Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Mechanics of individual isolated vortices in a cuprate superconductor


Superconductors often contain quantized microscopic whirlpools of electrons, called vortices, that can be modelled as one-dimensional elastic objects1. Vortices are a diverse area of study for condensed matter because of the interplay between thermal fluctuations, vortex–vortex interactions and the interaction of the vortex core with the three-dimensional disorder landscape2,3,4,5. Although vortex matter has been studied extensively1,6,7, the static and dynamic properties of an individual vortex have not. Here, we use magnetic force microscopy (MFM) to image and manipulate individual vortices in a detwinned YBa2Cu3O6.991 single crystal, directly measuring the interaction of a moving vortex with the local disorder potential. We find an unexpected and marked enhancement of the response of a vortex to pulling when we wiggle it transversely. In addition, we find enhanced vortex pinning anisotropy that suggests clustering of oxygen vacancies in our sample and demonstrates the power of MFM to probe vortex structure and microscopic defects that cause pinning.


A superconducting vortex is characterized by two length scales: the nanoscale core size and the much larger magnetic penetration depth, λ. Pinning can occur when the core is co-located with a defect that locally suppresses superconductivity. λ determines the decay length for the currents encircling the core and the elastic properties of a vortex. Here, we probe the dynamics of an individual driven vortex, which is especially interesting when pinning and elasticity compete. Furthermore, we establish a dragged vortex as a probe that extends deep into the bulk of the sample to interact with defects far from the surface, circumventing disadvantages of other local-probe techniques that give information only about the immediate vicinity of the surface8. Previous strategies for manipulating single vortices in superconductors usually applied forces relatively delocalized on the scale of λ (refs 9, 10, 11). We use magnetic force microscopy (MFM) to combine imaging and vortex manipulation with a level of control far beyond what has been demonstrated before12,13. This capability may enable testing vortex entanglement14 and schemes for quantum computation15,16.

Our sample is ideal for studying the interplay between pinning and elasticity, with weak, well-controlled, pinning and fairly rigid vortices. In YBa2Cu3O6.991 (YBCO), superconductivity arises in CuO2 planes, parallel to the a and b axes, and in Cu–O chains, along the b axis. In pristine samples, such as ours, oxygen vacancies in the chains are the dominant source of pinning17,18,19. The orthorhombic crystal structure gives rise to penetration depth anisotropy, enabling us to determine the orientation of the crystal axes in situ (see Supplementary Information, Fig. S1). We mounted the platelet-shaped sample with the c axis along and the a axis 9 from (Fig. 1a).

Figure 1: MFM imaging and manipulation of individual vortices in YBCO at T=22.3 K.
figure 1

a,b, Schematic diagrams, not drawn to scale, showing an MFM tip (triangles) that attracts a vortex (thick lines) in a sample with randomly distributed point pinning sites (dots): at ‘surveillance’ height, the applied force Flat is too weak to move the vortex (a); at manipulation height, the vortex moves right and then left, as the tip rasters over it (b). Here, we illustrate what happens in a scan along , as indicated by the arrow. Also shown are three configurations of the vortex, previously dragged along : the blue line on the left illustrates the vortex before the tip drags it to the right, the dashed blue line shows an intermediate configuration as it follows the tip and the green line on the right shows the final configuration, after the tip moves away. c,d, MFM scans for two different scan heights (colour scale gives Fz/ z; fast scan and slow scan directions are indicated on the frame): z=420 nm (maximum applied lateral force Flatmax≈6 pN), not low enough to perturb vortices at this temperature (c); z=170 nm (Flatmax≈12 pN), low enough to drag the vortices significantly (d). Inset: Scan at 5.2 K, showing a stationary vortex at tip height and force comparable to those in the main panel. e, Line cut through the data in c along the dashed line, showing the signal from a stationary vortex (blue). Overlapping it is a line cut from the reverse scan (green). f, Line cut through the data in d along the dashed line, showing a typical signal from a dragged vortex. The right arrow shows the data acquired with the tip moving along , as in d; the left arrow shows the data acquired with the tip moving back along .

MFM uses a sharp magnetic tip on a flexible cantilever. Our tip magnetization provided an attractive tip–vortex force, F. While rastering in the xy plane, parallel to the sample surface, we measured local variations in the resonant frequency of the cantilever to determine Fz/ z (ref. 20). We deliberately used the lateral components of F, , for vortex manipulation.

At low temperature (T≈5 K), we observed no vortex motion up to our largest lateral force, 20 pN. At higher temperatures, pinning is reduced, and we could reduce the tip–sample distance z to tune from non-invasive imaging to manipulation. Figure 1 shows typical examples for individual, well-isolated, vortices. The similarity of the behaviour of vortices pinned at different locations indicates the uniformity of the pinning landscape in this sample.

Figure 1d shows one of our two main findings: ‘vortex wiggling’. Adding an alternating transverse force enhances vortex dragging markedly. The wiggling occurs because of the rastering associated with imaging: between incremental steps forward along the ‘slow’ scan direction, we raster the tip left and right along the ‘fast’ scan axis. If Flat≡|Flat| is small, this creates an image of a stationary vortex (Fig. 1a,c,e). When Flat is large, the vortex moves as the tip passes over it (Fig. 1b,d,f). Although this motion is substantial in the quasi-one-dimensional (1D) scans along the fast axis (Fig. 1f), it is much larger along the slow axis (Fig. 1d).

We study wiggling further in Fig. 2. Figure 2a shows a scan that we acquired after imaging the same area over and over, resulting in an enhanced wiggling effect. Line scans along from that image (Fig. 2b) do not differ from Fig. 1f. To study the vortex after completing the scan in Fig. 2a, we moved the tip back and forth over the centre of the vortex along to obtain Fig. 2c,d. Details of the motion along the fast axis (Fig. 2b) are similar to motion along what was the slow axis (Fig. 2c,d)—a vortex moves in jerks, reminiscent of avalanches5—but the total distance moved differs substantially. Moreover, Fig. 2c,d shows that although a vortex moves very freely between the initial and final positions in Fig. 2a, it does not readily move outside this range. In fact, we were never able to permanently drag a vortex very far from its original location, contrary to the case in thin films12. This tethering suggests that each vortex was pinned along its full length across the 40-μm-thick crystal, and that we observed the vortex stretching.

Figure 2: MFM image and line scans at T=20 K, showing how wiggling enhances dragging along the slow direction.
figure 2

a, Scan at z=80 nm (Flatmax≈20 pN), acquired after repeated imaging, reversing the slow scan direction for each new scan, which enhances the wiggling effect. Scan directions are denoted on the frame; dashed lines show the trajectories of the line scans in bd. Inset: Scan with similar parameters at 5.2 K, where vortices were immobile. b, Line scans from a along the horizontal dashed line. Arrows show the scan direction. c,d, Immediately after the scan in a, we scanned back and forth along the vertical dashed line at z=80 nm ((c) scans down, (d) scans up). Indices: Order of line-scan acquisition.

A vortex presumably stops moving where elasticity and pinning balance Flat. Qualitatively, wiggling helps segments of the vortex to depin, facilitating the extra motion along the slow axis. Confirming this is Fig. 2 with the enhancement of the effect by adding wiggling cycles (further test in Supplementary Information, Fig. S2). Wiggling is reminiscent of ‘vortex shaking’, used to accelerate equilibration in vortex matter by oscillating a magnetic field perpendicular to the applied magnetic field generating the vortices6,21,22, and may be the mechanism for it. The models presented below describe motion without wiggling, as we observe along the fast axis. Our single-vortex data should be amenable to more advanced and quantitative theoretical modelling to describe the wiggling.

The behaviour along the fast axis can be analysed as individual one-dimensional scans. As the tip approaches a vortex, Flat increases until, if it overcomes pinning, the vortex moves. The vortex then moves until pinning and the growing elastic force balance Flat, presumably when Flat is maximal, enabling us to treat this as a static problem. The dependence of w, the distance dragged along the fast axis, on Flatmax≡max(Flat) is shown in Fig. 3. We have constructed a model based on weak collective pinning (WCP) for a single vortex1 to explain this data (see Supplementary Information, Discussion S2). WCP assumes that pinning is only by the collective, cumulative, effect of many pinning sites, each too weak to pin a vortex on its own, and that vortices are elastic strings23, as described in Ginzburg–Landau theory1. A characteristic length, Lc, emerges from the competition between pinning and elasticity: a vortex takes advantage of pinning by bending on a length LLc, but it cannot bend for LLc. In WCP, the vortex is broken into elastically coupled Lc segments, each pinned by a characteristic force, Fp.

Figure 3: Force dependence of the dragged distance, w, along the fast axis.
figure 3

a, Force calibration: magnitude of peaks from vortices, max( Fz/ z)≡ Fzmax/ z, versus scan height at various temperatures. Clearly the temperature dependence in this range is weak. The solid line is a fit to (h0=358±5 nm, , Supplementary Information, Discussion S1). The excellent fit enables us to use . The maximum applied lateral force is given by Flatmax=α Fzmax. For a wide range of tip shapes 0.3<α<0.4 (ref. 30). We set α=0.35, adding at most 25% systematic error to Flatmax. Inset: Single line from a scan at z=65 nm, T=5.2 K, showing the peak height for an immobile vortex (here, max( Fz/ z)=365 pN μm−1). b, Distance moved by the vortex along the fast direction versus z (top axis) acquired at T=25 K versus Flatmax (bottom axis). In addition to the maximum w (filled circles), we plot the distribution (diamonds and crosses), which shows the stochasticity of the vortex motion. Other errors are not shown. Dashed lines are fits to equation (1) (along , ; along : F1=4.1±0.7 pN, ). Inset: Subsequent line scans showing the jerky nature of the vortex motion and how w was extracted from the difference of the vortex positions in pairs of subsequent line scans.

We assume that each vortex is initially along the c axis, that only the top portion interacts directly with the tip and that Lcλa b (where λa b is the in-plane penetration depth). Each Lc segment is subject to elastic forces from neighbouring segments and a pinning force up to Fp, modelled as static friction. We find that the top portion of a vortex depins when Flatmax>FpΛ/Lc (Λ of order λa b) and that:

for FlatmaxFpΛ/Lc (see Supplementary Information, Discussion S3). Here, F1/Fp≈2Λ/Lc and is the vortex line tension. Figure 3b shows a reasonable fit for large Flatmax, where the exact shape of the top portion of the vortex and the fine details of the pinning landscape are not important.

Figure 3b also highlights our second main finding—in-plane anisotropy due to the crystal: we can drag a vortex farther along the fast axis if it is along the YBCO b axis than if it is along the a axis. This is also apparent in Fig. 4. Figure 4c,d shows the dependence of w on the fast scan angle (see Supplementary Information, Fig. S3, for w here). We found a similar effect using different tips (see Supplementary Information, Table S1) and for every vortex that we probed.

Figure 4: Images and analysis showing the anisotropy of dragging when the fast axis is along the a axis and when it is along the b axis.
figure 4

a,b, Vortex motion when the fast scan is along (a) and (b) (T=20 K, z=80 nm, Flatmax≈20 pN). Note the erratic nature of the motion and the abrupt snap-in to the tip on approaching the vortex along the slow axis, apparent as a sharp onset of the signal. Insets: Images of immobile vortices obtained with the same tip, scan height and scan directions at T=5.2 K. c,d, Distance moved along the fast axis, w, measured near the maximum lateral force, versus scan angle measured from . Bars denote 70% confidence intervals. Dashed lines show the fit described in the text, with the oxygen vacancy cluster size 2Rb as a free parameter. Fit result: 2Rb/ξa b=0.7. In cT=20 K at z=80 nm, 130 nm, 230 nm (Flatmax≈20, 15, 10 pN, respectively). In dz=80 nm, for T=20, 15, 10 K. e, Schematic diagram of vortex core meandering across the crystal in the presence of point defects clustered along the b axis.

Equation (1) explains the anisotropy qualitatively. The penetration depth imparts in-plane anisotropy to (refs 1, 24), implying that it is easier to tilt a vortex towards the b axis. In addition, because of the in-plane anisotropy of the vortex core radius, even for point pinning, the effective pinning potential is less steep along the b axis, implying a smaller depinning force. Equation (1) thus naturally explains the weak dependence of the anisotropy on Flatmax and T, seen in Fig. 4c,d. When FlatmaxF1, the only dependence on Flatmax is an overall scale. The same is true for the T dependence, because both the superconducting parameters and the defect structure depend only weakly on T in our range25.

For quantitative analysis, we have determined the angular dependence of (see Supplementary Information, Discussion S4), which depends on the anisotropy factor ζ. Fitting all five data sets in Fig. 4c,d, we find ζ=1.6 (see Supplementary Information, Fig. S5), in clear disagreement with our direct measurement (see Supplementary Information, Fig. S1) and the known value25, ζ=1.3. We surmise that there is an extra source of anisotropy.

A likely source for extra pinning anisotropy is nanoscale clustering of oxygen vacancies along the Cu–O chains26,27 (Fig. 4e). We modified our model (see Supplementary Information, Discussion S5), imposing ζ=1.3, and fit the data in Fig. 4c,d for the cluster size. We find clusters of order 10 vacancies along the Cu–O chains (see Supplementary Information, Discussion S5), large but reasonable for the sample’s length of time at room temperature, where oxygen vacancies migrate slowly and cluster28. It is also possible that non-Ginzburg–Landau physics affects the core structure29, changing details of the pinning-force anisotropy. These results demonstrate that single-vortex manipulation is a local probe of both the core and the defect structure on a scale down to the core size. For example, in samples without intrinsic ab anisotropy and with known defect structure, MFM could be used to probe the intrinsic structure of the vortex core itself.

Despite the fact that YBCO is one of the most studied superconductors, our data reveal major surprises about the behaviour of individual vortices. A model based on weak collective pinning for a single vortex quantitatively describes quasistatic aspects of vortex motion with the incorporation of anisotropy in the local microscopic pinning. This demonstrates that single-vortex manipulation is a local probe of the structure of both the vortex and the pinning defects. Further work is required to describe the dynamic aspects of individual vortex motion that we revealed: its stochastic nature and the marked effect of transverse wiggling. In particular: how do the dynamics alter the effective pinning landscape? How do they affect the mechanical properties? Practically, wiggling is an important tool for future experiments that require pulling vortices long distances, for example, in the study of vortex entanglement14. Our results show the utility of local force probes for accessing the pinning properties and mechanical behaviour of individual vortices, the collective behaviour of which is of great importance for the properties of superconductors.


Frequency-modulated MFM (ref. 20).

We oscillate the cantilever along and measure the resonant frequency, f0, which shifts by Δf in a force gradient. Assuming small oscillation amplitude, Fz/ z≈−2cΔf/f0 (where c is the cantilever spring constant, see Supplementary Information, Table S1).

Sample details.

The platelet-shaped single crystal was grown from flux in a BaZrO3 crucible for high purity and crystallinity17. The (001) surfaces were free of visible inclusions. Mechanical detwinning was followed by annealing to oxygen content 7−δ=6.991, implying Tc≈88 K (ref. 19). The sample was stored at room temperature for a few years. The finite ab anisotropy enabled us to identify crystal orientation by determining the directions along which vortex spacings were extremal (see Supplementary Information, Fig. S1). The ratio between these spacings is ζ=1.3, corroborating previous results on similar samples25.


  1. Blatter, G., Feigel’man, M. V., Geshkenbein, V. B., Larkin, A. I. & Vinokur, V. M. Vortices in high-temperature superconductors. Rev. Mod. Phys. 66, 1125–1388 (1994).

    ADS  Article  Google Scholar 

  2. Fisher, M. P. A. & Lee, D. H. Correspondence between two-dimensional bosons and a bulk superconductor in a magnetic field. Phys. Rev. B 39, 2756–2759 (1989).

    ADS  Article  Google Scholar 

  3. Nelson, D. R. & Vinokur, V. M. Boson localization and correlated pinning of superconducting vortex arrays. Phys. Rev. B 48, 13060–13097 (1993).

    ADS  Article  Google Scholar 

  4. Ertaş, D. & Kardar, M. Anisotropic scaling in depinning of a flux line. Phys. Rev. Lett. 73, 1703–1706 (1994).

    ADS  Article  Google Scholar 

  5. Sethna, J. P., Dahmen, K. A. & Myers, C. R. Crackling noise. Nature 410, 242–250 (2001).

    ADS  Article  Google Scholar 

  6. Avraham, N. et al. ‘Inverse’ melting of a vortex lattice. Nature 411, 451–454 (2001).

    ADS  Article  Google Scholar 

  7. Pardo, F., de la Cruz, F., Gammel, P. L., Bucher, E. & Bishop, D. J. Observation of smectic and moving-Bragg-glass phases in flowing vortex lattices. Nature 396, 348–350 (1998).

    ADS  Article  Google Scholar 

  8. Hoffman, J. E. et al. Imaging quasiparticle interference in Bi2Sr2CaCu2O8+δ . Science 297, 1148–1151 (2002).

    ADS  Article  Google Scholar 

  9. Park, G. S., Cunningham, C. E., Cabrera, B. & Huber, M. E. Vortex pinning force in a superconducting niobium strip. Phys. Rev. Lett. 68, 1920–1922 (1992).

    ADS  Article  Google Scholar 

  10. Breitwisch, M. & Finnemore, D. K. Pinning of a single Abrikosov vortex in superconducting Nb thin films using artificially induced pinning sites. Phys. Rev. B 62, 671–677 (2000).

    ADS  Article  Google Scholar 

  11. Gardner, B. W. et al. Manipulation of single vortices in YBa2Cu3O6.354 with a locally applied magnetic field. Appl. Phys. Lett. 80, 1010–1012 (2002).

    ADS  Article  Google Scholar 

  12. Moser, A., Hug, H. J., Stiefel, B. & Güntherodt, H.-J. Low temperature magnetic force microscopy on YBa2Cu3O7−δ thin films. J. Magn. Magn. Mater. 190, 114–123 (1998).

    ADS  Article  Google Scholar 

  13. Roseman, M. & Grütter, P. Magnetic imaging and dissipation force microscopy of vortices on superconducting Nb films. Appl. Surf. Sci. 188, 416–420 (2002).

    ADS  Article  Google Scholar 

  14. Olson Reichhardt, C. J. & Hastings, M. B. Do vortices entangle? Phys. Rev. Lett. 92, 157002 (2004).

    ADS  Article  Google Scholar 

  15. Berciu, M., Rappoport, T. G. & Boldizsár, J. Manipulating spin and charge in magnetic semiconductors using superconducting vortices. Nature 435, 71–75 (2005).

    ADS  Article  Google Scholar 

  16. Weeks, C., Rosenberg, G., Seradjeh, B. & Franz, M. Anyons in a weakly interacting system. Nature Phys. 3, 796–801 (2007).

    ADS  Article  Google Scholar 

  17. Liang, R., Bonn, D. A. & Hardy, W. N. Growth of high quality YBCO single crystals using BaZrO3 crucibles. Physica C 304, 105–111 (1998).

    ADS  Article  Google Scholar 

  18. Liang, R. X., Bonn, D. A. & Hardy, W. N. Preparation and X-ray characterization of highly ordered ortho-II phase YBa2Cu3O6.50 single crystals. Physica C 336, 57–62 (2000).

    ADS  Article  Google Scholar 

  19. Liang, R., Bonn, D. A. & Hardy, W. N. Evaluation of CuO2 plane hole doping in YBa2Cu3O6+x single crystals. Phys. Rev. B 73, 180505 (2006).

    ADS  Article  Google Scholar 

  20. Albrecht, T. R., Grütter, P., Horne, D. & Rugar, D. Frequency-modulation detection using high-Q cantilevers for enhanced force microscope sensitivity. J. Appl. Phys. 69, 668–673 (1991).

    ADS  Article  Google Scholar 

  21. Willemin, M. et al. Strong shift of the irreversibility line in high-Tc superconductors upon vortex shaking with an oscillating magnetic field. Phys. Rev. B 58, R5940–R5943 (1998).

    ADS  Article  Google Scholar 

  22. Brandt, E. H. & Mikitik, G. P. Why an ac magnetic field shifts the irreversibility line in type-II superconductors. Phys. Rev. Lett. 89, 027002 (2002).

    ADS  Article  Google Scholar 

  23. Brandt, E. H. Large range of validity of linear elasticity of the vortex lattice in high-Tc superconductors. Phys. Rev. Lett. 69, 1105–1108 (1992).

    ADS  Article  Google Scholar 

  24. Burlachkov, L. I. Structure of vortex lattice in biaxial superconductors. Europhys. Lett. 8, 673–677 (1989).

    ADS  Article  Google Scholar 

  25. Pereg-Barnea, T. et al. Absolute values of the London penetration depth in YBa2Cu3O6+y measured by zero field ESR spectroscopy on Gd doped single crystals. Phys. Rev. B 69, 184513 (2004).

    ADS  Article  Google Scholar 

  26. Erb, A. et al. Experimental evidence for fast cluster formation of chain oxygen vacancies in YBa2Cu3O7−δ as the origin of the fishtail anomaly. Solid State Commun. 112, 245–249 (1999).

    ADS  Article  Google Scholar 

  27. Nishizaki, T., Shibata, K., Maki, M. & Kobayashi, N Vortex phase transition and oxygen vacancy in YBa2Cu3Oy single crystals. J. Low Temp. Phys. 131, 931–940 (2003).

    ADS  Article  Google Scholar 

  28. Liang, R. et al. Preparation and characterization of homogeneous YBCO single crystals with doping level near the SC-AFM boundary. Physica C 383, 1–7 (2002).

    ADS  Article  Google Scholar 

  29. Sonier, J. E. et al. Expansion of the vortex cores in YBa2Cu3O6.95 at low magnetic fields. Phys. Rev. B 59, R729–R732 (1999).

    ADS  Article  Google Scholar 

  30. Wadas, A., Fritz, O., Hug, H. J. & Güntherodt, H.-J. Magnetic force microscopy signal of flux line above a semiinfinite type-II-superconductor—theoretical approach. Z. Phys. B 88, 317–320 (1992).

    ADS  Article  Google Scholar 

Download references


Research supported by DOE Contract No. DE-AC02-76SF00515, AFOSR grant FA50-05-1-0290, the Packard Foundation and the US–Israel Binational Science Foundation (BSF). The experimental set up was developed with extensive help from D. Rugar. We acknowledge useful discussions with J. R. Kirtley, H. Bluhm, G. P. Mikitik, E. H. Brandt and V. B. Geshkenbein.

Author information

Authors and Affiliations



Conception and design: O.M.A., L.L., E.W.J.S., J.E.H., N.C.K. and K.A.M. Experiments: O.M.A. and L.L. Analysis: O.M.A. and L.L. with ideas developed with E.Z. and K.A.M. Sample growth: D.A.B., R.L. and W.N.H. Manuscript preparation: O.M.A., L.L., E.Z. and K.A.M., with input from all co-authors.

Corresponding author

Correspondence to Ophir M. Auslaender.

Supplementary information

Supplementary Information

Supplementary Informations (PDF 420 kb)

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Auslaender, O., Luan, L., Straver, E. et al. Mechanics of individual isolated vortices in a cuprate superconductor. Nature Phys 5, 35–39 (2009).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing