carbonized hemin nanoparticles for boosting photodynamic anticancer therapy

Photodynamic therapy (PDT), which utilizes light excite photosensitizers (PSs) to generate reactive oxygen species (ROS) and consequently ablate cancer cells or diseased tissue, has attracted a great deal of attention in the last decades due to its unique advantages. However, the advancement of PDT is restricted by the inherent characteristics of PS and tumor microenvironment (TME). It is urgent to explore high-performance PSs with TME regulation capability and subsequently improve the therapeutic outcomes. Herein, we reported a newly engineered PS of polymer encapsulated carbonized hemin nanoparticles (P-CHNPs) via a facile synthesis procedure for boosting photodynamic anticancer therapy. Solvothermal treatment of hemin enabled the synthesized P-CHNPs to enhance oxidative stress in TME, which could be further amplified under light irradiation. Excellent in vitro and in vivo PDT effects were achieved due to the improved ROS (hydroxyl radicals and singlet oxygen) generation efficiency, hypoxia relief, and glutathione depletion. Moreover, the superior in vitro and in vivo biocompatibility and boosted PDT effect make the P-CHNPs a potential therapeutic agent for future translational research. We reported a newly engineered photosensitizer of polymer encapsulated carbonized hemin nanoparticles (P-CHNPs) via a facile synthesis procedure for boosting photodynamic therapy (PDT). The synthesized P-CHNPs achieved enhanced oxidative stress in tumor microenvironment, which could be further amplified under light irradiation, enabling excellent in vitro and in vivo PDT effects. Moreover, the superior in vitro and in vivo biocompatibility and boosted PDT effect make the P-CHNPs a potential therapeutic agent for future translational research.


Introduction
Cancer, the second leading cause of death currently, is one major public health issue with the increased incidence rate in the past several decades 1 . Various emerging cancer treatment strategies, including gene therapy 2 , photodynamic therapy (PDT) [3][4][5] , photothermal therapy (PTT) [6][7][8] , chemodynamic therapy (CDT), etc., have been proposed and demonstrated. Among these newly developed treatment strategies mentioned above, PDT, which utilizes photosensitizer (PS) in the presence of light with a specific wavelength to generate reactive oxygen species (ROS) to irreversibly destroy the targeted diseased tissue, is recognized as a promising treatment strategy with various benefits including noninvasiveness, low sideeffect, high spatial resolution, etc. [9][10][11] . Since approved for clinical use for the first time to treat bladder cancer in 1993, PDT has been clinically applied to treat various types of cancers 12 . However, PDT has not yet reached its full potential due to the limitation from PSs and tumor microenvironment (TME). Recently, many new PSs with improved ROS generation capability including fluorogens with aggregation-induced emission (AIE) characteristics (AIEgens) 13,14 , graphene quantum dots (GQDs) 15 , black phosphorus 16 , carbon dots (CDs) 17 , etc., have been designed and synthesized for PDT applications. The ROS quantum yield of GQDs could even reach 1.3 18 . Although the inherent ROS generation efficiency of emerging PSs was significantly enhanced, the ROS quantity in tumor site and consequently PDT efficiency were still subject to the TME features 19 , e.g., limited ROS quantity due to the hypoxia in the tumor site, scavenged ROS in cancer cells due to the overexpressed glutathione (GSH) of a tumor, etc. Thus, synergistic therapies such as PDT/PTT 20 , PDT/ chemotherapy 21 , PDT/immunotherapy 16 , and PDT/ CDT 22 , were employed to improve the therapeutic outcomes. It is worth to note that TME is featured with H 2 O 2 overexpression (0.1 to 1 mM), low catalase activity, mild acidity 23 . In the CDT process, under the assistant of Fenton ions (Fe 2+ ) or other Fenton-like ions, H 2 O 2 could be catalyzed via Fenton/Fenton-like reaction to generate cytotoxic hydroxyl radicals (•OH), one kind of ROS, and subsequently damage the tumors 24 . Recent advances showed that Fenton/Fenton-like reaction could produce both cytotoxic •OH and oxygen (O 2 ), and the quantity of both •OH and O 2 could be significantly enhanced under light irradiation via photo-Fenton reactions 25 . It means that endogenous H 2 O 2 can be decomposed to more •OH and O 2 once light irradiation was employed to accelerate Fenton-like reaction. Therefore, CDT could relieve O 2 deficiency in PDT and improve therapeutic effect, moreover, light irradiation could improve •OH and O 2 generation efficiency to enhance antitumor effects of CDT.
Considering that Fenton/Fenton-like reactions could improve the anticancer performance of PDT by amplifying the oxidative stress in TME, various therapeutic nanoagents have been designed and synthesized for CDT/PDT synergistic therapy. These efforts were mainly focused on functionalizing PSs with H 2 O 2 -responsed catalysts/enzymes such as Mn, Cu, Fe, Co, Pt-contained compounds to realize "all-in-one" multifunction 24 . The synthesized MSNs@CaO 2 -ICG@LA nanoagent 22 , UCNPs@TiO 2 @MnO 2 core/shell/ sheet nanocomposites 26 , and Au 2 Pt-PEG-Ce6 nanoformulation 27 , etc., achieved good anticancer performance, but these therapeutic nanoagents suffered from complicated synthesis and postprocessing procedures, and termination of ROS generation in TME. In order to further enhance the efficiency of CDT/PDT, some therapeutic agents with light amplified oxidative stress capability, such as UCNPs@Mn-SiO 3 @g-C 3 N 4 nanoplatforms 28 , Cu(II)-g-C 3 N 4 nanosheets 29 , manganese ferrite nanoparticle, and chlorin e6 (Ce6) anchored mesoporous silica nanoparticles (MFMSNs) 30 , and copper ferrite nanospheres 23 , have been designed and synthesized. However, these therapeutic nanoagents suffer from not only complicated synthesis and/or postprocessing procedures but also limited synergistic CDT/ PDT effects. Moreover, various heavy metal ions were contained in the synthesized nanoagents, potentially increasing unpredictable toxicity and subsequently limitation for their future clinical applications. It is urgent to develop superior biocompatible PSs via simple synthesis to efficiently amplify oxidative stress in TME and subsequently boost the anticancer performance of PDT.
Carbon nanomaterials, featured with superior biocompatibility, have been used as phototherapy (including PDT and PTT) and optical imaging nanoagents 31 . Most carbon nanoagents were commonly synthesized by simple carbonization of inert raw materials, indicating that carbonization could endow them with new functions. Thus, the carbonization of appropriate functional materials paves a new avenue to synthesize PSs with TME regulation capability. Hemin, which is Fe(III)-contained protoporphyrin IX and usually acts as the catalytic center of many protein families including cytochromes and hemoglobins, can catalyze various oxidation reactions to decompose H 2 O 2 to O 2 / •OH 32 . In addition, hemin tends to lose the iron in the porphyrin ring under acidic or hightemperature conditions to become porphyrin, which has high singlet oxygen ( 1 O 2 ) generation efficiency 33 . All these characteristics make hemin a good candidate for carbonization to form PS with oxidative stress amplification capability in TME and superior biocompatibility. However, most efforts have been devoted to packaging, carrying, and decorating with other materials to improve the dispersion of hemin for efficient catalytic activities up to now [34][35][36] . There were no reports about rational and facile synthesis methods to form PS, which could boost the PDT effect, using hemin as raw materials.
Here, we reported a rationally engineered PS with TME regulation capability and superior biocompatibility. Carbonized hemin nanoparticles (CHNPs) were designed and synthesized via facile solvothermal carbonization reaction and then encapsulated with an amphiphilic molecule to obtain polymer encapsulated carbonized hemin nanoparticles (P-CHNPs). As shown in Scheme 1, the proposed P-CHNPs could efficiently amplify the oxidative stress in TME.

Blood Vessel
Scheme 1 Scheme of the synthesis approach of P-CHNPs and therapeutic mechanism of light amplified oxidative stress in TME by P-CHNPs for boosting photodynamic anticancer therapy antioxidant defense system and remarkably enhanced the anticancer effect. Moreover, the oxidative stress in TME could be amplified with the aid of light irradiation, boosting PDT efficiency. It is worth to note that the superior in vitro and in vivo biocompatibility and boosted PDT effect of P-CHNPs guarantee the feasibility in anticancer therapy and future translational research.

Synthesis and characterization of P-CHNPs
The CHNPs were prepared by the solvothermal carbonized reaction using hemin as the raw materials. The size and morphology of the synthesized nanoparticles were characterized by transmission electron microscopy (TEM) and dynamic light scattering (DLS) measurement. The TEM images showed that the CHNPs had dispersive and uniform morphology (Figs. S1, S2a). The DLS results showed that the average hydrodynamic diameter of CHNPs was about 44 nm (Fig. S2b). In order to further improve the biocompatibility, CHNPs were encapsulated with amphiphilic polymer DSPE-mPEG to form P-CHNPs. The TEM images indicated that the P-CHNPs exhibited a core-shell structure with an average diameter of 73 nm ( Fig. 1a and Fig. S2c), and the DLS result was about 79 nm (Fig. S2d). The structural details of P-CHNPs were further investigated with high-resolution TEM (HRTEM) as shown in Fig. 1b. The high crystallinity with a lattice spacing of 0.24 nm ascribed to the (100) lattice plane of graphene was observed 37 . Then high-angle annular dark-field scanning TEM (HAADF-STEM) was applied to study the elemental composition and distribution of P-CHNPs. As shown in Fig. S3, the characteristic element P of DSPE-mPEG and element O were homogeneously distributed in the core region and in the whole nanoparticle respectively, demonstrating that CHNPs were encapsulated by DSPE-mPEG to form coreshell structure through hydrophobic interaction and consequently protect and stabilize the CHNPs. Fe, the characteristic element of hemin, was homogeneously distributed in the whole nanoparticle, indicating that Fe was released from hemin during solvothermal deferrization reaction and subsequently combined with O, N-containing functional groups existed in the whole nanoparticle. The homogeneously distributed Fe, which is favorable for electronic exchange with substrates such as H 2 O 2 , facilitates the Fenton/Fenton-like reaction. Furthermore, the energy-dispersive X-ray spectroscopy (EDX) revealed the existence and content of C, N, O, P, and Fe elements as shown in  38 were presented as shown in Fig. S5a. The C 1s displayed four characteristic peaks: C-C (284.2 eV), C-N (284.8 eV), C-O (286.2 eV), and C=O (288.8 eV) 38 (Fig. S5b), indicating that there were O, N-containing groups to combine the released Fe ion stemming from hemin deferrization. While the characteristic peaks of N 1s located at 399.1 and 400.2 eV (Fig. 1c), correspond to C=N/Fe-N and pyrrolic N respectively 39 . It means that there were coordination interactions between Fe and N-contained groups, enabling it to perform Fenton/Fenton-like reaction and generate 1 O 2 simultaneously 40 . Furthermore, the chemical form of the iron element, the key element for Fenton/Fenton-like reaction, was also analyzed as shown in Fig. 1d. The characteristic peaks of Fe 2p, i.e., Fe 2p 3/2 (712.4 eV) and Fe 2p 1/2 (728.8 eV), indicated the presence of Fe (III) 41 .
In order to study the new functions endowed by carbonization, the hemin nanoparticles (Hemin NPs, hemin was encapsulated with DSPE-mPEG) were also prepared for comparison. The UV-Vis absorption spectra of the synthesized Hemin NPs, CHNPs, and P-CHNPs were measured as shown in Fig. 1e. The Hemin NPs showed obvious characteristic absorption peaks at about 400 nm attributable to the raw materials hemin. It was observed that both CHNPs and P-CHNPs had main absorption peaks at 210 and 270 nm, which were derived from the ππ* transition of aromatic C=C bonds and n-π* transition of the functional groups with lone pairs electron, respectively 42 . Meanwhile, it also showed a broad absorption extended to 700 nm, which might originate from the functionalized surface groups of the nanoparticles 43 , and the shoulder peak at 404 nm likely originated from the noncompletely carbonized hemin/ porphyrin ring 44 . The P-CHNPs had excitationdependent emission features (Fig. S6) and the measured fluorescence quantum yield was 0.016 using riboflavin (Φ riboflavin = 0.23 in DMSO 45 ) as the reference, enabling image-guided anticancer therapy, while the raw material hemin had no fluorescence emission. Moreover, the encapsulation with DSPE-mPEG had no significant influence on the spectra of the synthesized CHNPs. Then the functional groups of P-CHNPs were analyzed using the Fourier transform infrared (FT-IR) spectroscopy as shown in Fig. 1f. In addition to the vibration bands of O-H/N-H, -CH 3 /-CH 2 , C-N, some characteristic vibrations were also recorded. Two FT-IR peaks at 1639 and 1609 cm −1 could be ascribed to the C=N and C=C stretching vibrations of the porphyrin ring, while the peak at 803 cm −1 indicated the presence of C-H out-of-plane ring deformation corresponding to pyrrole ring 46,47 . It can be deduced that not all the porphyrin rings were carbonized by the solvothermal reaction, enabling P-CHNPs to generate ROS as well as regulate TME. Moreover, the O, N-containing functional groups further improved the hydrophilicity and stability of the synthesized P-CHNPs in aqueous solutions.

TME regulation by P-CHNPs
Since the facile solvothermal reaction endowed P-CHNPs with new functions, the ROS generation and TME regulation capability of P-CHNPs as well as the amplification by light irradiation were characterized as shown in Fig. 2. 1 O 2 generation efficiency of P-CHNPs in an aqueous medium (50 μg mL −1 ) was evaluated under the light irradiation (400-700 nm, 70 mW cm −2 ) using 9,10-anthracenediyl-bis (methylene)dimalonic acid (ABDA) (50 μM) as the 1 O 2 indicator. As shown in Fig. 2a, the ABDA was almost consumed up in the presence of P-CHNPs after 14 min illumination, while in the absence of P-CHNPs, the absorption of ABDA was kept constant under the same light irradiation (Fig. S7), eliminating interference from light irradiation. Moreover, the 1 O 2 generation capability of hemin, the raw materials of P-CHNPs, was also investigated, and no obvious consumption of ABDA was observed, indicating that not raw materials but solvothermal treatment endows P-CHNPs with the 1 O 2 generation capability. In order to quantify 1 O 2 generation efficiency, one commercial photosensitizer Ce6 (Φ Ce6 = 0.66 in aqueous media 48 ) was selected as the reference. As shown in Fig. S8, the 1 O 2 generation capability of the synthesized P-CHNPs was measured as 0.35, which was much higher than that of one US Food and Drug Administration (FDA) approved PS, indocyanine green (ICG, Φ ICG = 0.002) 49 .
Since H 2 O 2 is overexpressed in TME, which could be regulated by P-CHNPs via Fenton/Fenton-like activity, the catalytic reaction products of H 2 O 2 , i.e., O 2 and •OH, were measured to study the oxidative stress in TME regulated by P-CHNPs. [Ru(dpp) 3 ]Cl 2 (RDPP), which fluorescence can be immediately quenched by O 2 50 , was selected as the indicator to monitor the generation of O 2 . As shown in Fig. 2b, the fluorescence intensity of RDPP was significantly decreased when RDPP was mixed with both P-CHNPs and H 2 O 2 , while no remarkable fluorescence intensity variation was observed when RDPP was mixed with either P-CHNPs or H 2 O 2 alone. It can be inferred that H 2 O 2 could be catalyzed by P-CHNPs to generate O 2 to quench the fluorescence of RDPP. Moreover, the fluorescence intensity of RDPP was further decreased when light irradiation (400-700 nm, 70 mW cm −2 , 20 min) was employed, indicating that light irradiation could efficiently enhance the generation of O 2 . Then, the influence of enhanced O 2 generation on 1 O 2 production was studied by the ABDA degradation experiments. As shown in Fig degradation of ABDA was significantly expedited when H 2 O 2 was added to the mixture solution of ABDA and P-CHNPs, while the H 2 O 2 alone had no obvious influence on the degradation of ABDA. It means that more O 2 supplied by the Fenton-like reaction remarkably improved the generation efficiency of 1 O 2 , and subsequently amplified the oxidative stress regulation capacity in TME. Meanwhile, the •OH generation capability, product of TME regulation via Fenton reaction under the assistant of P-CHNPs, was studied in H 2 O 2 solution using 3,3′,5,5′-tetramethylbenzidine (TMB) as the chromogenic substrate, which could be oxidized by the highly reactive •OH to appear an absorption peak at 650 nm. As shown in Fig. S9a, when TMB was mixed with either P-CHNPs or H 2 O 2 alone under mild acidic conditions (pH = 6.5), which was similar to the pH value in TME, no obvious absorption at 650 nm was detected even the reaction time of the mixture solution reached 1 h. While the strong absorption peak at 650 nm was recorded once the TMB was mixed with both P-CHNPs and H 2 O 2 , indicating efficient •OH generation via catalyzing H 2 O 2 by P-CHNPs. Considering that TME was featured with H 2 O 2 overexpression and mild acidity (typically around 6.5), the catalytic activity of P-CHNPs was investigated under different pH conditions to evaluate its oxidative stress regulation capability in TME. As shown in the insets of Figs. 2d and S9b, the characteristics absorption of TMB at 650 nm grew stronger with the decrement of pH value from 7.4 to 4.5, which was accompanied by the color changes from colorless to blue. It indicated that P-CHNPs possessed regulation capability in mild acidic (pH = 6.5) condition which is similar to TME acidity and were inactive in neutral (pH = 7.4) condition, enabling P-CHNPs to selectively regulate oxidative stress in TME. Moreover, the characteristic absorption of TMB grew stronger when light irradiation (400-700 nm, 70 mW cm −2 , 20min) was employed (Fig. 2d), indicating that light could efficiently enhance the H 2 O 2 decomposition to more lethal •OH.
As the well-known intracellular antioxidant, GSH, which can protect cells, is overexpressed in cancer cells and increases resistance to PDT. Thus, reduction of intracellular GSH level is of great importance for improving the anticancer performance of PDT. Considering that the Fe (III) in P-CHNPs could react with GSH, significantly lowering the GSH level, the GSH Colorimetric Assay Kit, which optical density value varies with the GSH content, was selected to investigate the GSH depletion capability of P-CHNPs. As shown in Fig. 2e, the optical density value decreased with the increment of P-CHNPs concentration, indicating that GSH was consumed by P-CHNPs. Meanwhile, the reaction products were also monitored with XPS as shown in Fig. 2f. Once reacted with GSH, the Fe 2p spectrum of P-CHNPs displayed two new characteristic peaks at 709 and 724 eV belonging to Fe (II) (red lines), which indicated that part of Fe (III) in P-CHNPs was reduced to catalytic Fe (II). These results showed that the reaction products of GSH and P-CHNPs contained Fe of mixed-valence states. Thus, GSH was efficiently depleted by P-CHNPs, enhancing the oxidative stress and therapeutical outcomes.
The mechanism of light amplified oxidative stress in TME The mechanism of light amplified oxidative stress in TME by P-CHNPs was summarized in Scheme 1. The Fe (III) in P-CHNPs could catalyze H 2 O 2 decomposition and be reduced to catalytic Fe (II) to form the Fe (III)/Fe (II) redox switch, but the Fenton-like reaction efficiency was very limited. Once light irradiation was employed, photoreduction of Fe (III) to Fe (II) was expedited, enabling the cycle of Fe (III) and Fe (II). It means that the Fe (III)/ Fe (II) redox switch is triggered by light irradiation and the termination of TME regulation via Fenton/Fentonlike reactions is efficiently avoided 51 . Meanwhile, the continuous Fenton/Fenton-like reactions catalyzed H 2 O 2 decomposition to generate cytotoxic •OH and O 2 with remarkably improved generation efficiency. Additionally, the P-CHNPs acted as efficient PS for PDT, hypoxiainduced limitation on the PDT effect was eliminated due to the self-supplied O 2 from TME regulation. GSH, overexpressed in tumor cells could reduce Fe (III) to catalytic Fe (II). Once GSH was depleted, the oxidative stress could be amplified and consequently enhance the anticancer effect. Overall, light could further amplify TME-mediated redox reaction and enable high generation efficiency of •OH and 1 O 2 , hypoxia relief, and GSH depletion, leading to boosted photodynamic anticancer therapy via amplified oxidative stress in TME.

In vitro biocompatibility and intracellular ROS generation capability of P-CHNPs
Before performing the in vitro study, the stability of P-CHNPs was evaluated by measuring the UV-vis absorption spectra. The P-CHNPs showed excellent physiological stability as the absorption peaks at 404 nm exhibited negligible fluctuations when incubated in different physiological solutions including phosphatebuffered saline (PBS) and cell medium (1640, DMEM) with 10% serum for up to 48 h (Fig. S11). The in vitro biocompatibility of P-CHNPs was first investigated by hemolysis assay. As shown in Fig. S12, no significant hemolysis (<5%) was observed when P-CHNPs were incubated with red blood cells (RBCs) for 12 h.
In order to further study the biocompatibility and specific oxidative stress regulation in cancer cells, various concentrations of P-CHNPs were incubated with normal cells and cancer cells for different incubation times respectively, and the cell viability was evaluated using standard Cell Counting Kit-8 (CCK-8). As shown in Fig. 3a, there was no significant difference between the control cells and normal cells treated with P-CHNPs in the concentration range of 50-300 μg mL −1 even for 48 h, demonstrating the excellent biocompatibility. While the cell viability was remarkably decreased for cancer cells with an increment of concentration of P-CHNPs from 0 to 300 μg mL −1 , indicating efficient •OH generation in cancer cells. It means that P-CHNPs could decompose the endogenous H 2 O 2 under mild acidity conditions while being inactive to a neutral condition in normal cells. The hypoxia relief capability of P-CHNPs was studied in 4T1 cells by selecting RDPP as the O 2 level indicator (Fig. S13). As compared with the 4T1 cells treated with RDPP alone or with RDPP/light irradiation, the 4T1 cells treated with RDPP and P-CHNPs showed weaker fluorescent intensity. And the fluorescent intensity was further decreased when 300 μM H 2 O 2 was incubated with 4T1 cells treated with RDPP and P-CHNPs, indicating intracellular O 2 supply by P-CHNPs via Fenton-like reaction. Moreover, when light irradiation was applied in the 4T1 cells treated with RDPP/P-CHNPs or RDPP/P-CHNPs/H 2 O 2 , the fluorescence intensity was decreased or completely quenched, these results clearly demonstrated that light irradiation promoted in situ H 2 O 2 decomposition and intracellular O 2 generation via P-CHNPs, efficiently overcoming tumor hypoxia.
The intracellular ROS generation capability of P-CHNPs was studied using 2′,7′-dichlorofluorescein diacetate (DCFH-DA) as the indicator. After incubating either with both of P-CHNPs and DCFH-DA or with DCFH-DA alone, the treated 4T1 cells were irradiated and imaged with confocal laser scanning microscopy (CLSM). As shown in Fig. 3b, after 10 s and 5 s light irradiation, a strong fluorescent signal of dichlorofluorescein (DCF) was observed within 4T1 cells treated with P-CHNPs with the concentration of 100 and 200 μg mL −1 respectively, demonstrating efficient and fast ROS generation capability of P-CHNPs. In contrast, no DCF signal was observed in the control cells, which eliminated any interference from light irradiation.

The fluorescence imaging and in vitro anticancer effect of P-CHNPs
To investigate the fluorescence imaging potential of P-CHNPs endowed by solvothermal reaction, HEK293 and 4T1 cells were incubated with P-CHNPs (100 μg mL −1 ) for 12 h. After being washed with PBS three times, the P-CHNPs stained cells were prepared for fluorescence imaging. As shown in Fig. 4a, strong fluorescence signals were observed, enabling imaging-guided PDT. Considering the excellent ROS ( 1 O 2 and •OH) generation capability, P-CHNPs were incubated with 4T1 cells to analyze the in vitro cancer cell ablation efficiency. To optimize the light dose for PDT, 4T1 cells were irradiated with light (400-700 nm, 100 mW cm −2 ) for 5, 10, 20, 30 min after incubated with/out P-CHNPs (200 μg mL −1 ) for 12 h, and then subsequently stained with the calcein-acetoxymethyl ester (calcein-AM) and propidium iodide (PI) for cell viability analysis via CLSM. As shown in Fig. S14, with an increment of light irradiation time, more cells were PIpositive. After 10 min light irradiation, about half of the 4T1 cells were PI-positive, once the light irradiation time reached 20 min, all the cells were ablated, ensuring excellent in vitro PDT effect. Meanwhile, the 4T1 cells only treated with light irradiation i.e., the light group showed the calcein-AM fluorescence, indicating that light irradiation alone did not induce cellular phototoxicity. To further study the cellular response to P-CHNPs, 4T1 cells treated with nothing (i.e., control group), light irradiation (i.e., Light group), P-CHNPs (i.e., PS group), and both of Light irradiation and P-CHNPs (i.e., PDT group) were analyzed and compared as shown in Fig. 4b. The 4T1 cells only treated with light irradiation showed the calcein-AM fluorescence, indicating that light irradiation alone did not induce cellular phototoxicity. And part of 4T1 cells treated with P-CHNPs were propidium iodide (PI) positive. It could be deduced that part of 4T1 cells were ablated by •OH generated within intracellular response process, which was consistent with CCK-8 results as shown in Fig. 3a. Meanwhile, all 4T1 cells treated with both P-CHNPs and light irradiation were PI-positive, indicating the excellent in vitro PDT effect. To investigate the generalizability of P-CHNPs for treating different cancers, various types of cancer cell lines, including HeLa, PC3, and SCC7 cells, were incubated with/out P-CHNPs and then treated with light irradiation (Fig. S15). All cells treated with both P-CHNPs and light irradiation were PI-positive, demonstrating the generality of P-CHNPs based PDT. Meanwhile, all cells treated with only light irradiation showed the obvious calcein-AM fluorescence, indicating that light irradiation alone did not induce cellular phototoxicity and eliminating any interference from light irradiation.

In vivo photodynamic anticancer effect of P-CHNPs
Before performing the in vivo anticancer studies, the in vivo and ex vivo fluorescence images were acquired at various time intervals to study the biodistribution of the administrated P-CHNPs (Fig. 5). To dynamically monitor the distribution of administrated P-CHNPs in the tumor site, the time-sequenced in vivo fluorescence images of P-CHNPs treated mice were recorded and analyzed (Fig. 5a, b). Once intratumorally injected of P-CHNPs, its strong fluorescence was observed in the tumor site, and the fluorescence signal covered the whole tumor site and reached the maximum at 1 h, which indicated that the P-CHNPs could efficiently reach the whole tumor, making it the optimal time point for the PDT applications. With a further increment of time, the fluorescence signal of P-CHNPs in the tumor site was gradually weakened, which could be attributed to the diffusion of P-CHNPs to the surroundings. Even so, the fluorescence signal of P-CHNPs in the tumor site were still apparent at 72 h post-injection, demonstrating the relative strong retention ability of P-CHNPs in the tumor site. The ex vivo fluorescence images of major organs and tumors excised from mice at 4, 12, 24, 48, and 72 h post intratumoral injection of P-CHNPs (8 mg kg −1 ) were also captured for analysis (Fig. 5c, d), the tumor showed much stronger fluorescence signal than other organs within 72 h postinjection of P-CHNPs, which was consistent with the in vivo fluorescence images of P-CHNPs treated mice. All these results demonstrated the effective preferential accumulation of P-CHNPs in tumors.
The synthesized P-CHNPs have shown excellent oxidative stress amplification capability, good biocompatibility, and excellent in vitro PDT effect, making P-CHNPs a promising in vivo PDT agent. The orthotopic breast tumor model, which is more similar to the practical clinical pathogenesis, was established by inoculating 4T1 cells in the abdominal mammary fat pad. Forty minutes after intratumorally injection of P-CHNPs (8 mg kg −1 ), mice were immediately irradiated with light (400-700 nm, 100 mW cm −2 ) for 20 min for the PDT group or 0 min for the PS group, respectively. While the mice in Control and Light groups were only treated with PBS or light irradiation, respectively. Moreover, the temperature during treatment was monitored by an IR thermal camera (Fig. S16), with an increment of treatment time, the temperature at the tumor site in PDT groups rose slowly. After 20 min irradiation, the temperature reached 37.5°C, which was lower than the temperature required for photothermal therapy (PTT). Thus, PTT-induced interference could be efficiently eliminated from this treatment. After treatment, the mice weight and tumor size were measured every 2 days, there was no significant body weight loss for all groups within 2 weeks as shown in Fig. 6a. It was obvious that the tumor size of mice in Light and Control groups kept increasing quickly, while the tumor size increment rate of PS treated mice was significantly lowered as compared with that of Light and Control groups, indicating the efficient oxidative stress regulation in TME due •OH generated via Fenton reaction under the assistant of P-CHNPs ( Fig. 6b and Fig. S17). Moreover, the tumor size of PDT treated mice was significantly decreased, which was comparable or better than common PDT as shown in Table S1. The boosted PDT with 97.7% tumor inhibition rate could be attributed to the amplified oxidative stress by P-CHNPs under light irradiation, wherein hypoxia was relieved, and GSH was depleted, thus the high quantity of ROS ( 1 O 2 and •OH) was generated in the tumor site. Another identical independent experiment was carried out, and a similar boosted PDT phenomenon was observed (Fig. S18), confirming the reproducibility of the excellent therapeutical outcomes endowed by the proposed PDT strategy. All mice were sacrificed on day 14, the practical tumor weight and tumor morphology were shown in Fig. 6c, d. The tumors of the PS group were smaller than that of the Light and Control groups, indicating that the efficient generation of cytotoxic •OH. Moreover, the tumors of the PDT group were significantly decreased, demonstrating the light amplified oxidative stress in TME and consequently boosted PDT. It was worth to note that conventional PDT could only suppress the tumor growth, the amplified oxidative stress in TME remarkably improved the therapeutic outcomes. The tumors were also harvested for hematoxylin and eosin (H&E) staining to observe the histological changes. As shown in Fig. 6e, no obvious abnormalities and lesions could be observed in the tumor slices stained with H&E for mice without any treatment or with light irradiation. Limited and noticeable nucleus dissociation and necrosis were found for the tumor slices in PS and PDT groups respectively, indicating cell death within the tumors.
In order to further evaluate the performance of P-CHNPs as a promising PDT agent, one commercial photosensitizer of Ce6 was selected for comparative studies. Various concentrations of Ce6 were incubated with normal cells and cancer cells for different incubation times respectively, and the cell viability was evaluated using CCK-8. There was no significant difference between the control cells and normal/cancer cells treated with Ce6 in the concentration of 0.25-3.5 μM (Fig. S19), indicating its negligible dark toxicity and excellent biocompatibility. While P-CHNPs exhibited remarkable toxicity to cancer cells but not to normal cells due to efficient •OH generation in cancer cells via decomposition of the endogenous H 2 O 2 under mild acidity condition (Fig. 3a). To analyze the in vitro cancer cell ablation efficiency of Ce6, 4T1 cells were incubated with/out Ce6 (3.0 μM). After light irradiation (400-700 nm, 100 mW cm −2 , 20 min), the cells were stained with calcein-AM and PI for viability analysis using CLSM. As shown in Fig. S20, all cells treated with both Ce6 and light irradiation, i.e., PDT group were PI-positive, since PI is a fluorescent nucleic acid stain that can permeate only the damaged membranes, it can be deduced that membranes of the nucleus were damaged by PDT effect, which was also observed in P-CHNPs based PDT effect. Before performing the in vivo studies, the biodistribution of administrated Ce6 was analyzed using in vivo and ex vivo fluorescence images. After intratumoral injection of Ce6 (5 mg kg −1 , typical clinical dosage), time-sequenced in vivo fluorescence images of Ce6 treated mice and ex vivo fluorescence images of tumors and major organs excised from Ce6 treated mice were recorded (Fig. S21). Ce6 accumulated in the tumor site at first, then quickly diffused to the liver, indicating that the Ce6 could be metabolized quickly by liver 52 . The short retention time limited the therapeutical outcomes. While the P-CHNPs possessed a longer retention time (Fig. 5), which ensured efficient generation of •OH and O 2 as well as GSH depletion, amplifying oxidative stress in TME and consequently boosting therapeutical outcomes. Then, Ce6-based (5 mg kg −1 ) and P-CHNPs-based (8 mg kg −1 ) in vivo photodynamic anticancer therapy were performed at similar conditions (Fig. S18). The tumor size of mice in Control (treated with PBS), Light (treated with light irradiation), Ce6 (treated with Ce6) groups kept increasing quickly, while the tumor size increment rate of P-CHNPs treated mice was significantly lowered. It confirmed that Ce6 had negligible dark toxicity and P-CHNPs possessed efficient oxidative stress regulation in TME. Meanwhile, the tumor size and weight of mice in Ce6 PDT (treated with both Ce6 and light irradiation) and P-CHNPs PDT (treated with both P-CHNPs and light irradiation) groups were significantly decreased, demonstrating the superior anticancer effect. Considering that P-CHNPs had much lower 1 O 2 generation capability than Ce6 but similar therapeutical outcomes, the excellent anticancer effect of P-CHNPs could be attributed to the efficient oxidative stress regulation in TME. In order to further boost its anticancer effect, the P-CHNPs could be optimized, e.g. improve 1 O 2 generation capability, shift the absorption band to the longer wavelength to increase the penetration depth and subsequently ensure PDT effect exists in the whole tumor, functionalize the nanoparticles to prolong the retention time and further amply the oxidative stress in TME, etc.

In vivo biocompatibility of P-CHNPs
In addition, the in vivo biocompatibility is another key parameter to evaluate the PDT agent. The blood was collected for routine hematology assays and blood biochemistry analysis on days 1, 8, and 14 after administration of P-CHNPs (8 mg kg −1 ) via subcutaneous injection. As shown in Fig. S22 and Table S2, no significant abnormities in hematology parameters and biochemical indicators, related to the hepatic function and kidney function, were observed, indicating the synthesized P-CHNPs have no obvious in vivo toxicity. Meanwhile, the major organs including heart, kidney, liver, lung, and spleen were also collected from sacrificed mice, which were treated with PDT, PS, etc., for analysis via H&E staining. As shown in Fig. S23, there were no signs of organ lesions for all groups, confirming the excellent in vivo biocompatibility of P-CHNPs.

Discussion
Hemin, Fe (III)-contained protoporphyrin IX, could be endogenously produced in the human body, ensuring superior biocompatibility for its biological applications. Although hemin inherently possesses catalyzation capability, its efficiency for oxidative stress amplification in TME and anticancer effect is extremely limited. Facile solvothermal carbonization reaction made hemin lose the iron to form deferrization porphyrin fragments or carbonized products with 1 O 2 generation capability, and the O, N-containing groups combined with the released Fe ion stemming from hemin deferrization, enabling the formed CHNPs to act as photosensitizer with oxidative stress amplification capability in TME. Encapsulating CHNPs with polymer to form P-CHNPs not only maintained the spectral characteristics but also improved the biocompatibility. Meanwhile, the formed P-CHNPs possessed brand-new and improved features including fluorescence emission, high ROS (including singlet oxygen and hydroxyl radicals) generation efficiency, oxygen self-supplement, GSH depletion, etc., enabling efficient oxidative stress amplification in TME for boosting photodynamic anticancer therapy. Moreover, the oxidative stress regulation in TME selectively occurred in tumor site featured with H 2 O 2 overexpression (0.1-1 mM), so •OH is only generated in the tumor-specific microenvironment but does little harm to normal tissues. Considering the increased glucose metabolic rates in tumors, glucose oxidase could be applied to catalyze glucose to generate H 2 O 2 and subsequently amply the oxidative stress. Furthermore, the oxidative stress could be further amplified in the PDT process once light irradiation was employed via a photo-Fenton reaction. All these features made P-CHNPs an excellent PS for photodynamic anticancer therapy. The in vivo tumor ablations experimental results showed that P-CHNPs based PDT could reduce the tumor size instead of suppressing tumor growth, which was almost unachievable in common PDT. The excellent therapeutical outcomes could be attributed to (I) light irradiation triggered the Fe (III)/Fe (II) redox switch and thus the termination of oxidative stress regulation in TME via Fenton/Fenton-like reactions was avoided, (II) high generation efficiency of •OH and O 2 due to P-CHNPs enabled TME regulation and light amplified oxidative stress, (III) O 2 self-supplied in TME which subsequently relieved oxygen deficiency and improved the generation of 1 O 2 , (IV) oxidative stress-induced damage to the tumor was exacerbated by GSH depletion. Moreover, superior in vitro and in vivo biocompatibility and PDT effect make the P-CHNPs a great potential therapeutic agent for future translational research.

Synthesis of CHNPs
The CHNPs were synthesized using the common solvothermal reaction. Briefly, 15 mg of hemin was dispersed in 25 mL of ethyl alcohol, which was followed by ultrasonication for 15 min and subsequently heating at 240°C for 24 h in an autoclave. After being air-cooled down to room temperature, the products were filtered by 0.22 μm membranes and purified with centrifugal ultrafiltration three times, finally, the CHNPs were obtained.

Encapsulation of CHNPs with polymer
To further improve the biocompatibility, the CHNPs were encapsulated with amphiphilic polymer. DSPE-mPEG (2 mg) and CHNPs (1 mg) were dissolved in 2 mL of tetrahydrofuran (THF), then the mixture was quickly injected into 18 mL of water under continuous sonication for 2 min. After the THF was evaporated, the aqueous solution was filtered with 0.22 μm membranes and purified with centrifugal ultrafiltration. Finally, the P-CHNPs were obtained and kept at 4°C for further use.

Singlet oxygen detection
The 1 O 2 generation efficiency of P-CHNPs was assessed by ABDA, a 1 O 2 indicator. Briefly, 50 μM ABDA and 50 μg mL −1 P-CHNPs were mixed to 2 mL aqueous solution. Subsequently, the cuvette was exposed to light (400-700 nm, 70 mW cm −2 ) for different time intervals. Corresponding absorption spectra were recorded immediately after each irradiation. In the presence of 1 O 2 , the absorbance of ABDA would significantly decrease due to the oxidative decomposition effect of 1 O 2 on ABDA.

Hydroxyl radicals detection
To evaluate the •OH generation capability of P-CHNPs, TMB, which can be oxidized by the highly reactive •OH to possess a maximum absorbance at about 650 nm, was selected as the •OH indicator. The PBS buffer solution (pH 6.5) containing TMB (800 μM) was mixed with P-CHNPs (50 μg mL −1 ) in the presence of H 2 O 2 (300 μM) with or without light irradiation. The TMB solutions treated with P-CHNPs or H 2 O 2 alone with/without light irradiation were used as control. The absorption spectra of the mixture solution were recorded.

The depletion of GSH
The GSH solution (650 μM), P-CHNPs aqueous solution (100, 200 μg mL −1 ), and extraction buffer solution were added sequentially. The mixture solution was maintained at 37°C for 60 min, then centrifuged to remove P-CHNPs, and finally, the supernatant was collected for further assay. The GSH depletion was measured according to the Kit assay protocol.

Cellular toxicity tests
4T1 cells and L02 cells were cultivated in RPMI 1640 (Roswell Park Memorial Institute) supplied with 10% fetal bovine serum (FBS), HEK293 cells, and HeLa cells were cultivated in DMEM (Dulbecco's modified eagle medium) supplied with 10% FBS. Cultures were maintained at 37°C under a humidified atmosphere containing 5% CO 2 . Cells were plated into a 96-well plate at a density of 5000 cells per well and cultured for 24 h, respectively. Then the medium was replaced by 100 μL of fresh culture medium containing P-CHNPs with various concentrations (50-300 μg mL −1 ). The medium and untreated cells were used as blank and control, respectively. After 24 or 48 h, the cultured medium was removed, and the cells were washed three times with PBS to remove the residual P-CHNPs. 100 μL of fresh medium containing 10 μL of CCK-8 was added to each well. After 2 h incubation at 37°C, the absorbance at 450 nm was measured using a microplate reader. The cells viability was calculated by the following equation: Cell Viability % ð Þ ¼ OD À OD Blank OD Control À OD Blank Ã 100

In vitro PDT effect evaluation
To evaluate the in vitro PDT effect of P-CHNPs, the 4T1 cells were seeded in a confocal dish at a density of 5000 cells per well, and then cultured at 37°C, 5% CO 2 atmosphere for 24 h. P-CHNPs (200 μg mL −1 ) were added to each well. After 12 h incubation, the P-CHNPs treated cells were washed with PBS three times to remove the residual P-CHNPs, which was followed by light irradiation (400-700 nm, 100 mW cm −2 , 20 min). After light irradiation, cells were incubated with fresh media for 4 h. And then, a fresh FBS-free culture medium containing calcein-AM (2 μM) and PI (2 μM) were added and incubated for another 30 min. After washing three times to remove the residual calcein-AM and PI, the treated cells were proceeded for fluorescent imaging using confocal laser scanning microscopy.

Animal model
All the animal experiments were approved by the bioethics committee of the school of biomedical engineering, Shanghai Jiao Tong University, and were consistent with regulations for the care and use of experimental animals in China. Five weeks old female BALB/c mice, originally purchased from SPF experimental animal center, were used to establish tumor model. Briefly, 1 × 10 6 4T1 cells were injected into the breast fat pad of each female BALB/c mouse (n = 4) to establish the orthotopic breast tumor model. Once the tumors grew to about 50 mm 3 in volume, the in vivo experiments were performed.

Therapeutic evaluation in tumor-bearing mice
The mice were randomly divided into four groups. Control group: administration with PBS (40 μL) alone; Light group: administration with PBS (40 μL) and light irradiation (400-700 nm, 100 mW cm −2 , 20 min); PS group: administration with P-CHNPs (8 mg kg −1 , 40 μL); PDT group: administration with P-CHNPs (8 mg kg −1 , 40 μL) and light irradiation (400-700 nm, 100 mW cm −2 , 20 min). P-CHNPs or PBS were injected intratumorally. During the treatment period (14 days), the tumor volume of all mice was measured every other day using a vernier caliper. On day 14, mice were sacrificed, then tumors in all groups were harvested and weighed. For histological analysis, the hematoxylin-eosin (H&E) staining of tumor slices was carried out. The greatest longitudinal diameter (length) and the greatest transverse diameter (width) were used to calculate the tumor volume: The tumor growth inhibition rates (IR) were calculated via the following formula: where TVt represents the mean tumor volume of the treated groups and TVc represents the mean tumor volume of the control group.

Statistical analysis
Data reported in this work were presented as the mean ± standard deviation (s.d.). Statistical analysis of data were performed with T-test analysis of variance. The level of significance was defined as *P < 0.05, **P < 0.01, ***P < 0.001, ****P < 0.0001.