Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Tearing as a test for mechanical characterization of thin adhesive films


Thin adhesive films have become increasingly important in applications involving packaging, coating or for advertising. Once a film is adhered to a substrate, flaps can be detached by tearing and peeling, but they narrow and collapse in pointy shapes. Similar geometries are observed when peeling ultrathin films grown or deposited on a solid substrate, or skinning the natural protective cover of a ripe fruit. Here, we show that the detached flaps have perfect triangular shapes with a well-defined vertex angle; this is a signature of the conversion of bending energy into surface energy of fracture and adhesion. In particular, this triangular shape of the tear encodes the mechanical parameters related to these three forms of energy and could form the basis of a quantitative assay for the mechanical characterization of thin adhesive films, nanofilms deposited on substrates or fruit skin.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Figure 1: Three rectangular flaps of adhesive film were cut and pulled at the same speed, and the resulting tears were digitally scanned.
Figure 2: Schematic diagram showing the side and top views of the experiment and the geometrical parameters involved to describe the shape of the tear.
Figure 3: Force versus width for different materials and substrates.
Figure 4: The angle of tearing for experiments with three different materials.
Figure 5: Value of the parameter η extracted from the experiments.

Similar content being viewed by others


  1. Eggers, J. Nonlinear dynamics and breakup of free-surface flows. Rev. Mod. Phys. 69, 865–930 (1997).

    Article  CAS  Google Scholar 

  2. Atkins, A. G. Proc. 10th Congr. on Material Testing 595–600 (Scientific Society of Mech. Engineers, Budapest, 1991).

    Google Scholar 

  3. Atkins, A. G. Opposite paths in the tearing of sheet materials. Endeavour 18, 2–10 (1994).

    Article  Google Scholar 

  4. Atkins, A. G. Ripping yarns. Science & public affairs. Autumn 19–23 (1994).

  5. Lawn, B. Fracture of Brittle Solids 2nd edn (Cambridge Univ. Press, Cambridge, 2004).

    Google Scholar 

  6. Audoly, B., Reis, P. & Roman, B. Cracks in thin sheets: When geometry rules the fracture path. Phys. Rev. Lett. 95, 025502 (2005).

    Article  CAS  Google Scholar 

  7. Ghatak, A. & Mahadevan, L. Crack street: the cycloidal wake of a cylinder tearing through a thin sheet. Phys. Rev. Lett. 91, 215507 (2003).

    Article  CAS  Google Scholar 

  8. De Gennes, P. G., Brochard, F. & Quérés, D. Capillarity and Wetting Phenomena (Springer, New York, 2003).

    Google Scholar 

  9. Kendall, K. Thin-films: the elastic term. J. Phys. D 8, 1449–1452 (1975).

    Article  Google Scholar 

  10. Cortet, P. P., Ciccotti, M. & Vanel, L. Imaging the stick-slip peeling of an adhesive tape under a constant load. J. Stat. Mech. P03005 (2007).

  11. Hong, D. C. & Yue, S. Deterministic chaos in failure dynamics: Dynamics of peeling of adhesive tape. Phys. Rev. Lett. 74, 254–257 (1995).

    Article  CAS  Google Scholar 

  12. De, R., Maybhate, A. & Ananthakrishna, G. Dynamics of stick-slip in peeling of an adhesive tape. Phys. Rev. E 70, 046223 (2004).

    Article  Google Scholar 

  13. Landau, L. & Lifshitz, E. M. Theory of Elasticity 3rd edn (Pergamon, New York, 1986).

    Google Scholar 

  14. Love, E. H. A Treatise on the Mathematical Theory of Elasticity (Dover, New York, 1944).

    Google Scholar 

  15. Struik, D. J. Lectures on Classical Differential Geometry (Dover, New York, 1988).

    Google Scholar 

  16. Witten, T. A. Stress focusing in elastic sheets. Rev. Mod. Phys. 79, 643–675 (2007).

    Article  Google Scholar 

  17. Cerda, E. & Mahadevan, L. Geometry and physics of wrinkling. Phys. Rev. Lett. 90, 074302 (2003).

    Article  CAS  Google Scholar 

  18. Stafford, C. et al. A buckling-based metrology for measuring the elastic moduli of polymeric thin films. Nature Mater. 3, 545–550 (2004).

    Article  CAS  Google Scholar 

  19. Huang, J. et al. Capillary wrinkling of floating thin polymer films. Science 317, 650–653 (2007).

    Article  CAS  Google Scholar 

  20. Matas, A. et al. Biomechanics and anatomy of Lycopersicon esculentum fruit peels and enzyme-treated samples. Am. J. Bot. 91, 352–360 (2004).

    Article  Google Scholar 

  21. Boisclair, G. & Pagé, J. Guide des Sciences Expérimentales 3rd edn (ERPI, Québec, 2004).

    Google Scholar 

Download references


We thank the Chicago–Chile Material Collaboration Project (DMR-0303072), Ecos-Conicyt project No. C03E04 and are grateful for the help of Francisco Melo in whose laboratory this experiment was carried out. This article was also greatly improved by comments from M. Adda-Bedia, B. Audoly, A. Boudaoud, F. Melo and K. Niklas. E.H. and E.C. acknowledge FONDAP Grant No. 11980002 for financial support. E.C. acknowledges the support of Anillo ACT 15, Fondecyt Project No. 1050083 and thanks Mauricio Cerda for help with the computer software. B.R. acknowledges support from the French ministry of research—ACI ‘structures minces’, and PMR from the European funding MechPlant.

Author information

Authors and Affiliations


Corresponding author

Correspondence to Enrique Cerda.

Supplementary information

Rights and permissions

Reprints and permissions

About this article

Cite this article

Hamm, E., Reis, P., LeBlanc, M. et al. Tearing as a test for mechanical characterization of thin adhesive films. Nature Mater 7, 386–390 (2008).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing