Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Disorder in quantum critical superconductors


In four classes of materials—the layered copper oxides, organics, iron pnictides and heavy-fermion compounds—an unconventional superconducting state emerges as a magnetic transition is tuned towards absolute zero temperature, that is, towards a magnetic quantum critical point1 (QCP). In most materials, the QCP is accessed by chemical substitution or applied pressure. CeCoIn5 is one of the few materials that are ‘born’ as a quantum critical superconductor2,3,4 and, therefore, offers the opportunity to explore the consequences of chemical disorder. Cadmium-doped crystals of CeCoIn5 are a particularly interesting case where Cd substitution induces long-range magnetic order5, as in Zn-doped copper oxides6,7. Applied pressure globally suppresses the Cd-induced magnetic order and restores bulk superconductivity. Here we show, however, that local magnetic correlations, whose spatial extent decreases with applied pressure, persist at the extrapolated QCP. The residual droplets of impurity-induced magnetic moments prevent the reappearance of conventional signatures of quantum criticality, but induce a heterogeneous electronic state. These discoveries show that spin droplets can be a source of electronic heterogeneity and emphasize the need for caution when interpreting the effects of tuning a correlated system by chemical substitution.


Impurities, defects in an otherwise homogeneous host, often are unwanted because their influence can mask intrinsic properties of the host material8. Impurities, however, also can be a double-edged sword by providing an avenue to induce interesting new phases of matter and to probe the underlying mechanism of exotic ground states, especially those that emerge from complex interactions in strongly correlated electron materials. In the high-transition-temperature (Tc) copper oxide superconductors, the intentional inclusion of small concentrations of non-magnetic impurities, such as Zn, induces magnetism around the impurity site and also enables visualization of the symmetry of the superconducting gap6,7,9,10. Nucleation of a charge density wave in regions surrounding impurity sites is another example of defects revealing the underlying competing phase by disorder11. With a growing number of classes of materials that show unusual sensitivity to impurities, understanding and controlling the emergent phases from impurities is an important open issue.

Materials that exhibit an extreme sensitivity to impurities often are near a zero-temperature, second-order phase transition, where quantum critical fluctuations of the associated order parameter diverge in space and time. Theory predicts that when disorder is coupled to these critical fluctuations local regions of an exotic phase can nucleate inside the host and change the nature of the phase transition; indeed, even long-range order of the nucleated phase is possible12,13,14. Nuclear magnetic resonance and scanning tunnelling microscopy have validated these predictions by showing that the host system locally responds to an impurity by creating an extended droplet of the new phase around an impurity6,15. Understanding how the local droplet evolves as a function of a control parameter or how the droplet interplays with the host phase, however, is less well known, partly owing to a lack of very pure compounds that are situated sufficiently close to a QCP. The quantum critical superconductor CeCoIn5 provides an ideal opportunity to probe the consequences of impurities on fluctuations of a quantum critical state. It forms readily as exceptionally high-quality single crystals, and the small (1 meV) characteristic energy of its ground state can be tuned easily with modest applied pressure or magnetic field without introducing additional disorder16,17,18. At ambient pressure, the quantum critical state of CeCoIn5, characterized by a linear-in-temperature electrical resistivity above Tc (ref. 3) and logarithmic divergence of the low-temperature electronic specific heat divided by temperature (C/T) (ref. 19), has been interpreted as being due to proximity to a field-induced magnetic QCP (refs 16, 20). Replacing one atomic per cent of In by Cd in CeCo(In1−xCdx)5 reduces Tc from 2.3 K (x = 0) to Tc = 1.2 K (x = 0.01) and induces microscopic coexistence of long-range antiferromagnetic order with TN = 2.8 K (refs 5, 21). For slightly larger x, superconductivity is suppressed completely and only Néel order remains. Introducing these Cd atoms into CeCoIn5 creates defects that produce a response consistent with theoretical expectations12,13,14.

Application of pressure accurately reverses the global effect of Cd substitutions, suppressing the long-range magnetic order and inducing a dome of superconductivity5. The fact that the global phase response of CeCoIn5 to cadmium doping can be undone by applied pressure suggests that a quantum critical state should reappear, but the critical point may be hidden by the pressure-induced superconducting state of Cd-doped crystals. This is precisely what is found in the isostructural compound CeRhIn5, which orders antiferromagnetically at atmospheric pressure in the absence of intentionally added impurities. Applying pressure to this correlated electron metal suppresses its long-range antiferromagnetism and induces a dome of bulk superconductivity that hides a QCP that is revealed in an applied magnetic field17,18. The pressure evolution of C/T in zero-field is shown in Fig. 1a as a function of temperature for CeCoIn5 doped with 1% Cd. Similar results are found for a sample doped with 1.5% Cd (see Supplementary Fig. 1). For comparison, we also plot the pressure dependence of C/T of the pristine reference compound CeRhIn5 in Fig. 1b. With applied pressure, TN is suppressed in both CeRhIn5 and Cd-doped CeCoIn5 compounds, and Tc increases. In contrast to CeRhIn5, however, the discontinuity ΔC = CCN, where CN is the normal-state specific heat at Tc, normalized by CN, ΔC/CN≈1.2 at Tc for Cd-doped CeCoIn5 at P = 1.21 GPa. This normalized discontinuity is less than 30% of the corresponding value in CeRhIn5 at 2.05 GPa or in pure CeCoIn5 at ambient pressure where these materials have nearly identical Tc values.

Figure 1: Pressure dependence of the specific heat of 1% Cd-doped CeCoIn5 and CeRhIn5.
figure 1

a, Specific heat divided by temperature for 1% Cd-doped CeCoIn5 in zero applied field and at pressures of 0.25 (black symbols), 0.60 (red), 0.98 (blue) and 1.21 GPa (orange). b, Specific heat divided by temperature for CeRhIn5 at 1.15 (black), 1.51 (red), 1.71 (blue) and 2.05 GPa (orange). In CeRhIn5, the spin entropy of Ce 4f local moments is transferred completely to the superconducting phase when magnetism is suppressed, resulting in a large ΔC/CN>4 at Tc (ref. 18). The qualitative difference between CeRhIn5 and Cd-doped CeCoIn5 exists even though the ordered magnetic moment in both is comparable, 0.7 μB. cf, Dependence on temperature of the specific heat divided by temperature of 1% Cd-doped CeCoIn5 under magnetic fields and pressures. c, 0.25 GPa at magnetic fields of 0 (black), 1.0 (red), 3.0 (green), 5.0 (blue) and 9.0 T (orange). d, 0.6 GPa at magnetic fields of 0 (black), 1.0 (red), 3.0 (blue) and 5.0 T (orange). e, 0.98 GPa at magnetic fields of 0 (black), 2.0 (red), 4.0 (green), 5.0 (blue) and 5.5 T (orange). f, 1.54 GPa at magnetic fields of 0 (black), 3.0 (red), 4.0 (green), 5.0 (blue) and 6.0 T (orange). Solid and dashed arrows indicate superconducting and antiferromagnetic transition temperatures, respectively. Values of C/T for different pressures were normalized against each other with an assumption that the entropy recovered at 10 K is the same for all pressures within each compound. This assumption is proved for Cd-doped CeCoIn5 as a function of Cd content at atmospheric pressure5.

The effect of a magnetic field on the specific heat of the 1% Cd-doped CeCoIn5 is summarized in Fig. 1c–f for pressures up to 1.54 GPa. For magnetic fields above the critical field Bc2, where superconductivity is completely destroyed, C/T at low temperatures decreases with decreasing temperature typical of a non-critical metal. At 0.98 GPa and 6.2 T, which is just above the upper critical field Bc2 at this pressure, there is a slight upturn in C/T at the lowest temperatures. This weak upturn, however, is distinct from undoped CeCoIn5, where C/T logarithmically diverges with decreasing temperature near Bc2 (ref. 16) and from CeRhIn5 at its quantum critical pressure, where C/T also diverges once superconductivity is suppressed by a magnetic field18. The prominent lack of a divergence in C/T of the Cd-doped compound indicates that quantum critical behaviour is avoided.

Supporting this lack of quantum criticality from specific heat measurements, the electrical resistivity ρ of 1% Cd-doped CeCoIn5 also does not show an anomalous temperature dependence characteristic of proximity to a QCP. Isothermal cuts of the low-temperature electrical resistivity as a function of pressure (Fig. 2a) show that ρ(P) decreases monotonically for TTc across the critical pressure Pc1( = 0.5 GPa), where TN becomes equal to Tc, and Pc2( = 1.0 GPa), the extrapolated critical point where TN extrapolates to 0 K inside the superconducting dome. Further, Fig. 2c shows a linear- T resistivity over a temperature range between 12 and 35 K at 1.89 GPa, but it becomes sub-linear in T at lower temperatures, in contrast to expectations of quantum criticality and the T-linear ρ(T) in pristine CeCoIn5 that extends to Tc (ref. 3). This sub-linear temperature dependence of the resistivity demonstrates that the spectrum of spin excitations has changed with doping such that the scattering rate below T* is reduced relative to a continuation of the T-linear resistivity to lower temperatures, a reduction in scattering arising from possible short-range magnetic correlations.

Figure 2: Electrical resistivity of 1% Cd-doped CeCoIn5 under pressure.
figure 2

a, Contour map of the electrical resistivity (ρa b) within the Ce–In plane plotted in the pressure–temperature plane. Tmax is a temperature where the resistivity reaches a maximum, and T* is the temperature below which the resistivity deviates from a T-linear dependence. An antiferromagnetic state coexists with superconductivity for P<0.5 GPa. b, In-plane resistivity ρa b as a function of temperature on a semi-logarithmic scale for representative pressures. Arrows mark the evolution of Tmax with pressure. The temperature Tmax at which ρ(T) is a maximum occurs at 34 K at ambient pressure and increases linearly with increasing pressure, which is typical of strongly correlated Ce-based materials, such as pure CeCoIn5, and reflects a pressure-induced increase of the hybridization between ligand electrons and the periodic array of Ce 4f-electrons. c, Resistivity, with the residual T = 0 value subtracted, divided by temperature, plotted against temperature for representative pressures. T* is marked by arrows.

The large jump in specific heat at Tc in pure CeCoIn5 and in CeRhIn5 at its pressure-tuned QCP is a consequence of the huge quantum disordered entropy of magnetic fluctuations that is recovered in the zero-temperature limit when superconductivity is suppressed by a magnetic field. In contrast, the specific heat jump in Cd-doped CeCoIn5 is smaller, even when these crystals are tuned to their putative critical point. This small jump, together with the absence of a signature for a diverging specific heat in a magnetic field and T-linear ρ(T) to Tc, indicates that the spectrum of magnetic fluctuations has changed in response to the presence of Cd impurities. When very dilute concentrations of non-magnetic impurities are added to CeCoIn5, a resonance in the electronic density of states develops from unitary scattering of the highly correlated band of conduction electrons by the local defect22. In this process, the non-magnetic defect acquires the magnetic character of a spin S = 1/2 Kondo impurity. At higher concentrations, local droplets of static magnetic order nucleate with a typical extent of a few lattice parameters21, and when these droplets overlap, long-range antiferromagnetic order develops. Although magnetic fluctuations may be suppressed locally through the nucleation of spin droplets around the Cd impurities, they should not be affected significantly at distances removed from these impurities where there is no static magnetism. Apparently, sufficient spectral weight remains in the unaffected fluctuations to produce a superconducting transition only slightly lower than that of pure CeCoIn5.

Figure 3a shows 115In nuclear quadrupolar resonance (NQR) spectra of the In(1) site for CeCoIn5 and 1% Cd-doped CeCoIn5. Three peaks A, B and C are observed in Cd-doped crystals21, where peak A probes the bulk of the unit cells as in pristine CeCoIn5. The existence of B and C peaks underscores the presence of a minority of In sites in an electronic environment not present in undoped CeCoIn5. Cd impurities significantly broaden the In(1) NQR spectra owing to the distribution of local electric field gradients. Figure 3b shows the temperature dependence of the spin-lattice relaxation rate 1/T1 measured at peak A of 1% Cd-doped CeCoIn5 under pressures to 1.51 GPa. At ambient pressure, 1/T1 is identical to the pure compound and follows a T1/4 temperature dependence in the disordered state, which is expected for a system in close proximity to an antiferromagnetic QCP (refs 21, 23). The observation that 1/T1 is a strong function of pressure yet independent of Cd doping provides microscopic evidence that pressure is not the reverse of doping. Taken with the specific heat data, these data imply that the electronic response to Cd doping is strongly inhomogeneous. As pressure tunes the system away from long-range magnetic order, the spin–spin correlation length, ξ, and therefore the size of the droplets, should decrease. In the temperature range around TN (P = 0), this is reflected in a rapid decrease of the relaxation rate 1/T1T ξα (refs 23, 24, 25, 26, 27) that is plotted in Fig. 3b. These NQR results provide microscopic evidence for the existence of spin droplets even when global long-range antiferromagnetic order is suppressed completely for pressures above Pc1.

Figure 3: Spin-lattice relaxation rate of 1% Cd-doped CeCoIn5 under pressure.
figure 3

a115In NQR spectra of the In(1) site at ambient pressure. 115In NQR spectra of CeCoIn5 and 1% Cd-doped CeCoIn5 are shown in the upper and lower parts of the panel. Indium sites in the unit cell of CeCoIn5 are indicated in the inset. In the Cd-doped crystals, additional peaks B and C appear at higher frequencies, and the original peak A is broadened and moved slightly to higher frequency. b, Dependence on temperature of the spin-lattice relaxation rate 1/T1 of CeCo(In0.99Cd0.01)5. Solid lines are guides to the eyes for pressures of 1 bar (black), 0.36 (red), 0.61 (green), 1.04 (blue) and 1.51 GPa (orange). The overall decrease in 1/T1, even at high temperatures, is found in pristine CeCoIn5 (ref. 26). The inset shows 1/T1 at 4 K as a function of pressure. Error bars describe the uncertainty in 1/T1. c, Schematic illustration of the dependence on pressure of the size of magnetic droplets. The Cd atoms that replace In in CeCoIn5 nucleate antiferromagnetic droplets surrounding the Cd site. The average distance between the droplets, which is approximately five lattice spacings at 0.75% Cd doping, is independent of pressure, but their spatial extent shrinks with pressure. For a pressure above Pc1 (the middle panel), the magnetic correlation length becomes shorter than inter-droplet spacing, leading to suppression of the long-ranged antiferromagnetic order. AFM, antiferromagnetic; SC, superconducting.

The nucleation and pressure evolution of spin droplets can be understood within the framework of a theoretical model that considers the competition between antiferromagnetism and d-wave superconductivity13 (details of the model are discussed in Supplementary Information). In the absence of impurities, this model gives negligible spectral weight in the magnetic channel and homogeneous d-wave superconductivity near a QCP. When a unitary scattering impurity is introduced, however, superconductivity is suppressed strongly around the defect but recovers over a distance of a coherence length away from the impurity. Concurrently, magnetic order is depressed at the impurity but is a maximum at the nearest Ce neighbour and decays over many lattice constants. As shown in Supplementary Fig. 4a,b, the superconducting order is robust against a change in effective bandwidth (or the external pressure), but the magnetic order is very sensitive. A slight increase in bandwidth rapidly dampens the long-range oscillatory magnetization and the amplitude of the nearest-neighbour magnetic order parameter. For a dilute concentration of impurity centres or at sufficiently wider bandwidths (higher pressures), there will be only magnetic droplets, but for a narrower bandwidth or higher concentration of scattering centres, magnetic correlations between sites induce global magnetic order. Predictions of this model are illustrated schematically in Fig. 3c.

The lack of signatures for quantum critical behaviour in Cd-doped CeCoIn5 manifests a new mechanism for the coexistence of magnetism and superconductivity and provides a different perspective for interpreting the response to disorder in other strongly correlated superconductors near a zero-temperature magnetic instability. As this work shows, tuning a system with or by disorder to a presumed magnetic QCP does not necessitate a quantum critical response and associated spectrum of quantum fluctuations. Although not all impurities may be unitary scatterers, the likelihood is high that they will be strong scatterers if the bandwidth of the host material is sufficiently narrow, as it is in many strongly correlated heavy-fermion compounds, such as CeCoIn5. The freezing of magnetic quantum fluctuations around impurity sites has broader consequences for the nature of electronic heterogeneity that is common to classes of strongly correlated electron systems.


Single crystals of CeCo(In1−xCdx)5 were synthesized by a standard In-flux technique and their basic physical properties were reported previously5. Electrical resistivity, specific heat and NQR measurements were performed under pressure for samples with Cd concentrations x = 0.01 and 0.015, where the concentration x is determined by microprobe measurements. A quasi-hydrostatic pressure environment was achieved in a Be–Cu/NiCrAl hybrid clamp-type cell with silicone oil as the transmitting medium and pressure in the cell was determined at low temperatures by inductive measurements of a change in the superconducting transition temperature of Sn that was placed inside the cell28. Specific heat measurements were performed by an a.c. calorimetric technique, where the voltage in Au/Fe(0.07%) thermocouple wire, attached to one facet of the crystal, was monitored and converted to a temperature change that is inversely proportional to the specific heat. Details of the a.c. calorimetric technique can be found elsewhere29. A standard four-probe technique was employed to measure the electrical resistivity using an LR700 resistance bridge. The spin-lattice relaxation time 1/T1 at the A site, which is associated with the bulk high-symmetry In(1) sites, was obtained at zero field by measuring the NQR of a single-crystalline sample.


  1. Taillefer, L. Scattering and pairing in cuprate superconductors. Annu. Rev. Condens. Matter Phys. 1, 51–70 (2010).

    ADS  Article  Google Scholar 

  2. Stockert, O. et al. Magnetically driven superconductivity in CeCu2Si2 . Nature Phys. 7, 119–124 (2011).

    ADS  Article  Google Scholar 

  3. Sidorov, V. A. et al. Superconductivity and quantum criticality in CeCoIn5 . Phys. Rev. Lett. 89, 157004 (2002).

    ADS  Article  Google Scholar 

  4. Matsumoto, Y. et al. Quantum criticality without tuning in the mixed valence compound β-YbAlB4 . Science 331, 316–319 (2011).

    ADS  Article  Google Scholar 

  5. Pham, L. D., Park, T., Maquilon, S., Thompson, J. D. & Fisk, Z. Reversible tuning of the heavy-fermion ground state in CeCoIn5 . Phys. Rev. Lett. 97, 056404 (2006).

    ADS  Article  Google Scholar 

  6. Alloul, H., Mendels, P., Casalta, H., Marucco, J. F. & Arabski, J. Correlation between magnetic and superconducting properties of Zn-substituted YBa2Cu3O6+x . Phys. Rev. Lett. 67, 3140–3143 (1991).

    ADS  Article  Google Scholar 

  7. Kimura, H., Kofu, M., Matsumoto, Y. & Hirota, K. Novel in-gap spin state in Zn-doped La1.85Sr0.15CuO4 . Phys. Rev. Lett. 91, 067002 (2003).

    ADS  Article  Google Scholar 

  8. Takagi, S. et al. No evidence for small-moment antiferromagnetism under ambient pressure in URu2Si2: Single-crystal 29Si NMR study. J. Phys. Soc. Jpn 76, 033708 (2007).

    ADS  Article  Google Scholar 

  9. Balatsky, A. V., Vekhter, I. & Zhu, J-X. Impurity-induced states in conventional and unconventional superconductors. Rev. Mod. Phys. 78, 373–433 (2006).

    ADS  Article  Google Scholar 

  10. Alloul, H., Bobroff, J., Gabay, M. & Hirschfeld, P. J. Defects in correlated metals and superconductors. Rev. Mod. Phys. 81, 45–108 (2009).

    ADS  Article  Google Scholar 

  11. Weitering, H. H. et al. Defect-mediated condensation of a charge density wave. Science 285, 2107–2110 (1999).

    Article  Google Scholar 

  12. Millis, A. J., Morr, D. K. & Schmalian, J. Local defect in metallic quantum critical systems. Phys. Rev. Lett. 87, 167202 (2001).

    ADS  Article  Google Scholar 

  13. Zhu, J-X., Martin, I. & Bishop, A. R. Spin and charge order around vortices and impurities in high- Tc superconductors. Phys. Rev. Lett. 89, 067003 (2002).

    ADS  Article  Google Scholar 

  14. Andersen, B. M., Hirschfeld, P. J., Kampf, A. P. & Schmid, M. Disorder-induced static antiferromagnetism in cuprate superconductors. Phys. Rev. Lett. 99, 147002 (2007).

    ADS  Article  Google Scholar 

  15. Pan, S. H. et al. Imaging the effects of individual zinc impurity atoms on superconductivity in Bi2Sr2CaCu2O8+d . Nature 403, 746–750 (2000).

    ADS  Article  Google Scholar 

  16. Bianchi, A., Movshovich, R., Vekhter, I., Pagliuso, P. G. & Sarrao, J. L. Avoided antiferromagnetic order and quantum critical point in CeCoIn5 . Phys. Rev. Lett. 91, 257001 (2003).

    ADS  Article  Google Scholar 

  17. Knebel, G., Aoki, D., Braithwaite, D., Salce, B. & Flouquet, J. Coexistence of antiferromagnetism and superconductivity in CeRhIn5 under high pressure and magnetic field. Phys. Rev. B 74, 020501 (2006).

    ADS  Article  Google Scholar 

  18. Park, T. et al. Hidden magnetism and quantum criticality in the heavy fermion superconductor CeRhIn5 . Nature 440, 65–68 (2006).

    ADS  Article  Google Scholar 

  19. Petrovic, C. et al. Heavy-fermion superconductivity in CeCoIn5 at 2.3 K. J. Phys. Condens. Matter 13, L337–L342 (2001).

    Article  Google Scholar 

  20. Paglione, J. et al. Nonvanishing energy scales at the quantum critical point of CeCoIn5 . Phys. Rev. Lett. 97, 106606 (2006).

    ADS  Article  Google Scholar 

  21. Urbano, R. R. et al. Interacting antiferromagnetic droplets in quantum critical CeCoIn5 . Phys. Rev. Lett. 99, 146402 (2007).

    ADS  Article  Google Scholar 

  22. Bauer, E. D. et al. Electronic inhomogeneity in a Kondo lattice. Proc. Natl Acad. Sci. USA 108, 6857–6861 (2011).

    ADS  Article  Google Scholar 

  23. Ishigaki, A. & Moriya, T. Nuclear magnetic relaxation around the magnetic instabilities in metals. J. Phys. Soc. Jpn 65, 3402–3403 (1996).

    ADS  Article  Google Scholar 

  24. Kohori, Y. et al. 115In NQR studies of CeRhIn5 and CeCoIn5 under high pressure. J. Alloys. Compd. 408, 51–53 (2006).

    Article  Google Scholar 

  25. Moriya, T. & Ueda, K. Spin fluctuations and high temperature superconductivity. Adv. Phys. 49, 555–606 (2000).

    ADS  Article  Google Scholar 

  26. Millis, A. J., Monien, H. & Pines, D. Phenomenological model of nuclear relaxation in the normal state of YBa2Cu3O7 . Phys. Rev. B 42, 167–178 (1990).

    ADS  Article  Google Scholar 

  27. Wolfe, P. & Abrahams, E. Quasiparticles beyond the Fermi liquid and heavy fermion criticality. Phys. Rev. B 84, 041101(R) (2011).

    ADS  Article  Google Scholar 

  28. Eiling, A. & Schilling, J. S. Pressure and temperature dependence of electrical resistivity of Pb and Sn from 1–300 K and 0–10 GPa-use as continuous resistive pressure monitor accurate over wide temperature range; superconductivity under pressure in Pb, Sn, and In. J. Phys. F 11, 623–639 (1981).

    ADS  Article  Google Scholar 

  29. Kraftmakher, Y. Modulation calorimetry and related techniques. Phys. Rep. 356, 1–117 (2002).

    ADS  Article  Google Scholar 

Download references


We thank F. Ronning, M. Vojta and J. Shim for helpful discussions. Work at Los Alamos was performed under the auspices of the US Department of Energy, Office of Science, Division of Materials Science and Engineering and supported in part by the Los Alamos LDRD program. Work at SKKU is supported by an NRF grant funded by the Korean Ministry of Education, Science & Technology (MEST) (No. 2012R1A3A2048816 & 220-2011-1-C00014). R.R.U. acknowledges FAPESP (No. 2012/05903-6). V.A.S. acknowledges support by RFBR Grant 12-02-00376. X.L. acknowledges NSFC (No. 11374257).

Author information

Authors and Affiliations



All authors discussed the results and commented on the manuscript. S.S. and X.L. performed the measurements and contributed equally to this work. R.R.U., V.A.S. and N.C. performed and analysed NQR experiments. E.D.B., L.D.P. and Z.F. provided samples, J-X.Z. performed theoretical calculations and T.P. and J.D.T. wrote the manuscript with input from all authors.

Corresponding authors

Correspondence to Tuson Park or J. D. Thompson.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Information (PDF 626 kb)

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Seo, S., Lu, X., Zhu, JX. et al. Disorder in quantum critical superconductors. Nature Phys 10, 120–125 (2014).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing