Rejuvenation is the structural excitation of glassy materials, and is a promising approach for improving the macroscopic deformability of metallic glasses. This atomistic study proposes the application of compressive hydrostatic pressure during the glass-forming quenching process and demonstrates highly rejuvenated glass states that have not been attainable without the application of pressure. Surprisingly, the pressure-promoted rejuvenation process increases the characteristic short- and medium-range order, even though it leads to a higher-energy glassy state. This ‘local order’–‘energy’ relation is completely opposite to conventional thinking regarding the relation, suggesting the presence of a well-ordered high-pressure glass/high-energy glass phase. We also demonstrate that the rejuvenated glass made by the pressure-promoted rejuvenation exhibits greater plastic performance than as-quenched glass, and greater strength and stiffness than glass made without the application of pressure. It is thus possible to tune the mechanical properties of glass using the pressure-promoted rejuvenation technique.
Rejuvenation is the opposite phenomena to ageing, and it has been investigated for decades in relation to molecular and polymeric glasses,1 and more recently in relation to metallic glasses (MGs).2–8 In contrast to rejuvenation, ageing is a structural relaxation of the glassy material that changes both the internal structure and mechanical properties of the glass. Well-aged glass usually exhibits brittle fracture triggered by shear band formation9 at an ambient temperature and usual strain rate. As brittle fracture is a fatal flaw in terms of the application of MGs as structural and mechanical materials, realising a highly rejuvenated state without losing strength and stiffness, and preventing both ageing and brittle fracture (i.e., maintaining the highly rejuvenated state for a long time) are key factors in expanding the applicability of MGs. Some mechanical approaches, such as the application of high-pressure torsion3 and shot peening5 to mechanically realise a rejuvenated state in MGs, have been proposed, but significant shape change or heterogeneous property distribution is unavoidable. Recently, thermal-based approaches such as thermal rejuvenation consisting of recovery annealing10 conducted above the glass transition temperature Tg followed by fast cooling have been proposed.2,6 The thermal approach can control not only the surface properties but also the interior of any glass component shape. It can be also utilised to maintain plastic performance in thermoplastic nanoimprinting of MG,11 which has been developed to realise low-cost fabrication of micro- and nano-sized devices. However, thermal rejuvenation requires rapid cooling after annealing, which should be faster than that of the initial glass-forming quenching process, and moreover it may lose intrinsic strength and elastic stiffness.2,6 These are serious drawbacks in terms of practical application of this approach. To overcome the practical drawbacks, we propose a pressure-promoted thermal rejuvenation technique here, in which pressure is applied during the glass-forming quenching process.
In this study, we performed molecular dynamics (MD) simulations that demonstrate the feasibility of the proposed pressure-promoted thermal rejuvenation process, and we discuss the underlying physics based on diffusivity, α-relaxation, Tg, and internal structure analyses. We found that pressure-promoted rejuvenation is achieved only when a comprehensive influence of three pressure effects on glass-forming process, i.e., effects of temperature-dependent liquid inherent structure energy, pressure-dependent diffusively slowdown (relaxation slowdown) and Tg increase, gains ascendancy over an increase in the Arrhenius–non-Arrhenius diffusivity transition temperature. Then, using MD uniaxial tensile test, we demonstrate that the pressure-promoted thermally rejuvenated glass actually has a weak strain localisation tendency, resulting in better plastic performance. We also examine the feasibility of the pressure-promoted thermal rejuvenation on various alloy systems. Note that some of the examined alloy systems do not exhibit pressure-promoted thermal rejuvenation because the comprehensive influence of three pressure effects fails to override the diffusivity transition temperature rise effect in these alloy systems.
Prediction of pressure-promoted thermal rejuvenation map
We constructed MG models via a melt-quenching process (A→D in Figure 1a) as follows. First, the molten alloy was equilibrated at 3,000 K for 100 ps (A→B) with zero external pressure; then, the model was quenched to 0 K at the same constant cooling rate of K=1.0 K/ps (B→C). Next, the potential energy was minimised using the steepest decent (SD) method at 0 K under zero pressure P=0 GPa (C→D). The constructed MG model (state D) is here referred to as the ‘as-quenched model.’ Using the as-quenched model, we then conducted thermal-pressure loading simulations (D→J) comprising the following steps: (1) loading of the hydrostatic pressure up to the applied pressure Pa at 0 K (D→E); (2) heating from 0 K to the annealing temperature Ta (E→F); (3) isothermal annealing at Ta and Pa for 1 ns (F→G); (4) cooling from Ta to 0 K (G→H) at a constant cooling rate of the K=1.0 K/ps as B→C, followed by minimisation of the potential energy using the SD method; (5) unloading of all normal stresses (σxx, σyy and σzz) independently from Pa to 0 GPa under zero velocity (H→I); and (6) minimising the potential energy under zero pressure using the SD method (I→J). The final obtained model (state J) will be hereafter referred to as the ‘annealed model.’ Cooling (B→C and G→H) is conducted at a constant cooling rate of K=1.0 K/ps and heating rate (E→F) is also 1.0 K/ps. Pressure loading (D→E) and unloading (H→I) are conducted at a constant rate of 0.1 GPa/ps. It is worth noting that the technique of thermal loading under high-pressure condition, such as 10 GPa and more, has been already realised in experiments.12
In this study, we primarily use the Zr50Cu40Al10 MG model, where interatomic interactions are computed using the embedded atom method (EAM) potentials.13 Figure 1b shows the change in the potential energy induced by the thermal-pressure loading process (D→J) ΔE=EJ−ED, where ED and EJ are the potential energies of the as-quenched and annealed models, respectively. ΔE represents the change in the glass state during the thermal-pressure loading process; ΔE becomes positive if rejuvenation occurs and falls below zero in the case of ageing.
Under zero external pressure (Pa=0 GPa), ΔE is solely induced by thermal loading. In Figure 1b, ΔE under the zero-pressure condition is negative below 1.3Tg and becomes almost zero above 1.3Tg. This result demonstrates that rejuvenation cannot be realised under zero pressure if the quenching process (G→H) cooling rates are equal to those of the initial melt-quenching process (B→C). Our previous work2 demonstrated the feasibility conditions for rejuvenation induced by thermal loading, and the thermal rejuvenation was found to be realised only when Ta was above 1.1Tg and when the cooling rate after isothermal annealing was higher than that of the initial melt-quenching process. This was because the fast cooling suppresses ageing during the glass-forming quenching process. Thus, the ΔE profile under zero external pressure shown in Figure 1b supports the conclusions of our previous work,2 even though the glass systems and employed interatomic potentials differ. On the other hand, ΔE profiles under ‘non-zero’ pressure conditions shift from those under zero pressure. The ΔE values for higher annealing temperatures Ta>1.1–1.2Tg clearly demonstrate that tensile pressure enhances ageing, whereas compressive pressure suppresses it. Thus, in this alloy system, the thermal rejuvenation is realised by the application of compressive external pressure instead of rapid quenching, but only when the annealing temperature is above the critical annealing temperature, 1.1–1.2Tg. The degree of rejuvenation increases with increased compressive pressure and/or annealing temperature up to ~1.3Tg, implying that the employed compressive pressure has the same role in increasing the cooling rate in the heating–annealing–quenching process (D→H) from a viewpoint of the degree of rejuvenation ΔE. To clarify effect of the cooling rate K of the processes B→C and G→H on ΔE, we also conducted the same initial melt-quenching (A→D) and subsequent thermal-pressure loading simulations (D→H) with the other several different cooling rates, such as K=0.01, 0.1 and 10 K/ps for Pa=5 GPa, Ta=1.3Tg(Pa), and confirmed that thermal rejuvenation was actually realised in all the cooling rates tested here, and moreover no significant changes in ΔE can be found in the cases of cooling rate K⩽1.0 K/ps (Supplementary Figure S3). It is worth noting that ΔE has the minimum value, in other words, ageing is the most striking, at around Ta~Tg(Pa) in Figure 1b. This is the result of a temperature dependency of two factors; (i) an allowable amount of relaxation (energy reduction) bounded by the energy state of equilibrium liquid, and (ii) an amount of relaxation during certain annealing time. The factor (i) decreases with increasing Ta, and rapidly decreases especially at above Tg, whereas the factor (ii) increases with increasing Ta, and rapidly increases especially at above Tg. As a result at Ta~Tg(Pa), the amount of ageing maximises because the relaxation rate is fast and moreover the large amount of relaxation is allowed (see a schematic illustration in Supplementary Figure S4).
To verify the feasibility of pressure-promoted thermal rejuvenation in other glass systems, we constructed eight different MG models via melt-quenching process (A→D) and applied the same thermal-pressure loading process (D→J) to the MG models, where the interatomic interactions were calculated from different interatomic potentials, such as Zr50Cu40Ag10 (EAM14), Cu50Zr50 (Finnis–Sinclair: FS15), Cu50Zr50 (Lennard–Jones: LJ16), Al90La10 (EAM17), Ni80P20 (EAM18), Pd82Si18 (EAM19), Zr80Pt20 (EAM20) and Al50Fe50 (FS21). Here we set Pa=5 GPa and Ta=1.3Tg(Pa). The resultant changes in the potential energy ΔE are summarised in Figure 2. Pressure-promoted thermal rejuvenation can be seen in many of the examined alloy systems, whereas pressure-promoted ‘ageing’ can be observed in Cu50Zr50 (LJ), Zr80Pt20 and Al50Fe50. This fact reveals that the effect of pressure on the atomic diffusion, which dominates the structural relaxation in the quenching process, is strongly dependent on alloy composition; in other words, it depends on atomic sizes and interatomic interactions. Similar alloy dependence of pressure effects on structural relaxation has been reported for an experimental tensile test conducted on a notched MG sample.22
Changes in internal structure by compressive pressure
To reveal the internal structure change induced by compressive pressure, we analysed icosahedral short-range order (SRO)23 and medium-range order (MRO) composed of interpenetrating icosahedra2,24,25 existing in the inherent structures of the quenching process from far above Tg to 0 K, under a constant cooling rate K and a constant pressure P. The inherent structure is defined as the structure of local minimum on the potential energy landscape at P=0 GPa, and it is calculated using the following process: first, the potential energy from an instantaneous atomic configuration in the cooling process is minimised using the SD method. Then, the pressure is unloaded from P to 0 GPa, and finally the potential energy is again minimised at 0 GPa. The results of the changes in internal structure are summarised in Figure 3, in which icosahedral SRO and MRO are surprisingly increased by compressive pressure in the case of Zr50Cu40Al10, and thus these ordered local structures are supersaturated and more tightly filled in by the compressive pressure application in cooling process, even though the compressive pressure leads to an energetically unstable (i.e., rejuvenated) glass state. These results reverse the conventional understanding of the relationship between characteristic topological order and energy state, in which much icosahedral SRO and MRO lead to an energetically more stable glass state and vice versa.23,24,26,27 Moreover, in the case of Cu50Zr50 (LJ), we cannot see a clear increase in the icosahedral SRO and MRO, even though the pressure leads to an energetically more stable (i.e., aged) glassy state (for other MG systems, see Supplementary Figure S6). These results suggest the presence of a well-ordered high-energy glassy state. It is worth noting that volume of the pressure-promoted thermally rejuvenated Zr50Cu40Al10 model with the compressive pressure application decreases with increasing the degree of rejuvenation ΔE (i.e., increasing the compressive pressure), and thus the volume is always smaller than that of as-quenched model (Supplementary Figure S7). On the other hand, the volume of thermally rejuvenated model with a rapid cooling rate of the G→H faster than that of the B→C, without compressive pressure application (pure thermal rejuvenation model2), increases with increasing the ΔE (i.e., increasing the cooling rate of the G→H process), and thus the volume is always larger than the as-quenched model (Supplementary Figure S7). This means that although if these rejuvenated glasses have the same degree of rejuvenation ΔE, these volumes are totally different; the former one has smaller and the latter one has larger volume than as-quenched model. More details of the volume and SRO analyses are plotted in Supplementary Figure S7. We show the schematic illustration of characteristics of glasses after the pure thermal rejuvenation and the pressure-promoted thermal rejuvenation in Figure 4, in which energy, density and SRO of as-quenched, pure thermally aged and rejuvenated, pressure-promoted thermally rejuvenated glasses are summarised.
Changes in deformation behaviour by pressure-promoted thermal rejuvenation
To demonstrate the pressure-promoted rejuvenation effect on the plastic performance, we performed uniaxial tensile simulations for three different Zr50Cu40Al10 models: the as-quenched model and the thermally rejuvenated models with and without pressure application, i.e., pressure-promoted thermal rejuvenation model and pure thermal rejuvenation model. Figure 5a shows the von Mises atomic strain evolution during uniaxial tensile tests with a constant strain rate of 108 1/s at 300 K. We can see marked strain localisation in the ‘as-quenched model’, whereas more homogeneous deformations with less strain localisation are observed in the two rejuvenated models (Supplementary Movies S5a, S5b and S5c). Thus, the rejuvenation induced by the thermal-pressure loading process can realise more homogeneous deformation than the as-quenched model. Figure 5b represents nominal stress and nominal strain relations along the loading direction (z direction) during the uniaxial loading tests. The maximum stress and elastic stiffness, slope of the stress–strain relation of the thermally rejuvenated model with pressure application are higher than those of the thermally rejuvenated model without pressure application. Moreover, the flow stress of the pressure-promoted thermal rejuvenation model is higher than those of the other two models. Thus, the pressure-promoted thermal rejuvenation process can realise higher strength and stiffness glass without significant loss of plastic deformability than a pure thermal rejuvenation process. We also conducted simple shear and nanoindentation simulations using the same Zr50Cu40Al10 models, which predicts that the excellent elastic and plastic performances of the thermally rejuvenated glass with pressure application is maintained even under different loading and boundary conditions (for the simple shear and nanoindentation simulations see Supplementary Figures S8 and S9, and also Supplementary Movies S8a, S8b, S8c, S9a and S9b).
The MGs constructed under high-pressure condition have rich SRO and MRO, but exhibit homogeneous deformation as shown in Figures 3 and 5. This trend is interesting, but not intuitive. As we revealed in our previous work,2 the pure thermal rejuvenation model shows more homogeneous deformation than as-quenched model. This can be understood by thinking of activation energy of local plastic deformation process, which is often called as shear transformation.28 A lower activation energy of the local plastic deformation process leads to more homogeneous deformation under a certain strain rate and temperature because the process is more equally activated everywhere in MG due to the less local stress state change by the activation of each process and then the MG has less opportunity to have a localised deformation, which will grow to shear band. The pure thermal rejuvenation model may have a lower activation energy of the plastic deformation process because the model is already in the high-energy rejuvenated state. The same way of thinking may be applicable also to the pressure-promoted thermal rejuvenation model. The pressure-promoted thermal rejuvenation model is also in a high-energy rejuvenated state, although the structural details are different from the pure thermal rejuvenation model, and thus it may have lower activation energy of the plastic deformation process. Therefore, the pressure-promoted thermal rejuvenation exhibits the homogeneous deformation. To confirm this scenario, we also performed nanoindentation simulations for several different pressure-promoted thermal rejuvenation (or ageing) models; Cu50Zr50(LJ) (ageing), Ni80P20 (rejuvenation) and Al90La10 (rejuvenation) in addition to Cu50Zr40Al10 (rejuvenation). All of the rejuvenated models actually exhibit more homogeneous deformation than that of as-quenched model, whereas the aged LJ model exhibits less homogeneous deformation (Supplementary Figures S9b, S10b, S11b, S12b; Supplementary Movies S9a, S9b, S10a, S10b, S11a, S11b, S12a and S12b). We should note that, regarding elastic stiffness and maximum load, these are maintained in Zr50Cu40Al10 (rejuvenation) or even increased in Cu50Zr50(LJ) (ageing), whereas decreased in Ni80P20 (rejuvenation) and Al90La10 (rejuvenation). Thus, among these glasses, only Zr50Cu40Al10 (rejuvenation) departs from the intuitive trend, that is, rejuvenation usually leads to lower stiffness and strength and ageing leads to higher. The excellent elastic performance of Zr50Cu40Al10 (rejuvenation) may arise from the significant increase of the icosahedral SRO by the pressure-promoted thermal rejuvenation (Figure 3a), because the icosahedral SRO structure has higher stiffness.24,27 The other rejuvenated Ni80P20 and Al90La10 glasses do not exhibit such significant SRO change. See again Supplementary Figure S6.
To understand the interesting dependency of the effects of pressure on the alloy composition seen in Figure 2, we discuss structural relaxation in the quenching process (G→H) both with and without the effects of pressure below. Figure 6a is a schematic of the change in the inherent structure energy29 of an alloy system during the cooling process from far above Tg to 0 K, under a constant cooling rate K. The inherent structure energy is the energy of inherent structure defined above. Figure 6b shows the actual change in the inherent structure energy of the Zr50Cu40Al10 and Cu50Zr50 (LJ) systems. In Figure 6b, we may reasonably define a transition temperature Tc as a kink temperature on the curve of the inherent energy change. Above the transition temperature Tc (quenching stage I; T⩾Tc), the system can be always in an equilibrium liquid state because of very short relaxation time of the high-temperature liquid. Below Tc (quenching stage II; T<Tc), owing to a lesser free volume, a finite activation energy for atomic structure relaxation is expected, leading to a finite relaxation time competes against the time of cooling process specified by the cooling rate. To examine the physical meaning of Tc, we computed the temperature-dependent diffusivity D and α-relaxation time τα of the Zr50Cu40Al10 and Cu50Zr50 (LJ) glasses, as shown in Figure 6c,d. Above T~1,100 (P=0 GPa) and T~1,200 K (P=5 GPa) in the case of Zr50Cu40Al10 and T~1,200 K (P=0 GPa) and T~1,500 K (P=5 GPa) in the case of Cu50Zr50 (LJ), the diffusion kinetics have a constant activation enthalpy for diffusion ΔG0, and obeys Arrhenius-type behaviour , where kB is the Boltzmann constant. In contrast, below these temperatures, the diffusion kinetics deviate from Arrhenius-type linear behaviour, indicating a change in the activation enthalpy for diffusion. Because these critical temperatures agree well with Tc’s obtained from the kink in Figure 6b, Tc could be understood as a transition temperature between Arrhenius and non-Arrhenius behaviours in diffusivity.30 Because a higher compressive pressure mechanically reduces the free volume, the pressure actually slows down the diffusion in both the alloys over the whole temperature range, as shown in Figure 6c, and these Tc tends to be higher, i.e., Tc(P)>Tc(0) for P>0, as shown in Figure 6b–d. It is worth noting that the same trend can be found in the pressure dependency of Tg31 (Supplementary Figure S2). In Figure 6d, α-relaxation time τα also drastically increases with decreasing temperature at the temperatures ranging from Tg to Tc. This is consistent with the diffusivity behaviour in Figure 6c. It should be noted that if the annealing time is too short compared with a typical relaxation time, such as α-relaxation time τα, the rejuvenation/ageing during the thermal rejuvenation are not sufficiently proceed regardless of with and without pressure application.2 The 1 ns annealing time used in this study is equivalent to or even longer than α-relaxation time τα at temperatures T>Tg (necessary temperature condition for the rejuvenation; see Figure 1b) as shown in Figure 6d. Thus, the 1 ns annealing time is long enough and does not affect on the rejuvenation.
The final inherent structure energy per atom of the state after the quenching process is completed (i.e., state H) at a given P can be expressed as
where K=dT/dt with t being time. Here is the rate of change of the inherent structure energy and Estage I(P, Tc(P)) is the inherent structure energy at the end of stage I (i.e., at the beginning of stage II). Hereafter, the inherent structure energy will be simply referred to as the ‘energy’. The degree of rejuvenation is estimated from the final energy difference ΔE(P)=EH(P)−EH(0), which can also be expressed as the sum of (I) the energy difference at the end of stage I (i.e., at the beginning of state II) ΔEstage I(P) between the P>0 and P=0 GPa conditions and (II) the difference in the total energy change in stage II ΔEstage II(P) between the P>0 and P=0 GPa states, with
From the equation and also schematic illustration shown in Figure 6a, we can find the following five factors can dominate the final energy difference ΔE(P). First, there are three factors in the stage I (T⩾Tc). (i) Temperature dependency of the energy. Usually there exists temperature dependency of liquid energy, and higher-temperature liquid tends to have higher energy,32 i.e., ∂E(P)/∂T>0(T⩾Tc(P)), although alloy dependency can be found as shown in Figure 6b. Larger temperature dependency leads to larger ΔEstage I, and then contributes to enhance the rejuvenation. (ii) Pressure dependency of energy at T⩾Tc(P). The change of energy by pressure can also contributes to the degree of rejuvenation ΔE(P) via changing ΔEstage I(P), but usually the pressure dependency should be small, actually error bars of the data with and without pressure are overlapping as seen in Figure 6b and Supplementary Figure S13a, because the liquid states at T⩾Tc(P) should be always well equilibrated regardless of with and without pressure application. (iii) Pressure dependency of Tc(P). The Tc has not only a strong pressure dependency but also a strong alloy dependency as seen in Figure 6c,d and Supplementary Figure S13b, because it should be closely related to the potential energy surface that determines the starting temperature of the α-relaxation.32 The higher Tc(P) causes α-relaxation to be initiated at higher temperature, then a rapid energy reduction occurs at earlier stage of the cooling process but below Tc. As a result the higher Tc(P) enhances more ageing. Second, there are two factors in the stage II (T<Tc). (iv) Pressure dependency of the relaxation time constant (energy reduction rate), which is the slope of the energy curve in Figure 6b, i.e., ∂E(P)/∂T(T<Tc(P)). Usually the relaxation time becomes longer and thus the energy reduction rate becomes slower with increasing pressure as seen in Figure 6b–d and Supplementary Figure S13a,b, because compressive pressure induces densification (see volume change in Supplementary Figure S13c, induces a less space for moving atom, may effectively suppress the local atomic shuffling and diffusion. (v) Pressure dependency of Tg(P). Tg(P) is related to the temperature at which the energy reduction rate significantly slows down as shown in Figure 6b,d and Supplementary Figure 13Sa,b. The pressure dependency of Tg(P) also has a strong alloy dependency as shown in Figure 6d. The reason should be the same as that of pressure dependency of Tc(P). Hence, the factors (i), (iv) and (v) enhance the rejuvenation, whereas the factor (iii) enhances the ageing. Because of the factor (iii), the energy curve under compressive pressure application is always below that of zero pressure at temperatures just below Tc(P). Therefore, the two energy curves (i.e., with and without pressure) should have a crossover to realise the rejuvenation eventually. As shown in Figure 6b, we actually observed the crossover between the energy–temperature curves both with and without pressure for the Zr50Cu40Al10, but not for the Cu50Zr50 (LJ) (details are given in Supplementary Figure S14). As the crossover temperature increases with increasing the ∂E(P)/∂T>0(T⩾Tc(P)) (factor (i)), the energy reduction rate (factor (iv)) and/or Tg(P) (factor (v)), and decreases with increasing Tc(P) (factor (iii)), the pressure induces two competing effects in the rejuvenation; (A) the factors (i), (iv) and (v), and (B) the factor (iii). In the case of Cu50Zr50 (LJ), the latter effect (B) overcomes the former effect (A), results in the pressure induces ageing. In contrast, in the case of Zr50Cu40Al10, as Tc increase is much smaller than that of Cu50Zr50 (LJ) (Figure 6c), the former effect overcomes the later effect, results in the pressure induces rejuvenation. Therefore, rejuvenation and ageing by thermal-pressure loading process can be predicted from these factors. It should be noted that all of the data determine that these factors are obtainable and predictable by MD simulation based on certain potential description of target alloy system as we performed above.
To clarify underlying physics of the pressure-promoted thermal rejuvenation process and characteristics of the pressure-promoted thermally rejuvenated glass, we additionally conducted energy decomposition analyses, which may provide origin of the pressure-promoted higher energy state (rejuvenation) of Zr50Cu40Al10 and lower-energy state (ageing) of Cu50Zr50 (LJ) from energetics and geometrical ordering viewpoints (Supplementary Figures S15 and S16). We found that in the pressure-promoted thermally rejuvenated and aged glass models, the icosahedral SRO has a significant lower-energy state than the other local structures as similar to the conventional MGs constructed under zero pressure (Supplementary Figure S16). Thus, in the energetics and geometrical ordering viewpoints, the high-energy state of the rejuvenated Zr50Cu40Al10 glass is attributed to the pressure-promoted significant energy increment of the local structures with lower ordering (i.e., non-icosahedral local structures) as schematically shown in Figure 4. The energy increment of the local structure with lower ordering is a result of the less diffusive and mechanical relaxation during the cooling process under the compressive pressure as discussed above Supplementary Figure S17). On the other hand, in the pressure-promoted thermally aged Cu50Zr50 (LJ) glass, the energy increment of the non-icosahedral local structures is not so significant (Supplementary Figure S15), because a mechanical relaxation (atomic rearrangement) unfortunately may proceed in the LJ central force field under the compressive pressure, whereas the diffusive relaxation is well suppressed. As a results, the total energy decreases in the Cu50Zr50 (LJ) glass.
It is worth noting that the less relaxation induced by pressure application may have great benefit also to the glass-forming ability. It effectively prevents a crystallisation of alloy during the quenching process, and thus may improve the apparent glass-forming ability of alloy. We should also note that although such a high cooling rate (K=1.0 K/ps) was used in the MD simulation because of the time-scale limitations of MD, the above discussion for rejuvenation and ageing should be maintained even at practical cooling rates, because by experiments we have confirmed that the ratio of cooling rate of the final quenching process (G→I) to the initial melt-quenching process (B→C) is the dominant factor for the degree of rejuvenation and ageing2 rather than the absolute cooling rates. In addition, the relationship between energy state and deformation behaviour observed in Figure 5 is also consistent with the critical fictive temperature concept, which identifies the brittle–ductile transition state of MG.33 At the fictive temperature Tf, the extrapolated glass line intersects the equilibrium liquid line (Figure 6e), thus the Tf represents the glass state and then more rejuvenated glass has higher Tf. The critical fictive temperature Tfc represents a transition glass state at between glass states showing brittle and ductile behaviours, i.e., a MG having Tfc>Tf is brittle, whereas having Tfc<Tf is ductile. Therefore, the critical fictive temperature concept naturally predicts that the pressure-promoted thermal rejuvenation, which leads to higher Tf, can improve the ductility of MGs. As we have shown in Figure 5, the rejuvenated glass having higher Tf exhibits more homogeneous deformation, supporting the validity of the fictive temperature-based discussion of ductility.
We have demonstrated in this study that the feasibility of pressure-promoted thermal rejuvenation for various alloy systems. It was found that rejuvenation is actually enhanced by applying external pressure in many alloy systems, whereas some alloy systems do not exhibit this response. Further, we clarified the underlying physics of pressure-promoted rejuvenation based on diffusivity, α-relaxation, Tg and internal structure analyses. The pressure-promoted rejuvenation is achieved only when the comprehensive influence of three pressure effects on glass-forming process, i.e., the effects of temperature-dependent liquid energy, pressure-dependent diffusively slowdown (relaxation slowdown) and pressure-dependent Tg increase, overcomes the effect of pressure-dependent increase in the Arrhenius–non-Arrhenius diffusivity transition temperature. Pressure-promoted thermal rejuvenation increases the icosahedral SRO and MRO, even though it leads to an energetically unstable glassy state. This result could change the conventional understanding of the relationship between energy and local structure in MGs, and it strongly indicates the necessity of new energetics of SRO and MRO under significant pressure. We found that the rejuvenated Zr50Cu40Al10 MG made by the pressure-promoted thermal rejuvenation process exhibits greater plastic performance than as-quenched glass, and greater strength and stiffness than glass made by the pure thermal rejuvenation process, and then we believe that this glass rejuvenation engineering technique could introduce a new avenue of research towards the development of glass-state control, and elastic and plastic performance control techniques by thermal processing. Moreover, the pressure effects allow us to increase the upper limit of reachable rejuvenation, which has been restricted by the practical upper limit of a cooling rate in previous rejuvenation-level control techniques with no pressure application.2 It also may allow us to extrinsically improve the apparent glass-forming ability of alloys by delaying crystallisation.
Materials and methods
Models for thermal-pressure loading process shown in Figures 1,2,3 and 6 consist of 10,000 atoms. It is worth noting that a bigger model composed of 100,000 atoms showed quantitatively the same results as the 10,000-atom model (Supplementary Figure S18). Ten different as-quenched models were prepared and then 10 independent thermal-pressure loading simulations were conducted to reduce the statistical errors of the data, which are due to the finite model size. Temperature and pressure during quench, anneal and heat process are controlled by the isothermal–isobaric ensemble.34–36
Models for uniaxial tensile simulations shown in Figure 5 consist of 1,280,000 atoms by organising 10,000-atom unit models (‘As-quench’, ‘Pressure-promoted thermal rejuvenation’ and ‘Pure thermal rejuvenation’ ) in an 8×1×16 array (x, y, z directions, respectively). The as-quenched unit model was constructed via melt-quenching from 3,000 to 0 K at a relatively slow cooling rate of 0.01 K/ps. The pressure-promoted thermal rejuvenation and pure thermal rejuvenation unit models were constructed via the thermal-pressure loading process of Pa=21 GPa and Pa=0 GPa, respectively, with Ta=1.3Tg(Pa). In case of Pa=0 GPa, thermal rejuvenation was realised by the relatively fast cooling rate of the final quenching process (G→H) 0.20 K/ps, whereas in case of Pa=21 GPa, the cooling rate of the final quenching process (G→H) is set to 0.01 K/ps, which is the same as that of the as-quenched unit model, and thus in this cooling rate condition the pressure application is necessary for rejuvenation. The assembled 1,280,000-atom simulation models were heated from 0 to 300 K at a rate of 1.0 K/ps and then relaxed at 300 K for 1.0 ns under full (i.e., x, y and z) periodic boundary and additionally relaxed at 300 K for 100 ps with partial periodic boundary condition only in y and z (free surface boundary in x). Using this model, we conducted uniaxial tensile simulations. Note that after the relaxation processes both the 1,280,000-atom simulation models, i.e., pressure-promoted thermal rejuvenation model and pure thermal rejuvenation model, had higher-energy states than the as-quenched model by 9.6 and 10.6 J/g, respectively. Energy reductions in the relaxation process for totally 1.1 ns were <1.0 J/g, implying that rejuvenated states are maintained during the deformation tests for 2 ns after the relaxation process.
Diffusivity D is calculated from the mean-square displacement of the atoms. α-Relaxation time τα is defined by the time needed for the self-intermediate scattering function at first peak of structural factor decays to 1/e.30
Struik, L. C. E. Physical Aging in Amorphous Polymers and Other Materials. (Elsevier, Houston, TX, USA, 1978).
Wakeda, M., Saida, J., Li, J. & Ogata, S. Controlled rejuvenation of amorphous metals with thermal processing. Sci. Rep. 5, 10545 (2015).
Meng, F., Tsuchiya, K., Ii, S. & Yokoyama, Y. Reversible transition of deformation mode by structural rejuvenation and relaxation in bulk metallic glass. Appl. Phys. Lett. 101, 121914 (2012).
Ketov, S. V. et al. Rejuvenation of metallic glasses by non-affine thermal strain. Nature 524, 200–203 (2015).
Concustell, A., Méar, F. O., Surinach, S., Baró, M. D. & Greer, A. L. Structural relaxation and rejuvenation in a metallic glass induced by shot-peening. Philos. Mag. Lett. 89, 831–840 (2009).
Saida, J., Yamada, R. & Wakeda, M. Recovery of less relaxed state in Zr-Al-Ni-Cu bulk metallic glass annealed above glass transition temperature. Appl. Phys. Lett. 103, 221910 (2013).
Adachi, N., Todaka, Y., Yokoyama, Y. & Umemoto, M. Improving the mechanical properties of Zr-based bulk metallic glass by controlling the activation energy for β-relaxation through plastic deformation. Appl. Phys. Lett. 105, 131910 (2014).
Kumar, G., Prades-Rodel, S., Blatter, A. & Schroers, J . Unusual brittle behavior of Pd-based bulk metallic glass. Scr. Mater. 65, 585–587 (2011).
Xi, X. K. et al. Fracture of brittle metallic glasses: brittleness or plasticity. Phys. Rev. Lett. 94, 125510 (2005).
Kumar, G., Rector, D., Conner, R. D. & Schroers, J. Embrittlement of Zr-based bulk metallic glasses. Acta Mater. 57, 3572–3583 (2009).
Kumar, G., Hong, X. T. & Schroers, J. Nanomoulding with amorphous metals. Nature 457, 868–872 (2009).
Wang, W. H. et al. Effect of pressure on nucleation and growth in the Zr46.75Ti8.25Cu7.5Ni10Be27.5 bulk glass-forming alloy investigated using in situ x-ray diffraction. Phys. Rev. B 68, 184105 (2003).
Cheng, Y. Q., Ma, E. & Sheng, H. W. Atomic level structure in multicomponent bulk metallic glass. Phys. Rev. Lett. 102, 245501 (2009).
Fujita, T. et al. Coupling between chemical and dynamic heterogeneities in a multicomponent bulk metallic glass. Phys. Rev. B 81, 140204 (2010).
Mendelev, M. I. et al. Development of suitable interatomic potentials for simulation of liquid and amorphous Cu-Zr alloys. Philos. Mag. 89, 967–987 (2009).
Kobayashi, S., Maeda, K. & Takeuchi, S. Computer simulation of deformation of amorphous Cu57Zr43 . Acta Metall. 28, 1641–1652 (1980).
Sheng, H. W., Cheng, Y. Q., Lee, P. L., Shastri, S. D. & Ma, E. Atomic packing in multicomponent aluminum-based metallic glasses. Acta Mater. 56, 6264–6272 (2008).
Sheng, H. W., Ma, E. & Kramar, M. J. Relating dynamic properties to atomic structure in metallic glasses. JOM 64, 856–881 (2012).
Ding, J., Cheng, Y. Q., Sheng, H. W. & Ma, E. Short-range structural signature of excess specific heat and fragility of metallic-glass-forming supercooled liquids. Phys. Rev. B 85, 060201 (2012).
Hirata, A. et al. Geometric frustration of icosahedron in metallic glasses. Science 341, 376–379 (2013).
Mendelev, M. I., Srolovitz, D. J., Ackland, G. J. & Han, S. Effect of Fe segregation on the migration of a non-symmetric Σ5 tilt grain boundary in Al. J. Mater. Res. 20, 208–218 (2005).
Wang, Z. T., Pan, J., Li, Y. & Schuh, C. A. Densification and strain hardening of a metallic glass under tension at room temperature. Phys. Rev. Lett. 111, 135504 (2013).
Frank, F. C. Supercooling of liquids. Proc. R. Soc. Lond. A Math. Phys. Sci. 215, 43–46 (1952).
Wakeda, M. & Shibutani, Y. Icosahedral clustering with medium-range order and local elastic properties of amorphous metals. Acta Mater. 58, 3963–3969 (2010).
Wakeda, M., Shibutani, Y. & Ogata, S. Atomistic study on medium-range order structures in amorphous metals. J. Soc. Mater. Sci. Japan 64, 156–162 (2015).
Ma, E. Tuning order in disorder. Nat. Mater. 14, 547 (2015).
Wakeda, M., Shibutani, Y., Ogata, S. & Park, J. Relationship between local geometrical factors and mechanical properties for Cu-Zr amorphous alloys. Intermetallics 15, 139–144 (2007).
Argon, A. S. Plastic deformation in metallic glasses. Acta Metall. 27, 47–58 (1979).
Stillinger, F. H. & Weber, T. A. Packing structures and transitions in liquids and solids. Science 225, 983–989 (1984).
Jaiswal, A., Egami, T. & Zhang, Y. Atomic-scale dynamics of a model glass-forming metallic liquid: Dynamical crossover, dynamical decoupling, and dynamical clustering. Phys. Rev. B 91, 134204 (2015).
Debenedetti, P. G. Metastable Liquid: Concepts And Principles. (Princeton Univ. Press, Princeton, NJ, USA, 1996).
Debenedetti, P. G. & Stillinger, F. H. Supercooled liquids and the glass transition. Nature 410, 259–267 (2001).
Kumar, G., Neibecker, P., Liu, Y. H. & Schroers, J. Critical fictive temperature for plasticity in metallic glasses. Nat. Commun. 4, 1536 (2013).
Nosé, S. A molecular dynamics method for simulations in the canonical ensemble. Mol. Phys. 52, 255–268 (1984).
Hoover, W. G. Canonical dynamics: equilibrium phase-space distributions. Phys. Rev. A 31, 1695–1697 (1985).
Parrinello, M. & Rahman, A. Polymorphic transitions in single crystals: a new molecular dynamics method. J. Appl. Phys. 52, 7182–7190 (1981).
Shimizu, F., Ogata, S. & Li, J. Theory of shear banding in metallic glasses and molecular dynamics calculations. Mater. Trans. 48, 2923–2927 (2007).
This work is supported by the following funding awards: Grants-in-Aid for Scientific Research in Innovative Area (no. 22102003), Scientific Research (A) (no. 23246025), Challenging Exploratory Research (no. 25630013) and the Elements Strategy Initiative for Structural Materials (ESISM).
The authors declare no conflict of interest.
About this article
Cite this article
Miyazaki, N., Wakeda, M., Wang, YJ. et al. Prediction of pressure-promoted thermal rejuvenation in metallic glasses. npj Comput Mater 2, 16013 (2016). https://doi.org/10.1038/npjcompumats.2016.13
High-pressure annealing driven nanocrystal formation in Zr50Cu40Al10 metallic glass and strength increase
Communications Materials (2020)
Breakdown of One-to-One Correspondence in Energy and Volume in a High-Pressure Heat-Treated Zr-Based Metallic Glass During Annealing
Scientific Reports (2020)
Dynamic probing of structural evolution for Co50Ni50 metallic glass during pressurized cooling using atomistic simulation
Journal of Molecular Modeling (2020)
Unveiling a new type of ultradense anomalous metallic glass with improved strength and ductility through a high-pressure heat treatment
NPG Asia Materials (2019)
Journal of Iron and Steel Research International (2018)