The honeycomb lattice of graphene is a unique two-dimensional system where the quantum mechanics of electrons is equivalent to that of relativistic Dirac fermions1,2. Novel nanometre-scale behaviour in this material, including electronic scattering3,4, spin-based phenomena5 and collective excitations6, is predicted to be sensitive to charge-carrier density. To probe local, carrier-density-dependent properties in graphene, we have carried out atomically resolved scanning tunnelling spectroscopy measurements on mechanically cleaved graphene flake devices equipped with tunable back-gate electrodes. We observe an unexpected gap-like feature in the graphene tunnelling spectrum that remains pinned to the Fermi level (EF) regardless of graphene electron density. This gap is found to arise from a suppression of electronic tunnelling to graphene states near EF and a simultaneous giant enhancement of electronic tunnelling at higher energies due to a phonon-mediated inelastic channel. Phonons thus act as a ‘floodgate’ that controls the flow of tunnelling electrons in graphene. This work reveals important new tunnelling processes in gate-tunable graphitic layers.
Graphene provides an ideal platform for the local study of high-mobility two-dimensional (2D) electrons because it can be fabricated on top of an insulating substrate. The availability of a back-gate electrode makes graphene the first gate-tunable 2D system directly accessible to scanning probe measurement (Fig. 1a). Previous experiments have demonstrated the power of scanning tunnelling microscopy (STM) to probe the local electronic structure of graphene grown epitaxially on SiC (refs 7, 8, 9). That system, however, cannot be easily gated, and questions remain as to the influence of the SiC substrate on the graphene layer6,10. Mechanically cleaved graphene is a desirable alternative to graphene grown on SiC because it can be readily gated and placed on well-controlled substrates (Fig. 1a), thus making it useful for extracting intrinsic graphene properties.
The STM topography of a gated graphene flake device is shown in Fig. 2a. Corrugations with a lateral dimension of a few nanometres and a vertical dimension of ∼1.5 Å (r.m.s. value over a 60×60 nm2 area) are observed, probably due to roughness in the underlying SiO2 (refs 11, 12). The graphene honeycomb lattice can be clearly resolved on top of the surface corrugation, as seen more clearly in Fig. 2b.
We explored the local electronic structure of these graphene flake devices using dI/dV measurements at zero gate voltage, as shown in Fig. 2c. Strikingly, the spectrum shows a ∼130 mV gap-like feature centred at the Fermi energy, EF, as opposed to the linear density of states that might be expected from elastic tunnelling to a Dirac cone. A local minimum in the tunnelling conductance spectrum can also be seen at VD=−138 mV, making the spectrum asymmetric about EF. Close examination of the low-bias spectrum (Fig. 2c, inset) reveals that the tunnelling conductance does not go to absolute zero in the gap region. These observations were reproduced on more than eight different flake devices, and the gap feature was observed in every spectrum acquired with calibrated STM tips (more than 30 different tips). The gap feature was seen to be independent of location on a sample, although the energy position of the adjacent dip feature, VD, varied with tip location. This observation (together with the fact that a similar gap feature of the same size was seen on a graphene/SiC sample9) is evidence against substrate-induced effects as the origin of the gap feature, because such effects would imply a gap that depends on spatial location as well as the type of substrate.
Changing the device gate voltage, Vg, causes the graphene Dirac point (ED) to shift energetically relative to EF, inducing a 2D charge-carrier density of n=α Vg, where α=7.1×1010 cm−2 V−1 (estimated using a simple capacitor model1,2). STM dI/dV spectra taken at the same location on graphene with gate voltages ranging from Vg=−60 to +60 V are shown in Fig. 3a. The width and energy position of the central gap feature do not show any dependence on gate voltage, but the conductance minimum at VD shifts monotonically with gate voltage, and even switches polarity (red arrows, Fig. 3a).
To further characterize the mysterious central gap feature, we measured both the temperature dependence and the effective barrier for electrons tunnelling into graphene. As shown in Fig. 4a, no significant temperature dependence is observed in graphene dI/dV spectra measured at T=4.8 and 77.5 K (this lack of temperature dependence was observed for −60 V<Vg<+60 V). Tunnel barrier measurements were carried out by measuring the STM tunnel current as a function of tip–sample separation (z) at constant bias for voltages inside and outside the gap, and identical measurements were also carried out on a gold sample using the same tip as a calibration. STM tunnel current depends exponentially on z, I∝e−z/λ, and the decay length (λ) gives a measure of the effective tunnel barrier. λ was obtained by fitting I versus z measurements at large z (tunnel junction resistance>30 GΩ) with an exponential function. As seen in Fig. 4b, λ for graphene is comparable to that observed in the gold calibration data (λ≈0.45 Å) for biases outside the gap, but decreases markedly to a value only half as large (λ≈0.25 Å) for biases within the gap.
How do we interpret the anomalous graphene energy gap behaviour and gate-voltage-dependent conductance minima? A consistent picture emerges if we consider phonon-mediated inelastic tunnelling of electrons into the graphene flake accompanied by a strong suppression of elastic tunnelling at EF. In what follows, we first establish a general inelastic origin of the central gap feature and we then discuss how our data can be explained by a novel phonon-based inelastic excitation mechanism.
STM tunnel current is generally enhanced if the bias voltage is high enough to provide tunnelling electrons with enough energy to induce excitations that have some threshold energy ℏω0 (Fig. 4c)13. This opens up a new inelastic tunnelling channel at bias voltages of ±ℏω0/e, causing steps in dI/dV spectra that are symmetric around EF and that lead to a gap-like feature with width 2ℏω0. In the case of our graphene measurements, ℏω0=63±2 meV (this corresponds to one half of the voltage separation between peak centres in d2I/dV2). Strong evidence for such an inelastic tunnelling mechanism in graphene (as opposed to some other gap-inducing mechanism) can be seen in our data by analysing the gate-voltage dependence of the conductance minimum observed at VD. If we assume that this minimum arises from inelastic tunnelling to the graphene Dirac point (a minimum in the density of states), then its energy location in our data (e VD) should be offset by ℏω0 from its true energy location, ED, in the graphene band structure (because each inelastically tunnelling electron loses energy ℏω0):
Because VD depends on gate voltage, this inelastic relation enables us to directly plot ED versus Vg, as shown in Fig. 3b. Identification of the conductance minimum at VD with the Dirac point energy, ED, can be confirmed by fitting this plot with the expected dependence as prescribed by the graphene linear band structure1,2. Here, vF is the Fermi velocity of graphene and V0 is the shift of the Dirac point (in terms of gate voltage) due to substrate doping. An excellent fit is obtained with vF=1.10±0.01×106 m s−1 and V0=−4.1±0.2 V, values that are consistent with those of previous studies1,2,14. This unambiguously identifies the observed conductance minimum at VD as the Dirac point and simultaneously verifies a graphene inelastic tunnelling channel as the origin of the central gap feature.
The question next arises as to what specific type of graphene inelastic excitation we are observing that has energy ℏω0≈63 meV. One possible attribution is the 67 meV out-of-plane acoustic graphene phonon modes located near the K/K′ points in reciprocal space15. Electrons with energy less than this phonon threshold energy tunnel elastically into graphene at EF (near the K point) with only a low probability due to suppression of electronic tunnelling into states with a large wave vector16,17. Once the threshold bias voltage ±ℏω0/e is reached, however, tunnelling into K point states is markedly enhanced (seen as more than a factor of 10 increase in tunnelling conductance) by the opening of a new inelastic channel. In this new mechanism, an electron first tunnels into the graphene σ* band near the Γ point in reciprocal space (a virtual transition as shown in Fig. 4d) before falling into an available K point state on the π band through the emission of a K′ point out-of-plane phonon (to conserve crystal momentum and energy). This phonon-mediated inelastic tunnelling process, which involves momentum-conserving virtual transitions between 2D electronic bands, is distinctly different from previously studied inelastic tunnelling in single molecules13,18 or localized spins19 where momentum is not a well-defined quantity owing to a lack of translational symmetry (phonon-induced inelastic tunnelling in single molecules typically leads to conductivity changes of the order of only 1% in contrast to the factor of 10 seen here18). This is also different from band-structure-dependent tunnelling in silicon20 because the wave-vector dependence seen here is a result of inelastic excitations that couple the unique electronic band structure and phonon spectrum of graphene. A recent calculation21 by Wehling et al. confirms this general interpretation through density functional theory. They find significant mixing of the graphene σ and π electron bands due to the out-of-plane phonon mode at K/K′, resulting in a strongly enhanced inelastic electron tunnel current. We note that there are three in-plane phonon modes at K/K′, but their contributions to this process are insignificant owing to the symmetries of the σ and π bands22.
This mechanism is strongly supported by our observed wavefunction spatial decay rates. Within the observed energy gap (at energies below the inelastic threshold), electrons have to tunnel directly into graphene states with large crystal momentum parallel to the surface (k∥=K or K′). Such states tend to decay rapidly in the vacuum region above a surface, because their evanescent local density of states is expected to fall off as16
where φ is the workfunction and m is the mass of an electron. This accounts for the strong suppression of tunnelling conductance within the energy gap region and leads to the small decay length observed in the low-bias elastic tunnelling channel. At voltages outside the gap (at energies above the inelastic threshold), however, electrons tunnel via virtual excitations to the σ*-band states near the Γ point which have k∥≈0. Such states tend to extend further into the vacuum, leading to a larger decay length. Using the two measured decay lengths (∼0.45 Å for k∥=0 and ∼0.25 Å for k∥=K) combined with equation (2), we are able to extract a workfunction of φ=4.6±0.2 eV and a graphene K point wave vector K=1.7±0.4 Å−1. These values agree well with the known workfunction of graphite and the known graphene K point wavevector K=1.7 Å−1. This behaviour explains why the gap feature seen here is not observed by other experimental techniques (such as angle-resolved photoemission spectroscopy and transport measurements) that are not sensitive to the spatial decay of the electron wavefunction at a surface. The observed lack of temperature dependence in our dI/dV spectra can also be explained by the fact that the K/K′ phonon energy is so much higher than kBT (kB is the Boltzmann constant).
It is possible to gain insight into the electron–phonon coupling strength that underlies the inelastic tunnelling process observed here. The ratio of phonon-mediated tunnelling conductance at energies just outside the gap compared with elastic tunnel conductance at energies inside the gap can be approximated as follows (see the Supplementary Information):
Here, Ve–ph is the intrinsic graphene electron–phonon coupling matrix element connecting electronic states at the Γ and K points in reciprocal space and Eσ is the energy of intermediate states near the Γ point on the σ* band (Eσ∼4 eV; ref. 23). If we take the STM tip height as z≈5 Å (estimated from the tip–sample junction impedance ≈2 GΩ) and use our measured ratio of (dI/dV)out/(dI/dV)in≈13, then equation (3) enables us to extract an experimental electron–phonon coupling strength Vel–ph≈0.4 eV, consistent with a theoretical estimate of Vel–ph≈0.5 eV based on a simple tight-binding model22 (see equations 5.16, 5.18 and 5.20 and figure 5–9 in ref. 24). Our experimental value of Vel–ph, however, should only be taken as a very rough estimate because the absolute tip-height above graphene, z, is not directly measured.
In summary, we have demonstrated the ability to measure atomically resolved local electronic structure of a graphene flake device while changing its charge-carrier density using a back gate. The resulting graphene spectra exhibit a prominent gap-like feature that arises from a unique phonon-mediated inelastic tunnelling process that is intrinsic to graphene. Phonons thus serve as a ‘floodgate’ in graphene by promoting electronic tunnelling above a phonon threshold energy. The resulting nonlinear tunnelling I–V behaviour will impact future graphene device applications that use electron tunnelling processes.
Our graphene monolayers were prepared in a similar fashion as in ref. 25. Monolayers of graphene were identified using an optical microscope, and were subsequently confirmed using Raman spectroscopy (Fig. 1b)26,27. Gold electrodes (30 nm) were attached to graphene using direct deposition through a stencil mask for surface cleanliness. The gold contacts remained Ohmic up to a source–drain voltage of 500 mV (contact resistance<300 Ω). Heavily doped Si under the SiO2 layer was used as a back gate, enabling us to vary the carrier density in the graphene (Fig. 1a). All graphene samples were annealed at 400 ∘C in ultrahigh vacuum for ∼10 h to ensure surface cleanliness before STM measurements.
Our STM measurements were carried out in an Omicron low-temperature STM at T=4.8 K and in an ultrahigh-vacuum environment with base pressure<10−11 mbar. STM measurements were conducted with chemically etched metal STM tips made of tungsten or platinum/iridium alloy. To ensure that our STM tips were free of anomalies in their electronic structure, we calibrated the tips by carrying out tunnelling differential conductance (dI/dV) measurements on a clean Au(111) surface both before and after graphene measurement. This calibration is crucial for obtaining reproducible intrinsic tunnelling spectra on graphene because tip contamination is known to induce spurious artefacts28 (see the Supplementary Information). dI/dV spectra were measured through lock-in detection9.
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Zhang, Y., Tan, Y.-W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Katsnelson, M. I., Novoselov, K. S. & Geim, A. K. Chiral tunnelling and the Klein paradox in graphene. Nature Phys. 2, 620–625 (2006).
Cheianov, V. V., Fal’ko, V. & Altshuler, B. L. The focusing of electron flow and a Veselago lens in graphene p–n junctions. Science 315, 1252–1255 (2007).
Son, Y. W., Cohen, M. L. & Louie, S. G. Half-metallic graphene nanoribbons. Nature 444, 347–349 (2006).
Bostwick, A., Ohta, T., Seyller, T., Horn, K. & Rotenberg, E. Quasiparticle dynamics in graphene. Nature Phys. 3, 36–40 (2007).
Rutter, G. M. et al. Scattering and interference in epitaxial graphene. Science 317, 219–222 (2007).
Mallet, P. et al. Electron states of mono- and bilayer graphene on SiC probed by scanning-tunneling microscopy. Phys. Rev. B 76, 041403 (2007).
Brar, V. W. et al. Scanning tunneling spectroscopy of inhomogeneous electronic structure in monolayer and bilayer graphene on SiC. Appl. Phys. Lett. 91, 122102 (2007).
Zhou, S. Y. et al. Substrate-induced bandgap opening in epitaxial graphene. Nature Mater. 6, 770–775 (2007).
Ishigami, M., Chen, J. H., Cullen, W. G., Fuhrer, M. S. & Williams, E. D. Atomic structure of graphene on SiO2 . Nano Lett. 7, 1643–1648 (2007).
Stolyarova, E. et al. High-resolution scanning tunneling microscopy imaging of mesoscopic graphene sheets on an insulating surface. Proc. Natl Acad. Sci. 104, 9209–9212 (2007).
Lambe, J. & Jaklevic, R. C. Molecular vibration spectra by inelastic electron tunneling. Phys. Rev. 165, 821 (1968).
Martin, J. et al. Observation of electron–hole puddles in graphene using a scanning single electron transistor. Nature Phys. 4, 144–148 (2008).
Mohr, M. et al. Phonon dispersion of graphite by inelastic x-ray scattering. Phys. Rev. B 76, 035439 (2007).
Tersoff, J. & Hamann, D. R. Theory and application for the scanning tunneling microscope. Phys. Rev. Lett. 50, 1998–2001 (1983).
Vitali, L. et al. Phonon and plasmon excitation in inelastic electron tunneling spectroscopy of graphite. Phys. Rev. B 69, 121414(R) (2004).
Stipe, B. C., Rezaei, M. A. & Ho, W. Single-molecule vibrational spectroscopy and microscopy. Science 280, 1732–1735 (1998).
Hirjibehedin, C. F., Lutz, C. P. & Heinrich, A. J. Spin coupling in engineered atomic structures. Science 312, 1021–1024 (2006).
Stroscio, J. A., Feenstra, R. M. & Fein, A. P. Electronic-structure of the Si(111)2×1 surface by scanning-tunneling microscopy. Phys. Rev. Lett. 57, 2579–2582 (1986).
Wehling, T. O., Grigorenko, I., Lichtenstein, A. I. & Balatsky, A. V. Phonon mediated tunneling into graphene. Preprint at <http://arxiv.org/abs/0803.4427> (2008).
Jiang, J. et al. Electron–phonon matrix elements in single-wall carbon nanotubes. Phys. Rev. B 72, 235408 (2005).
Sugawara, K., Sato, T., Souma, S., Takahashi, T. & Suematsu, H. Fermi surface and edge-localized states in graphite studied by high-resolution angle-resolved photoemission spectroscopy. Phys. Rev. B 73, 045124 (2006).
Samsonidze, G. PhD thesis (Massachusetts Institute of Technology, Massachusetts, 2006).
Novoselov, K. S. et al. Two-dimensional atomic crystals. Proc. Natl Acad. Sci. 102, 10451–10453 (2005).
Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006).
Gupta, A., Chen, G., Joshi, P., Tadigadapa, S. & Eklund, P. C. Raman scattering from high-frequency phonons in supported n-graphene layer films. Nano Lett. 6, 2667–2673 (2006).
Tiedje, T., Varon, J., Deckman, H. & Stokes, J. Tip contamination effects in ambient pressure scanning tunneling microscopy imaging of graphite. J. Vac. Sci. Technol. A 6, 372–375 (1988).
We thank D.-H. Lee, S. Louie, A. Balatsky, J. Moore, C. H. Park, G. Samsonidze, D. Wegner, L. Berbil-Bautista and C. Hirjibehedin for helpful discussions. This work was supported by the DOE under contract No. DE-AC03-76SF0098. Y.Z. and F.W. acknowledge postdoctoral fellowships and A.Z. acknowledges a professor fellowship, from the Miller Institute, UC Berkeley.
Rights and permissions
About this article
Cite this article
Zhang, Y., Brar, V., Wang, F. et al. Giant phonon-induced conductance in scanning tunnelling spectroscopy of gate-tunable graphene. Nature Phys 4, 627–630 (2008). https://doi.org/10.1038/nphys1022
This article is cited by
Improving stability in two-dimensional transistors with amorphous gate oxides by Fermi-level tuning
Nature Electronics (2022)
The ω3 scaling of the vibrational density of states in quasi-2D nanoconfined solids
Nature Communications (2022)
Correlation-driven electron-hole asymmetry in graphene field effect devices
npj Quantum Materials (2022)
Visualizing discrete Fermi surfaces and possible nodal-line to Weyl state evolution in ZrSiTe
npj Quantum Materials (2022)
Atomically resolved electronic properties in single layer graphene on α-Al2O3 (0001) by chemical vapor deposition
Scientific Reports (2022)