Chemical doping of organic semiconductors using molecular dopants plays a key role in the fabrication of efficient organic electronic devices. Although a variety of stable molecular p-dopants have been developed and successfully deployed in devices in the past decade, air-stable molecular n-dopants suitable for materials with low electron affinity are still elusive. Here we demonstrate that photo-activation of a cleavable air-stable dimeric dopant can result in kinetically stable and efficient n-doping of host semiconductors, whose reduction potentials are beyond the thermodynamic reach of the dimer’s effective reducing strength. Electron-transport layers doped in this manner are used to fabricate high-efficiency organic light-emitting diodes. Our strategy thus enables a new paradigm for using air-stable molecular dopants to improve conductivity in, and provide ohmic contacts to, organic semiconductors with very low electron affinity.

Access optionsAccess options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Change history

  • 15 December 2017

    In the version of this Article originally published, the source of 'ZADN' stated in the Methods should have read 'obtained as free research samples from Guangzhou ChinaRay Optoelectronic Materials' instead of 'China-Ray'. This has now been corrected in the online versions of the Article.


  1. 1.

    , & Doping of organic semiconductors. Phys. Status Solidi A 210, 9–43 (2013).

  2. 2.

    & Toward a comprehensive understanding of molecular doping organic semiconductors (review). J. Electron Spectrosc. Relat. Phenom. 204, 208–222 (2015).

  3. 3.

    et al. White organic light-emitting diodes with fluorescent tube efficiency. Nature 459, 234–239 (2009).

  4. 4.

    , , , & Alternative p-doped hole transport material for low operating voltage and high efficiency organic light-emitting diodes. Appl. Phys. Lett. 105, 113303 (2014).

  5. 5.

    et al. Improved organic p-i-n type solar cells with n-doped fluorinated hexaazatrinaphthylene derivatives HATNA-F6 and HATNA-F12 as transparent electron transport material. J. Appl. Phys. 115, 54515 (2014).

  6. 6.

    , , & p-type doping effect on the performance of organic-inorganic hybrid solar cells. Appl. Phys. Lett. 99, 233305 (2011).

  7. 7.

    et al. Doped organic transistors operating in the inversion and depletion regime. Nat. Commun. 4, 2775 (2013).

  8. 8.

    et al. High performance polythiophene thin-film transistors doped with very small amounts of an electron acceptor. Appl. Phys. Lett. 92, 63310 (2008).

  9. 9.

    et al. High mobility N-type transistors based on solution- sheared doped 6,13-Bis(triisopropylsilylethynyl)pentacene thin films. Adv. Mater. 25, 4663–4667 (2013).

  10. 10.

    et al. Passivation of trap states in unpurified and purified C60 and the influence on organic field-effect transistor performance. Appl. Phys. Lett. 101, 253303 (2012).

  11. 11.

    , & Molecular n-type doping for air-stable electron transport in vacuum-processed n-channel organic transistors. Appl. Phys. Lett. 97, 243305 (2010).

  12. 12.

    et al. Doped polymer semiconductors with ultrahigh and ultralow work functions for ohmic contacts. Nature 539, 536–540 (2016).

  13. 13.

    , , & Electron transport materials for organic light-emitting diodes. Chem. Mater. 16, 4556–4573 (2004).

  14. 14.

    , , & Molecular n-type doping of 1,4,5,8-naphthalene tetracarboxylic dianhydride by pyronin B studied using direct and inverse photoelectron spectroscopies. Adv. Funct. Mater. 16, 831–837 (2006).

  15. 15.

    et al. Pyronin B as a donor for n-type doping of organic thin films. Appl. Phys. Lett. 82, 4495–4497 (2003).

  16. 16.

    , , , & Leuco crystal violet as a dopant for n-doping of organic thin films of fullerene C60. J. Phys. Chem. B 108, 17076–17082 (2004).

  17. 17.

    et al. Acridine orange base as a dopant for n doping of C60 thin films. J. Appl. Phys. 100, 1–9 (2006).

  18. 18.

    et al. 2-(2-Methoxyphenyl)-1,3-dimethyl-1H-benzoimidazol-3-ium iodide as a new air-stable n-type dopant for vacuum-processed organic semiconductor thin films. J. Am. Chem. Soc. 134, 3999–4002 (2012).

  19. 19.

    , , & Use of a 1H-benzoimidazole derivative as an n-type dopant and to enable air-stable solution-processed n-channel organic thin-film transistors. J. Am. Chem. Soc. 132, 8852–8853 (2010).

  20. 20.

    et al. Solubility-limited extrinsic n-type doping of a high electron mobility polymer for thermoelectric applications. Adv. Mater. 26, 2825–2830 (2014).

  21. 21.

    et al. Effective solution- and vacuum-processed n-doping by dimers of benzimidazoline radicals. Adv. Mater. 26, 4268–4272 (2014).

  22. 22.

    , & Comparative study of the n-type doping efficiency in solution-processed fullerenes and fullerene derivatives. Adv. Funct. Mater. 24, 7116–7124 (2014).

  23. 23.

    et al. Mechanistic study on the solution-phase n-doping of 1,3-dimethyl-2-aryl-2,3-dihydro-1H-benzoimidazole derivatives. J. Am. Chem. Soc. 135, 15018–15025 (2013).

  24. 24.

    , & Trap-free electron transport in poly(p-phenylene vinylene) by deactivation of traps with n-type doping. Phys. Rev. B 81, 85201 (2010).

  25. 25.

    , & Solution phase n-doping of C60 and PCBM using tetrabutylammonium fluoride. J. Mater. Chem. A 2, 303–307 (2014).

  26. 26.

    et al. n-doping of organic electronic materials using air-stable organometallics: a mechanistic study of reduction by dimeric sandwich compounds. Chem. Eur. J. 18, 14760–14772 (2012).

  27. 27.

    et al. n-doping of organic electronic materials using air-stable organometallics. Adv. Mater. 24, 699–703 (2012).

  28. 28.

    et al. Solution doping of organic semiconductors using air-stable n-dopants. Appl. Phys. Lett. 100, 83305 (2012).

  29. 29.

    et al. Ultralow doping in organic semiconductors: evidence of trap filling. Phys. Rev. Lett. 109, 176601 (2012).

  30. 30.

    , , , & Dopant controlled trap-filling and conductivity enhancement in an electron-transport polymer. Appl. Phys. Lett. 106, 163301 (2015).

  31. 31.

    et al. Dimers of nineteen-electron sandwich compounds: crystal and electronic structures, and comparison of reducing strengths. Chem. Eur. J. 20, 15385–15394 (2014).

  32. 32.

    , , & Highly efficient organic devices based on electrically doped transport layers. Chem. Rev. 107, 1233–1271 (2007).

  33. 33.

    et al. Extremely low-voltage driving of organic light-emitting diodes with a Cs-doped phenyldipyrenylphosphine oxide layer as an electron-injection layer. Appl. Phys. Lett. 86, 33503 (2005).

  34. 34.

    & High-current injection and transport on order of kA/cm2 in organic light-emitting diodes having mixed organic/organic heterojunction interfaces. Jpn. J. Appl. Phys. 46, L861–L863 (2007).

  35. 35.

    & Suppression of exciton annihilation at high current densities in organic light-emitting diode resulting from energy-level alignments of carrier transport layers. Appl. Phys. Lett. 92, 63306 (2008).

  36. 36.

    & Electron affinities of organic materials used for organic light-emitting diodes: a low-energy inverse photoemission study. Org. Electron. 20, 24–30 (2015).

  37. 37.

    & Triplet emitter doped exciton harvesting layer for improved efficiency and long lifetime in blue phosphorescent organic light-emitting diodes. Synth. Met. 220, 573–577 (2016).

  38. 38.

    et al. Halogenation of a nonplanar molecular semiconductor to tune energy levels and bandgaps for electron transport. Chem. Mater. 27, 1892–1900 (2015).

  39. 39.

    et al. Contorted hexabenzocoronenes with extended heterocyclic moieties improve visible-light absorption and performance in organic solar cells. Chem. Mater. 28, 673–681 (2016).

  40. 40.

    et al. Efficient two layer LEDs on a polymer blend basis. Adv. Mater. 7, 551–554 (1995).

  41. 41.

    , , & Dipyrazolopyridine derivatives as bright blue electroluminescent materials. Appl. Phys. Lett. 77, 933–935 (2000).

  42. 42.

    et al. Improved efficiency in blue phosphorescent organic light-emitting devices using host materials of lower triplet energy than the phosphorescent blue emitter. Adv. Funct. Mater. 21, 3250–3258 (2011).

  43. 43.

    , , & Electron-hole interaction energy in the organic molecular semiconductor PTCDA. Chem. Phys. Lett. 272, 43–47 (1997).

Download references


A.K., X.L. and F.Z. acknowledge funding for this work from the National Science Foundation under grants DMR-1506097. Work in Berlin was supported by the Sfb951 (DFG) and the Helmholtz Energy-Alliance ‘Hybrid Photovoltaics’. B.P.R., M.A.F., and K.M.L. acknowledge funding for this work from the Department of Energy EERE SSL Program under Award #DE-EE0006672 and the Office of Basic Energy Sciences, Division of Materials Sciences and Engineering under Award #DE-SC0012458. Work at the Georgia Institute of Technology was supported by the National Science Foundation under grants DMR-1305247. We thank E. Longhi for synthetic assistance, E. List-Kratochvil for stimulating discussions about optical interference phenomena during UV/Vis measurements, G. Ligorio for performing PL measurements in Berlin, and A. Zykov, P. Schäfer and S. Kowarik for performing XRD measurements.

Author information


  1. Department of Electrical Engineering, Princeton University, Princeton, New Jersey 08544, USA

    • Xin Lin
    • , Kyung Min Lee
    • , Michael A. Fusella
    • , Fengyu Zhang
    • , Barry P. Rand
    •  & Antoine Kahn
  2. Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Albert-Einstein-Strasse 16, D-12489 Berlin, Germany

    • Berthold Wegner
    •  & Norbert Koch
  3. Institut für Physik & IRIS Adlershof, Humboldt-Universität zu Berlin, Brook-Taylor-Strasse 6, D-12489 Berlin, Germany

    • Berthold Wegner
    •  & Norbert Koch
  4. Center for Organic Photonics and Electronics and School of Chemistry and Biochemistry, Georgia Institute of Technology, Atlanta, Georgia 30332, USA

    • Karttikay Moudgil
    • , Stephen Barlow
    •  & Seth R. Marder
  5. Andlinger Center for Energy and the Environment, Princeton University, Princeton, New Jersey 08544, USA

    • Barry P. Rand


  1. Search for Xin Lin in:

  2. Search for Berthold Wegner in:

  3. Search for Kyung Min Lee in:

  4. Search for Michael A. Fusella in:

  5. Search for Fengyu Zhang in:

  6. Search for Karttikay Moudgil in:

  7. Search for Barry P. Rand in:

  8. Search for Stephen Barlow in:

  9. Search for Seth R. Marder in:

  10. Search for Norbert Koch in:

  11. Search for Antoine Kahn in:


X.L., B.W., K.M., A.K., N.K., S.R.M. and S.B. initialized this series of experiments. K.M., S.B. and S.R.M. synthesized the dopant molecules. X.L., B.W., A.K. and N.K. designed the work function and conductivity experiments, prepared the films, and carried out Kelvin probe, IV, AFM, UPS, XPS and IPES measurements. B.W. and N.K. conducted optical absorption spectroscopy. K.M.L. and B.P.R. performed part of the PL experiments in Princeton. X.L., K.M.L., M.A.F., B.P.R. and A.K. designed and performed EQEPV and OLED measurements. F.Z., K.M.L., X.L. and A.K. designed and fabricated samples for SIMS and RBS. All authors discussed the results and contributed to the manuscript.

Competing interests

The authors declare no competing financial interests.

Corresponding author

Correspondence to Antoine Kahn.

Supplementary information

PDF files

  1. 1.

    Supplementary Information

    Supplementary Information

About this article

Publication history