Abstract
The sol-gel transitions of linear low density polyethylenes in decalin, tetralin, o-xylene, and toluene were studied. Each sample was a copolymer of ethylene and butene-1, 4-methyl-pentene-1, or octene-1. A thermo-reversible gel was formed for each system and gel-melting temperatures were measured at concentrations of about 4–14 g/100 cm3. It was found experimentally that the gel-melting temperature depended on polymer concentration, molecular weight of the polymer, and the kind of comonomer. Moreover, the structure of crystallite involved in the gel was examined by a polarizing microscope and many spherulites were observed. The data were treated phenomenologically using the thermodynamic theory of Takahashi, Nakamura, and Kagawa, derived for the gel-melting temperature of a crystalline linear copolymer gel. In each solvent, a linear relationship was found to hold between the reciprocal absolute gel-melting temperature 1/Tmg, and ln V2N for samples having a same kind of comonomer, where V2 is the volume fraction of the polymer and N is the weight-average degree of polymerization.
Similar content being viewed by others
Article PDF
References
A. Takahashi, T. Nakamura, and I. Kagawa, Polym. J., 3, 207 (1972).
H. Matsuda, K. Araki, M. Yamada, and S. Kuroiwa, Rep. Prog. Polym. Phys. Jpn., 20, 69 (1977).
H. Matsuda and S. Kuroiwa, Rep. Prog. Polym. Phys. Jpn., 22, 45 (1979).
H. Matsuda, K. Araki, H. Fujimatsu, and S. Kuroiwa, Polym. J., 13, 587 (1981).
H. Matsuda, H. Fujimatsu, M. Imaizumi, and S. Kuroiwa, Polym. J., 13, 807 (1981).
J. E. Eldridge and J. D. Ferry, J. Phys. Chem., 58, 992 (1954).
A. Takahashi, M. Sakai, and T. Kato, Polym. J., 12, 335 (1980).
H. Matsuda, M. Imaizumi, H. Fujimatsu, S. Kuroiwa, and M. Okabe, Polym. J., 16, 151 (1984).
P. J. Barham, M. J. Hill, and A. Keller, Colloid Polym. Sci., 258, 899 (1980).
C. O. Edwards and L. Mandelkern, J. Polym. Sci., Polym. Lett. Ed., 20, 355 (1982).
H. Matsuda, H. Fujimatsu, M. Imaizumi, and S. Kuroiwa, Polym. Prepr., Jpn., 30, 575 (1981).
H. Matsuda, M. Imaizumi, H. Fujimatsu, and S. Kuroiwa, Rep. Prog. Polym. Phys. Jpn., 24, 41 (1981).
H. Matsuda, M. Imaizumi, M. Isayama, H. Fujimatsu, and S. Kuroiwa, Rep. Prog. Polym. Phys. Jpn., 25, 87 (1982).
P. J. Flory, J. Chem. Phys., 17, 223 (1949).
L. Mandelkern, J. Appl. Phys., 26, 443 (1955).
A. Takahashi, Polym. J., 4, 379 (1973).
A. Takahashi and S. Hiramitsu, Polym. J., 6, 103 (1974).
A. Takahashi, T. Kawaharada, and T. Kato, Polym. J., 11, 671 (1979).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Okabe, M., Isayama, M. & Matsuda, H. Sol-Gel Transitions of Linear Low Density Polyethylenes in Organic Solvents. Polym J 17, 369–376 (1985). https://doi.org/10.1295/polymj.17.369
Issue Date:
DOI: https://doi.org/10.1295/polymj.17.369
Keywords
This article is cited by
-
Organic aerogels from the polycondensation of resorcinol with formaldehyde
Journal of Materials Science (1989)