Abstract
We investigated the dyeing properties of polysiloxane networks formed on high-strength and high-modulus polyethylene fiber after hydroxyl groups were introduced onto the fiber surface by chemical treatment. Hydrogen peroxide in o-xylene emulsion in a volume ratio of 1:10 was emulsified by sonication. The emulsion was found to be effective for introduction of hydroxide groups onto the fiber surface. The introduced hydroxide groups reached maximum levels by treatment for approximately 5 min at 80°C. The treatment did not influence the tensile strength of the fiber. Utilizing a polysiloxane network in conjunction with the strong fiber surface formed by treating with 3-aminopropyltriethoxysilane (APS) solution, the dyeing properties of an anionic dye, C.I. Acid Blue 25 was examined. The dyeing resulted in a bluish polyethylene fiber and the color depended upon the duration of treatment with the APS solution. The method proposed in the present study can be used to dye a polyethylene fiber surface.
Similar content being viewed by others
Article PDF
References
J. C. Von der Heide and H. L. Wilson, Mod. Plastics, 38, 199 (1961).
K. Rossmann, J. Polym. Sci., 19, 141 (1956).
J. R. Hall, C. A. L. Westerdahl, A. T. Devine and M. J. Bodnar, J. Appl. Polym. Sci., 13, 2085 (1969).
C. Y. Kim, J. Evans, and D. A. I. Goring, J. Appl. Polym. Sci., 15, 1365 (1971).
A. R. Blythe, D. Briggs, C. R. Kendall, D. G. Rance, and V. J. I. Zichy, Polymer, 19, 1273 (1978).
D. Briggs, J. Adhes., 13, 287 (1982).
M. M. Kadash and C. G. Seefried, Jr., Plast. Eng., 41, 45 (1985).
F. C. Schwab and M. A. Kadash, J. Plast. Film Sheeting, 2, 119 (1986)
M. Rasch and D. Briggs, in “Adhesion”, K. W. Allen, Ed., Applied Science, London, 1982, vol. 6, pp 111—120.
B. Westerlind, A. Larsson, and M. Rigdahl, Intl. J. Adhes. Adhes., 7, 141 (1987).
A. Anon, Plastverarbeiter, 38, 63 (1987).
L. Mascia and G. E. Carr, Plast. Rubber Process. Appl., 9, 133 (1988).
G. E. Ealer, W. C. Harris, and S. B. Samuels, J. Plast. Film Sheeting, 6, 17 (1990).
H. P. Schreiber and F. St. Germain, J. Adhes. Sci. Technol., 4, 319 (1990).
A. Savolanien and J. Kuusipalo, Tappi J., 73, 133 (1990).
G. E. Ealer, S. B. Samuels, and W. C. Harris, Tappi J., 73, 145 (1990).
K. Bartos, Przegl. Wlok., 43, 417 (1989).
J. A. Lanauze and D. L. Myers, J. Appl. Polym. Sci., 40, 595 (1990).
M. Morra, E. Occhiello, L. Gila, and F. Garbassi, J. Adhes., 33, 77 (1990).
W. L. Wade, Jr., R. J Mammone, and M. Binder, J. Appl. Polym. Sci., 43, 1589 (1991).
P. J. C. Cheppell, J. R. Brown, G. A. George, and H. A. Willis, Surf. Interface Anal., 17, 143 (1991).
S. Corn, K. P. Vora, M. Strobel, and C. S. Lyons, J. Adhes. Sci. Technol., 5, 239 (1991).
D. F. Kagan and V. V. Prokopenko, Plast. Massy, 16, 39 (1991).
L. Dorn and W. Wahono, Kunststoffe, 81, 764 (1991).
R. Foerch, J. Izawa, and G. Spears, J. Adhes. Sci. Technol., 5, 549 (1991).
Z. F. Li, A. N. Netravali, and W. Sachse, J. Mate. Sci., 27, 4625 (1992).
B. Tissington, G. Pollard, and I. M. Ward, Composite Sci. Technol., 44, 185 (1992).
G. A. George and H. A. Willis, High Perform. Polym., 1, 335 (1989).
S. Gao and Y. Zeng, J. Appl. Polym. Sci., 47, 2065 (1993).
S. Gao and Y. Zeng, J. Appl. Polym. Sci., 47, 2093 (1993).
D. N. Hild and P. Schwartz, J. Adhes. Sci. Technol., 6, 897 (1992).
M. Zenkiewicz, Zesz. Nauk. Politech. Slask., Mech., 98, 130 (1990).
J. R. Brown, P. J. C. Chappell, and Z. Mathys, J. Mater. Sci., 27, 6475 (1992).
M. Osterhold and A. Wiechers, Materialpruefung, 35, 178 (1993).
Y. Yao, X. Liu, and Y. Zhu, J. Adhes. Sci. Technol. 7, 63 (1993).
M. H. Hansen, M. F. Finlayson, M. J. Castille, and J. D. Goins, Tappi J., 76, 171 (1993).
C. M. G. Carlsson and K. S. Johansson, Surf. Interface Anal., 20, 441 (1993).
Y. Chaoting, S. Gao, and Q. Mu, J. Mater. Sci., 28, 4883 (1993).
V. C. Della, L. Fambri, R. Fenner, C. Migliaresi, and A. Pegoretti, J. Mater. Sci., 29, 3919 (1994).
W. S. Gutowski and E. R. Pankevicius, Composite Interfaces, 1, 141 (1993).
S. Sapieha, J. Cerny, J. E. Klemberg-Sapieha, and L. Martinu, J. Adhes., 42, 91 (1993).
F. P. M. Mercx, Polymer, 35, 2098 (1994).
S. O’Kell, T. Henshaw, G. Farrow, M. Aindow, and C. Jones, Surf. Interface Anal., 23, 319 (1995).
D. M. Brewis, I. Mathieson, and M. Wolfensberger, Intl. J. Adhes. Adhes., 15, 87 (1995).
I. Sutherland, R. P. Popat, D. M. Brewis, and R. Calder, J. Adhes., 46, 79 (1994).
P. Masse, J. P. Cavrot, P. Francois, J. M. Lefebvre, and B. Escaig, Polym. Compos., 15, 247 (1994).
J. J. Ziccarelli, Mod. Plastics, 40, 125 (1962).
E. Piiroja and A. Dankovics, Plast. Massy, 7, 35 (1982).
E. Piiroja and H. Lippmaa, Acta Polymerica, 35, 669 (1984).
E. Sheng, I. Sutherland, D. M. Brewis, R. J. Heath, and R. H. Bradley, J. Mater. Chem., 4, 487 (1994).
W. H. Schrader and M. J. Bodnar, Plast. Technol., 3, 988 (1957).
M. J. Bodnar and W. J. Powers, Plast. Technol., 4, 721 (1958).
M. D. Anderson and M. J. Bodnar, Adhesive Age, 9 (Nov.), 26 (1964).
D. A. Olsen and A. J. Osteraas, J. Polym. Sci., Polym. chem. Ed., 7, 1913 (1969).
P. Blais, D. J. Carlsson, G. W. Csullog, and D. M. Wiles, J. Colloid Interface Sci., 47, 636 (1974).
K. Saito, Nippon Setchaku Kyoukaish, 27, 302 (1983).
C. Fonseca, J. M. Perena, J. G. Fatou, and A. Bello, J. Mater. Sci., 20, 3283 (1985).
A. Chew, R. H. Dahm, D. M. Brewis, D. Briggs, and D. G. Rance, J. Colloid Interface Sci., 110, 88 (1986).
M. Deyme, J. Colloid Interface Sci., 112, 183 (1986).
C. G. Golander and B. A. Sultan, J. Adhes. Sci. Technol., 2, 125 (1988).
V. V. Arslanov, A. A. Cherezov, A. E. Chalykh, and V. A. Ogarev, Vysokomol. Soedin., Ser: B, 25, 437 (1983).
E. S. Turkina and E. D. Yakhnin, Vysokomol. Soedin., Ser: A, 27, 643 (1985).
J. T. Simpson, Radiat. Phys. Chem., 25, 483 (1985).
K. Kato, J. Appl. Polym. Sci., 19, 951 (1975).
D. K. Owens, J. Appl. Polym. Sci., 19, 3315 (1975).
H. Fujimatsu, K. Iyo, H. Usami, and S. Ogasawara, Composite Interfaces, (in press).
H. Fujimatsu and S. Kuroiwa, Colloid Polym. Sci., 265, 747 (1987).
H. Fujimatsu and S. Kuroiwa, J. Colloid Interface Sci., 123, 309 (1988).
H. Fujimatsu, S. Ogasawara, N. Satoh, K. Komori, and S. Kuroiwa, Colloid Polym. Sci., 267, 500 (1989).
H. Fujimatsu, S. Ogasawara, N. Satoh, K. Komori, Y. Matsunaga, and S. Kuroiwa, Colloid Polym. Sci., 268, 143 (1990).
H. Fujimatsu, S. Ogasawara, and S. Kuroiwa, Colloid Polym. Sci., 268, 28 (1990).
H. Fujimatsu, S. Ogasawara, and S. Kuroiwa, J. Adhes. Sci. Technol., 4, 35 (1990).
H. Fujimatsu, N. Satoh, S. Yamamoto, H. Usami, S. Ogasawara, and S. Kuroiwa, Composite Interfaces, 2, 117 (1994).
C. A. Finch, “Polyvinyl Alcohol”, John Wiley & Sons, Inc., London, 1973, pp 214—216.
D. G. Kurth and T. Bein, Langmuir, 11, 3061 (1995).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fujimatsu, H., Imaizumi, M., Shibutani, N. et al. Modification of High-Strength and High-Modulus Polyethylene Fiber Surfaces for the Purpose of Dyeing. Polym J 33, 509–513 (2001). https://doi.org/10.1295/polymj.33.509
Issue Date:
DOI: https://doi.org/10.1295/polymj.33.509