Nanowires have attracted considerable interest as nanoscale interconnects and as the active components of both electronic and electromechanical devices. Nanomechanical measurements are a challenge, but remain key to the development and processing of novel nanowire-based devices. Here, we report a general method to measure the spectrum of nanowire mechanical properties based on nanowire bending under the lateral load from an atomic force microscope tip. We find that for Au nanowires, Young's modulus is essentially independent of diameter, whereas the yield strength is largest for the smallest diameter wires, with strengths up to 100 times that of bulk materials, and substantially larger than that reported for bulk nanocrystalline metals (BNMs)1,2,3,4,5. In contrast to BNMs, nanowire plasticity is characterized by strain-hardening, demonstrating that dislocation motion and pile-up is still operative down to diameters of 40 nm. Possible origins for the different mechanical properties of nanowires and BNMs are discussed.
This is a preview of subscription content, access via your institution
Open Access articles citing this article.
Nature Communications Open Access 27 September 2022
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Rent or buy this article
Prices vary by article type
Prices may be subject to local taxes which are calculated during checkout
Champion, Y. et al. Near-perfect elastoplasticity in pure nanocrystalline copper. Science 300, 310–311 (2003).
Lu, L., Sui, M. L. & Lu, K. Superplastic extensibility of nanocrystalline copper at room temperature. Science 287, 1463–1466 (2000).
Budrovic, Z., Swygenhoven, H. V., Derlet, P. M., Petegem, S. V. & Schmitt, B. Plastic deformation with reversible peak broadening in nanocrystalline nickel. Science 304, 273–276 (2004).
Lu, L., Shen, Y. F., Chen, X. H., Qian, L. H. & Lu, K. Ultrahigh strength and high electrical conductivity in copper. Science 304, 422–426 (2004).
Uchic, M. D., Dimiduk, D. M., Florando, J. N. & Nix, W. D. Sample dimensions influence strength and crystal plasticity. Science 305, 986–989 (2004).
Levitt, A. P. Whisker Technology (A. P. Levitt) Ch. 6 (Wiley-Interscience, New York, 1970).
Yu, M. F. et al. Strength and breaking mechanism of multiwalled carbon nanotubes under tensile load. Science 287, 637–640 (2000).
Poncharal, P., Wang, Z. L., Ugarte, D. & De Heer, W. A. Electrostatic deflections and electromechanical resonances of carbon nanotubes. Science 283, 1513–1516 (1999).
Gao, R. P. et al. Nanomechanics of individual carbon nanotubes from pyrolytically grown arrays. Phys. Rev. Lett. 85, 622–625 (2000).
Wong, E. W., Sheehan, P. E. & Lieber, C. M. Nanobeam mechanics: elasticity, strength, and toughness of nanorods and nanotubes. Science 277, 1971–1975 (1997).
Salvetat, J. P. et al. Elastic and shear moduli of single-walled carbon nanotube ropes. Phys. Rev. Lett. 82, 944–947 (1999).
Salvetat, J. P. et al. Elastic modulus of ordered and disordered multiwalled carbon nanotubes. Adv. Mater. 11, 161–165 (1999).
Kis, A. et al. Shear and Young's moduli of MoS2 nanotube ropes. Adv. Mater. 15, 733–736 (2003).
Cuenot, S., Champagne, S. D. & Nysten, B. Elastic modulus of polypyrrole nanotubes. Phys. Rev. Lett. 85, 1690–1693 (2000).
Walters, D. A. et al. Elastic strain of freely suspended single-wall carbon nanotube ropes. Appl. Phys. Lett. 74, 3803–3805 (1999).
Tombler, T. W. et al. Reversible electromechanical characteristics of carbon nanotubes under local-probe manipulation. Nature 405, 769–772 (2000).
Minot, E. D. et al. Tuning carbon nanotube band gaps with strain. Phys. Rev. Lett. 90, 1564011 (2003).
Falvo, M. R. et al. Bending and buckling of carbon nanotubes under large strain. Nature 389, 582–584 (1997).
Li, X. D., Gao, H. S., Murphy, C. J. & Caswell, K. K. Nanoindentation of silver nanowires. Nano Lett. 3, 1495–1498 (2003).
Agrait, N., Rubio, G. & Vieira, S. Plastic deformation of nanometer-scale gold connective necks. Phys. Rev. Lett. 74, 3995–3998 (1995).
Pan, Z. W. et al. Tensile tests of ropes of very long aligned multiwall carbon nanotubes. Appl. Phys. Lett. 74, 3152–3154 (1999).
Barrett, C. R., Nix, W. D. & Tetelman, A. S. in The Principles of Engineering Materials Ch. 6–8 (Prentice-Hall, Englewood Cliffs, New Jersey, 1973).
Koops, H. W. P., Kaya, A. & Weber, M. Fabrication and characterization of platinum nanocrystalline material grown by electron-beam induced deposition. J. Vac. Sci. Technol. B 13, 2400–2403 (1995).
Gere, J. M. & Timoshenko, S. P. in Mechanics of Materials Ch. 5.1.8 (PWS-KENT, Boston, Massachusettes, 1990).
Schwarz, U. D., Koster, P. & Wiesendanger, R. Quantitative analysis of lateral force microscopy experiments. Rev. Sci. Instrum. 67, 2560–2567 (1996).
Callister, W. D. Jr in Materials Science and Engineering 3rd edn, Ch. 6–8 (Wiley, New York, 1994).
Espinosa, H. D., Prorok, B. C. & Peng, B. Plasticity size effects in free-standing submicron polycrystalline FCC films subjected to pure tension. J. Mech. Phys. Solid 52, 667–689 (2004).
Kiely, J. D. & Houston, J. E. Nanomechanical properties of Au (111), (001), and (110) surfaces. Phys. Rev. B 57, 12588–12594 (1998).
Corcoran, S. G. & Colton, R. J. Anomalous plastic deformation at surfaces: Nanoindentation of gold single crystals. Phys. Rev. B 55, R16057–R16060 (1997).
Schiotz, J. & Jacobsen, K. W. A maximum in the strength of nanocrystalline copper. Science 301, 1357–1359 (2003).
Masuda, H. & Fukuda, K. Ordered metal nanohole arrays made by a two-step replication of honeycomb structures of anodic alumina. Science 268, 1466–1468 (1995).
Kovtyukhova, N. I. & Mallouk, T. E. Nanowires as building blocks for self-assembling logic and memory circuits. Chem. Eur. J. 8, 4354–4363 (2002).
We thank John Monaghan and Patrick Prendergast for the valuable discussions. This work was supported by Science Foundation Ireland under grant 00/PI.1/C077A.2.
The authors declare no competing financial interests.
About this article
Cite this article
Wu, B., Heidelberg, A. & Boland, J. Mechanical properties of ultrahigh-strength gold nanowires. Nature Mater 4, 525–529 (2005). https://doi.org/10.1038/nmat1403
This article is cited by
Role played by phonon drag on accuracy of MD simulations of nanowires due to deficiently selected strain rates
International Journal of Mechanics and Materials in Design (2023)
Hysteresis Loops and Compensation Behavior of Ferrimagnetic Mixed Spin (3/2,5/2) Hexagonal Ising Nanowire with Core-Shell Structure: Monte Carlo Simulation
Journal of Superconductivity and Novel Magnetism (2023)
Quantifying spectral thermal transport properties in framework of molecular dynamics simulations: a comprehensive review
Rare Metals (2023)
Size-Dependent Vibration of Porous Bishop Nanorod with Arbitrary Boundary Conditions and Nonlocal Elasticity Effects
Journal of Vibration Engineering & Technologies (2023)
Journal of Materials Engineering and Performance (2023)