Abstract
Advances in materials synthesis bring about many opportunities for technological applications, but are often accompanied by unprecedented complexity. This is clearly illustrated by the case of hierarchically organized zeolite catalysts, a class of crystalline microporous solids that has been revolutionized by the engineering of multilevel pore architectures, which combine unique chemical functionality with efficient molecular transport. Three key attributes, the crystal, the pore and the active site structure, can be expected to dominate the design process. This review examines the adequacy of the palette of techniques applied to characterize these distinguishing features and their catalytic impact.
Similar content being viewed by others
Introduction
Inspired by nature’s elegant examples and proclaimed as the next frontier in advanced materials design, ‘hierarchical organization’ has become a truly interdisciplinary phenomenon in the development of new technologies1,2,3,4,5,6. While the various uses of the quoted term are often considered as closely related, in materials science, it denotes the engineering of one or more phases to exploit structural order on different length scales1,2. The latter is pursued to enhance complementary characteristics (mechanical, thermal, electrical, optical, mass transfer and so on) and has the potential to bestow a performance unimaginable of the bulk constituents.
A field in which the development of hierarchically organized materials has experienced exceptional progress, having proven industrial relevance and reached advanced stages of the design, is that of zeolite catalysis5,6,7,8,9,10,11,12,13,14,15,16. In this context, a hierarchically organized zeolite (HOZ) is defined as a material that retains the crystalline order and associated functionality of a bulk (purely microporous) zeolite, but that also integrates a multilevel pore network. Analogous to improving the traffic circulation by introducing wide freeways along directions of major transit in cities, this centres on the introduction of an interconnected network of auxiliary meso- and/or macropores to enhance molecular transport in reactions in which diffusion is constrained within the micropores, which are typically of 0.3–1 nm in diameter. In this way, reactants and products can readily enter and leave the microporous domains, thereby maximizing the utilization of the active sites throughout the entire catalyst volume. The additional porosity levels can be configured either within (intracrystalline) or between (intercrystalline) the zeolite crystals, effectively shortening the diffusion path inside the micropores in both cases. This definition is further extended by the fact that additional phases may also be incorporated to achieve the desired porosity characteristics, such as in the case of inorganic or organic pillars, forming the basis of an endless spectrum of structural variants combining differing types, degrees and distributions of secondary porosity (Fig. 1).
The logical question follows: how can this information aid the design of a superior zeolite catalyst? Catalytic evaluation of HOZs has demonstrated numerous opportunities for enhanced performance in both traditional and emerging applications5,6,7. However, despite this extensive repertoire, for every competitive advantage there typically lies a threat. For example, as expected due to the increased external or mesopore surface area, HOZs are generally more active than their bulk predecessors in diffusion-constrained reactions, such as those involving the transformation of larger substrates or those undertaken in the liquid phase (Fig. 2a,b). The achievable enhancement strongly depends on the extent of mass transfer limitations and can exceed an order of magnitude7,15,16,17,18. Yet, this assumes that the active sites remain accessible and of similar quality. Depending on the acidity demands of the reaction, it has been shown that reductions in the strength and/or concentration of acid sites, which often accompany losses of the crystalline order, can impair or even reverse the catalytic benefits16,17,18. A similar case can be argued with respect to selectivity, where both beneficial and detrimental impacts have been evidenced over HOZs. Moreover, in chemical transformations involving multiple steps, different impacts may be observed on the selectivity to primary and secondary products17. Improvements are typically ascribed to the more efficient transport of the desired product out of the zeolite crystal9,16, while deteriorations are related to a loss of the shape-selective properties either because the diffusion path within the micropores is too short or due to the increased number of unselective active sites present at the external or mesopore surface (Fig. 2c)7,17,19. Finally, in terms of stability, the increased mesopore surface area in HOZs is known to significantly retard the rate of reversible deactivation in reactions suffering from prevalent coke deposition (Fig. 2d)20,21,22. On the other hand, reduced catalyst lifetimes have also been evidenced, which were ascribed to a compromised acidity and the poor quality of the auxiliary pore network22.
The above analysis points overwhelmingly towards the need for the application oriented design of HOZ catalysts, Three key attributes can be expected to dominate this process: the crystal, the pore and the active site structure. To date, the development and refinement of numerous synthetic protocols that enable the preparation of HOZs of any framework type or composition has been documented5,6,7,8,9,10,11,12,13. However, despite going hand in glove with progress in their synthesis, no review has previously examined the structural analysis of HOZs. The latter presents a far greater challenge than that of their bulk predecessors and is essential to rationalize their catalytic performance. For this purpose, the array of state-of-the-art techniques that have been applied to assess each of these parameters (Table 1) are critically examined, outlining the achievements and limitations and providing directions to push the boundaries of current approaches, respectively.
Synthesis mechanism
While this review does not comprehensively overview recent advances in the synthetic methodologies of HOZs, to understand their properties it is helpful to consider some important aspects regarding their synthesis. Here we focus on the fundamental question: what is known about the mechanism of hierarchical structuring of the porosity of a zeolite? Interrupting or suppressing the crystal growth in a given dimension and controlling the assembly during the synthesis, or dissolving the wall of a bulk zeolite by post-synthetic modification, have consequences that need to be understood. This can be considered at different length scales, both in terms of the resulting location and topology of mesopores and of the impact on the crystal and associated active site structure.
The mechanistic diversity can be appreciated by considering that HOZs can be synthesized by essentially opposite, bottom-up versus top-down, approaches (Fig. 3a). To date, the synthesis has predominantly been optimized through the experimental monitoring of key variables (Fig. 3b,c)15,23. Yet, while providing a mesoscopic framework through which to tackle the design, as with any trial and error approach, the finesse with which this can be accomplished depends on the comprehensiveness of the initial screening, and deviations from the established trends are highly probable. A clear example is found in the case of post-synthetic demetallation. In particular, the method of desilication in alkali media, which has been extensively studied due to its combined industrial readiness and versatility14,23, has experienced several paradigm shifts regarding the scope. For example, it took over 5 years to vanquish the initial dogma that the applicability was limited to a narrow compositional window of zeolites with Si/Al ratios of 25–50 (refs 24, 25). Similarly, the potentially key role of defects, which to date has remained rather obscure26, recently resurfaced when it was demonstrated that a defect free MFI-type zeolite was stable in alkaline media for up to 1 week27. The critical impact of the manufacturing conditions on the mesopore location and associated ability to enhance the transport attributes has also only lately been established28.
Progress in the understanding of how mesopore formation propagates through the crystal during demetallation, and the structure and functionality of the newly created mesopore wall, remains limited. Except in the case of processes targeting the hydrolytic extraction of more labile elements as boron or germanium located in crystallographically defined sites29,30,31, as has been elegantly exploited by Roth et al.29 through the ADOR (assembly–disassembly–organization–reassembly) approach, it is unclear at the molecular level which and why certain lattice positions and framework types are more susceptible to demetallation than others, what defects are created, as well as whether extraframework species form or may be reorganized by the treatment. Experimentally, the main obstacles are the detection limit and spatial sensitivity of existing characterization tools as nuclear magnetic resonance (NMR), X-ray diffraction (XRD) and extended X-ray absorption fine structure. On the other hand, the theoretical understanding remains in early stages. Only a handful of density functional theory studies have taken pioneering steps to calculate the potential hydrolysis pathways of desilication and dealumination and the structure of the resulting extraframework species, sometimes leading to surprising findings (Fig. 3d)32,33,34,35,36. For example, in the first study of the alkaline treatment of MFI-type zeolites, Zhai et al.33 reported that dealumination was more energetically favourable than desilication, but that leached aluminium species rapidly readsorbed on the zeolite. This would contradict the view based on experimental observations that aluminium exerts a stabilizing effect on the framework24,25. Nonetheless, the real processes are certainly more complex than those simulated, and a more exhaustive study of the elementary steps is required to gain confidence in the findings. In this respect, the large unit cells of zeolites and the presence of several water molecules and ions pose major challenges, which is why most works have only considered the removal of one or two atoms in the gas phase32. Taking into account collective effects arising due to the dynamic nature of the system and understanding the mesoscale propagation of the mesopores will constitute key milestones in future work.
Comparatively, an equally abundant list of questions can be elaborated for the direct synthesis of HOZs, which invariably is achieved through the application of variable quantities of specific templating species of different sizes and functionality37,38,39,40,41,42. One of the first challenges is to predict the complex behaviour of templating species within the synthesis gel. Towards this goal, most efforts have focused on characterizing the stepwise transformations occurring in relation to the diverse morphologies of the resulting zeolites. The atomic interaction of the template with framework metals has also been confirmed by solid state NMR (Fig. 3e)39,40,41,42. In an alternative approach, Ren et al.43 recently demonstrated a mesoscopic simulation approach that could open a window for investigating the formulation of hierarchical zeolites prepared by surfactant-driven routes (Fig. 3f). However, researchers still struggle to predict exactly how and to what extent a template will suppress the crystal growth and control the assembly and intergrowth behaviour of the resulting nanocrystals. Another bottom-up method that has seen growing interest is that of repetitive branching, in which HOZs in the form of intergrown (self-pillared) nanosheets are attained by introducing morphology modifying additives to induce intergrowth structures44,45,46,47. Advantageously for their technical potential, Inayat et al.47 recently demonstrated the possibility to attain zeolites with similar morphologies using readily available inorganic salts. The major importance of controlling zeolite nucleation, which has also enabled the template free preparation of three-dimensional (3D) nanosized EMT- and FAU-type zeolites48,49, indicate that an improved understanding of the synthesis and properties of HOZs will undoubtedly benefit the manufacturing efficiency and performance of these materials.
Crystal structure
The defining feature of a zeolite is a crystalline microporous framework, which originates its unique catalytic functionality. Indeed, the microenvironments defined by the periodic extension of interconnected channels and cavities impart the shape selectivity that is now a strong hallmark of zeolite catalysis. Yet, in endeavouring to reduce the diffusion path length within the micropores, the design of HOZs can stretch this definition to its limit. Apart from diminishing the size of the crystal domains, the introduction of auxiliary pore networks can result in increased defect concentrations or amorphization of the framework. Thus, the crystal structure is one of the first characteristics assessed in the preparation of HOZ catalysts.
While the initial structure elucidation relies upon X-ray powder diffraction, the reduced number of lattice planes to produce constructive interference in one or more directions means that the diffraction patterns of HOZs can become unrecognizable from those of bulk zeolites of equivalent framework type. This is clearly illustrated by comparing the simulated and experimental diffraction patterns of different types of HOZs (Fig. 4a,b). In the first example, the thickness of the crystal is reduced to that of a single unit cell in one direction, representative of the case of a two-dimensional nanosized zeolite50, and consequently no reflections with a component perpendicular to the layer are visible. On the other hand, if the size of the crystals is reduced to only a few unit cells in any direction, as in the case of a 3D nanosized zeolite, considerable broadening of all reflections would be expected. Another extreme case is that of ordered mesoporous zeolites in which the mesopores are regularly spaced and have a narrow size distribution51,52. Here, the ordering of mesopores originates reflections at very low angles. If the wall thickness, which can be estimated by comparison with the pore sizes determined by gas sorption, is equivalent to a unit cell or less, the periodicity of the zeolite will only be retained in one dimension (along the channels), and therefore the diffraction pattern would be quite different from that of the bulk zeolite. In fact, if the reflections of the zeolite are present, as seen in the experimental pattern51, the material could rather comprise a physical mixture of the two phases.
The shape of reflection profiles can differ widely in HOZs, and this can be exploited to access key insights such as the size of the coherently scattering crystalline domains and the presence of lattice imperfections and strain52,53. Nonetheless, few studies have attempted to extract this information by applying line profile analysis techniques. This could be related to experimental factors such as the need for high quality data and a precise knowledge of the instrumental contributions, or just to the magnitude of the challenge posed by such extreme line broadening. In this regard, the atomic pair distribution function, which is based on the analysis of interatomic distances via a total scattering approach, promises to become an invaluable tool once fully developed. It takes Bragg and diffuse scattering into account and so is applicable to both amorphous and crystalline materials. Its value has already been demonstrated in the analysis of the delaminated zeolite ITQ-2 (ref. 54).
However, it is essential to seek complementary information to assess the full structure of HOZs. For example, the absence of a unique stacking direction combined with the extremely small crystalline regions in single crystalline mesostructured zeolite nanosheets, such as those that can be attained by, for example, repetitive branching or templating strategies, can make it impossible to detect the intergrowths by XRD42,44,45,46,47. Here, high resolution transmission electron microscopy (TEM) can best expose the stacking faults, twinning and the nature of the mesopores between the crystals (Fig. 4c), playing an essential role in understanding the growth mechanism. Furthermore, because electrons interact more strongly with solids than X-rays, electron diffraction extends the analysis of crystalline materials to much smaller domain sizes, which has been exploited to solve the structures of complex intergrown zeolites as ITQ-39 (Fig. 4d)55. The development of the automated diffraction tomography and rotation electron diffraction methods have greatly increased the accessibility and efficiency of electron crystallography (Fig. 4e), and has been applied to confirm the 3D crystalline structure of HOZs41,56.
Nature and location of active sites
The optimization of the active site quality is crucial to maximize the catalytic benefit achievable over HOZ catalysts and demands a thorough understanding. In bulk zeolites, the design of active sites primarily concerns controlling the amount and siting of negatively charged AlO4− tetrahedra within the framework and the identity of the charge-compensating cations, which together determine the concentration and strength of Brønsted and Lewis acid sites. Comparatively, even if the crystal structure is fully preserved, it is easy to imagine that subtle distinctions may arise in HOZs, first because active sites associated with the large additional surface of the auxiliary pore network may have substantially different geometric and electronic environments from those located within the micropores, and second because changes in the aluminium speciation may be overlooked due to a limited sensitivity of analytical techniques. Significantly, a recent literature survey revealed a prominent reduction in the concentration of Brønsted acid sites in HOZs, with increasing mesoporous or external surface area independent of the framework type or synthesis (Fig. 5a,b)53. Furthermore, a linear relation was also observed between the strength and the concentration of Brønsted acid sites in HOZs prepared by demetallation (Fig. 5c)18. While early studies typically attributed distinctions in the acidic properties to the specific synthesis strategy, strong evidence attained by monitoring the evolution during successive preparation steps, indicates that the changes are most likely related to a reduced hydrothermal stability of framework aluminium in HOZs53,57.
Similarly to their bulk counterparts, the type, concentration and strength of the acid sites in HOZs are usually assessed through the infrared (IR) study of adsorbed pyridine. In the case of HOZs, however, the distribution of active sites between the internal and external zeolite surfaces requires special attention in view of the potentially more prominent catalytic role of the latter, particularly in transport or access limited reactions. This is typically approached by exploiting substituted bases of different size to selectively probe, for example, by IR or NMR, acid sites of differing size18,58,59,60, a powerful concept first developed in the form of the accessibility index60. However, this type of comparative analysis poses some challenges, as the range of acid sites sampled may also vary due to the distinct basicity of the probe molecules18. This is particularly relevant since an ideal base would detect only those sites having the required strength to catalyse the application of interest. The impact of the probe basicity may not be noticed in access limited reactions with relatively weak acidity demands, such as decalin cracking and the benzylation of toluene over MFI-type zeolites18,59, where direct correlations have been demonstrated between the concentration of acid sites at the external surface and the conversion achieved over HOZs. In contrast, distinct trends have been observed for transformations requiring stronger acid sites, such as the isopropylation of toluene or the esterification of benzyl alcohol with hexanoic acid over MFI-type zeolites18, where the probe molecule applied to quantify the amount of external acid sites (2,6-di-tert-butylpyridine) could not discriminate the relevant changes in the acid strength. Thus, the characterization of the acidity of the external surface remains an important challenge to enable optimization of the design of HOZ catalysts for diffusion-constrained processes.
The direct observation of the coordination of aluminium in HOZs by solid state NMR spectroscopy has been pursued to understand the structural origin of the acidity changes, commonly revealing the presence of penta- or octahedrally coordinated (non-framework) sites when the concentration of acid sites is reduced (Fig. 5d)53,61. However, the extensive broadening often observed in dehydrated samples due to quadrupolar interactions often hinders the precise quantitative comparison. Another major limitation of these bulk techniques is the lack of spatial resolution, from which it is impossible to gain insights into the relative distribution of active sites within the zeolite crystals. In pioneering work, Aramburo et al.62 recently demonstrated the application of scanning transmission X-ray microscopy to chemically probe the interior of micro-sized zeolite particles. In this way, they were able to follow the changes in quantity and coordination of aluminium upon steaming with a spatial resolution of ∼30 nm (Fig. 5e). Extending to higher resolutions, Khaleel et al.45 studied the Si/Al gradients within faujasite nanosheets by scanning TEM energy dispersive X-ray spectroscopy, which evidenced a 2.5-fold variation across the nanosheet (Fig. 5f). Understanding the catalytic impact of heterogeneities in the distribution and speciation of aluminium evidenced will undoubtedly be the subject of major future breakthroughs.
Pore architecture
Ultimately, the benefits of hierarchical organization in zeolites depend on our ability to precisely engineer the pore architecture and correspondingly the mass transfer properties for a targeted catalytic application. A hierarchical pore structure can be defined by three primary pillars, that is, the amount, the location and the connectivity of pores associated with each level. By correctly balancing these properties, an auxiliary pore systems should illuminate the microporous domains enabling their optimal function. Porosity analysis in HOZs is a multidimensional task encompassing the micropores and any meso-/macropores associated with the zeolite crystal in addition to the intercrystalline porosity of the zeolite phase as well as that further defined upon shaping into technical form. This section examines key aspects, assessing both the applicability and strategies to extend traditional methods as well as advanced multitechnique approaches, which can be exploited to gain insight into each of these critical parameters.
Size and amount
Early attempts to optimize the application-oriented design of HOZ catalysts were grounded on rationalizing the performance by the most directly quantifiable means, that is, the increase in the mesopore surface area of volume. As mentioned, due to the ubiquity of diffusion constraints, large activity enhancements could be readily demonstrated over HOZs in transformations involving bulky substrates and/or liquid-phase applications. For shape selective reactions, or those requiring well-defined acidic properties, it was quickly realized that extreme caution was required to ensure that the synthesis protocols preserved the integrity of the microporous domains. As such, one of the most successful descriptors for the performance of HOZs to date, the hierarchy factor and variants thereof, balanced these effects by factoring the relative mesopore surface area and micropore volume63. The ability to generically categorize zeolites of any framework type by readily assessable porosity characteristics was invaluable.
While both N2 and Ar sorption are popular methods for the textural characterization of HOZs (Fig. 6a–c), monatomic Ar is often preferred due to its smaller kinetic diameter (0.34 versus 0.37 nm), higher adsorption temperature (87 versus 77 K) and weaker fluid–wall interactions than diatomic N2, which help to reduce potential diffusion limitations and shift the adsorption within the micropores to higher pressures, respectively. In this respect, there has been little innovation on the traditional models applied to bulk zeolites. However, standard methods to access key structural parameters from N2 isotherms, such as the Brunauer–Emmett–Teller), t-plot and BJH (Barrett–Joyner–Halenda) methods, were developed using reference isotherms from non-porous materials. The inadequacy of these assumptions was recently demonstrated by the revelation that the t-plot analysis could lead to up to a 40% underestimation in the micropore volume64 (Fig. 6a). The difficulties associated with the derivation of pore size distributions (BJH) from N2 desorption, which often results in phantom contributions at 4 nm thought to depend on the pore connectivity, have also been extensively described65. Comparative analysis of the adsorption and desorption branches readily demonstrates this problem66 and enables estimation of the volume of occluded or constricted mesopores. More advanced implementations of the t-plot and BJH method generic to both nitrogen or argon isotherms have been proposed67,68,69, which remove the ambiguity of using the traditional BJH method with argon isotherms38.
For both bulk and HOZs, modern pore modelling techniques based on non-localized density functional theory (NLDFT) are now routinely adopted for the assessment of micro- and mesopore sizes, volumes and surface areas in a single approach, yielding a good agreement with Brunauer–Emmett–Teller surface area and capillary condensation70. Nevertheless, these approaches may be in danger of becoming too ‘press button’. Potential differences in the sorption properties of HOZs have yet to be rigorously addressed. Preliminary studies by Cho et al.52 revealed distinctions in the monoclinic–orthorhombic phase transition in an in situ XRD study of the structural changes during Ar sorption. Similarly, distinctions in the hydrophobicity evidenced by water sorption highlighted that the surface of the secondary pore networks should not be approached as identical to those of bulk zeolites71. Non-standard probes as hydrocarbons or water would no doubt find extended use for porosity characterization with the development of improved kernels for data analysis, and chemical interactions of the probe with the zeolite could be turned to advantage to gain further insight into the surface properties.
Mercury porosimetry offers a highly complementary tool22,72,73 for the comprehensive description of auxiliary pore systems integrating pores >4 nm in diameter, and becomes of paramount importance during the scale-up of zeolite catalysts into macroscopic-shaped forms. In principle, by coupling the information derived from Hg porosimetry and gas sorption, it is possible to access the pore size distribution across the entire range of length scales (Fig. 6c), the organization of which can be clearly visualized by FIB-SEM. Yet remarkably, until recently, no unified model had been developed to bridge the data from sorption isotherms and intrusion curves74. The convergence marks a transition from technique specific to unified descriptions of the pore structure, illustrating a clear direction for the development of new methods to gain insight into materials with hierarchical pore structures.
Location
Given the structural diversity of HOZs, a knowledge of the bulk porous properties alone is insufficient to establish crucial aspects regarding the integration of auxiliary pore systems, for example, whether the different porosity levels coexist in the same phase, how the pores are distributed and so on. In this regard, nothing is more tangible than the direct visualization of the pore architecture75. Compared with bulk zeolites, where microscopic techniques are primarily used to determine the particle size and morphology, the multidimensional challenge of examining the structural organization in HOZs has fuelled the development of much more advanced imaging approaches66,72,76,77. Fronting this movement, de Jong et al. elegantly exemplified the 3D TEM tomographic reconstruction and quantitative analysis of the pore network within commercial USY zeolite crystals66,76. While this enabled the derivation of the fraction of constricted mesopores, the tortuosity of the mesopore network and the size distribution of the remaining microporous domains (Fig. 6e)66, the catalytic relevance of these parameters has yet to be widely explored. At a similar time, Karwacki et al.77 took a different strategy, demonstrating the application of focused ion beam scanning electron microscopy to examine, with ∼5.2 nm resolution, the heterogeneity of the size of mesopores developed upon steaming with respect to the crystallographic orientation in individual coffin-shaped ZSM-5 crystals (100 × 20 × 20 μm3). Although potentially yielding valuable mechanistic clues to mesopore formation, it is unclear how these insights would translate to the smaller particle sizes and/or more complex morphologies typical of industrial zeolites, which would be difficult to directly examine by this method.
It is clear that optimal imaging approaches must deliver the right information while permitting a high throughput to enable good statistical representativeness. Thus, until improved methods are developed to automate image acquisition, tilt series alignment, reconstruction, and visualization and interpretation78, tomographic methods will likely not gain wide applicability for routine analysis. A bridge might come in the form of correlative strategies. For example, in model MFI-type zeolites of equivalent bulk porosity, the integration of the mesopores in distinct ‘open’ and ‘constricted’ configurations could be corroborated on the basis of a multitechnique assessment. Herein, the difference in mesopore volume determined by the application of mercury porosimetry in conjunction with nitrogen sorption, provided a measure of the accessibility of the auxiliary pore network (Fig. 6f). Further insight into the structural origin of the differing accessibility was attained through the simultaneous observation of the external and bulk structure by identical location secondary electron and high angle annular dark field imaging (Fig. 6g)22, which confirmed the more internal or external location of the mesopores. Of course electron-based techniques have well known limitations, such as the need for beam transparency in transmission modes, and the structural sensitivity of the sample to electron irradiation as well as to the cutting methods applied during the sample preparation and/or image acquisition. Here, strategies to minimize the sample exposure, such as through the use of scanning or low dose imaging modes, and to increase the sample tolerance, for example, through cryogenic cooling, are becoming increasingly popular79.
Connectivity
Independently of the amount or location, if the auxiliary pore networks are poorly connected they will not efficiently contribute to an improved mass transfer in HOZs. Connectivity is a complex multivariate parameter that embraces the interfaces between each porosity level, that is, the micro-mesopore, micro-macropore and meso-macropore unions. While the visualization and porosimetry approaches described capture certain features of the connectivity of the secondary pore systems, the most interesting aspect of the micro- and mesopore interface remains tantalizingly out of reach.
Although manifested in the response of numerous methods, so far very little progress has been made to quantitatively discern the impacts of pore connectivity. A clear example is that of gas sorption. Moving away from the standard analysis, recent work by Garcia-Martinez et al.56 demonstrated the potential to probe pore constrictions in a mesostructured USY zeolite via scanning the hysteresis loop in the Ar isotherms. While reversible pore adsorption was evidenced at 87 K, by lowering the temperature (77 and 64 K) it was possible to induce and thereby study the form of the hysteresis loops (Fig. 6b). Similar indications of the sensitivity of gas sorption were also attained by molecular simulations of Coasne et al.80, which suggest that the configuration of the hierarchical pore structure could disrupt capillary condensation, suppressing the hysteresis loop in N2 isotherms. However, it is important to note that hysteresis loops may also be suppressed by surface roughness as well as temperature, and the lack of hysteresis may be misinterpreted as a well-connected pore structure.
Only very recently, positron annihilation lifetime spectroscopy was shown to have unprecedented sensitivity to the pore architecture in HOZs22,28. Remarkably, a direct link between the escape of ortho-positronium species formed upon positron implantation to vacuum, which directly relates to the global connectivity of the pore network, and the catalyst lifetime of hierarchical MFI-type zeolites was established in the conversion of methanol to hydrocarbons (Fig. 6h)28. The dynamic way in which positrons interrogate a porous solid opens unique opportunities for the characterization of their pore architecture and chemical functionality81,82,83,84. However, this work is currently in very early stages and a number of practical factors, such as the need for a radioactive source and the lack of a comprehensive framework for spectral analysis and interpretation, need to be addressed to widen the applicability of the technique for the assessment of HOZs.
Notably, the sensitivity of positron annihilation lifetime spectroscopy was only initially recognized through the comparison of HOZs purposefully synthesized with distinct mesopore locations. This suggests that, with an improved understanding, there is still room for other less well known techniques to contribute to the growing demand for a precise structural understanding of hierarchical materials. For example, hyperpolarized 129Xe NMR85,86, which was previously shown to be sensitive to the exchange between the different pore environments in both delaminated and mesoporous zeolites, could yet offer a more tangible means to rationalize mass transfer behaviour. Since pore connectivity is among the main parameters influencing molecular transport, diffusion measurements of the actual substrates and products, can, in turn, be expected to contribute to the elucidation of pore connectivity. For example, the enhanced oil-to-gasoline conversion and reduced tendency to coke formation in various fluid catalytic cracking catalysts with increasing diffusivities, closely corroborates the relation between the catalyst lifetime and the pore connectivity87.
Guest diffusion and catalyst effectiveness
The primary aim of designing HOZs is to utilize active sites more efficiently in catalytic applications by improving the transport attributes, which can be expressed in terms of the catalyst effectiveness. Effectiveness factors and the expected concentration profiles of guests within zeolites can be estimated with knowledge of the effective diffusivity and some basic kinetic parameters. Depending on the rate of exchange between the micropores and the auxiliary pore network, two limiting cases can be identified that determines the relative contribution of mesopore diffusion (fast exchange) and the reduction in the characteristic diffusion length (slow exchange) to the overall transport enhancement of a given HOZ (Fig. 7a). Yet, although the superior performance of HOZs is commonly ascribed to facilitated molecular transport, until recently only a limited number of studies had measured the diffusion characteristics. Transport enhancements can in principle be simply accessed through any method capable of following the rates of uptake and release of a guest molecule, such as gravimetry46,88,89,90, IR or NMR spectroscopy90,91, or the zero-length column and frequency response methods90,91. However, in practice, variations in the absolute values and relative enhancements of the effective diffusivity over orders of magnitude are not uncommon depending on the technique, measurement conditions and probe molecules used, as well as the sample properties (Fig. 7b,c). In fact, for a given zeolite and hierarchical pore structure, the prevailing mechanism of intrinsic mass transfer can be altered by the guest molecules and the measurement conditions.
With respect to the sample, two particularly challenging aspects are dealing with the heterogeneity of the crystal and of the mesopore size and geometry, the effects of which may completely dominate over the governing mechanisms of mass transfer. Notably, due to the prevalence of transport resistances at the external surface92 or within the zeolite crystal93,94, even the mass transfer in bulk zeolites cannot be described by an intracrystalline diffusivity alone90,91. The situation only becomes more complex for HOZs, in which interfacial barriers between the additional porosity levels must also be accounted for. If the extension of the micropore domain is much smaller than that of the crystal, the contribution of such barriers to the overall transport could dominate over the resistance by micropore diffusion. Consequently, to attain any information about the microdynamic origins of transport enhancements, a highly involved analysis requiring dedicated expertise is normally essential.
To achieve the dream of predicting the concentration profiles of molecules within the pore networks, the in-depth exploration of the elementary processes of mass transfer through the application of microscopic diffusion measurements is essential. IR microimaging (Fig. 7d)95 as well as single molecule tracking96,97 and microspectroscopy98, can potentially distinguish the two limiting cases of guest distribution in HOZs. While single molecule tracking provides direct information about the rate of propagation of individual molecules, and thus the permeability of the pore spaces96, quasielastic neutron scattering90,99 and pulsed field gradient NMR90,91 offer complementary insights concerning whole molecular assemblies. Being applicable to any proton containing molecule, the range of probes amenable to the latter techniques significantly exceeds that of single molecule tracking, which so far necessitates the application of fluorophores. While the diffusion path lengths accessible by pulsed field gradient NMR vary from approximately a hundred nanometres to tens of micrometres, quasielastic neutron scattering is sensitive to displacements over nanometres enabling the rate of molecular displacements within the purely microporous regions to be monitored even in hierarchical pore systems. Complementing information about molecular exchange rates between different pore spaces may be provided by 129Xe NMR85,86 and solid state exchange NMR100 by exploiting their sensitivity to the chemical environment. Simulation studies searching of the structural origin of these resistances are also gaining increasing relevance101,102.
Though we now dispose of highly sophisticated techniques to quantify transport enhancements by measuring the uptake and release of guest molecule, the correlation with the catalytic properties of HOZs is still rather limited. These difficulties are largely related to the nanoscopic size of the crystalline domains in HOZs, given the fact that the monitoring of transient concentration profiles during mass separation and catalytic conversion has only quite recently become possible by microimaging in large bulk crystals95. Knowledge of such profiles, however, is a prerequisite of any in depth understanding of mass transfer phenomena, and it is expected that advancements will enable extension of the techniques to match or go beyond the reactivity mapping achieved through fluorescence microscopy (Fig. 7e)97,103.
Future directions
This review has demonstrated that the structural analysis of HOZs should not simply be approached in a similar manner to their bulk predecessors. New strategies are essential to access vital information about their crystal, active site and pore structure that is necessary to rationalize their performance. Several actions are viewed as critical to move forward with the design. Beginning with the synthesis, the attainment of an improved understanding of key mechanistic aspects, including the implications of integrating auxiliary pores at the atomic scale and the pore network organization at the mesoscale, will undoubtedly guide the development of more efficient zeolite catalysts. Theoretical studies are expected to hold great potential here, as approaches are devised to overcome the challenges posed by the system complexity.
As highlighted, the scope of established techniques requires careful reassessment to ensure the adequacy for the characterization of materials with multilevel pore structures, and, where necessary, new and improved methods to assess primary structural attributes need to be developed. For example, due to the dominant catalytic role in diffusion constrained reactions, a greater emphasis on the characterization of the active sites associated with the surface of the auxiliary pore network will be invaluable. Similarly, advanced methods are required to comprehensively analyse the impact of reductions in the coherent domain size on the crystal structure. Coupled to this, the wider comparative catalytic assessment of zeolites with different morphologies, which has so far only be tackled by a limited number of studies22,44,104, is essential to confirm the relative effectiveness. Herein, the reproducibility of the synthesis procedures between labs will be essential to corroborate the findings. Integral to the understanding and quantification of the improved catalyst effectiveness in HOZs, the advancement of methods to monitor guest profiles constitutes a primary challenge of future research.
Given the complexity of these multidimensional systems, intensive interdisciplinary research involving the development of integrated approaches and the comparison of model samples will be crucial to accomplish many of these tasks. Similarly, improved methods of data analysis and the wider accessibility of advanced analytical techniques will greatly facilitate the identification of structure–performance relations. We expect that many of the important aspects raised through the examination of HOZ catalysts will find broad general relevance in the design of other hierarchically organized materials.
Additional information
How to cite this article: Mitchell, S. et al. Structural analysis of hierarchically organized zeolites. Nat. Commun. 6:8633 doi: 10.1038/ncomms9633 (2015).
References
Lakes, R. Materials with structural hierarchy. Nature 361, 511–515 (1993) .
Brinker, C. J. Porous inorganic materials. Curr. Opin. Solid State Mater. Sci. 1, 798–805 (1996) .
Li, Y., Fu, Z.-Y. & Su, B.-L. Hierarchically-structured porous materials for energy conversion and storage. Adv. Funct. Mater. 22, 4634–4667 (2012) .
Gabardo, C. M., Zhu, Y., Soleymani, L. & Moran-Mirabal, J. M. Bench-top fabrication of hierarchically structured high-surface-area electrodes. Adv. Funct. Mater. 23, 3030–3039 (2013) .
Hartmann, M. Hierarchical zeolites: a proven strategy to combine shape selectivity with efficient mass transport. Angew. Chem. Int. Ed. 43, 5880–5882 (2004) .
Pérez-Ramírez, J., Christensen, C. H., Egeblad, K., Christensen, C. H. & Groen, J. C. Hierarchical zeolites: enhanced utilisation of microporous crystals in catalysis by advances in materials design. Chem. Soc. Rev. 37, 2530–2542 (2008) .
Holm, M. S., Taarning, E., Egeblad, K. & Christensen, C. H. Catalysis with hierarchical zeolites. Catal. Today 168, 3–16 (2011) .
Lopez-Orozco, S., Inayat, A., Schwab, A., Selvam, T. & Schwieger, W. Zeolitic materials with hierarchical porous structures. Adv. Mater. 23, 2602–2615 (2011) .
Möller, K. & Bein, T. Mesoporosity - a new dimension for zeolites. Chem. Soc. Rev. 42, 3689–3707 (2013) .
Mintova, S., Gilson, J.-P. & Valtchev, V. Advances in nanosized zeolites. Nanoscale 5, 6693–6703 (2013) .
Serrano, D. P., Escola, J. M. & Pizarro, P. Synthesis strategies in the search for hierarchical zeolites. Chem. Soc. Rev. 42, 4004–4035 (2013) .
Roth, W. J., Nachtigall, P., Morris, R. E. & Čejka, J. Two-dimensional zeolites: current status and perspectives. Chem. Rev. 114, 4807–4837 (2014) .
Chal, R., Gerardin, C., Bulut, M. & van Donk, S. Overview and industrial assessment of synthesis strategies towards zeolites with mesopores. ChemCatChem 3, 67–81 (2011) .
Pérez-Ramírez, J. et al. Expanding the horizons of hierarchical zeolites: beyond laboratory curiosity towards industrial realization. ChemCatChem 3, 1731–1734 (2011) .
Li, K., Valla, J. & Garcia-Martinez, J. Realizing the commercial potential of hierarchical zeolites: new opportunities in catalytic cracking. ChemCatChem 6, 46–66 (2014) .
Keller, T. C., Arras, J., Wershofen, S. & Pérez-Ramírez., J. Design of hierarchical zeolite catalysts for the manufacture of polyurethane intermediates. ACS Catal. 5, 734–743 (2015)An article demonstrating the need to optimize both the pore and crystal structure in order to attain industrial viable zeolite catalysts for the sustainable synthesis of polyurethane intermediates .
Musilová, Z., Žilkova, N., Park, S.-E. & Čejka, J. Aromatic transformations over mesoporous ZSM-5: advantages and disadvantages. Top. Catal. 53, 1457–1469 (2010)An article demonstrating the distinct catalytic impacts that hierarchical structuring can have in chemical transformations involving multiple steps .
Milina, M., Mitchell, S., Michels, N.-L., Kenvin, J. & Pérez Ramírez, J. Interdependence between porosity, acidity, and catalytic performance in hierarchical ZSM-5 zeolites prepared by post-synthetic modification. J. Catal. 308, 398–407 (2013) .
Jo, C., Ryoo, R., Žilková, N., Vitvarová, D. & Čejka, J. The effect of MFI zeolite lamellar and related mesostructures on toluene disproportionation and alkylation. Catal. Sci. Technol. 3, 2119–2129 (2013) .
Kim, J., Choi, M. & Ryoo, R. Effect of mesoporosity against the deactivation of MFI zeolite catalyst during the methanol-to-hydrocarbon conversion process. J. Catal. 269, 219–228 (2010) .
Bleken, F. L. et al. Catalyst deactivation by coke formation in microporous and desilicated zeolite H-ZSM-5 during the conversion of methanol to hydrocarbons. J. Catal. 307, 62–73 (2013) .
Milina, M., Mitchell, S., Cooke, D., Crivelli, P. & Pérez-Ramírez, J. Mesopore quality determines the lifetime of hierarchically structured zeolite catalysts. Nat. Commun. 5, 3922 (2014)First demonstration of the critical impact of mesopore topology on the performance of hierarchically organized zeolite catalysts .
Verboekend, D. & Pérez-Ramírez, J. Design of hierarchical zeolites by desilication. Catal. Sci. Technol. 1, 879–890 (2011) .
Groen, J. C., Peffer, L. A. A., Moulijn, J. A. & Pérez-Ramírez, J. Mechanism of hierarchical porosity development in MFI zeolites by desilication: the role of aluminium as a pore-directing agent. Chem. Eur. J. 11, 4983–4994 (2005) .
Verboekend, D. & Pérez-Ramírez, J. Desilication mechanism revisited: highly mesoporous all-silica zeolites enabled through pore-directing agents. Chem. Eur. J. 17, 1137–1147 (2011) .
Svelle, S. et al. How defects and crystal morphology control the effects of desilication. Catal. Today 168, 38–47 (2011) .
Fodor, D., Redondo, A. B., Krumeich, F. & van Bokhoven, J. A. Role of defects in pore formation in MFI zeolites. J. Phys. Chem. C 119, 5447–5453 (2015) .
Milina, M., Mitchell, S., Cooke, D., Crivelli, P. & Pérez-Ramírez, J. Impact of pore connectivity on the design of long-lived zeolite catalysts. Angew. Chem. Int. Ed. 54, 1591–1594 (2015) .
Roth, W. et al. A family of zeolites with controlled pore size prepared using a top-down method. Nat. Chem. 5, 628–633 (2013) .
Wheatley, P. S. et al. Zeolites with continuously tuneable porosity. Angew. Chem. Int. Ed. 126, 13426–13430 (2014) .
Ouyang, X. et al. Single-step delamination of a MWW borosilicate layered zeolite precursor under mild conditions without surfactant and sonication. J. Am. Chem. Soc. 136, 1449–1461 (2014) .
Silaghi, M.-C., Chizallet, C. & Raybaud, P. Challenges on molecular aspects of dealumination and desilication of zeolites. Microporous Mesoporous Mater. 191, 82–96 (2014)A review of the molecular scale understanding of zeolite demetallation .
Zhai, D. et al. Dissolution and absorption: a molecular mechanism of mesopore formation in alkaline treatment of zeolite. Chem. Mater. 27, 67–74 (2014) .
Silaghi, M.-C. et al. Regioselectivity of Al-O bond hydrolysis during zeolites dealumination unified by Brønsted-Evans-Polanyi relationship. ACS Catal. 5, 11–15 (2015) .
Lisboa, O., Sanchez, M. & Ruette, M. Modelling extraframework aluminum (EFAL) formation in the zeolite ZSM-5 using parametric quantum and DFT methods. J. Mol. Catal. A Chem. 294, 93–101 (2008) .
Malola, S., Svelle, S., Bleken, F. L. & Swang, O. Detailed reaction paths for dealumination and desilication from density functional calculations. Angew. Chem. Int. Ed. 51, 652–655 (2012) .
Na, K. et al. Pillared MFI zeolite nanosheets of a single-unit-cell thickness. J. Am. Chem. Soc. 132, 4169–4177 (2010) .
Na, K. et al. Directing zeolite structures into hierarchically nanoporous architectures. Science 333, 328–332 (2011) .
Messinger, R. J., Na, K., Seo, Y., Ryoo, R. & Chmelka, B. F. Co-development of crystalline and mesoscopic order in mesostructured zeolite nanosheets. Angew. Chem. Int. Ed. 53, 1–6 (2014) .
Serrano, D. P. et al. Molecular and meso- and macroscopic properties of hierarchical nanocrystalline ZSM-5 zeolite prepared by seed silanization. Chem. Mater. 21, 641–654 (2009) .
Zhu, J. et al. Highly mesoporous single-crystalline zeolite beta synthesized using a nonsurfactant cationic polymer as a dual-function template. J. Am. Chem. Soc. 136, 2503–2510 (2014) .
Xu, D. et al. π–π interaction of aromatic groups in amphiphilic molecules directing for single-crystalline mesostructured zeolite nanosheets. Nat. Commun. 5, 4262 (2014) .
Ren, Y., Liu, B., Kiryutina, T., Xi, H. & Qian, Y. Investigation of structure formation mechanism of a mesoporous zeolite by mesoscopic simulation. Chem. Phys. 448, 9–14 (2015) .
Zhang, X. et al. Synthesis of self-pillared zeolite nanosheets by repetitive branching. Science 336, 1684–1687 (2012)A comprehensive article characterizing the crystal, active site, and pore structure and the enhanced diffusion and catalytic properties of hierarchical MFI zeolites .
Khaleel, M., Wagner, A. J., Mkhoyan, A. & Tsapatsis, M. On the rotational intergrowth of hierarchical FAU/EMT zeolites. Angew. Chem. Int. Ed. 53, 9456–9461 (2014) .
Xu, D. et al. On the synthesis and adsorption properties of single-unit-cell hierarchical zeolites made by rotational intergrowths. Adv. Funct. Mater. 24, 201–208 (2014) .
Inayat, A., Schneider, C. & Schwieger, W. Organic-free synthesis of layer-like FAU-type zeolites. Chem. Commun. 51, 279–281 (2015) .
Ng, E.-P., Chateigner, D., Bein, T., Valtchev, V. & Mintova, S. Capturing ultrasmall EMT zeolite from template-free systems. Science 335, 70–73 (2012) .
Awala, H. et al. Template-free nanosized faujasite-type zeolites. Nat. Mater. 14, 447–451 (2015) .
Choi, M. et al. Stable single-unit-cell nanosheets of zeolite MFI as active and long-lived catalysts. Nature 461, 246–249 (2009) .
García-Martínez, J., Johnson, M., Valla, J., Li, K. & Ying, J. Y. Mesostructured zeolite Y – high hydrothermal stability and superior FCC performance. Catal. Sci. Technol. 2, 987–994 (2012) .
Cho, H. S. et al. Study of argon gas adsorption in ordered mesoporous MFI zeolite framework. J. Phys. Chem. C 116, 25300–25308 (2012)Advanced in-situ gas adsorption powder X-ray diffraction synchrotron studies on a model ordered mesoporous MFI-type zeolite .
Mitchell, S. et al. Redistribution of aluminum during the preparation of hierarchical zeolites by desilication. Chem. Eur. J. 21, 14156–14164 (2015) .
Narkhede, V. V. & Gies, H. Crystal structure of MCM-22 (MWW) and its delaminated zeolite ITQ-2 from high-resolution powder X-ray diffraction data: an analysis using Rietveld technique and atomic pair distribution function. Chem. Mater. 21, 4339–4346 (2014) .
Willhammar, T. et al. Structure and catalytic properties of the most complex intergrown zeolite ITQ-39 determined by electron crystallography. Nat. Chem. 4, 188–194 (2012) .
Garcia-Martinez, J. et al. Evidence of intracrystalline mesostructured porosity in zeolites by advanced gas sorption, electron tomography and rotation electron diffraction. ChemCatChem 6, 3110–3115 (2014)An article introducing advanced gas sorption and electron-based techniques to characterize hierarchically organized porosity in zeolites .
Serrano, D. P., Garcia, R. A., Linares, M. & Gil, B. Influence of the calcination treatment on the catalytic properties of hierarchical ZSM-5. Catal. Today 179, 91–101 (2012) .
Serrano, D. P. et al. Acidic and catalytic properties of hierarchical zeolites and hybrid ordered mesoporous materials assembled from MFI protozeolitic units. J. Catal. 279, 366–380 (2011) .
Seo, Y., Cho, K., Jung, Y. & Ryoo, R. Characterization of the surface acidity of MFI nanosheets by 31P NMR of adsorbed phosphine oxides and catalytic cracking of decalin. ACS Catal. 3, 713–720 (2013)First application of basic alkylphosphines to characterize the surface acidity of MFI nanosheets .
Thibault-Starzyk, F. et al. Quantification of enhanced acid site accessibility in hierarchical zeolites – the accessibility index. J. Catal. 264, 11–14 (2009) .
Aelst, J. V. et al. Hierarchization of USY zeolite by NH4OH. A postsynthetic process investigated by NMR and XRD. J. Phys. Chem. C 118, 22573–22582 (2014)Comprehensive study of the structural evolution during the hierarchization of a USY zeolite by NMR and XRD .
Aramburo, L. R. et al. 3D nanoscale chemical imaging of the distribution of aluminum coordination environments in zeolites with soft X-ray microscopy. ChemPhysChem 14, 496–499 (2013)Pioneering contribution on the characterization of the distribution and coordination of aluminum within zeolites .
Pérez-Ramírez, J., Verboekend, D., Bonilla, A. & Abelló, A. Zeolite catalysts with tunable hierarchy factor by pore-growth moderators. Adv. Funct. Mater. 19, 3972–3979 (2009) .
Galarneau, A., Villemot, F., Rodriguez, J., Fajula, F. & Coasne, B. Validity of the t-plot method to assess microporosity in hierarchical micro/mesoporous materials. Langmuir 30, 13266–13274 (2014) .
Groen, J. C., Peffer, L. A. & Pérez-Ramírez, J. Pore size determination in modified micro-and mesoporous materials. Pitfalls and limitations in gas adsorption data analysis. Microporous Mesoporous Mater. 60, 1–17 (2003) .
Zečević, J., Gommes, C. J., Friedrich, H., de Jongh, P. E. & de Jong, K. P. Mesoporosity of zeolite Y: quantitative three-dimensional study by image analysis of electron tomograms. Angew. Chem. Int. Ed. 51, 4213–4217 (2012) .
Kruk, M., Jaroniec, M. & Sayari, A. Application of large pore MCM-41 molecular sieves to improve pore size analysis using nitrogen adsorption measurements. Langmuir 13, 6267–6273 (1997) .
Kruk, M. & Jaroniec, M. Accurate method for calculating mesopore size distributions from argon adsorption data at 87K developed using model MCM-41 materials. Chem. Mater. 12, 222–230 (2000) .
Galarneau, A., Cambon, H., Di Renzo, F. & Fajula, F. True microporosity and surface area of mesoporous SBA-15 silicas as a function of synthesis temperature. Langmuir 17, 8328–8335 (2001) .
Ravikovitch, P. I. & Neimark, A. V. Calculations of pore size distributions in nanoporous materials from adsorption and desorption isotherms. Stud. Surf. Sci. Catal. 129, 597–606 (2000) .
Thommes, M., Mitchell, S. & Pérez-Ramírez, J. Surface and pore structure assessment of hierarchical MFI zeolites by advanced water and argon sorption studies. J. Phys. Chem. C 116, 18816–18823 (2012) .
Mitchell, S., Michels, N.-L., Kunze, K. & Pérez-Ramírez, J. Visualization of hierarchically structured zeolite bodies from macro to nano length scales. Nat. Chem. 4, 825–831 (2012) .
Möller, K., Yilmaz, B., Müller, U. & Bein, T. Hierarchical zeolite beta via nanoparticle assembly with a cationic polymer. Chem. Mater. 23, 4301–4310 (2011) .
Kenvin, J., Jagiello, J., Mitchell, S. & Pérez-Ramírez, J. Unified method to the total pore volume and pore size distribution of hierarchical zeolites from argon adsorption and mercury intrusion. Langmuir 31, 1242–1247 (2015) .
Wei, Y., Parmentier, T. E., de Jong, K. P. & Zečević, J. Tailoring and visualizing the pore architecture of hierarchical zeolites. Chem. Soc. Rev. 44, 7234–7261 (2015)A comprehensive review of the approaches which have been developed to visualize the pore architecture of hierarchically organized zeolites .
de Jong, K. P. et al. Zeolite Y crystals with trimodal porosity as ideal hydrocracking catalysts. Angew. Chem. Int. Ed. 49, 10074–10078 (2010) .
Karwacki, L. et al. Architecture-dependent distribution of mesopores in steamed zeolite crystals as visualized by FIB-SEM tomography. Angew. Chem. Int. Ed. 50, 1294–1298 (2011) .
Fernandez, J.-J. Computational methods for materials characterization by electron tomography. Curr. Opin. Solid State Mater. Sci. 17, 93–106 (2013) .
Willhammar, T., Mayoral, A. & Zou, X. 3D reconstruction of the atomic structures from high angle annular dark field (HAADF) STEM images and its application on zeolite silicalite-1. Dalton Trans. 43, 14158–14163 (2014) .
Coasne, B., Galarneau, A., Gerardin, C., Fajula, F. & Villemot, F. Molecular simulation of adsorption and transport in hierarchical porous materials. Langmuir 29, 7864–7875 (2013) .
Gidley, D. W., Peng, H.-G. & Vallery, R. S. Positron annihilation as a method to characterize porous solids. Annu. Rev. Mater. Res. 36, 49–79 (2006) .
Jean, Y. C., Van Horn, J. D., Hung, W. S. & Lee, K.-R. Perspective of positron annihilation spectroscopy in polymers. Macromolecules 46, 7133–7145 (2013) .
Tuomisto, F. & Makkonen, I. Defect identification in semiconductors with positron annihilation: experiment and theory. Rev. Mod. Phys. 85, 1583–1631 (2013) .
Goldanskii, V. N. & Frisov, V. G. The chemistry of new atoms. Russ. Chem. Rev. 40, 633–656 (1971) .
Liu, Y. et al. Direct observation of the mesopores in ZSM-5 zeolites with hierarchical porous structures by laser-hyperpolarized 129Xe NMR. J. Phys. Chem. C 112, 15375–15381 (2008) .
Cho, K., Cho, H. A., Menorval, L. C. de & Ryoo, R. Generation of mesoporosity in LTA zeolites by organosilane surfactant for rapid molecular transport in catalytic application. Chem. Mater. 21, 5664–5673 (2009) .
Kortunov, P. et al. Diffusion in fluid catalytic cracking catalysts on various displacement scaled and its role in catalytic performance. Chem. Mater. 17, 2466–2474 (2005) .
Groen, J. C. et al. Direct demonstration of enhanced diffusion in mesoporous ZSM-5 zeolite obtained via controlled desilication. J. Am. Chem. Soc. 129, 355–360 (2007) .
Gueudré, L., Milina, M., Mitchell, S. & Pérez-Ramírez, J. Superior mass transfer properties of technical zeolite bodies with hierarchical porosity. Adv. Funct. Mater. 24, 209–219 (2014)First correlation between the diffusion properties and the degree of mesoporosity of hierarchical zeolite catalysts .
Kärger, J., Ruthen, D. M. & Theodorou, D. N. Diffusion in Nanoporous Materials Wiley (2012) .
Kärger, J. In-depth study of surface resistances in nanoporous materials by microscopic diffusion measurement. Microporous Mesoporous Mater. 189, 126–135 (2014) .
Kärger, J. Transport phenomena in nanoporous materials. ChemPhysChem 16, 24–51 (2015) .
Vasenkov, S. & Kärger, J. Evidence for the existence of intracrystalline transport barriers in MFI-type zeolites: a model consistency check using MC simulations. Microporous Mesoporous Mater. 55, 139–145 (2002) .
Adem, Z., Guenneau, F., Springuel-Huet, M. A. & Gedeon, A. PFG NMR investigations of hydrocarbon diffusion in large NaX zeolite crystals: effect of internal field gradients on diffusion data. Microporous Mesoporous Mater. 114, 337–342 (2008) .
Kärger, J. et al. Microimaging of transient guest profiles to monitor mass transfer in nanoporous materials. Nat. Mater. 13, 333–343 (2014) .
Zürner, A., Kirstein, J., Döblingern, M., Bräuchle, C. & Bein, T. Visualizing single-molecule diffusion in mesoporous materials. Nature 450, 705–709 (2007) .
Weckhuysen, B. M. Chemical imaging of spatial heterogeneities in catalytic solids at different length and time scales. Angew. Chem. Int. Ed. 48, 4910–4943 (2009) .
Stavitski, E. & Weckhuysen, B. M. Infrared and Raman imaging of heterogeneous catalysts. Chem. Soc. Rev. 39, 4615–4625 (2010) .
Jobic, H. & Theodorou, D. Quasi-elastic neutron scattering and molecular dynamics simulations as complementary techniques for studying diffusion in zeolites. Microporous Mesoporous Mater. 102, 21–50 (2007) .
Magusin, P. C. M., Schuring, D., van Oers, E. M., Haan, J. W. & van Santen, R. A. n-pentane hopping in zeolite ZK-5 studied with 13C NMR. Magn. Reson. Chem. 37, S108–S117 (1999) .
Combariza, A. F. & Sastre, G. Influence of zeolite surface in the sorption of methane from molecular dynamics. J. Phys. Chem. C 115, 13751–13758 (2011) .
Zimmermann, N. E. R., Zabel, T. J. & Keil, F. J. Transport into nanosheets: diffusion equations put to test. J. Phys. Chem. C 117, 7384–7390 (2013) .
Roeffaers, M. B. J. et al. Super-resolution reactivity mapping of nanostructured catalyst particles. Angew. Chem. Int. Ed. 48, 9285–9289 (2009) .
Kim, J.-C., Ryoo, R., Opanasenko, M. V., Shamzhy, M. V. & Čejka, J. Mesoporous MFI zeolite nanosponge as a high-performance catalyst in the Pechmann condensation reaction. ACS Catal. 5, 2596–2604 (2015) .
Melhorn, D., Valiullin, R., Kärger, J., Cho, K. & Ryoo, R. Exploring the hierarchy of transport phenomena in hierarchical pore systems by NMR diffusion measurement. Microporous Mesoporous Mater. 164, 273–279 (2012) .
Verboekend, D., Vilé, G. & Pérez-Ramírez, J. Mesopore formation in USY and beta zeolites by base leaching: selection criteria and optimization of pore-directing agents. Cryst. Growth Des. 12, 3123–3132 (2012) .
Machoke, A. G. et al. Micro/macroporous system: MFI-type zeolite crystals with embedded macropores. Adv. Funct. Mater. 27, 1066–1070 (2014) .
Corma, A., Fornes, V., Pergher, S. B., Maesen, Th. L. M. & Buglass, J. G. Delaminated zeolite precursors as selective acidic catalysts. Nature 396, 353–356 (1998) .
Chen, H. et al. Hydrothermal synthesis of zeolites with three-dimensionally ordered mesoporous-imprinted structures. J. Am. Chem. Soc. 133, 12390–12393 (2011) .
Opanasenko, M. et al. Hierarchical hybrid organic-inorganic materials with tunable textural properties obtained using zeolitic-layered precursors. J. Am. Chem. Soc. 136, 2511–2519 (2014) .
Chang, C. C., Teixeira, A. R., Li, C., Dauenhauer, P. J. & Fan, W. Enhanced molecular transport in hierarchical silicalite-1. Langmuir 29, 13945–13950 (2013) .
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Mitchell, S., Pinar, A., Kenvin, J. et al. Structural analysis of hierarchically organized zeolites. Nat Commun 6, 8633 (2015). https://doi.org/10.1038/ncomms9633
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms9633
This article is cited by
-
Investigation of ortho-positronium annihilation for porous materials with different geometries and topologies
Scientific Reports (2023)
-
The potential of zeolite nanocomposites in removing microplastics, ammonia, and trace metals from wastewater and their role in phytoremediation
Environmental Science and Pollution Research (2023)
-
Isomerization of linear hexane over acid-modified nanosized nickel-containing natural Ukrainian zeolites
Applied Nanoscience (2022)
-
N-Butyl-cyclohexane as a probe molecule to evaluate fresh and deactivated zeolite acid catalysts
Reaction Kinetics, Mechanisms and Catalysis (2022)
-
Zinc Modified Hierarchical ZSM-5 for Aromatisation of Propane
Journal of Porous Materials (2022)