For the purpose of elucidating the mechanism of the helix-sense inversion phenomena characteristic of poly(aspartic ester)s, we synthesized two diblock copolymers comprising poly(β-phenethyl l-aspartate) (PA) and poly(γ-benzyl l-glutamate) (BG) blocks designated as BG-PA and PA-BG in the order from the C-terminus to the N-terminus. A triblock copolymer sample such as poly(γ-benzyll-glutamate)-b-poly(β-phenethyll-aspartate)-b-poly(γ-benzyl l-glutamate) (BG-PA-BG) was also prepared. The screw sense of α-helical block copolymers was investigated in 1,1,2,2-tetrachloroethane (TCE) solution by the 1H nuclear magnetic resonance (NMR) and circular dichroism techniques as a function of temperature. For the BG-PA diblock copolymer, the helix-sense of the PA block was completely reversed from right- to left-handed at 100°C on heating. The thermal behaviors of triblock copolymer BG-PA-BG was found to be very similar to those of the poly(γ-benzyl l-glutamate) (BG) homopolymer, indicating that the reversal of the screw-sense was entirely restrained. From these observations, we have concluded that during heating, the helix–helix transition proceeds predominantly from the N-terminus in the α-helical polyaspartate system.
Similar content being viewed by others
Article PDF
References
E. R. Blout and R. H. Karlson, J. Am. Chem. Soc., 80, 1259 (1958).
R. H. Karlson, K. S. Norland, G. D. Fasman, and E. R. Blout, J. Am. Chem. Soc., 82, 2268 (1960).
E. M. Bradbury, A. R. Downie, A. Elliott, and W. E. Hanby, Proc. Roy. Soc. London A, 259, 110 (1960).
E. M. Bradbury, B. G. Carpenter, and H. Goldman, Biopolymers, 6, 837 (1968).
E. M. Bradbury, B. G. Carpenter, and R. M. Stephens, Biopolymers, 6, 905 (1968).
M. Hashimoto and J. Aritomi, Bull. Chem. Soc. Jpn., 39, 2707 (1966).
M. Hashimoto and S. Arakawa, Bull. Chem. Soc. Jpn., 40, 1698 (1967).
M. Goodman, C. M. Deber, and A. M. Felix, J. Am. Chem. Soc., 84, 3773 (1962).
M. Goodman, A. M. Felix, C. M. Deber, A. R. Brause, and G. Schwartz, Biopolymers, 1, 371 (1963).
C. Toniolo, M. L. Falxa, and M. Goodman, Biopolymers, 6, 1579 (1968).
Y. Tsujita, N. Fujii, Y. Imoto, A. Takizawa, and T. Kinoshita, J. Polym. Sci., Polym. Chem. Ed., 22, 2533 (1984).
R. Nishizima, Y. Tsujita, and A. Takizawa, Polymer, 26, 379 (1985).
L. Paolillo, P. Temussi, E. Trivellone, E. M. Bradbury, and C. Crane-Robinson, Biopolymers, 10, 2555 (1971).
S. Sasaki, Y. Yasumoto, and I. Uematsu, Macromolecules, 14, 1797 (1981).
J. Watanabe, S. Okamoto, K. Satoh, K. Sakajiri, H. Furuya, and A. Abe, Macromolecules, 29, 7084 (1996).
K. Sakajiri, K. Satoh, K. Yoshioka, S. Kawauchi, and J. Watanabe, J. Mol. Struct., 477, 175 (1999).
H. Toriumi, N. Saso, Y. Yasumoto, S. Sasaki, and I. Uematsu, Polym. J., 11, 977 (1979).
A. Abe, S. Okamoto, N. Kimura, K. Tamura, H. Onigawara, and J. Watanabe, Acta Polym., 44, 54 (1993).
J. Watanabe, S. Okamoto, and A. Abe, Liq. Cryst., 15, 259 (1993).
S. Okamoto, H. Furuya, and A. Abe, Polym. J., 27, 746 (1995).
A. Abe, H. Furuya, and S. Okamoto, Biopolymers. Peptide Science, 43, 405 (1997).
A. Abe, H. Furuya, and S. Okamoto, Polym. Sci., Ser. A, 38, 317 (1996).
S. Okamoto, Ph. D. Dissertation in Polymer Chemistry, Tokyo Institute of Technology, 1995.
W. H. Daly and D. Poche, Tetrahedron Lett., 29, 5859 (1988).
J. C. Mitchell, A. E. Woodward, and P. Doty, J. Am. Chem. Soc., 79, 3955 (1957).
Y. Hayashi, A. Teramoto, K. Kawahara, and H. Fujita, Biopolymers, 8, 403 (1969).
E. M. Bradbury, B. G. Carpenter, C. Crane-Robinson, and H. Goldman, Macromolecules, 4, 557 (1971).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ushiyama, A., Furuya, H., Abe, A. et al. The Mechanism of the Helix-Sense Inversion of Polyaspartates as Revealed by the Study of Model Block Copolymers. Polym J 34, 450–454 (2002). https://doi.org/10.1295/polymj.34.450
Issue Date:
DOI: https://doi.org/10.1295/polymj.34.450