Abstract
Spacing of the 1.5 Å-meridional reflection characteristic of the α-helical conformation and corresponding integrated intensity for poly(γ-benzyl D-glutamate), poly(γ-methyl D-glutamate), copoly(γ-benzyl L-glutamate, γ-methyl L-glutamate), and the racemic form of poly(γ-benzyl glutamate) were measured as a function of temperature from −90 to 120°C. Except for racemic poly(γ-benzyl glutamate), it was found that the spacing—temperature curve shows a discontinuity in slope in the vicinity of room temperature, which has been attributed to the onset of side-chain motion. This suggests that the transition is a crystalline phase transition of the second order. The linear thermal expansion coefficients of the 1.5 Å spacings for these polymers all were in order of magnitude of 10−5/°C. It has been suggested that anharmonic vibration is affected by the nature of the side chain and by the side-chain motion. The intensity was found to decrease with increasing temperature, which was interpreted in terms of a Debye—Waller temperature factor for helical backbone atoms. From the temperature dependence of the 1.5 Å-reflection intensity, Young’s modulus of the helix in the direction of the helical axis was estimated. Both the spacing and the intensity of racemic poly(γ-benzyl glutamate) were found to show a small but definite sudden change in the vicinity of 80°C. These indicate that the first-order phase transition at 80°C is accompanied by not only the breakdown of regular stacks of benzyl groups but also a sudden change in the mobility of the α-helical backbone.
Similar content being viewed by others
Article PDF
References
J. A. E. Kail, J. A. Sauer, and A. E. Woodward, J. Phys. Chem., 66, 1292 (1962).
K. Hikichi, J. Phys. Soc. Jpn., 19, 2167 (1964).
A. Tsutsumi, Jpn. J. Appl. Phys., 9, 1130 (1970).
S. Ogawa, H. Obata, and T. Hatakeyama, Proc. 5th Intl. Congr. Rheol. Vol. III, S. Onogi, Ed., University of Tokyo Press, Tokyo, 1970, p 385.
F. Happey D. W. Jones, and B. W. Watson, Biopolymers, 10, 2039 (1971).
R. G. Saba, J. A. Sauer, and A. E. Woodward, J. Polym. Sci., Part A, 1, 1483 (1963).
K. Hikichi, K. Saito, M. Kakeko, and J. Furuichi, J. Phys. Soc. Jpn., 19, 577 (1964).
S. Makino, K. Kamashima, S. Kubota, and S. Sugai, Jpn. J. Appl. Phys., 3, 55 (1964).
S. Sugai, K. Kamashima, S. Makino, and J. Noguchi, J. Polym. Sci., Part A-2, 4, 183 (1966).
J. V. Koleske and R. D. Lundberg, Macromolecules, 2, 438 (1969).
A. Hiltner, J. M. Anderson, and E. Borkowski, Macromolecules, 5, 446 (1971).
A. Tsutsumi, K. Hikichi, T. Takahashi, Y. Yamashita, N. Matsushima, K. Kanke, and M. Kaneko, J. Macromol. Sci., Phys., B8, 413 (1973).
A. Hiltner, J. M. Anderson, and E. Bear, J. Macromol. Sci., Phys., 8, 431, (1973).
Y. Tsujita and I. Uematsu, Polym. J., 6, 274 (1974).
T. Fukuzawa, I. Uematsu, and Y. Uematsu, Polym. J., 6, 537 (1974).
T. Takahashi, A. Tsutsumi, K. Hikichi, and M. Kaneko, Macromolecules, 7, 806 (1974).
C. H. Bamford, A. Elliott, and W. E. Hanby, “Synthetic Polypeptides,” Academic Press, New York, N.Y., 1956, Chapters 7 and 8.
G. D. Fasman, “Poly-α-amino Acids,” Marcel Dekker, Inc., New York, N.Y., 1967.
L. E. Alexander, “X-ray Diffraction Methods in Polymer Science,” John Wiley & Sons, Inc., New York, N. Y., 1969, p 78.
C. H. Bamford, L. Brown, A. Elliott, W. E. Hanby, and I. F. Trotter, Proc. Roy. Soc., B141, 49 (1953).
A. Elliott, R. D. B. Fraser, and T. P. MacRae, J. Mol. Biol., 11, 821 (1965).
D. A. D. Parry and A. Elliott, J. Mol. Biol., 25, 1 (1967).
J. M. Squire and A. Elliott, Mol. Cryst. Liq. Cryst., 7, 821 (1969).
N. Matsushima, K. Hikichi, A. Tsutsumi, and M. Kaneko, Polym. J., 7, 44 (1975).
K. Hikichi, A. Tsutsumi, S. Isozaki, and M. Kaneko, Polym. J., 7, 646 (1975).
D. E. Eisenberg and W. Kauzman, “The Structure and Properties of Water,” Oxford University Press, Ely House, London W.1. 1969, p 104.
A. Roig and M. Cortijo, Biopolymers, 10, 321 (1971).
T. Hiraoki, A. Tsutsumi, K. Hikichi, and M. Kaneko, Rep. Prog. Polym. Phys. Jpn., 17, 575 (1974).
L. Pauling and R. B. Corey, Proc. Nat. Acad. Sci., 37, 4241 (1951).
Y. Mitsui, Y. Iitaka, and M. Tsuboi, J. Mol. Biol., 24, 15 (1967).
S. Kotoda, K. Takagi, Y. Uematsu, and I. Uematsu, Rep. Prog. Polym. Phys. Jpn., 15, 629 (1972).
K. Itoh and T. Shimanouchi, Biopolymers, 9, 383 (1970).
J. M. Squire and A. Elliott, J. Mol. Biol., 65, 291 (1972).
N. Matsushima, K. Hikichi, A. Tsutsumi, and M. Kaneko, Polym. J., 7, 382 (1975).
W. T. Wilser and D. B. Fitchen, Biopolymers, 13, 1435 (1974).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Matsushima, N., Hikichi, K., Tsutsumi, A. et al. X-Ray Scattering of Synthetic Poly(α-amino acid)s in the Solid State. III. Temperature Dependence of the 1.5 Å-Meridional Reflection of the α-Helix. Polym J 8, 88–95 (1976). https://doi.org/10.1295/polymj.8.88
Issue Date:
DOI: https://doi.org/10.1295/polymj.8.88
Keywords
This article is cited by
-
Why Proteins are Big: Length Scale Effects on Equilibria and Kinetics
The Protein Journal (2019)