Abstract
2D materials are considered for applications that require strong lightmatter interaction because of the apparently giant oscillator strength of the exciton transitions in the absorbance spectrum. Nevertheless, the effective oscillator strengths of these transitions have been scarcely reported, nor is there a consistent interpretation of the obtained values. Here, we analyse the transition dipole moment and the ensuing oscillator strength of the exciton transition in 2D CdSe nanoplatelets by means of the optically induced Stark effect (OSE). Intriguingly, we find that the exciton absorption line reacts to a high intensity optical field as a transition with an oscillator strength F_{Stark} that is 50 times smaller than expected based on the linear absorption coefficient. We propose that the pronounced exciton absorption line should be seen as the sum of multiple, low oscillator strength transitions, rather than a single high oscillator strength one, a feat we assign to strong exciton centerofmass localization. Within the quantum mechanical description of excitons, this 50fold difference between both oscillator strengths corresponds to the ratio between the coherence area of the exciton’s center of mass and the total area, which yields a coherence area of a mere 6.1 nm^{2}. Since we find that the coherence area increases with reducing temperature, we conclude that thermal effects, related to lattice vibrations, contribute to exciton localization. In further support of this localization model, we show that F_{Stark} is independent of the nanoplatelet area, correctly predicts the radiative lifetime, and lines up for strongly confined quantum dot systems.
Similar content being viewed by others
Introduction
Colloidal quantum wells of CdSe^{1,2} have attracted much attention in the past years due to narrow, excitonrelated absorption features, an increased lightmatter interaction, strong light amplification^{3,4,5,6,7} and excitonpolariton formation^{8,9}. As twodimensional (2D) materials, these socalled nanoplatelets fall in between atomically thin 2D materials, such as transition metal dichalcogenides^{10,11}, and the usually much thicker epitaxially grown quantum wells. Moreover, being capped by organic ligands, nanoplatelets are intrinsically embedded within a low permittivity environment. This dielectric confinement substantially enhances the exciton binding energy^{12}. While the exciton binding energy of 15 meV in bulk CdSe should increase to 60 meV in a 2D CdSe quantum well^{13}, typical estimates amount to ~190 meV for 4.5 monolayer (1.21 nm) thick CdSe nanoplatelets^{3,7,14,15}. With such binding energies, excitons in nanoplatelets are stable quasiparticles at room temperature, and excitonrelated transitions have been used to develop room temperature nanoplateletbased light emitting diodes^{16} and lasers^{3}.
At cryogenic temperatures, the heavyhole bright exciton in CdSe nanoplatelets was found to exhibit a radiative decay rate of ~1 ps^{−1}, a rate that also determined the exciton dephasing^{14}. Similar observations were made in the case of epitaxial quantum wells^{17,18}, and attributed to the large inplane coherence area of the exciton centerofmass motion in these systems. Intriguingly, recent reports based on statefilling models proposed that even at room temperature, this coherence might be close to 100 nm^{2}, a number that seems incompatible with the nanosecond radiative lifetime reported by various authors^{19,20,21}. In addition, several studies indicated the potential for strong coupling of excitonic transitions with the light field at room temperature using 4.5 monolayer CdSe nanoplatelets, a feat that requires narrow transition lines with large oscillator strength^{8,9}. Using an elaborate fitting procedure of excitonpolariton dispersion curves, heavy hole transition dipole moments of 575 Debye (D) at room temperature were extracted. Although promising, such dipole moments seem disruptively large as compared to literature reports on comparable material systems, such as epitaxial quantum wells (6 D)^{22}, three and twodimensional perovskites (46 and 15 D, respectively)^{23,24}, carbon nanotubes (12 D)^{25}, and transition metaldichalcogenides (7 D for WSe_{2}^{26}, 51 D for WS_{2}^{27}, and 9 D for MoSe_{2} at 77K)^{28}.
In studies, the optical Stark effect (OSE) is used as a method to extract the desired dipole moment^{22,27}. Using OSE spectroscopy, one pumps the material using a femtosecond pump pulse detuned relative to the exciton transition and measures the induced energy shift of the exciton using a broad, whitelight probe pulse. This method alleviates the need for electrical contacting^{29} and does not rely on real charge carriers, thereby eliminating any spurious effects of defect trapping and assumptions on statefilling or electronhole overlap^{19,20}. Recent work by Diroll showed that also CdSe nanoplatelets display such a Stark effect and dipole moments in the range 15–23 D were extracted, numbers which are very much in line with other 2D materials^{30}. However, translating such dipole moments into dimensionless oscillator strengths leads to numbers of around one. Since oscillator strengths of 5–15 are routinely found for 0D colloidal quantum dots, such a result questions whether lightmatter coupling in 2D nanoplatelets is particularly strong and warrants a deeper investigation into the exciton oscillator strength of these materials.
In this work, we extend the use of polarization resolved OSE spectroscopy to develop a consistent interpretation of the oscillator strength of 2D excitons. First, we confirm the report of Diroll, measuring transition dipole moments of 18 D for 4.5 ML CdSe nanoplatelets. Next, we translate these values into a dimensionless oscillator strength and conclude it is fifty times smaller than the oscillator strength of the exciton transition as derived from the linear absorbance spectrum using previously published methods^{31}. We argue that this discrepancy results from a strong localization of the centerofmass of the exciton. Since a nanoplatelet can host multiple localized excitons, centerofmass localization can strongly reduce the oscillator strength of a single exciton transition—as measured by the Starkeffect—without affecting the overall oscillator strength of the exciton absorption. Translating this interpretation into a quantum mechanical description, we show that the ratio between the oscillator strengths yields the coherence area of the heavyhole bright exciton at room temperature, resulting in a value of ≈6.1 nm^{2}. Interestingly, similar measurements at 77 K yield a coherence area of ≈12 nm^{2}; a result suggesting that thermal effects such as lattice vibrations contribute significantly to exciton localization. Further supporting the interpretation of exciton localization, we show that the coherence area and the ensuing oscillator strength does not depend on the nanoplatelet area at room temperature, and that localization accounts for the radiative lifetime of the exciton. Finally, we show that the integrated bandedge absorbance yield similar oscillator strengths as the OSE experiment in the case of CdSe colloidal QDs, suggesting that such 0D systems effectively host electronhole pairs delocalized over the entire nanocrystal volume at room temperature.
Results
The optical stark effect
To study the lightmatter coupling in CdSe platelets, we assessed the optical Stark effect (OSE) of the heavyhole exciton using white light pumpprobe spectroscopy. All following optical experiments were carried out at room temperature, except when mentioned otherwiseThe OSE is typically described within a dressed atom picture as the result of the coherent interaction between a twolevel system and a photon field. Figure 1 shows the principle behind the OSE applied to a twolevel system that corresponds to a platelet in its ground state \(\left\ 0\ \right\rangle \) and in the state \(\left\ {\rm{X}}\ \right\rangle \) where it holds a single exciton. In that case, a resonant pump at frequency ω = ω_{0→X} will couple the degenerate states \(\left\ 0\ \right\rangle \left\ n\ \right\rangle \) and \(\left\ {\rm{X}}\ \right\rangle \left\ n1\ \right\rangle \) – in which the platelet is either in the ground state \(\left\ 0\ \right\rangle \) or the excited state \(\left\ {\rm{X}}\ \right\rangle \) and the optical field contains n or n − 1 photons – to form mixed lightmatter states split by the Rabi frequency \({{{\Omega }}}_{0}^{2}={{\mathcal{E}}}^{2}{\mu }_{0\to {\rm{X}}}^{2}/{\hbar }^{2}\). Here, \({\mathcal{E}}\) is the root mean square of the electric field associated with the pump light and μ_{0→X} is the transition dipole moment of the ground state to exciton transition.
When the pump laser is off resonance, the uncoupled states \(\left\ 0\ \right\rangle \left\ n\ \right\rangle \) and \(\left\ {\rm{X}}\ \right\rangle \left\ n1\ \right\rangle \) are split by the absolute value of the laser detuning Δω = ω − ω_{0→X}, see Fig. 2a. In that case, coupling only leads to a mere shift of these initial states when the laser detuning strongly exceeds the Rabi frequency. For a negative detuning (ω < ω_{0→X}), the case shown in Fig. 1, the result is an increased splitting between the lower energy state \(\left\ 0\ \right\rangle \left\ n\ \right\rangle \) and the higher energy state \(\left\ X\ \right\rangle \left\ n1\ \right\rangle \). From the perspective of the original twolevel system, this leads to an increase of the transition energy between the states \(\left\ 0\ \right\rangle \) and \(\left\ {\rm{X}}\ \right\rangle \), i.e., the optical Stark effect, by an amount ΔE given by (see Fig. 2a):
Negative detuning has the advantage that the pump pulse can induce an OSE, without creating real excitons by 1photon absorption. Furthermore, we ensured that pump intensities were sufficiently low so as to avoid significant 2photon absorption^{32}. Under such conditions, a coincident white light probe beam can measure the shift of the exciton absorbance proper, without statefilling, exciton saturation or bandgap renormalization obscuring the measured transient absorption spectrum; a process represented in Fig. 1^{33,34}.
In practice, we analyzed the optically induced Stark effect by illuminating a film of CdSe nanoplatelets using a 120 fs pump pulse detuned to lower photon energies as compared to the heavy hole exciton transition, see “Methods” section for details. The transient shift of the exciton transition induced by the pump was then analyzed by means of a broadband probe, of which we measured the change in absorbance ΔA = A − A_{0} as a function of the pumpprobe delay. This delay was varied via a mechanical delay stage to obtain 2D timeenergy maps of ΔA for a given detuning of the pump laser. Moreover, as CdSe nanoplatelets are not isotropic, we used two different combinations of linear polarization for the pump and probe, denoted here as copolarized (xx) and crosspolarized (xy).
The optical stark effect of CdSe nanoplatelets
In this study, we worked with 4.5 monolayer (ML) CdSe nanoplatelets, which were synthesized using a modification of the procedure proposed by Ithurria et al. (see “Methods” Section)^{1}. Figure 2a displays a typical bright field transmission electron microscope (TEM) image of the nanoplatelets^{2}. From the TEM image, we obtained the average lateral dimensions of the nanoplatelets. Unless stated otherwise, results reported in this manuscript pertain to a sample with a 34 × 9.6 nm^{2} area, see Supplementary Information S1. For the optical experiments, thin films of CdSe nanoplatelets were deposited on a transparent fused silica substrate using spincoating from nheptane, forming ~250 nm thick smooth films, see Fig. 2b. We preferred thin films in this case to avoid strong, solventinduced artifacts in the pumpprobe measurements at short time delays that can occur when using apolar solvents, such as hexane.
Figure 2c shows the absorption spectrum and its first derivative of the nanoplatelets studied here as a function of energy. We observe pronounced features at 2.42 and 2.58 eV, related to the formation of heavy and light hole excitons, respectively^{1}. We decomposed the absorption spectrum into contributions from the two exciton transitions and the associated 2D free carrier absorption profiles C_{HH,LH}, see Supplementary Information S2 and Fig. 2d. A binding energy for the heavy hole exciton of ~190 meV is extracted, which matches well with literature estimates^{14,29}. Importantly, such a binding energy corresponds to a 2D Bohr radius of 1.5 nm. Note that this Bohr radius is substantially smaller than the lateral extension of the nanoplatelets, which implies that excitons only exhibit weak lateral confinement. The fluorescence decay of these samples with 65% quantum yield reveals an average lifetime of 6.6 ns, as is shown in Supplementary Information S3.
Figure 3a shows a typical 2D map of ΔA recorded on a film of 4.5 ML CdSe nanoplatelets using a pump pulse at 580 nm (2.14 eV, Δ = 288 meV) for a parallel pumpprobe polarization. One clearly observes distinct and shortlived antisymmetric features around the HH and LH resonances. Looking at the transient absorbance spectrum at zero time delay (see Fig. 3b), we retrieve similar spectra for both combinations of pumpprobe polarization, albeit with a different absolute signal for the same pump power. As highlighted in the case of ΔA_{xx}, these spectra closely resemble the first derivative of the linear absorption spectrum. In that case, the reduced absorbance at the low energy side and the increased absorbance at the high energy side of the exciton absorption point toward a blueshift of the exciton transition, which is indeed what the optical Stark effect should bring about. Finally, Fig. 3a highlights the temporal width of the transient absorbance ΔA around the heavyhole exciton. With a full width at half maximum of 180 fs, a number closely corresponding to the convolution of a 120 fs pump and a 120 fs probe, this implies that we indeed look at an instantaneous variation of the exciton absorbance. This agrees with the expected instantaneous nature of the coherent optical Stark effect since dephasing at room temperature was shown to be limited to sub100 fs using 2D electronic spectroscopy^{35,36}. Moreover, the lack of a longlived bleach or photoinduced absorption confirms that the detuned pump laser used here does not create real excitons, see Supplementary Information S4. Given the agreement between the transient absorbance spectrum and the first derivative of the linear absorbance shown in Fig. 3b, we calculate the shift of the exciton transition as the coefficient relating ΔA and ∂A_{0}/∂E:^{37}
A complication in the case of the anisotropic nanoplatelets studied here is that both the pump and probe polarization, and the orientation of the platelet relative to both, will influence the relation between the energy shift ΔE and the change in absorbance ΔA. In Supplementary Information S5, we explicitly consider the different combinations of nanoplatelet orientations and pump and probe polarizations to obtain expressions that relate ΔA_{xx} and ΔA_{xy} to the spectral shift ΔE:
The coefficients f_{ij} can be calculated when the dielectric parameters of the platelet environment are known. Taking the wellknown scenario of a dilute dispersion of platelets in hexane, the correction coefficients f_{xx} and f_{xy} would amount to 0.73 and 0.35, respectively, see Supplementary Information S5. Figure 3b confirms that the copolarized transient absorbance ΔA_{xx} is about twice as large as the crosspolarized transient absorbance ΔA_{xy}. While this rough estimate agrees byandlarge with the calculated estimate of f_{xx}/f_{xy} = 2.09, one should realize that the correction factors will be somewhat different for nanoplatelets in the thin films used here, due to the reduced dielectric screening, a point we will come back to later.
Before quantifying the exciton shift ΔE, we first evaluated our results in view of Eq. (1) by analyzing ΔA_{xx} and ΔA_{xy} as a function of light intensity and detuning. As shown in Fig. 4a, changing the pump power at constant detuning Δω results in a strong increase in the transient absorbance at a given probe photon energy E_{probe}. Figure 4b represents the variation of ΔA_{xx} and ΔA_{xy} at E_{probe} = 2.395 eV, which corresponds to the minimum of the ΔA spectrum as indicated in Fig. 4a. One readily sees that the transient absorbance scales linearly with the pump power, or with the electric field squared, a trend that agrees with the expression of the optical Stark effect and the linear relation between the transient absorbance and the shift ΔE of the exciton absorbance. Moreover, keeping the pump power constant and increasing the detuning ∣Δω∣ leads to a gradual reduction of ΔA_{xx} and ΔA_{xy} that scales as 1/∣Δω∣. We thus conclude that the transient absorbance does reflect the optical Stark effect of the exciton transition.
Finally, the ratio of the slopes of the best fits to ΔA_{xx} and ΔA_{xy} in Fig. 4b amounts to 1.75. This figure is somewhat smaller than the ratio of 2.09 we calculated for an apolar solvent environment, which probably reflects the reduced screening in the nanoplatelet film. In fact, a ratio f_{xx}/f_{xy} = 1.75 would be obtained if the environment had a refractive index of 2.13, see Supplementary Information S5. This number is reasonable for a film consisting of close packed nanoplatelets capped by oleate ligands, and as such, we can reliably quantify ΔE using the corresponding correction coefficient f_{xx} = 0.75, see Supplementary Information S5.
The oscillator strength of the exciton transition
Having validated the functional form set forth in Eq. (1) and having verified the conversion of ΔA into ΔE, we can use Eq. (1) to calculate the transition dipole moment μ_{0→X} linked to the formation of the bright heavy hole exciton. This yields a value of 18 D (see Supplementary Information S6), a figure that compares reasonably well to the 9 D found for slightly less confined 5.5 ML CdSe nanoplatelets using timeresolved AC Stark spectroscopy^{29}. In addition, from the transition dipole moment, we can calculate the oscillator strength F_{Stark} of the exciton transition as^{31}:
Here, m_{e} is the free electron mass and ω is the angular frequency at the HH position. This expression yields F_{Stark} = 3.1 for the 4.5 ML CdSe platelets of 326 nm^{2}, a number of the same magnitude as the oscillator strength F = 0.5−1 reported for the exciton transition in dielectrically confined singlelayer perovskite nanoplatelets^{24}. Interestingly, since transition energies are comparable for both systems, this points toward a stronger transition dipole moment in CdSe nanoplatelets. On the other hand, this oscillator strength is about 3–4 times smaller than the oscillator strength of the bandedge transition in CdSe QDs, for which values up to 10 were reported^{38}. Clearly, this outcome challenges the idea of a giant oscillator strength of the exciton transition in room temperature CdSe nanoplatelets. We note that this conclusion also holds for all the reports in literature on OSE extracted dipole moments of varying 2D materials.
An alternative approach to determine the oscillator strength of the exciton transition starts from the linear absorption spectrum. When rescaling this spectrum to an intrinsic absorption coefficient spectrum μ_{i}(ℏω), the oscillator strength of the exciton transition can be calculated from the integrated exciton absorption feature μ_{i,int}, as outlined by the shaded area in Fig. 2d and Supplementary Information S2^{31}:
Using an average local field factor of ∣f_{LF}∣^{2} = 0.328 for the nanoplatelets in hexane used here, we estimate F_{Abs} = 165 ± 1.5 for the 4.5 ML platelets, see Supplementary Information S2. Intriguingly, this number exceeds the value obtained through the optical Stark effect by over a factor of 50, and it also strongly exceeds the oscillator strength reported for the bandedge transition of CdSe QDs^{38}.
Discussion
Localized versus delocalized 2D excitons
To understand the very disparate oscillator strengths of the exciton transition as obtained from the optical Stark effect and the linear absorption spectrum, we start from the description of the 2D exciton wave function \(\left\ X\ \right\rangle \) as the product of a centerofmass part \(\left\psi ({\bf{R}})\right\rangle \) and an internal part \(\left\chi ({\bf{r}})\right\rangle \). Here, R is the 2D position vector of the exciton centerofmass, whereas r is the internal coordinate vector, measuring the difference between the position of the electron and the hole. The centerofmass part \(\left\psi \right\rangle \) can be expanded in terms of plain waves, each characterized by a different 2D centerofmass wavevector K. Of the different plain waves centerofmass states, only the state \(\left{\bf{K}}=0\right\rangle \) is optically bright since the momentum change of the electronic states upon absorption of a photon is negligible. Importantly, the oscillator strength F_{K=0} of the transition from the ground state to this \(\left{\bf{K}}=0\right\rangle \) scales proportional to the platelet area, see Supporting Information S7^{39}. As sketched in Figure 5a, the \(\left{\bf{K}}=0\right\rangle \) state describes in real space an exciton state with a centerofmass that is fully delocalized across the entire nanoplatelet.
The delocalized exciton is an eigenstate of the periodic crystal lattice. Deviations from this perfect structure, such as (static) stacking faults of the crystal, thickness variations or changes in surface composition, and (dynamic) lattice vibrations, will tend to localize the exciton centerofmass^{40,41}. Such localized excitons can be described by wave packets, i.e., linear combinations of plain waves centered around a given centerofmass wavevector. While a more general approach is presented in Supporting Information S7, we assess the effect of centerofmass localization here by describing the centerofmass wavefunction as a 2D Gaussian wave packet characterized in real space by the wave function ψ(R) and in reciprocal space by the corresponding Fourier transform ϕ(K):
Here, σ measures the realspace delocalization of the centerofmass (see Fig. 5). We should note that various localization mechanisms could give rise to different localized wavefunctions. However, as argued in Supporting Information S7, the conceptual picture put forward here does not depend on the assumption of a Gaussian wave packet.
As outlined in Fig. 5, increasing the localization in real space enhances the delocalization in reciprocal space, and reduces the contribution ∣ϕ(0)∣^{2} of the bright \(\left{\bf{K}}=0\right\rangle \) state to the localized exciton. Using this model of a Gaussian wave packet, the probability P_{0} to find a wave packet in the \(\left{\bf{K}}=0\right\rangle \) state can be written more precisely as:
Here, we used the fact that a single state occupies an area 4π^{2}/S in reciprocal space, with S the platelet area (see Fig. 5 for a 1D equivalent). As a result, we find that the oscillator strength F_{X} to form a localized exciton state centered around K = 0 in reciprocal space can be written as a function of F_{K=0} as:
In the second equation, we interpreted 8πσ^{2} as the socalled coherence area S_{coh} of the wave packet, see Supporting Information S7. We thus retrieve the result already put forward by Feldmann et al.^{42}, that exciton localization reduces the effective oscillator strength to form a 2D exciton by a factor S_{coh}/S.
According to Eq. (8), a transition to form a localized exciton will have a smaller oscillator strength than the formation of the K = 0 exciton. However, each nanoplatelet will have multiple localized excitons as eigenstates, which are related with the plain wave basis by a unitary transformation. Therefore, the sum of the weight P_{0} (see Eq. (7)) over the different localized exciton states equals 1. We thus conclude that the distinction between localized and delocalized excitons does not affect the integrated absorption coefficient, such that F_{abs} yields an estimate of F_{K=0}. On the other hand, when the coherence between these different localized exciton states addressed by the pump pulse is lost within the duration of that pulse, the optical Stark measurement addresses a collection of independent, localized excitons, and measures the transition dipole moment of forming a single localized exciton. Under such conditions, the ratio F_{Stark}/F_{abs} provides a measure of the coherence area of the 2D exciton in CdSe nanoplatelets:
Note that a similar argument follows from Dicke’s treatment of optical transition in a collection of n twolevel systems^{43}, which would be localized excitons for the case studied in this work. Using the experimental values found for F_{Stark} and F_{abs} for the 326 nm^{2} sample, Eq. (9) yields a coherence area S_{coh} = 6.1 nm^{2}. Returning to the Gaussian wavepacket, this corresponds to a radial spread on the exciton centerofmass of \({\sigma }_{R}=\sqrt{2}\sigma \approx 0.70\ {\rm{nm}}\).
In line with the discussion of exciton absorption by Elliot^{39}, F_{Abs} should increase proportionally with the nanoplatelet area S. This point is confirmed in Fig. 6a, where we display F_{Abs} as determined for 5 different sets of 4.5 ML nanoplatelets, with areas ranging from 68 to 326 nm^{2}. The coherence area S_{coh}, on the other hand, is determined by disturbances of the periodic crystal structure, such as lattice vibrations, impurities or an irregular surface termination (see later). Since the smallest area of the nanoplatelets studied still exceeds the estimated coherence area by one order of magnitude, we expect that such disturbances will yield the same coherence area – and thus the same F_{Stark} – for the different nanoplatelets studied. Fig. 6a confirms this point. While F_{Abs} increases almost 5fold when raising the nanoplatelet area from 68 to 326 nm^{2}, we obtain an average < F_{Stark} > of 2.6 without any systematic variation throughout the series of nanoplatelets analysed.
The radiative lifetime of the exciton
Following the interpretation put forward in the previous section that F_{Stark} measures the oscillator strength of forming a single, localized exciton in a CdSe nanoplatelet, the same oscillator strength should determine the radiative recombination rate k_{rad} of such a localized exciton. Due to the small energy splitting between the dark and bright exciton states, the heavy hole exciton will only be half of the time in a bright state. Taking this occupation probability into account, k_{rad} can be obtained from F_{Stark} according to:^{31,44}
Here, all symbols have their usual meaning. Using F_{Stark} = 3.1 for the 326 nm^{2} sample, we obtain k_{rad} = 0.18 ns^{−1}, a rate that corresponds to a radiative lifetime τ_{Stark} = 5.6 ns. This figure agrees well with the average luminescent lifetime τ_{PL} = 6.6 ns we determined from the fluorescence decay and is on par with the 6.4 ns measured by Morgan et al. for similar 4.5 ML CdSe nanoplatelets^{20}. This lifetime is slightly larger than the 3.7 ns measured for highly efficient CdSe nanoplatelets passivated with a CdS crown by Leemans et al.^{21}. Figure 6b compares the lifetime determined by OSE spectroscopy, τ_{Stark}, and the luminescent lifetime, τ_{PL}, for 4.5 ML CdSe nanoplatelets with various surface area. Similar to F_{Stark}, we find that τ_{PL} is independent of the surface area and that the both numbers coincide within the statistical error on the analysis.
Based on this result, we conclude that interpreting the ratio F_{Stark}/F_{Abs} as the ratio between the exciton coherence area and the total nanoplatelet area leads to a consistent interpretation. F_{Abs} is proportional to the total platelet area and determines the pronounced exciton feature in the absorption spectrum, while F_{Stark} is proportional to the coherence area of the localized exciton and is the relevant quantity to understand the radiative lifetime of the exciton. This result questions previously published estimates of the exciton area at room temperature of 96 nm^{2} or 21 nm^{2} for similar 4.5 ML nanoplatelets^{19,20}. Such large coherence areas would yield significantly shorter room temperature radiative lifetimes than measured experimentally. Opposite from the approach used here, these estimates analysed the reduction of the exciton absorption with increasing exciton population from a statefilling perspective, a method hampered by accurate understanding of the saturation of exciton absorpiton in 2D systems, which are bosons showing no exclusion principle, and/or complications due to charge trapping. We stress that the OSE produces an oscillator strength that directly predicts the correct radiative lifetime, without need for corrections such as electronhole overlap or thermal equilibria with supposed higher lying energy levels^{20}.
On the origin of exciton localization
While nanoplatelets appear as highly crystalline structures with a welldefined surface chemistry^{2,45}, stacking faults or local variations in surface termination seem unavoidable in such extended crystallites. In addition, lattice vibrations make that atoms permanently oscillate around their equilibrium position. The resulting static and dynamic deviations of the actual electronic potential from that of the perfectly periodic crystal lattice localizes the exciton centerofmass^{40}. It was argued by Efros et al. that the exciton coherence area is related to the energy variations these deviations bring about^{40}. This point can be understood from the inverse relation between localization in real space and delocalization in reciprocal space; a fundamental aspect of the uncertainty principle highlighted in Fig. 5. More quantitatively, to reduce the variation of the centerofmass in real space to σ_{X}, a variation of \({\sigma }_{{K}_{X}}\ge 1/2{\sigma }_{X}\) is needed at least. Reaching states with such a wave vector requires an additional energy ΔE relative to the K = 0 state of:
Here, we replaced \({\sigma }_{{K}_{X}}\) by 1/2σ_{X} and we applied the Gaussian wave packet to identify σ_{X} with σ. A difficulty to use the above equation is the uncertainty on the hole effective mass for CdSe, which is highly anisotropic and reported values range from 0.45 to 1.21 along [100] and from 1.61 to 1.92 along [111]. Even so, taking the total exciton mass M = m_{e} + m_{h} equal to the free electron mass, we obtain a localization energy of ≈35 meV; a figure that may overestimate ΔE but is still comparable to thermal energy at room temperature.
The correspondence between the localization energy and thermal energy suggests that exciton localization is in part caused by thermal effects. To assess this point, we analyzed the variation of F_{Stark} as a function of temperature, down to 77 K, see Supporting Information S8 for experimental details. As can be seen in Figure 7a, the instantaneous transient absorbance when pumping below the bandgap corresponds to the derivative of the absorption spectrum at 295 K and 77 K, alike. However, reducing temperature to 77 K significantly enhances the magnitude of the transient absorbance under similar pump conditions. While a quantification of this transient absorbance into an energy shift ΔE requires the absorbance spectrum and the screening factors f_{xx} and f_{xy} at the relevant temperature, a first estimate of ΔE can be obtained by assuming these quantities to be temperature independent. This is not unreasonable as the shape of the transient absorption spectrum measured at 77 K matches quite well the derivative of the absorption spectrum measured at 295 K. As shown in Figure 7a, such an analysis leads to an estimated increase of F_{Stark} by more than a factor of 2 when cooling down the nanoplatelets to 77 K. We thus conclude that thermal effects directly contribute to exciton localization.
When measuring the optical Stark effect through subbandgap pumpprobe spectroscopy, the pump pulse does not created excitons but rather changes the photon energy at which excitons are formed. Exciton localization by thermal effects can therefore involve temperaturedependent changes of the potential energy landscape, for example linked to lattice vibrations, not an activation energy that may prevent initially formed excitons from exploring a static the potential energy landscape at low temperature. In the absence of any additional localization due to static imperfections, lowering the temperature could thus lead to fully delocalized excitons under cryogenic conditions, as argued by Naeem et al.^{14} through fourwave mixing experiments at 4 K. Under such conditions, F_{Stark} will increase to become equal to F_{Abs}, and the radiative lifetime of the bright exciton will shorten by a factor S_{coh,298} K/S. In the case of 326 nm^{2} nanplatelets, the resulting τ_{rad,4 K} would amount to 105 ps, a number that agrees with published experimental results^{1,14}.
Acknowledging that excitons in 2D nanoplatelets exhibit a significant localization of the exciton centerofmass, the question arises as to how this compares to 0D quantum dots. To address this point, we analyzed the nonlinear Stark effect of a film consisting of 6.25 nm CdSe quantum dots. For details on the synthesis and properties of the QDs, see Methods section and Supporting Information S1. Fig. 7b represents the absorbance spectrum and a ΔA trace at zero time delay recorded on this film upon excitation using a 700 nm pump laser, see Supporting Information S10 for more details. Also in this case, it can be seen that this pulse, which has a detuning Δ of 150 meV relative to the bandedge transition, induces a transient absorbance around the bandedge that resembles the derivative of the absorbance spectrum. From the corresponding energy shift, we estimate an oscillator strength F_{Stark} = 8.4 for the bandedge exciton. On the other hand, calculating the oscillator strength from the integrated absorption coefficient spectrum yields F_{abs} = 11.9, see Supporting Information S10. This number agrees with published values^{38}, and highlights that, opposite from CdSe nanoplatelets, the ratio F_{Stark}/F_{abs} is around 1 in the case of CdSe quantum dots. Hence, for 0D quantum dots, the coherence volume of the exciton and the volume of the nanocrystal effectively coincide, i.e., the exciton is fully delocalized over the entire nanocrystal. Clearly, this lack of localization is intrinsically linked to the electron and the hole occupying states showing 3dimensional quantization with quantization energies exceeding the localization energy. Hence, one could use the finding that the ratio F_{Stark}/F_{abs} is nearunity as a fingerprint of strong confinement and thus identify zerodimensional quantum systems.
In conclusion, we analyzed the oscillator strength of the exciton transition in 4.5 monolayer CdSe nanoplatelets. By means of the optical Stark effect, induced and measured through contactfree femtosecond pumpprobe spectroscopy, we obtain an oscillator strength that is smaller by a factor of 50 than the oscillator strength derived from the integrated absorption coefficient. We attribute this difference to exciton localization within the CdSe nanoplatelet. Since multiple localized excitons can be formed, localization does not affect the absorption coefficient of the exciton transition. However, since coherence between different localized excitons is lost within the time span of the ca. 100 femtosecond pump pulse, the Stark shift of individual localized excitons is measured^{35}. Having rationalized the ratio between both oscillator strengths as the ratio between the exciton coherence area and the total nanoplatelet area, we obtain an exciton coherence area of 6.1 nm^{2} at room temperature. Importantly, opposed to commonly used statefilling models, we can use the optical Stark measurement to calculate the exact radiative lifetime, without any assumptions^{19,20}. This internally consistent picture indicates that the coherence area of excitons in 4.5 ML CdSe nanoplatelets is considerably smaller than the total nanoplatelet area.
When reducing temperatures to 77 K, the coherence area increases more than twofold, suggesting that exciton localization is at least partially a thermal effect. This conclusion is supported by the fact that thermal energy at room temperature can suffice to localize the exciton centerofmass in the observed coherence area. Remaining decoherence and localization will most likely stem from crystal imperfections such as twin defects, missing surface ligands, etc. Clearly, the expected giant oscillator strength does not manifest itself at room temperature due to intrinsic limitations of the material, rather than impurity or defect localization, thereby limiting the potential for their use in strong lightmatter coupling scenarios at room temperature. When applying the same approach to CdSe QDs, we find that oscillator strengths measured through the optical Stark effect and the integrated absorption coefficient are comparable. This suggests that in such systems, electronhole pairs are fully delocalized across the entire quantum dot volume and that the agreement between both oscillator strengths can be used as a descriptor to identify zerodimensional quantum systems. Finally, our work suggests that the numerous reports on transition dipole moments in 2D materials report the oscillator strength of strongly localized excitons. The commonly used OSE experiment is as such more of a probe for exciton localization and the effective oscillator strength under the measurement conditions, rather than revealing the maximum achievable oscillator strength, relevant for device applications.
Materials and methods
Synthetic methods
Chemicals
Toluene (>99.8%), methanol (>99.85%), isopropanol (>99.7%) and acetone (>99.5%) were purchased from Fiers; oleic acid (90%), cadmium oxide (>99.99% metals bases), selenium (99.999%) and 1octadecene (ODE, tech.) were purchased from Alfa Aesar; trioctylphospine (TOP, 97%) was purchased from Strem Chemicals. All chemicals were used without further purification.
Synthesis
Details on the synthesis of varying area nanoplatelets and bulklike CdSe quantum dots is laid out in the Supplementary Information.
Pumpprobe spectroscopy
Setup
Samples were excited using 120 femtosecond pump pulses with varying wavelengths created from the 800 nm fundamental (Spitfire Ace, Spectra Physics) through nonlinear conversion in an OPA (Light Conversion TOPAS). Equally short probe pulses were generated in a 2 mm CaF_{2} crystal using the 800 nm fundamental. The pulses were delayed relative to the pump using a delay stage with 33 fs bidirectional accuracy. The probe spectrum in our experiments covers the UVVIS window from 350 nm up to 750 nm, yet we focus our attention on the region near the band edge, i.e., the heavyhole transition at 510 nm for the CdSe platelets and the 1S1S transitions manifold at 645 nm for the CdSe QDs. Pump and probe pulses were linearly polarized using appropriate polarization optics, in particular a broadband quartzMgF_{2} quarter wave plate (Newport) is used for the probe and a Bérek compensator or calcite polarizer (Newport) is used to rotate or fix the pump polarization. For variable temperature experiments, the same samples as for the room temperature experiments are loaded in a vacuum contact cryostat which is backfilled with liquid nitrogen.
Photon flux calculation
The photon flux is calculated from the average power, the repetition rate and the beam area. The latter is obtained through a Thorlabs CCD beam profiler, and defined as A_{beam} = 2π × σ_{x}σ_{y} where σ_{i} is the standard deviation in the i = x, y direction.
References
Ithurria, S. et al. Colloidal nanoplatelets with twodimensional electronic structure. Nat. Mater. 10, 936–941 (2011).
Singh, S. et al. Colloidal CdSe nanoplatelets, a model for surface chemistry/optoelectronic property relations in semiconductor nanocrystals. J. Am. Chem. Soc. 140, 13292–13300 (2018).
Grim, J. Q. et al. Continuouswave biexciton lasing at room temperature using solutionprocessed quantum wells. Nat. Nanotech. 9, 891–895 (2014).
She, C. et al. Red, yellow, green, and blue amplified spontaneous emission and lasing using colloidal CdSe nanoplatelets. ACS Nano 9, 9475–9485 (2015).
She, C. et al. Lowthreshold stimulated emission using colloidal quantum wells. Nano Lett. 14, 2772–7 (2014).
Guzelturk, B., Pelton, M., Olutas, M. & Demir, H. V. Giant Modal Gain Coefficients in Colloidal IIVI Nanoplatelets. Nano Lett. https://doi.org/10.1021/acs.nanolett.8b03891 (2018).
Geiregat, P. et al. Thermodynamic equilibrium between excitons and excitonic molecules dictates optical gain in colloidal cdse quantum wells. J. Phys. Chem. Lett. 10, 3637–3644 (2019).
Flatten, L. C. et al. Strong exciton photon coupling with colloidal nanoplatelets in an open microcavity. Nano Lett. 16, 7137–7141 (2016).
Winkler, J. M. et al. Roomtemperature strong coupling of CdSe nanoplatelets and plasmonic hole arrays. Nano Lett. 19, 08–115 (2019).
Mak, K. & Shan, J. Photonics and optoelectronics of 2D semicondcutor transition metal dichalcogenides. Nat. Publ. Group 10, 216–226 (2016).
Wang, Q. H., KalantarZadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of twodimensional transition metal dichalcogenides. Nat. Nanotech. 7, 699–712 (2012).
Kumagai, M. & Takagahara, T. Excitonic and nonlinearoptical properties of dielectric quantumwell structures. Phys. Rev. B 40, 12359 (1989).
Pelant, I. & Valenta, J. Luminescence spectroscopy of semiconductors (2012).
Naeem, A. et al. Giant exciton oscillator strength and radiatively limited dephasing in twodimensional platelets. Phys. Rev. B 91, 8–12 (2015).
Tomar, R. et al. A Charge Carrier Cooling Bottleneck opens up NonExcitonic Gain Mechanisms in Colloidal CdSe Quantum Wells. J. Phys. Chem. C https://doi.org/10.1021/acs.jpcc.9b02085 (2019).
Giovanella, U. et al. Efficient solutionprocessed nanoplateletbased lightemitting diodes with high operational stability in air. Nano Lett. 18, 3441–3448 (2018)..
Lefebvre, P. et al. Recombination dynamics of free and localized excitons in GaN/Ga0.93Al0.07N quantum wells. Phys. Rev. B 57, R9447–R9450 (1998).
Andreani, L. C., Tassone, F. & Bassani, F. Radiative lifetime of free excitons in quantum wells. Sol. St. Comm. 77, 641–645 (1991).
Li, Q., Liu, Q., Schaller, R. D. & Lian, T. Reducing the optical gain threshold in twodimensional CdSe nanoplatelets by the giant oscillator strength transition effect. J. Phys. Chem. Lett. 10, 1624–1632 (2019).
Morgan, D. P. & Kelley, D. F. Exciton localization and radiative lifetimes in CdSe Nanoplatelets. J. Phys. Chem. C. 123, 18665–18675 (2019).
Leemans, J. et al. Nearedge ligand stripping and robust radiative exciton recombination in CdSe/CdS core/crown nanoplatelets. J. Phys. Chem. Lett. 11, 3339–3344 (2020).
Von Lehmen, A., Chemla, D. S., Heritage, J. P. & Zucker, J. E. Optical stark effect on excitons in GaAs quantum wells. Opt. Lett. 11, 609 (1986).
Yang, Y. et al. Large polarization dependent exciton optical stark effect in lead iodide perovskites. Nat. Comm. 7, 1–5 (2016).
Giovanni, D. et al. Tunable roomtemperature spinselective optical stark effect in solutionprocessed layered halide perovskites. Sci. Adv. 4, 1–7 (2016).
Song, D. et al. Measurement of the optical stark effect in semiconducting carbon nanotubes. Appl. Phys. A 96, 283–287 (2009).
Kim, J. et al. Ultrafast generation of pseudomagnetic field for valley excitons in WSe2 monolayers. Science 346, 1205–1208 (2014).
Sie, E. J. et al. Valleyselective optical stark effect in monolayer WS2. Nat. Mater. 14, 290–294 (2014).
Yong, C. K. et al. Biexcitonic optical stark effects in monolayer molybdenum diselenide. Nat. Phys. 14, 3–8 (2018).
Scott, R. et al. Timeresolved stark spectroscopy in CdSe nanoplatelets: exciton binding energy, polarizability, and fielddependent radiative rates. Nano Lett. 26, 6576–6583 (2016).
Diroll, B. T. Circularly polarized optical stark effect in CdSe colloidal quantum wells. Nano Lett. 20, 7889–7895 (2020).
Hens, Z. & Moreels, I. Light absorption by colloidal semiconductor quantum dots. J. Mater. Chem. 22, 10406–10415 (2012).
Heckmann, J. et al. Directed twophoton absorption in CdSe nanoplatelets revealed by kspace spectroscopy. Nano Lett. 17, 6321–6329 (2017).
Combescot, M. & Combescot, R. Optical stark effect of the exciton: biexcitonic origin of the shift. Phys. Rev. B 40, 3788–3801 (1989).
SchmittRink, S., Chemla, D. S. & Miller, D. A. B. Theory of transient excitonic optical nonlinearities in semiconductor quantumwell structures. Phys. Rev. B 32, 6601–6609 (1985).
Cassette, E., Pensack, R. D., Mahler, B. & Scholes, G. D. Roomtemperature exciton coherence and dephasing in twodimensional nanostructures. Nat. Commun. 6, 6086 (2015).
Weidman, M. C., Seitz, M., Stranks, S. D. & Tisdale, W. A. Highly tunable colloidal perovskite nanoplatelets through variable cation, metal, and halide composition. ACS Nano 10, 7830–7839 (2016).
Geiregat, P. et al. Coulomb shifts upon exciton addition to photoexcited PbS colloidal quantum dots. J. Phys. Chem. C. 118, 22284–22290 (2014).
Moreels, I. et al. Optical properties of zincblende cadmium selenide quantum dots. J. Phys. Chem. C. 114, 6371–6376 (2010).
Elliott, R. J. Intensity of optical absorption by excitons. Phys. Rev. 108, 1384–1389 (1957).
Efros, A. L., Wetzel, C. & Worlock, J. M. Effect of a random adiabatic potential on the optical properties of twodimensional excitons. Phys. Rev. B 52, 8384–8390 (1995).
Schnabel, R. et al. Influence of exicton localization on recombination lineshapes: InxGa1x/GaAs quantum wells as a model. Phys. Rev. B 46, 9873–9876 (1992).
Feldmann, J. et al. linewidth dependence of radiative exciton lifetimes in quantum wells. Phys. Rev. Lett. 59, 2337–2340 (1987).
Dicke, R. H. Coherence in spontaneous radiation processes. Phys. Rev. 93, 99–110 (1954).
Shornikova, E. V. et al. Addressing the exciton fine structure in colloidal nanocrystals: the case of CdSe nanoplatelets. Nanoscale 10, 646–656 (2018).
Christodoulou, S. et al. Chlorideinduced thickness control in cdse nanoplatelets. Nano Lett. 18, 6248–6254 (2018).
Acknowledgements
P.G. acknowledges support from FWOVlaanderen (12K8216N). Z.H. acknowledges the Research Foundation Flanders (research projects 17006602 and G0F0920N) and Ghent University (GOA no. 01G01513) for funding. A.J.H acknowledges the ERC and NWOTTW. S. Bisschop is acknowledged for SEM imaging of the platelet layers and K. De Nolf for help with the CdSe QD/platelet synthesis respectively.This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (grant agreement no. 714876 PHOCONA).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Geiregat, P., Rodá, C., Tanghe, I. et al. Localizationlimited exciton oscillator strength in colloidal CdSe nanoplatelets revealed by the optically induced stark effect. Light Sci Appl 10, 112 (2021). https://doi.org/10.1038/s4137702100548z
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s4137702100548z
This article is cited by

Linear and nonlinear electrooptical transitions in CDSE nanoplatelets
Optical and Quantum Electronics (2024)