Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Induced superconductivity in the quantum spin Hall edge


Topological insulators are a newly discovered phase of matter characterized by gapped bulk states surrounded by conducting boundary states1,2,3. Since their theoretical discovery, these materials have encouraged intense efforts to study their properties and capabilities. Among the most striking results of this activity are proposals to engineer a new variety of superconductor at the surfaces of topological insulators4,5. These topological superconductors would be capable of supporting localized Majorana fermions, particles whose braiding properties have been proposed as the basis of a fault-tolerant quantum computer6. Despite the clear theoretical motivation, a conclusive realization of topological superconductivity remains an outstanding experimental goal. Here we present measurements of superconductivity induced in two-dimensional HgTe/HgCdTe quantum wells, a material that becomes a quantum spin Hall insulator when the well width exceeds dC = 6.3 nm (ref. 7). In wells that are 7.5 nm wide, we find that supercurrents are confined to the one-dimensional sample edges as the bulk density is depleted. However, when the well width is decreased to 4.5 nm the edge supercurrents cannot be distinguished from those in the bulk. Our results provide evidence for supercurrents induced in the helical edges of the quantum spin Hall effect, establishing this system as a promising avenue towards topological superconductivity. In addition to directly confirming the existence of the topological edge channels, our results also provide a measurement of their widths, which range from 180 nm to 408 nm.


Topological superconductors, like topological insulators, possess a bulk energy gap and gapless surface states. In a topological superconductor, the surface states are predicted to manifest as zero-energy Majorana fermions, fractionalized modes that pair to form conventional fermions. Owing to their non-Abelian braiding statistics, achieving control of these Majorana modes is desirable both fundamentally and for applications to quantum information processing. Proposals towards realizing Majorana fermions have focused on their emergence within fractional quantum Hall states8 and spinless p + ip superconductors9, and on their direct engineering using s-wave superconductors combined with topological insulators or semiconductors10,11. Particularly appealing are implementations in one-dimensional (1D) systems, where restriction to a single spin degree of freedom combined with proximity to an s-wave superconductor would provide the basis for topological superconductivity12. Effort in this direction has been advanced by studies of nanowire systems13,14,15,16,17,18 and by excess current measurements on InAs/GaSb devices19.

An attractive route towards a 1D topological superconductor originates from the 2D quantum spin Hall (QSH) insulator. This topological phase of matter was recently predicted20,21 and observed22,23 in transport measurements of HgTe/HgCdTe quantum wells thicker than a critical thickness dC = 6.3 nm. Due to strong spin–orbit coupling the bulk bands of the system invert, crossing only at the edges of the system to form 1D counterpropagating helical modes. Time-reversal symmetry ensures protection of these modes against elastic backscattering over distances shorter than the coherence length24. The helical nature of the edge modes makes them a particularly appealing path towards topological superconductivity, owing to the intrinsic elimination of their spin degree of freedom. Here we report measurements of supercurrents induced in HgTe/HgCdTe quantum well heterostructures. As the system enters the QSH regime we find that these supercurrents become confined to the topological edge modes, verifying their existence and providing a microscopic picture of the QSH state.

Our approach consists of a two-terminal Josephson junction, with a rectangular section of quantum well located between two superconducting leads (Fig. 1). At a given bulk carrier density, the presence or absence of helical edge channels influences the supercurrent density profile across the width of the junction. In the simplest case the supercurrent density is uniform throughout the device, and edge channels are indistinguishable from bulk channels (Fig. 1a). This behaviour would be expected for a non-topological junction (quantum well width smaller than dC), or in a topological junction (quantum well width larger than dC) far from the bulk insulating regime.

Figure 1: Expected two-terminal behaviour in different regimes of a topological quantum well.
figure 1

a, When the bulk of a sample is filled with charge carriers, supercurrent can flow uniformly across the junction, corresponding to a flat supercurrent density JS(x). A perpendicular magnetic field B modulates the maximum critical current ICmax, resulting in a single-slit Fraunhofer interference pattern. b, As the bulk carriers are depleted, the supercurrent density develops peaks owing to the presence of the helical edges. This evolution towards edge-dominated transport appears in the interference pattern as a narrowing central lobe width and more pronounced side-lobe amplitudes. c, When no bulk carriers remain, the supercurrent is carried only along the helical edges. In this regime the interference results in a sinusoidal double-slit pattern, with an overall decay in B that is determined by the width of the edge channels.

In a topological junction, decreasing the bulk carrier density brings the device closer to the QSH insulator regime (Fig. 1b). Scanning superconducting quantum interference device (SQUID) measurements suggest that over a range of bulk densities the QSH edge channels coexist with bulk states, and can carry considerably more edge current than would be expected for a non-topological conductor25. In the two-terminal configuration, this helical edge contribution appears as peaks in the supercurrent density at each edge. When the bulk density becomes sufficiently low, these edge peaks are the only features in the supercurrent density (Fig. 1c). Then the supercurrent is carried solely along the helical edges, and the system is in the regime of the quantum spin Hall superconductor.

Placing such a Josephson junction in a perpendicular magnetic field B provides a way to measure the supercurrent density in the quantum well. In general, the maximum supercurrent that can flow through a Josephson junction is periodically modulated by a magnetic field. Typically, the period of the modulation corresponds to the magnetic flux quantum Φ0 = h/2e. In our junctions this period matches the area of the HgTe region plus half the area occupied by each contact, a result of the Meissner effect. The particular shape of the critical current interference pattern depends on the phase-sensitive summation of the supercurrents traversing the junction26. In the case of a symmetric supercurrent distribution, this integral takes the simple form:

Here LJ is the length of the junction along the direction of current, accounting for the magnetic flux focusing from the contacts.

It is evident that different supercurrent densities JS(x) in the junction can give rise to different interference patterns ICmax(B). The flat supercurrent density of a trivial conductor corresponds to a single-slit Fraunhofer pattern |(sin(πLJBW/Φ0))/(πLJBW/Φ0)|, characterized by a central lobe width of 2Φ0 and side lobes decaying with 1/B dependence (Fig. 1a). As helical edges emerge, this single-slit interference evolves towards the more sinusoidal oscillation characteristic of a SQUID (Fig. 1b). The central lobe width shrinks to Φ0 when only edge supercurrents remain, with the side lobe decay determined by the widths of the edge channels (Fig. 1c). Measuring the dependence of ICmax on B therefore provides a convenient way to measure the distribution of supercurrent in a junction. To quantitatively extract JS(x) from the measured quantity ICmax(B) we follow an approach where non-zero ICmax(B) minima are ascribed to an asymmetric supercurrent distribution27. Although other effects may lead to non-zero minima in ICmax(B), we consider here only the possibility of an odd component in JS(x). Full details of the extraction procedure can be found in the Supplementary Information.

To study how supercurrents flow in the QSH regime, we measure a Josephson junction consisting of a 7.5-nm-wide quantum well contacted by titanium/aluminium leads28. Our contact lengths are each 1 μm, and the contact separation is 800 nm. The junction width of 4 μm is defined by etched mesa edges. A voltage VG applied to a global top gate allows us to tune the carrier density in the junction. At each value of VG and B, the critical current ICmax is determined by increasing the current through the junction while monitoring the voltage across the leads. The behaviour observed in this device is reproducible in several other similar junctions, as reported in the Supplementary Information.

As a function of the top-gate voltage, the overall behaviour of the junction evolves between two extremes. At more positive gate voltage and higher bulk density, the critical current envelope strongly resembles a single-slit pattern (Fig. 2a). This type of interference suggests a nearly uniform supercurrent density throughout the sample, confirmed by transformation to the JS(x) picture (Fig. 2b). This nearly flat distribution indicates that the quantum well is in the high carrier density regime of an essentially trivial conductor.

Figure 2: General behaviour observed in the topological Josephson junction.
figure 2

a, A map of the differential resistance across the junction, measured with the top gate at VG = 1.05 V, shows the single-slit interference characteristic of a uniform supercurrent density. b, The supercurrent density, extracted for VG = 1.05 V, is consistent with trivial charge transport throughout the bulk of the junction. c, When the top-gate voltage is lowered to VG = −0.425 V, the differential resistance shows a more sinusoidal interference pattern. d, Using the interference envelope measured at VG = −0.425 V, the supercurrent density is clearly dominated by the contribution from the edges. In this regime almost no supercurrent passes through the bulk.

At more negative gate voltage and lower bulk density, the critical current envelope becomes close to a sinusoidal oscillation (Fig. 2c). The shift towards a SQUID-like interference pattern corresponds to the development of sharp peaks in supercurrent density at the mesa edges (Fig. 2d).

We can track this evolution in a single device by measuring the critical current envelope at a series of gate voltages. As the top gate is varied from VG = 1.05 V to VG = −0.45 V, the maximum critical current decreases from 505 nA to 5.7 nA. At the same time, the overall critical current behaviour shows a narrowing of the central interference lobe, from 2Φ0 at positive gate voltages to Φ0 at negative gate voltages (Fig. 3a, b). The side lobes additionally become continuously more pronounced, indicating the confinement of supercurrent to channels at the edges of the junction (Fig. 3c, d). The normal resistance, measured at large bias to overcome superconductivity, increases from 160 Ω to 3,000 Ω over the range of this transition (Fig. 3e). Although it is possible to gate further towards depletion, the critical currents become too small to reliably measure and no meaningful supercurrent density can be extracted.

Figure 3: Continuous evolution with gating in the topological Josephson junction.
figure 3

a, As the top gate is varied from VG = 1.05 V to VG = −0.45 V, the maximum critical current decreases from 505 nA to 5.7 nA. b, Normalizing the interference patterns to their peak values reveals the evolution towards sinusoidal interference. c, Using the envelope at each gate voltage, the evolution of the supercurrent density can be visualized. d, By normalizing each supercurrent density to its maximum value, the transition from trivial to edge-dominated supercurrent transport can be clearly seen. e, This transition occurs as the normal device resistance increases from 160 Ω to 3,000 Ω. f, At the most negative gate voltage, VG = −0.45 V, the supercurrent density provides a measurement of the edge widths.

At the most negative gate voltage, VG = −0.45 V, we can estimate the widths of the supercurrent-carrying edge channels using a Gaussian line shape (Fig. 3f). Using this method, we find widths of 408 nm and 319 nm for the two edges. Our measurements of edge widths in another device with similar dimensions, as well as one with a 2 μm mesa width, show edges as narrow as 180 nm (Supplementary Information). These width variations, as well as the normal-state resistance that is low compared with the resistance h/2e2 for two ballistic 1D channels, suggest the presence of additional edge modes or of bulk modes coupled too weakly across the junction to carry supercurrent.

To provide further evidence that the observed edge supercurrents are topological in nature, we next turn to a heterostructure with a quantum well width of 4.5 nm. In this device, the well width is smaller than the critical width dC, so that the sample is not expected to enter the QSH regime. Near zero top-gate voltage and a normal resistance of 270 Ω, the critical current interference pattern has a maximum of 243 nA and resembles a single-slit envelope (Fig. 4a, b). On energizing the top gate and decreasing the bulk density, the single-slit pattern persists. In contrast to the wide well sample, this behaviour corresponds to a supercurrent density that remains distributed throughout the junction even as the normal resistance rises to several kΩ (Fig. 4c–f). As the edge supercurrents are present only when the well width is larger than dC, we conclude that our observations provide evidence for induced superconductivity in the helical QSH edge states.

Figure 4: Continuous evolution with gating in the non-topological Josephson junction.
figure 4

a, As the top gate is varied from VG = 0 V to VG = −1.5 V, the maximum critical current decreases from 243 nA to 4.4 nA. b, Normalizing the interference patterns to their peak values shows the stability of the single-slit pattern over a wide range of gating. c, Using the envelope at each gate voltage, the evolution of the supercurrent density can be visualized. d, Normalizing each supercurrent density to its maximum value shows that the supercurrent remains distributed throughout the device. e, This roughly uniform supercurrent distribution remains even as the device resistance increases from 215 Ω to almost 2,500 Ω. f, A line trace of the supercurrent density close to depletion further demonstrates that the supercurrent flows throughout the device.

By studying Fraunhofer interference, our measurements provide detailed information about the supercurrent distribution in HgTe quantum wells. In the quantum spin Hall regime, this interferometry confirms the existence of topological edge channels associated with the quantum spin Hall insulating state. Our observed supercurrent distributions additionally provide the first direct measurements of the helical edges’ spatial extent. In general, our application of this Fourier imaging technique to HgTe quantum wells could be widely adopted as a method to elucidate the microscopic structure of topological materials. In our devices, the observation of Josephson supercurrents through the helical edge channels establishes the HgTe/HgCdTe system as a platform in which to pursue topological superconductivity and Majorana bound states, whether through following existing theoretical proposals or those yet to be formulated29,30,31.


  1. Hasan, M. Z. & Kane, C. L. Colloquium: Topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).

    ADS  Article  Google Scholar 

  2. Qi, X-L. & Zhang, S-C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).

    ADS  Article  Google Scholar 

  3. Kane, C. L. & Mele, E. J. Z2 topological order and the quantum spin Hall effect. Phys. Rev. Lett. 95, 146802 (2005).

    ADS  Article  Google Scholar 

  4. Fu, L. & Kane, C. L. Superconducting proximity effect and majorana fermions at the surface of a topological insulator. Phys. Rev. Lett. 100, 096407 (2008).

    ADS  Article  Google Scholar 

  5. Fu, L. & Kane, C. L. Josephson current and noise at a superconductor/quantum-spin-Hall-insulator/superconductor junction. Phys. Rev. B 79, 161408 (2009).

    ADS  Article  Google Scholar 

  6. Nayak, C. et al. Non-abelian anyons and topological quantum computation. Rev. Mod. Phys. 80, 1083–1159 (2008).

    ADS  MathSciNet  Article  Google Scholar 

  7. Konig, M. et al. The quantum spin Hall effect: Theory and experiment. J. Phys. Soc. Jpn 77, 031007 (2008).

    ADS  Article  Google Scholar 

  8. Moore, G. & Read, N. Nonabelions in the fractional quantum Hall effect. Nucl. Phys. B 360, 362–396 (1991).

    ADS  MathSciNet  Article  Google Scholar 

  9. Read, N. & Green, D. Paired states of fermions in two dimensions with breaking of parity and time-reversal symmetries and the fractional quantum Hall effect. Phys. Rev. B 61, 10267–10297 (2000).

    ADS  Article  Google Scholar 

  10. Sau, J. D., Lutchyn, R. M., Tewari, S. & Sarma, S. D. Generic new platform for topological quantum computation using semiconductor heterostructures. Phys. Rev. Lett. 104, 040502 (2010).

    ADS  Article  Google Scholar 

  11. Alicea, J. Majorana fermions in a tunable semiconductor device. Phys. Rev. B 81, 125318 (2010).

    ADS  Article  Google Scholar 

  12. Kitaev, A. Y. Unpaired majorana fermions in quantum wires. Phys.-Usp. 44, 131–136 (2001).

    ADS  Article  Google Scholar 

  13. Mourik, V. et al. Signatures of majorana fermions in hybrid superconductor–semiconductor nanowire devices. Science 336, 1003–1007 (2012).

    ADS  Article  Google Scholar 

  14. Das, A. et al. Zero-bias peaks and splitting in Al–InAs nanowire topological superconductor as a signature of majorana fermions. Nature Phys. 8, 887–895 (2012).

    ADS  Article  Google Scholar 

  15. Rokhinson, L. P., Liu, X. & Furdyna, J. K. The fractional a.c. Josephson effect in a semiconductor–superconductor nanowire as a signature of majorana particles. Nature Phys. 8, 795–799 (2012).

    ADS  Article  Google Scholar 

  16. Lee, E. J. H. et al. Zero-bias anomaly in a nanowire quantum dot coupled to superconductors. Phys. Rev. Lett. 109, 186802 (2012).

    ADS  Article  Google Scholar 

  17. Churchill, H. O. H. et al. Superconductor-nanowire devices from tunneling to the multichannel regime: Zero-bias oscillations and magnetoconductance crossover. Phys. Rev. B 87, 241401(R) (2013).

    ADS  Article  Google Scholar 

  18. Finck, A. D. K. et al. Anomalous modulation of a zero-bias peak in a hybrid nanowire-superconductor device. Phys. Rev. Lett. 110, 126406 (2013).

    ADS  Article  Google Scholar 

  19. Knez, I., Du, R-R. & Sullivan, G. Andreev reflection of helical edge modes in InAs/GaSb quantum spin Hall insulator. Phys. Rev. Lett. 109, 186603 (2012).

    ADS  Article  Google Scholar 

  20. Bernevig, B. A. & Zhang, S-C. Quantum spin Hall effect. Phys. Rev. Lett. 96, 106802 (2006).

    ADS  Article  Google Scholar 

  21. Bernevig, B. A., Zhang, S-C. & Hughes, T. L. Quantum spin Hall effect and topological phase transition in HgTe quantum wells. Science 314, 1757–1761 (2006).

    ADS  Article  Google Scholar 

  22. Konig, M. et al. Quantum spin Hall insulator state in HgTe quantum wells. Science 318, 766–770 (2007).

    ADS  Article  Google Scholar 

  23. Roth, A. et al. Nonlocal transport in the quantum spin Hall state. Science 325, 294–297 (2009).

    ADS  Article  Google Scholar 

  24. Schmidt, T. L., Rachel, S., Oppen, F. v. & Glazman, L. I. Inelastic electron backscattering in a generic helical edge channel. Phys. Rev. Lett. 108, 156402 (2012).

    ADS  Article  Google Scholar 

  25. Nowack, K. C. et al. Imaging currents in HgTe quantum wells in the quantum spin Hall regime. Nature Mater. 12, 787–791 (2013).

    ADS  Article  Google Scholar 

  26. Tinkham, M. Introduction to Superconductivity (Dover Publications Inc., 2004).

    Google Scholar 

  27. Dynes, R. C. & Fulton, T. A. Supercurrent density distribution in Josephson junctions. Phys. Rev. B 3, 3015–3023 (1971).

    ADS  Article  Google Scholar 

  28. Oostinga, J. B. et al. Josephson supercurrent through the topological surface states of strained bulk HgTe. Phys. Rev. X 3, 021007 (2013).

    Google Scholar 

  29. Sau, J. D. et al. Non-abelian quantum order in spin–orbit coupled semiconductors: Search for topological majorana particles in solid-state systems. Phys. Rev. B 82, 214509 (2010).

    ADS  Article  Google Scholar 

  30. Jiang, L. et al. Unconventional Josephson signatures of majorana bound states. Phys. Rev. Lett. 107, 236401 (2011).

    ADS  Article  Google Scholar 

  31. Mi, S. et al. Proposal for the detection and braiding of majorana fermions in a quantum spin Hall insulator. Phys. Rev. B 87, 241405(R) (2013).

    ADS  Article  Google Scholar 

Download references


We acknowledge A. Akhmerov and J. D. Sau for theoretical discussions. We acknowledge financial support from Microsoft Corporation Project Q, the NSF DMR-1206016, the STC Center for Integrated Quantum Materials, NSF Grant No. DMR-1231319, the DOE SCGF Program, the German Research Foundation (DFG-JST joint research programme ‘Topological Electronics’), and EU ERC-AG programme (project 3-TOP).

Author information

Authors and Affiliations



All authors contributed collaboratively to all aspects of the work. Device fabrication, measurements, data analysis and manuscript preparation were carried out at Harvard by S.H., H.R., T.W. and A.Y. All authors contributed to development of the fabrication process. P.L., M.M., C.B., H.B. and L.W.M. carried out the molecular beam epitaxy at Würzburg.

Corresponding author

Correspondence to Amir Yacoby.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Information (PDF 1421 kb)

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hart, S., Ren, H., Wagner, T. et al. Induced superconductivity in the quantum spin Hall edge. Nature Phys 10, 638–643 (2014).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing