Abstract
Morphologies, some physical properties, and biodegradability were investigated for the binary blends of natural poly(3-hydroxybutyrate) [P(3HB)] with chemosynthetic poly(butylene succinate-co-butylene adipate) (PBSA) and poly(butylene succinate-co-ε-caprolactone) (PBSC) prepared using a simple casting procedure. The DSC thermogram of each blend system revealed two distinct glass transitions independent of blend composition. The radial growth rate of P(3HB) spherulite in the blends, observed on a polarizing microscopy, almost kept constant in the blends with P(3HB) content ranged from 50 wt% to 100 wt%. These results indicate that P(3HB) and PBSA, and P(3HB) and PBSC are immiscible in the amorphous state. The enzymatic degradation of blend film was carried out in phosphate buffer (pH 7.5) at 37°C in the presence of P(3HB) depolymerase purified from Alcaligenes faecalis T1. The degradation behavior of blends was monitored by observing UV spectra, measurement of weight-loss and NMR analysis. As a general, the weight-loss rates of blends increased with the increase of P(3HB) content except the blends contained 90 wt% P(3HB) in which a weight-loss was about three times faster than that of pure P(3HB) films. After the beginning of degradation, the content of P(3HB) in films decreased faster than those of blend partners. The biodegradability of aliphatic polyester is suggested to be controllable by blending.
Similar content being viewed by others
Article PDF
References
Y. Doi, “Microbial Polyesters,” VCH Publishers, New York, N.Y., 1990.
P. A Holmes, in “Developments in Crystalline Polymers-2,” D. C. Bassett, Ed., Elsevier, London, 1988, p 1.
A. J. Anderson and E. A. Dawes, Microbiol. Rev., 54, 450 (1990).
R. Sharma and A. R. Ray, J.M.S.-Rev. Macromol. Chem. Phys., C35, 327 (1995).
Y. Hori and A. Yamaguchi, Macromolecules, 28, 406 (1995).
T. Kobayashi, A. Yamaguchi, T. Hagiwara, and Y. Hori, Polymer, 36, 4707 (1995).
N. Koyama and Y. Doi, Macromolecules, 30, 826 (1997).
H. Abe, Y. Doi, H. Aoki, and T. Akehata, Macromolecules, 31, 1791 (1998).
P. Greco and E. Martuscelli, Polymer, 30, 1475 (1989).
Y. Kumagai and Y. Doi, Polym. Degrad. Stab., 36, 241 (1992).
N. Lotti, M. Pizzoli, G. Ceccorulli, and M. Scandola, Polymer, 34, 4935 (1993).
M. Avella and E. Martuscelli, Polymer, 29, 1731 (1988).
M. Avella, E. Martuscelli, and P. Greco, Polymer, 32, 1647 (1991).
Y. Kumagai and Y. Doi, Polym. Degrad. Stab., 35, 87 (1992).
M. Avella, E. Martuscelli, and M. Raimo, Polymer, 34, 3234 (1993).
Y. Azuma, N. Yoshie, M. Sakurai, Y. Inoue, and R. Chûjô, Polymer, 33, 4763 (1992).
L. Zhang, C. Xiong, and X. Deng, Polymer, 37, 235 (1996).
N. Koyama and Y. Doi, Polymer, 38, 1589 (1997).
N. Koyama and Y. Doi, Can. J. Microbiol., 41 (Suppl. 1), 316 (1995).
A. Lisuardi, A. Schoenberg, M. Gada, R. A. Gross, and S. P. McCarthy, Polym. Mater. Sci. Eng., 67, 298 (1992).
S. J. Organ and P. J. Barham, Polymer, 34, 459 (1993).
P. J. Barham, P. Barker, and S. J. Organ, FEMS Microbiol. Rev., 103, 289 (1992).
H. Satoh, N. Yoshie, and Y. Inoue, Polymer, 35, 286 (1994).
L. Finelli, M. Scandola, and P. Sadocco, Macromol. Chem. Phys., 199, 695 (1998).
G. Ceccorulli, M. Pizzoli, and M. Scandola, Macromolecules, 26, 6722 (1993).
G. Tomasi and M. Scandola, J. M. S.-Pure Appl. Polym. Sci., A32, 671 (1995).
T. Ikejima, K. Yagi, and Y. Inoue, Macromol. Chem. Phys., in press.
Y. Kumagai and Y. Doi, Polym. Degrad. Stab., 37, 253 (1992).
H. Abe, I. Matsubara, and Y. Doi, Macromolecules, 28, 844 (1995).
M. Scandola, M. L. Focarrete, G. Adamus, W. Sikorska, I. Baranowska, S. Swierczek, M. Gnatowski, M. Kowalczuk, and Z. Jedlinski, Macromolecules, 30, 2568 (1997).
E. Takiyama, I. Niikura, and Y. Hatano, U.S. Patent, 5 306 787, 1993.
E. Takiyama and T. Fujimaki, in “Biodegradable Plastics and Polymer,” Y. Doi and K. Fukuda, Ed., Elsevier Science B. V., Amsterdam, The Netherlands, 1994, p 150.
Y. Shirakura, T. Fukui, T. Saito, Y. Okamoto, T. Narikawa, K. Koide, K. Tomita, T. Takemasa, and S. Masamune, Biochim. Biophys. Acta, 880, 46 (1986).
K. Kasuya, Y. Inoue, and Y. Doi, Int. J. Biol. Macromol., 19, 35 (1996).
P. Barham, A. J. Keller, E. L. Otun, and P. A. Holmes, J. Mater. Sci., 19, 2781 (1984).
H. Abe, Y. Doi, H. Aoki, T. Akehata, Y. Hori, and A. Yamaguchi, Macromolecules, 28, 7630 (1995).
H. Abe, Y. Doi, Y. Hori, and T. Hagiwara, Polymer, 39, 59 (1998).
M. Scandola, M. L. Focarete, M. Gazzano, A. Matuszowicz, W. Sikorska, G. Adamus, P. Kurcok, M. Kowalczuk, and Z. Jedlinski, Macromolecules, 30, 7743 (1997).
T. Fukui, T. Narikawa, K. Miwa, Y. Shirakura, T. Saito, and K. Tomita, Biochim. Biophys. Acta, 952, 164 (1988).
K. Mukai, K. Yamada, and Y. Doi, Int. J. Biol. Macromol., 15, 361 (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
He, Y., Masuda, T., Cao, A. et al. Thermal, Crystallization, and Biodegradation Behavior of Poly(3-hydroxybutyrate) Blends with Poly(butylene succinate-co-butylene adipate) and Poly(butylene succinate-co-ε-caprolactone). Polym J 31, 184–192 (1999). https://doi.org/10.1295/polymj.31.184
Issue Date:
DOI: https://doi.org/10.1295/polymj.31.184